Preparation of Novel Flaxseed Oil/Beeswax Oleogel Systems and Its Application in the Improvement of Sodium Alginate Films

The purpose of this study was to prepare a novel kind of flaxseed oil (FO)/beeswax oleogel system and apply it to improve the properties of sodium alginate films. Three single factors, namely the ratio of beeswax/FO, the addition of oleogel, and the addition of glycerol, were optimized based on the comprehensive score of film characteristics: elongation at break (EAB), tensile strength (TS), hydroxyl radical clearance (HRC), and water vapor permeability (WVP) of the film. When the ratio of beeswax/FO was 7.807%, the addition of oleogel was 4.829%, and the addition of glycerol was 31.088%, the comprehensive score of the film characteristics was maximum. Moreover, the Decapterus maruadsi preserved by the produced films were assessed for drip loss, pH, total volatile basic nitrogen (TVB-N), thiobarbituric acid reactive substance (TBARS), and fatty acids composition. In comparison to the control, the produced films incorporated with linseed oil/beeswax oleogel had a longer shelf-life than Decapterus maruadsi. In conclusion, the oleogel system prepared via linseed oil/beeswax had good stability and hydrophobicity, which can significantly improve the characteristics of the film and extend the shelf-life of Decapterus maruadsi.


Introduction
In recent years, with the strengthening of people's environmental awareness, natural and degradable food packaging materials have gradually become a research hotspot.In particular, natural polymer materials (proteins, polysaccharides, lipids, or a mixture of these ingredients) have attracted people's attention due to their biodegradability, mechanical resistance, and ability to inhibit oxygen and water [1].The application of polysaccharidebased edible film in food provides a new opportunity for developing new food packaging.Polysaccharide edible membranes are made from a mixture of natural polysaccharides, additives (emulsifiers and plasticizers), and functional ingredients (antibacterial agents/antioxidants), with the advantages of being renewable and safe to eat [2].
Alginate is a marine-derived polysaccharide composed of D-mannouronic acid and Lgulonuronic acid in different arrangements and molecular weights.Sodium alginate comes from a wide range of sources and has the advantages of safety, nontoxicity, low cost, suitable gel properties, hydrophilicity, and so on.However, whether it is polysaccharide-based film or protein-based film, their oxygen and water barrier is not good enough.Thus, some hydrophobic/lipid substances can usually be added to the film to solve this problem.At the same time, one single lipid addition cannot achieve multiple film quality improvements.Therefore, it is necessary to add some additional mixture to the film-forming matrix to optimize the edible film to perform a number of predetermined functions, so that they can effectively replace synthetic packaging [3].Due to the limitations of forming edible films from a single material, composite components containing a variety of materials, such as hydrophilic colloid and lipid components, are usually used to make the films [4].The addition of oil to edible film can improve the water barrier properties, decrease its moisture absorption characteristics, reduce the surface roughness of the film, and enhance the specular reflectance of the air-film interface [4].Although there have been some literature reports on the addition of lipids to edible films, it should be noted that the oil is hydrophobic, it easily leaks out in the film-forming process, and even oxidizes [3,4].Thus, oleogel seems to be a good choice, which has been widely considered by scientific researchers.
Oleogel is an effective method to obtain ideal plant solid fat by adding gel factor to vegetable oil to interfere with oil crystallization.The oleogel can self-assemble to form a three-dimensional network to trap the oil, thus slowing down the oil migration.Flaxseed oil (FO) is rich in unsaturated fatty acids, especially linoleic acid and alpha-linolenic acid.Alpha-linolenic acid is an essential fatty acid for maintaining normal physiological functions and growth and development of the body and has various physiological functions, such as improving immunity, improving vision, lowering cholesterol, and preventing cardiovascular diseases [5,6].FO is widely used in fat replacement because of its high content of n−3 fatty acids [7,8].
The addition of wax is helpful for maintaining the oleogel with good stability.Beeswax has unique texture properties, and stable oleogel with high oil binding can be obtained by adding a low concentration [9].Although there is a progressive increase in exploring the potential applications of oleogels in food systems, no literature is available on the use of oleogels as ingredients of edible films except for studies carried out by Yousuf et al. [3], Xiao et al. [10], Li et al. [11], and Shin et al. [12].
Therefore, the study aimed to prepare a novel kind of FO/beeswax oleogel system and apply it to the improvement of the properties of sodium alginate films in order to provide an innovative basis and application reference for the research and development of new composite films.The effect of the ratio of beeswax/FO on the EAB (A), TS(B), HRC(C), and WVP(D) of the film were shown in Figure 1a.When the ratio of beeswax/FO was 2-10%, EAB and HRC of the films first increased and then decreased (p < 0.05), and TS and WVP decreased first and then increased (p < 0.05).When the ratio of beeswax/FO was 8%, EAB had the maximum value, TS had the lowest value, and HRC also had the maximum value.When the ratio of beeswax/FO was 4%, WVP had the minimum value, and the film had the best water vapor barrier ability.Natural waxes are often used to prepare oleogels [3].Meng, Li, Li, and Liu [13] studied the difference between three oleogels structured by three foodgrade plant waxes, namely rice bran wax, palm wax, and beeswax.They found that the beeswax-based oleogels had the highest oil-holding capacity, and the microcrystal structure was the smallest, which showed a fine acicular shape.Moreover, the chemical composition (beeswax and flaxseed oil) of the oleogel more or less interacted with sodium alginate, and different mass fractions of gels led to great differences in the crystal types of oleogel.Therefore, the addition of beeswax/FO characterized with different crystal types resulted in different properties of the films.As shown in Figure 1b, the addition of oleogel on the EAB (A), TS(B), HRC(C), and WVP(D) of the film is presented, respectively.The oleogel was a composite system.When the oleogel was added to the sodium alginate solution, the internal structure and mechanical properties of the film were changed.The EAB, TS, and HRC of the films did not change regularly with the increase of oleogels addition.When the oleogel content was 5%, the EAB, HRC, and WVP of the film had large values, while TS was the smallest.EAS and TS are important indicators for measuring the mechanical properties of packaging materials, and these two indicators are also important technical indicators affecting industrial applications [14].Fabra, Talens, and Chiralt [15] reported that the addition of oil to the film matrix is believed to cause a disruption in the biopolymer network which subsequently results in an increase in flexibility and a decline in tensile strength.However, in this study, there was no obvious regular increase or decrease in EAB and TS in oleogel-containing films, which indicated that the oleogel-containing films may restrain the deterioration of biopolymer matrix of sodium alginate-based films.In addition, WVP showed an overall decreasing trend.Especially in the range of 5 to 9%, the WVP was greatly decreased.The occurrence of this phenomenon was related to the addition of oleogel, which can increase the hydrophobicity of the film.According to Zhang et al. [16], adding ginger oil to the film can reduce the WVP of the film.As shown in Figure 1b, the addition of oleogel on the EAB (A), TS (B), HRC (C), and WVP (D) of the film is presented, respectively.The oleogel was a composite system.When the oleogel was added to the sodium alginate solution, the internal structure and mechanical properties of the film were changed.The EAB, TS, and HRC of the films did not change regularly with the increase of oleogels addition.When the oleogel content was 5%, the EAB, HRC, and WVP of the film had large values, while TS was the smallest.EAS and TS are important indicators for measuring the mechanical properties of packaging materials, and these two indicators are also important technical indicators affecting industrial applications [14].Fabra, Talens, and Chiralt [15] reported that the addition of oil to the film matrix is believed to cause a disruption in the biopolymer network which subsequently results in an increase in flexibility and a decline in tensile strength.However, in this study, there was no obvious regular increase or decrease in EAB and TS in oleogel-containing films, which indicated that the oleogel-containing films may restrain the deterioration of biopolymer matrix of sodium alginate-based films.In addition, WVP showed an overall decreasing trend.Especially in the range of 5 to 9%, the WVP was greatly decreased.The occurrence of this phenomenon was related to the addition of oleogel, which can increase the hydrophobicity of the film.According to Zhang et al. [16], adding ginger oil to the film can reduce the WVP of the film.

Effect of the Addition of Glycerol on EAB, TS, HRC, and WVP of the Film
The effect of the addition of glycerol on the EAB (A), TS(B), HRC(C), and WVP(D) of the films are presented in the Figure 1c.Glycerol, as a plasticizer, can break the original structure of polysaccharide polymer and form new hydrogen bonds, thus enhancing plasticity.According to Wang, Wang, Wang, and Wang [17], different plasticizers had different effects on the properties of different substrates, and the appropriate addition of glycerol can improve the mechanical and barrier properties of the film.This phenomenon may be due to the relatively small molecular weight of glycerol, which contains more hydroxyl groups so that it has a good hydrophilicity.Small molecules of plasticizer can penetrate into the internal structure of the film, forming a new intermolecular force, which makes the structure of the film become loose from dense [18].At the same time, plasticizer is a hydrophilic agent, which affects the evaporation of water in the film, and thus cause the thickness, structure, and features to change [19].

Comprehensive Score Analysis of Indicator Film Properties 2.2.1. Suitability Test
In this study, 3 × 3 groups of data (Table 1) were randomly selected for principal component analysis, and EAB, TS, HRC, and WVP values of the film were calculated as analysis objects.The Kaiser-Meyer-Olkin measure of sampling adequacy was used to justify the reliability of the comprehensive score of the film properties.If the value was closer to 1, the analysis was reasonable; if the value was less than 0.5, the analysis was unreasonable and useless [20].The Bartlett test of sphericity is a method to test the degree of correlation between various variables.When the significance level value is less than 0.05, the factor analysis may be useful.Therefore, analysis of the comprehensive score (0.677) via the Kaiser-Meyer-Olkin measure of sampling adequacy and Bartlett's test of sphericity was useful and appropriate (Table 2).The output result of the principal component distribution and scree plot are shown in Figure 2a,b.It can be seen from the load diagram that the four factors naturally clustered into two categories, V 1 , V 4, and V 2 had a large load on component 1, in which V 1 and V 4 were positively correlated with the principal component, while V 2 was negatively correlated with the principal component, and V 3 had a large load on component 2. Two factors of the eigenvalue curve had an eigenvalue greater than 0. The cumulative variance contribution rate of the two factors reached 89.408% (>85%), that is, the two factors extracted reflected the information of 89.408% of the original four indexes, as shown in Table 3
Via calculation, the effect of the ratio of beeswax/FO, the addition of oleogel, and the addition of glycerol on the comprehensive score of the film's characteristics are shown in Figure 3.When the ratio of beeswax/FO was 8%, the addition of oleogel was 5%, and the addition of glycerol was 30%, all of the comprehensive scores of the film in each single factor test group had the maximum value.According to this result, the subsequent response surface optimization experiment was carried out.
Gels 2024, 10, x FOR PEER REVIEW 7 of 22 weights of the four indicators of the indicator film (EAB, TS, HRC and WVP) were obtained as follows: 0.31, 0.24, 0.12, and 0.33, respectively, and the comprehensive score of the indicator film performance was obtained: S = 0.31P1 + 0.24P2 + 0.12P3 + 0.33P4.Via calculation, the effect of the ratio of beeswax/FO, the addition of oleogel, and the addition of glycerol on the comprehensive score of the film's characteristics are shown in Figure 3.When the ratio of beeswax/FO was 8%, the addition of oleogel was 5%, and the addition of glycerol was 30%, all of the comprehensive scores of the film in each single factor test group had the maximum value.According to this result, the subsequent response surface optimization experiment was carried out.

Results of Box-Behnken Design (BBD)
Based on single factor results, the ratio of beeswax/FO, the addition of oleogel, and the addition of glycerol were selected as the investigation factors, which were expressed as A, B and C respectively.The experimental design and results are shown in Table 4.The response surface plots (a,c,e) and contour plots (b,d,f) of the effects of the interaction of each factor on the comprehensive score are shown in Figure 4.The coefficients of the models were calculated, and the predicted model was as follows, respectively: (1) The effect of the ratio of beeswax/FO, the addition of oleogel, and the addition of glycerol on the comprehensive score of the film's characteristics.

Results of Box-Behnken Design (BBD)
Based on single factor results, the ratio of beeswax/FO, the addition of oleogel, and the addition of glycerol were selected as the investigation factors, which were expressed as A, B and C respectively.The experimental design and results are shown in Table 4.The response surface plots (a,c,e) and contour plots (b,d,f) of the effects of the interaction of each factor on the comprehensive score are shown in Figure 4.The coefficients of the models were calculated, and the predicted model was as follows, respectively: The results of ANOVA for the quadratic model are shown in Table 4 (Y), indicating that the model was highly appropriate for the prediction.The significance of each coefficient was determined via F-value and p-value.Generally, the larger the F value was, the smaller the p value was.Thus, it can be concluded from the F value of the Y model that the model was significant.The significant terms of the model characterized by the significance level also led to the lack of goodness of fit for the model.Moreover, the higher the coefficient of determination (R 2 ), the better the reasonability of the model.Overall, R 2 , the fraction of the variation of the response by the model, adjusted R 2 and regression p-value and lack of fit values > 0.05 all indicated that the model was well-fitted to the experimental data points [22].The adequate precision for the system was 7.546, which was greater than 4, therefore, the adequate signal was obtained [23].The response surface and contour maps of the pairwise interactions of factors A and B, A and C, and B and C are shown in Figure 4a, Figure 4b, Figure 4c, respectively.As can be seen from Figure 4a,b, the slope of the response surface was relatively gentle, indicating that the interaction between AB and AC was not significant (p > 0.05), while the slope of the response surface in Figure 4c was steeper, and the contours were distributed in a uniform and tight micro-oval shape, indicating that the interaction between BC was significant.The results of ANOVA were consistent with the result of Table 4 (P AB (0.2536 > 0.05), P AC (0.7352 > 0.05), and P BC (0.0402 < 0.05).The interaction between factors were detected in all the samples mostly in the order BC (the addition of oleogel and the addition of glycerol) > AB (the ratio of beeswax/FO and the addition of oleogel) > AC (the ratio of beeswax/FO and the addition of glycerol).

Verification Test
Based on the mathematical model, the optimal experimental conditions were as follows: the ratio of beeswax/FO was 7.807%, the addition of oleogel was 4.829%, the addition of glycerol was 31.088%, and the predicted Y of the film characteristics was 47.5725.Based on the above optimal parameters, the EAB, TS, HRC, and WVP of the film were 58.21 ± 1.58%, 25.11 ± 1.24 MPa, 57.66 ± 1.44%, and (0.82 ± 0.04) ×10 −5 g•cm/cm 2 •Kpa•h, respectively, and the actual value of the Y was 46.1624, which was close to the predicted value.The difference between the actual value and predicted value was not significant (p > 0.05).Therefore, the experiments showed that the model was reliable.

Analysis of Scanning Election Microscopy (SEM)
The surface morphology and cross section morphology of sodium alginate film with linseed oil/beeswax oleogel prepared under optimal experimental conditions were characterized via SEM (Figure 5).The result showed that the superficial structure of the film was uneven, grainy, and rough (Figure 5a).The film had a relatively uniform, continuous, and dense structure, and had tiny pores (Figure 5b,c).This may be due to the hydrophobicity of oleogels, which accumulate into hydrophobic clumps in the original hydrocolloid matrix, resulting in uneven mixing of the water phase and the oil phase [24].A heterogeneous surface and rough cross appearance were also reported by Yousuf et al. [3] for karaya gum-based films added with schisandra chinensis oil and its oleogel.
acterized via SEM (Figure 5).The result showed that the superficial structure of the film was uneven, grainy, and rough (Figure 5a).The film had a relatively uniform, continuous, and dense structure, and had tiny pores (Figure 5b,c).This may be due to the hydrophobicity of oleogels, which accumulate into hydrophobic clumps in the original hydrocolloid matrix, resulting in uneven mixing of the water phase and the oil phase [24].A heterogeneous surface and rough cross appearance were also reported by Yousuf et al. [3] for karaya gum-based films added with schisandra chinensis oil and its oleogel.The Decapterus maruadsi was packaged with two types of films, which was the sodium alginate film added with linseed oil/beeswax oleogel as the experimental group (EG), and the other was sodium alginate film only with added linseed oil as a control group (CG).It The Decapterus maruadsi was packaged with two types of films, which was the sodium alginate film added with linseed oil/beeswax oleogel as the experimental group (EG), and the other was sodium alginate film only with added linseed oil as a control group (CG).It can be seen from Figure 6a that the drip loss of EG and CG both increased with the extension of storage time at 25 • C and 37 • C (p < 0.05).The dripping loss of CG (0.30~0.75%) was always higher than that of EG (0.23~0.71%) during the 0~48 h at 25 • C storage.The changes at 37 • C were similar to those at 25 • C.This suggested that the addition of linseed oil/beeswax oleogel can significantly reduce the drip loss of the samples.This effect was superior to the addition of linseed oil alone, which may be related to the hydrophobic behavior of the added oil/oleogel [16].

Change of pH Value
The changes of pH of the samples during storage were shown in Figure 6b.The pH of EG and CG decreased first in the prestorage period, then increased significantly during the late storage period.When at 25 • C storage temperature, the pH value of CG varied from 6.29 to 7.14, and that of EG varied from 6.45 to 6.99.This phenomenon may be speculated that in the early stage of storage, bacteria used small molecules of organic matter to ferment fish and produce acid.With the progress of storage, proteins in fish will be further decomposed into a nitrogen-containing alkaline with small molecules under the action of bacteria [25].Similarly, the pH value of CG varied from 6.35 to 7.44, and that of EG varied from 6.39 to 6.99, indicating that the pH value of EG changed more steadily than that of CG, and the sodium alginate film added with linseed oil/beeswax oleogel can inhibit the degeneration of Decapterus maruadsi during storage more effectively.
sion of storage time at 25 °C and 37 °C (p < 0.05).The dripping loss of CG (0.30~0.75%) was always higher than that of EG (0.23~0.71%) during the 0~48 h at 25 °C storage.The changes at 37 °C were similar to those at 25 °C.This suggested that the addition of linseed oil/beeswax oleogel can significantly reduce the drip loss of the samples.This effect was superior to the addition of linseed oil alone, which may be related to the hydrophobic behavior of the added oil/oleogel [16].

Change of pH Value
The changes of pH of the samples during storage were shown in Figure 6b.The pH of EG and CG decreased first in the prestorage period, then increased significantly during the late storage period.When at 25 °C storage temperature, the pH value of CG varied from 6.29 to 7.14, and that of EG varied from 6.45 to 6.99.This phenomenon may be speculated that in the early stage of storage, bacteria used small molecules of organic matter to ferment fish and produce acid.With the progress of storage, proteins in fish will be further decomposed into a nitrogen-containing alkaline with small molecules under the action of bacteria [25].Similarly, the pH value of CG varied from 6.35 to 7.44, and that of EG varied from 6.39 to 6.99, indicating that the pH value of EG changed more steadily than that of CG, and the sodium alginate film added with linseed oil/beeswax oleogel can inhibit the degeneration of Decapterus maruadsi during storage more effectively.

Change of Total Volatile Basic Nitrogen (TVB-N)
TVB-N content is an important index to judge the freshness of meat.If the value of sample is greater than 25 mg/100 g, it is considered to be rotten meat [26].The change of TVB-N of EG and CG under different storage conditions are shown in Figure 6c.The TVB-N value of all tested samples increased with the extension of storage at 25 • C and 37 • C (p < 0.05).After 48 h storage at 25 • C, the TVB-N value of CG increased to 26.35 mg/100 g, while that of EG increased to 24.48 mg/100 g.During 12 h storage at 36 • C, the TVB-N value of CG increased to 30.16 mg/100 g, while that of EG increased to 27.12 mg/100 g.Under the same storage conditions, the TVB-N value of CG increased faster and higher than EG, which indicated that the addition of linseed oil/beeswax oleogel can effectively inhibit the deterioration of proteins of Decapterus maruadsi.

Change of Thiobarbituric Acid Reactive Substance (TBARS)
As shown in Figure 6d, the TBARS of EG and CG increased significantly with the extension of storage (p < 0.05).The two-group increased significantly during the period of 24 h to 36 h at 25 • C, as well as the storage of 2 h to 4 h at 37 • C. CG changed more rapidly than EG during storage.Similar results were reported by Hamdani, et al. [27] and Yousuf [3]; the addition of the oleogel to the edible film can make the film have a more significant antioxidant effect, and the effect of addition in the form of oleogel or only pure oil was quite different.The stronger the antioxidant properties were, the slower the deterioration of fats and proteins.Thus, the novel oleogel added to the film can enhance the preservation effect of the film on fish products, improve the quality of Decapterus maruadsi during storage, and extend the shelf-life.

Correlation Analysis of the Change of Each Index
In order to screen suitable indicators for product shelf-life prediction, the relationship between various indicators of Decapterus maruadsi preserved via the sodium alginate films were analyzed, and the correlation analysis between various indicators under different conditions was established.As shown in the Figure 7, the Pearson correlation coefficient (r) varied between −1 and 1, and the degree of correlation was better explained using the color scale.In the figure, TVB-N was positively correlated with drip loss, pH and TBARS, while it negatively correlated with the effect of PUFA.In addition, the correlation between TVB-N and various indicators was high, and most of them were greater than 0.9.In view of this, TVB-N was selected to construct a shelf-life prediction model for Decapterus maruadsi preserved via the sodium alginate films.In order to screen suitable indicators for product shelf-life prediction, the relationship between various indicators of Decapterus maruadsi preserved via the sodium alginate films were analyzed, and the correlation analysis between various indicators under different conditions was established.As shown in the Figure 7, the Pearson correlation coefficient (r) varied between −1 and 1, and the degree of correlation was better explained using the color scale.In the figure, TVB-N was positively correlated with drip loss, pH and TBARS, while it negatively correlated with the effect of PUFA.In addition, the correlation between TVB-N and various indicators was high, and most of them were greater than 0.9.In view of this, TVB-N was selected to construct a shelf-life prediction model for Decapterus maruadsi preserved via the sodium alginate films.The fitting linear regression equation, regression coefficient R 2, and rate constant k values can be seen from Table 6.The multiple correlation coefficient R 2 of the regression equations established at storage temperatures of 25 • C (298.15 K) and 37 • C (310.15 K) were both greater than 0.90, indicating that the regression equation had a high degree of fit.At the same time, the obtained rate constant k values were 0.43903 (EG at 25 • C), 1.98921 (EG at 37 • C), 0.48708 (CG at 25 • C), and 2.20737 (CG at 25 • C), respectively.The linear equation of EG y = −11.64310015x+ 38.22796 was obtained via plotting the inverse 1/T of the storage temperature with lnK.The activation energy Ea of the peroxide value was 9.6805 × 10 4 J/mol and the prefactor k 0 was 4.00122 × 10 16 .On this basis, the Arrhenius equation of EG, the kinetic equation and the shelf-life prediction equation between the peroxidation rate constant k and the storage temperature T during the storage of Decapterus maruadsi preserved via the sodium alginate films under different storage conditions were established as follows: Arrhenius equation: First-order dynamic equation: Similarly, the linear equation of CG y = −11.64466872x+ 38.33708 was obtained via plotting the inverse 1/T of the storage temperature with lnK.The activation energy Ea of the peroxide value was 9.6818 × 10 4 J/mol and the prefactor k 0 was 4.46254 × 10 16 .On this basis, the Arrhenius equation of CG, the kinetic equation and the shelf-life prediction equation between the peroxidation rate constant k and the storage temperature T during the storage of Decapterus maruadsi preserved via the sodium alginate films under different storage conditions were established as follows: Arrhenius equation: According to the shelf-life prediction equation, when the storage temperature, initial TVB-N value, and final TVB-N value were determined, the storage time of Decapterus maruadsi preserved via the sodium alginate films under different storage conditions under a certain temperature condition can be calculated, so that its shelf-life can be predicted.In addition, the storage temperature, initial TVB-N value, and storage time of Decapterus maruadsi preserved via the sodium alginate films under different storage conditions can also be used to calculate the final TVB-N value after a certain period of storage at the determined storage temperature, so as to monitor the change of its quality.

Prediction of Kinetic Model of TVB-N value of Decapterus Maruadsi Preserved via the Sodium Alginate Films under Different Storage Conditions
According to the national limited standard (the TVB-N value was 25 mg/100 g), the predicted shelf-life of EG at 25 • C and 37 • C was 56.6365 (approx.56.6 h) and 12.5000 d (approx.12.5 h).The predicted shelf-life of CG at 25 • C and 37 • C was 42.7086 (approx.42.7 h) and 9.4241 h (approx.9.4 h), which may provide the theoretical references for the safe storage of products.On the whole, the Decapterus maruadsi preserved via the sodium alginate films added with linseed oil/beeswax oleogel had good storage resistance, and the Decapterus preserved with sodium alginate film added with linseed oil/beeswax oleogel had a longer shelf-life than that preserved with sodium alginate film added only with linseed oil (Table 6).

Conclusions
The novel oleogel can be successfully applied to the edible film, which can improve the barrier property and texture characteristics of the film.When the ratio of beeswax/FO was 7.807%, the addition of oleogel was 4.829%, and the addition of glycerol was 31.088%, the comprehensive score of the film characteristics had the maximum, and the EAB, TS, HRC, and WVP of the film were 58.21 ± 1.58%, 25.11 ± 1.24 MPa, 57.66 ± 1.44%, and (0.82 ± 0.04) × 10 −5 g•cm/cm 2 •KPa•h, respectively.In comparison to control, the sodium alginate films incorporated with linseed oil/beeswax oleogel can effectively inhibit the quality deterioration of Decapterus maruadsi, which had a longer shelf-life.The preservation effect of the film incorporated with linseed oil/beeswax oleogel was better than that of film incorporated only with linseed oil.In a word, linseed oil/beeswax oleogel can be used to develop novel types of biodegradable films, which can reduce water vapor permeability, keep excellent mechanical properties, and effectively extend the shelf-life of Decapterus maruadsi.weight) were purchased from RT-Mart (Zhangzhou, Fujian, China), and transported to the laboratory alive.

Oleogel Preparation
Oleogel was prepared with yellow beeswax as the oleogelator at a concentration of 2~10%, corresponding to the FO.The beeswax was accurately weighed and dispersed in FO.Then, heat the mixture at 80 • C in a water bath (DF-101S, Shanghai Lichen Bangxi Instrument Technology Co., Ltd., Shanghai, China), and stir gently for 20 min to blend well.Then, cool the mixture to room temperature to get oleogel [3].

Oleogel Preparation
Based on the preliminary experiments, 1.5% sodium alginate was considered to be the appropriate concentration for preparing films.Accurately weigh the sodium alginate, and dissolve in distilled water; the mixture was kept in a hot water bath for 30 min at 80 • C. Glycerol was added to the mixture as a plasticizer at a concentration of 15~35% of the weight of film.Add the oleogel at different levels (1~9%), and stir the mixture at 1000 rpm for 20 min at 60 • C on a magnetic stirrer (DF-101S, Shanghai Lichen Bangxi Instrument Technology Co., Ltd., Shanghai, China).The mixture was cooled and treated via ultrasound for 20 min to remove air bubbles (KQ3200E, Xinzhi biotechnology Co., Ltd., Ningbo, China).Take 25 g of the final film liquid mixture and pour it onto a plate with a diameter of 90 mm and dry it in a hot air stove at 30 • C for 24 h.Before analysis, the film was stripped from the plate and stored in a dryer containing saturated sodium bromide solution for at least 48 h.

Single Factor Experiment
Investigate the effects of three single factors (the ratio of beeswax/FO (2~10%), the addition of oleogel (1~9%), and the addition of glycerol (15~35%) on the EAB, TS, HRC, and WVP of the film.The thickness of films was tested with a digital micrometer (BMD-25D, Mitutoyo Mfg.Co., Ltd., Kawasaki, Japan).Five random regions were selected and the average values was calculated.

Mechanical Properties
The TS and EAB were determined via the texture analyzer (CT3-10K, American Bollerfly Company, Middleboro, MA, USA).The films were cut into strips of 8.0 cm × 2.0 cm.The initial clamping distance was 60 mm and the crosshead velocity was 50 mm/min [28].

HRC
Take an appropriate amount of edible film and dissolve it with water to prepare the 0.8% film solution.The 50 µL sample solution was accurately removed, and 50 µL FeSO 4 (6 mmol/L) and 100 µL H 2 O 2 (6 mmol/L) were added, then fully shaken and placed for 10 min.Add 50 µL salicylic acid (6 mmol/L), shake with partial vibration, and place at room temperature for 30 min.The absorbance was tested at 510 nm.The HRC was calculated according to Formula (8): where A 0 was the light absorption value of the blank tube, A i was the light absorption value of the sample tube.
and washed with tap water.The fish was collected and stored in ice for 24 h for further treatment.Before experimentation, the fish was cut into 2 cm × 2 cm × 0.2 cm fillets.The methodological protocol of the current study was approved by the welfare and ethics committee in animal experiment of College of Biological Science and Technology, Minnan Normal University.The samples were stored at 25 • C for 0, 12, 24, 36, and 48 h, and at 37 • C for 0, 2, 4, 6, and 8 h, respectively.The changes of water content, TVB-N value, pH value, TBARS value, and fatty acid composition were determined at each time period.The Decapterus maruadsi preserved with film added with oleogel was the experimental group (EG), and the fish preserved with film added only with FO was the control group (CG).The content of TVB-N was determined via the Kjeldahl method (Kjeltec 8400, FOSS, Hiller) [31].The result was expressed as mg of nitrogen per 100 g of sample.

pH Value
The calibrated portable pH meter (Testo735-2, Testo AG, Baden-Wurttemberg, Germany) was used to test the pH value.Each sample was measured at three different locations and the results were expressed as the average of the three trials [32].

TBARS Analysis
Add 45 mL of frozen 20% (w/v) trichloroacetic acid (TCA) to 5.0 g Decapterus maruadsi samples, extract at room temperature for about 1 h, then centrifuge at 4000× g for 15 min, add 5 mL of supernatant to 5 mL of 0.02 M TBA, heat at 95 • C for 30 min, and cool to room temperature with tap water.TBARS value was expressed as mg of malondialdehyde (MDA) per kg of sample.

Fatty Acid Composition
The fatty acid extraction, methyl ester reaction and gas chromatographic determination were referred to as in Xue [33].

Arrhenius Equation
The Arrhenius equation can reflect the relationship between the change rate constant (k) and the thermodynamic temperature (T).When the rate constant under different temperature conditions is calculated, a line with a slope of −Ea/R and a linear equation with

2. 1 . 3 .
Effect of the Addition of Glycerol on EAB, TS, HRC, and WVP of the Film The effect of the addition of glycerol on the EAB (A), TS(B), HRC(C), and WVP(D) of the films are presented in the Figure1c.Glycerol, as a plasticizer, can break the original structure of polysaccharide polymer and form new hydrogen bonds, thus enhancing plas-

Figure 1 .
Figure 1.Effect of ratio of beeswax/FO (a), addition of oleogel (b), and addition of glycerol (c) on the EAB, TS, HRC, and WVP of the film, respectively.((a): The effect of the ratio of beeswax/FO on the EAB (A), TS (B), HRC (C), and WVP (D) of the film.(b): The effect of the addition of oleogel on the EAB (A), TS (B), HRC (C), and WVP (D) of the film.(c): The effect of the addition of glycerol on the EAB (A), TS (B), HRC (C), and WVP (D) of the film.)2.1.2.Effect of the Addition of Oleogel on the EAB, TS, HRC, and WVP of the Film

Figure 2 .
Figure 2. The analysis of principal component distribution (a) and scree plot (b).

Figure 2 .
Figure 2. The analysis of principal component distribution (a) and scree plot (b).

Figure 3 .
Figure 3. the effect of the ratio of beeswax/FO, the addition of oleogel, and the addition of glycerol on the comprehensive score of the film's characteristics.

Figure 4 .Table 4 .
Figure 4. Response surface plots (a,c,e) and contour plots (b,d,f) of the effects of the interaction of various factors on the comprehensive score.Table 4. Experimental design plan, results, and variance analysis of response surface experiment.TestThe Ratio of Beeswax/FO (A)

Figure 4 .
Figure 4. Response surface plots (a,c,e) and contour plots (b,d,f) of the effects of the interaction of various factors on the comprehensive score.

Figure 7 .
Figure 7.The correlation analysis of the change of each index.(Figure (a): the result of EG at 25 °C; Figure (b): the result of CG at 25 °C; Figure (c): the result of EG at 37 °C; Figure (d): the result of EG at 37 °C.The correlations were represented by different stars shadows.) 2.7.Establishment and Verification of the Kinetic Model of Quality Change in Decapterus Maruadsi Preserved via the Sodium Alginate Films 2.7.1.Regression Equation of TVB-N of Decapterus Maruadsi Preserved via the Sodium Alginate Films under Different Storage Conditions

Figure 7 .
Figure 7.The correlation analysis of the change of each index.((a): the result of EG at 25 • C; (b): the result of CG at 25 • C; (c): the result of EG at 37 • C; (d): the result of EG at 37 • C. The correlations were represented by different stars shadows).

4. 8 .
Establishment of Kinetic Model of Decapterus Maruadsi during Storage 4.8.1.First-Order Kinetic EquationMost of the changes in food processing follow the zero-order or first-order reaction model[34].The first-order reaction kinetics equation is shown in Equation (14):A = A 0 ekt(14)A: the quality index values at t d; A 0 : the quality index values at 0 d; K: the change rate constant of storage quality index; T: the storage time of the sample (d).

Table 1 .
Test data of contribution rate via principal component analysis.

Table 2 .
KMO and Bartlett spherical test for the dimension reduction model of edible film characteristics index.

Table 3 .
Eigenvalues and cumulative variance contribution rates of the related components.

Table 4 .
Experimental design plan, results, and variance analysis of response surface experiment.

Table 5 .
Change of fatty acids composition of Decapterus maruadsi during storage at 25 • C and 37 • C.

Table 5 .
Cont.Note.Values were mean ± SD (n = 3).Values of EG and CG in a row with different superscript lowercase letters (a-e) differed significantly (p < 0.05).Establishment and Verification of the Kinetic Model of Quality Change in Decapterus Maruadsi Preserved via the Sodium Alginate Films 2.7.1.Regression Equation of TVB-N of Decapterus Maruadsi Preserved via the Sodium Alginate Films under Different Storage Conditions

Table 6 .
Regression equations for TVB-N and shelf-life of Decapterus maruadsi at different storage temperatures.