Development and Evaluation of Liquid Plaster Loaded with Chromolaena odorata Leaf Extract Endowed with Several Beneficial Properties to Wound Healing

Liquid plaster (LP) is a recently developed wound dressing product that can be used to cover wounds in various parts of the body, especially small injuries or wounds in body parts involved in movement. Given the benefits and applications of LP, this study aimed to develop and evaluate Chromolaena odorata extract-loaded LP with antimicrobial and hemostasis effects. The study was first conducted through the extraction of Choromolaena odorata leaf by using an ethanol maceration technique and identification of the compounds with high-performance liquid chromatography. The LP loaded with Chromolaena odorata extract demonstrates an ability to inhibit S. aureus and S. epidermidis at a MIC of 0.25 mg/mL and MBC of 0.5 mg/mL. The antioxidant activity test was performed by ABTS and DPPH methods demonstrating the free-radical scavenging activity of the extract. The blood clotting activity was established by varying the concentration of Choromolaena odorata leaf extract from 0.0625 mg/mL to 1 mg/mL. The formulation of the film-forming system was developed by varying the solvent, polymer, and plasticizer proportions. The optimum formulation displayed fast film-forming with high elasticity of the film. Moreover, the 20 mg/mL herbal extract-loaded LP provided an antibacterial effect with admissible water vapor transmission and low skin irritation. As a result, the study demonstrates the possibility of introducing the Chromolaena odorata extract-loaded LP to increase the effectiveness of wound healing and the antibacterial effect on the skin.


Introduction
Acute skin wounds can be caused from superficial scratches to deep injuries, and they can be completely healed with minimal or no scar formation within 3 weeks [1]. Although most dermal wounds are healed by a natural healing process, this process may be retarded by several factors such as infection, movement, and foreign bodies, etc. [2]. If the wounds are covered with dressing, they are continuously exposed to proteinases and chemotactic, complement, and growth factors, which can be lost in the exposed wound [3]. As a result, various wound dressing materials have been developed and used to protect and keep wounds moist. These dressings also enhance re-epithelialization and collagen synthesis. They also promote angiogenesis by creating hypoxia to the wound bed and decrease wound-bed pH which leads to a decrease in the wound infection. Different types of

Physical Appearance, Identification and Quantification of Active Substance from Chromolaena odorata Extracts
The crude product after evaporation of Chromolaena odorata ethanol extracts was dark green slurry and its extraction yield (% of the final extract weight in comparison to the crude weight) was 11.67 ± 0.99%. After that, the major compounds from the Chromolaena odorata extract were identified and quantified by HPLC technique as shown in Figure 1a. The HPLC chromatograms of the reference standards, gallic acid, quercetin, and apigenin provided retention time peaks of 4.7, 8.0, and 10.6 min, respectively (Figure 1b). The retention times are in agreement with the previous study by Chen and team which reported the following HPLC conditions: the mobile phase composition of methanol/acetonitrile/acetic acid/phosphoric acid/water at a 200/100/10/10/200 ratio, detecting the wavelength of 352 nm, and retention time of gallic acid, quercetin and apigenin were 4.2, 7-9 and 12-15 min, respectively [20]. After the standard curves were generated, the amount and percent yield of gallic acid, quercetin, and apigenin from Chromolaena odorata extracts were quantified as presented in Table 1. The amount of the flavonoids from crude was close to the previous work by Thophon and colleagues reporting that gallic acid and quercetin from Chromolaena odorata ethanol extracts were 0.154 g and 0.031 g per 100 g of the crude extract, respectively. Moreover, the other flavonoid substances were found in the amount of 1.016 g from 100 g of the extract [21]. These findings support the preservation of the major active chemicals found in Chromolaena odorata leaves collected in Chonburi province. Additionally, as previously documented, ethanol maceration proved a suitable extraction technique for flavonoid extractions [22].

Antimicrobial Activity of Chromolaena odorata Extracts
The MIC of Chromolaena odorata extracts was determined by broth dilution, then MBC was measured by subculturing the broths used for MIC determination onto fresh agar plates. Finally, the antimicrobial activity of Chromolaena odorata extracts at different concentrations was confirmed by the agar well diffusion method. As presented in Table 2 MIC of Chromolaena odorata extracts against S. epidermidis and S. aureus were equivalence at 0.25 mg/mL and those of MBC were 0.5 mg/mL. The MIC and MBC results from this study were better than previously reported by Thophon and team [21] who informed us that the MIC of ethanolic leaf of Chromolaena odorata extracts inhibiting S. epidermidis and S. aureus were 0.81 and 6.25 mg/mL, respectively. The MBC against S. epidermidis and S. aureus was 1.62 and 12.5 mg/mL, respectively.

Antimicrobial Activity of Chromolaena odorata Extracts
The MIC of Chromolaena odorata extracts was determined by broth dilution, then MBC was measured by subculturing the broths used for MIC determination onto fresh agar plates. Finally, the antimicrobial activity of Chromolaena odorata extracts at different concentrations was confirmed by the agar well diffusion method. As presented in Table 2 MIC of Chromolaena odorata extracts against S. epidermidis and S. aureus were equivalence at 0.25 mg/mL and those of MBC were 0.5 mg/mL. The MIC and MBC results from this study were better than previously reported by Thophon and team [21] who informed us that the MIC of ethanolic leaf of Chromolaena odorata extracts inhibiting S. epidermidis and S. aureus were 0.81 and 6.25 mg/mL, respectively. The MBC against S. epidermidis and S. aureus was 1.62 and 12.5 mg/mL, respectively.  Antimicrobial activity of different concentrations Chromolaena odorata extracts and 25 mg/mL clindamycin solution was further tested by the agar-well diffusion method as illustrated in Figure 2. When the concentration of Chromolaena odorata extracts was increased, the antibacterial activity against S. epidermidis and S. aureus increased. Although the inhibition zone of 1 mg/mL Chromolaena odorata extracts was lower than that of 25 mg/mL clindamycin solution (commercial product concentration), the tested concentration of Chromolaena odorata extracts was lower than the clindamycin solution by 25 times. The results are comparable to those reported by Thophon et al., who found that Chromolaena odorata extracts had inhibition zones of 16.0 ± 0.50 and 13.0 ± 1.0 against S. epidermidis and S. aureus, respectively [21]. the inhibition zone of 1 mg/mL Chromolaena odorata extracts was lower than that of 25 mg/mL clindamycin solution (commercial product concentration), the tested concentration of Chromolaena odorata extracts was lower than the clindamycin solution by 25 times. The results are comparable to those reported by Thophon et al., who found that Chromolaena odorata extracts had inhibition zones of 16.0 ± 0.50 and 13.0 ± 1.0 against S. epidermidis and S. aureus, respectively [21].

Antioxidant Activity of Chromolaena odorata Extracts
IC50 (half maximal inhibitory concentration) values of Chromolaena odorata extracts tested by ABTS and DPPH assay were 88.31 ± 4.42 and 143.92 ± 3.40 µg/mL, respectively. The standard references for these tests were gallic acid which is a strong antioxidant with free radical scavenging activities. In this study, gallic acid (positive control) showed antioxidant activity at IC50 of 1.24 ± 0.0996 and 1.97 ± 0.14 µg/mL for ABTS and DPPH assay, respectively, which was lower than the extract. The scavenging activity result from ABTS test of Chromolaena odorata extracts exhibited lower IC50 than that of DPPH method. The antioxidant activity result of the Chromolaena odorata extracts was in agreement with the previous report by Omokhua and colleagues [23].

Antioxidant Activity of Chromolaena odorata Extracts
IC 50 (half maximal inhibitory concentration) values of Chromolaena odorata extracts tested by ABTS and DPPH assay were 88.31 ± 4.42 and 143.92 ± 3.40 µg/mL, respectively. The standard references for these tests were gallic acid which is a strong antioxidant with free radical scavenging activities. In this study, gallic acid (positive control) showed antioxidant activity at IC 50 of 1.24 ± 0.0996 and 1.97 ± 0.14 µg/mL for ABTS and DPPH assay, respectively, which was lower than the extract. The scavenging activity result from ABTS test of Chromolaena odorata extracts exhibited lower IC 50 than that of DPPH method. The antioxidant activity result of the Chromolaena odorata extracts was in agreement with the previous report by Omokhua and colleagues [23].

Blood Coagulation Test of Chromolaena odorata Extract
Blood coagulation test of Chromolaena odorata extracts, positive (DMSO) and negative (normal saline) controls were depicted in Figure 3. It was found that Chromolaena odorata extracts at the concentration range of 0.0625-1 mg/mL provided platelet coagulant activities with an average platelet coagulation size of 0.5-1.0 mm. Protein precipitated in the positive control (DMSO), producing blood coagulation. Normal saline, on the other hand, had no effect on blood coagulation. The blood coagulation mechanism of Chromolaena odorata extracts was proposed before by Akomas et al. explaining that the hemostatic property of Chromolaena odorata has been attributed to the presence of tannins and saponins in the leaf extracts. Tannins have been implicated in the hemostatic activity of plants where they arrest bleeding from damaged or injured vessels by precipitating proteins to form vascular plugs. Moreover, saponins have been reported to have precipitating and coagulative properties [24]. had no effect on blood coagulation. The blood coagulation mechanism of Chromolaena odorata extracts was proposed before by Akomas et al. explaining that the hemostatic property of Chromolaena odorata has been attributed to the presence of tannins and saponins in the leaf extracts. Tannins have been implicated in the hemostatic activity of plants where they arrest bleeding from damaged or injured vessels by precipitating proteins to form vascular plugs. Moreover, saponins have been reported to have precipitating and coagulative properties [24].

Cytotoxicity
Effects of Chromolaena odorata extract on MRC-5 cell viability was monitored by the MTT cell viability assay. The cells were treated by 15.625-1000 µg/mL of Chromolaena odorata extract for 24 h. As illustrated in Figure 4, at 125 µg/mL and higher concentrations of Chromolaena odorata extract, cell viability was severely reduced. The IC50 of Chromolaena odorata extract cytotoxicity was 673.23 µg/mL which is moderate toxicity for natural component [25]. This IC50 value was slightly higher than the previous report by R.N. Asomugha and colleagues revealing that the cytotoxicity IC50 of Chromolaena odorata extract to brain shrimp was 324-392 µg/mL [26]. This might be owing to the fact that different test cells and extraction methods were used.

Cytotoxicity
Effects of Chromolaena odorata extract on MRC-5 cell viability was monitored by the MTT cell viability assay. The cells were treated by 15.625-1000 µg/mL of Chromolaena odorata extract for 24 h. As illustrated in Figure 4, at 125 µg/mL and higher concentrations of Chromolaena odorata extract, cell viability was severely reduced. The IC 50 of Chromolaena odorata extract cytotoxicity was 673.23 µg/mL which is moderate toxicity for natural component [25]. This IC 50 value was slightly higher than the previous report by R.N. Asomugha and colleagues revealing that the cytotoxicity IC 50 of Chromolaena odorata extract to brain shrimp was 324-392 µg/mL [26]. This might be owing to the fact that different test cells and extraction methods were used. had no effect on blood coagulation. The blood coagulation mechanism of Chromolaena odorata extracts was proposed before by Akomas et al. explaining that the hemostatic property of Chromolaena odorata has been attributed to the presence of tannins and saponins in the leaf extracts. Tannins have been implicated in the hemostatic activity of plants where they arrest bleeding from damaged or injured vessels by precipitating proteins to form vascular plugs. Moreover, saponins have been reported to have precipitating and coagulative properties [24].

Cytotoxicity
Effects of Chromolaena odorata extract on MRC-5 cell viability was monitored by the MTT cell viability assay. The cells were treated by 15.625-1000 µg/mL of Chromolaena odorata extract for 24 h. As illustrated in Figure 4, at 125 µg/mL and higher concentrations of Chromolaena odorata extract, cell viability was severely reduced. The IC50 of Chromolaena odorata extract cytotoxicity was 673.23 µg/mL which is moderate toxicity for natural component [25]. This IC50 value was slightly higher than the previous report by R.N. Asomugha and colleagues revealing that the cytotoxicity IC50 of Chromolaena odorata extract to brain shrimp was 324-392 µg/mL [26]. This might be owing to the fact that different test cells and extraction methods were used. Effects of Chromolaena odorata extract on MRC-5 cell viability. Cells were exposed to 15.625-1000 µg/mL of Chromolaena odorata extract for 24 h. The percentage of cell viability was determined by MTT cell viability assay. The results were represented as a percentage of control. Data were expressed as the mean ± SEM (n = 3). *** p < 0.001, significantly different from the control, ** p < 0.01, significantly different from the control, * p < 0.05, significantly different from the control.

Formulation of Liquid Plaster
Plastoid ® B could be clearly dissolved in ethyl acetate during the concentration range of 5-35% (w/w) (F1.1-1.7 from Table 4). However, only the dissolved Plastoid ® B at the concentration range of 25-35% (w/w) provided transparent thin film after drying.  Figure 5a. The dissolved Plastoid ® B at all concentrations showed shear thinning, a non-Newtonian characteristic in which viscosity reduces as shear rate increases, as seen in the figure [27]. However, yield stresses exist for Plastoid ® B gels with a concentration of 30% and 35% [28]. As shown in Figure 5b, adding PEG enhanced shear viscosity but the rheology behavior still was shear thinning. This finding is in line with a recent study that found PEG decreases the degree of polymer chain tangling. As a result, the mobility of the molecular chains improves, making it simpler for them to move under shear stress [29].
x FOR PEER REVIEW 8 of 24 The shear viscosity of various Plastoid ® B at shear rate of 1 s −1 (shear rate simulating pouring action [30]) is illustrated in Figure 6. As shown in Figure 5a, the viscosity was dependent on the polymer concentration (30-35% Plastoid ® B). Plastoid ® B shear viscosities were not different at concentrations ranging from 5 to 25%. The shear viscosity of  The shear viscosity of various Plastoid ® B at shear rate of 1 s −1 (shear rate simulating pouring action [30]) is illustrated in Figure 6. As shown in Figure 5a, the viscosity was dependent on the polymer concentration (30-35% Plastoid ® B). Plastoid ® B shear viscosities were not different at concentrations ranging from 5 to 25%. The shear viscosity of reference product A and B were 2.64 ± 0.07 Pa s and 4.49 ± 1.38 Pa s, respectively, which was close to that of 30% Plastoid ® B (9.66 ± 5.18 Pa s). Therefore, formulation of 30% Plastoid ® B was selected for further testing and product development. Then, different solvent systems (ethyl acetate:isopropyl alcohol) were applied to dissolve Plastoid ® B at a concentration of 30% and their shear viscosities were measured as depicted in Figure 6b. The viscosity of all dissolved Plastoid ® B preparations was considerably decreased when the isopropyl alcohol component was increased. When the isopropyl alcohol portions were 40 or 60% of the solvent, the shear viscosities were not different and close to those of the commercial products.

PEER REVIEW 9 of 24
40 or 60% of the solvent, the shear viscosities were not different and close to those of the commercial products.

Liquid Drying Time
Drying time profile of Plastoid ® B solution at different concentrations (5-35%) and the commercial products are presented in Figure 7. The weight dramatically decreased at first 5 min especially those of 5-20% Plastoid ® B solutions. The reason for this is that for-   Figure 7. The weight dramatically decreased at first 5 min especially those of 5-20% Plastoid ® B solutions. The reason for this is that formulations with low polymer concentrations have highly volatile solvents, which cause rapid evaporation. Furthermore, the Plastoid ® B solution concentration of 25-35% produced a drying time profile that was comparable to the reference products. The effect of solvent systems (ethyl acetate: isopropyl alcohol) and PEG portion (0-5%) on drying time were also monitored by W10min value which is the weight of formulation after 10 min of the time to dry test. The W10min values of different Plastoid ® B formulations are shown in Figure 8. By increasing the amount of isopropyl alcohol in the formulation, the rate of solvent evaporation was slowed. This is due to the boiling point of ethyl acetate (77.1 °C) being lower than that of isopropyl alcohol (82.5 °C) [31]. Furthermore, the majority of the results show that PEG slowed solvent evaporation, resulting in a higher weight remaining in the formulation. This outcome obeys Raoult's law, explaining that if any non-electrolyte substances (in this case, PEG) are dissolved in any solvent, the vapor pressure above the solution will be less than the pure solvent [32]. However, the W10min values of all the Plastoid ® B solutions were about the same as commercial products (69.23-84.10%). The effect of solvent systems (ethyl acetate: isopropyl alcohol) and PEG portion (0-5%) on drying time were also monitored by W 10min value which is the weight of formulation after 10 min of the time to dry test. The W 10min values of different Plastoid ® B formulations are shown in Figure 8. By increasing the amount of isopropyl alcohol in the formulation, the rate of solvent evaporation was slowed. This is due to the boiling point of ethyl acetate (77.1 • C) being lower than that of isopropyl alcohol (82.5 • C) [31]. Furthermore, the majority of the results show that PEG slowed solvent evaporation, resulting in a higher weight remaining in the formulation. This outcome obeys Raoult's law, explaining that if any nonelectrolyte substances (in this case, PEG) are dissolved in any solvent, the vapor pressure above the solution will be less than the pure solvent [32]. However, the W 10min values of all the Plastoid ® B solutions were about the same as commercial products (69.23-84.10%).

Film Mechanical Properties
Breaking strain and Young's modulus of the films prepared from 30% Plastoid ® B solution with different solvent systems (ethyl acetate, isopropyl alcohol) and PEG portions compared to the commercial reference products are shown in Figure 9. It was found that adding PEG could enhance film elongation. Moreover, the maximum breaking strain was around 350%, which was greater than that of the reference products (Figure 9a). The Young's modulus values were in consonance with the breaking strain values. As shown in Figure 9b, the Young's modulus values were reduced when PEG was added to the liquid plaster formulation. PEG works as a plasticizer well in a solvent ratio (ethyl acetate: isopropyl alcohol) range of 60:40 to 20:80. This might be because of the polarity difference between ethyl acetate (relative polarity of 0.228) and isopropyl alcohol (relative polarity of 0.546) [33]. As reported in a previous research study [34], the higher portion of isopropyl alcohol elevated the solvent polarity, which can escalate film elongation. This might be due to the fact that PEG 400 is a hydrophilic molecule with a dielectric constant of 12.4, allowing it to distribute completely across polymer chains in a high polarity solvent [35].

Film Mechanical Properties
Breaking strain and Young's modulus of the films prepared from 30% Plastoid ® B solution with different solvent systems (ethyl acetate, isopropyl alcohol) and PEG portions compared to the commercial reference products are shown in Figure 9. It was found that adding PEG could enhance film elongation. Moreover, the maximum breaking strain was around 350%, which was greater than that of the reference products (Figure 9a). The Young's modulus values were in consonance with the breaking strain values. As shown in Figure 9b, the Young's modulus values were reduced when PEG was added to the liquid plaster formulation. PEG works as a plasticizer well in a solvent ratio (ethyl acetate: isopropyl alcohol) range of 60:40 to 20:80. This might be because of the polarity difference between ethyl acetate (relative polarity of 0.228) and isopropyl alcohol (relative polarity of 0.546) [33]. As reported in a previous research study [34], the higher portion of isopropyl alcohol elevated the solvent polarity, which can escalate film elongation. This might be due to the fact that PEG 400 is a hydrophilic molecule with a dielectric constant of 12.4, allowing it to distribute completely across polymer chains in a high polarity solvent [35].

Physical Properties and Antimicrobial Activity of Liquid Plaster Formulation Loaded Chromolaena odorata Extract
The liquid plaster formulation composed of 30% Plastoid ® B, 2% PEG, and the solven of ethyl acetate and isopropyl alcohol at a ratio of 60:40 was selected for Chromolaena odo rata extract loading because this formulation offered proper viscosity, drying period, an film mechanical properties. The Chromolaena odorata extract loading concentration of 2

Physical Properties and Antimicrobial Activity of Liquid Plaster Formulation Loaded Chromolaena odorata Extract
The liquid plaster formulation composed of 30% Plastoid ® B, 2% PEG, and the solvent of ethyl acetate and isopropyl alcohol at a ratio of 60:40 was selected for Chromolaena odorata extract loading because this formulation offered proper viscosity, drying period, and film mechanical properties. The Chromolaena odorata extract loading concentration of 20 mg/mL was used for the formulation because this concentration provided antimicrobial activity, antioxidant activity, and hemostatic property with low cytotoxicity. The prepared liquid plaster formulation loaded with Chromolaena odorata extract was evaluated under the topics of shear viscosity, time to dry, Young's modulus, water vapor transmission, and antimicrobial activity to monitor the effect of the herbal extract on formulation properties.

Shear Viscosity, Film Drying, and Young's Modulus
The shear viscosity, film drying in terms of W 10min , and Young's modulus of the blank liquid plaster formulation and liquid plaster formulation loaded with Chromolaena odorata extract compared to the reference products are presented in Table 3. Shear viscosity and film drying time were not affected by adding Chromolaena odorata extract to the formulation. The extract elevated Young's modulus from the blank film, indicating the liquid plaster formulation loaded with Chromolaena odorata extract has higher strength with similar film stretching to the blank film. The Young's modulus values of the liquid plaster containing Chromolaena odorata and the referred products, on the other hand, are acceptable since they can still be stretched. The shear viscosity at 1 s −1 of the liquid plaster formulations (extract load/blank) was higher than the reference products. The liquid plaster formulation's film drying time was quite similar to that of the reference product A.

Water Vapor Transmission
The water vapor transmission study of the Chromolaena odorata extract loaded cast film and blank film was presented in Figure 10. The experiment lasted 5 days, with the weight of the calcium chloride-filled container covered with films steadily increasing. The weight gain of the bottle covered with the Chromolaena odorata extract-loaded cast film was significantly higher than that of blank film. The water vapor transmission rate of the Chromolaena odorata extract-loaded cast film and blank film were 110.13 and 91.96 g m −2 d −1 , respectively. The water vapor transmission rates of the reference products A and B were higher than those of the extract-loaded film and blank film, which were 442.35 and 458.66 g m −2 d −1 , respectively.

Antimicrobial Activity by Agar Well Diffusion Method
The clear zone diameter of the 25 mg/mL clindamycin solution (positive control), negative controls, the reference products, and different concentrations of Chromolaena odorata extract loaded film against S. epidermidis and S. aureus are illustrated in Figure 11. The antimicrobial activity of the Chromolaena odorata extract-loaded liquid plasters against S. epidermidis and S. aureus by the agar-well diffusion method was in the same direction. The liquid plasters containing 20-50 mg (4X-10X MBC) Chromolaena odorata extract inhibit growth of S. epidermidis and S. aureus. While the clear zone could not be observed from the negative controls (blank films and distilled water) and the liquid plasters containing 5-10 mg of Chromolaena odorata extract, they could be observed from the negative controls (blank films and distilled water). The reason that the liquid plaster film containing a low concentration of Chromolaena odorata extract could not inhibit microbial growth was explained in the work of Rosa and team [38]. The result was discussed, and it was found that films require an adequate concentration and dispersion of the antimicrobial compound in their surface matrix. Once the concentration of the antimicrobial compound is sufficient, the compound will be released from all the points on the surface, reaching the minimum bactericidal concentration. Although the prepared liquid plaster film had a lower water vapor transmission rate than the reference products, the values were nevertheless comparable to the commercial wound dressing products (50 to 6512 g m −2 d −1 ) described in the previous study [36]. As a result, the herbal extract-loaded films appear to allow rather more water vapor to pass through than the blank film. This was explained before by Saringat and his research team, reporting that incorporation of an insoluble substance into the film caused irregular spots and holes enhancing moisture permeability [37].

Antimicrobial Activity by Agar Well Diffusion Method
The clear zone diameter of the 25 mg/mL clindamycin solution (positive control), negative controls, the reference products, and different concentrations of Chromolaena odorata extract loaded film against S. epidermidis and S. aureus are illustrated in Figure 11. The antimicrobial activity of the Chromolaena odorata extract-loaded liquid plasters against S. epidermidis and S. aureus by the agar-well diffusion method was in the same direction. The liquid plasters containing 20-50 mg (4X-10X MBC) Chromolaena odorata extract inhibit growth of S. epidermidis and S. aureus. While the clear zone could not be observed from the negative controls (blank films and distilled water) and the liquid plasters containing 5-10 mg of Chromolaena odorata extract, they could be observed from the negative controls (blank films and distilled water). The reason that the liquid plaster film containing a low concentration of Chromolaena odorata extract could not inhibit microbial growth was explained in the work of Rosa and team [38]. The result was discussed, and it was found that films require an adequate concentration and dispersion of the antimicrobial compound in their surface matrix. Once the concentration of the antimicrobial compound is sufficient, the compound will be released from all the points on the surface, reaching the minimum bactericidal concentration.

In Vivo Study of Skin Irritation, Transepidermal Water Loss and Skin Density after Liquid Plaster Use
Skin irritation, transepidermal water loss, and skin density of 27 healthy volunteers after use of liquid plaster and the reference products were measured using Antera 3D (Miravex, Ireland) and DermaLab Combo (Cortex, Denmark). Two optimized liquid plas-

In Vivo Study of Skin Irritation, Transepidermal Water Loss and Skin Density after Liquid Plaster Use
Skin irritation, transepidermal water loss, and skin density of 27 healthy volunteers after use of liquid plaster and the reference products were measured using Antera 3D (Miravex, Ireland) and DermaLab Combo (Cortex, Denmark). Two optimized liquid plaster formulations (Formulation 1: 30% Plastiod B, 2% PEG and Formulation 2: 35% Plastiod B, 2% PEG under solvent system of 40% ethyl acetate: 60% isopropyl alcohol) and the reference product were selected for the in vivo evaluation as depicted in Figure 11. After usage, all of the products slightly induced skin redness (Figure 12a). The images taken from the Antera 3D is shown in Figure S1. They were not, however, the source of the severe skin irritation and rash. More redness scores may result from film peeling off, which is common in adhesive plaster application, and the redness disappeared within 5-10 min [39]. As demonstrated in Figure 12b, after using the herb extract-loaded optimization liquid plaster, skin density slightly rose as measured by a high frequency ultrasound probe [40]. This might be because the solvents (ethyl acetate and isopropyl alcohol) used in the liquid plaster altered epithelial tissue resulting in higher skin density, temporarily [41]. All liquid plaster samples had no effect on skin integrity, therefore the amount of water that passively evaporates through skin to the external environment did not alter as seen in Figure 12c. that passively evaporates through skin to the external environment did not alter as seen in Figure 12c.

Conclusions
In the present study, Chromolaena odorata leaves were extracted by the maceration method with ethanol. By the HPLC method monitoring, the main active compounds (gallic acid, quercetin, and apigenin) were present in the extract. The extract demonstrated several pharmacological activities, including antibacterial, antioxidant, and blood coagu-

Conclusions
In the present study, Chromolaena odorata leaves were extracted by the maceration method with ethanol. By the HPLC method monitoring, the main active compounds (gallic acid, quercetin, and apigenin) were present in the extract. The extract demonstrated several pharmacological activities, including antibacterial, antioxidant, and blood coagulation, which can enhance the wound-healing process. The cytotoxicity test of the extract exhibited moderate toxicity for natural components. The liquid plaster formulation was optimized by varying the plastoid ® B and PEG concentrations dissolved in several solvent systems. The formulation of 30% plastoid ® B, 2% PEG, and a solvent mixture of 60:40 ethyl acetate and isopropyl alcohol had shear viscosity, drying time, and film mechanical characteristics that were appropriate for liquid plaster dosage forms and comparable to the reference products. The Chromolaena odorata extract could successfully load the liquid plaster and, at a concentration of 20-50 mg/mL, the plaster could inhibit growth of S. epidermidis and S. aureus. The dry film allowed water vapor transmission at a rate of 110.13 g m −2 d −1 . The liquid plaster containing Chromolaena odorata extract did not produce significant skin irritation in the in-vivo skin test. Furthermore, the finished product could improve skin density. According to the findings, the Chromolaena odorata-loaded liquid plaster has a significant chance of being used in clinical settings to treat infected wounds in people and animals. To establish the test results in this study, the true scenario of the product utilized in the wound healing study must be investigated further.

Chromolaena odorata Extract
The fresh leaves of Chromolaena odorata were collected in June 2020 in Chonburi province area and then cleaned with water. The Chromolaena odorata leaves were identified by Dr. Boonyadist Vongsak, Faculty of Pharmaceutical Sciences, Burapha University, Thailand. The voucher specimens (KM No.0415001, KM No.0415002, and KM No.0415003) were deposited at the Faculty of Pharmaceutical Sciences, Burapha University, Thailand. After that, 20 g of fresh leaves were soaked with 200 mL of 95% (v/v) ethanol for 24 h. The mixtures were filtered through Whatman filter paper No.1, and concentrated using a rotary evaporator (R-100, Buchi, Switzerland) at 78 • C. The dark brownish-green viscous residues were dried by freeze-drying (freeze dryer, Labconco, Edwards Limited, UK) for 24 h. The dried product was kept in a tightly closed brown vial at 4 • C until used. Dimethyl sulfoxide (DMSO) at a concentration of 99.9% was used as a dissolving agent to make further tests.

Identification and Quantification of Active Substance from Chromolaena odorata Extracts
According to the previous reports [42], three important active substances (gallic acid, quercetin, and apigenin) of Chromolaena odorata extracts can be used to monitor the efficiency of the extraction process. The isolated flavonoids (gallic acid, quercetin, and apigenin) were quantified using high-performance liquid chromatography coupled with an ultraviolet detector (HPLC-UV) (SPD-M20A, Shimadzu, Japan), as previously reported and validated by Xiao-qing Chen and Jian-bo Xiao [20]. The analytical column used in the present study was a C18 reverse-phase KinetexTM column (C18, 2504.6 mm, pore size 5 m, Phenomenex, CA, USA). The mobile phase was a mixture of methanol, acetonitrile, acetic acid, phosphoric acid and water (200:100:10:10:200 by volume). The detecting wavelength was 272 nm and the flow rate was 0.60 mL/min. The volume of the injecting sample was 6.0 l. The HPLC system was set to run at room temperature (28 ± 1 • C).
The referenced standard solutions of gallic acid, quercetin, and apigenin were prepared by dissolving in methanol in the concentration range of 1.5625-100 µg/mL. Then the prepared standard solutions were filtered through a 0.45 m membrane before being injected into the HPLC. After that, the standard curves of gallic acid, quercetin, and apigenin were generated. The Chromolaena odorata extracts sample was prepared by dissolving the crude extracts in methanol at the concentration of 1 mg/mL. Then the sample was filtered by a 0.45 µm membrane before being injected into the HPLC with similar conditions as described before.

Antimicrobial Activity of Chromolaena odorata Extracts
Staphylococcus aureus (ATCC6538) and Staphylococcus epidermidis (ATCC14990) strains were selected as testing organisms due to their representation of Gram-positive bacteria on human skin and mucosal surfaces [43]. The bacterial stock cultures were incubated at 37 • C for 24 h on nutrient agar. The bacterial suspensions were compared to a 0.5 McFarland turbidity standard to obtain 10 7 -10 8 CFU/mL.

Disk Diffusion Method
The antimicrobial activity of Chromolaena odorata extracts against two pathogenic bacteria was investigated by the agar disk diffusion method [5]. The herbal extracts with concentrations of 100, 200, and 300 mg/mL were screened for antibacterial activity against S. aureus and S. epidermidis. The test cultures were spread on the nutrient agar plate. Whatman filter paper (No.1) as a disk was cut 0.6 cm in diameter, adsorbed with Chromolaena odorata extract solutions and then placed on a prepared plate. Plates were incubated at 37 • C for 18 to 24 h. DMSO was used as a negative control. The zones of growth inhibition (including the diameter of the disk) were recorded in diameter (mm). The experiments were conducted in triplicate.

Minimum Inhibitory Concentration (MIC)
The MIC of Chromolaena odorata extract was established using the macro broth dilution procedure to estimate the liquid plaster loading dose of the herbal extract. The testing microbes were prepared by transferring Staphylococcus aureus and Staphylococcus epidermidis to Mueller Hinton Broth (MHB) and incubated at 37 • C for 3-4 h. To determine the MIC, the Chromolaena odorata extract was diluted in test tubes to concentrations of 1000, 500, 250, 125, 62.5, and 31.25 µg/mL. Then, in each test tube containing Chromolaena odorata extract, 5 mL of MHB was added. The Chromolaena odorata extracts and microbe mixes were then incubated for 16-18 h at 37 • C. The turbidity of the mixture in the test tubes after incubation was used to monitor the growth of microorganisms. The MIC was determined to be the lowest concentration of propolis extract that can inhibit microbial growth [44].

Minimum Bactericidal Concentration (MBC)
The MBC of Chromolaena odorata extract was explored by streaking the turbid mixture from the MIC test on the surface of Mueller Hinton Agar (MHA) and incubating at 37 • C for 16-18 h. If the concentration of Chromolaena odorata extract is high enough, microbial colonies will not be found on the MHA plate [45].

ABTS Assay
The ABTS radical-scavenging test is widely used to determine the antioxidant activity of both hydrophilic and lipophilic compounds. The experiment was performed according to an improved method as described by Heng et al. [46] with some modification. An ABTS solution was prepared at a concentration of 7 mM, then it was kept in darkness at room temperature (25 • C) for 18 h. The Chromolaena odorata extracts with different concentrations (0.3125-1 mg/mL) were tested by mixing 160 µL of 7 mM ABTS solution in 96-well microplates. The final absorbance was measured at 734 nm. Then, ABTS radical scavenging activity was calculated as presented in Equation (1), ABTS radical scavenging activity = Abs control − Abs sample Abs control × 100 (1) where, Abs control is absorbance of ABTS radical and methanol; Abs sample is absorbance of ABTS radical and Chromolaena odorata extract. All experiments were performed in triplicate.

DPPH Assay
Determination of scavenging stable DPPH free radicals was a very fast method to evaluate the antioxidant activity of the extracts in a very short time. The mechanism of the DPPH method is the determination of the antiradical power of an antioxidant by measurement of the decrease in the absorbance of DPPH at 517 nm. This results in a color change from purple to yellow due to the donation of hydrogen to form a stable DPPH-H molecule. In this study, the DPPH assay method was modified from Omokhua et al. [47] as reported before. The extract was tested at six different concentrations: 0.5, 0.25, 0.125, 0.625, and 0.3125 mg/mL. The DPPH solution was prepared in the concentration of 60 µM, then 40 µL of a methanolic solution of the extract was added. The mixture was shaken vigorously and allowed to stand for 45 min in the dark. The decrease in absorbance was measured at 517 nm against a blank (ethanol) with a spectrophotometer. From a calibration curve obtained with different amounts of extract, the DPPH radical scavenging activity was calculated as described in Equation (2), DPPH radical scavenging activity = Abs control − Abs sample Abs control × 100 (2) where, Abs control is absorbance of DPPH radical and methanol; Abs sample is absorbance of DPPH radical and Chromolaena odorata extract. All experiments were performed in triplicate.

Blood Coagulation Test of Chromolaena odorata Extract
Blood coagulation activity of Chromolaena odorata extract was evaluated to simulate the function of the extracts in wound hemostatic [48]. In the test, platelets of cow blood were collected by centrifugation of plasma at 400 rpm for 10 min at room temperature and the supernatant fluid was removed. The precipitate was resuspended in a 0.85% NaCl solution (normal saline) and centrifuged again at 400 rpm for 10 min at room temperature. Then, the supernatant fluid was removed. The cleansing processes with normal saline and centrifugation were repeated until the supernatant fluid was clarified. After that, the platelets were stored at 4 • C until further analysis for no longer than 5 days. For the blood coagulation test, the blood sample was diluted in normal saline (1:10 dilution). Chromolaena odorata extract at the concentration of 0.0625-1 mg/mL was mixed in a ratio of 1:1 (v/v). DMSO at a concentration of 1% and normal saline were used as the positive and negative controls, respectively. The blood coagulation was observed using an optical microscope (Eclipse E200MV R, Nikon, Japan).

Cytotoxicity
Cell viability assays were performed based on the 3-(4,5-dimethylthiazol-2-yl)-2,5diphenyltetrazolium bromide (MTT) colorimetric method. MRC-5 cells which are human diploid cell line were seeded at a density of 10,000 cells per well in a 96-well plate and incubated for 24 h at 37 • C in a 5% CO 2 atmosphere. Cells were treated with 15.625, 31.25, 62.5, 125, 250, 500 and 1000 µg/mL of Chromolaena odorata extract in triplicate for 24 h. Then, 10 µL of 5 mg/mL MTT in PBS solution was directly added into each well and incubated at 37 • C for 3 h. Cultured media was aspirated and a 100 µL aliquot of absolute DMSO was then added. Absorbance (OD) values were measured by a microplate reader (Metertech, Taiwan) at a wavelength of 570 nanometers. The percentage of cell viability was calculated by using the following equation.

Formulation of Liquid Plaster
Liquid plaster was prepared by dissolving Plastoid ® B together with other excipients in the solvents. The effect of polymer concentration, solvent systems, and amount of plasticizer were varied to find a suitable formulation for further development by loading of Chromolaena odorata extract as presented in Table 4. Two reference products of liquid plaster which are available in the market as and OTC products in Thailand were also assessed for comparison purposes. Rheological property is a crucial parameter that needs to be monitored to predict the behavior of the liquid plaster during product application on the skin. Moreover, physical appearances including clarity, precipitation, and viscosity were visually observed and photographed. Then, the rheological behaviors of the liquid plasters were monitored using the rheometer (KINEXUS Lab+, MS603S/01, Malvern Panalytical Ltd., Surrey, United Kingdom) in flow curve measurement mode (viscosity vs. shear rate). The measurement temperature was set to 25 • C, the shear rate was set to 0.1-10 Pa.s, and the viscosity at 1 s −1 shear rate was chosen as a representative of the formulation. The experiment was carried out in triplicate.

Liquid Drying Time
The drying times of liquid plaster from different formulations were assessed to simulate the practical application of the products. The test was conducted by dropping liquid plaster for 0.5 g on the glass plate. Then the weight change was closely monitored by the 4 digit analytical balance (MS603S/01, METTLER-TOLEDO, Switzerland) for 60 min. Each test was carried out in triplicate.

Film Mechanical Properties
The film sample for the mechanical test was prepared by pouring liquid plaster on the glass plate at the size of 5 × 15 cm 2 . The film was dried under ambient conditions then cut into a size of 1 × 10 cm 2 . The thickness was controlled and measured by the digital caliper. Breaking strain of the testing films was assessed using the texture analyzer (TA.XT.Plus, Stable Micro Systems Ltd., Surrey, UK). The breaking strain percentage and Young's modulus were calculated following Equations (4) and (5), respectively.

Water Vapor Transmission
Permeability of water vapor is the principal property of the wound dressing patch. Keeping the wound at optimal moisture can promote wound healing via wound reepithelialization and contraction enhancement [49]. Therefore, water vapor transmission of the thin film from liquid plaster was examined. The film was prepared as described in the film mechanical properties test. Then, the film was then cut into a disc and placed in the mouth of a cylindrical cup filled with 15 g of calcium chloride. The bottle was kept at a temperature of 25-30 • C and 75% ± 5% relative humidity. The weight changes were monitored for 5 days. Then the water vapor transmission rate (WVTR) was calculated as presented Equation (6): Water vapor transmission rate (WVTR) = W 1 − W 2 t 2 − t 1 (6) where W 1 and W 2 are the initial and endpoint weight of calcium chloride. And t 1 and t 2 is the initial time and the end test time, respectively. All measurements were repeated three times.

Antibacterial Activity of Films Loaded Chromolaena odorata Extract
Agar well diffusion method was applied to test the antibacterial activity of films loaded with Chromolaena odorata extract. Testing bacteria, Staphylococcus aureus, and Staphylococcus epidermidis, were prepared at a concentration of 10 8 CFU/mL which turbidity was equal to a 0.5 McFarland standard. Then, the testing bacterial solutions were spread on the MHA plates. After that, the MHA plates were punctured to receive a well with a diameter size of 8 mm. The liquid plaster loaded with Chromolaena odorata extract at concentrations of 0 (negative control), 1, 1.5, and 2 mg/mL, and 25 mg/mL clindamycin solution (positive control) were transferred to the wells on the MHA plates. Then, the plates were incubated at 37 • C for 16-18 h [45].

In Vivo Study of Skin Irritation, Transepidermal Water Loss and Skin Density after Liquid Plaster Use
The in vivo study of skin irritation, transepidermal water loss (TEWL) and skin density after use of the liquid plaster from two optimal formulations and the market reference product A were performed by 27 healthy volunteers ranging in age from 20 to 50 years. The selection of volunteers and test methods were conducted in accordance with the ethical principles described in the Declaration of Burapha University (Ethical code: IRB1-053/2564).
The tests on people have to conform to the World Medical Association Declaration of Helsinki [50]. To conduct the study, 0.5 mL of sample was applied to the volunteer's skin inside part of the arm area for a size of 1 × 3 cm 2 . The film was peeled off after it had been formed (dry film) for 2 min. The 3D imaging camera from Antera 3D (Miravex, Ireland), the skin color probe, TEWL probe, and the high frequency ultrasound probe from DermaLab Combo (Cortex, Denmark) were used to monitor skin parameters such as skin redness for the irritation test, TEWL, and skin density before and after the liquid plaster application.

Statistical Analysis
The data were statistically analyzed using one-way ANOVA followed by Tukey's Honestly Significant Difference (HSD) post hoc test was used to analyze the data from the three independent experiments.