Effects of Caustic Extraction on Properties of Viscose Grade Dissolving Pulp

Viscose, a cellulose-based commodity fibre, is produced by pulping and bleaching of wood, yielding a high quality “dissolving pulp” which is then spun. During pulping and bleaching, effective hemicellulose extraction is required to allow fibre production. We present a design of experiments (DoE) approach to optimise caustic extraction in a total chlorine free (TCF) bleaching sequence (O-CE-Z-P) of beech wood sulphite pulp. Temperature and sodium hydroxide concentration were varied to identify highest xylan extraction yield, and a maximum xylan removal of 83% was achieved at 20 ◦C and 120 g/L NaOH. Additionally, caustic extraction conditions were derived from the DoE model that led to pulps with high yield, high alpha cellulose content or uniform cellulose molecular weight distribution. Pulps from verification experiments exhibited good reactivity in viscose application tests. Hence, the presented O-CE-Z-P bleaching sequence can be considered as suitable for integrated viscose fibre production. We assume that the presented caustic extraction model will be useful for pulp and biorefinery researchers who work on caustic biorefinery processes involving hardwood feedstocks.


Introduction
Every year 100 million tons of fibres are produced globally to make textiles and technical products that serve human well-being.Less than half of these fibres are currently made from renewable resources such as cotton or wood [1].From an environmental viewpoint, wood as raw material for cellulose fibre production is beneficial in terms of reduced irrigation water requirements and ecotoxicity, as compared to cotton [1].The production of viscose fibres from wood in an integrated viscose fibre plant (i.e., combined dissolving pulp and viscose production) also produces fewer greenhouse gas emissions than petroleum-based and even bio-based polyethylene terephthalate fibre production [2].
To make viscose fibres, wood chips are initially converted to "brown-stock" pulp using either the kraft or the sulphite process that remove a high amount of non-cellulosic wood constituents such as hemicellulose and lignin.Subsequently, the pulp is further purified by a suitable sequence of bleaching stages to the dissolving pulp quality required by the respective fibre process [3,4].Dissolving pulp is a type of pulp having a high cellulose content (>90%), high purity, brightness, cellulose reactivity, and a uniform molecular weight distribution [3].
Bleaching sequences usually have at least one stage that is aimed at hemicellulose removal, because hemicellulose is process-disturbing in the viscose process [5].This is particularly true for low molecular weight xylan, while high molecular weight xylan might be fibre forming, depending on its morphological distribution in the pulp [6].Typically, hemicellulose reducing bleaching stages are either acidic or alkaline treatments, the latter classified as cold caustic extractions (CCE) at temperatures of 25-45 • C and hot caustic extraction (HCE) at 70-120 • C [7].At higher temperatures, the treatments become rather unspecific and lead to side reactions including acidic or alkaline cellulose degradation [8] and hence the pulp yield of CCE is systematically higher than the pulp yield of HCE [9].Caustic extraction of sulphite pulp is already applied in total chlorine free (TCF) bleaching sequences and with the goal to improve metal removal [10,11], whereas especially HCE of kraft pulp is not reasonable as the pulp was already treated with hot alkali during pulping.Enzymatic removal of residual hemicellulose by xylanases and combinations of caustic extraction and xylanase treatments have also been reported as a more specific means to purify pulp but are known to have a limited effect on dissolving sulphite pulps, with xylan removals being usually lower than 50% [12][13][14][15].
Many reports exist on the effects of caustic extraction on kraft pulp, but papers on caustic extraction of sulphite pulp are rare as well as on its application in a TCF bleaching sequence.Herein, we report on the optimisation of caustic extraction of sulphite pulp, the full analysis of the dissolving pulp after the complete TCF bleaching, and on the application of the obtained hemicellulose poor pulp in viscose fibre production.To the best of our knowledge, this is the first time the TCF bleaching of sulphite pulp including a caustic extraction was studied with respect to the viscose process.

Alkaline Extraction
Never-dried beech sulphite pulp, which was delignified with oxygen (O), was supplied by Lenzing AG (Austria).Wet pulp equivalent to 80 g oven dry (od) pulp was put into polyethylene flasks (DoE-screening) or a lab high-shear mixer (validation experiments) and heated to the desired reaction temperature.Then, the preheated NaOH solution was added, the suspension with a consistency of 10% was well mixed and reacted at the corresponding temperature.After 30 min, the pulp was filtered through a glass frit and the filtrate weighed and subjected to density, and dissolved organic carbon (DOC) content analysis.
The pulp was washed five times for 2 min with a NaOH solution (20 g/L, 80 g) and filtered.Again, the filtrate was weighed and analysed.During all alkaline filtrations, as little air as possible was sucked through the pulp to prevent oxidation of the cellulosic material.Then, the pulp was washed ten times with deionized water (80 g each), the fibres separated by mixing in water for 10 min at a consistency of 3%, filtrated, and washed five times with water (160 g) to ensure a pulp pH below 8.5.The combined filtrates were weighed and analysed.
The extraction yield was calculated based on the amount of starting material minus the sum of DOC found in all extraction solutions and washing filtrates.The DOC content of the lyes and washing filtrates was determined according to ÖNORM EN 1484 [16].

Pulp Characterisation
The kappa number of the pulp was analysed according to Tappi T236cm-85 (typical relative standard deviation (rsd) of the analysis is 5%), intrinsic viscosity according to SCAN-CM 15:99 (rsd 1%), brightness according to ISO 2470-1 (rsd 0.2%), and alkali resistance R10 and R18 (the amount of pulp that is insoluble in 10% and 18% NaOH solution, respectively) according to DIN 54355 (rsd 0.2%) [17][18][19][20].Fourier-transform Raman spectroscopy was used to determine the degree of crystallinity as well as the cellulose II content of the pulp samples (rsd 5%, respectively) [21].To determine the carbohydrate content of pulps and filtrates, the samples were subjected to two-stage total hydrolysis with sulphuric acid and analysed by high-performance anion exchange chromatography with pulsed amperometric detection (rsd 0.7% and 1.9% of glucan and xylan content, respectively) [22].The molar mass distribution of the pulps was determined by size-exclusion chromatography (SEC) with multiangle light scattering and refractive index detection in a LiCl/dimethylacetamide solution [23].The polydispersity index (PDI) of the pulps was calculated according to Equation (1), where M w is the weight average molecular weight and M n is the number average molecular weight (rsd of PDI 9.7%).The lower is the PDI-value, the more uniform is the molecular weight distribution of the pulp.
Moreover, the applicability of some pulp samples as viscose was tested.Thus, viscose was prepared in laboratory scale including steeping of the pulp in NaOH solution, pressing, shredding, ageing, preparation of xanthate by reaction with CS 2 , ripening and dissolving in NaOH [24].The particle content and Treiber filterability of the viscose was analysed (rsd 4.1% of particle content, and rsd 2.5% of filter value) [25], a high-quality viscose is characterised by low particle content and high Treiber filtration value [26].

Design of Experiments
A design of experiment approach was chosen to keep the number of extraction experiments to a minimum and to create a model which reliably predicts experimental conditions giving pulps with desired features.The program Design Expert 10 was used for setting up a face centred central composite experimental design for alkaline extractions with NaOH concentrations ranging 40-120 g/L and extraction temperatures of 20-80 • C. Duplicates were performed for the experiments at the corners and the centre point of the experimental design (squares in Figure 1).
Processes 2019, 7, x FOR PEER REVIEW 3 of 11 determine the carbohydrate content of pulps and filtrates, the samples were subjected to two-stage total hydrolysis with sulphuric acid and analysed by high-performance anion exchange chromatography with pulsed amperometric detection (rsd 0.7% and 1.9% of glucan and xylan content, respectively) [22].The molar mass distribution of the pulps was determined by size-exclusion chromatography (SEC) with multiangle light scattering and refractive index detection in a LiCl/dimethylacetamide solution [23].The polydispersity index (PDI) of the pulps was calculated according to Equation (1), where Mw is the weight average molecular weight and Mn is the number average molecular weight (rsd of PDI 9.7%).The lower is the PDI-value, the more uniform is the molecular weight distribution of the pulp.
Moreover, the applicability of some pulp samples as viscose was tested.Thus, viscose was prepared in laboratory scale including steeping of the pulp in NaOH solution, pressing, shredding, ageing, preparation of xanthate by reaction with CS2, ripening and dissolving in NaOH [24].The particle content and Treiber filterability of the viscose was analysed (rsd 4.1% of particle content, and rsd 2.5% of filter value) [25], a high-quality viscose is characterised by low particle content and high Treiber filtration value [26].The 14 obtained pulps were analysed (Table A1) and a response surface model was calculated for each feature (Table A2).The experimental errors were determined from the replicates.Then, three more extractions (crosses in Figure 1) were carried out to verify the models.The 14 obtained pulps were analysed (Table A1) and a response surface model was calculated for each feature (Table A2).The experimental errors were determined from the replicates.Then, three more extractions (crosses in Figure 1) were carried out to verify the models.

DoE Models, Effects of Alkaline Extraction on Pulp
With the help of DoE, 14 experiments were chosen and carried out to study the effect of NaOH concentration and temperature during caustic extraction on the kappa number, brightness, viscosity, alkali resistance R10 and R18, PDI, glucan and xylan content, cellulose crystallinity index, and cellulose II content of oxygen delignified sulphite pulp (see Table A1).The pulp yield of the extraction was also examined and statistical models were determined to describe the experimental data (Table A2).
All determined responses showed a complex correlation to temperature and NaOH concentration.More precisely, the xylan content (Figure 2) and pulp viscosity (Figure A1) decreased or increased, respectively, with elevated NaOH concentration but were least affected at intermediate temperatures.With the help of DoE, 14 experiments were chosen and carried out to study the effect of NaOH concentration and temperature during caustic extraction on the kappa number, brightness, viscosity, alkali resistance R10 and R18, PDI, glucan and xylan content, cellulose crystallinity index, and cellulose II content of oxygen delignified sulphite pulp (see Table A1).The pulp yield of the extraction was also examined and statistical models were determined to describe the experimental data (Table A2).
All determined responses showed a complex correlation to temperature and NaOH concentration.More precisely, the xylan content (Figure 2) and pulp viscosity (Figure A1) decreased or increased, respectively, with elevated NaOH concentration but were least affected at intermediate temperatures.The xylan content of the pulp could be significantly reduced; a maximum reduction from 2.4% to 0.4% was achieved at 20 °C and 120 g/L NaOH, which corresponds to a reduction of 83%.In contrast, only 17% of xylan was removed by caustic extraction at 50 °C and 40 g/L NaOH.In general, more xylan was extracted at lower temperatures due to the removal mechanism: pulp easily swells at temperatures of 0-40 °C in alkaline solutions making short molecular chains accessible and allowing them to dissolve [27].As depicted in Figure 3, the more hemicellulose was extracted, the higher was the NaOH concentration and more intensive was the swelling.Similar observations were The xylan content of the pulp could be significantly reduced; a maximum reduction from 2.4% to 0.4% was achieved at 20 • C and 120 g/L NaOH, which corresponds to a reduction of 83%.In contrast, only 17% of xylan was removed by caustic extraction at 50 • C and 40 g/L NaOH.In general, more xylan was extracted at lower temperatures due to the removal mechanism: pulp easily swells at temperatures of 0-40 • C in alkaline solutions making short molecular chains accessible and allowing them to dissolve [27].As depicted in Figure 3, the more hemicellulose was extracted, the higher was the NaOH concentration and more intensive was the swelling.The xylan content of the pulp could be significantly reduced; a maximum reduction from 2.4% to 0.4% was achieved at 20 °C and 120 g/L NaOH, which corresponds to a reduction of 83%.In contrast, only 17% of xylan was removed by caustic extraction at 50 °C and 40 g/L NaOH.In general, more xylan was extracted at lower temperatures due to the removal mechanism: pulp easily swells at temperatures of 0-40 °C in alkaline solutions making short molecular chains accessible and allowing them to dissolve [27].As depicted in Figure 3, the more hemicellulose was extracted, the higher was the NaOH concentration and more intensive was the swelling.Similar observations were The extraction of hemicellulose from the sulphite pulp was accompanied by cellulose removal, resulting in significant yield losses with lower achieved xylan content (see Figure 3).However, short chain cellulose is a minor component of pulp and therefore cold caustic extraction and accompanied swelling is highly selective to hemicellulose removal.It consequently caused an increase in the alkali resistance R18, a narrowing of the molecular weight distribution as well as PDI decrease, and consequently an increase of the average pulp viscosity (see Figure 4).The extraction of hemicellulose from the sulphite pulp was accompanied by cellulose removal, resulting in significant yield losses with lower achieved xylan content (see Figure 3).However, short chain cellulose is a minor component of pulp and therefore cold caustic extraction and accompanied swelling is highly selective to hemicellulose removal.It consequently caused an increase in the alkali resistance R18, a narrowing of the molecular weight distribution as well as PDI decrease, and consequently an increase of the average pulp viscosity (see Figure 4).When the caustic extraction temperature increases at constant NaOH concentration, pulp swelling is reduced and xylan dissolution is hampered [29].The main carbohydrate removal mechanism changes from the physical phenomenon to less effective chemical degradation reactions.Then, alkaline peeling gains importance, which degrades cellulose and hemicellulose in comparable rates making it a less selective carbohydrate removal mechanism.Therefore, in our study, comparatively more hemicellulose remained in the pulp at higher temperatures (see Figure 3).However, the pulp yield did not significantly decrease at 80 °C due to peeling, as strong alkaline cellulose degradation including hydrolysis begins only at temperatures exceeding 140 °C [7].
Moreover, by also applying caustic extraction the pulp brightness was slightly improved, the effect being largest at high NaOH concentration and very low temperatures (Figure A2).In contrast, the kappa number was always lowered from 1.2 to 0.9 and was virtually independent of the extraction conditions (Table A1).Removal of chromophores from pulp by caustic extraction was not expected, because caustic extraction is not primarily applied for brightness improvement purposes and alkaline fibre swelling cannot significantly contribute to lignin removal [30], as well as sulphite pulping of hardwood followed by oxygen delignification is already a very effective lignin removal process.The remaining chromophores might comprise condensed wood extractives or minor amounts of lignin chemically bonded to hemicellulose.As caustic extraction does not degrade these compounds, our proposed explanation is that they might be removed by co-extraction with hemicellulose [7].When the caustic extraction temperature increases at constant NaOH concentration, pulp swelling is reduced and xylan dissolution is hampered [29].The main carbohydrate removal mechanism changes from the physical phenomenon to less effective chemical degradation reactions.Then, alkaline peeling gains importance, which degrades cellulose and hemicellulose in comparable rates making it a less selective carbohydrate removal mechanism.Therefore, in our study, comparatively more hemicellulose remained in the pulp at higher temperatures (see Figure 3).However, the pulp yield did not significantly decrease at 80 • C due to peeling, as strong alkaline cellulose degradation including hydrolysis begins only at temperatures exceeding 140 • C [7].
Moreover, by also applying caustic extraction the pulp brightness was slightly improved, the effect being largest at high NaOH concentration and very low temperatures (Figure A2).In contrast, the kappa number was always lowered from 1.2 to 0.9 and was virtually independent of the extraction conditions (Table A1).Removal of chromophores from pulp by caustic extraction was not expected, because caustic extraction is not primarily applied for brightness improvement purposes and alkaline fibre swelling cannot significantly contribute to lignin removal [30], as well as sulphite pulping of hardwood followed by oxygen delignification is already a very effective lignin removal process.The remaining chromophores might comprise condensed wood extractives or minor amounts of lignin chemically bonded to hemicellulose.As caustic extraction does not degrade these compounds, our proposed explanation is that they might be removed by co-extraction with hemicellulose [7].

Targeted Extraction
The statistical models from the DoE experiments (Table A2) were used to determine caustic extraction conditions, which ideally satisfy the typical requirements of dissolving pulp producers: the pulp should be obtained in high yield, with low xylan content, high R18, and appropriate viscosity.Furthermore, a high pulp reactivity is desired, which is attributed to low crystallinity and low cellulose II content [4,15].Clearly, not all of these objectives can be realised by a single caustic extraction.Therefore, different targets were defined for three single model validation experiments (see Table 1).The objective of the first extraction CE1 was to obtain a pulp in high yield as well as in high purity represented by high R18 and low xylan content.It has been reported before that sulphite pulps with very high cellulose contents of 98% can be obtained by applying caustic extractions at temperatures of 5-50 • C and NaOH concentrations of 20-140 g/L [28].As described above, the caustic extraction selectivity is highest at low temperatures in terms of xylan removal while glucan is preserved.However, a high temperature process is more easily integrated into an existing bleaching sequence.Hence, lower yields were accepted for CE2 and CE3, while nevertheless a high R18 was aimed at in CE2.A low PDI was targeted by CE3, and therefore the response surface models provided us with extraction conditions preventing significant pulp degradation and securing the cellulose chain lengths.
Caustic extractions according to the validation experiments CE1, CE2, and CE3 were carried out.The predicted and actual properties of the three obtained pulps after caustic extraction are listed in Table 2.The experimental pulp properties agree with the predicted values within the standard deviation σ, proving that the DoE models were valid.However, the cellulose II content could only be predicted with unreasonably high σ and the yield of experiment CE3 with 89.1% was significantly lower than predicted (92.3%).This might be due to the fact that the extraction conditions of experiment CE3 were located on the outer borders of the DoE model (see Figure 1) giving rise to a higher uncertainty of prediction or that a different experimental setup was used for validation experiments.A lab high-shear mixer was used instead of polyethylene flasks for caustic extraction resulting in higher yield losses during handling.All three caustic extraction experiments had similar effects on the sulphite pulp (see Table 2).The pulp brightness was raised by 3-5% points and the xylan content was reduced by about 50%.As expected, highest yield was achieved in experiment CE1 due to the lowest applied temperature.However, even under the harshest applied conditions of 82 g/L NaOH and 80 • C in CE3, no significant peeling of the long-chain cellulose appeared.Since alkaline cellulose degradation begins at temperatures exceeding 140 • C [7], the distribution of high molar mass carbohydrates remained basically constant, as illustrated in Figure 5 for CE3.Only low molecular weight hemicellulose was extracted under the given conditions probably by the swelling and dissolution process.Consequently, the xylan content in the pulp declined to 1.1% and the alkali resistances R10 and R18 increased to 87.7% and 95.8%, respectively (Table 2).Moreover, the average pulp viscosity increased while the PDI was reduced as the molecular weight distribution became narrower.
extracted under the given conditions probably by the swelling and dissolution process.Consequently, the xylan content in the pulp declined to 1.1% and the alkali resistances R10 and R18 increased to 87.7% and 95.8%, respectively (Table 2).Moreover, the average pulp viscosity increased while the PDI was reduced as the molecular weight distribution became narrower.

Bleaching and Viscose Testing
After caustic extraction, the pulp was bleached with ozone and peroxide, i.e., a TCF bleaching sequence was applied.The superior quality of the extracted pulp comprised very low kappa number, very high brightness, high R18, and low PDI as well as very low residual xylan content.Overall pulp yields of 92.6%, 89.4% and 84.8% were achieved in the O-CE-Z-P bleaching sequence for CE1, CE2, and CE3, respectively.Even though a yield of 96.3% has been reported for a TCF bleaching of beech sulphite pulp, our results were still in an acceptable range, as the reported pulp was only treated with peroxide and the brightness was 88.5% ISO [31].
The molecular weight distribution of the pulp along the bleaching sequence is depicted in Figure 5. Caustic extraction clearly reduced the amount of short chain hemicellulose, as discussed above.The high molecular weight cellulose was not significantly shortened by caustic extraction.In

Bleaching and Viscose Testing
After caustic extraction, the pulp was bleached with ozone and peroxide, i.e., a TCF bleaching sequence was applied.The superior quality of the extracted pulp comprised very low kappa number, very high brightness, high R18, and low PDI as well as very low residual xylan content.Overall pulp yields of 92.6%, 89.4% and 84.8% were achieved in the O-CE-Z-P bleaching sequence for CE1, CE2, and CE3, respectively.Even though a yield of 96.3% has been reported for a TCF bleaching of beech sulphite pulp, our results were still in an acceptable range, as the reported pulp was only treated with peroxide and the brightness was 88.5% ISO [31].
The molecular weight distribution of the pulp along the bleaching sequence is depicted in Figure 5. Caustic extraction clearly reduced the amount of short chain hemicellulose, as discussed above.The high molecular weight cellulose was not significantly shortened by caustic extraction.In contrast, ozone bleaching caused oxidation of the cellulosic hydroxyl groups and subsequent hydrolysis of internal glycosidic bonds led to a chain length reduction, which is observed in Figure 5 by a shift of the right-end curve to lower molecular mass [32].
Whenever native cellulose-the structure named cellulose I-is subjected to strong alkaline solutions, it undergoes mercerization.The hydrogen bonds between the carbohydrate chains are loosened, the cellulose swells and upon neutralisation it changes its structure to cellulose II, which is less reactive towards chemicals compared to cellulose I. Usually, the crystallinity of cellulose is decreased during mercerization (see Table 2), which in turn results in an increased reactivity.Hence, the effect of caustic extraction on the reactivity of pulp is complex and not easily predicted and, therefore, the actual viscose quality needs to be tested by the Treiber filterability and the particle content.The test results shown in Table 2 prove the bleached pulp gave a high-quality viscose, as the filtration values around 400 g/cm 2 were quite high and only a few particles were detected.Presumably, the variations in crystallinity and cellulose II of the pulp did not have a notable effect on the viscose process, because during steeping and ageing in the viscose process the alkali cellulose undergoes more intense mercerization exceeding the mercerization by caustic extraction.The obtained pulps were therefore highly suitable for industrial processing.

Process Viability
Dissolving pulp of very high quality can be produced from sulphite pulp by O-CE-Z-P bleaching.This process offers therefore high potential for the production not only of viscose but also of other value-added products requiring highly pure pulp, such as lyocell or cellulose filaments.
The applied O-CE-Z-P bleaching sequence is also energetically favourable and can be integrated into existing TCF bleaching sequences.A typical O-CE-Z-P temperature profile could be 100 • C, 80 • C, 50 • C, and 70 • C and hence the temperature descends slowly through the treatment.
The demonstrated caustic extraction utilised lyes with a NaOH concentration of 70-80 g/L.Since alkali lyes of this composition are usually not available in sulphite or kraft pulp mills but are a crucial resource in viscose production, the application of the O-CE-Z-P bleaching sequence could be of particular interest in a pulp mill with integrated viscose production.As hemicellulosic degradation products accumulate in viscose lyes during the recycling in the viscose production and need to be removed, e.g., by nanofiltration [5] or other membrane separation processes [33], it would be economically advantageous to constantly direct part of the viscose lye to caustic extraction, consequently keep the carbohydrate concentration in the viscose production low and possibly save the installation of costly separation equipment.In addition, the lyes used in caustic extraction could even be redirected to the preceding oxygen bleaching stage and, consequently, large amounts of fresh lye could be saved or its utilisation could even be omitted from the bleaching sequence.
By applying a caustic extraction in the bleaching of pulp, hemicelluloses are removed from pulp at an earlier point in the process compared to usual residual hemicellulose degradation during viscose steeping and ageing.Moreover, the extracted hemicelluloses exhibit longer chain lengths compared to the low molecular weight hemicellulose obtained from the steeping lye.Because oligomeric sugar containing lyes are of special interest in a biorefinery context, where they are further processed, e.g., into xylooligosaccharides for prebiotic formulations [34,35], a co-product of higher market value can be separated by the described process.
The overall yield of the applied bleaching sequence was acceptable, but pulp producers strive for highest possible product amounts.However, applying the O-CE-Z-P bleached pulp in a viscose process certainly gives higher viscose yields and throughput, because carbohydrate losses due to hemicellulose removal would be significantly reduced during ageing and steeping, as hemicellulose had already been removed almost quantitatively.Additionally, the aging time could be reduced because the viscosity of the pulps was much lower.Hence, O-CE-Z-P bleached sulphite pulp can be considered as a promising resource for the viscose or lyocell process.

Conclusions
Dissolving pulp in outstanding purity was obtained from sulphite beech pulp by application of an O-CE-Z-P bleaching sequence.Up to 83% of xylan was removed from the pulp, and only minor yield losses arose from cellulose degradation.The major benefit of caustic extraction as described here is its high selectivity, as yield loss corresponds to xylan extraction while cellulose is preserved, whereas during hot caustic extraction significant cellulose losses occur [7].Caustic extractions carried out at about 80 • C with 60-80 g/L NaOH were economically feasible, because pulp was obtained in good yield and an energetically moderate temperature profile was applied throughout the bleaching sequence.
The dissolving pulp showed very good reactivity in viscose application tests, and its high purity makes it a promising candidate for further high-value products.Application of the described bleaching process in a pulp mill with integrated viscose production offers economic and environmental advantages for the whole process due to the complementary utilisation of viscose lyes and hemicellulose as a co-product.Acknowledgments: We express our gratitude to the Lenzing AG for their kind contributions.

Conflicts of Interest:
The authors declare no conflict of interest.

A
design of experiment approach was chosen to keep the number of extraction experiments to a minimum and to create a model which reliably predicts experimental conditions giving pulps with desired features.The program Design Expert 10 was used for setting up a face centred central composite experimental design for alkaline extractions with NaOH concentrations ranging 40-120 g/L and extraction temperatures of 20-80 °C.Duplicates were performed for the experiments at the corners and the centre point of the experimental design (squares in Figure 1).

Figure 2 .
Figure 2. The xylan content of extracted sulphite pulp in correlation to temperature and NaOH concentration.

Figure 3 .
Figure 3.The residual xylan contents and pulp yields of caustic extraction experiments (averages of duplicates are shown).

Figure 2 .
Figure 2. The xylan content of extracted sulphite pulp in correlation to temperature and NaOH concentration.
Similar observations were made by Wayman and Sherk, who obtained chlorinated sulphite pulps with very high cellulose contents of >99% by caustic extraction with 120-140 g/L NaOH at 15-20 • C [28].

Figure 2 .
Figure 2. The xylan content of extracted sulphite pulp in correlation to temperature and NaOH concentration.

Figure 3 .
Figure 3.The residual xylan contents and pulp yields of caustic extraction experiments (averages of duplicates are shown).

Figure 3 .
Figure 3.The residual xylan contents and pulp yields of caustic extraction experiments (averages of duplicates are shown).

Processes 2019, 7 ,
x FOR PEER REVIEW 5 of 11 made by Wayman and Sherk, who obtained chlorinated sulphite pulps with very high cellulose contents of >99% by caustic extraction with 120-140 g/L NaOH at 15-20 °C [28].

Figure 5 .
Figure 5. Distribution of pulp molecular weight.

Figure 5 .
Figure 5. Distribution of pulp molecular weight.
Author Contributions: Investigation, C.F.; writing-draft preparation, I.G.; writing-editing R.B. and G.S.; visualisation, I.G.; and conceptualisation and supervision, K.F.Funding: Financial support was provided by the Austrian government; the provinces of Lower Austria, Upper Austria, and Carinthia; and by Lenzing AG.

Figure A1 .
Figure A1.Response surface of pulp viscosity in correlation with temperature and NaOH concentration.

Figure A2 .
Figure A2.Response surface of brightn in correlation with temperature and Na concentration.

Figure A1 .
Figure A1.Response surface of pulp viscosity in correlation with temperature and NaOH concentration.019, 7, x FOR PEER REVIEW 10 of 11

Figure A2 .
Figure A2.Response surface of brightness in correlation with temperature and NaOH concentration.

Figure A2 .
Figure A2.Response surface of brightness in correlation with temperature and NaOH concentration.

Table 1 .
Targets and conditions of validation experiments.

Table 2 .
Pulp properties of oxygen delignified pulp, pulp after alkaline extraction (predicted and actual), and further Z-P-bleached dissolving pulp.

Table A1 .
DoE layout and results.

Table A2 .
Coefficients of response regression models with the equation: response = X + A + B + A•B +A 2 + B 2 .A is temperature and B is NaOH concentration.