Adsorption Characteristics of Modified Bamboo Charcoal on Cu(II) and Cd(II) in Water

With the development of industry in recent years, heavy metal contamination in water and substrate, which may pose a serious threat to human health if left untreated, has attracted increasing attention. Biochar is commonly used as an adsorbent/immobilizer for heavy metals in water and substrates because of its wide range of raw materials, low production cost, and good adsorption performance. In this paper, we selected abundant Moso bamboo as the raw material to make biochar (bamboo charcoal), modified bamboo charcoal using different methods to find the modified product with the best adsorption effect, assessed the adsorption performance of modified bamboo charcoal on Cu(II) and Cd(II) in solution, and investigated the effects of the solution concentration, adsorption time, pH, and temperature on the adsorption effect of KAM500-400-3 on Cu(II) and Cd(II). The effect of the solution concentration, adsorption time, pH, and temperature on the adsorption effect of KAM500-400-3 on Cu(II) and Cd(II) was investigated, and the adsorption mechanism of KAM500-400-3 on heavy metals Cu(II) and Cd(II) was analyzed by fitting the adsorption kinetics, adsorption isotherms, and adsorption thermodynamics. The adsorption/fixation characteristics of modified bamboo charcoal on heavy metals Cu(II) and Cd(II) in water and substrate were investigated. This study aimed to identify an effective material for the treatment of heavy metals in water and substrates and provide a reference for their application in practical engineering.


Introduction
With the continuous improvement in people's day-to-day lives and industry production levels, the pollution of water and sediment by heavy metals is also increasing. At the same time, various sources of heavy metals are also increasing, mainly from industrial production such as the machinery processing industry, steelmaking, the nonferrous metal smelting industry, etc. In addition, automobile emissions, the disposal of waste batteries, and the abuse of agricultural fertilizers in daily life can cause serious heavy metal pollution in river bottom mud [1,2].
The composition of surface river and lake sediments is complex, mainly including clay, sediment, organic matter, and various mineral bodies [3,4]. Heavy metals in sediment mainly originate from polluted water bodies, and a series of transformation and migration processes such as adsorption-desorption, precipitation-dissolution, complexationdecomplexation, ion exchange, and redox occur between the sediment and the water body [5].
Because of their slow mobility and long residence time, heavy metals in the sediment are not degraded easily by microorganisms [6], and if they are not treated in time, they will become a "new source of pollution", polluting the water body twice, poisoning the plants and animals in the water, and then further endangering human life and health through transmission via the food chain [7].
Prolonged exposure to heavy metal ions can cause serious harm to the human body, such as affecting the activity of enzymes, the nervous system, and some organs with

Main Experimental Apparatus and Materials
The selected biomass material in this experiment is Phyllostachys pubescens, which is from a bamboo forest in Jurong, Jiangsu Province. Table 2 lists the experimental instruments, instrument specifications, and applications required for this experiment. Table 3 lists the reagents, specifications, and purity required for this experiment. The water used in this experiment is ultrapure water (the resistivity is 18.25 MQ·cm) [32]. Environmental scanning electron microscope-energy spectrometer QUANTA200 Obtain sample surface morphology and micro area elements 10 Specific surface area analyzer ASAP200 Aperture structure of analytical sample 11 Fourier transform infrared spectrometer VERTEX80v Analysis of sample surface 12 Constant-temperature water bath (HH-2) HH-2 Heated sample

Preparation Method of Bamboo Charcoal
Moso bamboo, retrieved from a bamboo forest in Jurong, was washed with tap water and deionized water and dried naturally. The Moso bamboo was dried in a constanttemperature drying oven at 80 • C after being cut into small pieces with a chainsaw [33]. The dried bamboo pieces were cut into strips with branch shears and ground to a powder with a 100 mesh sieve to obtain 100 mesh bamboo powder in a self-sealing bag. A quartz tube was filled with 100 g of 100 mesh bamboo powder and placed in a tube furnace. We set the charring temperature of the tube furnace to 400 • C, 500 • C, 600 • C, or 700 • C. The heating procedure was 10 • C per minute, and the temperature was kept at the set temperature for an hour and then gradually cooled down [34]. After the temperature was lowered to room temperature, the Moso bamboo biochar was taken out and stored in sealed bags, which were labeled BC400, BC500, BC600, and BC700 according to the charring temperature.
Please see the Preparation methods of modified bamboo charcoal, Analysis of surface morphology and element distribution of bamboo charcoal, Specific surface area determination, FT-IR analysis, Adsorption experiments of bamboo charcoal and modified bamboo charcoal on heavy metals Cu(II) and Cd(II) in the Supplementary Material.

Effect of Charring Temperature
The effect of charring temperature on the ability of bamboo char to adsorb heavy metals Cu(II) and Cd(II) is shown in Figure 1. The bamboo charcoal fired at the charring temperatures of 400 • C, 500 • C, 600 • C, and 700 • C was recorded as BC400, BC500, BC600, and BC700, respectively. The initial concentrations of heavy metals Cu(II) and Cd(II) in the experiments were all 50 mg/L, the pH was 6, and the volumes added were all 120 mL at an ambient temperature of 25 • C. The adsorption amounts of BC400, BC500, BC600, and BC700 were 1.79 mg/g, 2.48 mg/g, 2.53 mg/g, and 2.56 mg/g for Cu(II) and 2.89 mg/g, 3.96 mg/g, and 4.01 mg/g for Cd(II), respectively. The adsorption amounts of BC400 were significantly smaller than those of BC500, BC600, and BC700, and the adsorption amounts of the latter three were not significantly different. The results showed that when the charring temperature was lower, the adsorption amounts of Cu(II) and Cd(II) were smaller, and when the charring temperature was higher than 500 • C, the adsorption amounts of bam-boo char increased, but the increment was smaller. The reason behind this phenomenon is Toxics 2022, 10, 787 5 of 24 that, with the increasing carbonization temperature, the functional groups on the surface of bamboo charcoal will be more evenly distributed. In addition, the increase in carbonization temperature will create a more abundant pore structure for activated carbon, and the increase in the specific surface area of carbon will help to increase the adsorption capacity. The adsorption capacities of BC600 and BC700 were only 2.02% and 3.22% higher than those of BC500 for heavy metal Cu, and 1.26% and 4.04% higher than those of BC500 for heavy metal Cd. Considering the time cost and energy consumption for the preparation of the three in the tube furnace, BC500 was selected for the following modification experiments.
Toxics 2022, 10, x FOR PEER REVIEW 6 of 28 consumption for the preparation of the three in the tube furnace, BC500 was selected for the following modification experiments.

Effects of Different Modification Methods
(1) KOH-modified bamboo charcoal The ability of KOH-modified bamboo charcoal to adsorb Cu(II) and Cd(II) at different concentrations is shown in Figure 2. KOH-modified bamboo charcoal was labeled as KBC500-0.5, KBC500-1, KBC500-2, and KBC500-4 in descending order according to the concentration of KOH solution mixed with it: 0.5 mol/L, 1 mol/L, 2 mol/L, or 4 mol/L. Heavy metal Cu(I) adsorption amounts of KBC500-0.5, KBC500-1, KBC500-2, and KBC500-4 were 3.96 mg/g, 4.18 mg/g, 6.60 mg/g, and 7.27 mg/g, respectively, whereas heavy metal Cd(II) adsorption amounts were 7.00 mg/g, 10.51 mg/g, and 10.51 mg/g, respectively. The adsorption amounts of unmodified BC-500 for Cu(II) and Cd(II) were 2.48 mg/g and 3.96 mg/g, respectively, which could be attributed to the stronger adsorption capacity of KOH-modified carbon for heavy metals Cu(II) and Cd(II). The specific surface area of bamboo char increased after alkali treatment, as did the type and number of oxygen-containing functional groups on the surface, enhancing its effect on the adsorption of heavy metals Cu(II) and Cd(II) [35]. The growth rate of the adsorption capacity of charcoal reached its maximum when the concentration of KOH was 2 mol/L. The growth efficiency of the adsorption capacity of charcoal for Cu(II) decreased when the concentration was greater than 2 mol/L, and the adsorption amount of Cd(II) decreased as well, probably because the KOH solution neutralized the acidic oxygencontaining functional groups on the surface of BC500, resulting in a decrease in acidic oxygen-containing functional groups and an increase in basic oxygen-containing functional groups [36][37][38][39]. The KOH solution will cause the etching effect of BC500: as its concentration increases, new pores will form on the surface, the original pores on the surface will gradually increase, and the specific surface area will also increase [40]. However, when the alkali concentration is too high, the acidic oxygen-containing functional groups on the surface of BC500 are consumed, resulting in a slow increase or even a decrease in the specific surface area of BC500 [41][42][43]. In summary, KBC500-2 has

(1) KOH-modified bamboo charcoal
The ability of KOH-modified bamboo charcoal to adsorb Cu(II) and Cd(II) at different concentrations is shown in Figure 2. KOH-modified bamboo charcoal was labeled as KBC500-0.5, KBC500-1, KBC500-2, and KBC500-4 in descending order according to the concentration of KOH solution mixed with it: 0.5 mol/L, 1 mol/L, 2 mol/L, or 4 mol/L. Heavy metal Cu(I) adsorption amounts of KBC500-0.5, KBC500-1, KBC500-2, and KBC500-4 were 3.96 mg/g, 4.18 mg/g, 6.60 mg/g, and 7.27 mg/g, respectively, whereas heavy metal Cd(II) adsorption amounts were 7.00 mg/g, 10.51 mg/g, and 10.51 mg/g, respectively. The adsorption amounts of unmodified BC-500 for Cu(II) and Cd(II) were 2.48 mg/g and 3.96 mg/g, respectively, which could be attributed to the stronger adsorption capacity of KOH-modified carbon for heavy metals Cu(II) and Cd(II). The specific surface area of bamboo char increased after alkali treatment, as did the type and number of oxygencontaining functional groups on the surface, enhancing its effect on the adsorption of heavy metals Cu(II) and Cd(II) [35]. The growth rate of the adsorption capacity of charcoal reached its maximum when the concentration of KOH was 2 mol/L. The growth efficiency of the adsorption capacity of charcoal for Cu(II) decreased when the concentration was greater than 2 mol/L, and the adsorption amount of Cd(II) decreased as well, probably because the KOH solution neutralized the acidic oxygen-containing functional groups on the surface of BC500, resulting in a decrease in acidic oxygen-containing functional groups and an increase in basic oxygen-containing functional groups [36][37][38][39]. The KOH solution will cause the etching effect of BC500: as its concentration increases, new pores will form on the surface, the original pores on the surface will gradually increase, and the specific Toxics 2022, 10, 787 6 of 24 surface area will also increase [40]. However, when the alkali concentration is too high, the acidic oxygen-containing functional groups on the surface of BC500 are consumed, resulting in a slow increase or even a decrease in the specific surface area of BC500 [41][42][43]. In summary, KBC500-2 has the best adsorption capacity for heavy metals Cu(II) and Cd(II) when the KOH concentration is 2 mol/L.  (2) KOH-activated bamboo charcoal ① Charcoal-to-alkali ratio The adsorption amounts of Cu(II) and Cd(II) adsorbed by KOH-modified carbon with different alkali-carbon ratios are shown in Figure 3. For 700-3, the adsorption amounts were 14.45 mg/g, 20.23 mg/g, 23.73 mg/g, and 28.70 mg/g for Cu(II), and 17.51 mg/g, 20.05 mg/g, 20.39 mg/g, and 22.65 mg/g for Cd(II), respectively, which shows that when the ratio of KOH to BC500 is larger, the effect of KOH activation modification is good. This may be because, when the alkali-to-carbon ratio is small, KOH only reacts with the surface phase of BC500 and cannot form a large number of micropores and mesopores [44]. When the alkali-to-carbon ratio is further expanded, KOH can enter the graphite layer of the carbon and react with the inner carbon, consuming a large amount of carbon to produce carbon monoxide and hydrogen, which makes the pore volume of the carbon and the number of mesopores and micropores increase. In summary, when the alkali carbon ratio is 3:1, the best adsorption effects for Cu(II) and Cd(II) are obtained. (2) KOH-activated bamboo charcoal 1 Charcoal-to-alkali ratio The adsorption amounts of Cu(II) and Cd(II) adsorbed by KOH-modified carbon with different alkali-carbon ratios are shown in Figure 3. For 700-3, the adsorption amounts were 14.45 mg/g, 20.23 mg/g, 23.73 mg/g, and 28.70 mg/g for Cu(II), and 17.51 mg/g, 20.05 mg/g, 20.39 mg/g, and 22.65 mg/g for Cd(II), respectively, which shows that when the ratio of KOH to BC500 is larger, the effect of KOH activation modification is good. This may be because, when the alkali-to-carbon ratio is small, KOH only reacts with the surface phase of BC500 and cannot form a large number of micropores and mesopores [44]. When the alkali-to-carbon ratio is further expanded, KOH can enter the graphite layer of the carbon and react with the inner carbon, consuming a large amount of carbon to produce carbon monoxide and hydrogen, which makes the pore volume of the carbon and the number of mesopores and micropores increase. In summary, when the alkali carbon ratio is 3:1, the best adsorption effects for Cu(II) and Cd(II) are obtained.  ② Temperature The amounts of Cu(II) and Cd(II) adsorbed by KOH-activated modified bamboo charcoal at different activation temperatures are shown in Figure 4. The adsorption amounts of Cu(II) and Cd(II) were 29.79 mg/g, 19.97 mg/g, 20.20 mg/g, and 20.20 mg/g, respectively, when the activation temperature was 400 °C, 500 °C, 600 °C, and 700 °C. The adsorption amounts for Cu(II) were 29.79 mg/g, 19.97 mg/g, 20.20 mg/g, and 28.70 mg/g, and for Cd(II), they were 27.20 mg/g, 16.69 mg/g, 17.59 mg/g, and 22.65 mg/g, respectively,  The amounts of Cu(II) and Cd(II) adsorbed by KOH-activated modified bamboo charcoal at different activation temperatures are shown in Figure 4. The adsorption amounts of Cu(II) and Cd(II) were 29.79 mg/g, 19.97 mg/g, 20.20 mg/g, and 20.20 mg/g, respectively, when the activation temperature was 400 • C, 500 • C, 600 • C, and 700 • C. The adsorption amounts for Cu(II) were 29.79 mg/g, 19.97 mg/g, 20.20 mg/g, and 28.70 mg/g, and for Cd(II), they were 27.20 mg/g, 16.69 mg/g, 17.59 mg/g, and 22.65 mg/g, respectively, when the activation temperature was 400 • C. The adsorption of Cd(II) and Cu(II) was the highest. This may be due to the fact that increasing the activation temperature at a high alkali-to-carbon ratio causes significant ablation of the carbon, which reduces the active carbon spots on the surface and consequently decreases the adsorption performance of the carbon [45,46]. A similar phenomenon has been observed, i.e., the saturation adsorption capacity of the char is roughly negatively correlated with the activation temperature when the alkali-to-carbon ratio is too high, and the larger the alkali-to-carbon ratio, the more obvious the phenomenon is.

② Temperature
The amounts of Cu(II) and Cd(II) adsorbed by KOH-activated modified bamboo charcoal at different activation temperatures are shown in Figure 4. The adsorption amounts of Cu(II) and Cd(II) were 29.79 mg/g, 19.97 mg/g, 20.20 mg/g, and 20.20 mg/g, respectively, when the activation temperature was 400 °C, 500 °C, 600 °C, and 700 °C. The adsorption amounts for Cu(II) were 29.79 mg/g, 19.97 mg/g, 20.20 mg/g, and 28.70 mg/g, and for Cd(II), they were 27.20 mg/g, 16.69 mg/g, 17.59 mg/g, and 22.65 mg/g, respectively, when the activation temperature was 400 °C. The adsorption of Cd(II) and Cu(II) was the highest. This may be due to the fact that increasing the activation temperature at a high alkali-to-carbon ratio causes significant ablation of the carbon, which reduces the active carbon spots on the surface and consequently decreases the adsorption performance of the carbon [45,46]. A similar phenomenon has been observed, i.e., the saturation adsorption capacity of the char is roughly negatively correlated with the activation temperature when the alkali-to-carbon ratio is too high, and the larger the alkali-to-carbon ratio, the more obvious the phenomenon is. The ability of HNO 3 -modified charcoal to adsorb Cu(II) and Cd(II) at different concentrations is shown in Figure 5. HNO 3 -modified bamboo charcoal is labeled as HBC500-5, HBC500-10, HBC00-20, and HBC500-30, in descending order of the mass fraction of HNO 3 solution mixed with it at 5%, 10%, 20%, and 30%, respectively. The adsorption amounts of HBC500-5, HBC500-10, HBC00-20, and HBC500-30 for heavy metal Cu(II) were 3.71 mg/g, 4.59 mg/g, 7.03 mg/g, and 8.81 mg/g, respectively, and the adsorption amounts of heavy metal Cd(II) were 4.48 mg/g, 5.06 mg/g, 9.07 mg/g, and 12.07 mg/g, respectively. The adsorption capacities of unmodified BC500 for Cu(II) and Cd(II) were 2.48 mg/g and 3.96 mg/g, respectively, and the adsorption capacities of HNO3-modified bamboo charcoal increased with increasing HNO3 mass fraction. The adsorption capacity of bamboo charcoal for Cu(II) and Cd(II) gradually increased, and the strongest adsorption capacity was achieved when the mass fraction of HNO 3 was 30%, i.e., HBC500-30. This may be due to the fact that the number of oxygenated acidic functional groups, such as carboxyl groups, on the surface of BC500 gradually increased with the increase in the mass fraction of HNO 3 and it was also experimentally confirmed that the porosity and specific surface area of the carbon increased significantly when the mass fraction of HNO 3 was 30%. strongest adsorption capacity was achieved when the mass fraction of HNO3 was 30%, i.e., HBC500-30. This may be due to the fact that the number of oxygenated acidic functional groups, such as carboxyl groups, on the surface of BC500 gradually increased with the increase in the mass fraction of HNO3 and it was also experimentally confirmed that the porosity and specific surface area of the carbon increased significantly when the mass fraction of HNO3 was 30%.

Morphological Analysis
The surface morphologies of bamboo charcoal, as well as modified bamboo charcoal, are shown in Figure 6. Figure 6a-d shows the surface morphologies of unmodified BC500, KBC500-2-, HBC500-30-, and KAM500-400-3-modified charcoal, respectively. As can be seen from Figure 6, the surface of unmodified BC500 is smoother, and the char is mainly tubular in shape with a relatively intact structure. The surface of KBC-500-2 modified by KOH alkali obviously became very rough; a large number of round and oval collapses

Morphological Analysis
The surface morphologies of bamboo charcoal, as well as modified bamboo charcoal, are shown in Figure 6. Figure 6a-d shows the surface morphologies of unmodified BC500, KBC500-2-, HBC500-30-, and KAM500-400-3-modified charcoal, respectively. As can be seen from Figure 6, the surface of unmodified BC500 is smoother, and the char is mainly tubular in shape with a relatively intact structure. The surface of KBC-500-2 modified by KOH alkali obviously became very rough; a large number of round and oval collapses appeared, and the distribution was more uniform. The morphology was similar to that of honeycomb, which indicated that KOH would cause the char to generate a pore structure or even break the char structure [47][48][49]. The shape of HBC500-30 modified by HNO 3 is similar to that of unmodified BC500-parallel tubular bundles-but the surface appears scaly and relatively rough. The surface of KAM500-400-3 after KOH activation showed a lot of collapse and unevenness; its structure was far from that of BC500, and large pores were clearly visible on the cross section.
Toxics 2022, 10, x FOR PEER REVIEW 10 of 28 appeared, and the distribution was more uniform. The morphology was similar to that of honeycomb, which indicated that KOH would cause the char to generate a pore structure or even break the char structure [47][48][49]. The shape of HBC500-30 modified by HNO3 is similar to that of unmodified BC500-parallel tubular bundles-but the surface appears scaly and relatively rough. The surface of KAM500-400-3 after KOH activation showed a lot of collapse and unevenness; its structure was far from that of BC500, and large pores were clearly visible on the cross section.

Measurement of Specific Surface Area
The porous structure parameters of bamboo charcoal and modified bamboo charcoal are shown in Table 4. Generally speaking, the specific surface area, total pore capacity, and average pore diameter of carbon will increase after acid-base modification, but the detected results are inconsistent with the expected situation. These parameters, KBC500-2 and HBC500-30, are lower than the unmodified BC500 in destroying the structure of the carbon surface, which is the same as the SEM. The specific surface area of KAM500-400-3 is 1.45 times that of BC500, the total pore capacity is 4.57 times that of BC500, and the average aperture is 5.16 times that of BC500. These values are also much higher than the porous structural parameters of bamboo charcoal and modified bamboo charcoal. The

Measurement of Specific Surface Area
The porous structure parameters of bamboo charcoal and modified bamboo charcoal are shown in Table 4. Generally speaking, the specific surface area, total pore capacity, and average pore diameter of carbon will increase after acid-base modification, but the detected results are inconsistent with the expected situation. These parameters, KBC500-2 and HBC500-30, are lower than the unmodified BC500 in destroying the structure of the carbon surface, which is the same as the SEM. The specific surface area of KAM500-400-3 is 1.45 times that of BC500, the total pore capacity is 4.57 times that of BC500, and the average aperture is 5.16 times that of BC500. These values are also much higher than the porous structural parameters of bamboo charcoal and modified bamboo charcoal. The specific surface area, pore size, and pore capacity of the carbon surface can effectively increase the adsorption capacity of heavy metals Cu(II) and Cd(II) [50].

Surface Functional Group Determination
The characteristic FT-IR spectra peaks of bamboo charcoal and bamboo charcoalmodified charcoal, as shown in Figure 7 for BC500, are mainly aromatic hydrocarbons (C-H and C = C), fatty hydrocarbons (-CH x ), hydroxyl groups (-OH), etc. The characteristic spectrum peak of KBC500-2 increases the oxygen-containing functional group (C-O-C) compared with BC500, and its vibration mode is aromatic ether expansion vibration. HBC500-30 contains fewer aromatic hydrocarbons (C-H) than BC500, probably because HNO3 is strongly oxidized as a strong acid, oxidizing some unstable functional groups and neutralizing them with the alkaline functional groups on the carbon surface [51][52][53][54][55]. In addition, HBC500-30 forms an aromatic hydrocarbon (C = C), an oxygen-containing functional group (C-O-C), and a fatty hydrocarbon (-CH 2 −), whose vibration modes are aromatic ring skeleton vibration, aromatic ether expansion vibration, and symmetry extension vibration of the long-chain methylene group, respectively. Compared with BC500, KAM500-400-3 has significantly more absorption peaks, including aromatic hydrocarbon (C-H), oxygen-containing functional group (C-O-C), adipose C hydrocarbon (-CH x ), etc. The vibration modes are respectively the out of plane bending vibration of aromatic ring C-H, the stretching vibration of aromatic ether, the in-plane bending vibration of aromatic ring C-H, and the antisymmetric stretching vibration of long chain methylene, which further explains the reason why the KOH activated carbon has strong adsorption capacity for heavy metals Cu (II) and Cd (II). [56,57].

Element Distribution
The distribution of the elements before and after the adsorption of heavy metals Cu(II) and Cd(II) is shown in Table 5. BC500, KAM500-400-3, KAM500-400-3, and HBC500-30, after the adsorption of Cu(II), had a percentage content of 0.27%, 1.62%, 7.77%, and 0.41%, respectively. The percentage content of the adsorbed Cd(II) was 1.36%, 1.61%, 8.42%, and 1.70%, respectively. This further proves that the adsorption capacity of the modified carbon for the heavy metals Cu(II) and Cd(II) will be improved. The three modification methods had the following effects: bamboo charcoal modified by HNO3 and KOH had a better adsorption effect than unmodified bamboo charcoal, but the improvement in adsorption performance was not significant; and the heavy metal Cu(II) was adsorbed after modification by KOH activation. The capacity of Cd(II) was significantly enhanced, as shown by the results of the above adsorption experiments.

Element Distribution
The distribution of the elements before and after the adsorption of heavy metals Cu(II) and Cd(II) is shown in Table 5. BC500, KAM500-400-3, KAM500-400-3, and HBC500-30, after the adsorption of Cu(II), had a percentage content of 0.27%, 1.62%, 7.77%, and 0.41%, respectively. The percentage content of the adsorbed Cd(II) was 1.36%, 1.61%, 8.42%, and 1.70%, respectively. This further proves that the adsorption capacity of the modified carbon for the heavy metals Cu(II) and Cd(II) will be improved. The three modification methods had the following effects: bamboo charcoal modified by HNO 3 and KOH had a better adsorption effect than unmodified bamboo charcoal, but the improvement in adsorption performance was not significant; and the heavy metal Cu(II) was adsorbed after modification by KOH activation. The capacity of Cd(II) was significantly enhanced, as shown by the results of the above adsorption experiments.
In this section, the effect of charring temperature on the adsorption capacity of bamboo char for heavy metals Cu(II) and Cd(II) is investigated, and the char with optimal charring temperature is modified with KOH, activated with KOH, and modified with HNO 3 , respectively. The results were as follows.
The adsorption capacity of bamboo char for the heavy metals Cu(II) and Cd(II) was proportional to the charring temperature, i.e., the adsorption capacity of bamboo char increased as the charring temperature increased gradually. The adsorption capacity of BC400 was significantly smaller than that of BC500, BC600, and BC700, and the difference between the adsorption capacities of the latter three was not significant [58][59][60][61]. The adsorption capacities of BC600 and BC700 for heavy metals Cu(II) were only 2.02% and 3.22% higher than those of BC500, respectively, and 1.26% and 4.04% higher than those of BC500 for heavy metal Cd(II); considering the time cost and energy consumption of the three tube furnace preparations, BC500 was selected for the subsequent modification experiments [62]. The KOH-modified, KOH-activated modified, and HNO 3 -modified bamboo charcoals were better than the unmodified ones in terms of the adsorption of heavy metals Cu(II) and Cd(II) [63]. Among them, the optimal conditions for KOH modification were a KOH concentration of 2 mol/L, KOH activation modification at an alkali-to-carbon ratio of 3:1, and an activation temperature of 400 • C. The best adsorption capacity of HNO 3 modification, with a mass fraction of HNO 3 of 30% for heavy metals Cu(II) and Cd(II), i.e., KBC500-2, KAM500-400-3, and HBC500-30, indicated the best modified bamboo charcoal for the three modification methods. Among the three, KAM500-400-3 had the highest adsorption capacity for heavy metals Cu(II) and Cd(II) [64][65][66].
The morphology of the modified char surface became relatively rough compared with that before the modification, and a large number of pores appeared. The specific surface area, total pore volume, and average pore size of the acid-base-modified bamboo char were smaller than those of the unmodified bamboo char, while the specific surface area of KAM500-400-3 was 1.45 times that of BC500, the total pore volume was 4.57 times that of BC500, and the average pore size was 5.16 times that of BC500. Meanwhile, the number and types of functional groups on the surface of the modified carbon were significantly increased, among which the number of absorption peaks of KAM500-400-3 increased the most. The results of an elemental analysis showed that the proportion of O elements in the bamboo char modified by HNO 3 and KOH activation increased significantly, and the proportion of Cu and Cd elements in the modified bamboo char with adsorbed Cu(II) and Cd(II) was the largest in KAM500-400-3 [67,68].
In summary, when the conditions of KOH activation modification were a 3:1 alkali-tocarbon ratio and 400 • C activation temperature, KAM500-400-3 had the strongest adsorption capacity for heavy metals Cu(II) and Cd(II) among all modified bamboo charcoals, so it was selected for the adsorption characteristics study.

Effect of Solution Concentration
The relationship between the adsorption amount of KAM500-400-3 on Cu(II) and Cd(II) and the initial concentrations of Cu(II) and Cd(II) is shown in Figure 8. When the initial concentrations of Cu(II) and Cd(II) were 50 mg/L, 60 mg/L, and 70 mg/L, the adsorption amounts of KAM500-400-3 were 29.53 mg/g, 33.36 mg/g, and 35.24 mg/g for Cu(II) and 42.35 mg/g, 47.65 mg/g, and 48.68 mg/g for Cd(II), respectively. From the experimental results, it can be seen that the adsorption of Cu(II) and Cd(II) by the optimal modified effect carbon increased with the increase in the initial concentration, but the adsorption amount leveled off after reaching a certain adsorption time because the driving force to overcome the mass transfer resistance improved with the increase in the initial concentration [69][70][71][72][73]. When the initial solution of Cu(II) and Cd(II) is at a low concentration, the number of heavy metal Cu(II) and Cd(II) ions is limited. KAM500-400-3 has sufficient surface adsorption sites and functional groups, and a large number of active sites compete for the limited Cu(II) and Cd(II) ions. Cu(II) and Cd(II) ions and carbon adsorption can be produced rapidly, but the adsorption amount of KAM500-400-3 for heavy metals Cu(II) and Cd(II) is not high because the adsorption sites are not fully utilized. As the initial concentration increases, the concentration gradient between KAM500-400-3 and the solution interface increases, causing Cu(II) and Cd(II) to migrate from the solution to the solid surface, and a large amount of free Cu(II) and Cd(II) compete for the limited adsorption sites and functional groups on the surface of KAM500-400-3, causing it to gradually reach the adsorption saturation state. The excess of the optimal modified carbon at the initial concentration is converted into an excess of heavy metals Cu(II) and Cd(II), the adsorption amount does not increase indefinitely once it reaches a certain value.

Effect of Solution pH
The effects of different initial solution pH on the adsorption of Cu(II) and Cd(II) by the optimally modified bamboo charcoal are shown in Figure 9. When the pH is 2, the adsorption of Cu(II) and Cd(II) by the optimally modified bamboo charcoal is the smallest-11.28 mg/g and 20.54 mg/g, respectively. This indicates that a lower pH is not ideal for the adsorption of Cu(II) and Cd(II) by optimally modified bamboo charcoal, but the adsorption of Cu(II) and Cd(II) increased with an increase in solution pH (pH < 7).

Effect of Solution pH
The effects of different initial solution pH on the adsorption of Cu(II) and Cd(II) by the optimally modified bamboo charcoal are shown in Figure 9. When the pH is 2, the adsorption of Cu(II) and Cd(II) by the optimally modified bamboo charcoal is the smallest-11.28 mg/g and 20.54 mg/g, respectively. This indicates that a lower pH is not ideal for the adsorption of Cu(II) and Cd(II) by optimally modified bamboo charcoal, but the adsorption of Cu(II) and Cd(II) increased with an increase in solution pH (pH < 7). This is because the solution pH can change the morphology of heavy metals and affect the degree of protonation and deprotonation of functional groups on the surface of optimally modified bamboo charcoal [74,75]. When the pH of the solution is small and acidic, the ionic forms of Cu(II) and Cd(II) in the solution are primarily Cu(II), Cu(OH) + /Cd(II), and Cd(OH) + , and the H + in the solution will electrostatically repel them and compete for the active sites on the char surface together, inhibiting the adsorption of Cu(II) and Cd(II) on the char.

Effect of Adsorption Time and Adsorption Kinetics
The relationship between adsorption time and adsorption amounts of Cu(II) and Cd(II) by KAM500-400-3 is shown in Figure 10. The figure shows that when the Cu(II) and Cd(II) solution concentrations are 50 mg/L, 60 mg/L, and 70 mg/L, respectively, the adsorption time follows approximately the same trend as the adsorption amounts. The adsorption of Cu(II) by KAM500-400-3 increased rapidly in the first two hours of adsorption, increased slowly towards the adsorption equilibrium, and finally reached 29.53 mg/g, 33.36 mg/g, and 35.34 mg/g for Cd(II), respectively. The adsorption amount increased significantly in the first hour of adsorption and then slowly tended to the adsorption equilibrium. Because the adsorption sites, pore structure, and functional groups on the surface of KAM500-400-3 are sufficient at the start of adsorption, the Cu(II) and Cd(II) adsorption amounts change rapidly [79]. However, after a period of adsorption, the adsorption sites on the surface of KAM500-400-3 are gradually occupied by heavy metal ions, the pore structure is further filled, the functional groups form complexes with heavy metal ions to stabilize the carbon surface, and the adsorption rate decreases because the concentration of heavy metal ions in the solution decreases at this time. Furthermore, because the surface of KAM500-400-3 is filled with Cu(II)/Cd(II) charges, and the Cu(II)/Cd(II) charges in the solution produce repulsion, making further adsorption difficult, with the increase in adsorption time, the adsorption of KAM500-400-3 for Cu(II) and Cd(II) tends to plateau after reaching a certain amount [80]. When the pH of the solution gradually increases, OH − will be produced in the solution, and its amount will increase with the increase of pH.OH − can increase the number of negative charges on the carbon surface so as to attract cations such as Cu (II) and Cd (II). At this time, Cu (II), Cu (OH) + /Cd (II), Cd (OH) + and Cu (OH) 2 /Cd (OH) 2 precipitates will appear in the solution. However, when the pH value increases further, on the one hand, OH − will compete with Cu(II) and Cd(II) for the oxygen-containing groups on the surface of the optimally modified bamboo carbon, which will reduce the adsorption capacity; on the other hand, some precipitation reactions will occur with Cu(II) and Cd(II) to form strong oxidizing precipitates, which will inhibit the adsorption of the optimally modified bamboo carbon, and thus, the adsorption capacity will be reduced accordingly [76][77][78].

Effect of Adsorption Time and Adsorption Kinetics
The relationship between adsorption time and adsorption amounts of Cu(II) and Cd(II) by KAM500-400-3 is shown in Figure 10. The figure shows that when the Cu(II) and Cd(II) solution concentrations are 50 mg/L, 60 mg/L, and 70 mg/L, respectively, the adsorption time follows approximately the same trend as the adsorption amounts. The adsorption of Cu(II) by KAM500-400-3 increased rapidly in the first two hours of adsorption, increased slowly towards the adsorption equilibrium, and finally reached 29.53 mg/g, 33.36 mg/g, and 35.34 mg/g for Cd(II), respectively. The adsorption amount increased significantly in the first hour of adsorption and then slowly tended to the adsorption equilibrium. Because the adsorption sites, pore structure, and functional groups on the surface of KAM500-400-3 are sufficient at the start of adsorption, the Cu(II) and Cd(II) adsorption amounts change rapidly [79]. However, after a period of adsorption, the adsorption sites on the surface of KAM500-400-3 are gradually occupied by heavy metal ions, the pore structure is further filled, the functional groups form complexes with heavy metal ions to stabilize the carbon surface, and the adsorption rate decreases because the concentration of heavy metal ions in the solution decreases at this time. Furthermore, because the surface of KAM500-400-3 is filled with Cu(II)/Cd(II) charges, and the Cu(II)/Cd(II) charges in the solution produce repulsion, making further adsorption difficult, with the increase in adsorption time, the adsorption of KAM500-400-3 for Cu(II) and Cd(II) tends to plateau after reaching a certain amount [80]. In order to investigate the adsorption mechanism of Cu(II) and Cd(II) by the optimal effect modified bamboo charcoal, the proposed primary kinetic model shown in Figure 11 and the proposed secondary kinetic model shown in Figure 12 were introduced in this experiment to investigate the adsorption process, and the fitted data of the kinetic model are shown in Table 6. The R 2 values of modified bamboo charcoal with optimal effect for adsorption of Cu(II) at concentrations of 50 mg/L, 60 mg/L, and 70 mg/L were 0.8119, 0.8006, and 0.7932, respectively, and the R 2 values for adsorption of Cd(II) at concentrations of 50 mg/L, 60 mg/L, and 70 mg/L were 0.8248, 0.9250, and 0.732, respectively. In the proposed secondary kinetic model, the R 2 values of modified bamboo carbon were 0.9968, 0.9760, and 0.9695 for the adsorption of Cu(II) at 50 mg/L, 60 mg/L, and 70 mg/L, respectively, and the R 2 values of Cd(II) at 50 mg/L, 60 mg/L, and 70 mg/L were 1, 2, and 3, respectively. When the proposed secondary kinetics were combined with the above experimental results, they fitted better than the proposed primary kinetics. This indicates that chemisorption and physical adsorption occur simultaneously in the adsorption of Cu(II) and Cd(II) by KAM500-400-3, with chemisorption being dominant. This chemisorption involves electron covalency or electron migration between the adsorbed material and the adsorbent, and physical adsorption such as precipitation and ion exchange may also exist. According to the kinetic time, equilibrium can be reached in about 6 hours for Cu(II) adsorption and 4 hours for Cd(II) adsorption by KAM500-400-3, which can be used to determine the adsorption time for subsequent experiments. In order to investigate the adsorption mechanism of Cu(II) and Cd(II) by the optimal effect modified bamboo charcoal, the proposed primary kinetic model shown in Figure 11 and the proposed secondary kinetic model shown in Figure 12 were introduced in this experiment to investigate the adsorption process, and the fitted data of the kinetic model are shown in Table 6. The R 2 values of modified bamboo charcoal with optimal effect for adsorption of Cu(II) at concentrations of 50 mg/L, 60 mg/L, and 70 mg/L were 0.8119, 0.8006, and 0.7932, respectively, and the R 2 values for adsorption of Cd(II) at concentrations of 50 mg/L, 60 mg/L, and 70 mg/L were 0.8248, 0.9250, and 0.732, respectively. In the proposed secondary kinetic model, the R 2 values of modified bamboo carbon were 0.9968, 0.9760, and 0.9695 for the adsorption of Cu(II) at 50 mg/L, 60 mg/L, and 70 mg/L, respectively, and the R 2 values of Cd(II) at 50 mg/L, 60 mg/L, and 70 mg/L were 1, 2, and 3, respectively. When the proposed secondary kinetics were combined with the above experimental results, they fitted better than the proposed primary kinetics. This indicates that chemisorption and physical adsorption occur simultaneously in the adsorption of Cu(II) and Cd(II) by KAM500-400-3, with chemisorption being dominant. This chemisorption involves electron covalency or electron migration between the adsorbed material and the adsorbent, and physical adsorption such as precipitation and ion exchange may also exist. According to the kinetic time, equilibrium can be reached in about 6 h for Cu(II) adsorption and 4 h for Cd(II) adsorption by KAM500-400-3, which can be used to determine the adsorption time for subsequent experiments. . This experiment employs an intraparticle diffusion model to further analyze the data in order to better understand the diffusion mechanism of Cu(II) and Cd(II) on KAM500-400-3, as shown in Figure 13. The intraparticle diffusion process mainly consists of three steps: mass transfer, adsorption, and diffusion. The intraparticle diffusion process of Cu(II) and Cd(II) on KAM500-400-3 has similar fitting results. In this study, the adsorption process (first stage) and diffusion process (second stage) are the main steps of intraparticle diffusion because the mass transfer process is completed in a very short time [81]. The slopes (kp1 and kp2) of the first and second stages for Cu(II) were 3.0492, 0.0876, 3.9562, 0.1229, and 4.6053, 0.0421, respectively, with KAM500-400-3 adsorption concentrations of 50 mg/L, 60 mg/L, and 70 mg/L. The correlation coefficients R1 2 were 0.9757, 0.9489, and 0.9468, and the R 2 values were 0.9918, 0.9762, and 0.9750, respectively. For Cd(II) with . This experiment employs an intraparticle diffusion model to further analyze the data in order to better understand the diffusion mechanism of Cu(II) and Cd(II) on KAM500-400-3, as shown in Figure 13. The intraparticle diffusion process mainly consists of three steps: mass transfer, adsorption, and diffusion. The intraparticle diffusion process of Cu(II) and Cd(II) on KAM500-400-3 has similar fitting results. In this study, the adsorption process (first stage) and diffusion process (second stage) are the main steps of intraparticle diffusion because the mass transfer process is completed in a very short time [81]. The slopes (kp1 and kp2) of the first and second stages for Cu(II) were 3.0492, 0.0876, 3.9562, 0.1229, and 4.6053, 0.0421, respectively, with KAM500-400-3 adsorption concentrations of 50 mg/L, 60 mg/L, and 70 mg/L. The correlation coefficients R1 2 were 0.9757, 0.9489, and 0.9468, and the R 2 values were 0.9918, 0.9762, and 0.9750, respectively. For Cd(II) with This experiment employs an intraparticle diffusion model to further analyze the data in order to better understand the diffusion mechanism of Cu(II) and Cd(II) on KAM500-400-3, as shown in Figure 13. The intraparticle diffusion process mainly consists of three steps: mass transfer, adsorption, and diffusion. The intraparticle diffusion process of Cu(II) and Cd(II) on KAM500-400-3 has similar fitting results. In this study, the adsorption process (first stage) and diffusion process (second stage) are the main steps of intraparticle diffusion because the mass transfer process is completed in a very short time [81]. The slopes (kp 1 and kp 2 ) of the first and second stages for Cu(II) were 3.0492, 0.0876, 3.9562, 0.1229, and 4.6053, 0.0421, respectively, with KAM500-400-3 adsorption concentrations of 50 mg/L, 60 mg/L, and 70 mg/L. The correlation coefficients R 1 2 were 0.9757, 0.9489, and 0.9468, and the R 2 values were 0.9918, 0.9762, and 0.9750, respectively. For Cd(II) with KAM500-400-3 adsorption concentrations of 50 mg/L, 60 mg/L, and 70 mg/L, the slopes of the first and second phases (kp 1 and kp 2 ) were 0.5828, 0.0352, 0.4187, 0.0627, and 0.4179, 0.0216, respectively. The correlation coefficients R 1 2 were 0.8680, 0.9094, and 0.9263, and the R 2 values were 0.9906, 0.9061, and 0.9092, respectively, indicating that Cu(II) and Cd(II) on KAM500-400-3 were consistent with the intraparticle diffusion model. The adsorption rates of Cu(II) and Cd(II) in the pores of KAM500-400-3 are higher than their diffusion rates in the particles. At the same time, the fitted lines of both did not cross the origin, signifying the existence of other rate control steps besides intraparticle diffusion.
Toxics 2022, 10, x FOR PEER REVIEW 19 KAM500-400-3 adsorption concentrations of 50 mg/L, 60 mg/L, and 70 mg/L, the slo the first and second phases (kp1 and kp2) were 0.5828, 0.0352, 0.4187, 0.0627, and 0 0.0216, respectively. The correlation coefficients R1 2 were 0.8680, 0.9094, and 0.9263 the R 2 values were 0.9906, 0.9061, and 0.9092, respectively, indicating that Cu(II Cd(II) on KAM500-400-3 were consistent with the intraparticle diffusion model adsorption rates of Cu(II) and Cd(II) in the pores of KAM500-400-3 are higher than diffusion rates in the particles. At the same time, the fitted lines of both did not cro origin, signifying the existence of other rate control steps besides intraparticle diffus

Adsorption Isotherms
The adsorption isotherms for Cu(II) and Cd(II) adsorption at different temperatures are shown in Figure 14. The adsorption amount of the modified bamboo charcoal increases continuously for these two heavy metals as the volume of Cu(II) solution increases from 60 to 160 mL and the volume of Cd(II) solution increases from 70 to 140 mL. The adsorption of Cu(II) and Cd(II) by modified bamboo charcoal increased with increasing equilibrium concentration, but the increase in adsorption decreased gradually [82]. At temperatures of 5 • C, 25 • C, and 45 • C, the adsorption amounts of optimally modified bamboo charcoal reached 31.12 mg/g, 32.57 mg/g, and 39.91 mg/g for Cu(II), and 43.83 mg/g, 48.00 mg/g, and 51.00 mg/g for Cd(II), when the volume of Cd(II) increased from 60 to 160 mL, respectively. According to the experimental results, the optimal modified bamboo charcoal is more effective at treating a large amount of Cu(II) and Cd(II) solution with a higher concentration and has a better adsorption effect on Cd(II) than Cu(II) [83].
In order to better understand the optimal effect of modified bamboo charcoal on the adsorption of Cu(II) and Cd(II), two models, Langmuir and Freundlich, were used to fit the data obtained from the experiments. Among them, the Langmuir model satisfies the monolayer adsorption model in the ideal case, the essence of which is the assumption of the same adsorption affinity between the adsorbent and the adsorbed material. In contrast, the Freundlich model expresses the multilayer adsorption in a non-ideal situation, where the adsorbed amount of adsorbent will increase when the concentration of adsorbent increases. The Langmuir model is plotted with Ce as the horizontal coordinate and Ce/qe as the vertical coordinate, as shown in Figure 15; the Freundlich model is plotted with lnCe as the horizontal coordinate and lnQe as the vertical coordinate, as shown in Figure 16. The parameters fitted to each model are detailed in Table 7. In order to better understand the optimal effect of modified bamboo charcoal on the adsorption of Cu(II) and Cd(II), two models, Langmuir and Freundlich, were used to fit the data obtained from the experiments. Among them, the Langmuir model satisfies the monolayer adsorption model in the ideal case, the essence of which is the assumption of the same adsorption affinity between the adsorbent and the adsorbed material. In contrast, the Freundlich model expresses the multilayer adsorption in a non-ideal situation, where the adsorbed amount of adsorbent will increase when the concentration of adsorbent increases. The Langmuir model is plotted with Ce as the horizontal coordinate and Ce/qe as the vertical coordinate, as shown in Figure 15; the Freundlich model is plotted with lnCe as the horizontal coordinate and lnQe as the vertical coordinate, as shown in Figure 16. The parameters fitted to each model are detailed in Table 7.   In order to better understand the optimal effect of modified bamboo charcoal on the adsorption of Cu(II) and Cd(II), two models, Langmuir and Freundlich, were used to fit the data obtained from the experiments. Among them, the Langmuir model satisfies the monolayer adsorption model in the ideal case, the essence of which is the assumption of the same adsorption affinity between the adsorbent and the adsorbed material. In contrast, the Freundlich model expresses the multilayer adsorption in a non-ideal situation, where the adsorbed amount of adsorbent will increase when the concentration of adsorbent increases. The Langmuir model is plotted with Ce as the horizontal coordinate and Ce/qe as the vertical coordinate, as shown in Figure 15; the Freundlich model is plotted with lnCe as the horizontal coordinate and lnQe as the vertical coordinate, as shown in Figure 16. The parameters fitted to each model are detailed in Table 7.     Kf in the Freundlich model represents the adsorption equilibrium concentration, i.e., the amount of adsorption per unit concentration, and the value of n is generally unlimited, while the value of 1/n is generally between 0 and 1. This represents the sensitivity of the adsorption amount to a change in solution concentration, and when 1/n is less than 0.5, it indicates that the adsorption process is simple. A comprehensive analysis of the values of Kf and 1/n shows that the value of Kf increases gradually with an increase in the adsorption temperature, which indicates that the higher the adsorption temperature, the better the adsorption capacity of KAM500-400-3 for Cu(II) and Cd(II), which is consistent with the conclusion obtained from the Langmuir model fitting, and the value of 1/n for Cu(II) at temperatures of 5 • C, 25 • C, and 45 • C. The values of 1/n were in the range of 0.04-0.13 for Cu(II) and 0.09-0.14 for Cd(II), which indicated that KAM500-400-3 could easily adsorb Cu(II) and Cd(II) [84].
The comprehensive analysis shows that the Langmuir model can more accurately describe the adsorption of KAM500-400-3 for Cu(II) and Cd(II) than the Freundlich model, indicating that the adsorption of Cu(II) and Cd(II) on KAM500-400-3 is monolayer adsorption and its main adsorption mechanism is chemisorption [85]. In addition, the R 2 values of the Freundlich model are also greater than 0.9, which indicates that the process of adsorption of Cu(II) and Cd(II) by the optimal effect modification is accompanied by physical adsorption in addition to chemical forces, which is consistent with the experimental results of adsorption kinetics.

Adsorption Thermodynamics
Substituting the experimental data into the equation, it can be seen from Table 8 that the free energy change ∆G 0 of the adsorption of Cu(II) by KAM500-400-3 is −9.70 kJ/mol, -10.74 kJ/mol, and −12.14 kJ/mol when the temperature is 5 • C (278 K), 25 • C (298 K), and 45 • C (318 K), respectively. The values of the free energy change AG0 of the adsorption of Cd(II) were −12.70 kJ/mol, −14.27 kJ/mol, −15.65 kJ/mol, respectively. With an increase in temperature, the value of the free energy change AG 0 of the adsorption kept decreasing and its absolute value kept increasing, indicating that the adsorption of Cu(II) and Cd(II) on KAM500-400-3 was spontaneous. The enthalpy changes of Cu(II) and Cd(II) adsorption on KAM500-400-3 are positive, 7.19 kJ/mol and 7.82 kJ/mol, respectively, which indicates that the adsorption of Cu(II) and Cd(II) on KAM500-400-3 is spontaneous, and the adsorption effect of KAM500-400-3 on heavy metals improves with increasing adsorption temperature, which is consistent with the conclusion obtained from the adsorption isotherm [86]. The 400-3 adsorption of Cu(II) and Cd(II) is heat-absorbing, increasing the temperature is beneficial for the removal of Cu(II) and Cd(II) by KAM500-400-3. Cu(II) and Cd(II) adsorp-tion entropy changes AS on KAM500-400-3 are 60.64 J/molK and 73.93 J/molK, respectively. The adsorption process of KAM500-400-3 on Cu(II) and Cd(II) is a reaction to the entropy increase.

Conclusions
In this study, the adsorption characteristics of optimal effect modified bamboo carbon KAM500-400-3 for heavy metals Cu(II) and Cd(II) were investigated using static and dynamic adsorption experiments. The effects of the solution concentration, adsorption time, pH, and temperature on the adsorption effect of KAM500-400-3 on Cu(II) and Cd(II) were investigated in the static adsorption experiments, and the adsorption mechanism of KAM500-400-3 on Cu(II) and Cd(II) was analyzed by fitting the adsorption kinetics, adsorption isotherms, and adsorption thermodynamics. The following conclusions were obtained: (1) The adsorption of heavy metals Cu(II) and Cd(II) by KAM500-400-3 is affected by solution concentration, adsorption time, pH, temperature, and other factors. When the initial concentration of heavy metals Cu(II) and Cd(II) increases, the adsorption amount also increases, and the relatively higher pH (pH = 6) and temperature are more favorable to the adsorption of the optimal modified effect carbon for heavy metals Cu(II) and Cd(II); (2) The results of the adsorption kinetic fitting showed that both the proposed primary and secondary kinetics could describe the process of Cu(II) and Cd(II) adsorption by KAM500-400-3 well, but the latter was a better fit. This indicates that chemisorption and physical adsorption of Cu(II) and Cd(II) by KAM500-400-3 occur simultaneously, with chemisorption dominating. This chemisorption involves electron covalency or electron migration between the adsorbed material and the adsorbent, and physical adsorption such as precipitation and ion exchange may also exist.
The adsorption isotherm fitting results showed that the correlation coefficients R 2 of both Langmuir and Freundlich models were greater than 0.9, indicating that they could both accurately describe the adsorption of KAM500-400-3 for Cu(II) and Cd(II), indicating that the process of adsorption of Cu(II) and Cd(II) by the optimal effect modification is accompanied by chemical forces. This is consistent with the experimental results of adsorption kinetics. The best fit of the Langmuir model among the two adsorption isotherm fitting models indicates that the adsorption of Cu(II) and Cd(II) on KAM500-400-3 is monolayer adsorption with chemisorption as the main adsorption mechanism.
The results of the adsorption thermodynamic fitting indicated that the adsorption of Cu(II) and Cd(II) on KAM500-400-3 was spontaneous and heat-absorbing, and the adsorption effect of KAM500-400-3 on heavy metals improved as the adsorption temperature increased, which is consistent with the conclusion obtained from the adsorption isotherm that the adsorption of Cu(II) and Cd(II) by KAM500-400-3 process is the reaction of entropy increase.
In this study, bamboo charcoal was prepared at different carbonization temperatures using Moso bamboo as a raw material, and the best carbonization temperature was investigated through adsorption experiments. Based on the shortcomings of the present study, the following work should be carried out: (1) The biomass material selected for this experiment was Moso bamboo. In future studies, we can try to select a variety of biomass materials for carbonization and modification to investigate their adsorption capacity for Cu(II) and Cd(II) in water as well as their immobilization effect on Cu(II) and Cd(II) contaminated sediment, and to determine the optimal biomass material; (2) The modification methods adopted in this experiment are mainly acid-base surface modification and activation modification. In future studies, we can also try redox modification by adding metal salts to biochar or adsorbent compound modification, or combine several modification methods to explore a better modification method for biochar [87]; (3) In this experiment, we only investigated the adsorption of Cu(II) and Cd(II) in the water body; we could consider the competition of heavy metals adsorption in the water body with mixed metals in a subsequent study; (4) This experiment did not consider the regeneration and reuse of modified bamboo charcoal adsorbed with Cu(II) and Cd(II). In subsequent experiments, we may consider regenerating the contaminated modified bamboo charcoal by acid regeneration and thermal regeneration, investigate the number of times it can be regenerated, and compare the effectiveness of each method in regenerating the modified bamboo charcoal.