Behavior of a Mixture of Metals for Competiting Adsorption Sites of Untreated and Alkali-Treated Rice Husk

: Elements are released into water bodies, affecting the environment and human health. To address this problem, the adsorption-desorption capacity of untreated rice husk (URH) and rice husk treated with alkali (RHTA) for Cu(II), Pb(II), Fe(II), Cd(II), and Zn(II) was investigated. Analyses during the process were performed by X-ray diffraction (XRD), scanning electron microscopy, and elemental analysis by energy dispersive X-ray spectroscopy (SEM-EDS), as well as Fourier transform infrared spectroscopy (FTIR). Adsorption-desorption kinetics and isotherms were carried out. The FTIR analysis of RHTA revealed a lowering of intensity of the bonding signals (OH, C-O, CH 2 , CH 3 , SiO 2 , Si-OH) and loss of some signals due to the adsorbent-elements interaction. The adsorption on RHTA presented higher adsorption of Fe, followed by Pb, Zn, Cu, and Cd. Meanwhile, in URH, the adsorption was Fe > Pb > Cu > Zn and Cd. On the other hand, the desorption values for RHTA were Zn > Cd > Pb > Cu > and Fe and Zn > Cd > Cu > Pb and Fe for URH. The adsorption kinetics showed that data fit (R 2 ≥ 0.89) to pseudo-second-order kinetics and Freundlich isotherms (R 2 ≥ 0.84) for both ATRH and URH, indicating that the process occurs in the multilayer form and is controlled by chemisorption, where the adsorption depends on the active sites of the adsorbent surface.


Introduction
The deterioration of water resources can result from various processes, including climatic and geological factors, as well as anthropogenic activities, such as agricultural practices, industrial and metallurgical activities, and waste generation [1].Consequently, industrial wastewater often contains pathogenic microorganisms, organic materials, and traces of heavy metals [2].These contaminants can enter water bodies directly or indirectly through daily human activities, contributing to surface water pollution [3].Among the heavy metal contaminants, zinc, nickel, iron, and copper are known to be essential for organisms proper development, although they can become harmful at concentrations exceeding those required by plants and animals [4].In contrast, metals like lead, mercury, and cadmium are not considered essential elements for individual development and pose risks to both the environment and human health due to their tendency to bioaccumulate in the body [1,5].Therefore, various methods have been employed to remove toxic elements from water, including adsorption-separation processes, membrane separation, flocculationbased separation using electrical and chemical agents, and separation based on oxidation state changes in sequential photocatalysis-adsorption systems.The choice of method depends on the nature of the specific contaminant of interest, and the success of contaminant removal is influenced by factors such as pH and temperature [6,7].
Most of the treatments used for the removal of these contaminants are characterized by problems in terms of installation, operation, and generation of secondary sludge, which represents another environmental problem that requires an appropriate solution for its disposal [8].However, the adsorption process aims for a technology that manages to reduce and remove some toxic compounds because of its high effectiveness, simple operation and control, low energy requirements, and environmental friendliness [9,10].
Therefore, organic adsorbents that intervene in the removal of different contaminants have been evaluated, including shells, stems, bark, and seeds, which reduce the concentration of potentially toxic elements in aqueous media [11,12].Some of the most widely used biosorbents for the removal of heavy metals include bacteria, fungi, algae, industrial wastes, and agricultural wastes [13].Agricultural residues are obtained from plants and crops that contain minerals, such as silica [14] and rice husk.These residues are mainly composed of cellulose, lignin, hemicellulose, oils, starch, and waxes, which is why they have a wide variety of functional groups [15], are considered low-cost, eco-friendly adsorbents [16], and have a high percentage of organic matter.
Likewise, it has been sought to potentiate the adsorbent capacity of the materials through the implementation of alkaline treatments using sodium hydroxide (NaOH), because they are effective, common, and easy to process for agro-industrial fibers, as they allow the reorganization and exposure of materials and functional groups in the adsorbent, thereby improving the adsorption process [17][18][19].Cellulose is a component that can be chemically modified for the removal of different contaminants, such as organic dyes and metal ions [16].This chemical modification contributes to a greater adsorption capacity because cellulosic adsorbents have a high sorption capacity owing to the availability of active hydroxyl groups, which is why, when chemically or physically modified, their efficiency improves [20].
Some examples of heavy metal adsorption using biomass functionalized, is one study where the authors treated flamboyant pods with citric acid for the adsorption of metals such as Cd 2+ , Ni 2+ , Zn 2+ , and Cu 2+ , showing that the carboxylic and phenolic functionalities of the adsorbent were relevant to make the removal of heavy metals more effective, in addition to indicating variations in the adsorption capacity of up to 0.20 mmol/g when removing the elements [21].Another example of this type of study is a work where they used two solutions to dope the surface of the oil tea camellia shells to improve functional groups that contained O, where more C=C groups were introduced, improving its adsorption properties since the doped materials showed O functional groups in which Pb 2+ and Cd 2+ joined in a higher percentage, although the latter did so in a lower percentage [22].On the other hand, a study was carried out using graphene oxide shows how this material has a promising advantage over others by having a large number of oxygen functional groups on its surface; in the study, NaOH and H 2 SO 4 were used as pretreatments for the adsorption of methylene blue, congo red, and Cd 2+ , where the material presented a more porous surface because a higher percentage of oxygen was present on its monolayer structure, where in turn, functional groups such as hydroxyl, alkoxy, and carboxyl allowed the adsorption of these contaminants [23].A final study is that in which coffee husks were used to remove Cd 2+ and Pb 2+ from wastewater.In this case, the shell was modified with NaOH and used in the form of biochar, where the results showed an increase that is comparable to conventional biosorbents, observing an elimination of 89.6% of Pb 2+ and 81.5% of Cd 2+, which is attributed to the creation or display of function,al groups and an increase in specific surface area [24].
There are sites that have a large amount of contamination by these potentially toxic elements (PTE) in water and sediments.Proof of this are some research works listed in Table 1.For this reason, in this study, the adsorption capacity of rice husk was evaluated with and without alkali-treatment to remove metals such as Cu(II), Pb(II), Fe(II), Cd(II), and Zn(II) from water.This biosorbent was selected because it is an agro-industrial residue that is produced in large quantities and discarded without any other use; however, it could be implemented as an efficient and low-cost solution to remove the afore mentioned contaminants in water containing high concentrations of these PTEs.

Biosorbent
Rice husk was used, considered an agro-industrial residue.Rice is the second-most consumed food in the world, and its global production has oscillated between 471 million tons, with an average per capita consumption of 57 kg/year [31].This residue has a high silica content, which varies between 5 and 30% depending on the rice species and the geographical area where it is located [14,32].This percentage is between 80 and 95 of the total composition of the ashes [33].In addition, it is composed of cellulose, hemicellulose, lignin, and crude protein, components that have been reported to contain organic and inorganic substances that make this residue chemically stable and have high mechanical resistance [34][35][36].
Because of its composition, rice husk can be used in three ways: for the production of chemicals, the production of compounds with a high silica content, and the production of energy and other products such as adsorbents through pyrolysis [35].These are the reasons why this biosorbent is used for the removal of various metals and dyes [37].

Biosorbent Treatment
The rice husk was treated with sodium hydroxide (NaOH).The material was left in contact with a 4% NaOH solution for 8 h.Subsequently, the excess solution was removed and stored at room temperature until use.

Rice Husk (Biosorbent) Characterization
The rice husk was characterized, including the composition of lignin, cellulose, and hemicellulose.These compounds have great relevance because they contain functional groups that can interact with metals.

Material Composition
In the characterization of the rice husk, the percentage of lignin, cellulose, holocellulose, hemicellulose, and ash was determined because these components have a large number of functional groups that intervene in the interaction between the biosorbent (rice husk rice) and heavy metals; therefore, agro-industrial residues containing a high lignin content present better heavy metal sorption properties [38].Some of the groups that are exposed to these compounds are the hydroxyl and carboxyl groups present in hemicellulose and lignin, phenol and carbonyl groups, aliphatic structures, and methoxyl and methylene groups of lignin [39,40].

Lignin
The Klason Lignin was performed by the Standard of Technical Association of the Pulp & Paper Industry (TAPPI T 222), which is the residue that remains after acid hydrolysis of the treated sample.First, 1 g of the biosorbent was weighed, mixed with 15 mL of 72% H 2 SO 4 , and allowed to settle for 12 h.Subsequently, the content was transferred to a 1000 mL flask, and 560 mL of deionized water was added.The flask was connected to a refrigerant, boiled for 4 h, filtered through a filter plate, and allowed to dry at 105 • C for 24 h before being weighed.The percentage of lignin is calculated based on Equation (1).

Holocellulose
To determine the percentage of holocellulose, 2 g of biosorbent was weighed, which was placed in a 250 mL Erlemeyer flask, and 63 mL of deionized water were added, in addition to placing 0.2 mL of CH 3 COOH and 0.6 g of NaClO 2 .The flask was heated to 80 • C in a water bath, shaken every 15 min, and the process was repeated every hour until three additions were completed.The contents were filtered, washed with deionized water, and dried at 60 • C for 24 h, after which they were weighed.The percentage of holocellulose was calculated based on Equation (2).

Cellulose
Cellulose was determined by weighing 1 g of holocellulose in a 100 mL Erlenmeyer flask, then adding 5 mL of NaOH (17.5%), which was mixed with a glass rod.Subsequently, 2.5 mL of NaOH (17.5%) was added every 5 min until 12.5 mL was used and then kept at room temperature for 30 min.Then, 16.5 mL of deionized water was added at 20 • C to convert the NaOH from 17.5% to 8.3%, mixing well, and maintaining the mixture for one hour.Once this time had elapsed, it was filtered and washed with 50 mL of 8.3% NaOH twice, and at the end, 7.5 mL of 10% CH 3 COOH was added, leaving in contact for 3 min.Subsequently, it was connected to a vacuum, washed with deionized water, dried at 105 • C for 12 h, and weighed.The percentage of cellulose was determined with Equation (3).

XR Diffraction
The X-ray diffraction (XRD) spectra of the rice husk samples with and without alkalitreated were obtained with Rigaku-Smart lab equipment (Rigaku Corporation, Japan) with a copper objective at 40 kV and 100 mA.The scan was performed from 10 to 100 • in increments of 0.02 • .

Fourier Transform Infrared Spectroscopy (FTIR)
The functional groups present in the rice husk samples, with and without treatment, were analyzed using Fourier transform infrared spectroscopy.The spectral scan was carried out in the range of 4000-400 cm −1 with a resolution of 2 cm −1 with a Nicolet 6700 spectrometer.The data were analyzed based on the obtained signals.

Scanning Electron Microscopy and Elemental Analysis by Energy Dispersive X-ray Spectroscopy
Morphological and elemental characterization of the scales was carried out with and without alkali-treated in the absence and presence of heavy metals.The analyses were performed using scanning electron microscopy (SEM) with a JEOL JSM 7401F (JEOL, Japan).The samples were analyzed under a high vacuum at 0.5 kV.The amplification used was ×1000.

Adsorption and Desorption Experiments
To know the ability to remove metals from water using rice husk, adsorption experiments were carried out on a multi-elemental solution that contained metals such as Cu(II), Fe(II), Pb(II), Cd(II), and Zn(II).Various works have reported the great capacity of this agro-industrial residue for the removal of metals and metalloids; for this reason, different treatments were used, such as untreated rice husk (URH) and rice husk treated with alkali (RHTA).In addition to using two amounts of residue (0.5 and 1 g); therefore, the treatments used are the following: 0.5 g untreated rice husk (URH0.5); 1 g untreated rice husk (URH1); 0.5 g rice husk treated with alkali (RHTA0.5);and 1 g rice husk treated with alkali (RHTA1).
The multielement solution was prepared at pH 5, with a metal concentration of 20 mg/L, pouring 125 mL into 250 mL Erlenmeyer flasks.Subsequently, one of the afore mentioned biosorbent treatments (URP0.5,URP1, RHTA0.5, and RHTA) was placed in each flask, which was carried out in triplicate.These flasks were shaken at 120 rpm at 28 • C for 10 h.
For the desorption experiment, the biosorbent previously used in the adsorption experiment was used, which was dried and later placed in 125 mL Erlenmeyer flasks, to which a CaCl 2 solution (0.5 M) was poured, to later be placed in stirring at 120 rpm for 24 h.

Adsorption Kinetics
The effect of contact time on metal adsorption was evaluated using the two treatments URH1 and RHTA1 to perform adsorption kinetics.Therefore, 180 mL of a mixture of Cu, Fe, Pb, Cd, and Zn were placed in Erlenmeyer flasks with different concentrations of 5, 10, 15, 20, 25, and 30 mg/L of each of the metals and the biosorbents of the two treatments, separately.Subsequently, it was stirred at 120 rpm, and samples were taken at 15-min intervals during the first hour, every 30 min in the second hour, and subsequently every hour for 8 h.
For this, the pseudo-first-order and pseudo-second-order models were used [41].The linearized model equations used are shown in Equations ( 5) and (6).

Adsorption Isotherms
The adsorption isotherms allow the evaluation of the characteristics of the biosorbent, in addition to providing information on the relationship between the adsorbent and the adsorbate to maximize the use of the biosorbents, providing information about the distribution of the adsorbate molecules between the solid and liquid phases [42][43][44].
To carry out the isotherms, the URH1 and RHTA1 treatments were used, as well as 6 different concentrations of the metals Cu, Fe, Pb, Cd, and Zn (5, 10, 15, 20, 25, 30 mg/L), where they were added 180 mL of the mixed metal solution in 250 mL flasks to shake at 120 rpm at 28 • C and then take samples for 8 h; this was determined through adsorption kinetics.
Subsequently, the Langmuir and Freundlich adsorption isotherm models were used, which allowed the analysis of the adsorption data, since with them information is obtained about the favorability of the adsorption process as well as the affinity of the adsorbate for the adsorbent [43].
Langmuir isotherm c e q e = 1 q max • b + 1 q max .c e (7) where: b (L/mg) = Langmuir's constant, related to binding sites and sorption energy q e (mg/g) = Metal adsorbed on the fibers in equilibrium c e (mg/L) = Metal concentration in the equilibrium solution q max (mg/g) = Maximum biosorption capacity Freundlich isotherm log q e = log k f + where: k f (L/g) and n (dimensional) = Freundlich's constants Where both constants indicate the extent of biosorption, the degree of non-linearity between the concentration of the solution and biosorption [45].

Metal Analysis
The metals were analyzed with a GBC Avanta, model 2.01 atomic absorption spectrometer (EAA), (GBC, Australia).Each of the values corresponds to the average of the three replicates carried out in the experiment.The standards used for the calibration of the EAA equipment were obtained from PERKIN ELMER PURE (Perkin Elmer, U.S.A.).

Statistical Analysis
The multiple comparison of means was performed by least square differences (LSD) 223 with a significance level (α) of 0.05, using the Statgraphics Centurion XVI (16.1.03version) (Statgraphics Technologies, Virginia, U.S.A.) statistical software, for metal analysis during adsorption and desorption experiments.

Biosorbent Composition
Table 2 shows the results obtained from the characterization of the rice husk, which show that this biosorbent has 28.4% lignin and a holocellulose percentage of 52.45%, of which 16.05% corresponds to hemicellulose and 36.40% to cellulose.Likewise, it was obtained that the percentage of ashes is 15.46% and that of humidity is 3.69%.The composition of this biosorbent has been previously reported, where the reported lignin percentage ranges between 19 and 12%, which is lower than what is indicated in this work and the percentage of cellulose is between 58 and 52%, which shows an increase according to what was obtained in this investigation [46,47]; however, in other investigation, the results are comparable to what was reported in this work, since the percentage of lignin, cellulose and hemice-llulose reported for the rice husk is 25%, 32%, and 13%, respectively [48].These differences between the components could be due to the different types of husk that come from various species of rice.However, it is important to note that the high amount of these components can improve the adsorption capacity of the biosorbent used since lignin contains aromatic groups as well as hydroxyl, methoxyl, and phenolic groups that are potential sites for interaction with cations such as heavy metals, among other contaminants [49].It is important to note that 17.06% corresponds to ash; this is comparable to that reported by other authors [23], where they indicate that 20% of the rice husk corresponds to ash, which has been reported to contain mainly silica (>90%) and metallic impurities [36].

X-ray Diffraction (XRD)
By X-ray diffraction analysis, peaks were observed at 5, 16, 22, and 35 • .The highest intensity peak was at 22 • , which was observed in all samples.In Figure 1a,b, the peaks at 5 and 16 • present little definition compared to the signal for these values in Figure 1c,d.The signal of the diffractograms is observed with greater noise after having carried out the interaction of the biosorbent with the multi-elemental solution.However, no substantial changes were observed, such as the appearance of new peaks or the absence of these, which could be attributed to the concentrations used.The identification of the phases in the sample allowed assigning the signals of cellulose (16 • , 22 • , and 35 • ) [50] and silica (22 • ) [51]; it could even be attributed to a 22 • overlap, this being a reported peak for both compounds.

Fourier Transform Infrared Spectroscopy (FTIR) (XRD)
Figure 2a,b show the FTIR analysis for the shell without treatment; the signal was observed at 3400 cm −1 , which has been reported for the stretching of the hydroxyl groups on the surface [52].Likewise, the signal found at 2900 cm −1 is attributed to CH3 and CH2 coming from aliphatic compounds, and in the range of 1600-1400 cm −1 , they have been reported as C-H signals coming from aromatic rings [42].Another of the signals with the highest intensity was recorded at 1050 cm −1 , which can be assigned together with the signal at 805 cm −1 to stretching vibrations for symmetrical and asymmetrical Si-O groups [53]; furthermore, these vibrations confirm the presence of silanol (Si-OH) and siloxanes groups (Si-O-Si-OH) [54][55][56].It was also possible to observe the elongation of the signal in the range of 1500 and 1250 cm −1 in Figure 2a, concerning the control (Figure 2b).The signal at 1000 cm −1 has been attributed to the presence of C-O (stretch) groups present in ester groups [52].However, due to the observed intensity of the peak at ~1000 cm −1 , it could be due to an overlap of signals for Si-O and C-O [57].
On the other hand, in Figure 2c,d, broad bands were observed in the ranges mentioned above.Particularly in Figure 2c, signals with less definition are seen in comparison with the control (Figure 2d).It is important to point out that even though peaks were found in similar ranges in the peel with and without treatment, the addition of NaOH caused the broadening of the signals at 3500 cm −1 and in the range of 1750-1000 cm −1 .The amplification or broadening of the signals or bands can be attributed to the interaction of the functional groups (-OH) with the metals in question [53].Likewise, it has been reported that treatment with NaOH can modify the functional groups on the surface and in turn increase the ionic ligands of the carboxyl, phosphate, and amino groups that have a high electro-attractive force with ions [18].Therefore, the FTIR analysis allowed us to

Fourier Transform Infrared Spectroscopy (FTIR) (XRD)
Figure 2a,b show the FTIR analysis for the shell without treatment; the signal was observed at 3400 cm −1 , which has been reported for the stretching of the hydroxyl groups on the surface [52].Likewise, the signal found at 2900 cm −1 is attributed to CH 3 and CH 2 coming from aliphatic compounds, and in the range of 1600-1400 cm −1 , they have been reported as C-H signals coming from aromatic rings [42].Another of the signals with the highest intensity was recorded at 1050 cm −1 , which can be assigned together with the signal at 805 cm −1 to stretching vibrations for symmetrical and asymmetrical Si-O groups [53]; furthermore, these vibrations confirm the presence of silanol (Si-OH) and siloxanes groups (Si-O-Si-OH) [54][55][56].It was also possible to observe the elongation of the signal in the range of 1500 and 1250 cm −1 in Figure 2a, concerning the control (Figure 2b).The signal at 1000 cm −1 has been attributed to the presence of C-O (stretch) groups present in ester groups [52].However, due to the observed intensity of the peak at ~1000 cm −1 , it could be due to an overlap of signals for Si-O and C-O [57].
On the other hand, in Figure 2c,d, broad bands were observed in the ranges mentioned above.Particularly in Figure 2c, signals with less definition are seen in comparison with the control (Figure 2d).It is important to point out that even though peaks were found in similar ranges in the peel with and without treatment, the addition of NaOH caused the broadening of the signals at 3500 cm −1 and in the range of 1750-1000 cm −1 .The amplification or broadening of the signals or bands can be attributed to the interaction of the functional groups (-OH) with the metals in question [53].Likewise, it has been reported that treatment with NaOH can modify the functional groups on the surface and in turn increase the ionic ligands of the carboxyl, phosphate, and amino groups that have a high electro-attractive force with ions [18].Therefore, the FTIR analysis allowed us to observe that the rice husk with and without treatment has active sites for the adsorption of the evaluated metals.
observe that the rice husk with and without treatment has active sites for the adsorption of the evaluated metals.

Scanning Electron Microscopy and Elemental Analysis by Energy Dispersive X-ray Spectroscopy
The SEM analyses allowed us to observe the morphology of the surface of the adsorbent without treatment with NaOH, before and after the adsorption process with metals.In Figure 3a, an irregular surface was observed, with apparent roughness resulting from the grooves and cracks in the material, which may favor the exposure of binding sites for metal adsorption [18].Likewise, in Figure 3b, folds were observed, causing roughness in the area analyzed.In the elemental analysis of the adsorbents (Figure 4), the decrease in the signal of elements such as P, C, K, and Ca was observed after the adsorption process, while in elements such as Fe and O, the signal increased.Even in the shell analyzed after adsorption, the signal corresponding to Cu (Lα 0.930) was observed.The increase in Fe and Cu signals can be attributed to their affinity for the active sites present in the adsorbent.

Scanning Electron Microscopy and Elemental Analysis by Energy Dispersive X-ray Spectroscopy
The SEM analyses allowed us to observe the morphology of the surface of the adsorbent without treatment with NaOH, before and after the adsorption process with metals.In Figure 3a, an irregular surface was observed, with apparent roughness resulting from the grooves and cracks in the material, which may favor the exposure of binding sites for metal adsorption [18].Likewise, in Figure 3b, folds were observed, causing roughness in the area analyzed.In the elemental analysis of the adsorbents (Figure 4), the decrease in the signal of elements such as P, C, K, and Ca was observed after the adsorption process, while in elements such as Fe and O, the signal increased.Even in the shell analyzed after adsorption, the signal corresponding to Cu (Lα 0.930) was observed.The increase in Fe and Cu signals can be attributed to their affinity for the active sites present in the adsorbent.
observe that the rice husk with and without treatment has active sites for the adsorption of the evaluated metals.

Scanning Electron Microscopy and Elemental Analysis by Energy Dispersive X-ray Spectroscopy
The SEM analyses allowed us to observe the morphology of the surface of the adsorbent without treatment with NaOH, before and after the adsorption process with metals.In Figure 3a, an irregular surface was observed, with apparent roughness resulting from the grooves and cracks in the material, which may favor the exposure of binding sites for metal adsorption [18].Likewise, in Figure 3b, folds were observed, causing roughness in the area analyzed.In the elemental analysis of the adsorbents (Figure 4), the decrease in the signal of elements such as P, C, K, and Ca was observed after the adsorption process, while in elements such as Fe and O, the signal increased.Even in the shell analyzed after adsorption, the signal corresponding to Cu (Lα 0.930) was observed.The increase in Fe and Cu signals can be attributed to their affinity for the active sites present in the adsorbent.
(a) (b)  Figure 5a,b shows the morphology of the husks treated with NaOH with and without metals.These husks presented a cracked surface with apparent reliefs; even scattered lumps were observed.Likewise, in the spectra generated by the elemental analysis, the signals with the highest intensity correspond to Ca, K, C, and P (Figure 6) compared to the signals presented by the elements in the husk before contact with the metals.It can even be observed (Figure 6a) that the Si signal (Kα 1.739) is extremely intense in comparison to rice husk treated with metals (Figure 6b), which can be attributed to the treatment with NaOH, causing the overexposure of the element in the adsorbent, and bonding with elements, that caused a lowering in the intensity in the presence of the heavy metals (Figure 6b), as it happened in the FTIR analysis (Figure 2c).Likewise, signals corresponding to elements such as Cu and Fe, which were present in the multi-elemental solution, were located at lower intensity.Figure 5a,b shows the morphology of the husks treated with NaOH with and without metals.These husks presented a cracked surface with apparent reliefs; even scattered lumps were observed.Likewise, in the spectra generated by the elemental analysis, the signals with the highest intensity correspond to Ca, K, C, and P (Figure 6) compared to the signals presented by the elements in the husk before contact with the metals.It can even be observed (Figure 6a) that the Si signal (Kα 1.739) is extremely intense in comparison to rice husk treated with metals (Figure 6b), which can be attributed to the treatment with NaOH, causing the overexposure of the element in the adsorbent, and bonding with elements, that caused a lowering in the intensity in the presence of the heavy metals (Figure 6b), as it happened in the FTIR analysis (Figure 2c).Likewise, signals corresponding to elements such as Cu and Fe, which were present in the multi-elemental solution, were located at lower intensity.Figure 5a,b shows the morphology of the husks treated with NaOH with and without metals.These husks presented a cracked surface with apparent reliefs; even scattered lumps were observed.Likewise, in the spectra generated by the elemental analysis, the signals with the highest intensity correspond to Ca, K, C, and P (Figure 6) compared to the signals presented by the elements in the husk before contact with the metals.It can even be observed (Figure 6a) that the Si signal (Kα 1.739) is extremely intense in comparison to rice husk treated with metals (Figure 6b), which can be attributed to the treatment with NaOH, causing the overexposure of the element in the adsorbent, and bonding with elements, that caused a lowering in the intensity in the presence of the heavy metals (Figure 6b), as it happened in the FTIR analysis (Figure 2c).Likewise, signals corresponding to elements such as Cu and Fe, which were present in the multi-elemental solution, were located at lower intensity.

Adsorption and Desorption of Metals
The pretreatments that are carried out in a biosorbent are of great importance since they allow improving the adsorption capacity of the material, exposing a greater number of functional groups that may be present on the surface, and to which metal ions can bind [58].Due to the above, in this investigation, it was decided to use a husk pretreatment with 10% NaOH to evaluate the percentage of metal removal.
Figure 7 shows the treatments used to remove the metals: Cu(II), Fe(II), Pb(II), Cd(II), and Zn(II).The adsorbent presented higher adsorption of Fe, followed by Pb, Zn, Cu, and Cd, respectively.On the other hand, it is important to point out that the metals, when found in a mixture, are not absorbed in the same proportion since there is competition between the available sites of the rice husk, which when joining the functional groups of the biosorbent and some sites are more related to certain metal ions [59].
In addition, it can be seen that for Fe the adsorption percentages are greater than 80% in any of the treatments, a significant difference (p < 0.05) was observed, which increases to 96% adsorption in the RHTA0.5 treatment compared to the other treatments.In the case of Pb, the biosorbent obtained removal percentages greater than 60%, with the URH1, RHTA0.5, and RHTA1 treatments showing the highest efficiency in the removal of this metal (82%, 80%, and 83%, respectively).On the other hand, zinc was removed by 83% when using RHTA1, contrary to the URH0.5, URH1, and RHTA0.5 treatments, where removal percentages between 21 and 37% were obtained.The removal percentages of Pb and Zn are lower than those reported by others author, in which removals of 92.28% and 95.62% are indicated, respectively, using rice husk ash [42]; however, this was not carried out in a mixture of metals, so there was no competition in the adsorption process.
In the case of Cu, this metal was adsorbed in a higher proportion when using the fibers with the treatment with alcali (RHTA0.5,RHTA1), obtaining 80% and 78% removal; however, the URH0.5 and URH1 treatments presented 24% and 36% effectiveness regarding the elimination of this metal.In the case of Cd, minimum adsorption percentages can be seen when using the biosorbent URH, obtaining up to 20% adsorption when using URH1.However, when using RHTA1, it is observed that this percentage increased to 40%, probably as a consequence of the greater number of functional groups exposed and with

Adsorption and Desorption of Metals
The pretreatments that are carried out in a biosorbent are of great importance since they allow improving the adsorption capacity of the material, exposing a greater number of functional groups that may be present on the surface, and to which metal ions can bind [58].Due to the above, in this investigation, it was decided to use a husk pretreatment with 10% NaOH to evaluate the percentage of metal removal.
Figure 7 shows the treatments used to remove the metals: Cu(II), Fe(II), Pb(II), Cd(II), and Zn(II).The adsorbent presented higher adsorption of Fe, followed by Pb, Zn, Cu, and Cd, respectively.On the other hand, it is important to point out that the metals, when found in a mixture, are not absorbed in the same proportion since there is competition between the available sites of the rice husk, which when joining the functional groups of the biosorbent and some sites are more related to certain metal ions [59].
In addition, it can be seen that for Fe the adsorption percentages are greater than 80% in any of the treatments, a significant difference (p < 0.05) was observed, which increases to 96% adsorption in the RHTA0.5 treatment compared to the other treatments.In the case of Pb, the biosorbent obtained removal percentages greater than 60%, with the URH1, RHTA0.5, and RHTA1 treatments showing the highest efficiency in the removal of this metal (82%, 80%, and 83%, respectively).On the other hand, zinc was removed by 83% when using RHTA1, contrary to the URH0.5, URH1, and RHTA0.5 treatments, where removal percentages between 21 and 37% were obtained.The removal percentages of Pb and Zn are lower than those reported by others author, in which removals of 92.28% and 95.62% are indicated, respectively, using rice husk ash [42]; however, this was not carried out in a mixture of metals, so there was no competition in the adsorption process.
which this metal can interact, since it is known that the functional groups that contain nitrogen have a strong affinity for the formation of complexes with metals, such as Cd, Cu, and Zn [60].In addition, it is important to point out that the pH plays an important factor; therefore, in this study, the pH was 5, which favors the adsorption of these metal ions, because if the pH is increased, the surface of the biosorbent becomes in a higher positive charge that promotes a slow removal of metal ions [12].
From the above mentioned, the formation of metal complexes or chelates with functional groups of carboxyl, hydroxyl, amino, phosphate, carbonyl, and amide, among others, can be inferred [61], which, on the surface of the biosorbent, these groups can act with redox activities [56].However, it is important to note that on the surface of the rice husk are silanol and siloxane groups [62], which present an interaction with heavy metals during their adsorption [55].
In this work, a competitive adsorption process was given since multi-element solutions contain elements with different electronegativity, ionic radius, and atomic weight.These characteristics make the ions compete for adsorption sites [54], even though they can change the adsorption behavior due to physical interactions on the surface, as it happened with the changes in the Cd adsorption behavior in the presence of Pb [63].Likewise, it has been reported that the evaluation of adsorption in single-element solutions presents a higher adsorption percentage compared to the processes with multi-element solutions [64].However, the evaluation of co-managed ions allows the adsorbents to be subjected to conditions, like those found in situ [65].Since it has been reported in natural water bodies, such as rivers, lakes, and groundwater, where different ions can coexist due to the leaching process of natural deposits or in consequence of industrial and mining wastewaters, where they may also contain different ions in their composition [66].In the case of Cu, this metal was adsorbed in a higher proportion when using the fibers with the treatment with alcali (RHTA0.5,RHTA1), obtaining 80% and 78% removal; however, the URH0.5 and URH1 treatments presented 24% and 36% effectiveness regarding the elimination of this metal.In the case of Cd, minimum adsorption percentages can be seen when using the biosorbent URH, obtaining up to 20% adsorption when using URH1.However, when using RHTA1, it is observed that this percentage increased to 40%, probably as a consequence of the greater number of functional groups exposed and with which this metal can interact, since it is known that the functional groups that contain nitrogen have a strong affinity for the formation of complexes with metals, such as Cd, Cu, and Zn [60].
In addition, it is important to point out that the pH plays an important factor; therefore, in this study, the pH was 5, which favors the adsorption of these metal ions, because if the pH is increased, the surface of the biosorbent becomes in a higher positive charge that promotes a slow removal of metal ions [12].
From the above mentioned, the formation of metal complexes or chelates with functional groups of carboxyl, hydroxyl, amino, phosphate, carbonyl, and amide, among others, can be inferred [61], which, on the surface of the biosorbent, these groups can act with redox activities [56].However, it is important to note that on the surface of the rice husk are silanol and siloxane groups [62], which present an interaction with heavy metals during their adsorption [55].
In this work, a competitive adsorption process was given since multi-element solutions contain elements with different electronegativity, ionic radius, and atomic weight.These characteristics make the ions compete for adsorption sites [54], even though they can change the adsorption behavior due to physical interactions on the surface, as it happened with the changes in the Cd adsorption behavior in the presence of Pb [63].Likewise, it has been reported that the evaluation of adsorption in single-element solutions presents a higher adsorption percentage compared to the processes with multi-element solutions [64].However, the evaluation of co-managed ions allows the adsorbents to be subjected to conditions, like those found in situ [65].Since it has been reported in natural water bodies, such as rivers, lakes, and groundwater, where different ions can coexist due to the leaching process of natural deposits or in consequence of industrial and mining wastewaters, where they may also contain different ions in their composition [66].
On the other hand, the desorption experiment was carried out using CaCl 2 [67,68], since an excess of this element can cause the release of metal ions from the biosorbent.The desorption percentage in this experiment was calculated based on the metal adsorbed during the previous experiment.Figure 8 shows the percentages of metal desorption in the different treatments used.It can be seen that the metal that is desorbed in the highest proportion is Cd, followed by Zn, Cu, Pb, and Fe.
Processes 2024, 12, x FOR PEER REVIEW 13 of 22 On the other hand, the desorption experiment was carried out using CaCl2 [67,68], since an excess of this element can cause the release of metal ions from the biosorbent.The desorption percentage in this experiment was calculated based on the metal adsorbed during the previous experiment.Figure 8 shows the percentages of metal desorption in the different treatments used.It can be seen that the metal that is desorbed in the highest proportion is Cd, followed by Zn, Cu, Pb, and Fe.The letters show statistically significant differences (p < 0.05) between the treatments of each metal; * indicates statistically significant differences between metals in a single treatment.The standard error value was placed on each bar.
In the case of Fe, it is shown that the desorption percentages are less than 10%, whereas the URH1 treatment was the one that presented a lower desorption percentage (0.5%) concerning the other treatments.The opposite was observed with Pb, where the URH1 treatment was the one that desorbed in a higher proportion (42%); however, the URH0.5, RHTA0.5, and RHTA1 treatments show desorption of 18%, 32%, and 28%, respectively.
Copper, for its part, presented greater desorption in the URH0.5 (52%) and URH1 (83%) treatments, while in the biosorbents with the pretreatment the desorption decreased, since in RHTA0.5 the desorbed percentage was 28% and RHTA1 was 24%.The percentage desorbed in zinc ranged between 53 and 63%, being URH1, RHTA0.5, and RHTA1 being those that presented a lower release of the metal.However, Cd showed significant desorption concerning the other metals in all the treatments used, achieving desorption percentages of 50-83%.

Adsorption Isotherms and Kinetics Adsorption
For the adsorption kinetics, the two types of pretreatments with the highest amount of biosorbent (URH1 and RHTA1) were used.Figures 9 and 10 show the pseudo-first and pseudo-second-order kinetics.The application of these models to the data obtained from a pseudo-first-order action of time has been used to evaluate which of the models best In the case of Fe, it is shown that the desorption percentages are less than 10%, whereas the URH1 treatment was the one that presented a lower desorption percentage (0.5%) concerning the other treatments.The opposite was observed with Pb, where the URH1 treatment was the one that desorbed in a higher proportion (42%); however, the URH0.5, RHTA0.5, and RHTA1 treatments show desorption of 18%, 32%, and 28%, respectively.
Copper, for its part, presented greater desorption in the URH0.5 (52%) and URH1 (83%) treatments, while in the biosorbents with the pretreatment the desorption decreased, since in RHTA0.5 the desorbed percentage was 28% and RHTA1 was 24%.The percentage desorbed in zinc ranged between 53 and 63%, being URH1, RHTA0.5, and RHTA1 being those that presented a lower release of the metal.However, Cd showed significant desorption concerning the other metals in all the treatments used, achieving desorption percentages of 50-83%.

Adsorption Isotherms and Kinetics Adsorption
For the adsorption kinetics, the two types of pretreatments with the highest amount of biosorbent (URH1 and RHTA1) were used.Figures 9 and 10 show the pseudo-first and pseudo-second-order kinetics.The application of these models to the data obtained from a pseudo-first-order action of time has been used to evaluate which of the models best explains the kinetics, as well as the passage of the metal ion in the biosorbent during adsorption [69].
Processes 2024, 12, x FOR PEER REVIEW 14 of 22 explains the kinetics, as well as the passage of the metal ion in the biosorbent during adsorption [69].
(a) (b) Table 3 shows the parameters of kinetics.The best adjustment of the data was presented when using the pseudo-second-order model in 4 of the metals used in the rice husk with and without treatment, with correlations greater than 0.886 for the URH and for the husk with pre-treatment, except for Cd, where the data had a better fit to the pseudo-firstorder model, with coefficients greater than 0.917.These results agree with other investigations [70,71], where the authors point out that the adsorption of different compounds in a solution using modified and unmodified biosorbents tends to adjust correctly to pseudo-second-order kinetics, in addition to the fact that this model can better fit most kinetic data sets [72], which indicates that the most important stage is the adsorption reaction, that is, the process is controlled by chemisorption, indicating attractive forces between the adsorbent and the adsorbate, additionally to the surface reaction that acts as the rate-limiting step, and the mechanism limited by diffusion [73], in fact that the adsorption rate depends to a greater extent on the active sites on the surface [74].Table 3 shows the parameters of kinetics.The best adjustment of the data was presented when using the pseudo-second-order model in 4 of the metals used in the rice husk with and without treatment, with correlations greater than 0.886 for the URH and for the husk with pre-treatment, except for Cd, where the data had a better fit to the pseudo-first-order model, with coefficients greater than 0.917.These results agree with other investigations [70,71], where the authors point out that the adsorption of different compounds in a solution using modified and unmodified biosorbents tends to adjust correctly to pseudo-second-order kinetics, in addition to the fact that this model can better fit most kinetic data sets [72], which indicates that the most important stage is the adsorption reaction, that is, the process is controlled by chemisorption, indicating attractive forces between the adsorbent and the adsorbate, additionally to the surface reaction that acts as the rate-limiting step, and the mechanism limited by diffusion [73], in fact that the adsorption rate depends to a greater extent on the active sites on the surface [74].However, it is important to note that in the pseudo-second-order kinetics, the adsorption rate is higher in URH, being Cu > Pb > Fe > Zn > Cd, while in the case of RHTA the behavior is Cu > Zn > Fe > Pb > Cd.On the hand, the adsorption capacities in the second-order mechanism differ between treatments, since the behavior in URH is Zn > Cu > Cd > Pb > Fe, while with RHTA it is Cd > Pb > Zn > Fe > Cu.
It should be noted that the adsorption capacities indicated by the kinetics are small (<2.487 when using URH and <3.308 with RHTA) compared to using other biosorbents for removal, such as those of coconut shells, orange peel, and activated charcoal adsorb Cu (3.07, 3.65 and 3.56 mg/g) [75][76][77], or other work, in where the q e of metals such as Pb, Cu, Zn and Ca adsorbed by slag (rock), is 115.8, 11.74, 10.53 and 9.92 mg/g, respectively [78], which are higher than those reported in this work; however, one of the studies indicates that for Cd and Zn of 0.476 and 3.182 mg/g when using a concentration of 50 mg/L adsorbed by rice husk ash [79].
The adsorption isotherms representing the adsorption capacity of URH and RHTA to remove Cu(II), Pb(II), Fe(II), Cd(II), and Zn(II) were used.To know the type of adsorption that is carried out by the biosorbent, for this purpose two types of isotherms were used: Langmuir and Freundlich, where the Langmuir isotherm supposes a surface with homogeneous sites, sorption energies equivalent and without interaction between the adsorbed species, that is, a monolayer is formed, which indicates that each binding site cannot accommodate more than one metal on the biosorbent surface [80] and this form of adsorption is carried out if the bond strength adsorbate-adsorbent molecules is stronger than adsorbate-solvent and adsorbent-solvent [81]; the Freundlich isotherm describes a multilayer adsorption [43].The parameters obtained from the Langmuir and Freundlich isotherm models using URH and RHTA are shown in Table 4.According to these models, the biosorbents with and without the pretreatment fit correctly to the Freundlich model (0.842-0.999) when in contact with the aforementioned metals, which would indicate that the adsorption process is carried out in the form of a multilayer [82]; while the Langmuir model, although with some metals the data were adjusted correctly, the fit was lower compared to Freundlich when the biosorbent was in contact with the metals, as can be seen in Figures 11 and 12.
adjusted correctly, the fit was lower compared to Freundlich when the biosorbent was in contact with the metals, as can be seen in Figures 11 and 12  These results found in the Freundlich isotherms could be because when the adsorption isotherms are carried out with low solute concentrations they are often linear, that is, the r 2 is higher [81]; however, some conditions do not allow this linearity, such as the mass of the solute versus the volume of solution, where an influence of this parameter has been observed due to two main reasons, such as the volume occupied by the suspended particles and their aggregation [83].

Conclusions
The characterization of the biosorbent indicates a high percentage of lignin and cellulose, in addition to silica, that was observed by XRD.These compounds presented the functional groups (OH, C-O, CH2, CH3, Si-O2, Si-OH, Si-O-Si-OH), which are reported to have active sites available in different biosorbents that could bond to metals.There is a potential to use the URH for its efficiency in removing high percentages of Fe and Pb and without the metal desorption from contaminated water containing a mixture of heavy metals.In other ways, it was determined that Cd and Zn were adsorbed at a lower extent to RHTA due to the presence of the other heavy metal competitors for the adsorption available sites.The metal adsorption studies indicate that, using RHTA, the adsorption of those metals is higher than 80%, except for Cd, where its removal was 42%.In addition, the RHTA desorbs the metals to a low (35%) extent, except for Cd and Zn.It was concluded that only Pb adsorption was enhanced by 80% in the ATRH; other ways Cd and Zn are highly desorbed from URH and RHTA by the presence of other heavy metals.
It is important to point out that it is possible to obtain the adsorption equilibrium by fitting the experimental data to the Freundlich model, which indicates that the rice husk adjusted correctly, the fit was lower compared to Freundlich when the biosorbent was in contact with the metals, as can be seen in Figures 11 and 12  These results found in the Freundlich isotherms could be because when the adsorption isotherms are carried out with low solute concentrations they are often linear, that is, the r 2 is higher [81]; however, some conditions do not allow this linearity, such as the mass of the solute versus the volume of solution, where an influence of this parameter has been observed due to two main reasons, such as the volume occupied by the suspended particles and their aggregation [83].

Conclusions
The characterization of the biosorbent indicates a high percentage of lignin and cellulose, in addition to silica, that was observed by XRD.These compounds presented the functional groups (OH, C-O, CH2, CH3, Si-O2, Si-OH, Si-O-Si-OH), which are reported to have active sites available in different biosorbents that could bond to metals.There is a potential to use the URH for its efficiency in removing high percentages of Fe and Pb and without the metal desorption from contaminated water containing a mixture of heavy metals.In other ways, it was determined that Cd and Zn were adsorbed at a lower extent to RHTA due to the presence of the other heavy metal competitors for the adsorption available sites.The metal adsorption studies indicate that, using RHTA, the adsorption of those metals is higher than 80%, except for Cd, where its removal was 42%.In addition, the RHTA desorbs the metals to a low (35%) extent, except for Cd and Zn.It was concluded that only Pb adsorption was enhanced by 80% in the ATRH; other ways Cd and Zn are highly desorbed from URH and RHTA by the presence of other heavy metals.
It is important to point out that it is possible to obtain the adsorption equilibrium by fitting the experimental data to the Freundlich model, which indicates that the rice husk These results found in the Freundlich isotherms could be because when the adsorption isotherms are carried out with low solute concentrations they are often linear, that is, the r 2 is higher [81]; however, some conditions do not allow this linearity, such as the mass of the solute versus the volume of solution, where an influence of this parameter has been observed due to two main reasons, such as the volume occupied by the suspended particles and their aggregation [83].

Conclusions
The characterization of the biosorbent indicates a high percentage of lignin and cellulose, in addition to silica, that was observed by XRD.These compounds presented the functional groups (OH, C-O, CH 2 , CH 3 , Si-O 2 , Si-OH, Si-O-Si-OH), which are reported to have active sites available in different biosorbents that could bond to metals.There is a potential to use the URH for its efficiency in removing high percentages of Fe and Pb and without the metal desorption from contaminated water containing a mixture of heavy metals.In other ways, it was determined that Cd and Zn were adsorbed at a lower extent to RHTA due to the presence of the other heavy metal competitors for the adsorption available sites.The metal adsorption studies indicate that, using RHTA, the adsorption of those metals is higher than 80%, except for Cd, where its removal was 42%.In addition, the RHTA desorbs the metals to a low (35%) extent, except for Cd and Zn.It was concluded that only Pb adsorption was enhanced by 80% in the ATRH; other ways Cd and Zn are highly desorbed from URH and RHTA by the presence of other heavy metals.
It is important to point out that it is possible to obtain the adsorption equilibrium by fitting the experimental data to the Freundlich model, which indicates that the rice husk adsorbed the heavy metals in the form of a multilayer.In addition, those data were

Figure 3 .
Figure 3. SEM analysis of URH: (a) Rice husk control (without heavy metals) and (b) rice husk with heavy metal.

Figure 5 .
Figure 5. SEM analysis of RHTA: (a) Rice husk without heavy metals (control) and (b) rice husk with heavy metals.

Figure 4 .
Figure 4. EDS analysis of URH: (a) Rice husk control (without heavy metals) and (b) rice husk with heavy metals.

Figure 3 .
Figure 3. SEM analysis of URH: (a) Rice husk control (without heavy metals) and (b) rice husk with heavy metal.

Figure 4 .
Figure 4. EDS analysis of URH: (a) Rice husk control (without heavy metals) and (b) rice husk with heavy metals.

Figure 5 .
Figure 5. SEM analysis of RHTA: (a) Rice husk without heavy metals (control) and (b) rice husk with heavy metals.

Figure 6 .
Figure 6.EDS analysis of RHTA: (a) Rice husk without heavy metals (control) and (b) rice husk with heavy metals.

Figure 7 .
Figure 7. Percentage of metal adsorption using different treatments: URH (untreated rice husk) and RHTA (rice husk treated with alkali); the number corresponds to the amount of mass employed.The letters show statistically significant differences (p < 0.05) between the treatments of each metal; * indicates statistically significant differences between metals in a single treatment.The standard error value was placed on each bar.

Figure 7 .
Figure 7. Percentage of metal adsorption using different treatments: URH (untreated rice husk) and RHTA (rice husk treated with alkali); the number corresponds to the amount of mass employed.The letters show statistically significant differences (p < 0.05) between the treatments of each metal; * indicates statistically significant differences between metals in a single treatment.The standard error value was placed on each bar.

Figure 8 .
Figure 8. Percentage of metal desorption using different treatments: URH (untreated rice husk) and RHTA (rice husk treated with alkali); the number corresponds to the amount of mass employed.The letters show statistically significant differences (p < 0.05) between the treatments of each metal; * indicates statistically significant differences between metals in a single treatment.The standard error value was placed on each bar.

Figure 8 .
Figure 8. Percentage of metal desorption using different treatments: URH (untreated rice husk) and RHTA (rice husk treated with alkali); the number corresponds to the amount of mass employed.The letters show statistically significant differences (p < 0.05) between the treatments of each metal; * indicates statistically significant differences between metals in a single treatment.The standard error value was placed on each bar.

Table 1 .
Examples of sites with heavy metal contamination around the world.

Table 3 .
Parameters obtained from adsorption kinetics pseudo-first and second-order using URH and RHTA.

Table 3 .
Parameters obtained from adsorption kinetics pseudo-first and second-order using URH and RHTA.

Table 4 .
Parameters obtained from Langmuir and Freundlich models isotherms using URH and RHTA.