Green Magnetic Nanoparticles CoFe 2 O 4 @Nb 5 O 2 Applied in Paracetamol Removal

: This study describes the synthesis of an innovative nanomaterial (patent application number BR 1020210000317) composed of cobalt ferrite functionalized in niobium pentoxide CoFe 2 O 4 @Nb 5 O 2 (CFNb), synthesized via green synthesis using tangerine peel extract. The material emphasizes the combination of a magnetic material (which allows for easy recovery after application) with niobium pentoxide (a metal which is abundant in Brazil). CFNb was applied as a catalyst for the paracetamol (PCT) degradation by photocatalysis. The new materials were characterized through surface and pore analysis (S BET , S EXT , S mic , V mic , and V TOTAL ), photoacoustic spectroscopy (PAS), zero charge point (pH PZC , scanning electron microscopy (SEM/EDS), and X-ray diffraction (XRD). The reaction parameters studied included pH and catalyst concentration. The results indicated that the CFNb nanocatalysts were efﬁcient in the paracetamol degradation, presenting better results in conditions of low pH (close to 2) and low catalyst concentration under irradiation of the 250 W mercury vapor lamp (greater than 28 mW · cm − 2 ) at 60 min of reaction.


Introduction
Catalysis is essential in several industries, allowing process optimization and reducing environmental impact [1].By using catalysts, it is possible to minimize the consumption of energy and raw materials and promote the conversion of harmful substances into more environmentally friendly products.There are two main types of catalytic process: homogeneous, in which the catalyst is in the same phase as the reactants and heterogeneous, in which the catalyst is usually solid in a different phase than the reactants.Most chemical processes make use of heterogeneous catalysis [2][3][4].
In Brazil, research on catalysts began in the 1970s [5], and since then, it has proved very useful in producing heterogeneous catalysts.With the advancement of nanoscience, the synthesis of selective and efficient nanocatalysts has been possible, allowing their recovery after reactions and reuse.Nanocatalysts are nanomaterials with catalytic properties, with dimensions in the order of nanometers (10 −9 m).Among them, magnetic nanocatalysts stand out, with advantages such as ease of recovery at the end of the process and the high catalytic efficiency of the metals that compose them [6,7].
This study combined two synthesis methods to produce nanocatalysts: synthesis by combustion in solution and reduction using plant extracts.The method employed can be categorized as green synthesis, as it adheres to the principles of green chemistry, specifically principles 1, 3, 5, and 7.These principles include the prevention of waste, the design of less dangerous chemical syntheses, the use of solvents and safer reaction conditions, and the use of renewable raw materials, respectively [10][11][12].
Different plant species are already used to obtain extracts (from leaves, flowers, or seeds) for synthesizing magnetic nanoparticles.The size and shape of the nanoparticles obtained will depend on the characteristic of the extract, the location of the plant from which it was extracted (i.e., leaves, fruits, or seeds), the reaction temperature, agitation rate, pH, and biological composition of the plant (such as flavonoids, terpenoids, amino acids, proteins, or sugars), among other factors [13].Tangerine (mandarin), whose specific classification is Citrus reticulata (C.reticulata), is one of the most important citrus genera [14].It is a widely consumed fruit with high vitamin C, B complex, flavonoids, carotenoids, and ascorbic acid [15].
Niobium is an abundant transition metal in Brazil, with about 98% of the world's known reserves located mainly in Amazonas, Goiás, and Minas Gerais.Its discovery in Brazilian territory occurred in the 1960s when not all the possible applications of this metal were yet known.It is widely used in metal alloys to provide strength and malleability, as well as in high-tech sectors such as rocket engines, producing superconducting wires, and other industrial applications confer high technological value to niobium.Niobium pentoxide (Nb 2 O 5 ) and its combinations with other compounds have been studied as photocatalysts.Researchers report the efficiency of the photocatalytic activity of niobium oxide in the degradation of dyes in textile industries [28] and of herbicides such as methylviologen [29], as well as in the reduction of atmospheric pollution [30] and emerging pollutants [31,32].
Emerging pollutants (EPs) are micropollutants considered persistent and refractory, which are currently not included in routine monitoring programs and which may be candidates for future regulation [33][34][35].Examples of EPs include surfactants, drugs, personal hygiene products, gasoline, and plasticizers [33,34,36].The concepts of EPs and contaminants of emerging concern (CECs) intersect concerning pollutants that are being identified in low concentrations in wastewater, which may require specific treatment for their removal, with conventional treatments being inefficient [33,37].
Paracetamol (or acetaminophen) is widely used worldwide as a drug without prescription.The main concern about increasing the consumption of this drug is that after ingested, about 90% of a therapeutic dose is excreted in the urine after 24 h.However, the increase in consumption raises the concern of accumulation of this drug in the food chain since it is not easily degraded by the usual treatment methods at wastewater treatment plants (WWTPs) [33].
This work aims to present a new green synthesis methodology to produce magnetic nanomaterials using tangerine peel extract.In addition, it shows the efficiency of cobalt ferrite functionalized in niobium pentoxide in the paracetamol degradation via the heterogeneous photocatalytic process.

Bibliometric Analysis
A bibliometric analysis was conducted using the Methodi Ordinatio [38] to evaluate the significance of the articles published in the last years about the subject studied.Firstly, we searched for the following terms in two science search websites: ((((ALL = (niobium)) OR ALL = (cobalt ferrite)) AND ALL = (catalyst)) AND ALL = (photocat*)) AND ALL = (magnetic).We found 155 and 139 articles in Web of Science and Science Direct, respectively.After excluding the duplicates, 248 papers were filtered by title, resulting in 211 related to this study.The importance of each article was determined using the InOrdinatio equation, Equation (1): According to Pagani (2022), IF represents the mean impact factor and corresponds to the selected journal metrics (JCR, CiteScore, SNIP, or SJR SCImago); ∆ is a value ranging from 1 to 10 assigned by the researcher, with higher values indicating a greater importance of the impact factor; λ is a value between 0 and 10 that the researcher assigns to the relevance of the publication year; Ω is a value between 0 and 10 that the researcher assigns to the significance of the publication's annual average of citations; ResearchYear denotes the year in which the research is being conducted, while PubYear represents the year the paper was published; ∑Ci is the total number of citations found in Google Scholar; and HalfLife refers to the median cited half-life of journals with JCR 2020 [38].

Bibliometric Analysis
A bibliometric analysis was conducted using the Methodi Ordinatio [38] to evaluate the significance of the articles published in the last years about the subject studied.Firstly, we searched for the following terms in two science search websites: ((((ALL = (niobium)) OR ALL = (cobalt ferrite)) AND ALL = (catalyst)) AND ALL = (photocat*)) AND ALL = (magnetic).We found 155 and 139 articles in Web of Science and Science Direct, respectively.After excluding the duplicates, 248 papers were filtered by title, resulting in 211 related to this study.The importance of each article was determined using the InOrdinatio equation, Equation (1): According to Pagani (2022), IF represents the mean impact factor and corresponds to the selected journal metrics (JCR, CiteScore, SNIP, or SJR SCImago); ∆ is a value ranging from 1 to 10 assigned by the researcher, with higher values indicating a greater importance of the impact factor; λ is a value between 0 and 10 that the researcher assigns to the relevance of the publication year; Ω is a value between 0 and 10 that the researcher assigns to the significance of the publication's annual average of citations; ResearchYear denotes the year in which the research is being conducted, while PubYear represents the year the paper was published; ∑Ci is the total number of citations found in Google Scholar; and HalfLife refers to the median cited half-life of journals with JCR 2020 [38].
Another relevant bibliometric analysis is about the years of publication of the more significant InOrdinatio articles, 63% of the publications are concentrated between 2019 and 2023, Figure 2a.The countries that lead the survey in this area are India, China, and Iran, in first, second, and third place, respectively, responsible for about 65% of the publications studied, Figure 2b.Bibliometric analysis of a subject is critical in research and academia, as it offers valuable insights into the relevance and impact of a particular area of study.By performing this analysis, it is possible to obtain quantitative information about the scientific production related to the topic, such as the number of publications, most cited authors, relevant journals, and trends over time.The Methodi Ordinatio is a current and efficient method of evaluating the articles found to be relevant to the chosen topic, as it classifies them in a ranking of relevance.
With this analysis, it was possible to identify trends and research advances about using cobalt ferrite as a catalyst and niobium as photocatalyst but have a gap in the combination of both nanomaterials to be applied in a photocatalyst.This is an unprecedented study; no result is found when you search for changing the Boolean OR by AND between niobium and cobalt ferrite.

Chemicals
Acetonitrile (CH₃CN), supplied by Merck S/A, Parque Rincão-SP, Brazil; anhydrous citric acid (C6H8O7), supplied by Perquim Rep. Com., Analytical Science, Ponta Grossa-PR, Brazil; anhydrous sodium sulfate (Na2SO4), supplied by Neon, Suzano-SP, Brazil; cobalt nitrate (Co(NO3)2.6H2O),supplied by Synth, Diadema-SP, Brazil; formic acid (CH2O2), supplied by Synth, Diadema-SP, Brazil; hydrochloric acid (HCl, 37%), supplied by VWR chemicals, São Paulo-SP, Brazil; iron nitrate (Fe(NO3)3.9H2O),supplied by Synth, Diadema-SP, Brazil; niobium pentoxide (Nb2O5), supplied by CBMM-Companhia Brasileira de Metalurgia e Mineração, Araxá-MG, Brazil; sodium hydroxide (NaOH), supplied by Dinâmica Química Contemporânea Ltd.a., Indaiatuba-SP, Brazil; and sulfuric acid (H2SO4), supplied by Dinâmica Química Contemporânea Ltd.a., Indaiatuba-SP, Brazil.Bibliometric analysis of a subject is critical in research and academia, as it offers valuable insights into the relevance and impact of a particular area of study.By performing this analysis, it is possible to obtain quantitative information about the scientific production related to the topic, such as the number of publications, most cited authors, relevant journals, and trends over time.The Methodi Ordinatio is a current and efficient method of evaluating the articles found to be relevant to the chosen topic, as it classifies them in a ranking of relevance.
With this analysis, it was possible to identify trends and research advances about using cobalt ferrite as a catalyst and niobium as photocatalyst but have a gap in the combination of both nanomaterials to be applied in a photocatalyst.This is an unprecedented study; no result is found when you search for changing the Boolean OR by AND between niobium and cobalt ferrite.

Tangerine Peel Extract
The first step to obtaining the catalyst is drying the tangerine peels, Figure 3-Step 1 (A).These peels were further subjected to washing under continuous water flow and had been previously dried in the sun to avoid fungal contamination.After this, the tangerine peels were placed in a drying oven (SL 102, SOLAB) at 353 ± 5 K for 18 h.Subsequently, the tangerine peels were crushed in an analytical mill (Q298A21, QUIMIS) and sieved to obtain a diameter lower than 425 µm (35 mesh) (wire-cloth test sieve, Bertel), Step 1 (B).Finally, the tangerine peels were stored until the next step.To obtain the tangerine peel extract, the following methodology was optimized: Step 1 (C), using an analytical balance (AUY220, SHIMADZU), 4.0 g of crushed tangerine peels were placed in a 250 mL round-bottom flask with 100 mL of distilled water, which was placed under magnetic stirring at room temperature (298 K) for 3 h (C-MAG HS 7, IKA).Next, the temperature was increased to 333 K for 1 h [16,39], the dispersion was further centrifuged at 4000 rpm (revolutions per minute) for 5 min to separate the tangerine peels from the supernatant (80-2B centrifuge, CENTRIBIO).After centrifugation, the supernatant was filtered through a paper filter to remove any possible peel in the solution.Finally, the obtained extract solution was stored in a freezer until use, completing the first step, Step 1 (D).The reducing power (EC50 RP) of this extract was 1.68 ± 0.03 mg mL −1 (analyzed by Centro de Investigação de Montanha-CIMO, Instituto Politécnico de Bragança, Bragança, Portugal).The EC50 values correspond to the concentration of extract that provides 50% of reducing power or antioxidant activity.Lower EC50 values mean higher antioxidant capacity of the samples [40].

Tangerine Peel Extract
The first step to obtaining the catalyst is drying the tangerine peels, Figure 3-Step 1 (A).These peels were further subjected to washing under continuous water flow and had been previously dried in the sun to avoid fungal contamination.After this, the tangerine peels were placed in a drying oven (SL 102, SOLAB) at 353 ± 5 K for 18 h.Subsequently, the tangerine peels were crushed in an analytical mill (Q298A21, QUIMIS) and sieved to obtain a diameter lower than 425 µm (35 mesh) (wire-cloth test sieve, Bertel), Step 1 (B).Finally, the tangerine peels were stored until the next step.To obtain the tangerine peel extract, the following methodology was optimized: Step 1 (C), using an analytical balance (AUY220, SHIMADZU), 4.0 g of crushed tangerine peels were placed in a 250 mL round-bottom flask with 100 mL of distilled water, which was placed under magnetic stirring at room temperature (298 K) for 3 h (C-MAG HS 7, IKA).Next, the temperature was increased to 333 K for 1 h [16,39], the dispersion was further centrifuged at 4000 rpm (revolutions per minute) for 5 min to separate the tangerine peels from the supernatant (80-2B centrifuge, CENTRIBIO).After centrifugation, the supernatant was filtered through a paper filter to remove any possible peel in the solution.Finally, the obtained extract solution was stored in a freezer until use, completing the first step, Step 1 (D).The reducing power (EC50 RP) of this extract was 1.68 ± 0.03 mg mL −1 (analyzed by Centro de Investigação de Montanha-CIMO, Instituto Politécnico de Bragança, Bragança, Portugal).The EC50 values correspond to the concentration of extract that provides 50% of reducing power or antioxidant activity.Lower EC50 values mean higher antioxidant capacity of the samples [40].In the second step, the cobalt ferrite functionalized catalysts in niobium pentoxide (CoFe2O4@Nb2O5) have been synthesized.The salts Fe 3+ (11.4 mmol) and Co 2+ (5.7 mmol) were weighed in a 150 mL Erlenmeyer flask.After 25 mL of tangerine peel extract (obtained in the first step) was added, the resultant solution showed an immediately black color, Step 2 (E).The Erlenmeyer was stirred in the shaker (TE-424, TECNAL) at 200 ± 2 rpm, 298 ± 2 K for 15 min.The theoretical weight of the cobalt ferrite formed was 1.33 g, so this amount of niobium pentoxide was weighed and added in the Erlenmeyer after the In the second step, the cobalt ferrite functionalized catalysts in niobium pentoxide (CoFe 2 O 4 @Nb 2 O 5 ) have been synthesized.The salts Fe 3+ (11.4 mmol) and Co 2+ (5.7 mmol) were weighed in a 150 mL Erlenmeyer flask.After 25 mL of tangerine peel extract (obtained in the first step) was added, the resultant solution showed an immediately black color, Step 2 (E).The Erlenmeyer was stirred in the shaker (TE-424, TECNAL) at 200 ± 2 rpm, 298 ± 2 K for 15 min.The theoretical weight of the cobalt ferrite formed was 1.33 g, so this amount of niobium pentoxide was weighed and added in the Erlenmeyer after the above referred 15 min, Step 2 (F).The mixture was stirred for more than 15 min under the same conditions.In sequence, the mixture was transferred to a porcelain crucible, which stayed in a drying oven for 4.5 h at 373 ± 10 K until forming a gel.Finally, the porcelain crucible with the gel was placed in a calcination furnace (N1200, NOVUS) with a heating ramp to increase the temperature to 423 K during 30 min and to keep it there for 1 h.The temperature was increased by 150 K per cycle (30 min to rise and 1 h in the final temperature) until it reached 873 K.After calcination, the resulting material in the porcelain crucible is cobalt ferrite functionalized in niobium (CFNb), Step 2 (G).

Magnetic Demonstration
A magnetic demonstration can be seen in the magnetic separation images over time.One catalyst sample (around 0.025 g) was placed in 5 mL of distilled water under stirring.The flask with this suspension was placed next to the magnet, and images were captured to register the separation.

Surface and Pore Analyzer
The determination of the specific surface area was carried out for the characterization of porous and finely dispersed solids [41].Analysis of N 2 adsorption-desorption isotherms at 77 K was carried out with a Quantachrome NOVATouch XL4 adsorption analyzer to determine the textural properties of prepared samples.The BET specific surface area (S BET ) was calculated by the Brunauer, Emmett, Teller method (BET).The external surface area (S ext ) and the micropore volume (Vmic) were obtained by using the t-method and employing the ASTM standard D-6556-01 to calculate the thickness (t).Then, the microporous surface area (S mic ) was calculated subtracting the Sext from S BET and the average pore width (W mic ) by approximation (W = 4 V mic /S mic ).The total pore volume (V Total ) was determined at p/p 0 = 0.98.

Photoacoustic Spectroscopy
Photoacoustic spectroscopy is applied to measure the effect of absorbed electromagnetic energy (particularly light) using acoustic detection to determine the band gap energy relevant to photocatalysis [42].Photoacoustic spectroscopy was performed at 200-700 nm, 800 W, and 23 Hz conditions.The catalyst samples were diluted in 80% silica (quartz powder) due to the color being too dark to analyze without dilution.The evaluated catalysts CFNb, as well as Nb 2 O 5 without calcination, which is an efficient photocatalyst used as a reference.

Point of Zero Charge (pHpzc)
The determination of pHpzc allows suppositions to be made about types of active surface centers and the adsorption abilities of surfaces [43].For this determination, approximately 0.09 g of material was added in 6 different Erlenmeyer flasks with different initial pH values (pH 0 ).The Erlenmeyer flasks were loaded with 15.0 mL of 0.01 mol•L −1 Na 2 SO 4 and their pHs were adjusted to different values (2.0, 4.0, 6.0, 8.0, 10.0, and 12.0) using 0.02 mol•L −1 NaOH and 0.02 mol•L −1 H 2 SO 4 solutions.The Erlenmeyer flasks were placed in an orbital shaker (TE-424, TECNAL) at 200 ± 3 rpm, 298 ± 2 K.After stirring, the suspension was separated from the catalyst using a magnet, and the final pH was measured (pH F ).The pH PZC corresponded to the average of the final pH values which tended to a constant value, regardless of the initial pH value [31,44].

Scanning Electron Microscopy (SEM) and Energy Dispersive Spectroscopy (EDS)
The topographic surface images were obtained using a scanning electron microscope model VEGA 3 LMU brand TESCAN, completed with a W 20 kV filament, 3.0 nm resolution, retractable SE and BSE detectors, and low-vacuum mode (500 Pa) chamber with an internal diameter of 230 mm and door opening of 148 mm, 5-axis compucentric stage, fully motorized, with X: 80 mm, Y: 60 mm, and Z: 47 mm movements, CCD camera for viewing the sample chamber and "chamberview" software, VegaTC operating software, data processing system and track ball.The microscope also has a DES Detector, model AZTec Energy X-Act, resolution 130 eV, Oxford.

X-ray Diffraction (XRD) Analysis
This test serves to analyze the crystal structure and to identify and quantify the crystalline phases of the samples [45].The X-ray diffractograms of the samples were obtained using a Rigaku diffractometer model Miniflex 600 with copper radiation (CuKα λ = 1.54 Å), in the Bragg angle range of 3 • ≤ 2θ ≤ 90 • , with a step of 0.05 • and time fixed count of 2 s per step in semi-continuous mode.The signals emitted are given as an intensity graph, whose unit is expressed in counts per second (cps) as a function of the scanning angle (2θ, or Bragg angle).To identify the materials, the signals obtained are compared with the literature to confirm the presence of the desired phase and/or other phases.The average crystallite sizes (L) were calculated by Scherrer's equation (2), which is given as follows: where k is a constant equal to 0.91, λ is the wavelength of the X-ray radiation (all diffraction patterns shown in this work were performed with CuKa radiation, so λ is 0.154 nm), θ is the diffraction angle in radians and β is the full width half maximum (FWHM) in radians.

Transmission Electron Microscopy
The transmission electron microscopy (TEM) images were obtained to verify their morphology with the help of a microscope (JOEL JEM-1250) of 120 kV.

Photocatalysis
Before tests, the calibration curve for quantification of paracetamol was charted in HPLC-high-performance liquid chromatography (YL Clarity 9100) equipped with a precolumn, C-18 column (Phenomenex), and a visible, ultraviolet detector (UV-VIS) at 243 nm, which identifies itself as a peak that elutes after approximately 3.5 min of scanning [46].The mobile phase comprised water and acetonitrile (80/20 volume ratio) with a 1.0 mL•min −1 flow rate.The concentration of the 20 mg•L −1 paracetamol solution was chosen based on the literature on paracetamol degradation [47][48][49].
All photocatalytic tests were performed in the photocatalytic chamber exemplified in Figure 4 with all elements that compose it.Therefore, the steps to carry out those tests were:

•
The paracetamol solution was placed in the reactor (B), which was established in the photocatalytic chamber (A); The mercury lamp (G) 250 Watts was lit, remaining on until the end of the reaction; • All nine samples of all reactions were analyzed using HPLC applying the calibration curve made initially as a reference.A design of experimental (DoE), as a central composite design (CCD), was carried out by varying the catalyst concentration and the pH of the solution, as shown in Table 1.To verify this catalyst's efficiency, photocatalysis tests were performed using only cobalt ferrite synthesized with the same extract (CFext) and niobium (Nb600) calcined with the same methodology, and compared and discussed the results.Additionally, reuse tests were conducted to demonstrate the CFNb applicability several times.

Catalyst Preparation
After completing the synthesis of the materials, in the recovery of the material that remains in the porcelain crucible after calcination, Step 2 (G), there is a weight loss of around 11 ± 3%, Figure 5a.The catalysts were stored in Falcon tubes until use, and the magnetic properties were tested by approaching with a magnet.The magnetic attraction is powerful enough that the magnet can hold the tube containing the sample, as shown in Figure 5b.A design of experimental (DoE), as a central composite design (CCD), was carried out by varying the catalyst concentration and the pH of the solution, as shown in Table 1.To verify this catalyst's efficiency, photocatalysis tests were performed using only cobalt ferrite synthesized with the same extract (CFext) and niobium (Nb600) calcined with the same methodology, and compared and discussed the results.Additionally, reuse tests were conducted to demonstrate the CFNb applicability several times.

Catalyst Preparation
After completing the synthesis of the materials, in the recovery of the material that remains in the porcelain crucible after calcination, Step 2 (G), there is a weight loss of around 11 ± 3%, Figure 5a.The catalysts were stored in Falcon tubes until use, and the magnetic properties were tested by approaching with a magnet.The magnetic attraction is powerful enough that the magnet can hold the tube containing the sample, as shown in Figure 5b.Besides the magnetic properties that facilitate the separation after using the magnetic nanoparticles in reactions, the type of synthesis created has several advantages over other types already reported in the literature.Among the benefits can be highlighted: utilization of biomass, namely fruit peels; extract production using only distilled water as a solvent and at room temperature; incorporation of the niobium pentoxide support in the same stage of synthesis of cobalt ferrite, when most other methods first suggest the synthesis of the precursor and then impregnation in the support, which would require more time and higher cost; high support incorporation compared to other methods, without losing or decreasing the magnetic properties of cobalt ferrite; added value to a raw material abundant in Brazilian territory, niobium; and low-cost synthesis, using common laboratory equipment.

Magnetic Demonstration
The catalyst suspension with a concentration of approximately 5 g.L −1 was placed next to the magnet and registered images at times: 0, 5, 10, 15, 20, 25, 30, 45, 60, and 120 s (Figure 6).We can note that around 30 s, a significant amount of the catalyst was already separated, and at the final time (120 s), practically the total catalyst was next to the magnet.Besides the magnetic properties that facilitate the separation after using the magnetic nanoparticles in reactions, the type of synthesis created has several advantages over other types already reported in the literature.Among the benefits can be highlighted: utilization of biomass, namely fruit peels; extract production using only distilled water as a solvent and at room temperature; incorporation of the niobium pentoxide support in the same stage of synthesis of cobalt ferrite, when most other methods first suggest the synthesis of the precursor and then impregnation in the support, which would require more time and higher cost; high support incorporation compared to other methods, without losing or decreasing the magnetic properties of cobalt ferrite; added value to a raw material abundant in Brazilian territory, niobium; and low-cost synthesis, using common laboratory equipment.

Magnetic Demonstration
The catalyst suspension with a concentration of approximately 5 g L −1 was placed next to the magnet and registered images at times: 0, 5, 10, 15, 20, 25, 30, 45, 60, and 120 s (Figure 6).We can note that around 30 s, a significant amount of the catalyst was already separated, and at the final time (120 s), practically the total catalyst was next to the magnet.Besides the magnetic properties that facilitate the separation after using the magnetic nanoparticles in reactions, the type of synthesis created has several advantages over other types already reported in the literature.Among the benefits can be highlighted: utilization of biomass, namely fruit peels; extract production using only distilled water as a solvent and at room temperature; incorporation of the niobium pentoxide support in the same stage of synthesis of cobalt ferrite, when most other methods first suggest the synthesis of the precursor and then impregnation in the support, which would require more time and higher cost; high support incorporation compared to other methods, without losing or decreasing the magnetic properties of cobalt ferrite; added value to a raw material abundant in Brazilian territory, niobium; and low-cost synthesis, using common laboratory equipment.

Magnetic Demonstration
The catalyst suspension with a concentration of approximately 5 g.L −1 was placed next to the magnet and registered images at times: 0, 5, 10, 15, 20, 25, 30, 45, 60, and 120 s (Figure 6).We can note that around 30 s, a significant amount of the catalyst was already separated, and at the final time (120 s), practically the total catalyst was next to the magnet.

Characterization Techniques 4.3.1. Surface and Pore Analyzer
The Surface and pore analysis was performed with just Nb 2 O 5 before nanoparticle synthesis.The values of the S BET , S ext , S mic , V mic , and V total were 185 m 2 •g, 88 m 2 •g, 97 m 2 •g, 50.3 mm 3 •g, and 158 mm 3 •g, respectively.Without calcination, the Nb 2 O 5 is amorphous until heat treatment at 673 K, and therefore must have presented higher values up to this temperature.In theory, using the material with higher S BET , S mic , and V mic would be more interesting, as it would better aggregate the cobalt ferrite particles and still have a higher surface area for active sites for catalysis.However, after mixing with the Fe 3+ and Co 2+ salts reagents and tangerine extract, there is another heat treatment step up to 873 K, and this temperature may also influence the behavior of both the Nb 2 O 5 and the final catalyst.According to the literature, the materials containing niobium pentoxide and cobalt ferrite have specific surface area BET (S BET ), Nb 2 O 5 calcined at 873 K has S BET between 22 and 57.8 mm 2 •g [50,51], without other compounds.Niobium pentoxide nanocomposites under the same temperature calcination can be S BET between 21.24 and 149.63 mm 2 •g [32,52].Cobalt ferrite in the literature has S BET 44 mm 2 •g at 673 K, and with carbon, the shell can be S BET around 330 mm 2 •g at 773 K [53,54].However, there is no specific comparison for the material CoFe 2 O 4 @Nb 2 O 5 , as it is an innovation.

Photoacoustic Spectroscopy
The photoacoustic spectrum (PAS) in the UV-Vis region of 200-700 nm for the catalyst showed a broad absorption band between 225-420 nm similar to the PA spectrum of non-calcined Nb 2 O 5 .Applying the photoacoustic method with phase resolution (PAPR) to the non-calcined Nb 2 O 5 spectrum, an average phase difference of (12 ± 3) • was observed between two absorption peaks.Therefore, the PAPR method indicated two regional absorber centers between 225-420 nm.The PAPR method found an absorption peak at 300 nm (peak 1), corresponding to the transition from ligand-to-metal charge transfer (LMCT) from O 2− to Nb 5+ , and another at around 450 nm (peak 2) due to niobium nanodomains.For all catalysts, peak 1 remained at approximately 300 nm.However, peak 2 shifted to around 50 nm compared to non-calcined Nb 2 O 5 .
The intensity of the photoacoustic signal did not change with increasing calcination temperature during the synthesis.This result, in addition to not indicating changes in the band gap and the absorption threshold, suggests a slight variation in the size of the crystal with the increase of the calcination temperature.
GAP energy was calculated using the linear method and the derivative method, and it was an average value very close to the value of the gap energy for Nb 2 O 5 recorded in the literature, equal to 3.1 eV [55].The GAP energy values are 3.14 eV (linear method) and 3.19 eV (derivative method) both for Nb 2 O 5 ; for the CFNb catalyst they are 3.12 eV (linear method) and 3.20 eV (derivative method).
As mentioned, the band gap value for Nb 2 O 5 in the literature is 3.1 eV, while for cobalt ferrite around 1.1 eV [56].Thus, it is observed that niobium pentoxide has more influence on this characteristic of the nanomaterial than the metal complex.To compare niobium pentoxide with different iron fractions, the band gap ranges from 3.05 to 3.94 eV, with values relatively close to those found in this work [32].Compared with TiO 2 P25, the most widely used commercial photocatalyst, it has a band gap equal to 3.2 eV [57].The fact that the synthesized catalysts have a band gap close to that of TiO 2 P25 reveals that they may also be promising for application in photocatalysis.

Point of Zero Charge (pHpzc)
Depending on the pH, the catalyst surface may be uncharged, negatively charged (pH > pH PZC ), or positively charged (pH < pH PZC ) [58].The isoelectric point, also known as PZC (point of zero charge), is the pH at which the suspended particles have zero net charges and no mobility in the electric field (pH PZC ) [8].From the results of pH PZC , it is possible to notice that CFNb has a pH PZC value of around 6.9, Figure 7. Compared with the literature, the niobium oxide (Nb 2 O 5 ) calcined at 873 K has 7.22 as a pH PZC value [31].The cobalt ferrite has the value of pH PZC 7.2 when calcined at 873 K [59].El-Khawaga et al. (2023) found a value of 6.9 for the pH PCZ , the same found in this work [60].
possible to notice that CFNb has a pHPZC value of around 6.9, Figure 7. Compared with the literature, the niobium oxide (Nb2O5) calcined at 873 K has 7.22 as a pHPZC value [31].The cobalt ferrite has the value of pHPZC 7.2 when calcined at 873 K [59].El-Khawaga et al. (2023) found a value of 6.9 for the pHPCZ, the same found in this work [60].

Scanning Electron Microscopy (SEM) and Energy Dispersive Spectroscopy (EDS)
The working principle of the SEM is related to an interaction between electrons and matter.The scanning electron microscope contains a source that generates an electron beam continuously fired in the sample during the test, scanning its surface.Thus, through a detector present in the equipment, it is possible to analyze the electron energies during the interaction between them and the surface, which is interpreted by the equipment and generates images, like in Figure 8, with a 10 µm scale.It is possible to observe clusters of nanomaterials, which are very typical of materials that have magnetic properties [13,23,26,[61][62][63].In addition, it is possible to observe the surface difference of the CFCANb sample, which was produced with commercial citric acid instead, with the tangerine extract.It has a planar surface, possibly because it formed larger clusters (in blocks).
Energy dispersive spectroscopy (EDS), which allows the detection and fraction of chemical elements on the surface, was performed for catalysts CFNb.The fraction of each component is summarized in weight: 33.6% is Oxygen, 27.3% is Iron, 24.8% is Niobium, and 14% is Cobalt.
It should be borne in mind that we expected to obtain the synthesis of nanomaterials of functionalized cobalt ferrite in niobium pentoxide of supposed molecular formula CoFe2O4@Nb2O5 and that the atomic weight of one mole of this component would be about 500.44 u (assuming Co = 58.93u, Fe = 55.845u, O = 16 u and Nb = 92.91 u).Recalling that the synthesis was performed with 50% w/w of CoFe2O4 and Nb2O5, the theoretical fraction by weight of each element would be O = 28.68%,Fe = 23.92%,Nb = 34.78%,and Co = 12.62%.These values are considered close to the values obtained.Therefore, it can be considered that CoFe2O4@Nb2O5 was the synthesized material.

Scanning Electron Microscopy (SEM) and Energy Dispersive Spectroscopy (EDS)
The working principle of the SEM is related to an interaction between electrons and matter.The scanning electron microscope contains a source that generates an electron beam continuously fired in the sample during the test, scanning its surface.Thus, through a detector present in the equipment, it is possible to analyze the electron energies during the interaction between them and the surface, which is interpreted by the equipment and generates images, like in Figure 8, with a 10 µm scale.It is possible to observe clusters of nanomaterials, which are very typical of materials that have magnetic properties [13,23,26,[61][62][63].In addition, it is possible to observe the surface difference of the CFCANb sample, which was produced with commercial citric acid instead, with the tangerine extract.It has a planar surface, possibly because it formed larger clusters (in blocks).
Energy dispersive spectroscopy (EDS), which allows the detection and fraction of chemical elements on the surface, was performed for catalysts CFNb.The fraction of each component is summarized in weight: 33.6% is Oxygen, 27.3% is Iron, 24.8% is Niobium, and 14% is Cobalt.
Figure 9 shows the X-ray diffractogram obtained for the samples CFNb.In this figure, the peaks related to ferrite were identified as cobalt and niobium pentoxide, represented by the acronyms CF and Nb, respectively.Comparing the patterns with the obtained results, it is observed that all samples have peaks in the diffraction angles for the mentioned components.Identifying the cobalt ferrite, the peaks appear around 2theta angles of 18.3°, 30.3°, 35.5°, 37.1°, 43.1°, 53.5°, and 62.6°, corresponding to the mentioned pattern.For the identification of niobium pentoxide, peaks for the 2theta angles of 22.6°, 28.4°, 36.4°,46.2°, 50.2°, 55.2°, and 71.1° were observed, which correspond to the patterns mentioned above.In this way, it is possible to identify that the obtained samples refer to the material of cobalt ferrite functionalized in niobium pentoxide.181), (002), (380), (182), and (382), respectively [52,69,70].
Figure 9 shows the X-ray diffractogram obtained for the samples CFNb.In this figure, the peaks related to ferrite were identified as cobalt and niobium pentoxide, represented by the acronyms CF and Nb, respectively.Comparing the patterns with the obtained results, it is observed that all samples have peaks in the diffraction angles for the mentioned components.Identifying the cobalt ferrite, the peaks appear around 2theta angles of 18.In this way, it is possible to identify that the obtained samples refer to the material of cobalt ferrite functionalized in niobium pentoxide.One way to better define the structure obtained is by using a characterization refinement to compare lattice parameters, which for each structure has its specificity.Another way is to manually calculate the lattice parameter () [71].The estimated lattice parameters' values were compared with those established by the cited standards (Table 2).It can be observed that the values of the lattice parameters for cobalt ferrite were very close to the values set as standard.As for niobium pentoxide, the values were more comparable to TT-Nb2O5 than T-Nb2O5, which concerns the pseudo-hexagonal phase, possibly the predominant phase in the material obtained.Further exploring the results of the XRD characterization, the average crystallite sizes (L) were calculated using Scherrer's Equation (2), obtaining the size of 24.10 nm for these magnetic nanoparticles.

Transmission Electron Microscopy
The TEM image shows the accumulation of the particles, which is a common characteristic of magnetic nanomaterials, Figure 10.The darker round represents the cobalt ferrite involved by the clearer amount (referent to niobium).The nanoparticle does not demonstrate a regular shape, but it is possible to conclude that the cobalt ferrite was synthesized in a niobium oxide structure.Using resources such as ImageJ, to interpret the size of the CFNb particles, the average particle size was calculated to be around 32.9 ± 3.5 nm.The particle average size value is close to that found by XRD.Furthermore, according to the literature, the average size of the cobalt ferrite synthesized by citrate at 873 K can be around 21 and 36 nm [72,73].One way to better define the structure obtained is by using a characterization refinement to compare lattice parameters, which for each structure has its specificity.Another way is to manually calculate the lattice parameter (a) [71].The estimated lattice parameters' values were compared with those established by the cited standards (Table 2).It can be observed that the values of the lattice parameters for cobalt ferrite were very close to the values set as standard.As for niobium pentoxide, the values were more comparable to TT-Nb 2 O 5 than T-Nb 2 O 5 , which concerns the pseudo-hexagonal phase, possibly the predominant phase in the material obtained.Further exploring the results of the XRD characterization, the average crystallite sizes (L) were calculated using Scherrer's Equation (2), obtaining the size of 24.10 nm for these magnetic nanoparticles.

Transmission Electron Microscopy
The TEM image shows the accumulation of the particles, which is a common characteristic of magnetic nanomaterials, Figure 10.The darker round represents the cobalt ferrite involved by the clearer amount (referent to niobium).The nanoparticle does not demonstrate a regular shape, but it is possible to conclude that the cobalt ferrite was synthesized in a niobium oxide structure.Using resources such as ImageJ, to interpret the size of the CFNb particles, the average particle size was calculated to be around 32.9 ± 3.5 nm.The particle average size value is close to that found by XRD.Furthermore, according to the literature, the average size of the cobalt ferrite synthesized by citrate at 873 K can be around 21 and 36 nm [72,73].

Photocatalysis
The tests were performed with a mercury vapor lamp of 250 W power and radiation measuring around 28 ± 2 mW•cm −2 .The preliminary test was conducted with 200 mL paracetamol solution 20 ppm, catalyst concentration 300 mg•L −1 , and pH 6.17 (without adjustment).This way, the paracetamol removal was just 2%.
Given the preliminary test result, we decided to perform the catalytic process with some additives to optimize the results.Thus, we chose to use 0.01 mol•L −1 formic acid (FA) [74] and 0.01 mol•L −1 NaOH for pH adjustment.The variation in catalyst concentration remained between 100 and 500 mg•L −1 because, as the catalyst is dark (tends to be black), adding too much catalyst would darken the solution, can impair the radiation effect, and decrease the efficiency of the photocatalytic process.The results were exciting but needed to be more satisfactory.This way, the conditions of planned runs (Table 1) were performed using hydrochloric acid (HA) to pH adjust.Both results were registered in Table 3 at two critical times for each.Figure 11

Photocatalysis
The tests were performed with a mercury vapor lamp of 250 W power and radiation measuring around 28 ± 2 mW•cm −2 .The preliminary test was conducted with 200 mL paracetamol solution 20 ppm, catalyst concentration 300 mg•L −1 , and pH 6.17 (without adjustment).This way, the paracetamol removal was just 2%.
Given the preliminary test result, we decided to perform the catalytic process with some additives to optimize the results.Thus, we chose to use 0.01 mol•L −1 formic acid (FA) [74] and 0.01 mol•L −1 NaOH for pH adjustment.The variation in catalyst concentration remained between 100 and 500 mg•L −1 because, as the catalyst is dark (tends to be black), adding too much catalyst would darken the solution, can impair the radiation effect, and decrease the efficiency of the photocatalytic process.The results were exciting but needed to be more satisfactory.This way, the conditions of planned runs (Table 1) were performed using hydrochloric acid (HA) to pH adjust.Both results were registered in Table 3 at two critical times for each.Figure 11     The results using formic acid to pH adjustment cannot be the better alternative, evidenced by the mechanism reaction study.The FA can be competitive with paracetamol using the hydroxyl.radical (HO•) to ozonization itself [75], Figure 12.However, to obtain more efficient degradation, the HA to pH adjustment is correct.
The results using formic acid to pH adjustment cannot be the better alternative, evidenced by the mechanism reaction study.The FA can be competitive with paracetamol using the hydroxyl.radical (HO•) to ozonization itself [75], Figure 12.However, to obtain more efficient degradation, the HA to pH adjustment is correct.According to the possible mechanisms proposed by Mukherjee et al., the degradation of the contaminant by photocatalysis would be caused by both the direct action of the photogenerated electron(e-)/hole (h+), which reduce/oxidize adsorbed molecules, and the attack of radicals generated during photocatalysis [31,76], Figure 13.Previous studies indicate that photocatalytic degradation strongly depends on HO• radicals.The PCT can be oxidized by the photocatalyst holes (hvb+) and by HO• radicals, with greater emphasis on the latter [31,77,78], according to the mechanism in the Figure 14.The emerging pollutant PCT has a lot of intermediates before complete degradation.According to the possible mechanisms proposed by Mukherjee et al., the degradation of the contaminant by photocatalysis would be caused by both the direct action of the photogenerated electron(e-)/hole (h+), which reduce/oxidize adsorbed molecules, and the attack of radicals generated during photocatalysis [31,76], Figure 13.
The results using formic acid to pH adjustment cannot be the better alternative, evidenced by the mechanism reaction study.The FA can be competitive with paracetamol using the hydroxyl.radical (HO•) to ozonization itself [75], Figure 12.However, to obtain more efficient degradation, the HA to pH adjustment is correct.According to the possible mechanisms proposed by Mukherjee et al., the degradation of the contaminant by photocatalysis would be caused by both the direct action of the photogenerated electron(e-)/hole (h+), which reduce/oxidize adsorbed molecules, and the attack of radicals generated during photocatalysis [31,76], Figure 13.Previous studies indicate that photocatalytic degradation strongly depends on HO• radicals.The PCT can be oxidized by the photocatalyst holes (hvb+) and by HO• radicals, with greater emphasis on the latter [31,77,78], according to the mechanism in the Figure 14.The emerging pollutant PCT has a lot of intermediates before complete degradation.Previous studies indicate that photocatalytic degradation strongly depends on HO• radicals.The PCT can be oxidized by the photocatalyst holes (h vb +) and by HO• radicals, with greater emphasis on the latter [31,77,78], according to the mechanism in the Figure 14.The emerging pollutant PCT has a lot of intermediates before complete degradation.
The results using formic acid to pH adjustment cannot be the better alternative, evidenced by the mechanism reaction study.The FA can be competitive with paracetamol using the hydroxyl.radical (HO•) to ozonization itself [75], Figure 12.However, to obtain more efficient degradation, the HA to pH adjustment is correct.According to the possible mechanisms proposed by Mukherjee et al., the degradation of the contaminant by photocatalysis would be caused by both the direct action of the photogenerated electron(e-)/hole (h+), which reduce/oxidize adsorbed molecules, and the attack of radicals generated during photocatalysis [31,76], Figure 13.Previous studies indicate that photocatalytic degradation strongly depends on HO• radicals.The PCT can be oxidized by the photocatalyst holes (hvb+) and by HO• radicals, with greater emphasis on the latter [31,77,78], according to the mechanism in the Figure 14.The emerging pollutant PCT has a lot of intermediates before complete degradation.Given the results obtained using HA for different catalyst concentrations, it was possible to observe, using the Pareto diagram, that the catalyst concentration also influences the PCT degradation, but only the pH effect is significant, Figure 15a.The contour plot confirms this response, showing that the lower the pH, the better the PCT degradation, Figure 15b.
Given the results obtained using HA for different catalyst concentrations, it was possible to observe, using the Pareto diagram, that the catalyst concentration also influences the PCT degradation, but only the pH effect is significant, Figure 15a.The contour plot confirms this showing that the lower the pH, the better the PCT degradation, Figure 15b.The comparative performance between CFNb, CFext, and Nb600, was performed like Run 2 conditions (pH 2.59, catalyst concentration 441.42 mg•L −1 ) due to this condition having the total PCT degradation lightly before that of others.After 60 min of reaction, the PCT degradation was 97.5%, 96.5%, and 90.2% to CFNb, CFext, and NB600, respectively, Figure 16.The performance of the CFNb is similar to the Nb600.Still, the advantage of using the CFNb is regarding recovery after the reaction, which can be reobtained for reuse several times or just separated from the supernatant for discarding.The comparative performance between CFNb, CFext, and Nb600, was performed like Run 2 conditions (pH 2.59, catalyst concentration 441.42 mg•L −1 ) due to this condition having the total PCT degradation lightly before that of others.After 60 min of reaction, the PCT degradation was 97.5%, 96.5%, and 90.2% to CFNb, CFext, and NB600, respectively, Figure 16.The performance of the CFNb is similar to the Nb600.Still, the advantage of using the CFNb is regarding recovery after the reaction, which can be reobtained for reuse several times or just separated from the supernatant for discarding.
Given the results obtained using HA for different catalyst concentrations, it was possible to observe, using the Pareto diagram, that the catalyst concentration also influences the PCT degradation, but only the pH effect is significant, Figure 15a.The contour plot confirms this response, showing that the lower the pH, the better the PCT degradation, Figure 15b.The comparative performance between CFNb, CFext, and Nb600, was performed like Run 2 conditions (pH 2.59, catalyst concentration 441.42 mg•L −1 ) due to this condition having the total PCT degradation lightly before that of others.After 60 min of reaction, the PCT degradation was 97.5%, 96.5%, and 90.2% to CFNb, CFext, and NB600, respectively, Figure 16.The performance of the CFNb is similar to the Nb600.Still, the advantage of using the CFNb is regarding recovery after the reaction, which can be reobtained for reuse several times or just separated from the supernatant for discarding.After 60 min of reaction, the PCT degradation was 97.5%, 96.5%, and 90.2% to CFNb, CFext, and NB600, respectively (Figure 17).In this way, the reuse performance of this catalyst is expressive and efficient.
After 60 min of reaction, the PCT degradation was 97.5%, 96.5%, and 90.2% to CFNb, CFext, and NB600, respectively (Figure 17).In this way, the reuse performance of this catalyst is expressive and efficient.

Conclusions
The new methodology via green synthesis can be used to synthesize magnetic nanoparticles easily and quickly.The methodology developed, and the combination of elements considered was worthy of a patent attempt for the method and product obtained.Among the various advantages of synthesis, the reuse of biomass residues, the low cost of obtaining the material, and the added value to a richly available component in Brazil (niobium) stand out.The catalytic nanomaterials were active in the studied photocatalytic reaction of acetaminophen degradation.Several experiments allowed the finding of the optimal operating conditions: using hydrochloric acid to adjust the pH, catalyst concentration between 100 mg•L −1 and 500 mg•L −1 , and mercury vapor lamp power of 250 W.Under these conditions, the proposed catalysts can achieve the objective of finding photocatalysis conditions that would totally degrade the emerging pollutant paracetamol.

Conclusions
The new methodology via green synthesis can be used to synthesize magnetic nanoparticles easily and quickly.The methodology developed, and the combination of elements considered was worthy of a patent attempt for the method and product obtained.Among the various advantages of synthesis, the reuse of biomass residues, the low cost of obtaining the material, and the added value to a richly available component in Brazil (niobium) stand out.The catalytic nanomaterials were active in the studied photocatalytic reaction of acetaminophen degradation.Several experiments allowed the finding of the optimal operating conditions: using hydrochloric acid to adjust the pH, catalyst concentration between 100 mg•L −1 and 500 mg•L −1 , and mercury vapor lamp power of 250 W.Under these conditions, the proposed catalysts can achieve the objective of finding photocatalysis conditions that would totally degrade the emerging pollutant paracetamol.

Figure 1 .
Figure 1.Word cloud with article keywords.Figure 1. Word cloud with article keywords.

Figure 1 .
Figure 1.Word cloud with article keywords.Figure 1. Word cloud with article keywords.

Figure 2 .
Figure 2. Bibliometric analysis: (a) published year versus relevant publications and (b) relevant publications versus research country.

Figure 2 .
Figure 2. Bibliometric analysis: (a) published year versus relevant publications and (b) relevant publications versus research country.

Figure 3 .
Figure 3. Route to the green synthesis method of functionalized cobalt ferrite in niobium pentoxide: (A) the tangerine peel after sun exposition; (B) the tangerine peel after drying and crushing; (C) the extraction with tangerine peel powder in distilled water; (D) the extract to storage and done to use; (E) mixture of the Co and Fe salts and tangerine peel extract; (F) Addition of the niobium pentoxide in the solution; and (G) Co2Fe3O4@Nb2O5 nanoparticles synthesized.

Figure 3 .
Figure 3. Route to the green synthesis method of functionalized cobalt ferrite in niobium pentoxide: (A) the tangerine peel after sun exposition; (B) the tangerine peel after drying and crushing; (C) the extraction with tangerine peel powder in distilled water; (D) the extract to storage and done to use; (E) mixture of the Co and Fe salts and tangerine peel extract; (F) Addition of the niobium pentoxide in the solution; and (G) Co 2 Fe 3 O 4 @Nb 2 O 5 nanoparticles synthesized.

Figure 4 .
Figure 4. Representation of the photocatalytic chamber and other elements for the photocatalytic reaction created by the research group: (A) photocatalytic chamber; (B) jacketed reactor; (C1) water entering the reactor; (C2) water flow from the reactor; (D) Magnetic stirring; (E) magnetic stirring plate; (F) pump for airflow; and (G) mercury lamp 250 Watts.

Figure 4 .
Figure 4. Representation of the photocatalytic chamber and other elements for the photocatalytic reaction created by the research group: (A) photocatalytic chamber; (B) jacketed reactor; (C1) water entering the reactor; (C2) water flow from the reactor; (D) Magnetic stirring; (E) magnetic stirring plate; (F) pump for airflow; and (G) mercury lamp 250 Watts.

Figure 5 .
Figure 5. CFNb nanocatalyst: (a) catalyst recovered for storage after completing step 2 (G) and (b) demonstrating the magnetic properties, all material, including the Falcon tube, is supported by a magnet.

Figure 6 .
Figure 6.Magnetic separation of the catalyst with the approximation of the magnet.

Figure 5 .
Figure 5. CFNb nanocatalyst: (a) catalyst recovered for storage after completing step 2 (G) and (b) demonstrating the magnetic properties, all material, including the Falcon tube, is supported by a magnet.

Figure 5 .
Figure 5. CFNb nanocatalyst: (a) catalyst recovered for storage after completing step 2 (G) and (b) demonstrating the magnetic properties, all material, including the Falcon tube, is supported by a magnet.

Figure 6 .
Figure 6.Magnetic separation of the catalyst with the approximation of the magnet.Figure 6. Magnetic separation of the catalyst with the approximation of the magnet.

Figure 6 .
Figure 6.Magnetic separation of the catalyst with the approximation of the magnet.Figure 6. Magnetic separation of the catalyst with the approximation of the magnet.

Figure 7 .
Figure 7. pHPZC values calculated by the average of the final pH values which tended to a constant value, the green dotted line in the graph represents the pHpzc value in axis y.

Figure 7 .
Figure 7. pH PZC values calculated by the average of the final pH values which tended to a constant value, the green dotted line in the graph represents the pHpzc value in axis y.
CoFe 2 O 4 @Nb 2 O 5 and that the atomic weight of one mole of this component would be about 500.44 u (assuming Co = 58.93u, Fe = 55.845u, O = 16 u and Nb = 92.91 u).Recalling that the synthesis was performed with 50% w/w of CoFe 2 O 4 and Nb 2 O 5 , the theoretical fraction by weight of each element would be O = 28.68%,Fe = 23.92%,Nb = 34.78%,and Co = 12.62%.These values are considered close to the values obtained.Therefore, it can be considered that CoFe 2 O 4 @Nb 2 O 5 was the synthesized material.
graphs (a) and (b) registered all the tests executed and the PCT removal over time.
graphs (a) and (b) registered all the tests executed and the PCT removal over time.

Figure 11 .
Figure 11.Preliminary photocatalytic tests for PCT removal with pH adjustment with (a) formic acid (FA) and (b) hydrochloric acid (HA).Figure 11.Preliminary photocatalytic tests for PCT removal with pH adjustment with (a) formic acid (FA) and (b) hydrochloric acid (HA).

Figure 11 .
Figure 11.Preliminary photocatalytic tests for PCT removal with pH adjustment with (a) formic acid (FA) and (b) hydrochloric acid (HA).Figure 11.Preliminary photocatalytic tests for PCT removal with pH adjustment with (a) formic acid (FA) and (b) hydrochloric acid (HA).

Figure 15 .
Figure 15.According to DOE proposed (a) a Pareto chart for the degradation of PCT and (b) a Contour plot for the degradation of PCT in 60 min of photocatalysis.

Figure 16 .
Figure 16.Comparison of the performance of CFNb, CFext, and Nb600 catalysts in 60 min of paracetamol degradation.

Figure 15 .
Figure 15.According to DOE proposed (a) a Pareto chart for the degradation of PCT and (b) a Contour plot for the degradation of PCT in 60 min of photocatalysis.

Figure 15 .
Figure 15.According to DOE proposed (a) a Pareto chart for the degradation of PCT and (b) a Contour plot for the degradation of PCT in 60 min of photocatalysis.

Figure 16 .
Figure 16.Comparison of the performance of CFNb, CFext, and Nb600 catalysts in 60 min of paracetamol degradation.

Figure 16 .
Figure 16.Comparison of the performance of CFNb, CFext, and Nb600 catalysts in 60 min of paracetamol degradation.

17 .
Figure 17.Comparison of the performance of CFNb in the first reaction and the next two reuses.

Figure 17 .
Figure 17.Comparison of the performance of CFNb in the first reaction and the next two reuses.

Table 1 .
Experimental design (codified values in brackets) based on two-factor CCD.

Table 1 .
Experimental design (codified values in brackets) based on two-factor CCD.

Table 2 .
Experimental design (codified values in brackets) based on two-factor CCD.

Table 2 .
Experimental design (codified values in brackets) based on two-factor CCD.

Table 3 .
Results of PCT removal with pH adjustment.

Table 3 .
Results of PCT removal with pH adjustment.