Enhancing the Photocatalytic Performance of BiVO 4 for Micropollutant Degradation by Fe and Ag Photomodiﬁcation

: Wider application of BiVO 4 (BVO) for photocatalytic water treatment is primarily limited by its modest photocatalytic effectiveness, despite its appropriately narrow band gap for low-cost, sunlight-facilitated water treatment processes. In this study, we have photomodiﬁed an isotype BVO, consisting of a tetragonal zircon and monoclinic scheelite phase, with Fe (Fe@BVO) and Ag (Ag@BVO) ionic precursors under UV illumination in an aqueous ethanol solution in order to assess their effect on the opto-electronic properties and effectiveness for the removal of ciproﬂoxacin (CIP). Fe@BVO failed to demonstrate enhanced effectiveness over pristine BVO, whereas all Ag@BVO achieved improved CIP degradation, especially 1% Ag@BVO. At pH 4 and 6, 1% Ag@BVO demonstrated nearly 24% greater removal of CIP than BVO alone. Photomodiﬁcation with Fe created surface oxygen vacancies, as conﬁrmed by XPS and Mott–Schottky analysis, which facilitated improved electron mobility, although no distinct Fe-containing phase nor Fe-doping was detected. On the other hand, the introduction of mid-band gap states by oxygen vacancies decreased the reducing power of the photogenerated electrons as the ﬂat band potentials were shifted to more positive values, thus likely negatively impacting superoxide formation. In contrast, Ag-photomodiﬁcation (Ag@BVO) resulted in the formation of Ag 2 O/AgO and Ag nanoparticles on the surface of BVO, which, under illumination, generated hot electrons by surface plasmon resonance and enhanced the mobility of photogenerated electrons. Our research underscores the pivotal role of photogenerated electrons for CIP degradation by BiVO 4 -based materials and emphasizes the importance of appropriate band-edge engineering for optimizing contaminant degradation.


Introduction
Bismuth vanadate (BiVO 4 ) is a non-toxic, chemically stable, n-type visible light photocatalyst that has shown promise in various environmental applications due to its favorable properties [1][2][3].Due to its favorable band gap of 2.4 eV, which facilitates the use of the solar spectrum, suitable band edge positions, and good stability under illumination BiVO 4 , is often investigated for photoelectrochemical water splitting and environmental remediation, either alone or as part of Z-schemes and composite photocatalysts [4][5][6][7][8][9].Its inherent photocatalytic performance depends on several parameters: the polymorph in question, particle size, and specific surface area [1,10,11].BiVO 4 is known to have three crystal polymorphs: two tetragonal forms, zirconia and scheelite analogues, and a monoclinic modification with a distorted scheelite structure.The monoclinic polymorph exhibits superior photocatalytic activity to the individual tetragonal polymorphs [3,12,13], and its efficacy in degrading organic dyes has been well-established [3].Nonetheless, specific modifications to further enhance the effectiveness of BiVO 4 are necessary, as even the monoclinic polymorph suffers from high recombination rates and low charge carrier mobility [14,15].Therefore, strategies to further enhance the photocatalytic properties of photocatalysts, including BiVO 4 , are doping, the formation of composites, introduction of a cocatalyst, morphological and crystalline modifications, the creation of novel nanostructures, and surface engineering [16][17][18].Doping and composite formation with other photocatalysts are the most common approaches, while photodeposition of cocatalysts, although not as common, holds substantial promise.
Cocatalysts aim to reduce the band gap of the formed composite, improving the optical response of the photocatalytic material and suppressing the recombination rate of photogenerated charges by sinking photogenerated charges (i.e., holes and/or electrons), and, in turn, maximizing the surface population of charge carriers on the newly formed composite photocatalyst [17,[19][20][21].In photodeposition, the procedure utilizes the photogenerated charges formed by the photocatalyst itself.For example, holes can oxidize transition metal complexes, leading to the deposition of their respective oxides on the surface of the photocatalyst, while electrons can reduce ionic species into their respective nanometals [22].
Herein, we have attempted to modify an isotype homojunction BiVO 4 consisting of a tetragonal and monoclinic phase, the synthesis and properties of which we have reported earlier [23,24], with iron and silver species using a photomodification procedure akin to photodeposition.To the best of our knowledge, this work represents the first time such a modification of an isotype homojunction BiVO 4 has been reported.Aqueous silver ions can be reduced to silver nanoparticles (AgNPs) on the surface of BiVO 4 , which could facilitate the inhibition of photogenerated charge recombination due to the formation of a Schottky barrier, increase light absorption in the visible range due to surface plasmon resonance (SPR), and generate hot electrons that can form superoxide radicals [25][26][27][28][29][30].We hypothesize that photomodification with Fe 2+ can induce defect states in the band structure of BiVO 4 , which can facilitate the inhibition of photogenerated charge recombination inhibition and modulate the band gap structure of BiVO 4 .In addition, Fe 2+ can undergo oxidation to form iron oxide species on the surface of BiVO 4 , leading to the formation of a Z-scheme and improving photocatalytic performance [31].Furthermore, as part of this work, we have attempted to modify the iso-type homojunction BiVO 4 materials without an inert atmosphere, in a medium consisting of 20:80 v:v ethanol-water.The photocatalytic performance of the obtained materials was investigated for the degradation of ciprofloxacin (CIP), a synthetic antibiotic used to treat respiratory, urinary, and skin infections in humans and animals, as a model organic pollutant.In the environment, CIP adversely affects the development and reproduction of several aquatic organisms and contributes to the proliferation of antibiotic resistant pathogens [32,33].The novel insights into the effects of Ag and Fe photomodification on iso-type homojunction BiVO 4 presented herein pave the way to a broader application of iso-type homojunction BiVO 4 and contributes to the knowledge on BiVO 4 band structure engineering.

Synthesis of BiVO 4 and Photomodification of Ag and Fe Species
BiVO 4 was prepared by a co-precipitation method as described in previous work [34].In brief, bismuth(III) nitrate pentahydrate (Bi(NO 3 ) 3 × 5H 2 O, VWR Chemicals, Lutterworth, UK), ammonium metavanadate (NH 4 VO 3 , Acros Organics, Geel, Belgium), ethylenediaminetetraacetic acid disodium salt dihydrate (EDTA-2Na, T.T.T., Sveta Nedjelja, Croatia), and nitric acid (HNO 3 , Lach-ner, Neratovice, Czech Republic) were used.First, solutions of 0.2 M bismuth(III) nitrate and 0.2 M ammonium metavanadate were prepared by dissolving the required amounts in 1.5 M nitric acid (HNO 3 , Lach-ner, Neratovice, Czech Republic) with stirring at 80 • C. For the preparation of the stock nitric acid solution, ultra-pure water was used, which was sourced from a DirectQ-3 UV (Merck Millipore, Burlington, MA, USA).Then, an appropriate amount of Na-EDTA was added to obtain a concentration of 0.02 M Na-EDTA in the aforementioned Bi 3+ precursor solution.The precursor solutions were quantitatively combined in a 1:1 v/v ratio and were allowed to stir for one week at room temperature in the dark.BiVO 4 was separated from the reaction solution by centrifugation at 1370× g for 3 min (EBA 21, Andreas Hettich GmbH, Tuttlingen, Germany).The precipitate was washed with ultrapure water three times and centrifuged consecutively.The BiVO 4 slurry obtained after final washing was dried at 80 • C until dry in a natural convection laboratory oven (UN-55, Memmert, Schwabach, Germany).The dried product was ground using an agate pestle and mortar and was calcined in air at 450 • C for 2 h in a muffle furnace (LP-08, Instrumentaria, Zagreb, Croatia).
For the photomodification procedure of Ag or Fe species, in order to obtain Ag@BVO and Fe@BVO, silver (I) nitrate (AgNO 3 , Kemika, Zagreb, Croatia) and iron (III) chloride hexahydrate (FeCl 3 × 6H 2 O, Kemika, Zagreb, Croatia) were used, respectively.Photomodification was performed with an intensely mixed dispersion of pristine BiVO 4 (γ(BiVO 4 ) = 10,000 mg L −1 ) in a solution of 20:80 v/v ethanol:water.To this dispersion, an appropriate amount of Ag or Fe precursors was added in order to achieve 1, 8, or 15 wt% Ag or 5, 27.5, or 50 wt% Fe content.The dispersion was placed under intense, unfiltered, and collimated irradiation of a 450 W xenon arc lamp (XBO 450W OFR, Osram, Germany) housed in a research arc lamp housing (Oriel/Newport, Irvine, CA, USA).The lamp was operated in constant power mode with a model 69920 arc lamp power supply (Oriel/Newport, Irvine, CA, USA).After illumination over 60 min, the samples were washed and dried as described previously for pristine BiVO 4 .

Photocatalytic Experiments
The experiments were carried out in a photocatalytic reactor equipped with a watercooling jacket placed under a collimated beam of simulated solar light passed through an AM1.5 global air mass filter (Oriel/Newport Corporation, Irvine, CA, USA) using the research arc lamp and source outlined in Section 2.1.The volume of the working solution during the experiments was 80 ± 0.5 mL.The pH of the solution was adjusted beforehand to suit the conditions determined by the statistical experimental planning approach.Full factorial design (FFD) experimental plans, Table S1, were used to simultaneously investigate the effect of the Ag or Fe wt% and pH on the photocatalytic effectiveness for the degradation of ciprofloxacin (CIP) as a model pollutant at a concentration of 50 µM.Designs with three center points per block were utilized in order to provide a good experimental error or noise assessment and to better estimate this variability.For this purpose, Design Expert 10.1 (StatEase, Minneapolis, MN, USA) and Statistica 13.5 (TIBCO Software, Palo Alto, CA, USA) software was utilized.

Characterization of the Photocatalysts 2.4.1. Identification of Crystalline Phases
The crystallinity and composition of the obtained photocatalysts was analyzed by powder X-ray diffraction (PXRD) using a MiniFlex 600 (Rigaku, Tokyo, Japan) equipped with a Cu Kα X-ray tube, a D/tex 1D silicon detector, and a sample spinner attachment.The X-ray tube was operated at a voltage of 40 kV and current of 10 mA.The samples were finely ground by hand using a pestle and mortar.XRD data acquisition and analysis was performed in SmartLab II studio v4.3.287.0 software (Rigaku, Tokyo, Japan).The data were recorded at a scan rate of 5 • min −1 , with a step size of 0.01 • and 30 rpm sample stage rotation.The Crystallography Open Database (COD) 2020 was used to identify mineral phases.

Characterization of Surface Elemental Composition and Electronic States
The morphology of the gold-sputtered samples was investigated using an Ultra Plus field-emission scanning electron microscope (FE-SEM, Zeiss, Oberkochen, Germany) in addition to energy dispersive X-ray spectroscopy (EDS) characterization of the unsputtered samples in order to assess the surface composition.A 2 kV FE-SEM acceleration voltage was used.X-ray Photoelectron Spectroscopy (XPS) measurements on immobilized samples on FTO glass substrates were taken.In brief, fluorine-doped, tin-oxide-coated glass (FTO, Sigma Aldrich, St. Louis, MO, USA) was coated with a dispersion of the sample in silica/titanate sol-gel binder, as described previously in Section 2.3.The XPS characterization was performed using a VersaProbe III (Version AD) by PHI (Chanhassen, MN, USA) equipped with a hemispherical analyzer and a monochromatic Al Kα X-ray source.Survey spectra were measured using a pass energy of 224 eV and a step of 0.8 eV.Data were acquired using the ESCApe 1.4 software (Shimadzu-Kratos, Wharfside, Manchester, UK).The fitting of the core spectra was performed using CasaXPS 2.3 software (Casa Software Ltd., Teignmouth, UK).

Determination of Opto-Electronic Properties
Electrochemical characterization was performed according to our previous work [35].A total of three layers were deposited onto an FTO substrate to prepare the working photoelectrodes.The coated FTO substrates were used as working electrodes in a typical-three electrode electrochemical setup, while a platinum (Pt) wire was used as a counter electrode, and a saturated calomel (SCE) reference electrode was utilized.An SP-150 potentiostat/galvanostat (Biologic, Seyssinet-Pariset, France) was used to perform the linear sweep voltammetry (LSV) and electrochemical impedance spectroscopy (EIS) measurements.The electrochemical experiments were conducted in the dark and under illumination by a white light emitting diode (LED).The LSV measurements were performed at a scan rate of 20 mV s −1 from −0.5 V to +1.5 V vs. SCE.The EIS measurements were performed at 0 V vs. SCE at a frequency sweep from 100 kHz to 100 mHz using an AC amplitude of ±5 mV in relation to the open circuit potential.A 0.1 M solution of sodium chloride (0.1 M NaCl, 99%, Sigma-Aldrich, Waltham, MA, USA) was used as the electrolyte.The obtained EIS data were fitted to a model of an equivalent electrical circuit depicted in Figure S8 [36,37].For this purpose, ZSimpWin 3.2 software was used (Ametek Scientific Instruments, Berwyn, PA, USA).Additionally, Mott-Schottky measurements were carried out to determine the Fermi level of the samples [35].Open circuit potentials (OCPs) were measured by allowing the photoelectrodes to stabilize for 10 min, after which they were exposed to illumination for 10 min, after which the light source was turned off.The diffuse reflectance spectra (DRS) of immobilized samples on glass substrates was measured using a 2600i UV-Vis spectrophotometer equipped with an ISR-2600Plus integrating sphere (Shimadzu, Kyoto, Japan).The recorded spectra were plotted as Tauc plots using the Kubelka-Munk transformation [35].

Photocatalytic Effectiveness of Fe@BVO and Ag@BVO towards CIP Degradation
The aqueous solutions of CIP can undergo photolysis; thus, when considering photocatalytic degradation, the contribution of photolysis has to be taken into account.As shown in Figure S1, at pH 4, CIP is stable towards photolysis even after 240 min.At pH 6, the extent of photolysis is negligible, i.e., is less than 2%.Slightly alkaline conditions, on the other hand, favor photolysis.At pH 8, nearly 23% of CIP underwent photolytic degradation after 240 min.These results are in agreement with the findings of Torniainen et al. [38], whereby CIP was shown to be prone to photolysis in its zwitterionic form.
The activity of Fe@BVO and Ag@BVO for the degradation of CIP in photocatalytic experiments, according to the experimental plan in Table S2, and non-modified BVO as a reference are shown in Figure S2 (Supplementary Information).The contribution to the removal of CIP from the solution onto the immobilized films was established by measuring the extent of adsorption in the dark (shown in Figure S2 as the period from −30 to 0 min).At pH 4 and pH 6, the extent of adsorption is less than 8%; thus, the removal achieved during the photocatalytic experiments under illumination at these pH values corresponds to direct degradation of CIP.However, at pH 8, the extent of removal during the initial dark period is somewhat greater, with the greatest extent of adsorption being achieved by 50% Fe@BVO, which is equal to 16.1%.
The response surfaces, i.e., removal extents of CIP achieved in the investigated experiments, are shown in Figure 1.As observable by glancing at the results in Figure S2, the effect of Fe wt% content on the effectiveness of Fe@BVO is, at best, marginal, whereas the Ag loading on Ag@BVO had a marked effect.Moreover, the effectiveness of Ag@BVO at pH 4 for the removal of CIP is relatively unaffected by the wt% of Ag during the photomodification procedure (Figure S2A), unlike at pH 6 and pH 8. Furthermore, as can be seen, Ag loadings greater than 1% seemingly negatively affected the performance of the Ag@BVO photocatalyst.The Fe loading in Fe@BVO did not show a significant effect for the removal of CIP; moreover, with higher Fe loadings, the photocatalytic performance decreased.In the performed experiments, at pH 4 and pH 6, Fe@BVO achieved a removal of CIP that was within 5% of BVO alone in nearly all cases.However, at pH 8, 5% and 50% Fe@BVO achieved a markedly lower removal than BVO alone, i.e., 16.7% less CIP was removed with 5% Fe@BVO and 18.0% with 50% Fe@BVO (Figure S1).In order to ascertain the effects of the Fe-and Ag-modification of BVO, analysis of variance (ANOVA) of the gathered data provided further insights and helped elucidate the margins of experimental error.
decreased.In the performed experiments, at pH 4 and pH 6, Fe@BVO achieved a removal of CIP that was within 5% of BVO alone in nearly all cases.However, at pH 8, 5% and 50% Fe@BVO achieved a markedly lower removal than BVO alone, i.e., 16.7% less CIP was removed with 5% Fe@BVO and 18.0% with 50% Fe@BVO (Figure S1).In order to ascertain the effects of the Fe-and Ag-modification of BVO, analysis of variance (ANOVA) of the gathered data provided further insights and helped elucidate the margins of experimental error.
The F-value for the model equation R1 describing the removal of CIP by the Fe@BVO process (Equation ( 1)) is 57.88, indicating that the model explains variance very well.In addition, the p-value of <0.0001 implies that the model is significant.Furthermore, the R 2 value is 0.9797, implying a good fit to the obtained data.The adjusted R 2 , equal to 0.9957, The obtained response surface models for the degradation of CIP by Fe@BVO and Ag@BVO are shown in Figure 1A,B, respectively.The response surface quadratic model equation for the removal of CIP by Fe@BVO (R 1 ) is shown in Equation (1): The F-value for the model equation R 1 describing the removal of CIP by the Fe@BVO process (Equation ( 1)) is 57.88, indicating that the model explains variance very well.In addition, the p-value of <0.0001 implies that the model is significant.Furthermore, the R 2 value is 0.9797, implying a good fit to the obtained data.The adjusted R 2 , equal to 0.9957, which takes into account the number of variables in the model and their relevance, suggests that the independent variables contribute significantly to the predicted response.However, the only significant factors, from a standpoint of the p-value, in the model R 1 are X 1 (p ≤ 0.0001) and X 1 2 (p = 0.0036).A summary of the analysis of variance is provided in Table S2, thus painting a somewhat contrasting picture and implying potential model overfitting.Despite the non-significance of the remainder of the parameters, these parameters contribute for the accounting of the additional variance in the removal model, mostly through non-linear relationships or small-magnitude interactions.The Pred-R 2 of 0.8252 implies that the model should generalize new data well, and the adequate precision ratio of 22.74 implies that the signal-to-noise ratio is very good.In other words, based on the performed experiments, we can infer that the Fe loading in the photomodification procedure and/or pH in the Fe@BVO process have an intricate interplay that needs to be elucidated further, which is not immediately evident from Figure S2.The response model equation R 1 reveals that pH has, by far, the largest effect on the degradation of CIP, and that alkaline conditions are more favorable for CIP degradation, considering the positive weight of the factor X 1 .This can only be partly attributed photolysis.The photocatalytic degradation experiments were carried out under illumination for 90 min; therefore, the extent of photolysis is small (Figure S1).It is likely that the Fe-photomodification facilitated improved photocatalytic activity in alkaline conditions.
On the other hand, the response surface quadratic model equation for the removal of CIP with the Ag@BVO process (R 2 ) is shown in Equation ( 2): The high F-value (102.58) and very small p-value (<0.0001) reveal that the model is statistically significant, i.e., that the model can explain a substantial amount of variance in the modeled response and to a larger extent than model R 1 .The large R 2 value of 0.9884 and adjusted R 2 of 0.9788 suggest that the model explains a large proportion of the variance of the response.In addition, the predicted R 2 of 0.9186 is in good agreement with the adjusted R 2 .Both X 1 and X 2 parameters are significant, with p values of <0.0001 and 0.0025, respectively.These p-values indicate that both pH and Ag wt% significantly impact the response, i.e., the removal extent of CIP in the Ag@BVO process.The interaction term X 1 × X 2 has a p-value of 0.9258, implying that the interaction between pH and Ag wt% is not significant in explaining the variation in the removal extent of CIP, unlike in the case with Fe@BVO.The quadratic terms, i.e., X 1 2 and X 2 2 , are equal to 0.5012 and 0.9549, implying that these terms are not significant for the response of the Ag@BVO model.Indeed, as can be seen from Figure 1B, the removal extent of CIP is linearly dependent on pH and Ag wt%.Considering the model equation, pH is the dominant contributing factor for the removal of CIP, whereas the Ag wt% has a negative impact, implying that lower silver loadings are more favorable.That is to be expected above a certain point, as photomodification with silver can block active sites of BVO and increase recombination rates [27].
In order to elucidate the effects of BVO modification on photocatalytic performance, the obtained materials were characterized in detail.

Characterization of the Fe@BVO and Ag@BVO Photocatalysts
Powder X-ray diffraction analysis revealed that the crystalline structure of the iso-type homojunctions is retained, and, in the case of the Ag modified samples, metallic silver has been identified as a phase present in the samples 8% Ag@BVO and 15% Ag@BVO, as shown in Figure 2 (for the sake of brevity, only the concentrations corresponding to highest X 2 coded-variables are shown).Interestingly, no iron species were identified, regardless of the instrumental parameters, i.e., slower scan rate and faster sample spinner settings.The identified phases, according to the Crystallography Open Database, correspond to the following entry cards: clinobisvanite (COD 9013437) and dreyerite (COD 9011741) in all cases, and, for the silver modified sample, correspond to metallic silver (COD 9013047).Thus, XRD has confirmed that the iso-type homojunction BiVO 4 is able to reduce Ag + species to metallic nanosilver particles, presumably on the {010} facets [39].
In pursuit of Fe within the Fe@BVO, we turned to SEM/EDS.A side-by-side comparison of the 27.5 wt% Fe and 8 wt% Ag modified BVO, i.e., the compositions corresponding to the middle-coded variables X 2 in the performed DoE runs, are shown in Figure 3.The morphology of the obtained materials can be described as globular aggregates roughly of ~1 µm of diameter, formed by fusion of smaller individual particles (micrographs for all of the samples are given in Figure S3).The observed morphology is consistent for the morphology of pristine BVO [23], which is to be expected considering that photomodification is a mild procedure.The photodeposited species are not observable immediately on the surface of the BiVO 4 particles, which is unsurprising considering their small crystallite size evident from the reasonably broad peaks at Figure 2. In the case of Fe@BVO, interestingly, no iron species were detected in the EDS spectra, akin to XRD, as shown in Figure S4.In the case of Ag@BVO, the presence of Ag is notable on the X-ray energy dispersive spectra for samples prepared with 8 wt% and 15 wt% Ag, as shown in Figure S5; however, at 1% Ag, the characteristic Lα electron was not detected, again in agreement with XRD.Presumably, the intensity of the characteristic Ag Lα peaks is indistinguishable from the background in the case of 1 wt% Ag@BVO.
In pursuit of Fe within the Fe@BVO, we turned to SEM/EDS.A side-by-side comparison of the 27.5 wt% Fe and 8 wt% Ag modified BVO, i.e., the compositions corresponding to the middle-coded variables X2 in the performed DoE runs, are shown in Figure 3.The morphology of the obtained materials can be described as globular aggregates roughly of ~1 µm of diameter, formed by fusion of smaller individual particles (micrographs for all of the samples are given in Figure S3).The observed morphology is consistent for the morphology of pristine BVO [23], which is to be expected considering that photomodification is a mild procedure.The photodeposited species are not observable immediately on the surface of the BiVO4 particles, which is unsurprising considering their small crystallite size evident from the reasonably broad peaks at Figure 2. In the case of Fe@BVO, interestingly, no iron species were detected in the EDS spectra, akin to XRD, as shown in Figure S4.In the case of Ag@BVO, the presence of Ag is notable on the X-ray energy dispersive spectra for samples prepared with 8 wt% and 15 wt% Ag, as shown in Figure S5; however, at 1% Ag, the characteristic Lα electron was not detected, again in agreement with XRD.Presumably, the intensity of the characteristic Ag Lα peaks is indistinguishable from the background in the case of 1 wt% Ag@BVO.
In order to further elucidate the properties of Fe@BVO and Ag@BVO samples, survey XPS spectra were recorded, as shown in Figure 4 (only the spectra for 50% Fe@BVO and 15% Ag@BVO are shown).The Ti 2p 3/2 peak and Si 2p spectra originate from the silica/titanate coating used to immobilize BiVO 4 on FTO glass substrates for analysis, whereas C 1s implies leftover organics, most likely in the binder, owing to the low-temperature fixation procedure.In the context of BiVO 4 , typical binding energies for O 1s are in the range of 531 eV to 532 eV, whereas, for Bi 4f 5/2 , the binding energies are 163 eV to 164 eV [40,41].Again, no Fe species were identified, as was demonstrated previously by XRD and SEM/EDS, whereas, for Ag@BVO samples, the characteristic Ag 3d spectrum was observed in all cases.The observed O 1s spectra can be partly attributed to oxygen in the coating used to prepare the samples for XPS analysis and, to some extent, to oxygen within BiVO 4 , as shown in Table 1.The bulk of the O 1s corresponds to OH − groups [42].The Bi 4f 5/2 peak binding energies for 1% Ag@BVO and 5% Fe@BVO are relatively typical for pristine BiVO 4 .However, the Bi 4f 5/2 spectra for the 8% Ag@BVO and 27.5% Fe@BVO samples indicate that surface Bi 3+ ions in the lattice have somewhat reduced oxidation states than would be expected.These reduced binding energies imply the formation of Bi-Bi bonds in the samples [43].On the other hand, the greater binding energies for Bi 4f 5/2 in the case of 15% Ag@BVO and 50% Fe@BVO imply a higher oxidation state relative to pristine BiVO 4 .The peak position of the characteristic Ag 3d spectrum observed in Ag@BVO samples implies the presence of Ag + ions, i.e., the formation of surface oxidized silver species during photomodification [44].The decrease in binding energy of Ag 3d with growing Ag content is to be expected, as the surface-formed silver oxides on the AgNPs interact with a larger bulk of silver nanoparticles, i.e., a greater initial concentration of Ag + precursor leads to the formation of somewhat larger AgNPs.This oxide appears to be limited to fringes of the silver nanoparticles, as the only crystalline-silver-containing phase identified by XRD was metallic silver.Indeed, deconvoluted Ag 3d spectra shown in Figure S6 reveal that, with increasing Ag content during the photodeposition procedure, the overall oxidation state of Ag species decreases.In the case of 1% Ag@BVO, only AgO and Ag 2 O species were detected.However, at the highest Ag loading, no characteristic peak for Ag 2 O was detected, and the content of metallic Ag is greater than for 8% Ag@BVO.Thus, at higher Ag loadings, AgNPs are formed on the BiVO 4 surface, which are oxidized to a certain extent.The AgNPs are likely coated with the oxide layer, considering that the fringes of AgNPs are highly reactive [45].
Table 1.Characteristic spectra and corresponding XPS binding energies for Ag@BVO and Fe@BVO samples.

Spectra
Binding Energy in Sample, eV 1% Ag@BVO 8% Ag@BVO 15% Ag@BVO 5% Fe@BVO  In order to further elucidate the properties of Fe@BVO and Ag@BVO samples, survey XPS spectra were recorded, as shown in Figure 4 (only the spectra for 50% Fe@BVO and 15% Ag@BVO are shown).The Ti 2p3/2 peak and Si 2p spectra originate from the silica/titanate coating used to immobilize BiVO4 on FTO glass substrates for analysis, whereas C 1s implies leftover organics, most likely in the binder, owing to the low-temperature fixation procedure.In the context of BiVO4, typical binding energies for O 1s are in the range of 531 eV to 532 eV, whereas, for Bi 4f5/2, the binding energies are 163 eV to 164 eV [40,41].Again, no Fe species were identified, as was demonstrated previously by XRD and SEM/EDS, whereas, for Ag@BVO samples, the characteristic Ag 3d spectrum was ob- reveal that, with increasing Ag content during the photodeposition procedure, the overall oxidation state of Ag species decreases.In the case of 1% Ag@BVO, only AgO and Ag2O species were detected.However, at the highest Ag loading, no characteristic peak for Ag2O was detected, and the content of metallic Ag is greater than for 8% Ag@BVO.Thus, at higher Ag loadings, AgNPs are formed on the BiVO4 surface, which are oxidized to a certain extent.The AgNPs are likely coated with the oxide layer, considering that the fringes of AgNPs are highly reactive [45].Table 1.Characteristic spectra and corresponding XPS binding energies for Ag@BVO and Fe@BVO samples:

Spectra
Binding Energy in Sample, eV 1% Ag@BVO 8% Ag@BVO 15% Ag@BVO 5% Fe@BVO 27.5% Fe@BVO 50% In general, smaller Ag nanoparticles (AgNPs) are more reactive than their larger counterparts and have a partial electron-donating character [46,47].With lower Ag In general, smaller Ag nanoparticles (AgNPs) are more reactive than their larger counterparts and have a partial electron-donating character [46,47].With lower Ag loading, it is likely that smaller nanoparticles are obtained, which are more susceptible to oxidation.In the case of Fe@BVO samples, an Fe concentration dependent behavior can be observed as well.Taking into consideration the standard reduction potentials of Fe 2+ and Bi 3+ , we can arrive at a hasty conclusion that reduction of Bi 3+ with Fe 2+ is unlikely (Fe 3+ + e − → Fe 2+ , E • = +0.770V; Bi 3+ + 3e − → Bi 0 , E • = +0.309V), which would be the case in the absence of light.However, during the attempted photomodification procedure, photogenerated holes accumulate on {110} facets of BiVO 4 [39].The holes may oxidize Fe 2+ to Fe 3+ , thus forming surface oxygen vacancies by the reaction of Fe 2+ with the Bi-O bond, thereby leading to a decreased Bi 4f 5/2 splitting binding energy as detected by XPS.The scavenging of the photogenerated holes by Fe 2+ , in turn, leads to an increased accumulation of photogenerated electrons on the {010} BiVO 4 facets [39], facilitating O 2 reduction to hydrogen peroxide [48].Thus, favorable circumstances occur for the initiation of the photo-Fenton process during the photomodification procedure, whereby additional hydroxyl radicals (•OH) are generated.The •OH then, in turn, can fill oxygen vacancies formed in BiVO 4 formed by the aforementioned Fe 2+ hole scavenging, thus leading to a greater Bi 4f 5/2 binding energy for 50% Fe@BVO in relation to 27.5% Fe@BVO.The formation of oxygen vacancies can mediate the photogenerated charge recombination rates or facilitate electron mobility, into which electrochemical characterization will provide insights.In addition, oxygen vacancies are likely most stable in alkaline conditions [49], thus explaining the favorable effect of pH on the degradation of CIP with Fe@BVO observed in Figure 1B.Ab initio studies have shown that oxygen vacancies in the bulk of BiVO 4 trap electrons and thus may help hinder recombination, whereas those on the surface may facilitate charge recombination [50].Experimentalists have reported contrasting effects of oxygen vacancies on the electronic conductivity of BiVO 4 [51,52]; hence, further electrochemical characterization was deemed necessary to validate the hypothesis of the beneficial oxygen vacancy effect on Fe@BVO and to assess the effectiveness of Ag as an electron sink for Ag@BVO.In order to support this hypothesis, linear sweep voltammetry (LSV) and electrochemical impedance spectra (EIS) in the dark (D-) and under illumination (L-) were recorded.In addition, charge transfer resistances (R ct ) were determined by fitting the EIS data to an equivalent circuit model, as shown in Figure S8.The R ct values are provided in Table S5.The equivalent circuit chosen uses a constant phase element (CPE) due to the heterogeneity of the photoelectrode surface [37].
The LSV in the case of have so far confirmed the beneficial effect of the oxygen vacancies, as the photocurrent densities of the 27.5% and 50% Fe@BVO are improved over BVO alone, as shown in Figure 5A, stemming from the improved electron mobility.In the case of 5% Fe@BVO, a marginal improvement can be seen over BVO alone, owing to the lower density of oxygen vacancies.EIS has revealed that the charge carrier mobility, i.e., conductivity, has also increased in the case of the Fe@BVO in relation to pristine BVO, as shown in Figure 5C, as determined by the decreasing Nyquist semicircle radius.Thus, we can assert that the iso-type homojunction BVO benefits from surface oxygen vacancies, unlike monoclinic BVO alone [50].The R ct values for Fe@BVO, as shown in Table S5, have decreased in the dark in relation to BVO alone.The oxygen vacancies formed in the 5% and 27.5% Fe@BVO samples act as electron donors, thus enhancing the n-type behavior of BVO.In the case of 50% Fe@BVO, the notable changes in the Bi atom electronic environment and oxygen vacancies may have a synergistic role for electron transfer.Under illumination, the R ct of Fe@BVO are less than half of BVO alone.In addition, the increasing Fe loading has had a positive impact on decreasing R ct , although not to a great extent.However, the increased concentration of oxygen vacancies did not affect the band gap, i.e., the Fe@BVO samples exhibit a band gap energy similar to pristine BVO, as shown in Figure S7.In the case of Ag@BVO, we can see similar photocurrent densities regardless of the initial Ag wt% loading, as shown in Figure 5B.The anodic peaks at ~0.07 V vs. SCE correspond to the oxidation of AgNPs on the surface of BiVO 4 .EIS has revealed similar charge carrier mobilities for 1% and 8% Ag, which are improved over BVO alone, whereas 15% Ag@BVO has markedly improved charge carrier mobility, as can be seen in Figure 5D, due to greatly enhanced photogenerated electron scavenging [53].The measured charge transfer resistance for BiVO 4 on FTO electrode substrate in the dark is akin to the value reported in the literature by Chatchai et al. [54].In the dark, 1% Ag@BVO demonstrated a significantly greater R ct in relation to BVO alone, implying that silver oxide species impede charge transfer dynamics.At 8% Ag loading, the R ct decreased, presumably due to the presence of metallic silver facilitating charge transfer.In the case of 15% Ag@BVO, R ct is similar to BVO alone, presumably due to the formation of a Schottky barrier caused by a greater extent of band bending, and, hence, broadening the charge depletion region.However, under illumination, a stark decrease in R ct is observed for all Ag@BVO samples, where a nearly five-fold reduction in charge transfer resistance is observed.The presence of AgNPs on the surface of Ag@BVO samples is notable from the weak surface plasmon resonance observed in the 2.0 to 2.2 eV range, whereas the band gap is marginally decreased by 0.04 eV, as shown in Figure S7.However, the improved photo-electrochemical properties of higher Ag content in the case of Ag@BVO are offset by the blockage of photocatalytic active sites, which leads to decreased effectiveness towards CIP degradation, as evidenced by the response surface model R 2 shown above.The flat band potential (E fb ) of the Fe and Ag modified BVO samples, determined by extrapolating the Mott-Schottky intercept with the x-axis in Figure S9, revealed a shift to more positive values.In particular, the flat band potential increased by 0.108 V for 50% Fe@BVO, whereas 15% Ag@BVO demonstrated a more positive shift by 0.219 V. Despite these shifts, the band gap remained largely the same.For Fe@VO, this hints at the formation of new quantum states within the band gap by oxygen vacancies.The oxygen vacancies lead to an absence of 2p orbitals in the conduction band of BVO and thus cause a relative increase in the contribution of Bi cation orbitals in the valence band.Furthermore, these oxygen vacancies act as intermediate defects in the band gap, which facilitate electron transfer to the conduction band [55].On the other hand, the positive shift of the flat band potential and the consecutive positive shift in the conduction band potential make Fe@BVO less likely to produce superoxide radicals, which are a major contributor to CIP degradation [56].The faster shift of the open circuit potential after the photoelectrode is no longer illuminated towards a more positive potential, as shown in Figure S10A.This, in turn, implies that oxygen vacancies facilitate photogenerated charge recombination.These results are consistent with the findings made by Wang et al. [50].In the case of Ag@BVO, the deposited AgNPs lead to the formation of a Schottky barrier.As the electrons migrate to the AgNPs, holes accumulate on the surface of the BVO, leading to the observed band bending effect and consequential flat band shift to more positive potentials [28].The SPR of AgNPs on the surface of BVO contributes to the degradation of CIP by generating hot electrons, which facilitate reduction of oxygen to the superoxide radical [57].While the Schottky barrier that forms at the AgNP/BVO interface could help photogenerated charge recombination, this effect is offset by the hot electrons generated by SPR that rapidly recombine with photogenerated holes.These electrons likely have sufficient energy to overcome the Schottky barrier and tend to rapidly recombine with holes, as can be seen in Figure S10B.The OCP shift towards the initial potential in the dark after termination of illumination is much faster than for Fe@BVO, implying faster charge recombination in Ag@BVO in relation to Fe@BVO and the iso-type homojunction BVO alone.

Conclusions
The Fe photomodification on the pristine BVO iso-type homojunction lead to the formation of oxygen vacancies, as evidenced by XPS and Mott-Schottky analysis, which have facilitated improved electron mobility and increased the oxidative power of photogener-

Figure 1 .
Figure 1.Response surface models for (A) the removal of CIP with the Fe@BVO photocatalyst and (B) with the Ag@BVO photocatalyst.The obtained response surface models for the degradation of CIP by Fe@BVO and Ag@BVO are shown in Figure 1A,B, respectively.The response surface quadratic model equation for the removal of CIP by Fe@BVO (R1) is shown in Equation (1):  = 41.22 + 15.26 ×  + 0.96 ×  − 0.95 ×  ×  + 5.70 − 5.45(1)

Figure 1 .
Figure 1.Response surface models for (A) the removal of CIP with the Fe@BVO photocatalyst and (B) with the Ag@BVO photocatalyst.