Plasma-Derived Graphene-Based Materials for Water Purification and Energy Storage

Several crucial problems, such as rapid population growth and extended demands for food, water and fuels, could lead to a severe lack of clean water and an energy crisis in the coming decade. Therefore, low-cost and highly-efficient technologies related to filtration of alternative water supplies (e.g., purification of wastewater and water-rich liquids) and advanced energy storage (e.g., supercapacitors) could play a crucial role to overcome such challenges. A promising class of solid materials for these purposes is exfoliated graphene, and more specifically, its nanoporous forms that exhibit large specific surface areas and pore volumes. In the current work, two plasma-exfoliated graphene-based materials with distinctive morphological and porosity features, including non-porous and low-specific surface area platelets versus nanoporous and high-specific surface area flakes, were tested as filters for water purification purposes (i.e., decolourization and deacidification) and as electrodes for supercapacitors (i.e., ion electrosorption). The findings of this study suggest that a nanoporous and large specific surface area graphene-based material promotes the water purification behaviour by removing contaminants from water-based solutions as well as the energy storage performance by confining ions of aqueous electrolytes.


Introduction
Exfoliated graphene, a two-dimensional single-layer of sp 2 -bonded carbon atoms distributed in hexagonal cells, has been the subject of considerable research since the beginning of the 21st century due to its unique electronic, thermal, optical and mechanical properties [1,2].Few-layer graphene (FLG), composed of a limited number of stacked graphene layers, can be also produced in a porous form [3], thus providing high specific surface areas and pore volumes combined with tunable pore sizes [4].Apart from these surface-related features, porous graphene-based materials possess other significant advantages such as low densities, reasonably good thermochemical stability, excellent recyclability, environmental friendliness and non-toxicity [5,6].Micro-mechanical exfoliation of pyrolytic graphite [7], chemical vapor deposition via cracking of carbon sources [8], chemical C 2019, 5, 16 2 of 12 reduction of graphite oxide [9] as well as electrochemical exfoliation of graphite [10] are the main production routes for graphene-based materials.However, the plasma-induced exfoliation of natural graphite can be considered an as efficient, not solution-based, catalyst-free, cost-effective and environmental-benign approach to produce FLG materials of high-purity in bulk quantities.Using this method, the generated plasma modifies the graphitic surface either by physical ablation or chemical functionalization, thus allowing the production of graphene-based materials with different porosities (ranging from non-porous to highly nanoporous) and surface chemistries (e.g., functional groups, dopants, etc.) [11,12].
The production of microporous (i.e., pore widths below 2 nm) FLG materials for selective gas, liquid and ion adsorption, and in particular for efficient water purification and energy storage, has been the topic of on-going investigations [13][14][15][16].In the next decade, the rapid increase of the global population, fast-growing demands for food and water, extended droughts and scarcity of freshwater sources (i.e., they make up only 0.5% of world's overall water resources) will probably lead to a severe lack of clean water [12,14,15].In addition, the intensively-growing demands for energy in combination with the finite amount of available fossil fuels resources (oil, natural gas, coal, etc.) could deteriorate even more the currently negative energy landscape.Therefore, low-cost and highly-efficient technologies for filtration of alternative water supplies (purification of wastewater and water-rich liquids, desalination of sea water, etc.) and advanced energy storage (supercapacitors, hybrid batteries, etc.) might provide potential solutions for future water and energy crises [17][18][19][20].Apart from the classical purification techniques (e.g., sand filtration, sedimentation, etc.), there are some other methods that could yield potential for high-performance filtering.Among those, distillation and reverse osmosis are particularly of importance [21][22][23].Carbon nanotube membranes were studied for water permeation and flow via reverse osmosis towards wastewater treatment and sea water desalination [24][25][26].Granular activated carbon, which often contains Si due to its excellent antibacterial properties [6], is also used as effective adsorbent material in commercial water filters [27].In contrast to standard routes of storing electrical energy in batteries, electrical double-layer capacitors, also called supercapacitors, use an operation principle which is based on a simple potential-induced electrosorption of ions from ionic liquids as well as aqueous or organic electrolytes onto the surface of charged electrodes (usually carbons) [28].Furthermore, when aqueous electrolytes are used the systems are non-toxic and environmental friendly [18].
In this work, two plasma-derived graphene-based powders with different porosity characteristics (i.e., nanoporous and large specific surface area flakes versus non-porous and low specific surface area platelets) were examined for two different applications.The first one involved water purification (i.e., decolourization and deacidification) based on simple and reproducible filtering experiments using Coca-Cola ® (Atlanta, GA, USA) as a coloured water-rich liquid and graphene powders as filters.Coca-Cola ® is one of the most popular soft beverages consumed worldwide with more than 1.9 billion servings per day [29].This product includes various ingredients with the basic ones being carbonated water (~90%), sugar (a mixture of glucose and fructose), caramel colour, phosphoric acid, caffeine and natural flavours [30].The characteristic "brownish" colour is specifically attributed to the caramel colour E150d, which is an acid-proof sulphite ammonia-based caramel [31].Dispersion and wettability tests were also carried out to evaluate the interaction of these materials with distilled water and other solvents (e.g., ethanol) along with pH measurements using pH test strips in a basic effort to evaluate the acidity of the filtered water.The second application was related to electrochemical energy storage (i.e., ion electrosorption) by assembling electrical double-layer capacitor devices consisting of an aqueous electrolyte and graphene-based electrodes.The energy storage performance was evaluated by cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS) measurements.The morphological, structural and porosity properties of the selected powders were characterized by scanning electron microscopy (SEM), X-ray diffraction (XRD), small-angle X-ray scattering (SAXS) and nitrogen (N 2 ) gas adsorption/desorption measurements at 77 K, respectively.

Materials and Experimental Methods
The two graphene powders investigated in this study were provided by Perpetuus Carbon Technologies (Ammanford, United Kingdom).These included: (a) graphene nanoplatelets (GNP) with <5 µm diameter, <50 nm thickness, 2 wt.% -COOH content and 96% purity and (b) few-layer graphene flakes (FLG) with stacks of 3-6 layers, <2 µm diameter, <3 nm thickness, 2 wt.% -COOH content and 96% purity.Both materials were produced by exposing natural flake graphite in argon plasma for two different time periods using a custom-made multi-electrode dielectric barrier discharge plasma reactor, as described elsewhere [4,32].Figure 1 (upper left) allows to visualize the difference in the volume occupied from 2 g of each graphene powder.The packing density in a fixed-volume container (2 mL) was estimated to be ~0.18 and ~0.22 g/cm 3 for GNP and FLG, respectively.
with an approximately 8-times oversized counter electrode (CE) as a quasi-reference [38], consisting of commercially available activated carbon (YP-80F, Kuraray Chemical Co., Osaka, Japan) electrodes prepared as described above with a reduced amount of PTFE binder (5 wt.%).The cell was built as a multi-layered assembly with two Pt current collectors, a CE, a working electrode (WE) and a glass fiber separator (Whatman GF/A) in between the electrodes.The WE had a diameter of 6 mm and a thickness of 300 ± 20 μm and an aqueous 1 M caesium chloride (CsCl) solution was used as the electrolyte.Cyclic voltammetry (CV) measurements were performed in the range of ± 0.6 V against the quasi reference.CV curves were recorded for various scan rates ranging from 0.5 up to 100 mV/s.The specific capacitance (C) was calculated according to: where I is the current, m is the mass of the WE and ∆ is the voltage window.EIS studies were performed at 0 V with a root-mean-square (RMS) value of ±5 mV over a frequency range from 10 mHz to 100 kHz with 10 points per decade.Galvanostatic charge-discharge (GCD) measurements were performed in the potential range between −0.6 and +0.6 V with different specific currents ranging from 0.25 up to 1 A/g.

Morphological, Structural and Porosity Studies
SEM images of the GNP and FLG powders are shown in Figure 2a,b.The platelets of the GNP material (Figure 2a) are agglomerated and exhibit a smooth surface.In contrast, in Figure 2b the surface of the FLG material looks much rougher and defective due to the extended plasma ablation procedure.As supported by the N2 adsorption data presented below, the highly-defective structure of the FLG sample provides a much larger specific surface area as compared to the GNP sample.
X-ray diffractograms of the GNP and FLG powders are presented in Figure 2c,d.As shown in Figure 2c, the GNP powder appears to be highly-crystalline and exhibits a similar structure to graphite (JCPDS card no 75-1621).The XRD peaks infer that the GNP consists mainly of graphitic The surface morphology was studied by using a Quanta 200 scanning electron microscope (FEI, Hillsboro, OR, USA) at acceleration voltages of 25-30 kV and a working distance of 10 mm.XRD measurements were performed using a D8 Advance diffractometer (Bruker-AXS, Karlsruhe, Germany) equipped with Cu K α radiation (λ ~1.54 Å) at 40 kV voltage and 40 mA current.The X-ray diffractograms were recorded using a continuous scan speed mode between the diffraction angles (2θ) of 10 • and 60 • , a 0.01 • step width and a 0.5 • /min scan speed.SAXS measurements were performed with a N8 Horizon SAXS (Bruker-AXS, Karlsruhe, Germany) facility operated with an X-ray micro-source at 50 kV voltage and 1 mA current delivering Cu Kα radiation.The SAXS curves were recorded with a Vantec 500 detector and azimuthally averaged, using the software Fit2D [33], leading to the scattered intensity as a function of the scattering vector (Q = 4πsinθ/λ).The resulting scattering curves were normalized to the corresponding transmission value measured with a glassy carbon standard [34].N 2 gas adsorption/desorption isotherms were recorded at 77 K using a Autosorb MP-1 gas sorption analyzer (Quantachrome Instruments, Boynton Beach, FL, USA), a liquid N 2 bath and ultra-pure (99.999%)N 2 gas.Prior to the measurements, samples of ~50 mg were degassed under vacuum (10 −6 mbar) at 250 • C for 12 h to remove any physisorbed species/contaminants from the surface of the materials.Brunauer-Emmet-Teller (BET) areas were calculated by following the relevant consistency criteria [35].The pore size distribution analysis was carried out by using the equilibrium the Quenched Solid Density Functional Theory (QSDFT) kernel for slit-shape pores [36].
Powder dispersion tests were carried out in distilled water and ethanol by mixing 50 mg of powder with 100 mL of solvent in each case.The solutions were placed in an ultrasonic bath for 10 min to achieve a more uniform mixture.Digital photographs were taken at regular intervals for up to 44 days.Ethanol was used for comparison as a common liquid for carbon powder dispersion experiments.Wettability tests on graphene electrodes/films were performed using a DSA100 contact-angle device (Krüss, Hamburg, Germany) and distilled water.The electrodes were prepared by mixing the graphene powders with 10 wt.% polytetrafluoroethylene (PTFE; Sigma-Aldrich, St. Louis, Missouri, USA) binder in distilled water.The received pastes were rolled in a rolling press (MTI Corporation, Richmond, CA, USA) until they reached a thickness of 300 ± 20 µm and then dried for 24 h at 120 • C and 5 mbar in a vacuum oven.For the wettability tests, a water droplet of 2 µL was placed onto the surface of the as-prepared graphene electrodes.The contact angles were recorded once the droplet was in contact with the surface by taking a digital picture.Additionally, the time required for full sorption of the droplets within the films was measured and respective pictures were taken every 2 min.
The purification experiments were performed by placing 1 g of graphene powder in a commercial coffee filter (Melitta Filtertüten Original 1 × 2) mounted on a glass flask.An empty coffee filter with no powder was used as a reference.This simple experimental setup is illustrated in Figure 1.Coca-Cola ® was gradually poured on top of the filter, passed through the powder and the product was collected after a few minutes.Then, the filtered water was re-poured once again onto the filter and passed through the powder for a second filtering cycle.Digital pictures of the products were taken after both cycles.Commercial pH paper strips were dipped in the filtered liquids to observe changes in their pH value.
Electrochemical characterization of the electrodes was performed with a Reference 600 potentiostat (Gamry, Warminster Township, PA, USA) using a custom-built cell with a polyether ether ketone (PEEK) housing and Ti pistons connected to two separate electrical contacts.The pistons are spring loaded to apply a well-defined constant pressure on the actual supercapacitor cell built between these pistons [37].All measurements were performed with an asymmetric half-cell setup with an approximately 8-times oversized counter electrode (CE) as a quasi-reference [38], consisting of commercially available activated carbon (YP-80F, Kuraray Chemical Co., Osaka, Japan) electrodes prepared as described above with a reduced amount of PTFE binder (5 wt.%).The cell was built as a multi-layered assembly with two Pt current collectors, a CE, a working electrode (WE) and a glass fiber separator (Whatman GF/A) in between the electrodes.The WE had a diameter of 6 mm and a thickness of 300 ± 20 µm and an aqueous 1 M caesium chloride (CsCl) solution was used as the electrolyte.Cyclic voltammetry (CV) measurements were performed in the range of ± 0.6 V against the quasi reference.CV curves were recorded for various scan rates ranging from 0.5 up to 100 mV/s.The specific capacitance (C) was calculated according to: where I is the current, m is the mass of the WE and ∆U is the voltage window.EIS studies were performed at 0 V with a root-mean-square (RMS) value of ±5 mV over a frequency range from 10 mHz to 100 kHz with 10 points per decade.Galvanostatic charge-discharge (GCD) measurements were performed in the potential range between −0.6 and +0.6 V with different specific currents ranging from 0.25 up to 1 A/g.

Morphological, Structural and Porosity Studies
SEM images of the GNP and FLG powders are shown in Figure 2a,b.The platelets of the GNP material (Figure 2a) are agglomerated and exhibit a smooth surface.In contrast, in Figure 2b the surface of the FLG material looks much rougher and defective due to the extended plasma ablation procedure.As supported by the N 2 adsorption data presented below, the highly-defective structure of the FLG sample provides a much larger specific surface area as compared to the GNP sample.

Dispersion and Wettability Studies
The dispersions of GNP and FLG powders in distilled water and ethanol are exemplified in Figure 3. On the one hand, GNP was fully dispersible in ethanol but formed some sort of gel with distilled water (i.e., a very thick viscous liquid) right after preparing the dispersions, as indicated in X-ray diffractograms of the GNP and FLG powders are presented in Figure 2c,d.As shown in Figure 2c, the GNP powder appears to be highly-crystalline and exhibits a similar structure to C 2019, 5, 16 6 of 12 graphite (JCPDS card no 75-1621).The XRD peaks infer that the GNP consists mainly of graphitic carbon without significant presence of impurities.Figure 2d indicates that the FLG powder is much less crystalline and much more defective than the GNP, which is in good agreement with the SEM observations.Except for the main stacking peak at about 26 • referring to the (002) graphitic reflection and the less intense peaks at about 43 • and 54 • representing the (100)/(101) and (004) crystal planes, respectively, no evidence of other species was detected.
The SAXS curve of the GNP powder (Figure 2e) shows the typical decay intensity (I ∝ Q −4 ) for a two-phase system with a smooth surface described by Porod's law [39].In contrast, the FLG sample shows a clear deviation from this ideal system with the intensity decaying rather with I ∝ Q −3 .This can be either explained by a fractal pore structure [40] or alternatively by electron density fluctuation due to imperfect stacking and defects in the graphene sheets [41,42].Such a result is expected due to the controlled "destruction" of the carbon surface via plasma ablation and is consistent with the SEM observations.Even though, no quantitative analysis of the SAXS data was performed [43], they support the N 2 sorption analysis of very small pores and a much higher specific surface area of the FLG sample as compared to GNP.
The N 2 adsorption/desorption isotherms recorded at 77 K for the degassed FLG and GNP powders are shown in Figure 2f.The much higher N 2 uptake of the FLG at low relative pressures (P/P 0 < 0.01) is attributed to its microporosity (i.e., pore widths < 2 nm) [4].In addition, the formation of a small hysteresis loop between the adsorption and desorption curves for the FLG is related to capillary condensation of N 2 gas within mesopores (i.e., pore sizes of 2-50 nm) [44].The adsorbed N 2 amounts increase abruptly for both powders at higher relative pressures (P/P 0 > 0.95) without reaching a clear "plateau" due to adsorption onto external surfaces and/or condensation in macropores (i.e., pore widths > 50 nm) [44,45].Therefore, the N 2 adsorption behaviour indicates that the GNP is mainly non-porous (macropores may exist though), while the FLG combines microporous, mesoporous and macroporous characteristics.This is supported by the QSDFT-based pore size distribution analysis (see inset of Figure 2f), which indicates the existence of sub-nanometer pores (showing a peak at around 0.7 nm).The BET area of the degassed FLG powder is almost 40 times higher than that of GNP (i.e., ~776 m 2 /g vs. ~20 m 2 /g).The linear multi-point BET plots of the degassed GNP and FLG powders are presented in Figure 2g,h, respectively.

Dispersion and Wettability Studies
The dispersions of GNP and FLG powders in distilled water and ethanol are exemplified in Figure 3. On the one hand, GNP was fully dispersible in ethanol but formed some sort of gel with distilled water (i.e., a very thick viscous liquid) right after preparing the dispersions, as indicated in Figure 3a.After 48 h (Figure 3b), the dispersion segregated completely in ethanol by forming a thin layer both on the top and bottom of the solution, while it segregated partially in distilled water with some powder still appearing on the top of the solution.The same behaviour was observed even after 44 days as seen in Figure 3c.In contrast, FLG is fully dispersible both in distilled water and ethanol, as shown in Figure 3d.After 48 h (Figure 3e) and even after 44 days (Figure 3f), there is no indication of separation between the FLG powder and the solvent [46].The findings obtained by water contact angle measurements for the as-prepared GNP and FLG thin films are summarized in Figure 3g.The GNP electrode had a higher contact angle with the water droplet as compared to the FLG electrode (i.e., ~126 • for GNP and ~87 • for FLG).Contact angles larger than 90 • indicate a hydrophobic behaviour while those smaller than 90 • are characteristic for a hydrophilic behaviour [47].The reason for the (slight) hydrophilicity of the FLG sample might be related to the defect-induced highly-porous surface of the FLG sample in contrast to the non-porous GNP surface.Furthermore, the time it took the samples to fully soak the water droplet was shorter for FLG than for GNP (i.e., ~16.5 min for GNP and 12.5 min for FLG).
(i.e., ~126° for GNP and ~87° for FLG).Contact angles larger than 90° indicate a hydrophobic behaviour while those smaller than 90° are characteristic for a hydrophilic behaviour [47].The reason for the (slight) hydrophilicity of the FLG sample might be related to the defect-induced highly-porous surface of the FLG sample in contrast to the non-porous GNP surface.Furthermore, the time it took the samples to fully soak the water droplet was shorter for FLG than for GNP (i.e., ~16.5 min for GNP and 12.5 min for FLG).

Filtration Studies
The purification behaviour of the GNP and FLG powders towards coloured water-based liquids such as a Coca-Cola ® is demonstrated in Figure 4. Coca-Cola ® filtered only with a coffee filter is included as a reference in Figure 4a.The GNP powder showed no effective filtering behaviour and even contaminated the final product (i.e., black-coloured GNP-Coca-Cola ® mixture in Figure 4b).The FLG powder, however, made the filtered Coca-Cola ® much more transparent, although some very small powder particles were able to pass through the filter (see Figure 4b).A second filtering cycle was repeated using the same FLG-based filters (from the first cycle) to further purify the water-based liquid.As shown in Figure 4c, the second-time filtered Coca-Cola ® product got even more transparent and did not show any observable signs of powder contamination.Therefore, the FLG-based filter was able to decolourize the Coca-Cola ® after two cycles of filtration based on visual inspection.
The outcome of pH measurements using commercial pH paper strips is presented in Figure 4d.The pH value lies between 2 and 3 by filtering the Coca-Cola ® with only a coffee filter; i.e., without

Filtration Studies
The purification behaviour of the GNP and FLG powders towards coloured water-based liquids such as a Coca-Cola ® is demonstrated in Figure 4. Coca-Cola ® filtered only with a coffee filter is included as a reference in Figure 4a.The GNP powder showed no effective filtering behaviour and even contaminated the final product (i.e., black-coloured GNP-Coca-Cola ® mixture in Figure 4b).The FLG powder, however, made the filtered Coca-Cola ® much more transparent, although some very small powder particles were able to pass through the filter (see Figure 4b).A second filtering cycle was repeated using the same FLG-based filters (from the first cycle) to further purify the water-based liquid.As shown in Figure 4c, the second-time filtered Coca-Cola ® product got even more transparent and did not show any observable signs of powder contamination.Therefore, the FLG-based filter was able to decolourize the Coca-Cola ® after two cycles of filtration based on visual inspection.
The outcome of pH measurements using commercial pH paper strips is presented in Figure 4d.The pH value lies between 2 and 3 by filtering the Coca-Cola ® with only a coffee filter; i.e., without FLG powder.It should be noted that Coca-Cola ® has a pH value of ~2.5 according to the literature [48], which is attributed to the presence of phosphoric acid.However, when the FLG powder was used as a filtering material, the pH value moved closer to the neutral side of the pH scale (i.e., pH value 5-6 after two cycles vs. pH ~7 for pure water).Even though these results are only a qualitative indication based on a visual analysis of these strips, there is strong evidence that the FLG powder partially neutralizes the acidic behaviour of the Coca-Cola ® .
FLG powder.It should be noted that Coca-Cola ® has a pH value of ~2.5 according to the literature [48], which is attributed to the presence of phosphoric acid.However, when the FLG powder was used as a filtering material, the pH value moved closer to the neutral side of the pH scale (i.e., pH value 5-6 after two cycles vs. pH ~7 for pure water).Even though these results are only a qualitative indication based on a visual analysis of these strips, there is strong evidence that the FLG powder partially neutralizes the acidic behaviour of the Coca-Cola ® .

Electrochemical Studies
Besides filtration, the same graphene-based materials were also evaluated with respect to energy storage purposes.The electrochemical performance data of the GNP-and FLG-based supercapacitor electrodes using 1 M CsCl aqueous electrolyte are summarized in Figure 5.The CV curves for different scanning rates (i.e., 1, 10 and 100 mV/s) appear to be almost symmetric (see Figure 5a).Specifically, for the FLG sample, the rectangular shape of the CV curves and the gravimetric capacitance values indicate a proper capacitive behaviour and its suitability as an electrode material for supercapacitor devices.The rate handling tests between 0.5 and 100 mV/s are presented in Figure 5b.A maximum gravimetric capacitance of ~57 F/g and ~5 F/g was recorded for FLG and GNP electrodes, respectively, for the scanning rate of 0.5 mV/s.The capacitance values drop by 42 and 31% for FLG and GNP, respectively, upon increasing the scanning rate up to 100 mV/s, as seen in the inset of Figure 5b.The ion diffusion characteristics in the porous FLG can be different from the non-porous GNP, thus leading to a more significantly reduced relative capacitance for FLG at higher scan rates.In any case, the FLG outperforms the GNP in terms of capacitance (ratio ~11.5:1 at 0.5 mV) due to its nanoporous structure and consequently much larger available specific surface area (i.e., ~776 vs. ~20 m 2 /g, respectively).Recent experimental and computational studies suggested that charged ions can be stored more effectively in sub-nanometer pore widths with the highest degree of confinement [49,50].With respect to their electrochemical cyclic stability, both samples showed no capacitance loss after 400 charge/discharge cycles.The Nyquist plots, presented in Figure 5c, highlight the typical electrical double-layer behaviour and an almost ideal capacitive behaviour for the FLG.The low

Electrochemical Studies
Besides filtration, the same graphene-based materials were also evaluated with respect to energy storage purposes.The electrochemical performance data of the GNP-and FLG-based supercapacitor electrodes using 1 M CsCl aqueous electrolyte are summarized in Figure 5.The CV curves for different scanning rates (i.e., 1, 10 and 100 mV/s) appear to be almost symmetric (see Figure 5a).Specifically, for the FLG sample, the rectangular shape of the CV curves and the gravimetric capacitance values indicate a proper capacitive behaviour and its suitability as an electrode material for supercapacitor devices.The rate handling tests between 0.5 and 100 mV/s are presented in Figure 5b.A maximum gravimetric capacitance of ~57 F/g and ~5 F/g was recorded for FLG and GNP electrodes, respectively, for the scanning rate of 0.5 mV/s.The capacitance values drop by 42 and 31% for FLG and GNP, respectively, upon increasing the scanning rate up to 100 mV/s, as seen in the inset of Figure 5b.The ion diffusion characteristics in the porous FLG can be different from the non-porous GNP, thus leading to a more significantly reduced relative capacitance for FLG at higher scan rates.In any case, the FLG outperforms the GNP in terms of capacitance (ratio ~11.5:1 at 0.5 mV) due to its nanoporous structure and consequently much larger available specific surface area (i.e., ~776 vs. ~20 m 2 /g, respectively).Recent experimental and computational studies suggested that charged ions can be stored more effectively in sub-nanometer pore widths with the highest degree of confinement [49,50].With respect to their electrochemical cyclic stability, both samples showed no capacitance loss after 400 charge/discharge cycles.The Nyquist plots, presented in Figure 5c, highlight the typical electrical double-layer behaviour and an almost ideal capacitive behaviour for the FLG.The low equivalent series resistance for both samples (i.e., 0.10 and 0.13 Ω•cm 2 for GNP and FLG, respectively), as shown in the inset of Figure 5c, suggests a good conductivity and low internal resistance for the half-cell setup [51].The GCD curves, shown in Figure 5d, indicate a nearly linear behaviour which is characteristic of electrical double layer capacitance.equivalent series resistance for both samples (i.e., 0.10 and 0.13 Ω•cm 2 for GNP and FLG, respectively), as shown in the inset of Figure 5c, suggests a good conductivity and low internal resistance for the half-cell setup [51].The GCD curves, shown in Figure 5d, indicate a nearly linear behaviour which is characteristic of electrical double layer capacitance.

Conclusions
In this work, two graphene-based materials which differ in terms of morphology and pore structure have been examined for their water purification and electrochemical energy storage performance.The tested samples included smooth, highly-crystalline, non-porous and low-specific surface area (~20 m 2 /g) graphene nanoplatelets (GNP) and defective, less-crystalline, nanoporous and high-specific surface area (~776 m 2 /g) few-layer graphene flakes (FLG).Both materials were derived from plasma-induced exfoliation of natural flake graphite.The GNP powder showed partial dispersibility in distilled water and ethanol, while the FLG powder was fully dispersible in both solvents even after several weeks.The GNP sample exhibited a higher contact angle with distilled water, however, the FLG sample showed faster kinetics towards water adsorption.In terms of potential applications, the FLG powder has proven to be an efficient filtering material for both decolourization and deacidification of water-rich substances such as Coca-Cola ® .Moreover, the FLG was used as a proper electrode material for ion electrosorption in a model supercapacitor device.In contrast, the GNP-based filters and electrodes failed in both applications.Therefore, the increased specific surface area and the nano-sized pores of the FLG material seem to be the inherent parameters determining its effectivity towards water purification and energy storage purposes.

Conclusions
In this work, two graphene-based materials which differ in terms of morphology and pore structure have been examined for their water purification and electrochemical energy storage performance.The tested samples included smooth, highly-crystalline, non-porous and low-specific surface area (~20 m 2 /g) graphene nanoplatelets (GNP) and defective, less-crystalline, nanoporous and high-specific surface area (~776 m 2 /g) few-layer graphene flakes (FLG).Both materials were derived from plasma-induced exfoliation of natural flake graphite.The GNP powder showed partial dispersibility in distilled water and ethanol, while the FLG powder was fully dispersible in both solvents even after several weeks.The GNP sample exhibited a higher contact angle with distilled water, however, the FLG sample showed faster kinetics towards water adsorption.In terms of potential applications, the FLG powder has proven to be an efficient filtering material for both decolourization and deacidification of water-rich substances such as Coca-Cola ® .Moreover, the FLG was used as a proper electrode material for ion electrosorption in a model supercapacitor device.In contrast, the GNP-based filters and electrodes failed in both applications.Therefore, the increased specific surface area and the nano-sized pores of the FLG material seem to be the inherent parameters determining its effectivity towards water purification and energy storage purposes.

Figure 1 .
Figure 1.Difference in the volume occupied by 2 g of GNP and FLG powders (upper left); filtration setup for water purification showing a coffee filter filled with graphene powder (right), an empty coffee filter used for reference (middle) and the pure Coca-Cola ® (left).

Figure 1 .
Figure 1.Difference in the volume occupied by 2 g of GNP and FLG powders (upper left); filtration setup for water purification showing a coffee filter filled with graphene powder (right), an empty coffee filter used for reference (middle) and the pure Coca-Cola ® (left).

Figure 3 .
Figure 3. Dispersions of (a-c) GNP and (d-f) FLG powders with distilled water and ethanol directly after mixing, after 48 h and after 44 days, respectively; (g) digital pictures taken every 2 min for the water contact angle measurements of the as-prepared GNP and FLG thin films.

Figure 3 .
Figure 3. Dispersions of (a-c) GNP and (d-f) FLG powders with distilled water and ethanol directly after mixing, after 48 h and after 44 days, respectively; (g) digital pictures taken every 2 min for the water contact angle measurements of the as-prepared GNP and FLG thin films.

Figure 4 .
Figure 4. (a) Coca-Cola ® filtered only with a coffee filter, (b) water-based liquids derived from Coca-Cola ® upon filtration with GNP and FLG powders (first purification cycle), (c) water-based liquids derived from Coca-Cola ® following two cycles of filtration with the FLG powder and (d) pictures of commercial pH paper strips; from left to right: pure Coca-Cola ® (value extracted from literature [48]), Coca-Cola ® filtered only with a coffee filter and Coca-Cola ® filtered with FLG powder after one and two filtration cycles.

Figure 4 .
Figure 4. (a) Coca-Cola ® filtered only with a coffee filter, (b) water-based liquids derived from Coca-Cola ® upon filtration with GNP and FLG powders (first purification cycle), (c) water-based liquids derived from Coca-Cola ® following two cycles of filtration with the FLG powder and (d) pictures of commercial pH paper strips; from left to right: pure Coca-Cola ® (value extracted from literature [48]), Coca-Cola ® filtered only with a coffee filter and Coca-Cola ® filtered with FLG powder after one and two filtration cycles.

Figure 5 .
Figure 5. Electrochemical characterization of the FLG and GNP powders based on (a) CV curves with different scan rates (1, 10 and 100 mV/s), (b) rate handling tests between 0.5 and 100 mV/s based on CV, (c) Nyquist plots of the impedance spectra and (d) GCD curves for different specific currents (0.25, 0.5 and 1 A/g).

Figure 5 .
Figure 5. Electrochemical characterization of the FLG and GNP powders based on (a) CV curves with different scan rates (1, 10 and 100 mV/s), (b) rate handling tests between 0.5 and 100 mV/s based on CV, (c) Nyquist plots of the impedance spectra and (d) GCD curves for different specific currents (0.25, 0.5 and 1 A/g).