Metal-Catalyzed Degradation of Cellulose in Ionic Liquid Media

Biomass conversion to 5-hydroxymethylfurfural (HMF) has been widely investigated as a sustainable alternative to petroleum-based feedstock, since it can be efficiently converted to fuel, plastic, polyester, and other industrial chemicals. In this report, the degradation of commercial cellulose, the isomerization of glucose to fructose, and the conversion of glucose to HMF in 1-butyl-3-methylimidazolium chloride ([BMIM]Cl]) using metal catalysts (CrCl3, ZnCl2, MgCl2) as well as tungsten and molybdenum oxide-based polyoxometalates (POM) were investigated. Tungsten and molybdenum oxide-based POMs in ionic liquids (IL) were able to degrade cellulose to majority glucose and epimerize glucose to mannose (in the case of the molybdenum oxide-based POM). A certain amount of glucose was also converted to HMF. The tungsten oxide-based POM in IL showed good activity for cellulose degradation but the overall products yield remained 28.6% lower than those obtained using CrCl3 as a catalyst. Lowering the cellulose loading did not significantly influence the results and the addition of water to the reaction medium decreased the product yields remarkably.


Introduction
An efficient utilization of renewable biomass resources, particularly lignocellulosic biomass, is important from the viewpoint of the production of industrial platform chemicals and fuels (Figure 1) [1].An appropriate technology would efficiently deconstruct the biomass to release cellulose and hemicellulose and hydrolyze cellulosic components to generate oligosaccharides [2].
Of the fundamental building blocks from biorefineries, 5-hydroxymethylfurfural (HMF) is considered a key intermediate for the development of biomass-based products, because a series of compounds such as organic acids, polymer precursors, and biofuels derive from it [3].
Hence the selective catalytic conversion of cellulose to a platform chemical such as glucose, HMF, sorbitol or gluconic acid under mild conditions is the most desirable route in industry [4,5].However, a high-yield, low-cost, energy-efficient, and direct conversion method for cellulose to HMF is still a challenge to researchers in the field.
Ionic liquids (ILs) are being investigated as effective low-impact solvents for the conversion of cellulose due to being relatively easy to handle, recyclable, and in possession of a negligible vapor pressure.Moreover, ILs have an ability to solubilize low-toxicity metal catalysts for the direct conversion of cellulose to value-added chemicals.However, most published papers focus mainly on the advantages of ionic liquids in the separation of cellulose from lignocellulosic biomass over traditional methods [6][7][8][9].From previous studies it appears that when using cellulose as a feedstock for HMF formation, the key steps are the dissolution and depolymerisation of cellulose to glucose monomers and not the isomerization to fructose and subsequent dehydration of fructose to HMF.Cellulose has an abundant number of intra-and intermolecular hydrogen bonds that make it intrinsically recalcitrant to depolymerize which is why ionic liquids as solvents can provide a solution due to their specific ability to dissolve the compound [10].ILs appear to be even more advantageous in overcoming these problems as they can act as both solvents and catalysts [7].The catalytic conversion of biomass-derived carbohydrates to value-added chemicals is a commercially important reaction and requires the use of both Lewis and Brønsted acids.Multifunctional ILs with both types of acidity are promising catalysts as well as solvents for the one-pot conversion of glucose to value-added chemicals.
Until now, the production of HMF with glucose as a feedstock has efficiently used chromium chloride catalyst together with ionic liquids.Zhao et al. [11] were the first to report an unparalleled yield of 69% HMF catalyzed by chromium (II) chloride (CrCl2) in a medium of 1-ethyl-3-methylimidazolium chloride ([EMIM]Cl) at 100 °C for 3 h.Recently, the dehydration of glucose to HMF with a yield of about 67% was achieved in [EMIM]Cl and N,N-dimethylacetamide (DMA) by using CrCl2 or CrCl3 at 100 °C for 6 h [12].Dehydration of cellulose to HMF with a yield of about 89% was achieved in [EMIM]Cl by using CrCl2 at 120 °C for 6 h [13]).
The catalytic activity of a ZnCl3-containing IL was found to be highly Lewis acidic, and was the controlling parameter for glucose conversion, resulting in yields of 13.4%, 23.8%, and 67.1% of HMF, levulinic acid (LA) and formic acid (FA), respectively.These multifunctional chlorometallate ILs were found to be recyclable with no loss of metal chloride from their anion [14].
Brønsted acidic ionic liquids (BAILs) showed a very good catalytic effect on the conversion of raw biomass to C5 sugars and furfural.In water medium the remarkably high yield of C5 sugars from bagasse, 88%, was obtained using 1-methyl-3(3-sulfopropyl)-imidazolium hydrogen sulfate ([C3SO3HMIM][HSO4]).Similarly, with this BAIL, a high yield (73%) of furfural was obtained in the one-pot method using a water/toluene biphasic solvent system [15].
Calculations revealed the dependence of the catalytic performance of [C3SO3HMIM][HSO4] BAIL on the acidity and nucleophilicity of its constituent ions [16].
1,1,3,3-tetramethylguanidine tetrafluoroborate ([TMG]BF4) as a solvent was confirmed to exhibit excellent catalytic activity in the conversion of C6 carbohydrates to HMF.The HMF yields from the conversion of fructose, glucose, cellobiose, and microcrystalline cellulose (MCC) were 74%, 27%, 20%, and 18%, respectively [17].From previous studies it appears that when using cellulose as a feedstock for HMF formation, the key steps are the dissolution and depolymerisation of cellulose to glucose monomers and not the isomerization to fructose and subsequent dehydration of fructose to HMF.Cellulose has an abundant number of intra-and intermolecular hydrogen bonds that make it intrinsically recalcitrant to depolymerize which is why ionic liquids as solvents can provide a solution due to their specific ability to dissolve the compound [10].ILs appear to be even more advantageous in overcoming these problems as they can act as both solvents and catalysts [7].The catalytic conversion of biomass-derived carbohydrates to value-added chemicals is a commercially important reaction and requires the use of both Lewis and Brønsted acids.Multifunctional ILs with both types of acidity are promising catalysts as well as solvents for the one-pot conversion of glucose to value-added chemicals.
Until now, the production of HMF with glucose as a feedstock has efficiently used chromium chloride catalyst together with ionic liquids.Zhao et al. [11] were the first to report an unparalleled yield of 69% HMF catalyzed by chromium (II) chloride (CrCl 2 ) in a medium of 1-ethyl-3-methylimidazolium chloride ([EMIM]Cl) at 100 • C for 3 h.Recently, the dehydration of glucose to HMF with a yield of about 67% was achieved in [EMIM]Cl and N,N-dimethylacetamide (DMA) by using CrCl 2 or CrCl 3 at 100 • C for 6 h [12].Dehydration of cellulose to HMF with a yield of about 89% was achieved in [EMIM]Cl by using CrCl 2 at 120 • C for 6 h [13]).
The catalytic activity of a ZnCl 3 -containing IL was found to be highly Lewis acidic, and was the controlling parameter for glucose conversion, resulting in yields of 13.4%, 23.8%, and 67.1% of HMF, levulinic acid (LA) and formic acid (FA), respectively.These multifunctional chlorometallate ILs were found to be recyclable with no loss of metal chloride from their anion [14].
Brønsted acidic ionic liquids (BAILs) showed a very good catalytic effect on the conversion of raw biomass to C5 sugars and furfural.In water medium the remarkably high yield of C5 sugars from bagasse, 88%, was obtained using 1-methyl-3(3-sulfopropyl)-imidazolium hydrogen sulfate ([C 3 SO 3 HMIM][HSO 4 ]).Similarly, with this BAIL, a high yield (73%) of furfural was obtained in the one-pot method using a water/toluene biphasic solvent system [15].
Calculations revealed the dependence of the catalytic performance of [C 3 SO 3 HMIM][HSO 4 ] BAIL on the acidity and nucleophilicity of its constituent ions [16].
The search for effective catalysts has brought polyoxometalates-anionic metal oxides under consideration because of their unique properties, such as strong Brønsted acidity, good oxidizing ability, high water tolerance, low corrosiveness, and recoverability.In addition, POMs have exhibited a promising performance in the transformation of cellulose into platform chemicals in both homogeneous and heterogeneous systems [18].
A review by Deng et al. [19] highlights the following good catalytic properties of POMs in the conversion of cellulose to platform chemicals: tunable acidity, redox potential, and solubility in various media, which allow the rational design of active sites on molecular and atomic scales; 5.
high thermal and oxidative stability as compared with common molecular catalysts such as organometallic complexes and enzymes; 6.
ease of handling and separation, and the relatively low corrosiveness, possibly owing to the generated corrosion-inhibiting films, which allow them to act as environmentally friendly liquid-phase catalysts, unlike mineral acids.
Another approach is to use task-specific ionic liquids with polyoxometalates (POMs) contained in them.Due to their high negative charge and large metal-oxide framework, POMs can react with a variety of cationic organic groups to form novel functional ionic liquids, POMs-ILs.IL cations with various structures and properties can provide organic blocks to modify POM catalysts, thanks to their acidity, polarity, solubility, redox properties, and surface structures.
Polyoxomethalates-based ionic liquids (POM-IL) as solid acid catalysts have been used for the direct conversion of fructose to HMF.The phosphotungstic acid (HPW)-derived ionic liquid shows the highest catalytic performance (up to 99% of the yield) in the formation of HMF.In this study, the catalyst afforded a good yield of HMF from inulin (76%) and sucrose (45%) as well [20].
In another work [21], POM-IL were synthesized and employed for the one-pot dissolution and conversion of powdered switchgrass biomass.For comparison purposes, Avicel Cellulose was also treated under identical conditions.The most promising for biomass conversion was found to be the combination of phosphotungstic acid hydrate and 1-butyl-3-methylimidazolium bromide.Avicel Cellulose was then utilized for the hydrolysis at 200 • C for 120 min, and as a result, approximately 31 wt % of the biomass and 13 wt % of Avicel Cellulose were converted to water-soluble products; i.e., sugars obtained from the deconstructed cellulose [21].
There are some other examples where heteropolyacids act as efficient catalysts for the conversion of glucose.For example, a 98% conversion of glucose to HMF in ionic liquids and a 99% selectivity of HMF were attained after a 3 h reaction time at 393 K by using 12-molybdophosphoric acid in a mixture of either 1-ethyl-3-methylimidazolium or 1-butyl-3-methylimidazolium chloride with acetonitrile as a co-solvent [22].
Analysis of ILs-containing samples where capillary electrophoresis (CE) is proposed as an effective method for the simultaneous determination of mono-, di-and oligosaccharides, as well as HMF and organic acids (acetic and levulinic acids can be formed during degradation of HMF), is no easy task [23,24].The objective of this case study was to compare molybdenum and tungsten oxide-based POM-ILs catalytic performance with metal catalysts, such as CrCl 3 , ZnCl 2 and MgCl 2 using ILs as solvents.

Results and Discussion
The main goal was to monitor the transformation of microcrystalline cellulose to HMF via glucose and fructose by different widely-studied catalysts and compare the results with molybdenum and tungsten oxide-based POMs-ILs.Although the isomerization and epimerization of glucose might occur, the formation of fructose predominated.The formation of fructose via isomerization required some reorganization of the intermediate, whereas the formation of mannose is reported through rotation around the C2-C3 bond [25].One of the glucose isomerization reaction pathways is analogous to that observed in metalloenzymes, such as D-xylose isomerase (XI), which contain two divalent Lewis acid metal centers (Mg 2+ or Mn 2+ ) confined within a hydrophobic pocket [26,27].The reaction pathway includes the ring-opening of glucose and coordination with glucose O1 and O2 atoms prior to the isomerization of the ring-opened glucose chain from position C2 to C1 (via 1,2 intramolecular hydride shift) [28].
Table 1 (Table S1) shows, the conversion of cellulose to HMF in [BMIM]Cl at 100 • C for 24 h with ZnCl 2 , MgCl 2 , CrCl 3 , molybdenum and tungsten oxide-based POM-ILs as catalysts.In the case of molybdenum and tungsten oxides-based POM-ILs the main products were monosaccharides.Table 1 also contains the total product yields where all of the obtained products are summarized.As expected, the sample with no catalyst did not contain any of the investigated products.The tungsten oxide-based POM showed good activity for cellulose degradation, however, the overall yield of products (glucose and HMF) remained 29% lower than that obtained with CrCl 3 as a catalyst.The main product formed was glucose instead of HMF.The molybdenum oxide-based POM was the only catalyst that was able to epimerize glucose to mannose, while the latter accounted for 22% of the products obtained.The catalytic activity of the molybdenum oxide-based POM remained remarkably lower and the overall product yields (glucose, mannose and HMF) were 82% less compared to CrCl 3 .The catalytic ability of MgCl 2 and ZnCl 2 were the lowest and HMF yields were 6.8% and 8.4% of that obtained with CrCl 3 , respectively.Some metal chlorides are very effective as catalysts for the synthesis of HMF in ILs [29,30].The isomerization of glucose into fructose is favored by the presence of Lewis acid sites [25].Figure 2 shows the mechanism proposed by Zhou et al. for the interaction of metal chlorides with glucose in ILs such as [BMIM]Cl.According to this mechanism, good catalytic performance of CrCl 3 •6H 2 O may be explained by the formation of a more stable metal chloride-glucose complex due to the stronger coordination ability of Cl − with a chromium center [29][30][31].
Li et al. [32] demonstrated in their study that according to density functional theory (DFT) calculations, isomerization of glucose to fructose over tungsten oxide-based catalysts is possible because of Lewis acid sites (W6+), terminal W-oxo groups that are Lewis basic sites, and proton mediators, such as "structural" and physisorbed water on the oxide surface.According to their study the key aspect of the catalytic mechanism is the proton shift from C2 → C1 that is promoted by a synergistic action of the Lewis acid sites, which is followed by a proton-transfer [32].Ju et al. [33] demonstrated in their 13 C NMR study that molybdenum-based POMs are active and selective catalysts for the epimerization of aldoses.The epimerization mechanism involves electron transfer from the aldose to the molybdenum oxide octahedra surface units of the POM followed by an intra molecular C1 → C2 carbon shift.They also report that replacing Mo with W in the Kegging structure POM resulted in loss of the epimerization activity, indicating that the molybdenum octahedral located in the cagelike structure of the POM play an important role in activating the epimerization of glucose [33].
Nguyen et al. [34] demonstrated in their 13 C NMR and 1 H NMR study that glucose epimerization to mannose using Lewis acids, such as MCl 3 in aqueous phase (CrCl 3 was also tested), proceeds via two parallel mechanisms: first a reverse C2 → C1 hydride transfer followed by a C1 → C2 intramolecular carbon shift.They also report that MCl 3 are also able to epimerize glucose to mannose in low yields and since fructose formation is predominant, the hydride transfer is the more dominant pathway of glucose conversion [34].Nguyen et al. [34] demonstrated in their 13 C NMR and 1 H NMR study that glucose epimerization to mannose using Lewis acids, such as MCl3 in aqueous phase (CrCl3 was also tested), proceeds via two parallel mechanisms: first a reverse C2 → C1 hydride transfer followed by a C1 → C2 intramolecular carbon shift.They also report that MCl3 are also able to epimerize glucose to mannose in low yields and since fructose formation is predominant, the hydride transfer is the more dominant pathway of glucose conversion [34].S2 and S3) shows the effect of time on the yield of glucose, mannose and HMF from cellulose at 100 and 120 °C for 72 h using tungsten and molybdenum oxide-based POMs as catalysts.

Reaction Time for POM-IL Catalysts
(a) (b) In the case of the molybdenum oxide-based POM, prolonging the reaction time improved the HMF yield at 100 °C and the plateau in its concentration was not achieved by 72 h.The same trend held true for the yields of glucose and mannose.At 120 °C, glucose and mannose were not detected and the maximum HMF yield remained lower than the yield obtained at 100 °C.The maximum HMF yield, which was achieved at 24 h, was 52% lower, and furthermore, it started to decrease with

Reaction Time for POM-IL Catalysts
Figure 3 (Tables S2 and S3) shows the effect of time on the yield of glucose, mannose and HMF from cellulose at 100 and 120 • C for 72 h using tungsten and molybdenum oxide-based POMs as catalysts.
Inorganics 2018, x FOR PEER REVIEW 5 of 11 Nguyen et al. [34] demonstrated in their 13 C NMR and 1 H NMR study that glucose epimerization to mannose using Lewis acids, such as MCl3 in aqueous phase (CrCl3 was also tested), proceeds via two parallel mechanisms: first a reverse C2 → C1 hydride transfer followed by a C1 → C2 intramolecular carbon shift.They also report that MCl3 are also able to epimerize glucose to mannose in low yields and since fructose formation is predominant, the hydride transfer is the more dominant pathway of glucose conversion [34].S2 and S3) shows the effect of time on the yield of glucose, mannose and HMF from cellulose at 100 and 120 °C for 72 h using tungsten and molybdenum oxide-based POMs as catalysts.In the case of the molybdenum oxide-based POM, prolonging the reaction time improved the HMF yield at 100 °C and the plateau in its concentration was not achieved by 72 h.The same trend held true for the yields of glucose and mannose.At 120 °C, glucose and mannose were not detected and the maximum HMF yield remained lower than the yield obtained at 100 °C.The maximum HMF yield, which was achieved at 24 h, was 52% lower, and furthermore, it started to decrease with a longer reaction time.In the case of the tungsten oxide-based POM, prolonging the reaction time at In the case of the molybdenum oxide-based POM, prolonging the reaction time improved the HMF yield at 100 • C and the plateau in its concentration was not achieved by 72 h.The same trend held true for the yields of glucose and mannose.At 120 • C, glucose and mannose were not detected and the maximum HMF yield remained lower than the yield obtained at 100 • C. The maximum HMF yield, which was achieved at 24 h, was 52% lower, and furthermore, it started to decrease with a longer reaction time.In the case of the tungsten oxide-based POM, prolonging the reaction time at 100 • C improved the glucose yield up to 24 h and then a plateau was achieved.The HMF yield increased slowly for 72 h.Eminov et al. [7] reported that the highest HMF yield with CrCl 3 •6H 2 O as a catalyst in [BMIM]Cl was obtained at 120 • C and it was 5 times higher than the yield obtained at 100 • C. In this work, the temperature was also increased by 20 • C, yet the ability to convert glucose to HMF was not improved.Instead, the opposite effect was observed: glucose was not present in any sample and the maximum HMF yield was achieved at 8 h, remaining 81.4% lower than the result obtained at 100 • C. According to the literature the lower yield could be caused by humin formation at higher temperatures [36].Possible humin formation is also supported by the fact that a dark precipitate was formed when the higher temperature was used.

Cellulose Loading and the Efficiency of POM Formation
Chidambaram and Bell [22] reported that in [BMIM]Cl at 120 • C 3% of glucose is converted to humin even without using a catalyst.During the investigated process humins can be also formed due to the oligomerization of glucose or fructose with itself as well as with HMF.However, this is inhibiting the conversion of cellulose to shorter oligomers and glucose [36,37].The of glucose and conversion to the other products must be balanced well to avoid the formation of humins.Thereby, cellulose loadings of 5 and 10 wt % were selected to investigate the effectivity of HMF formation at 120 • C.
Figure 4 (Table S4) shows the results for conversion of cellulose to HMF in [BMIM]Cl at 120 • C by using tungsten and molybdenum oxide-based POMs at 5 wt % and 10 wt % substrate loading.The HMF yield followed the same trend in spite of substrate loading for both the catalysts used.In the case of the molybdenum oxide-based POM-IL the maximum HMF yield was achieved at 24 h and was 52.2% of the maximum yield obtained with a 10 wt % catalyst loading.The maximum HMF yield for the tungsten oxide-based catalyst was achieved during 8 h and made 46.8% of the yield obtained with a 10% substrate loading.In addition, all samples obtained from 48 and 72 h experiments contained dark colored precipitate that was most probably humin.Lowering the substrate loading did not improve the conversion to HMF. catalyst in [BMIM]Cl was obtained at 120 °C and it was 5 times higher than the yield obtained at 100 °C.In this work, the temperature was also increased by 20 °C, yet the ability to convert glucose to HMF was not improved.Instead, the opposite effect was observed: glucose was not present in any sample and the maximum HMF yield was achieved at 8 h, remaining 81.4% lower than the result obtained at 100 °C.According to the literature the lower yield could be caused by humin formation at higher temperatures [36].Possible humin formation is also supported by the fact that a dark precipitate was formed when the higher temperature was used.

Cellulose Loading and the Efficiency of POM Formation
Chidambaram and Bell [22] reported that in [BMIM]Cl at 120 °C 3% of glucose is converted to humin even without using a catalyst.During the investigated process humins can be also formed due to the oligomerization of glucose or fructose with itself as well as with HMF.However, this is inhibiting the conversion of cellulose to shorter oligomers and glucose [36,37].The formation of glucose and conversion to the other products must be balanced well to avoid the formation of humins.Thereby, cellulose loadings of 5 and 10 wt % were selected to investigate the effectivity of HMF formation at 120 °C.
Figure 4 (Table S4) shows the results for conversion of cellulose to HMF in [BMIM]Cl at 120 °C by using tungsten and molybdenum oxide-based POMs at 5 wt % and 10 wt % substrate loading.The HMF yield followed the same trend in spite of substrate loading for both the catalysts used.In the case of the molybdenum oxide-based POM-IL the maximum HMF yield was achieved at 24 h and was 52.2% of the maximum yield obtained with a 10 wt % catalyst loading.The maximum HMF yield for the tungsten oxide-based catalyst was achieved during 8 h and made 46.8% of the yield obtained with a 10% substrate loading.In addition, all samples obtained from 48 and 72 h experiments contained dark colored precipitate that was most probably humin.Lowering the substrate loading did not improve the conversion to HMF.S5 and S6) shows the cellulose degradation at 100 °C for 72 h to evaluate the efficiency of POM formation in the IL medium.The catalyst (phosphotungstic acid hydrate) was added either 20 min before or 3 h after the substrate.
The highest glucose and HMF yields were when the catalyst was added to the sample before the substrate, with respective yields at 73.7% and 68.4% higher.These results show that the formation of POM is more efficient when the catalyst was added before the substrate.S5 and S6) shows the cellulose degradation at 100 • C for 72 h to evaluate the efficiency of POM formation in the IL medium.The catalyst (phosphotungstic acid hydrate) was added either 20 min before or 3 h after the substrate.
The highest glucose and HMF yields were when the catalyst was added to the sample before the substrate, with respective yields at 73.7% and 68.4% higher.These results show that the formation of POM is more efficient when the catalyst was added before the substrate.

Effect of the Water Content of the Reaction Medium on the Conversion of Cellulose to HMF
Some data is available from the literature on metal catalysts.Zhang et al. [10] reported an increase of HMF yield from glucose in the presence of a higher amount of water in [EMIM]Cl when CrCl2 was used as a catalyst.From the other side, Zhao et al. [12] reported that water has no influence on reaction yields.No data was available for POM-s.Since [BMIM]Cl is a hydroscopic ionic liquid, the influence of water content on the reaction dynamics by using tungsten oxide-based POM as catalysts was studied (Figure 6, Tables S7 and S8).The efficiency of HMF conversion and the influence of the reaction medium water content on the process were evaluated at 100 °C for 72 h.Tungsten (VI) and molybdenum (VI) are expected to form POMs with imidazolium-based ILs.POMs are a class of anionic metal-oxygen clusters built by the connection of [MO]x polyhedral of the early transition metals in their highest oxidation states [38].
In the case of the tungsten oxide-based POM, the highest glucose and HMF yields in the presence of water were respectively 76.3% and 67.4% lower.The same tendency was observed with the molybdenum oxide-based POM-IL: the yields of glucose, mannose and HMF were correspondingly 72.7%, 59.2% and 52.8% lower in the presence of water.The experiment showed that increasing the water content resulted in the loss of catalytic activity of both the catalysts used.

Effect of the Water Content of the Reaction Medium on the Conversion of Cellulose to HMF
Some data is available from the literature on metal catalysts.Zhang et al. [10] reported an increase of HMF yield from glucose in the presence of a higher amount of water in [EMIM]Cl when CrCl 2 was used as a catalyst.From the other side, Zhao et al. [12] reported that water has no influence on reaction yields.No data was available for POM-s.Since [BMIM]Cl is a hydroscopic ionic liquid, the influence of water content on the reaction dynamics by using tungsten oxide-based POM as catalysts was studied (Figure 6, Tables S7 and S8).The efficiency of HMF conversion and the influence of the reaction medium water content on the process were evaluated at 100 • C for 72 h.

Effect of the Water Content of the Reaction Medium on the Conversion of Cellulose to HMF
Some data is available from the literature on metal catalysts.Zhang et al. [10] reported an increase of HMF yield from glucose in the presence of a higher amount of water in [EMIM]Cl when CrCl2 was used as a catalyst.From the other side, Zhao et al. [12] reported that water has no influence on reaction yields.No data was available for POM-s.Since [BMIM]Cl is a hydroscopic ionic liquid, the influence of water content on the reaction dynamics by using tungsten oxide-based POM as catalysts was studied (Figure 6, Tables S7 and S8).The efficiency of HMF conversion and the influence of the reaction medium water content on the process were evaluated at 100 °C for 72 h.Tungsten (VI) and molybdenum (VI) are expected to form POMs with imidazolium-based ILs.POMs are a class of anionic metal-oxygen clusters built by the connection of [MO]x polyhedral of the early transition metals in their highest oxidation states [38].
In the case of the tungsten oxide-based POM, the highest glucose and HMF yields in the presence of water were respectively 76.3% and 67.4% lower.The same tendency was observed with the molybdenum oxide-based POM-IL: the yields of glucose, mannose and HMF were correspondingly 72.7%, 59.2% and 52.8% lower in the presence of water.The experiment showed that increasing the water content resulted in the loss of catalytic activity of both the catalysts used.Tungsten (VI) and molybdenum (VI) are expected to form POMs with imidazolium-based ILs.POMs are a class of anionic metal-oxygen clusters built by the connection of [MO]x polyhedral of the early transition metals in their highest oxidation states [38].

Catalytic Formation of HMF from Cellulose
In the case of the tungsten oxide-based POM, the highest glucose and HMF yields in the presence of water were respectively 76.3% and 67.4% lower.The same tendency was observed with the molybdenum oxide-based POM-IL: the yields of glucose, mannose and HMF were correspondingly 72.7%, 59.2% and 52.8% lower in the presence of water.The experiment showed that increasing the water content resulted in the loss of catalytic activity of both the catalysts used.

Catalytic Formation of HMF from Cellulose
All experiments were carried out under aerobic conditions using dried ionic liquids; however, IL was handled and weighed as quickly as possible to prevent further absorption of water.All the catalysts used were in their hydrated form.Catalysts CrCl 3 , ZnCl 2 , MgCl 2 , phosphotungstic acid hydrate, phosphomolybdic acid hydrate and microcrystalline cellulose were obtained from Sigma-Aldrich (Sigma-Aldrich, Steinheim, Germany) and were used as received.[BMIM]Cl was obtained from IoLiTec (Ionic Liquids Technologies GmbH, Heilbronn, Germany) and was vacuum-dried before use.The IL water content, which was checked by Karl-Fischer-Titration, was 0.6-0.7%.Catalyst loading was 10 wt % of the substrate in all cases, the substrate loading was 10 wt % from the solvent in most cases, if not otherwise stated, and the sample typically contained 1 g of IL.The experiments were carried out on a magnetic stirrer plate at 100 or 120 • C in open flasks with constant stirring.All the concentrations of oligo-and monosaccharides and HMF in reaction media were determined by CE and were analyzed at least in triplicate [23].At first, the catalyst was dissolved in IL and after 20 min the cellulose (substrate) was added to the reaction mixture.The samples to compare different catalysts (Table 1) were collected at 24 h after the addition of cellulose.Unusually, a long reaction time (considering the speed of CrCl 3 catalyst) was chosen because preliminary testing showed a slow conversion for molybdenum and tungsten oxide-based POMs.

Analysis
All the samples were analyzed by capillary electrophoresis and the yields were calculated based on calibration curves constructed using authentic standards.CE separations were performed using an Agilent 3D instrument (Agilent Technologies, Waldbronn, Germany) equipped with a diode array UV/Vis detector.Data acquisition and instrument control were carried out using Agilent Technologies HP 3D Chemstation software.The separation was performed using a fused silica capillary with an effective length of 61.5 cm (total length 70 cm) and ID of 22.5 µm (Polymicro Technologies Inc., Wilmington, DE, USA).Capillary walls contained a semi-permanent coating with [C 14 MIM]Cl that was added to the background electrolyte (BGE).The BGE was composed of 138 mM NaOH, 40 mM maleic acid and 5 mM [C 14 MIM]Cl.The samples were injected hydrodynamically under a pressure of 50 mbar for 20 s and the separations were performed at 25 • C by using a voltage of −21 kV.The detection wavelength was 210 nm in the case of carbohydrates and 270 nm for HMF.Before each run the capillary was filled with BGE for 7 min and between the runs it was flushed with 1 M NaOH for 2 min and ultrapure water for 3 min.BGE was prepared on the first day and stored at room temperature for one month.All these conditions were developed in our previous study [23].Standards used to construct calibration curves and BGE substances, namely D-(+)-glucose, D-(−)-fructose, D-(+)-mannose, D-(+)-cellobiose, sucrose, HMF, maleic acid and NaOH, were obtained from Sigma-Aldrich and were used as received.[C 14 MIM]Cl was obtained from IoLiTec and was vacuum dried before use.

Conclusions
It has been shown that tungsten and molybdenum oxide-based polyoxometalates were able to decompose cellulose.The main decomposition products were carbohydrates such as glucose and mannose.The ability of the polyoxometalates to convert glucose to 5-hydroxymethylfurfural remained low in the mild conditions used and the overall product yields with the use of the tungsten oxide-based polyoxometalates remained 28.6% lower compared to the yield obtained with CrCl 3 .It was expected that increasing the temperature would improve the conversion of HMF but, surprisingly, increasing the temperature by 20 • C did not increase the HMF outcome.The increase of the water content of the reaction medium, an influencing factor in fructose dehydration, resulted in the loss of catalytic activity of tungsten and molybdenum oxide-based polyoxometalates.

Supplementary Materials:
The following are available online at http://www.mdpi.com/2304-6740/6/3/78/s1,Table S1: Glucose, mannose and HMF contents in cellulose samples degraded in [BMIM]Cl using ZnCl 2 , MgCl 2 , CrCl 3 , tungsten (W-POM) and molybdenum (Mo-POM) oxide-based POMs as catalysts, Table S2: Conversion of cellulose to glucose, mannose and HMF in [BMIM]Cl at 100 and 120 • C by using POMs based on molybdenum oxide, Table S3: Conversion of cellulose to glucose, mannose and HMF in [BMIM]Cl at 100 and 120 • C by using POMs based on tungsten oxide, Table S4: Efficiency of cellulose degradation in [BMIM]Cl at 100 • C by using phosphotungstic acid hydrate added 20 min before the substrate, Table S5: Conversion of cellulose to HMF in [BMIM]Cl at 120 • C by using tungsten and molybdenum oxides-based POMs at 5 and 10% substrate loading, Table S6: Efficiency of cellulose degradation in [BMIM]Cl at 100 • C by using phosphotungstic acid hydrate added 3 h after the substrate, Table S7: Conversion of cellulose to glucose, mannose and HMF in [BMIM]Cl at 100 • C in the presence of water (10 wt % of solvent) by using POMs based on tungsten oxide, Table S8: Conversion of cellulose to glucose, mannose and HMF in [BMIM]Cl at 100 • C in the presence of water (10 wt % of solvent) by using POMs based on (a) tungsten oxide, (b) molybdenum oxide.
Author Contributions: T.A. and M.V. conceived and designed the experiments; T.A. performed the experiments; T.A. and M.V. analyzed the data; M.V. and M.L. contributed reagents/materials/analysis tools.The manuscript was written through contributions of all authors.
Funding: This research received no external funding.

Figure 1 .
Figure 1.Typical platform chemicals produced from the catalytic transformations of cellulose.

Figure 1 .
Figure 1.Typical platform chemicals produced from the catalytic transformations of cellulose.

Figure 3 (
Figure 3 (TablesS2 and S3) shows the effect of time on the yield of glucose, mannose and HMF from cellulose at 100 and 120 °C for 72 h using tungsten and molybdenum oxide-based POMs as catalysts.

Figure 3 .
Figure 3. Conversion of cellulose to glucose, mannose and HMF in [BMIM]Cl at 100 and 120 °C by using POMs based on (a) molybdenum oxide and (b) tungsten oxide.Catalyst loading was 10 wt % from cellulose and cellulose loading was 10 wt % from solvent.

Figure 3 (
Figure 3 (TablesS2 and S3) shows the effect of time on the yield of glucose, mannose and HMF from cellulose at 100 and 120 °C for 72 h using tungsten and molybdenum oxide-based POMs as catalysts.

Figure 3 .
Figure 3. Conversion of cellulose to glucose, mannose and HMF in [BMIM]Cl at 100 and 120 °C by using POMs based on (a) molybdenum oxide and (b) tungsten oxide.Catalyst loading was 10 wt % from cellulose and cellulose loading was 10 wt % from solvent.

Figure 3 .
Figure 3. Conversion of cellulose to glucose, mannose and HMF in [BMIM]Cl at 100 and 120 • C by using POMs based on (a) molybdenum oxide and (b) tungsten oxide.Catalyst loading was 10 wt % from cellulose and cellulose loading was 10 wt % from solvent.

Figure 4 .
Figure 4. Conversion of cellulose to HMF in [BMIM]Cl at 120 °C by using tungsten and molybdenum oxide-based POMs at 5 and 10% substrate loading.Catalyst loading was 10 wt % from cellulose and cellulose loading was 5 or 10 wt % from solvent.

Figure 5 (
Figure 5 (TablesS5 and S6) shows the cellulose degradation at 100 °C for 72 h to evaluate the efficiency of POM formation in the IL medium.The catalyst (phosphotungstic acid hydrate) was added either 20 min before or 3 h after the substrate.The highest glucose and HMF yields were when the catalyst was added to the sample before the substrate, with respective yields at 73.7% and 68.4% higher.These results show that the formation of POM is more efficient when the catalyst was added before the substrate.

Figure 4 .
Figure 4. Conversion of cellulose to HMF in [BMIM]Cl at 120 • C by using tungsten and molybdenum oxide-based POMs at 5 and 10% substrate loading.Catalyst loading was 10 wt % from cellulose and cellulose loading was 5 or 10 wt % from solvent.

Figure 5 (
Figure 5 (TablesS5 and S6) shows the cellulose degradation at 100 • C for 72 h to evaluate the efficiency of POM formation in the IL medium.The catalyst (phosphotungstic acid hydrate) was added either 20 min before or 3 h after the substrate.The highest glucose and HMF yields were when the catalyst was added to the sample before the substrate, with respective yields at 73.7% and 68.4% higher.These results show that the formation of POM is more efficient when the catalyst was added before the substrate.

Figure 5 .
Figure 5. Efficiency of cellulose degradation in [BMIM]Cl at 100 °C by using phosphotungstic acid hydrate added (a) 20 min before the substrate, (b) 3 h after the substrate.Catalyst loading was 10 wt % from cellulose and cellulose loading was 10 wt % from solvent.

Figure 6 .
Figure 6.Conversion of cellulose to glucose, mannose and HMF in [BMIM]Cl at 100 °C in the presence of water (10 wt % of solvent) by using POMs based on (a) tungsten oxide, (b) molybdenum oxide.Catalyst loading was 10 wt % from cellulose and cellulose loading was 10 wt % from solvent.

Figure 5 .
Figure 5. Efficiency of cellulose degradation in [BMIM]Cl at 100 • C by using phosphotungstic acid hydrate added (a) 20 min before the substrate, (b) 3 h after the substrate.Catalyst loading was 10 wt % from cellulose and cellulose loading was 10 wt % from solvent.

Figure 5 .
Figure 5. Efficiency of cellulose degradation in [BMIM]Cl at 100 °C by using phosphotungstic acid hydrate added (a) 20 min before the substrate, (b) 3 h after the substrate.Catalyst loading was 10 wt % from cellulose and cellulose loading was 10 wt % from solvent.

Figure 6 .
Figure 6.Conversion of cellulose to glucose, mannose and HMF in [BMIM]Cl at 100 °C in the presence of water (10 wt % of solvent) by using POMs based on (a) tungsten oxide, (b) molybdenum oxide.Catalyst loading was 10 wt % from cellulose and cellulose loading was 10 wt % from solvent.

Figure 6 .
Figure 6.Conversion of cellulose to glucose, mannose and HMF in [BMIM]Cl at 100 • C in the presence of water (10 wt % of solvent) by using POMs based on (a) tungsten oxide, (b) molybdenum oxide.Catalyst loading was 10 wt % from cellulose and cellulose loading was 10 wt % from solvent.