A Review on Impacting Parameters for Photocatalytic Degradation of Organic Effluents by Ferrites and Their Nanocomposites

: Traditional wastewater treatment methods, such as reverse osmosis, adsorption, desalination, and others, are outweighed by the photocatalytic degradation of organic pollutants. Ferrites are prominent photocatalysts due to their tunable band gaps, surface areas, and magnetic properties, which render photodegradation economical. Ferrites and their nanocomposites have been reported as promising visible light active photocatalysts. The photocatalytic system is heavily re-liant on a number of factors that influence the photodegradation of organic effluents. This review demonstrates various parameters such as substrate concentration, pH of solution, photocatalyst quantity, photocatalyst surface area, metal and non-metal ion doping, light intensity, irradiation time, quenchers, etc. affecting the photocatalytic degradation of organic effluents by ferrite nano-particles and their nanocomposites in detail. The photodegradation efficiency of the ferrite nano-particles alters with the change in the value of pH of the solution, which further depends upon the nature of the pollutant used. A dose of the substrate and the photocatalyst must be optimized so as to attain better photodegradation efficiency. Photocatalysts with different surface areas change the amount of active sites, which in turn affects the degradation of pollutant and render it a crucial factor. In addition, the mechanism of the action of photocatalysis is elaborated in this review. Future research perspectives for the advancement of ferrites and their nanocomposites are deliber-ated in order to improve their use as photocatalysts.

Advanced oxidation processes (AOPs) are quite effective for wastewater remediation. Reducing the concentration of harmful compounds in wastewater is the primary goal of AOPs before its discharge. To generate high-potential chemical oxidants on-site, ozone (O3), UV/visible light, hydrogen peroxide (H2O2), and Fenton's reagent (Fe(II)/H2O2) can be used [20]. Photocatalysis is one of the renowned AOPs because photocatalysts can utilize UV/visible or solar energy to degrade pollutants, making photocatalysis economically feasible [21,22]. Photocatalysis is a process whereby a catalyst initiates or stimulates a chemical reaction using light. This mechanism is referred to as a "photocatalytic reaction" [23,24]. For treating wastewater-containing organic pollutants and dyes, heterogeneous photocatalysis using AOPs is an excellent option because it uses renewable solar energy. Therefore, it is strongly recommended to eliminate organic pollutants and colours [25]. Various reactive species, such as hydroxyl radicals (HO.), superoxide anion (O2 − ), holes (h + ), and singlet oxygen (O2 1 ), degrade contaminants adsorbed on the surface of a photocatalyst [26]. Apart from these oxidants, other solution parameters such as the pH of the solution [27], photocatalyst quantity [28], photocatalyst surface area [29], metal and non-metal ion doping [30], light exposure, irradiation time [31], and quenchers [28] also influence the photodegradation of organic pollutants.
Ferrites and their composites-because of their effective adsorption efficiency, excellent visible light catalytic activity, and outstanding Fenton reaction potential-have been regarded as promising materials for the removal of contaminants such as heavy metal/metalloids and organics [32]. Due to the decrease in particle size due to nanoscale confinement and surface effects, the magnetic properties of ferrite nanoparticles display peculiar characteristics that differ from those of bulk equivalent materials [33]. The advantages of magnetic ferrite nanoparticles include their affordability and excellent physical and chemical stability [34]. The magnetic, electric, and optical properties of the matter are affected by the behaviour of the ferrites in the nanoscale range, which is dominated by the quantum effect [35].
As of April 2023, search results on the Science Direct database for the phrase "photocatalytic activity of ferrite" in the titles of publications, keywords, and abstracts of the reviews are displayed in Figure 1. The publications on pure, doped, and composite (binary, ternary, and quaternary) MFe2O4 are included in the search results. There was a sizable rise in the number of publications between 2015 and 2023. Due to their magnetic properties, simplicity in synthesis, availability of precursors, and biocompatibility, ferrites have received extensive research interest in the field of the photocatalytic degradation of pollutants. The impact of various parameters on the photodegradation of organic pollutants using ferrite and their nanocomposites as photocatalysts, however, is not discussed in any of the reviews. Focusing on these issues, this review provides a thorough discussion of each parameter with regard to the photodegradation of the reported organic pollutants, a brief overview of the synthesis of ferrites and their nanocomposites, and a discussion of the photodegradation mechanism of organic pollutants. Finally, conclusions are drawn and the future research areas that still require attention are listed.

Structure of Ferrites
Ferrites are considered prominent photocatalysts because of their tunable band gaps, stability, distinctive magnetic properties, and low cost of production. In general, the chemical formula of ferrites is AB2O4. The tetrahedral (A) and octahedral (B) sites are occupied by metal cations, and the arrangement of the oxygen anions is cubic closed packing, as shown in Figure 2. This structure can provide different combinations of metal cations due to the balanced negative charges of oxygen anions. When all the A sites are occupied by divalent metal cations and the B sites are occupied by iron (III) cations, the structure that is obtained is called a normal spinel structure, having the formula Me A [Fe2

Methods of Synthesis of Ferrites and Their Nanocomposites
There are many different chemical and physical processes used for the synthesis of ferrite nanoparticles. Ball milling is a mechanical method for solid-state synthesis and is frequently used to grind powders into extremely tiny particles. Being a cost-effective and eco-friendly approach, it is mostly used in industries for large-scale production. However, the size and shape of ferrite nanoparticles are non-uniform. Regulation of the preparative parameters is required, including concentration, pH, type of complexing agent, temperature, etc. Ferrites are typically produced at a temperature of several hundred degrees. At higher temperatures, it is challenging to deposit film ferrites of a consistent quality. In addition, due to the release of poisonous gases during deposition, high-temperature processes are more susceptible to environmental pollution. Oxidation of metallic substrates and corrosion are prevented using low temperature deposition techniques. Table  1 represents the advantages and disadvantages of various physical and chemical methods used in the synthesis of ferrites and their nanocomposites.

Microwave and Hydrothermal
 Yield is high with low processing period  Costly equipment  Irregularity in particle shape and size Among various chemical methods used in the synthesis of ferrites, different methods have their own advantages and disadvantages. For example, the solvothermal method can be used to control the particle size of the synthesized material [47,48]. The sol-gel method is one of the best methods as it yields ferrite with more surface area of the nanoparticles, which is useful for the degradation of pollutants [49-52].
However, due to their magnetic nature and strong magnetic dipole interactions, magnetic NPs are particularly susceptible to agglomeration [53]. The agglomeration observed in these NPs also restricts their use in various applications [53][54][55][56][57][58][59]. To overcome these problems, different techniques have been proposed, such as doping and the fabrication of composites using wet chemical methods (hydrothermal, solvothermal), sol-gel, co-precipitation, combustion, and ultrasonication methods. Various ferrites which have been synthesized using these methods and their use as photocatalysts in the degradation of various pollutants is discussed in Table 2.
Hollow microspheres of Ce 3+ -doped NiCo-ferrites were synthesized using a carbon sphere as a template in a template-based deposition and surface reaction method [60]. The hydrothermal method showed the particle size of carbon sphere as 0.5 µm, while the template-based method showed the particle size of Ni0.5Co0.5Fe2O4 as 300 nm. Graphene-based CuCe0.2Fel.8O4 nanocomposites were synthesized using the hydrothermal method [61,62]. Furthermore, on examining the morphology, thermal stability, and crystal structure of CuFe2O4, CuCe0.2Fel.8O4 ferrite NPs, and graphene-based CuCe0.2Fel.8O4, the graphene was found to have distinct effects on the crystallite size, surface morphology, lattice strain, and thermal stability of the CuCe0.2Fel.8O4 ferrite NPs.
Nitrogen-doped 3D magnetic graphene gels were synthesized through one-pot hydrothermal synthesis, and it was found that the reduction in GO, N doping process, and generation of Fe3O4 particles occur simultaneously and are accompanied by 3D self-assembly [63]. Nitrogen-doped magnetic graphene gels were considered organized frameworks of graphene sheets with a uniform dispersion of the Fe3O4 NPs. The wet-chemical method is a synthetic route that deals with the chemical reactions in the solution phase using precursors at proper experimental conditions. The spinel ferrites were prepared through a chemical reaction between aqueous solutions of metal nitrates, ferric nitrates, and oxalyl dihydrazide [64].  In the ultrasonication method, the sound energy is applied to agitate the particles in the solution, which causes physical and chemical transformations for the preparation of nanocomposites [81]. Various studies have demonstrated that this approach is the simplest way to synthesize ferrite-based nanocomposites due to its low-cost and use of distilled water rather than other solvents. The nanocomposite of the carbon quantum dots with trimetallic strontium-titanium ferrite synthesized via an ultrasonication approach possesses a high-specific surface area (101.3 m 2 g −1 ) anda low band gap coupled with fluorescence-quenching, which facilitated the transfer of the photo-induced charge carriers. This feature is very useful for the photodegradation of nitroaromatics [82].Hierarchical nanoflowers of MgFe2O4, bentonite and boron, phosphorous co-doped graphene oxide synthesized using the ultrasonication method showed that chiffon-like co-doped graphene oxide nanosheets were wrapped on the MgFe2O4-bentonite surface, resulting in a porous flower-like morphology. The excellent conductivity of the co-doped nanosheets allowed for a quick charge carrier transport, which aided in the separation of those carriers during the photocatalytic reaction [83]. Cationic surfactant cetyltrimethyl ammonium bromide was chosen to coat the MgFe2O4because its negatively charged surface can interact with the surfactant during ultrasonication [84]. Similarly, the nanocomposite of calcium ferrite with nitrogen-doped graphene oxide (CaFe2O4-NGO) with magnetic properties was synthesized using this approach has been effectively used for the degradation of p-nitrophenol [85].
Apart from the ultrasonication method, the sol-gel approach was also used in the synthesis of ferrite-based nanocomposites, and additional material was added during the synthesis of ferrite. MgFe2O4-bentonite nanocomposites were synthesized in different w/w ratios using this method for the degradation of the p-nitrophenol [86]. The optical band gap of the MgFe2O4 NPs is 2.58 eV, and this decreases to 2.26 eV with increasing bentonite content in nanocomposites due to the presence of Fermi levels. A similar nanocomposite was synthesized for the degradation of martius yellow. It was found that this nanocomposite showed better degradation for malathion as compared to the p-nitrophenol and martius yellow [87]. This may be due to the resonance stabilization of the structure of the martius yellow [86,88].
Cobalt ferrite/reduced GO nanocomposites were prepared using the membrane-solvothermal method [89]. Scanning electron micrographs of nanocomposite showed the presence of most of the rod-shaped CoFe2O4 scattered beside the graphene, and only a few CoFe2O4 nanorods successfully loaded on the graphene. GO-supported ferrite (MFe2O4, M = Fe, Co and Ni) nanocomposites were prepared using the solvothermal method [90]. The uniform size (20-30 nm) of MFe2O4 microspheres was seen in the transmission electron micrograph. Vibrational sample magnetometry studies revealed a superparamagnetic behavior of all the nanocomposites with Ms values between 41 and 43 emug −1 at room temperature. The removal of the dye pollution was found to be useful with the help of the nanocomposites.
The co-precipitation method is widely used as a liquid phase method in the synthesis of ferrite-based nanocomposites. The co-precipitation and hydrothermal methods were used in the synthesis of core-shell ZnFe2O4/ZnS composites [91]. A characterization of the synthesized composite showed the presence of a layer of ZnS clusters on the surface of the ZnFe2O4 NPs. The band gap energy was observed to be 2.2 eV, showing the possibility of its application as a photocatalyst under visible light irradiation. The relative energy band positions in the ZnFe2O4 and ZnS were considered a main advantage for the improved separation of electron-hole pairs. Moreover, the easy magnetic collection of the composite materials was due to the sufficient magnetization of the ZnFe2O4 core. Thus, the different methods induce different properties in the ferrite-based nanocomposites, and each property has its own advantage for the photocatalytic degradation of organic pollutants.

Impacting Parameters for Photocatalytic Activity of Ferrites and Their Nanocomposites
The photocatalytic activity of ferrite NPs and their nanocomposites is reliant on various parameters, such as the substrate concentration, pH of the solution, photocatalyst quantity, surface area of the photocatalyst, metal and non-metal ion doping, light intensity, irradiation time, quenchers, etc. The impact of each parameter on the photodegradation of organic effluents is discussed in detail in the subsequent subsections.

Effect of pH
Solution pH is an important variable in wastewater treatment as it influences the photocatalytic degradation of organic compounds. The pH of heterogeneous catalysts changes the surface charge, and, as a result, the photocatalytic activity of the catalyst changes [92,93].
The surface charge of the catalyst plays a vital role for the photodegradation of anionic dyes, which was determined using spinel NixZn1−xFe2O4 (x = 0.0 to 1.0) NPs [29]. The maximum degradation was achieved at pH 3, due to the electrostatic desirability among the anionic dye and the positively charged surface. At basic pH values, the surface of the catalyst became negatively charged, which caused an electrostatic repulsion between the anionic dye and catalyst, thus retarding the degradation of the dyes (Figure 3a). Similar observations were recorded during the photocatalysis of the methylene blue dye using bismuth ferrite (BiFeO3) NPs, where the dye was completely degraded under visible light irradiation for 80 min [94]. Further, it was reported that sunlight and the presence of a photocatalyst are essential for the dye degradation process. Dye degradation was found to be 53% under dark conditions with the presence of only a catalyst. The dye removal efficiency was negligible in the absence of a catalyst and light. After irradiation under visible light with neutral and acidic pH conditions, no decrease in the concentration of dye was observed. This means that the excitation of dye molecules by photon and then the dispersion of their excitation energy had no role in the decolorization of the dye. However, at a basic pH, the rate of photolysis was high due to the generation of hydroxyl radicals through the generation of hydroxyl ions which degraded the methylene blue dye. This study was supported using an electron spin resonance spectroscopy [95]. The coating of the titania-silica (TiO2-SiO2) on the cobalt ferrite (CoFe2O4) NPs changes the properties on the photocatalyst surface. The SiO2 layer between the CoFe2O4 and TiO2 may prevent the charge injection from the semiconductor TiO2 to the magnetic CoFe2O4, which in turn led to the increase in photocatalytic activity towards the methylene blue dye. Under the acidic conditions, the charge on the TiO2 surface was positive, which provided electrostatic interactions for anionic dye molecules [96,97]. The removal of the congo red using Ni0.6Co0.4Fe2O4 was found to be at a maximum for pH 3 (40.28%) and decreased gradually up to pH 10 (15.45%), which was supported by the isoelectric point value of the dye [98].
The Ag/AgBr/NiFe2O4 plasmonic photocatalyst exhibited a superior photocatalytic performance in the photodecomposition of the cationic Rhodamine B dye under visible light irradiation. The zero-point charge (pHzpc) of the catalyst was about 5.2. Thus, the composite was negatively charged above that pH and provided electrostatic attractions for the cationic dye molecules [99]. The Mn0.5Zn0.125Mg0.375Fe2O4 NPs were stabilized at a basic pH, having negative zeta potential (−75.14 eV), which was very important for the photocatalytic degradation of the cationic Rhodamine B dye, as shown in Figure 3b [100]. The ciprofloxacin and remazol deep red dye were degraded using MRuxFe2−xO4 (M = Ni, Cu) [101]. The dye degradation efficiency was observed to be 93% after 60 min at pH 2.5, which decreased at higher pH levels. In addition, H2O2 was used to degrade the ciprofloxacin without changing the pH of the pure solution. The ciprofloxacin degraded to its greatest extent over a 120-min period at pH 2.5.
Acetamiprid and imidacloprid both belong to the neonicotenoid class of pesticides, but showed different optimum pH values for their maximum degradation using Fe3O4/GO-Fe3O4/CoFe2O4/GO-CoFe2O4and CoFe2O4photocatalyst, respectively. In case of acetamiprid degradation, maximum degradation was achieved at pH 3 [102]. At basic pH values, a decline in photocatalytic activity was observed because of ferrous excess hydroxyl ions reactions. This reaction led to the formation of yellowish-brown ferric hydroxide sludge, which ultimately covered the active sites of the catalyst and hence contributed to the reduction in overall efficiency. The degradation potentials of the catalyst (in all cases) dropped when the pH approached basic values. In the case of the imidacloprid, maximum degradation was achieved at pH > 7.0, which may be attributed to the formation of the hydroxide radicals on the surface of ZnO/CoFe2O4 magnetic nanocomposite, leading to the degradation of the imidacloprid pesticide [103].
In case of the phenolic compounds, such as phenol, 2-nitrophenol, 2-chlorophenol, p-chlorophenol, 2, 4, and 6-tricholorophenol, maximum degradation occurred in the pH range of 5 to 11, using ammonia modified graphene-Fe3O4, ZnFe2O4 multi-porous microbricks/graphene, Fe3O4@β-CD, and Fe3O4-gC3N4 nanocomposites [104][105][106][107]. Under alkaline conditions, the interaction between the phenolic compounds and photocatalyst is retarded due to the instability of the oxygen functionalities of the graphene sheets, which are deprotonated and dissolved in the aqueous medium. Contrary results were obtained for the maximum degradation of the phenol (94.2%), which was achieved at pH 3.5, using manganese ferrite [108]. This may be due to the presence of peroxydisulfate, as its adsorption on the positively charged catalyst surface in the pH range of 3-6 was more intense due to its negatively charged SO4¯·radical. In the pH range of 3-7, efficiencies greater than 90% were attained, but at values of pH up to 9, efficiency decreased to 65%.
Thus, the pH of the solution plays a crucial role in the degradation of pollutants. However, the optimum pH for the removal of the organic effluents using ferrites and their nanocomposites as photocatalysts depends upon the type of photocatalyst and the type of organic effluent used.

Effect of Catalyst Dose
The dose of ferrites used in the photodegradation process is another important parameter. Various studies have reported that the photocatalyst dose is highly related to the degradation of the organic pollutants during photocatalysis [84,109].
The methylene blue dye degradation increased upto a certain level when the magnetic catalyst Ni0.6Zn0.4Fe2O4 loading was increased [29,110]. Furthermore, the negative influence of the catalyst loading on the degradation was observed. The initial rise in the degradation was due to the increase in the number of the active sites present on the surface of the catalyst, increasing the production of ·OH and O 2− · radicals. Similar results were reported for the degradation of the methylene blue using MFe2O4 (M = Co, Ni, Cu, Zn) and ZnFe2O4, respectively [111,112]. The decrease after a certain time was due to ei-ther the aggregation of catalyst particles at high concentrations, causing a decrease in the number of surface active sites, or an increase in the opacity and light scattering of the catalyst particles at high concentrations, leading to a decrease. The maximum photodegradation of the methyl orange using ZnSm1.5Fe0.5O4 photocatalyst was achieved with 0.1 g/100 mL of catalyst. Unfavourable light scattering and a decrease in the light flow decreased the efficiency of the degradation, even on increasing the amount of catalysts [113]. The ciprofloxacin and remazol deep red dye were degraded using Ru-doped nanoferrites and as a function of the catalyst dosage. The percentage degradation was found to be at a maximum at 0.50 gL −1 ferrite concentration in both cases. The availability of more catalytic sites was expected to increase the degradation efficiency with increasing catalyst amounts; however, a large amount of ferrite causes turbidity of the solution, which prevents light from reaching the reaction medium and tends to impair the degradation process [101]. Using the Mn0.75Co0.25Fe2O NPs, the effectiveness of the catalyst concentration towards methylene blue degradation after UV light exposure was investigated. The catalyst dose was varied from 10 to 30 mg. It was found that the Ct/C0 value decreased from 0.14 to 0.05, indicating an improvement in the degradation performance [114]. On increasing the Mn0.5Zn0.125Mg0.375Fe2O4 photocatalyst dose, it was found that the value of the Ct/C0 declines from 60 to 50, corresponding to 40% to 50% Rhodamine B removal after 80 min. The higher doses of the catalyst led to an increased absorption of photons by the catalyst, and the degradation efficiency improved (Figure 4a). Similar behavior has been observed while using CoFe2O4/rGO composite as a photocatalyst for the degradation of methylene blue dye [115]. When the catalyst dosage was increased upto 0.5 gL −1 , the degradation efficiency increased to 47% due to the increased absorption of photons on the surface of the photocatalyst (Figure 4b). However, overdoses of the sample (1 gL −1 ) led to falls in the degradation effectiveness. Barium ferrite for the degradation of basic yellow 28, methylene blue, acid orange 7, and basic violet showed similar increases with increases in the catalyst loading from 1 to 10 gL −1 [76]. The influence of the catalyst dose on the degradation efficiency of acetamiprid was studied by varying the catalyst dose from 0 to 200 mg L −1 . On increasing the amount of GO-Fe3O4and GO-CoFe2O4 upto certain limit, the degradation increases because of the availability of more catalyst sites for the absorption of light [102]. Effective degradation was achieved for each of the four catalysts, at a catalyst dose of 100 mg L −1 , and the trend of degrading the acetamiprid was observed increase. However, a further increase in the catalyst concentration led to decreased degradation rates because of the agglomeration of the catalyst. CuCe-Ferrite/TiO2 was used for the photodegradation of the reactive red 250 dye, and the efficiency was found to be 100% using 0.32g/100mL of the catalyst. A shift to more wavelength was observed due to the combination of CuCe-Ferrite andTiO2 and hence the absorption of more visible light [28]. Adapted with permission [115]; copyright (2020), Elsevier.
Thus, the photocatalyst dose is an important factor that affects the efficiency of a photocatalyst. In general, it is observed that increasing the photocatalyst dose can lead to a higher efficiency of photo degradation. However, excessively high concentrations can lead to the aggregation of ferrites, which can reduce their efficiency [84].

Effect of Surface Area of Photocatalyst
The photocatalytic activity of the nanomaterials is enhanced when their surface area is large. The surface area of the nanoparticles is increased with a decrease in particle size, ultimately improving their dispersion in a solution and enhancing their interaction with pollutants. This leads to an improvement in their photocatalytic activity.
The effect of the surface areas of the magnetic NPs system NixZn1−xFe2O4, with different concentrations of Ni 2+ ions (0.0≤x≤1.0), on the photocatalytic degradation of methylene blue was studied [29]. The Ni0.6Zn0.4Fe2O4was found to have better photocatalytic activity, having a surface area of (36.6 m 2 g −1 ) [110]. The particle size and morphology of the Cu1−xMnxFe2O4 effects the photocatalytic degradation of the 4-chlorophenol [116]. For the photodegradation of pendimethalin, core-shell nanocomposites of Sr0.4Ti0.6Fe2O4.6@SiO2 were used. The increased specific surface area and more active sites observed in the scanning electron and transmission electron micrographs were attributed to the higher photocatalytic efficiency in the core-shell nanocomposites. The highest percentage photodegradation of the pendimethalin was observed in the Sr0.4Ti0.6Fe2O4.6@SiO2 core-shell nanocomposites, which was found to be 96% [117]. The study on the influence of Zn content on the efficiency of Zn/Fe2O4 degradation in visible light radiation [118] reported that there was a 40% residual concentration of carbamazepine after an 80-min iron oxide irradiation. On the other hand, the residual carbamazepine concentration decreased as the zinc content increased ( Figure 5). Since photocatalytic degradation is a surface-mediated process, the improved degradation efficiency is the result of the increased specific surface area of the zinc-rich nanoparticles [119].
The calcination temperature also plays vital role in the increase of the surface area of the photocatalyst. It was observed that on decreasing the calcination temperature of MgFe2O4 from 600°C to 500°C, the particle size of the NPs increased which in turn increased the surface area and ultimately enhanced the photocatalytic activity [120]. The removal of the basic yellow 28, methylene blue, acid orange 7, and basic violet has been studied using barium ferrite composite [76].The complete decomposition of the dye was observed using 1000°C sintered catalyst, while catalysts that were sintered at 700°C or 800°C degraded only 30% of the dye. The superior removal efficiency of the catalyst sintered at 1000°C was due to presence of more barium ferrite phase. On the contrary, the degradation of the congo red, methyl orange, methylene blue, Rhodamine B, 4-nitrophenol, and 4-chlorophenol using the CoFe2O4 xerogel was found to decrease from 96% to 75% when it was calcined at a temperature range of 500-900°C. As the calcining temperature rose, the rate of degradation of the nano-CoFe2O4 photocatalyst decreased, which was related to the BET-specific surface area of the CoFe2O4 NPs [121]. Figure 5. Effect of Zn content on the degradation ofcarbamazepine using ZnFe2O4 NPs. Adapted with permission [118]; copyright (2021), Elsevier.
Hence, the particle size, surface area, and availability of the active sites are very important characteristics for enhancing photocatalytic properties. Small particle sizes with high crystallinity are crucial in this regard because their higher specific surface area encourages greater photocatalytic activity. Sometimes, synthesizing at a high temperature is necessary to create particles with a high crystallinity, but it also increases the particle size. As a result, one must consider how to maximize crystallinity without sacrificing particle size [122].

Effect of Substrate Concentration
The dependence of the substrate concentration on the photocatalytic reaction rate is an important factor. The photocatalytic degradation was the highest for 10 mg·L −1 of dye concentration, which decreased on further increasing the methyl orange concentration from 10 to 30 mg L −1 due to absorption of solar light by the dye [113]. A contradictory behavior was observed while using the CoFe2O4/rGO photocatalyst for the methylene blue [115]. The photocatalytic efficiency of the CoFe2O4/rGO photocatalyst increased from 47 to 55% on raising the initial dye concentration from 2 to 5 mg·L −1 and decreased to 45% for 15 mg·L −1 . The strong interactions between the nanocomposite and dye molecules were responsible for the initial rise in the degradation efficiency ( Figure 6). However, lesser photons adsorption by the photocatalyst due to the increase in the methylene blue dye decreased the activity of the catalyst. Similar behavior was observed in MFe2O4 (M = Co, Ni, Cu, Zn) for the degradation of the methylene blue upto 94% using 20 mg·L −1 of photocatalyst. The efficiency decreased to 65% for a 50 mg·L -1 methylene blue solution. However, the limited production of the active radicals, which were insufficient to degrade the higher concentration of the methylene blue dye, was the main factor in the outcome. The photogeneration of the electron-hole pairs was also hampered by the highly concentrated methylene blue dye solution, as it reduced photon penetration in the solution phase [111]. Similar results were observed during the degradation of the methylene blue dye using CuFe2O4/TiO2 and ZnFe2O4 [109,112].
The effect of the substrate concentration on the photodegradation of reactive red 250 dye using TiO2 and CuCe-Ferrite/TiO2 NPs has been examined [28]. When the concentration of the reactive red 250 was increased to 100 ppm, a decrease in the chemical oxygen demand was observed over TiO2 and CuCe-Ferrite/TiO2 NPs. These observations were correlated to a decrease in the light penetration because an increase in the reactive red 250 dye concentration resulted in the incorporation of additional reactive red 250 dye molecules onto the TiO2 and CuCe-Ferrite/TiO2 NPs. The Fe3O4, GOFe3O4, CoFe2O4, and GO-CoFe2O4 effectively (80%) degraded 10 mg·L −1 solution of acetamiprid. The degradation efficiency was observed to be 100% on increasing the acetamiprid from 2 to 8 mg·L −1 . However, as the pesticide dose was increased from 10 mg·L −1 to 16 mg·L −1 , more active sites were occupied due to the increased addition of pollutant molecules [102].

Effect of Irradiation Intensity and Time
The intensity of the irradiation is another important factor responsible for the photodegradation process. The effect of the irradiation intensity has been studied for the photocatalytic degradation of basic yellow 28, methylene blue, acid orange 7, basic violet using barium ferrite, and rGO composite [76]. With an increase in the irradiation intensity from 3500 to 15,000 lx, the degradation efficiency went from 3 to 25%. The degradation rose to 47.4% with an additional increase in the irradiation intensity to 26,000 lx. The clear indication that the catalyst activity was based on photocatalysis rather than any other assumed mechanisms was due to the sizeable increase in degradation with irradiation intensity. At higher irradiation intensities, the catalyst surface was exposed to more photons, which can be used to fuel the degradation process.
The effect of irradiation time has been studied for the photodegradation of methylene blue using CoFe2O4/rGO. The degradation efficiency increased on increasing the irradiation time to 180 min with catalyst dosage of 0.5 gL −1 , and a methylene blue dye concentration of 5 mg·L −1 reached a relatively stable value [115] (Figure 4b and 6). ZnFe2O4 NPs were used to measure the rate of the methylene blue dye decomposition over time. When the dye was exposed to UV light, the degradation increased (99.8%) with longer exposure times, up to 45 min. A plateau was reached after 45 min because the degradation did not increase [112].
A rapid increase in the degradation of acetamiprid was observed when the irradiation time was varied from 15 to 120 min and studied at an ideal pH, oxidant dose, dose of pesticide, and catalyst. The rate slowed down with time, and the active sites required 60 min to completely degrade the pollutant [102]. When the magnesium ions were doped in the cobalt ferrite NPs at various fractions, the rate of photo degradation increased and the degradation time fell to 225 min, which was 330 min for the pure cobalt ferrite. An increase in the Mg 2+ concentration decreases the rate of degradation due to the consequent increase in the number of active sites on the surface of the photocatalyst [123].

Effect of Doping
The doping of ferrites is also emerging as a new method for enhancing photocatalytic potential, as doped ferrites display enhanced visible light absorption and improved photodegradation efficiency towards various types of organic pollutants [122].
The effectiveness of MRuxFe2−xO4 (M= Ni, Cu) NPs was assessed for remazol deep red and ciprofloxacin photocatalytic degradation [101]. With an increasing Ru content, the catalytic activity of the MRuxFe2−xO4 (x = 0, 0.02, 0.06, 0.1, and 0.4) increased. The NiRu0.4Fe1.6O4 demonstrated the best catalytic performance, with complete degradation in 5 min. When the Ru was substituted, the increased catalytic activity supported the preference for the octahedral site. The CuRuxFe2−xO4 showed an increase in the photo-catalytic efficiency, which was found to be 92% for x = 0.02, whereas with further substitution up to x = 0.06 and x = 0.1, the degradation time reached 120 min and 90 min, respectively. Similarly, when the Ti content in the ternary-doped Sr1−xTixFe2O4+δ ferrite was increased from 0.3 to 0.6, the band gap was decreased from 2.45 to 2.18 eV, which increased the charge carrier concentration and decreased the barrier height from 1.20 to 1.02 eV, compared to the pure SrFe2O4 and TiFe2O5 [83]. These features were very helpful for the degradation of the p-nitrophenol, pendimethalin and martius yellow with apparent rate constant values 1.9 × 10 −2 min −1 , 2.3 × 10 −2 min −1 , and 1.3 × 10 −2 min −1 , respectively. Similar results have been reported for the degradation of rhodamine B dye [124].
Furthermore, doping Y 3+ into pure CoFe2O4has improved the stability of the composite and increased photocatalytic activity compared to that of pure CoFe2O4 NPs [125]. The doping increased the stability and effectiveness of the CoFe2O4 NPs when exposed to visible light. However, higher concentrations of metal ions may cause the photocatalyst to lose its crystallite and have more internal defects. As a result, it decreased the efficiency of the photocatalytic system. Moreover, the photocatalytic activity was increased by using rare earth metals such as Dy 3+ , Nd 3+ , Eu 3+ , Gd 3+ , and others as dopants [126]. The photocatalytic efficiency increased, while the energy band gap decreased (1.95 to 1.42) when the Sm 3+ was doped into the pure ZnFe2O4 (ZnSmxFe2−XO4). High photocatalytic degradation of methyl orange was observed when the ZnSm1.5Fe0.5O4 NPs were used as a photocatalyst. After 80 min, 92.3% of the degradation was observed [113].
Generally, the doping of ferrites causes a narrowing of the band gap, which aids in in the absorption of lower energy photons and trapping of electrons [127][128][129]. This renders them a superior visible light active photocatalyst compared to the other nanomaterials. However, it is difficult to predict the best kind of dopant, as their efficiency can change with changes in other operational parameters.

Effect of Quenchers
In order to conclude the probable photocatalytic degradation mechanism of different organic pollutants over the photocatalyst surface, various quenchers have been added to study the quenching effect. It has been observed that the use of various scavengers decreases the photocatalytic degradation efficiencies [28]. Different quenchers, such as ethylene diamine tetraacetate (EDTA, h + scavenger), methanol/butanol (CH3OH/C4H9OH, • OH scavenger), ascorbic acid (C6H8O6, • O 2− scavenger), and sodium azide (NaN3, O2 * species) work according to the following reactions: Singlet oxygen forms charge transfer complex with N3 − which ultimately decomposes into N3 radical.
Various studies based on photocatalysis have demonstrated that out of ethylene diamine tetraacetate, methanol/butanol, ascorbic acid, and sodium azide, ascorbic acid possesses the highest inhibiting effect, which means that the • O 2− radicals were primary species responsible for the degradation of the organic pollutants [84,117,130].The addition of ascorbic acid greatly quenched (61.8%) the photodegradation of the martius yellow, followed by the butanol (73.7%), ethylene diamine tetraacetate (92.3%) and methanol (90.9%), using magnesium ferrite-bentonite as a photocatalyst [88]. This might be due to the increase in the number of the hydroxyl radicals in the presence of hydrogen peroxide, a potent oxidising agent [114]. A similar quenching effect was studied for methyl orange and tetracycline degradation [131].
However, a limited number of papers have been published addressing the effect of quenchers on the degradation of organic pollutants. Thus, clear insight about the influence of quenchers has not been explored yet.

Photodegradation Mechanism
Photocatalysis using ferrite-based nanomaterials as photocatalysts involves the interaction of photons of light to breakdown various organic pollutants [132][133][134][135][136]. They consist of semiconductors with large bandgaps where electrons are readily promoted from valence into the conduction band after the absorption of photons. This results in the generation of photoexcited electrons (e − ) and positive-valence band holes (h + ). The photocatalytic mechanism of degradation works through pollutants being reduced or oxidized by photoexcited electrons (e − ) and holes (h + ). In water, hydroxide ( − OH) ions (generated when positive-valence band holes (h + ) are trapped by water) are non-selective strong oxidizing agents that oxidize organic pollutants to water and gaseous products. Similarly, photoexcited electrons can react with O2 to form other reactive oxygen species that can be used to further degrade pollutants [132,137]. The photocatalytic degradation of organic pollutants, such as rhodamine B, imidacloprid, and acetamiprid, has been reported for Ag/AgBr/NiFe2O4 and ZnO/CoFe2O4 [138][139][140][141].
In the case of doped ferrite NPs, the doped element enhances the photocatalytic potential of the pristine ferrite materials; for example, cerium doping in cobalt ferrite NPs plays the important role of electron scavenger [141]. The interfacial electron transfer, photo-excited charge generation, and inhibition of (e − -h + ) recombination were completely dependent on the Ce 4f level (Equation (1)). The electron-scavenging efficiency of Ce 4+ helps to capture the conduction-band electrons, and due to its Lewis acidic nature, it was found to be more effective at trapping electrons compared to the molecular oxygen (Equation (2)). Through an oxidation process (Equation (3)), the electron was transferred to the adsorbed O2, and superoxide radical anions (-O2 − ) were formed [115]. These reactive oxygen species helped in the degradation of the RhB dye.

RhB + ROS → Degraded products
Meanwhile, the H2O molecules can easily scavenge h + to produce -OH radicals (Equation (4)). The rhodamine B dye can be decomposed into CO2, H2O, and mineral acids.
The incorporation of ferrites into ultraviolet and visible light active metal oxides, polymers, carbon materials, etc. is another way to photodegrade organic pollutants.  The recovery of carbon-based materials is quite difficult due to their poor visible light absorption properties, which decrease their efficiency as photocatalysts for the removal of organic pollutants from wastewater. However, they are viewed as potential resources for improving the efficiency of MFe2O4 as a photocatalyst. Reduced graphene oxide sheets act as an electron trap center, which, as shown in Figure 8a, significantly enhances the photocatalytic activity of the MFe2O4 nanoparticles [148][149][150][151]. Polymers, such as polyaniline, are another type of supporting material. The positions of the highest and lowest occupied molecular orbitals (HOMO and LUMO) are −1.9 and 0.8 eV, respectively, as depicted in Figure 8b. When exposed to visible light, polyaniline on absorption undergoes π-π* transition. When the excited electron in the lowest occupied molecular orbital is transferred to the conduction band, it produces the reactive species, which are responsible for degrading the organic pollutants [152,153].
Ferrite NPs are also combined with a variety of materials, such as metal sulphide [154], metal phosphate [155], metal oxyhalide [156], metal vanadate [3], metal titanate [157], etc., which makes their degradation mechanism different. MgFe2O4/Bi2MoO6 composites have been used to degrade malachite green dye [158]. Free radicals were produced through the Z-scheme mechanism, as shown in Figure 9. Due to the difference in the band gaps of the MgFe2O4 and Bi2MoO6, photogenerated electrons from the conduction band of the latter material diffuse to the valence band and become effectively trapped. Radicals produced by photogenerated holes and electrons, such as hydroxyl and superoxide, are also involved in the photodegradation process. Using the SnFe2O4/ZnFe2O4 heterostructure, the degradation of tetracycline observed followed the S-scheme mechanism (Figure 9), where holes in the valence band of the SnFe2O4 were neutralised by the photogenerated electrons in the ZnFe2O4 [159]. As a result, the availability of holes in the ZnFe2O4 and electrons in the SnFe2O4 makes the production of hydroxyl and superoxide radicals possible. Figure 9. Free radicals production using S-scheme and Z-scheme mechanisms. Adapted with permission [159]; copyright (2021), Elsevier.

Reusability and Stability
The ideal photocatalyst is one that is reusable and has high photocatalytic efficiency under visible light [160]. Therefore, one of the crucial steps is to recycle photocatalysts for the development of heterogeneous photocatalysis. Recent research has shown that magnetic nanoparticles can be successfully recycled using magnetic separation techniques [161][162][163][164][165].
Five consecutive cycles of photodegradation were conducted to examine the stability of Sr0.4Ti0.6Fe2O4.6@SiO2. A slight decrease (<7.0%) in the photocatalytic efficiency of pendimethalin was found after five runs, which was due to adsorption of the intermediate product on the surface of the photocatalyst where active sites are blocked [117]. Similar results were found when the hierarchical nanoflowers of the MgFe2O4, Bentonite and B-, P-co-doped Graphene Oxide were tested for their reusability and stability. The degradation efficiency was found to be decreased by only 5% after 5 consecutive cycles [83].
Generally, most of the magnetic nanocomposites can be reused upto three to four cycles, demonstrating their reusability when used for the photodegradation of pollutants from wastewater [75,101,112,166].

Conclusions and Future Perspective
In this review, the impact of different parameters on the photocatalytic degradation of organic effluents using ferrites and their nanocomposites has been elaborated. Differ-ent types of photodegradation mechanisms of ferrites and their nanocomposites are discussed. The use of visible light sensitive ferrite-based nanomaterials as photocatalysts for the remediation of wastewater and degradation of organic contaminants like pharmaceuticals, phenols, dyes, and other persistent organic pollutants is one of the most active research areas at the moment. The bulk synthesis of ferrite nanoparticles is needed for practical applications. Using chemical methods, the yield of ferrites is low, whereas physical methods yield ferrites in bulk but in micrometer regime. Future research can be focused on the bulk synthesis of ferrites using green and atomically efficient chemical methods and facile physical methods that can yield ferrites in nanometer range. Moreover, while evaluating the degradation efficacy of a photocatalyst, the pollutant concentration must always be taken into account, regardless of the pollutant that is intended to be removed. So, predicting the pollutant concentration and optimization of the catalyst dose must therefore be taken into account. Generally, ferrites and their nanocomposites, due to their appealing properties, such as their ease of surface modification and stability, are promising nanomaterials for addressing a variety of issues. Even though there have been many studies on ferrites, more research is needed on different parameters that affect the degradation of various organic pollutants under visible light, and technology having the potential to optimize the influential parameters is needed for the photocatalysis process to be more economical.