Novel SAW Temperature Sensor with Pt/Ti/AlN/Mo/AlN/Si Structure for High Temperature Application

: In this paper, a surface acoustic wave (SAW) temperature sensor with a Pt/Ti/AlN/Mo/AlN/Si structure was prepared, and the high temperature characteristics of the sensors at 20–600 ◦ C under different electrode metallization rates (


Introduction
Temperature detection, whether in industrial production or daily life, has received great attention.However, in aerospace [1,2], geothermal research [3], turbine engines [4] and other fields, when monitoring super high temperatures, traditional temperature sensors generally require transmission lines and power supplies, such as thermocouples and optical fibers, which lead to cumbersome wiring, interference with working conditions and even accidents, so it is very difficult to implement temperature measurement for highspeed objects or objects in confined spaces [5].Therefore, passive wireless sensors have irreplaceable advantages.Although infrared temperature measurement, LC resonator temperature measurement and reflective antenna temperature measurement can achieve a passive wireless state, they are limited by factors such as poor anti-electromagnetic interference ability, large size and short wireless transmission distance.SAW stands for acoustic surface waves, which are waves that propagate on the surface or interface of elastomers, and the wave speed is much smaller than that of electromagnetic waves; ) were measured.It was found that frequent device mutation occurred in the first high-temperature test, and that the mutation point decreased with the increase in the electrode metallization rate (

Introduction
Temperature detection, whether in industrial production or daily life, has received great attention.However, in aerospace [1,2], geothermal research [3], turbine engines [4] and other fields, when monitoring super high temperatures, traditional temperature sensors generally require transmission lines and power supplies, such as thermocouples and optical fibers, which lead to cumbersome wiring, interference with working conditions and even accidents, so it is very difficult to implement temperature measurement for highspeed objects or objects in confined spaces [5].Therefore, passive wireless sensors have irreplaceable advantages.Although infrared temperature measurement, LC resonator temperature measurement and reflective antenna temperature measurement can achieve a passive wireless state, they are limited by factors such as poor anti-electromagnetic interference ability, large size and short wireless transmission distance.SAW stands for acoustic surface waves, which are waves that propagate on the surface or interface of elastomers, and the wave speed is much smaller than that of electromagnetic waves; .; Wu

Introduction
Temperature detection, whether in industrial production or daily life, has received great attention.However, in aerospace [1,2], geothermal research [3], turbine engines [4] and other fields, when monitoring super high temperatures, traditional temperature sensors generally require transmission lines and power supplies, such as thermocouples and optical fibers, which lead to cumbersome wiring, interference with working conditions and even accidents, so it is very difficult to implement temperature measurement for high-speed objects or objects in confined spaces [5].Therefore, passive wireless sensors have irreplaceable advantages.Although infrared temperature measurement, LC resonator temperature measurement and reflective antenna temperature measurement can achieve a passive wireless state, they are limited by factors such as poor anti-electromagnetic interference ability, large size and short wireless transmission distance.SAW stands for acoustic surface waves, which are waves that propagate on the surface or interface of elastomers, and the wave speed is much smaller than that of electromagnetic waves; therefore, they can be used in the development of miniature devices.SAW devices have the advantages of being passive wireless devices [6,7], having strong antiinterference ability, being of a small size, being low-priced, being compatible with the MEMS process and large-scale manufacturing, and being an important means to achieve high temperature measurement in harsh and closed environments [8][9][10].SAW resonant sensors generally consist of interdigital electrodes (IDTs), reflective barriers, and piezoelectric substrates, which can be piezoelectric films, piezoelectric single crystals, and piezoelectric ceramics.Piezoelectric films are generally grown on substrates such as diamond, sapphire, SiC and Si.Compared to traditional piezoelectric materials such as quartz, lithium niobate (LN), and potassium lanthanum silicate (LGS), AlN has a higher melting point of up to 2000 • C [11], good piezoelectric characteristics below 1150 • C [12], and higher sound velocity (5500 m/s in the a-axis and 11,345 m/s in the c-axis) [13], therefore often being used in the preparation of SAW devices [13][14][15][16].Additionally, because it has the best piezoelectric properties and the highest sound velocity in the (002) orientation, the preparation of AlN in the (002) orientation is a goal.
Single-crystal Si is a common substrate, and AlN is used as a piezoelectric material; the research of G. F. Iriarte [17] found that the bottom electrode layer affects the growth of AlN films, which in turn affects their electroacoustic performance.HOANG Trang [18] found that adding a Mo bottom electrode layer under the AlN layer could increase the gain of the SAW filter, and experiments showed that its frequency increased, the loss decreased, and the electromechanical coupling coefficient increased.Therefore, in this paper, Mo was selected as the bottom electrode material to promote the growth of AlN in the (002) orientation and improve the electromechanical coupling coefficient of the device [17][18][19][20].At the same time, the AlN seed layer was added to alleviate the problem of large lattice mismatch between Si and Mo.Of course, it also had another role in helping the AlN piezoelectric layer to grow.Pt has a melting point of 1768 • C, which gives good oxidation resistance and high temperature stability, so Pt was selected as the IDT electrode material, and Ti was added as the adhesion layer to prevent the precious Pt metal from falling off due to poor adhesion with AlN.The SAW temperature sensor with a Pt/Ti/AlN/Mo/AlN/Si structure was prepared, and the AlN grown by this structure had a good (002) orientation.The high-temperature RF test set consisted primarily of a vector network analyzer (E5061B, Keysight) and a high-temperature tube furnace.In the test of the temperature sensitivity characteristics of the sensor, we found that the frequency-temperature relationship (f-T) curve of the sensor after multiple high-temperature tests had higher linearity and a more stable performance than the sample tested once did, its return loss (S11) value became smaller, and the figure of merit Q became larger, which means that the overall performance of the device was significantly improved.This phenomenon is discussed in detail in this article.

Design and Simulation
The design of the sensor structure was simulated using the simulation software COMSOL Multiphysics.The main resonant mode of the sensor was designed as a Rayleigh resonant mode, which has two modes: a symmetric mode and antisymmetric mode, as shown in Figure 1a,b.Among them, the eigenfrequencies corresponding to the symmetric mode became the resonant frequency, and the eigenfrequencies corresponding to the opposing modes became the inverse resonant frequency.
It is known that the appropriate bottom electrode layer has a positive effect on the electromechanical coupling coefficient of the device and the growth of the piezoelectric layer as discussed in the Introduction [17][18][19][20], so we first simulated the center frequency of the overall structure of the device to verify the positive effect of the AlN seed layer on the sensor; the two structures were Pt/Ti/AlN/Mo/AlN/Si and Pt/Ti/AlN/Mo/Si.The material data used for the simulation are shown in Tables 1 and 2, and the simulation results are summarized in Table 3.The resonant frequency of a device with a seed layer is 197.8MHz, and the center frequency of a device without a seed layer is also 197.8 MHz.Based on the simulation results, firstly, it was believed that the addition of an AlN seed layer would not have a negative impact on the device; secondly, due to the limitations of the simulation, the quality of each layer of film in the simulation was consistent, the real growth of the film would be affected by the substrate's structure, and the seed layer would generally promote the growth of the specific orientation of the piezoelectric layer, so the Pt/Ti/AlN/Mo/AlN/Si structure was adopted in this article.
Chemosensors 2023, 11, x FOR PEER REVIEW 3 of 13 on the simulation results, firstly, it was believed that the addition of an AlN seed layer would not have a negative impact on the device; secondly, due to the limitations of the simulation, the quality of each layer of film in the simulation was consistent, the real growth of the film would be affected by the substrate's structure, and the seed layer would generally promote the growth of the specific orientation of the piezoelectric layer, so the Pt/Ti/AlN/Mo/AlN/Si structure was adopted in this article.In addition, we simulated the influence of sensor film thickness and electrode structure parameters on a sensor's performance, and combined the experiences and process conditions cited in the literature to obtain the final sensor structure data.The simulation showed that the resonant frequency decreases with an increase in the thickness of the electrode, but that the stability of a too-thin electrode will be poor at a high temperature, so the electrode thickness was designed to be 200 nm ± 10 nm.According to the experience of the process and the simulation results, it is believed that the film easily crackes when the thickness of the AlN piezoelectric layer is too high, and that the piezoelectric excitation effect is poor when it is too thin, so the AlN design was chosen to be 1 µm.Combined with the experiences and process conditions cited in the literature experience, the wavelength (λ) was designed to be 24 µm, the pore size (W) was 90λ, the number of reflected gate pairs (Nr) and interdigital electrode pairs (Nt) was 100 pairs, and the interdigital spacing (P) was 12 µm.These are summarized in Table 4.In addition, there were three device structures with different metallization rates (

Introduction
Temperature detection, whether in industrial production or da great attention.However, in aerospace [1,2], geothermal research [3] and other fields, when monitoring super high temperatures, tradition sors generally require transmission lines and power supplies, such as optical fibers, which lead to cumbersome wiring, interference with and even accidents, so it is very difficult to implement temperature me speed objects or objects in confined spaces [5].Therefore, passive w irreplaceable advantages.Although infrared temperature measure temperature measurement and reflective antenna temperature measu a passive wireless state, they are limited by factors such as poor anti terference ability, large size and short wireless transmission distan acoustic surface waves, which are waves that propagate on the surfac tomers, and the wave speed is much smaller than that of elec  In this paper, a surface acoustic wave (SAW) temperature sensor with a o/AlN/Si structure was prepared, and the high temperature characteristics of the sen-00 °C under different electrode metallization rates ( ղ ) were measured.It was found nt device mutation occurred in the first high-temperature test, and that the mutation ased with the increase in the electrode metallization rate (ղ).In the subsequent test, the e stable, the sensor's center frequency increased, the return loss (S11) decreased and the erit (Q) increased.After annealing the same sensors at 600 °C for 30 min, they could formance improvement in the first test, meaning that proper annealing can improve senance.In addition, the annealed SAW sensor was tested in the temperature range of 20hich met the requirement of a temperature range of 20-900 °C, its f-T curve was linear, f merit (Q) was 34.5 and the sensitivity was 46.6 KHz/K.SAW sensor; high temperature; electrode metallization rate; annealing ction erature detection, whether in industrial production or daily life, has received tion.However, in aerospace [1,2], geothermal research [3], turbine engines [4] fields, when monitoring super high temperatures, traditional temperature senally require transmission lines and power supplies, such as thermocouples and ers, which lead to cumbersome wiring, interference with working conditions ccidents, so it is very difficult to implement temperature measurement for highcts or objects in confined spaces [5].Therefore, passive wireless sensors have ble advantages.Although infrared temperature measurement, LC resonator re measurement and reflective antenna temperature measurement can achieve wireless state, they are limited by factors such as poor anti-electromagnetic inability, large size and short wireless transmission distance.SAW stands for rface waves, which are waves that propagate on the surface or interface of elasnd the wave speed is much smaller than that of electromagnetic waves;

Introduction
Temperature detection, whether in industrial production or daily life, has received great attention.However, in aerospace [1,2], geothermal research [3], turbine engines [4] and other fields, when monitoring super high temperatures, traditional temperature sensors generally require transmission lines and power supplies, such as thermocouples and optical fibers, which lead to cumbersome wiring, interference with working conditions and even accidents, so it is very difficult to implement temperature measurement for highspeed objects or objects in confined spaces [5].Therefore, passive wireless sensors have irreplaceable advantages.Although infrared temperature measurement, LC resonator temperature measurement and reflective antenna temperature measurement can achieve a passive wireless state, they are limited by factors such as poor anti-electromagnetic interference ability, large size and short wireless transmission distance.SAW stands for acoustic surface waves, which are waves that propagate on the surface or interface of elastomers, and the wave speed is much smaller than that of electromagnetic waves; = 50; and Sample 3:

Introduction
Temperature detection, whether in industrial production or daily life, has received great attention.However, in aerospace [1,2], geothermal research [3], turbine engines [4] and other fields, when monitoring super high temperatures, traditional temperature sensors generally require transmission lines and power supplies, such as thermocouples and optical fibers, which lead to cumbersome wiring, interference with working conditions and even accidents, so it is very difficult to implement temperature measurement for highspeed objects or objects in confined spaces [5].Therefore, passive wireless sensors have irreplaceable advantages.Although infrared temperature measurement, LC resonator temperature measurement and reflective antenna temperature measurement can achieve a passive wireless state, they are limited by factors such as poor anti-electromagnetic interference ability, large size and short wireless transmission distance.SAW stands for acoustic surface waves, which are waves that propagate on the surface or interface of elastomers, and the wave speed is much smaller than that of electromagnetic waves; = 67%), and the interdigital electrode widths were 3, 6 and 8 µm, respectively.The electrode metallization rate (

Introduction
Temperature detection, whether in industrial production or daily life, has re great attention.However, in aerospace [1,2], geothermal research [3], turbine engi and other fields, when monitoring super high temperatures, traditional temperatu sors generally require transmission lines and power supplies, such as thermocoupl optical fibers, which lead to cumbersome wiring, interference with working cond and even accidents, so it is very difficult to implement temperature measurement fo speed objects or objects in confined spaces [5].Therefore, passive wireless sensor irreplaceable advantages.Although infrared temperature measurement, LC res temperature measurement and reflective antenna temperature measurement can a a passive wireless state, they are limited by factors such as poor anti-electromagne terference ability, large size and short wireless transmission distance.SAW stan acoustic surface waves, which are waves that propagate on the surface or interface o tomers, and the wave speed is much smaller than that of electromagnetic w ) is the ratio of the width of the interdigital electrode strip to its interval in the single-period interdigital space (P).

Materials and Methods
AlN films were deposited by the commonly used reactive radio frequency magnetron sputtering method (Sigma fxP, SPTS), RF-250W and a substrate temperature of 200 • C. X-ray diffraction (XRD) was used to analyze the crystal orientation of the deposited AlN thin films, the full width at half of the maximum (FWHM) value reflected its orientation consistency, and the smaller the value, the better the orientation.The deposition of other thin films like Pt/Ti are also by magnetron sputtering deposition.Field emission scanning electron microscopy (SEM) was used to monitor film surface topography, thickness, and facet structure.
The sensor preparation process firstly involved cleaning the Si sheet, and then magnetron sputtering was performed to grow a 30 nm AlN seed layer, 100 nm Mo bottom electrode layer and 1 µm AlN piezoelectric layer.Sputtering was performed to grow a 10 nm Ti and 200 nm Pt upper electrode layer, and then photolithographic development was performed.Then, through ion beam etching (IBE), Pt/Ti films were etched into the shape of the interdigital electrode, and degumming was finally performed.The specific process steps are shown in Figure 2. The schematic diagram of Pt/Ti/AlN/Mo/AlN/Si SAW sensors is shown in Figure 3.
In order to perform the high-temperature test, the sensor was first packaged in a simple high-temperature resistant package: the sensor was glued to a ceramic strip of a length of 60 cm with high-temperature resistant inorganic glue (Ausband A520), the sensor pad and PCB were then connected through wires, and the connection point was bonded with Pt paste.The end with the adhesive sensor was extended by about 50 cm into the high-temperature tube furnace (DTL-600, DTK-01, DEARTO) with a high temperature range and could be heated to 1200 • C. Tubular furnaces have the property of precise temperature control to ensure accurate temperature measurements.We connected the PCB to the vector network analyzer (E5061B, Keysight) through an RF cable, which set the sweep range to be from 30 MHz to 500 MHz; the number of sweep points was 1800, and the intermediate frequency bandwidth was 10 KHz.The vector network analyzer was used to detect the change of S-parameter S11 and frequency in sensors with the temperature, and to obtain the relationship between frequency and temperature (f-T).They had a linear relationship, which is explained in the next formula.The schematic and physical diagrams of the experimental setup are shown in Figure 4a,b, respectively.In order to perform the high-temperature test, the sensor was first packaged in a simple high-temperature resistant package: the sensor was glued to a ceramic strip of a length of 60 cm with high-temperature resistant inorganic glue (Ausband A520), the sensor pad and PCB were then connected through wires, and the connection point was bonded with Pt paste.The end with the adhesive sensor was extended by about 50 cm into the hightemperature tube furnace (DTL-600, DTK-01, DEARTO) with a high temperature range and could be heated to 1200 °C.Tubular furnaces have the property of precise temperature control to ensure accurate temperature measurements.We connected the PCB to the vector network analyzer (E5061B, Keysight) through an RF cable, which set the sweep range to be from 30 MHz to 500 MHz; the number of sweep points was 1800, and the intermediate frequency bandwidth was 10 KHz.The vector network analyzer was used to detect the change of S-parameter S11 and frequency in sensors with the temperature, and to obtain the relationship between frequency and temperature (f-T).They had a linear relationship, which is explained in the next formula.The schematic and physical diagrams of the experimental setup are shown in Figure 4a,b, respectively.In order to perform the high-temperature test, the sensor was first packaged in a sim ple high-temperature resistant package: the sensor was glued to a ceramic strip of a length of 60 cm with high-temperature resistant inorganic glue (Ausband A520), the sensor pad and PCB were then connected through wires, and the connection point was bonded with Pt paste.The end with the adhesive sensor was extended by about 50 cm into the high temperature tube furnace (DTL-600, DTK-01, DEARTO) with a high temperature rang and could be heated to 1200 °C.Tubular furnaces have the property of precise temperatur control to ensure accurate temperature measurements.We connected the PCB to the vec tor network analyzer (E5061B, Keysight) through an RF cable, which set the sweep rang to be from 30 MHz to 500 MHz; the number of sweep points was 1800, and the interme diate frequency bandwidth was 10 KHz.The vector network analyzer was used to detec the change of S-parameter S11 and frequency in sensors with the temperature, and to ob tain the relationship between frequency and temperature (f-T).They had a linear relation ship, which is explained in the next formula.The schematic and physical diagrams of th experimental setup are shown in Figure 4a,b, respectively.In order to perform the high-temperature test, the sensor was first packaged in a simple high-temperature resistant package: the sensor was glued to a ceramic strip of a length of 60 cm with high-temperature resistant inorganic glue (Ausband A520), the sensor pad and PCB were then connected through wires, and the connection point was bonded with Pt paste.The end with the adhesive sensor was extended by about 50 cm into the hightemperature tube furnace (DTL-600, DTK-01, DEARTO) with a high temperature range and could be heated to 1200 °C.Tubular furnaces have the property of precise temperature control to ensure accurate temperature measurements.We connected the PCB to the vector network analyzer (E5061B, Keysight) through an RF cable, which set the sweep range to be from 30 MHz to 500 MHz; the number of sweep points was 1800, and the intermediate frequency bandwidth was 10 KHz.The vector network analyzer was used to detect the change of S-parameter S11 and frequency in sensors with the temperature, and to obtain the relationship between frequency and temperature (f-T).They had a linear relationship, which is explained in the next formula.The schematic and physical diagrams of the experimental setup are shown in Figure 4a,b, respectively.The temperature characteristic equation represents the relationship between temperature and frequency in a SAW sensor [21]: where T 0 is the reference temperature, T is the detection temperature, f 0 is the resonant frequency corresponding to the reference temperature (T 0 ), and A, B, and C are the first, second, and third order frequency temperature coefficients, respectively.When the piezoelectric material is determined, the temperature coefficients of the second order and later orders are small and negligible.
The relationship between the resonant frequency and the amount of temperature change can be simplified by the resonant frequency expression: where λ SAW is the SAW wavelength, which is related to the interdigital transducer finger spacing and acoustic reflection grid array, and the size change caused by temperature change is small.V SAW is the SAW velocity, and the change in V SAW relative to the SAW propagation speed is negligible.
where A is the first frequency temperature coefficient.It can also be expressed as TCF, which represents the sensitivity of the temperature sensor.According to the above Equation ( 4), the temperature of the object to be measured can be obtained through a measurement of the frequency and the f-T relationship.From this formula, we can also find that the change in frequency and temperature is linear, that is, that the f-T curve tends to be linear.
In previous tests, it was found that the frequency of the sample did not change significantly with the temperature before it reached 300 • C, and that there was a good f-T relationship above 300 • C. Therefore, in the following test, in order to ensure the accuracy of the experiment, when testing the sensor at high temperatures, data was collected every 20 K below 300 • C and every 50 K above 300 • C by a network analyzer.

Results and Discussion
The XRD test found that the AlN in the AlN/Mo/AlN/Si structure had a (002) orientation at about 36.1 • and a full width at the half maxumym (FWHM) of 0.21 • , showing a higher C-axis orientation.SEM was performed on a cross-sectional plane, showing a columnar structure, validating the results of the XRD test as shown in Figure 5.The results show that the AlN/Mo/AlN/Si structure grew a good C-axis AlN piezoelectric film.The cross-finger electrode morphology of the vegetation was observed by SEM, and the electrode morphology was good, as shown in Figure 6.The high-temperature test was carried out in the temperature range of 20-600 °C, and Samples 1, 2 and 3 were tested multiple times; we found that the first test result was very different from the result of the second test, and that the data became stable after multiple tests.Figure 7 shows the temperature-frequency-S11 relationship (T-f-S11) between Samples 1, 2, and 3.The high-temperature test was carried out in the temperature range of 20-600 • C, and Samples 1, 2 and 3 were tested multiple times; we found that the first test result was very different from the result of the second test, and that the data became stable after multiple tests.Figure 7 shows the temperature-frequency-S11 relationship (T-f-S11) between Samples 1, 2, and 3.The high-temperature test was carried out in the temperature range of 20-600 °C, and Samples 1, 2 and 3 were tested multiple times; we found that the first test result was very different from the result of the second test, and that the data became stable after multiple tests.Figure 7 shows the temperature-frequency-S11 relationship (T-f-S11) between Samples 1, 2, and 3.

Analysis of the First Temperature Test
Observing Figure 7(a1,b1,c1), it can be seen that as the temperature increases, the frequency change is unstable or even unchanged, and a large change occurs at a certain temperature point, called the "mutation point".In Sample 1 (ղ = 25%), the point is T = 200 °C ; in Sample 2 (ղ = 50%), the point is T = 140 °C; and in Sample 3 (ղ = 67%), the point is T = 100 °C.It can be found that the higher the metallization rate, the smaller the temperature point at which the mutation occurs.At the same time, we can also find that the T-S11 curve has a "maximum loss point".In Sample 1 (ղ = 25%), the point is T = 200 °C; in Sample 2 (ղ = 50%), the point is T = 120 °C; and in Sample 3 (ղ = 67%), the point is T = 100 °C.Addi tionally, the higher the metallization rate is, the sooner the "maximum loss point" appears As can be seen from Equation (2), there are two factors that affect the change in the frequency of the sensor, which are the piezoelectric film and metal electrode.On the othe hand, the propagation of surface acoustic waves is also largely influenced by these two factors.Generally, as can be seen from Equations (3)-( 5), the influence of the electrode is this paper, a surface acoustic wave (SAW) temperature sensor with a o/AlN/Si structure was prepared, and the high temperature characteristics of the sen-0 °C under different electrode metallization rates ( ղ ) were measured.It was found t device mutation occurred in the first high-temperature test, and that the mutation sed with the increase in the electrode metallization rate (ղ).In the subsequent test, the stable, the sensor's center frequency increased, the return loss (S11) decreased and the rit (Q) increased.After annealing the same sensors at 600 °C for 30 min, they could rmance improvement in the first test, meaning that proper annealing can improve sennce.In addition, the annealed SAW sensor was tested in the temperature range of 20ch met the requirement of a temperature range of 20-900 °C, its f-T curve was linear, merit (Q) was 34.aper, a surface acoustic wave (SAW) temperature sensor with a structure was prepared, and the high temperature characteristics of the senr different electrode metallization rates ( ղ ) were measured.It was found utation occurred in the first high-temperature test, and that the mutation he increase in the electrode metallization rate (ղ).In the subsequent test, the sensor's center frequency increased, the return loss (S11) decreased and the reased.After annealing the same sensors at 600 °C for 30 min, they could provement in the first test, meaning that proper annealing can improve sendition, the annealed SAW sensor was tested in the temperature range of 20e requirement of a temperature range of 20-900 °C, its f-T curve was linear, was 34.5 and the sensitivity was 46.6 KHz/K.r; high temperature; electrode metallization rate; annealing = 67%).

Analysis of the First Temperature Test
Observing Figure 7(a1,b1,c1), it can be seen that as the temperature increases, the frequency change is unstable or even unchanged, and a large change occurs at a certain temperature point, called the "mutation point".In Sample 1 ( Abstract: In this paper, a surface acoustic wave (SAW) temperature sensor with a Pt/Ti/AlN/Mo/AlN/Si structure was prepared, and the high temperature characteristics of the sensors at 20-600 °C under different electrode metallization rates ( ղ ) were measured.It was found that frequent device mutation occurred in the first high-temperature test, and that the mutation point decreased with the increase in the electrode metallization rate (ղ).In the subsequent test, the data became stable, the sensor's center frequency increased, the return loss (S11) decreased and the factor of merit (Q) increased.After annealing the same sensors at 600 °C for 30 min, they could = 25%), the point is T = 200

t:
In this paper, a surface acoustic wave (SAW) temperature sensor with a N/Mo/AlN/Si structure was prepared, and the high temperature characteristics of the sen-0-600 °C under different electrode metallization rates ( ղ ) were measured.It was found uent device mutation occurred in the first high-temperature test, and that the mutation creased with the increase in the electrode metallization rate (ղ).In the subsequent test, the ame stable, the sensor's center frequency increased, the return loss (S11) decreased and the f merit (Q) increased.After annealing the same sensors at 600 °C for 30 min, they could performance improvement in the first test, meaning that proper annealing can improve senormance.In addition, the annealed SAW sensor was tested in the temperature range of 20-, which met the requirement of a temperature range of 20-900 °C, its f-T curve was linear, r of merit (Q) was 34.5 and the sensitivity was 46.6 KHz/K.ds: SAW sensor; high temperature; electrode metallization rate; annealing duction mperature detection, whether in industrial production or daily life, has received ttention.However, in aerospace [1,2], geothermal research [3], turbine engines [4] er fields, when monitoring super high temperatures, traditional temperature sennerally require transmission lines and power supplies, such as thermocouples and fibers, which lead to cumbersome wiring, interference with working conditions n accidents, so it is very difficult to implement temperature measurement for highbjects or objects in confined spaces [5].Therefore, passive wireless sensors have eable advantages.Although infrared temperature measurement, LC resonator ature measurement and reflective antenna temperature measurement can achieve ve wireless state, they are limited by factors such as poor anti-electromagnetic ince ability, large size and short wireless transmission distance.SAW stands for c surface waves, which are waves that propagate on the surface or interface of elas-, and the wave speed is much smaller than that of electromagnetic waves;

Introduction
Temperature detection, whether in industrial production or daily life, has received great attention.However, in aerospace [1,2], geothermal research [3], turbine engines [4] and other fields, when monitoring super high temperatures, traditional temperature sensors generally require transmission lines and power supplies, such as thermocouples and optical fibers, which lead to cumbersome wiring, interference with working conditions and even accidents, so it is very difficult to implement temperature measurement for highspeed objects or objects in confined spaces [5].Therefore, passive wireless sensors have irreplaceable advantages.Although infrared temperature measurement, LC resonator temperature measurement and reflective antenna temperature measurement can achieve a passive wireless state, they are limited by factors such as poor anti-electromagnetic interference ability, large size and short wireless transmission distance.SAW stands for acoustic surface waves, which are waves that propagate on the surface or interface of elastomers, and the wave speed is much smaller than that of electromagnetic waves; = 67%), the point is T = 100 • C. Additionally, the higher the metallization rate is, the sooner the "maximum loss point" appears.
As can be seen from Equation (2), there are two factors that affect the change in the frequency of the sensor, which are the piezoelectric film and metal electrode.On the other hand, the propagation of surface acoustic waves is also largely influenced by these two factors.Generally, as can be seen from Equations (3)-( 5), the influence of the electrode is very small, and the frequency and temperature relationship is linear.However, it is clear that the f-T curve in Figure 7(a1,b1,c1) does not have a linear relationship, and that the change in the "mutation point" is related to the metallization rate, which indicates that the electrode has a greater influence at this time.Changes in the T-S11 curve can also prove this.We consider the maximum point of S11 to be the maximum point of the thermal loss of electrode resistance.In terms of the influence of the metallization rate, electrode loading effects are also known to affect device performance [22], and the coverage of interdigital electrodes on piezoelectric thin films and their boundaries also affects SAW propagation.

Analysis after Multiple Temperature Tests
Observing the data after multiple tests, as shown in Figure 7(a2,b2,c2), it can be seen that the f-T curves have a better linear relationship than those in Figure 7(a1,b1,c1).Additionally, as the temperature increases, the frequency decreases.It can be seen from Equation ( 5) that in the case of stable performance of the piezoelectric film, the increase in temperature will lead to a decrease in the velocity on the AlN film, and because of Equation ( 2), when the wavelength is fixed, the frequency is positively correlated with the velocity, so the frequency is negatively correlated with the temperature.At the same time, the return loss (S11) increases with increasing temperature, which means that as the temperature increases, the performance of the device decreases.
where V R0 is the reference velocity, m 0 is the reference mass density, T 0 is the reference temperature, and k m , k s , and k τ are the corresponding correlation coefficients.Comparing (a2), (b2) and (c2) in Figure 7, it can be seen that the slopes of the f-T curves are different, that is, the sensitivity (∆f /∆T) is different, and the calculation shows that the sensitivity of Sample 1 is 14.77 KHz/K, the sensitivity of Sample 2 is 17.27 KHz/K, and the sensitivity of Sample 3 is 12.34 KHz/K.These are summarized in Table 5.The comparison shows that Sample 2 (when

Introduction
Temperature detection, whether in industrial production or daily life, has received great attention.However, in aerospace [1,2], geothermal research [3], turbine engines [4] and other fields, when monitoring super high temperatures, traditional temperature sensors generally require transmission lines and power supplies, such as thermocouples and optical fibers, which lead to cumbersome wiring, interference with working conditions and even accidents, so it is very difficult to implement temperature measurement for highspeed objects or objects in confined spaces [5].Therefore, passive wireless sensors have irreplaceable advantages.Although infrared temperature measurement, LC resonator In this paper, a surface acoustic wave (SAW) temperature sensor with a o/AlN/Si structure was prepared, and the high temperature characteristics of the sen-00 °C under different electrode metallization rates ( ղ ) were measured.It was found nt device mutation occurred in the first high-temperature test, and that the mutation ased with the increase in the electrode metallization rate (ղ).In the subsequent test, the e stable, the sensor's center frequency increased, the return loss (S11) decreased and the erit (Q) increased.After annealing the same sensors at 600 °C for 30 min, they could formance improvement in the first test, meaning that proper annealing can improve senance.In addition, the annealed SAW sensor was tested in the temperature range of 20hich met the requirement of a temperature range of 20-900 °C, its f-T curve was linear, f merit (Q) was 34.5 and the sensitivity was 46.6 KHz/K.SAW sensor; high temperature; electrode metallization rate; annealing ction erature detection, whether in industrial production or daily life, has received tion.However, in aerospace [1,2], geothermal research [3], turbine engines [4] fields, when monitoring super high temperatures, traditional temperature senally require transmission lines and power supplies, such as thermocouples and ers, which lead to cumbersome wiring, interference with working conditions ccidents, so it is very difficult to implement temperature measurement for highcts or objects in confined spaces [5].Therefore, passive wireless sensors have = 50%, the interdigital electrode is a uniform IDT, and that it has the greatest promotion effect on the propagation of the acoustic surface and the electromechanical coupling ability of the device.Carefully observing the slope of the f-T curves, we find that with 300 • C as a turning point, the slope of the f-T curve changes slightly below and above 300 • C. Additionally, it can be seen that the slope of the T-S11 curve also has 300 • C as a turning point; especially, the slope increases significantly after 300 • C, which means that the loss rate of the device becomes larger and the sensor performance decreases faster.

Comparison of the First Test and Multiple Tests
Comparing the data of T = 300 • C after the first test with the multiple tests performed, as shown in (a3), (b3) and (c3) in Figure 7, it is clear that the S11 curve of the multiple tests in (b3) and (c3) has a higher frequency and lower return loss.However, (a3) is anomalous, and it is easy to see that the resonant frequency in the first test is very different from that after multiple tests.As reported in the literature [23], when the velocity of the substrate is higher than that of the piezoelectric film, multiple modes of SAW can exist in the same SAW resonator at the same time.Additionally, because we designed the AlN seed layer, we think that the peak that appeared in the first test may not have been a Rayleigh mode excited by the AlN piezoelectric layer, but the wave of other modes excited by the AlN seed layer.Therefore, the frequency change between the first test and the multiple tests performed after is very large, which may have been due to the instability of the AlN piezoelectric layer film, or because of its special IDT structure (

Introduction
Temperature detection, whether in industrial production or daily life, has received great attention.However, in aerospace [1,2], geothermal research [3], turbine engines [4] and other fields, when monitoring super high temperatures, traditional temperature sensors generally require transmission lines and power supplies, such as thermocouples and optical fibers, which lead to cumbersome wiring, interference with working conditions and even accidents, so it is very difficult to implement temperature measurement for highspeed objects or objects in confined spaces [5].Therefore, passive wireless sensors have irreplaceable advantages.Although infrared temperature measurement, LC resonator temperature measurement and reflective antenna temperature measurement can achieve a passive wireless state, they are limited by factors such as poor anti-electromagnetic interference ability, large size and short wireless transmission distance.SAW stands for acoustic surface waves, which are waves that propagate on the surface or interface of elastomers, and the wave speed is much smaller than that of electromagnetic waves; = 25%), but more detailed content needs to be further investigated Additionally, the Q value of the sample that had undergone multiple tests was calculated by the figure of merit (Q) calculation shown in Equation (6).
where f r is center frequency, and ∆f, 3dB is the 3 dB bandwidth of the sensor.The figure of merit (Q) refers to the energy utilization of the device, which represents the relationship between stored energy and consumed energy, and can also be expressed by the resonant frequency and 3 dB bandwidth in Equation ( 5).It is known by the calculations that were performed that the Q value of Sample 1 is 34.8, the Q value of Sample 2 is 19.8 and the Q value of Sample 3 is 25.5.These are summarized in ract: In this paper, a surface acoustic wave (SAW) temperature sensor with a /AlN/Mo/AlN/Si structure was prepared, and the high temperature characteristics of the senat 20-600 °C under different electrode metallization rates ( ղ ) were measured.It was found frequent device mutation occurred in the first high-temperature test, and that the mutation t decreased with the increase in the electrode metallization rate (ղ).In the subsequent test, the became stable, the sensor's center frequency increased, the return loss (S11) decreased and the r of merit (Q) increased.After annealing the same sensors at 600 °C for 30 min, they could ve performance improvement in the first test, meaning that proper annealing can improve senerformance.In addition, the annealed SAW sensor was tested in the temperature range of 20-°C, which met the requirement of a temperature range of 20-900 °C, its f-T curve was linear, actor of merit (Q) was 34.5 and the sensitivity was 46.6 KHz/K.words: SAW sensor; high temperature; electrode metallization rate; annealing troduction Temperature detection, whether in industrial production or daily life, has received t attention.However, in aerospace [1,2], geothermal research [3], turbine engines [4] other fields, when monitoring super high temperatures, traditional temperature sengenerally require transmission lines and power supplies, such as thermocouples and cal fibers, which lead to cumbersome wiring, interference with working conditions even accidents, so it is very difficult to implement temperature measurement for highd objects or objects in confined spaces [5].Therefore, passive wireless sensors have laceable advantages.Although infrared temperature measurement, LC resonator perature measurement and reflective antenna temperature measurement can achieve ssive wireless state, they are limited by factors such as poor anti-electromagnetic inrence ability, large size and short wireless transmission distance.SAW stands for stic surface waves, which are waves that propagate on the surface or interface of elasers, and the wave speed is much smaller than that of electromagnetic waves; = 25%) has the largest figure of merit (Q).We think this has to do with its minimal metallization rate.
Comparing Figure 7(a1,b1,c1) with Figure 7(a2,b2,c2), the curve of the latter has higher linearity and stronger regularity, indicating that the temperature measurement performance of the SAW sensor was better and that the stability was higher after multiple tests.We believe that this is mainly due to internal stresses, poor crystallinity or defects in the film, which can be eliminated by annealing [24][25][26].

Comparison before and after Annealing
To validate our hypothesis, the above three samples were annealed to compare device performance before and after annealing.Since the previously tested samples were tested at temperatures of up to 600 • C, the samples were annealed at 600 • C for 30 min.The annealed samples were also subjected to high-temperature tests at 20-600 • C. Figure 8 shows the f-T relationship before and after annealing, and it can be found that the frequency of the annealed sample is significantly higher than that of the unannealed sample, and that its f-T relationship is also more stable and linear.In particular, the annealed samples performed very well in the first high-temperature test.This means that proper annealing can indeed improve the performance of the device.To validate our hypothesis, the above three samples were annealed to compare device performance before and after annealing.Since the previously tested samples were tested at temperatures of up to 600 °C, the samples were annealed at 600 °C for 30 min.The annealed samples were also subjected to high-temperature tests at 20-600 °C. Figure 8 shows the f-T relationship before and after annealing, and it can be found that the frequency of the annealed sample is significantly higher than that of the unannealed sample, and that its f-T relationship is also more stable and linear.In particular, the annealed samples performed very well in the first high-temperature test.This means that proper annealing can indeed improve the performance of the device.

High-Temperature Test of Annealed Sensor
Since the annealed sample exhibited relatively stable temperature sensitivity characteristics in the first test, we believed that it had great potential to perform well tests with a wider temperature range.Therefore, we carried out a high-temperature test at 20-1000 Since the annealed sample exhibited relatively stable temperature sensitivity characteristics in the first test, we believed that it had great potential to perform well tests with a wider temperature range.Therefore, we carried out a high-temperature test at 20-1000 • C on the sensor annealed for 30 min at 600 • C to explore the maximum temperature measurement range of a Pt/Ti/AlN/Mo/AlN/Si-structured SAW temperature sensor.Using the vector network analyzer to obtain a stable S11 curve, Figure 9 shows the S11 curve (a) and f-T relationship (b) of Sample 1, from which it can be seen that the device has a significant peak at 20-900 • C.However, the peak disappears at 1000 • C, indicating device failure.It can be seen that the sample can perform temperature measurement from 20 • C to 900 • C; its figure of merit (Q) is calculated to be 34.5, and the sensitivity is calculated to be 46.6 KHz/K.

Conclusions
In conclusion, after XRD and SEM characterization, it was found that the AlN piezoelectric layer grown by the AlN/Mo/AlN/Si structure had a good (002) orientation.Through high-temperature RF test experiments, it was found that the frequency and temperature curves of devices prepared with a Pt/Ti/AlN/Mo/AlN/Si structure produce mutation points due to the unstable properties of films and electrode deformation before annealing.The value of the mutation point is related to the size of the electrode.After annealing at 600 °C for 30 min, the center frequency of the device increased and S11 decreased.The annealed device had a good linear f-T curve under the high-temperature test conducted at temperatures from 20 °C to 900 °C, but at the same time, the device electrode was partially damaged at high temperatures, and the AlN was oxidized and split the contact surface due to its mismatch with Mo's coefficient of thermal expansion.The replacement of the bottom electrode material and the addition of a protective layer to the upper electrode are considered viable steps to improve the performance of the device.Figure 10a shows the Pt electrode that failed after the 20-1000 • C test, which has large particles and cavities caused by Pt recrystallization and agglomeration at high temperatures [27].Figure 10b shows the cross-sectional view of the device, and that the multilayer film structure of AlN/Mo/AlN/Si underwent oxidative deformation at a high temperature.The morphology of the AlN layer changed greatly, as reported in the literature [28], and the AlN exposed to air began to oxidize at 800-900 • C, the rate of which abruptly increased at 1000 • C.Moreover, since the coefficient of thermal expansion of AlN (4.5 × 10 −6 /K) is different from that of Mo (5.35 × 10 −6 /K), this mismatch played a driving role, so that the contact surface of the two had a large split layer after high-temperature oxidation and cooling.This proves that the sensor's structure fails at high temperatures and also explains why it has no peak at 1000 • C.

Conclusions
In conclusion, after XRD and SEM characterization, it was found that the AlN piezoelectric layer grown by the AlN/Mo/AlN/Si structure had a good (002) orientation.Through high-temperature RF test experiments, it was found that the frequency and temperature curves of devices prepared with a Pt/Ti/AlN/Mo/AlN/Si structure produce mutation points due to the unstable properties of films and electrode deformation before annealing.The value of the mutation point is related to the size of the electrode.After annealing at 600 °C for 30 min, the center frequency of the device increased and S11 decreased.The annealed device had a good linear f-T curve under the high-temperature test

Conclusions
In conclusion, after XRD and SEM characterization, it was found that the AlN piezoelectric layer grown by the AlN/Mo/AlN/Si structure had a good (002) orientation.Through high-temperature RF test experiments, it was found that the frequency and temperature curves of devices prepared with a Pt/Ti/AlN/Mo/AlN/Si structure produce and conommons Ate (https://creaes/by/4.0/).

Figure 4 .
Figure 4. (a) Schematic diagram of high-temperature test; (b) physical diagram of high-temperature test.

Figure 5 .
Figure 5. (a) XRD curve of AlN thin film; (b) SEM results of AlN thin film.

Figure 5 .
Figure 5. (a) XRD curve of AlN thin film; (b) SEM results of AlN thin film.

Figure 5 .
Figure 5. (a) XRD curve of AlN thin film; (b) SEM results of AlN thin film.

Figure 9 .
Figure 9. High−temperature test curve of a temperature range of 20−1000 • C: (a) S11 curve and (b) f−T curve.

Figure 10 .
Figure 10.(a) Pt electrode that failed after a 20−1000 • C test; (b) cross-sectional view of a failed sensor after a 20−1000 • C test.

Table 1 .
Material constant and temperature coefficient of AlN.

Table 1 .
Material constant and temperature coefficient of AlN.