Evaluation of Rate of Adhesion of Lactobacillus namurensis Strain GYP-74 to Porous Fine Ceramics

: This study aimed to evaluate the ratio of adherence of lactic acid bacteria (LAB) to porous ﬁne ceramics in order to develop a novel LAB-rich pickle container for the production of functional fermented vegetables. Some LAB were isolated from the salted rice bran used for pickling (Nukadoko in Japanese). These isolates were classiﬁed in Lactobacillus namurensis by phylogenetic analysis. Some pottery-shard (PS) samples were prepared by varying the mixing rate of polyacetal (POM) resin to clay (0–30% ( v/v )) and the burning temperature (1000 ◦ C or 1100 ◦ C). A test of the adherence of strain GYP-74 to the PSs was performed. The results showed that the adherence rate was signiﬁcantly higher in the PSs burned at 1100 ◦ C as compared with those burned at 1000 ◦ C. A pore distribution analysis showed that pore sizes of less than a few µ m and pore sizes in the range of a few µ m to a few hundred µ m were mainly distributed in the PSs without and with POM, respectively. X-ray diffraction analysis showed that both PSs with and without POM contained quartz and hematite. The PSs burned at 1000 ◦ C and 1100 ◦ C speciﬁcally contained microcline and mullite, respectively. This study revealed the basal information regarding what makes PSs adequate for LAB adhesion.


Introduction
Miyazaki Prefecture, Japan, set forth the food business promotion plan in 2013 and set the efficient utilization of local foods including vegetables with added value as a basic objective. Under this plan, the creation of novel local industry in the field of fisheries is expected to occur based on an industry-academia-government collaboration. In Miyazaki, the production of white radish is ranked fifth in Japan, and fermented radishes in a salted rice bran bed (Nukazuke in Japanese) are a very well-known food. Nukazuke is fermented by various microbes in salted rice bran (Nukadoko in Japanese). The storage of the Nukadoko depends on natural fermentation by microbes. In other words, Nukadoko produces the complex microflora. It has been reported that the bacterial flora in Nukadoko mainly contains lactic acid bacteria (LAB) [1,2]. Through the fermentation of LAB, a fermented flavor which is mainly based on the formation of volatile organic acids was formed and coupled with an umami flavor. In rice bran products, LAB contributes to the taste and long-term preservation. Surprisingly, Nukadoko can be kept without spoilage for 100 years [1].
Eating fermented food containing sufficient LAB cells is considered to be the ingestion of "probiotics". Some species of LABs have been identified as probiotics for various host animals including aquacultured species [3][4][5]. Generally, probiotics are defined as live microbial feed additives that improve the microbial condition of the host animal's gastrointestinal tract [6]. Probiotics include components of microbial cells that stimulate the immune system against pathogens [7]. Probiotics can improve the health of the host in mammalians, including humans, and in aquaculture species [8,9]. The effects of probiotics in humans have been reported to include improvement in the resistance to infectious disease, the modification of blood lipid profiles and blood pressure, growth enhancement for undernourished young children, the prevention of vaginal infections and inflammatory bowel diseases, inhibition of diarrhea, and protection against Helicobacter pylori colonization of the stomach [10][11][12][13][14]. In addition, some LAB species produce functional and bioactive substances such as γ-amino butyric acids (GABA). GABA is synthesized from L-glutamic acids by L-glutamate decarboxylase [15] and provides beneficial effects in humans such as stress relief and decreasing the blood pressure [16].
This evidence indicates that the ingestion of fermented foods such as Nukazuke is good for human health. Thus, we planned to develop a specific fermentation container to enrich the LAB cells to efficiently and sufficiently supply LAB to consumers. The goal was to develop a container with a surface to which LAB can easily adhere. Bacterial adhesion to a solid surface is the first step in the production of extracellular polymeric substances (EPS) and the formation of biofilm and colonies [17,18]. EPS are especially well known to be an important factor in bacterial adhesion in bridging between the cell surface and the surface of the materials. Generally, bacteria easily or willingly adhere to rough surfaces or to the insides of pores. It is well known that surface roughness is an important factor for the attachment of bacterial cells to surfaces prior to biofilm formation. In the first step, bacteria migrate towards the materials, and the bacterial cells move to the surface of the materials by their motility or by passive moving based on the Brownian motion [19][20][21]. In the next step, bacterial cells move close to the surface, and irreversible binding between cells and surface occurs. Similarly, the bacterial attachment is very complex due to the hydrophobicity and chemistry of the surface, flow conditions, and cell structures [20,[22][23][24]. In case of Staphylococcus aureus, the presence of nanoscale roughness on a steel surface induced an increase in bacterial attachment to a steel surface [25]. In the field of wastewater treatment, selection of materials is a key factor for induction of initial formation of bacterial biofilms. In the case of four bacterial strains (Alcaligenes faecalis, Cytophaga hutchinsonii, Bacillus subtilis and Escherichia coli), carbon fiber is considered as one of the support materials for biofilms for wastewater treatment [26]. Flagella are known to be a bacterial adhesive factor. Song et al. reported that the flagella play a role in increasing the contact with the surface [27]. On the other hand, research on protecting against the adherence of harmful bacterial by reducing the contact area has been carried out. These findings indicated that the bacterial adhesion to materials, such as the container used for bacterial fermentation, can be increased by controlling the roughness and pore size of the surface and by enlarging the contact area.
This study aimed to examine the characteristics of pottery that are adequate for LAB adhesion. The adherence ratio of the LAB isolated from the salted rice bran bed was evaluated with pottery shards (PS) with different resin sizes and contents, and that were fired at different temperatures. In this study, especially, we focused on porous ceramics as the material and the relationship between the pore sizes and the adherence ratio of LAB.

Isolation of LAB
The salted rice bran used for pickling (Nukadoko) maintained by Kimura Tsukemono Miyazaki Kougyo Co. Ltd., Miyazaki, Japan, was used for the isolation of LAB. Samples to Processes 2021, 9, 658 3 of 11 isolate LAB were suspended in a sterile physiological saline solution (0.85% NaCl (w/v)), shaken vigorously and left for 10 min at room temperature. The solution, except for precipitate, was serially diluted in a physiological saline solution, and the diluted samples were plated on de Man, Rogosa and Sharpe (MRS) agar plate medium consisting of 2 g glucose, 0.5 g yeast extract, 1 g peptone, 1 g meat extract, 0.5 g sodium acetate, 0.2 g ammonium citrate, 10 mg MgSO 4 ·7H 2 O, 5 mg MnSO 4 ·5H 2 O, 0.2 g K 2 HPO 4 ·7H 2 O, 2 mL tween 80 (50 mg/mL distilled water), 1.5 g agar and 100 mL distilled water (pH 6.5). These plates were incubated at 28 • C for 24-48 h.
The white colonies were randomly picked up and streaked on Glucose-Yeast-Peptone (GYP) agar consisting of 1 g glucose, 1 g yeast extract, 0.5 g peptone, 0.2 g meat extract, 0.2 g sodium acetate, 0.5 mL salt solution (MgSO 4 ·7H 2 O 40 mg, MnSO 4 ·5H 2 O 20 mg, FeSO 4 ·7H 2 O 2 mg, NaCl 2 mg per 1 mL distilled water), 1 mL tween 80 (50 mg/mL distilled water), 1.5 g agar and 100 mL distilled water (pH 6.8) containing 0.5% CaCO 3 (w/v) as an indicator for acid production. These plates were incubated at 28 • C for 24-72 h. This study has been approved by the research ethics committee in the Department of Marine Biology and Environmental Sciences, University of Miyazaki.

DNA Extraction of Strain GYP-74 and Amplification of 16S rRNA Gene by Polymerase Chain Reaction (PCR)
Total genomic DNA was extracted from cultured cells of strain GYP-74 in GYP liquid medium according to the method of Vural and Ozgun with a slight modification [28]. The cells suspended in 400 µL of Tris-EDTA (TE) buffer (10 mM Tris-HCl (pH 8.0) and 1 mM Ethylenediaminetetraacetic acid (EDAT)) were mixed with 20 µL protease K (6 mg/mL) and 80 µL sodium dodecyl sulfate (5%, w/v) at 60 • C for 2 h. The cell lysates were subsequently treated with phenol/chloroform and precipitated with 99.5% ethanol solution and 3M (w/v) sodium acetate solution. The DNA pellet was subsequently washed with 70% ethanol solution. The DNA pellet was dried in a vacuum desiccator and re-suspended in 50 µL of TE buffer. The solution was used as a template DNA solution for polymerase chain reaction (PCR) assay.

Basic Local Alignment Search Tool (BLAST) Analysis and Construction of Phylogenetic Tree
The nucleotide sequence of 16S rRNA of strain GYP-74 was deposited in the database of the National Center for Biotechnology Information (NCBI). The closest known relatives of the partial 16S rRNA gene sequence were searched using the BLAST method [30] and the sequence data set of 16S rRNA of LAB including strain GYP-74 were aligned together using CLUSTALX version 1.83 [31]. Pairwise evolutionary distances were calculated according to the model of , and the phylogenetic trees were constructed by the neighbor-joining statistical method [33] using Mega version 7.0 [34]. Bootstrap values were set at 1000 replications.

Adherent Test of Strain GYP-74 to PS and Morphological Observation with a Scanning Electron Microscope (SEM)
Strain GYP-74 was selected based on phylogenetic analysis and growth rate, and used for further experiments. PS was prepared for the adherence test. Clay was fired at 1000 • C or 1100 • C with or without polyacetal (POM; pore size 0.2 mm or 0.5mm, blending amount 0, 10, 20 and 30%). PS was prepared by cutting the fired clay.
Each PS (approx. 5 × 5 mm) was weighed and added to a test tube containing 1/100 strength MRS broth. As a control, a silicon shard was used. These test tubes were sterilized by autoclaving, and strain GYP-74 pre-cultured in MRS broth was added to the test tubes at 10 5 cfu/mL. The test tubes were incubated at 27 • C for 45 h. After incubation, each PS was aseptically collected and washed with 5 mL of sterile 0.85% (w/v) NaCl solution three times. The washed PS was crushed well in a mortar using a pestle, and serially diluted with sterile 0.85% (w/v) NaCl solution. Each dilution was inoculated on an MRS agar plate medium and incubated at 30 • C for 72 h. The colony number on the plate was counted to calculate the cells adherent to PS.
The remaining PS was fixed with glutaraldehyde solution and dehydrated with ethanol solutions as described above. The samples were mounted on an aluminum SEM stub with carbon conductive tape. The cells attached to the surface of PS and to the pores were observed and photographed with an SEM (SU3500, Hitachi, Tokyo, Japan). The cells of strain GYP-74 cultured in MRS medium were also observed with an SEM to confirm the cell morphology.

Analysis of the Pore Distribution Using a Mercury Porosimeter
The pore distributions were analyzed using a mercury porosimeter (AutoPore IV 9500, Micromeritics Instrument Corporation, Norcross, GA, USA). The various PSs were fired into a circular cylindrical shape. The diameter and height were about 10 and 15 mm, respectively.

X-ray Diffraction Analysis of the PS
The various PSs were powdered and measured using an X-ray diffractometer (X'Part PRO MRD, PANalytical, Almelo, The Netherlands) with CuKα radiation to identify the crystalline form. The range of the measured angle was from 10 to 70 degrees. The crystal form was identified by comparing it with the obtained diffraction pattern and the powder diffraction file database released by the International Center for Diffraction Data.

Statistical Analysis
Experimental data were analyzed using one way analysis of variance followed by the Tukey-Kramer test (BellCurve for Excel, Social Survey Research Information Co., Ltd., Tokyo, Japan).

Isolation of LAB and Identification Based on Morphological Observation, BLAST Research and Phylogenetic Analysis
Twenty strains were isolated from the salted rice bran bed. A partial length of the 16S rRNA gene nucleotide sequence (1449 bp) of strain GYP-74 was deposited in the data bank with accession number LC327006. Figure 1 shows the result of phylogenetic analysis. The 16S rRNA gene sequence of strain GYP-74 used in the adherence test was located in the cluster of Lactobacillus namurensis. BLAST searches also confirmed the identities (on the basis of the highest score obtained) as L. namurensis NBRC 107158. The morphological observation with an SEM showed that the cell form of strain GYP-74 was rod-shaped ( Figure 2). cluster of Lactobacillus namurensis. BLAST searches also confirmed the identities (on the basis of the highest score obtained) as L. namurensis NBRC 107158. The morphological observation with an SEM showed that the cell form of strain GYP-74 was rod-shaped (Figure 2). Nakayama et al. reported that two species, L. namurensis and L. acetotolerans were the dominant LAB in Nukadoko [2]. Sakamoto et al. reported that the doubling time was significantly different between L. namurensis (6.2 h) and L. acetotolerancs (92.9 h), and that it was difficult to culture L. acetotolerancs [1]. Some studies reported that various fermented foods by LAB such as Nukazuke with L. namurensis as a dominant LAB, fermented milk and fish sauce showed a blood pressure-reducing effect (angiotensin converting enzyme inhibitory effect) and antioxidant activities [35][36][37]. Enrichment of some LAB to porous ceramics has potential for the improvement of lifestyle-related diseases.   Figure 3 shows the number of cells that were adherent to the PS. In the control, no adherent cells were observed. In the case of PS without POM or with POM with the same pore size, the adherent cell numbers in PS burned at 1100 °C were significantly higher than those in PS burned at 1000 °C. The blending quantity of POM in PS influenced the adherence ratio of strain GYP-74. In the case of a 0.2 mm pore size fired at 1100 °C, the adherent ratio was significantly higher at the 30% POM-blending quantity (#7) than for was difficult to culture L. acetotolerancs [1]. Some studies reported that various fermented foods by LAB such as Nukazuke with L. namurensis as a dominant LAB, fermented milk and fish sauce showed a blood pressure-reducing effect (angiotensin converting enzyme inhibitory effect) and antioxidant activities [35][36][37]. Enrichment of some LAB to porous ceramics has potential for the improvement of lifestyle-related diseases. Figure 3 shows the number of cells that were adherent to the PS. In the control, no adherent cells were observed. In the case of PS without POM or with POM with the same pore size, the adherent cell numbers in PS burned at 1100 • C were significantly higher than those in PS burned at 1000 • C. The blending quantity of POM in PS influenced the adherence ratio of strain GYP-74. In the case of a 0.2 mm pore size fired at 1100 • C, the adherent ratio was significantly higher at the 30% POM-blending quantity (#7) than for other groups (#5 and #6). In the case with a 0.5 mm pore size at 1100 • C, the adherence ratio was significantly lower at the 30% POM-blending quantity (#13) than for other groups (#11 and #12). The highest adherence ratio was observed among all groups at 0.2-mm pore size, a 1100 • C firing temperature and a 30% POM blending quantity (#7). Figure 4 shows pictures of the surface of the clay without resin fired at 1000 • C (#1) and the 30% POM resin-containing PS fired at 1100 • C by electron microscopic observation. Numerous cells were observed on the surface of #13 as compared with #1. In particular, the cells adhered locally to the hollow parts of the pores.  Figure 3 shows the number of cells that were adherent to the PS. In the control, no adherent cells were observed. In the case of PS without POM or with POM with the same pore size, the adherent cell numbers in PS burned at 1100 °C were significantly higher than those in PS burned at 1000 °C. The blending quantity of POM in PS influenced the adherence ratio of strain GYP-74. In the case of a 0.2 mm pore size fired at 1100 °C, the adherent ratio was significantly higher at the 30% POM-blending quantity (#7) than for other groups (#5 and #6). In the case with a 0.5 mm pore size at 1100 °C, the adherence ratio was significantly lower at the 30% POM-blending quantity (#13) than for other groups (#11 and #12). The highest adherence ratio was observed among all groups at 0.2mm pore size, a 1100 °C firing temperature and a 30% POM blending quantity (#7). Figure 4 shows pictures of the surface of the clay without resin fired at 1000 °C (#1) and the 30% POM resin-containing PS fired at 1100 °C by electron microscopic observation. Numerous cells were observed on the surface of #13 as compared with #1. In particular, the cells adhered locally to the hollow parts of the pores.    Figure 5 shows the result of an analysis of the pore distribution using a mercury porosimeter. In the case of PS without POM (only clay) fired at 1000 °C, the pore diameter distribution of the porous body was 0.4-50 µm, and mainly concentrated to 1 µm (Figure  Figure 5 shows the result of an analysis of the pore distribution using a mercury porosimeter. In the case of PS without POM (only clay) fired at 1000 • C, the pore diameter distribution of the porous body was 0.4-50 µm, and mainly concentrated to 1 µm (Figure 5 #1). By increasing the firing temperature to 1100 • C, the peak value shifted to 4-5 µm (Figure 5 #2). A tendency of the peak value to increase with the increase in the burning temperature was observed in the case of PS with POM ( Figure 5 #4, #6, #9 and #12). The peak value obviously increased to more than 10 µm with the addition of POM irrespective of the change in the firing temperatures. The results of the adherence test showed that the number of adherent cells was higher in the POM-containing PS fired at 1000 • C (Figure 3).  Figure 5 shows the result of an analysis of the pore distribution using a mercury porosimeter. In the case of PS without POM (only clay) fired at 1000 °C, the pore diameter distribution of the porous body was 0.4-50 µm, and mainly concentrated to 1 µm ( Figure  5 #1). By increasing the firing temperature to 1100 °C, the peak value shifted to 4-5 µm (Figure 5 #2). A tendency of the peak value to increase with the increase in the burning temperature was observed in the case of PS with POM ( Figure 5 #4, #6, #9 and #12). The peak value obviously increased to more than 10 µm with the addition of POM irrespective of the change in the firing temperatures. The results of the adherence test showed that the number of adherent cells was higher in the POM-containing PS fired at 1000 °C (Figure 3). Yamamoto et al. described that the adherence ratio of beneficial bacteria to porous fine ceramics was significantly higher in ceramics having more than a 10 µm pore size as compared to those having a less-than-10 µm pore size [38]. This report agrees with our result. Pereira et al. evaluated the retention of bacterial biomass to four types of porous microcarriers (sepiolite, caly, pozzolana, and form glass) with different pore sizes, and found that the attached bacterial biomass was higher in sepiolite (pore size: cell size crevices) and clay (pore size: 10-100 µm) compared to pozzolana and foam glass (having a 10-300 µm and 20-1000 µm pore size, respectively) [39]. The present study and studies by Yamamoto et al. described that the adherence ratio of beneficial bacteria to porous fine ceramics was significantly higher in ceramics having more than a 10 µm pore size as compared to those having a less-than-10 µm pore size [38]. This report agrees with our result. Pereira et al. evaluated the retention of bacterial biomass to four types of porous microcarriers (sepiolite, caly, pozzolana, and form glass) with different pore sizes, and found that the attached bacterial biomass was higher in sepiolite (pore size: cell size crevices) and clay (pore size: 10-100 µm) compared to pozzolana and foam glass (having a 10-300 µm and 20-1000 µm pore size, respectively) [39]. The present study and studies by Yamamoto et al. and Pereira et al. indicate that the adequate pore size for bacterial adhesion is from bacterial cell sizes to less than 100 µm. Rajab et al. reported that the cell length of L. delbrueckii subsp. lactis, L. paracasei, L. acidophilus, and L. rhamnosus was 5.2-7.6 µm, and significantly longer than other Lactobacillus strains, L. sakei subsp. sakei, L. reuteri and L. plantarum with 1.6-2.8 µm cell length [40]. In the present study, the cell length of L. namurensis was estimated to be approximately 2-10 µm by light-microscopic and SEM observation. Figures 3 and 5 show that the adhered cell number was higher in the pottery shards having more than a few µm pore size, which indicates that cell size and pore size affected the cell adherence. Figure 6 shows the results of X-ray diffraction analysis of the PS. In the case of PS fired at 1000 • C (#3), microcline was specifically formed. In the case of PS fired at 1100 • C Processes 2021, 9, 658 8 of 11 (#5), mullite was specifically formed. The quarts and hematite were detected at both temperatures. Generally, a diameter of 10-200 µm is the pore size necessary for excellent microbial growth because fluids containing nutrients have to pass through pores to supply the energy to the bacteria. Kitaoka et al. reported that porous materials prepared from mud mainly consist of silica, and no difference in their chemical characteristics was found [41]. Therefore, it is considered that the space in the porous materials strongly influenced the bacterial adherence.

X-ray Diffraction Analysis
namurensis was estimated to be approximately 2-10 µm by light-microscopic and SEM observation. Figures 3 and 5 show that the adhered cell number was higher in the pottery shards having more than a few µm pore size, which indicates that cell size and pore size affected the cell adherence. Figure 6 shows the results of X-ray diffraction analysis of the PS. In the case of PS fired at 1000 °C (#3), microcline was specifically formed. In the case of PS fired at 1100 °C (#5), mullite was specifically formed. The quarts and hematite were detected at both temperatures. Generally, a diameter of 10-200 µm is the pore size necessary for excellent microbial growth because fluids containing nutrients have to pass through pores to supply the energy to the bacteria. Kitaoka et al. reported that porous materials prepared from mud mainly consist of silica, and no difference in their chemical characteristics was found [41]. Therefore, it is considered that the space in the porous materials strongly influenced the bacterial adherence. Probiotic studies have focused on the adherence to the gastrointestinal tract in host animals. The adherence mechanisms are related to the components present on the surface of the epithelium of the intestine such as mucin, collagens and fibronectin [42,43]. However, it is assumed that the mechanisms of adherence to porous materials are significantly different. The mucus layer which covers the intestinal epithelium of humans consists of two layers: the inner and outer layer. Basically, dominant bacteria in the intestine are detected in only the outer layer, and bacteria show the adherence to mucin which is a main component of mucus in the intestine. Adhesin is known as an adherence factor in bacterial cells which exhibits a receptor-bonding ability in mucin. Many LAB have the adhesion mechanism to intestinal mucus via glycans [44,45]. Holst et al. reported that L. plantarum has a mannose-specific adhesin [46]. The process of bacterial adhesion to intestinal mucus is mainly divided into three steps: (1) adhesion via adhesin, (2) aggregation among bacterial cells, and (3) colonization to the mucus of the intestine [47]. On the other hand, the Probiotic studies have focused on the adherence to the gastrointestinal tract in host animals. The adherence mechanisms are related to the components present on the surface of the epithelium of the intestine such as mucin, collagens and fibronectin [42,43]. However, it is assumed that the mechanisms of adherence to porous materials are significantly different. The mucus layer which covers the intestinal epithelium of humans consists of two layers: the inner and outer layer. Basically, dominant bacteria in the intestine are detected in only the outer layer, and bacteria show the adherence to mucin which is a main component of mucus in the intestine. Adhesin is known as an adherence factor in bacterial cells which exhibits a receptor-bonding ability in mucin. Many LAB have the adhesion mechanism to intestinal mucus via glycans [44,45]. Holst et al. reported that L. plantarum has a mannosespecific adhesin [46]. The process of bacterial adhesion to intestinal mucus is mainly divided into three steps: (1) adhesion via adhesin, (2) aggregation among bacterial cells, and (3) colonization to the mucus of the intestine [47]. On the other hand, the adhesion mechanisms of bacteria to materials such as ceramics are significantly different to those done via glycan.

X-Ray Diffraction Analysis
In the present study, we focus on the relationship between the pore sizes and the ratio of adherence. However, interactions between bacteria and material's surface consist of very complex mechanisms, and bacteria can migrate towards a surface based on physical forces such as gravitational settling, hydrodynamic forces and Brownian motion, and/or their own motility with flagella [21]. Some studies reported that the surface roughness and surface wetting also affect the adherence of bacteria to the material surfaces. Katsikogianni and Missirlis reported that bacteria preferentially adhere to surface irregularities whose typical sizes are of the order of their own diameters [48]. Ammar et al. reconstructed the topography of the bacterial cell and substrate surfaces using Surface Element Integration (SEI) technique. They compared SEI predictions with those of a simple model for surface roughness, results indicated that three parameters linked with the surface roughness have an impact on the height of the energy barrier [49]. Some studies indicated that the cell surface hydrophobicity of S. aureus, known as a major human pathogen, is a main factor for its own adhesion ability, and it harbors the adhesion genes and adhesin genes [22,50]. Slullitel et al. reported that there is no superiority of ceramics against adhesion of biofilm-producing S. aureus and S. epidermidis, and E. coli [51]. Some reports, mainly related to dental implants, have indicated that the surface roughness and wettability influenced bacterial adhesion to materials [48,52]. It is generally known that bacteria prefer to grow on available surfaces of materials than in the aqueous phase [53], and Kirov indicated that this adherent process was related to bacterial chemotaxis and haptotaxis [54]. Taylor et al. found that the surface roughness of poly methyl methacrylate induced a significant increase in bacterial adhesion [55]. In further studies, the surface roughness and hydrophobicity should be measured to comprehensively understand the adhesion mechanism of strain GYP-74. Additionally, implementation of an adherence test with wide varieties of LAB will support the versatility of the fermentation container prepared with porous ceramics. The present study showed that the pore size and the distribution varied by controlling the burning temperature and ratio of the POM content, and the adherent ratio of strain GYP-74 also varied.

Conclusions
This study provided the preliminary data on the relationship between L. namurensis adherence and pore size distribution in porous fine ceramics. In this paper, we isolated L. namurensis strain GYP-74 from salted rice bran (Nukadoko). We report that the distribution of pore size and the crystal form in the PS can be controlled by arranging the firing temperatures. The adhesion rate of strain GYP-74 increased in the PS which had pore sizes greater than their own cell size. When we make the fermentation container to enrich LAB, considering the pore size and the cell size of target LAB makes the adhesion efficiency of LAB cells increase.