Diffusion Model of Parallel Plate Crack Grouting Based on Foaming Expansion Characteristics of Polymer Slurry

Polymers as a new chemical grouting material have been widely used in fractured rock mass; however, the understanding of polymer diffusion characteristics still needs to be further improved. In order to study the diffusion mechanism of foamed polymer slurry in rock fissures, the radial diffusion model of polymer single crack grouting is derived in consideration of the factors such as grouting volume, crack width and expansion rate. The influence of different factors on slurry diffusion radius, diffusion pressure and flow rate is analyzed, The diffusion model is verified by finite element numerical simulation. The findings show that (1) The results of slurry diffusion radius, pressure and velocity distribution at different times under different working conditions in the present model are in good agreement with the analytical solution; (2) The diffusion pressure is directly proportional to the grouting volume and expansion multiple, and inversely proportional to the crack width. In addition, diffusion pressure decreases with the increase of diffusion distance, and the pressure at the corresponding distance increases slowly with time, and finally tends to be stable; (3) For the same section, the radial velocity decreases slowly with the increase of time; for different sections, the flow velocity increases sharply with the increase of the distance between the section and the central axis of the grouting hole.


Introduction
In underground construction, grouting is one of the effective technical means to improve rock mechanical properties and block groundwater [1][2][3][4][5][6]. Grouting refers to injecting the slurry with cementitious capacity into the cracks, voids or cavities in the rock layer (or soil layer) through grouting drilling holes or grouting pipes, which can drive away the water and air in the cracks, voids or cavities, cement the original loose soil particles or cracks into a whole, and form a "stone body" with new structure, high strength and strong waterproof and impermeability, so as to improve the performance of the rock (soil) layer [7]. In recent years, many new grouting materials and equipment have been come into use, which greatly improves the effectiveness of grouting plugging. With the advantages of safety and environmental protection, fast response, high expansion rate, impermeability and durability, polymer materials have become grouting materials with excellent comprehensive performance [8], and are widely used in foundation reinforcement, dam seepage prevention, road maintenance, etc.
The diffusion mechanism of slurry in rock and soil fractures has always been the focus of research. Many scholars have studied the migration law of slurry in fractured rock mass. Generally, the fractured rock mass is simplified as a parallel plate model [9][10][11][12]. According to different slurry constitutive equations, the diffusion of slurry in rock fractures is studied by the analytical method, and the slurry flow and pressure distribution equations are established to explore the flow law of slurry in fractured rock mass. Some scholars regard the slurry as Newtonian fluid and deduce the fracture grouting diffusion model. For instance, Zhang et al. [13] established a two-dimensional slurry flow model in fractures considering fracture roughness and groundwater viscous resistance, and Li et al. [14] deduced an ideal self-expanding slurry single fracture diffusion model; Furthermore, other scholars regard the slurry as Bingham fluid and deduce the crack grouting diffusion model. For example, Gustafson et al. [15] proposed the analytical model for calculating the penetration length of silica sol grouting. Liu et al. [16] proposed the grouting numerical model of water-rich broken sandstone for ordinary portland cement 42.5 (PO. 42.5), aluminum sulfate cement 42.5 (sac. 42.5) and self-developed cement-based composite grouting material (CGM). And a crack grouting diffusion model considering the time-varying viscosity of cement slurry has been proposed [17].
In the diffusion of one-dimensional flow model, Amadei and Savage [18] proposed a one-dimensional flow model of Bingham slurry in the channel between parallel walls, and analyzed the influence of pressure gradients on slurry flow characteristics; Luo et al. [19] deduced the flow equation of Bingham slurry in one-dimensional inclined single fracture, and analyzed the effects of fracture inclination, viscosity and other factors on the velocity of slurry. In the two-dimensional radial diffusion model, Tani et al. [9] studied the radial diffusion law of cement slurry diffusing in the cracks between parallel plates; while Zhan et al. [20,21] established a hydrodynamic grouting diffusion model of single fracture and analyzed the influence of water flow velocity on the slurry diffusion range. Zhang et al. [22] proposed a theoretical model of horizontal fracture grouting diffusion considering the temporal and spatial variation of slurry viscosity under the condition of a constant grouting rate.
In general, great progress has been made in the research on crack grouting mechanism at home and abroad; however, the existing models take constant density slurry such as sodium silicate, cement slurry and ordinary chemical slurry as the objects, and there is no research on the crack grouting diffusion model of foamed polymer slurry. Two component foamed polyurethane generally has faster reaction speeds and larger expansion rates. According to the added foaming dose, it can expand 10-30 times in 6-30 s [8]. Due to the expansibility of polymer slurry and the void structure characteristics of injected medium, the diffusion characteristics of polymers are more complex, which also brings great difficulties to the selection of polymer grouting parameters in engineering practice [23].
In this paper, based on the foaming expansion characteristics of polymer slurry and the theory of viscous hydrodynamics, the radial diffusion model of foaming polymer in single crack considering the self-expansion characteristics of polymer is theoretically deduced. In addition, the numerical simulation of grouting diffusion in parallel plate cracks is established by using finite element software (Comsol Multiphysics), which verifies the accuracy of the present analysis model. The diffusion model can fully consider the influence of grouting volume, crack opening, radial distance, time, expansion ratio and other factors on diffusion characteristics of slurry, and has a certain reference value for the theoretical research of foam polymer slurry crack grouting.

Density Model
Here, three kinds of polymer grouting materials (10 times expansion rate, 20 times expansion rate and 30 times expansion rate) are taken as the research object. First, the exfactory expansion rate of the polymer is calibrated and verified. A self-made reaction vessel for measuring the expansion rate of polymers was made according to the requirement of the test (Figure 1), which is mainly composed of a plexiglass cylinder with a bottom. Meanwhile, in order to observe the change of expansion volume, a scale is pasted on the reaction cylinder, and a high-definition camera(HD) is used to capture the expansion rise height of the polymer at different times. The two-component polymer grouting materials are mixed according to the requirements of the same quality and poured into the reaction vessel for reaction expansion at room temperature.
Mathematics 2021, 9, 2907 3 of 18 before and after the reaction. It can be seen from the figure that the three polymer grouting materials have expanded to a certain extent after reaction. In particular, it can be clearly seen from Figure 2 that the three polymers have expanded from the original height of 2.5 cm to 11.5 cm, 21 cm and 31.5 cm, respectively. In addition, the heights of consolidated polymers with 20 and 30 times the expansion ratio are 1.83 and 2.74 times, respectively. It can be proved that the ex-factory expansion ratio of the three polymers is reliable within the allowable range of test error.  The density integrity relationship is obtained by the nonlinear fitting of the experimental results.  Figures 1 and 2, respectively, show the morphology photos of the consolidated body of three polymers in the reaction cylinder and the comparison diagram of slurry height before and after the reaction. It can be seen from the figure that the three polymer grouting materials have expanded to a certain extent after reaction. In particular, it can be clearly seen from Figure 2 that the three polymers have expanded from the original height of 2.5 cm to 11.5 cm, 21 cm and 31.5 cm, respectively. In addition, the heights of consolidated polymers with 20 and 30 times the expansion ratio are 1.83 and 2.74 times, respectively. It can be proved that the ex-factory expansion ratio of the three polymers is reliable within the allowable range of test error.
Mathematics 2021, 9, 2907 3 of 19 are mixed according to the requirements of the same quality and poured into the reaction vessel for reaction expansion at room temperature. Figures 1 and 2, respectively, show the morphology photos of the consolidated body of three polymers in the reaction cylinder and the comparison diagram of slurry height before and after the reaction. It can be seen from the figure that the three polymer grouting materials have expanded to a certain extent after reaction. In particular, it can be clearly seen from Figure 2 that the three polymers have expanded from the original height of 2.5 cm to 11.5 cm, 21 cm and 31.5 cm, respectively. In addition, the heights of consolidated polymers with 20 and 30 times the expansion ratio are 1.83 and 2.74 times, respectively. It can be proved that the ex-factory expansion ratio of the three polymers is reliable within the allowable range of test error.  The density integrity relationship is obtained by the nonlinear fitting of the experimental results.  The density integrity relationship is obtained by the nonlinear fitting of the experimental results.

Basic Hypothesis
Based on the existing derivation method of fracture diffusion model, the following assumptions were made [24,25]: (1) the slurry is a homogeneous isotropic fluid; (2) There is no slip boundary at the upper and lower surfaces of the crack, that is, the slurry velocity at the contact with the wall is 0; (3) The slurry is in a laminar flow during the diffusion process; (4) The slurry is a Newtonian fluid, and its viscosity and flow pattern remain unchanged in the grouting process; (5) The fracture wall is rigid, and there is no deformation under the pressure of the slurry; (6) The groutability of the slurry is good, and there is no blockage, and the movement of the slurry in the fracture model is a full plane radiation; (7) The crack wall has no adsorption effect on the slurry, and there is no precipitation during the movement of the slurry.

Diffusion Model Derived
The schematic diagram of single crack grouting [14] is shown in Figure 3, and its opening of crack is h, and the radius of grouting hole is R 0 . It is assumed that the polymer slurry will flow radially around the grouting hole between the upper and lower crack surfaces; and ignoring the grouting pressure in the grouting hole, the slurry will flow in the crack completely by virtue of the volume expansion mechanism.

Basic Hypothesis
Based on the existing derivation method of fracture diffusion model, the following assumptions were made [24,25]: (1) the slurry is a homogeneous isotropic fluid; (2) There is no slip boundary at the upper and lower surfaces of the crack, that is, the slurry velocity at the contact with the wall is 0; (3) The slurry is in a laminar flow during the diffusion process; (4) The slurry is a Newtonian fluid, and its viscosity and flow pattern remain unchanged in the grouting process; (5) The fracture wall is rigid, and there is no deformation under the pressure of the slurry; (6) The groutability of the slurry is good, and there is no blockage, and the movement of the slurry in the fracture model is a full plane radiation; (7) The crack wall has no adsorption effect on the slurry, and there is no precipitation during the movement of the slurry.

Diffusion Model Derived
The schematic diagram of single crack grouting [14] is shown in Figure 3, and its opening of crack is h, and the radius of grouting hole is R0. It is assumed that the polymer slurry will flow radially around the grouting hole between the upper and lower crack surfaces; and ignoring the grouting pressure in the grouting hole, the slurry will flow in the crack completely by virtue of the volume expansion mechanism. Taking any fluid unit from the basin (see Figure 4), the external force on the fluid element are a normal stress p and the shear stressτ, and there is no shear resistance between the radial planes perpendicular to the crack plane. If the influence of velocity change is not considered, the sum of the respective force along the direction of the center radial axial axis of the single element should be equal to zero [26].
prΔθΔz-p + dp dr Δr (r + Δr)ΔθΔr + p + dp dr High-order trace elements are omitted, it can be expressed by According to Newton's law of frictional resistance, the shear force can be expressed by Taking any fluid unit from the basin (see Figure 4), the external force on the fluid element are a normal stress p and the shear stressτ, and there is no shear resistance between the radial planes perpendicular to the crack plane. If the influence of velocity change is not considered, the sum of the respective force along the direction of the center radial axial axis of the single element should be equal to zero [26]. pr∆θ∆z− p + dp dr ∆r (r + ∆r)∆θ∆r+ p + dp dr  Integrating from Equations (3) and (4): High-order trace elements are omitted, it can be expressed by dp According to Newton's law of frictional resistance, the shear force can be expressed by Integrating from Equations (3) and (4): By substituting the boundary condition ∂u r ∂z z=0 = 0 into the above formula, the following is obtained: Then we integrate Z and substitute the boundary conditions ∂u r ∂z z=0 = 0 into the above formula: Substituting the boundary conditions u r | z=± h 2 = 0 into the above formula, it is rewritten as [17]: where: u r is slurry viscosity. Then the average flow velocity on the cross section of slurry crack is: Let the diffusion radius of slurry at time t be Rt. For any slurry within the range of R ≤ R t , let the increment of filling range after volume expansion within t be R. Due to the low of conservation of mass, it can be expressed by [14]: where: ρ(t) = Ae −Bt + C After sorting: Further, it can be obtained that: when ∆t → 0 , the first two terms are Substituting Equation (13) into Equation (12), it can be obtained, when After sorting: when ∆t → 0 , ∆r → 0 , Equation (16) can be rewritten into differential form: If the radial average velocity is equal to the change rate of radius with time, we have Combining Equations (9) and (18), we have dp Substituting Equation (19) into Equation (8), we have Integrating equation (19) with R, we have Assuming that the radius of the initially injected slurry is R 0 , since the total mass of the slurry remains unchanged during the slurry diffusion process, it can be expressed at the time t, The diffusion radius of slurry at time t can be written as Substituting Equation (23) into Equation (18), it can be obtained that the average velocity at the interface between slurry and air at time t, when t = 0 s, the slurry pressure is the same as the atmospheric pressure P 0 at the interface between slurry and air. According to Formula (21), we have where, C = p 0 + Substituting it into Equation (21), we have where 0 ≤ r ≤ R t .

Governing Equations
In order to verify the correctness of the numerical method, the numerical simulation of polymer slurry parallel plate crack grouting diffusion was carried out. Under the assumption of ideal mixing and rapid reaction, the polymer is regarded as a continuum with the characteristics of compressible Newtonian fluid. The growth of bubbles causes the dependence of polymer density on time. The diffusion and flow of polymers in the crack follow the mass conservation equation and momentum conservation equation. Ignoring the tension of the surface, the diffusion velocity and pressure can be expressed as: where ρ is the mixing density; U is the velocity vector; t is the time; P is the pressure; η is shear viscosity; G is the acceleration of gravity.

Level Set Method
The level set method tracks the interface position by solving the transport equation of the level set function, that is, by tracking the level set function ϕ to determine the interface of fluid. For convective transport, the velocity vector can be calculated by the Navier Stokes equation.
where γ and ε is a reinitialization parameter. In this paper ε is taken as the maximum element size in the domain. γ is equal to 1. Within a given value range of level set function, the fluid characteristics transition smoothly from liquid to gas. The level set function changes between 0 and 1, and it is expressed as 0 or 1 in the two fluids. Specifically, it is 0 in the liquid phase and 1 in the gas phase. On the interface between liquid and gas, the corresponding level set function value ϕ = 0.5. The density can be expressed by the level set function The dynamic viscosity can be expressed by where ρ 1 = density of polymer; ρ 2 = density of air; µ 1 = viscosity of polymer; and µ 2 = viscosity of air.

Numerical Realization (Boundary and Initial Conditions)
The self-expansion of polymer in a single crack with a radius of 1.3 m and a crack opening of 6mm is analyzed using a parallel plate model, as shown in Figure 5. It is assumed that the static pressure grouting stage has been completed, so some parts of the crack at t = 0 s will initially be filled with unexpanded polymer grouting. Taking the circle with radius r 0 as the initial shape of diffusion and assuming that the static pressure grouting stage has been completed, the grouting amount is the quality required to diffuse to the corresponding radius r 0 , and R 0 is calculated by where ρ1 = density of polymer; ρ2 = density of air; μ1 = viscosity of polymer; and μ2 = viscosity of air.

Numerical Realization (Boundary and Initial Conditions)
The self-expansion of polymer in a single crack with a radius of 1.3 m and a crack opening of 6mm is analyzed using a parallel plate model, as shown in Figure 5. It is assumed that the static pressure grouting stage has been completed, so some parts of the crack at t = 0 s will initially be filled with unexpanded polymer grouting. Taking the circle with radius r0 as the initial shape of diffusion and assuming that the static pressure grouting stage has been completed, the grouting amount is the quality required to diffuse to the corresponding radius r0, and R0 is calculated by In this paper, 3 types of polymer material are selected, and the grouting amount is 125 g, 250 g and 370 g. The initial density of slurry ρ is 1172.86 kg/m 3 . The initial radius R0 calculated by Formula (32) is 0.11 m, 0.15 m and 0.18 m, respectively.
The UDFs function (user-defined functions) is used to edit the user-defined function of the attribute change of slurry fluid, so as to realize the real-time adjustment of density parameters in the process of slurry expansion.

Numerical Verification of Diffusion Model
The reliability of the grouting model is verified by comparing the numerical solution with the analytical solution. Figure 6 shows the theoretical curve and simulation curve of diffusion radius with time under different grouting quantities. It can be seen from the figure that the curve obtained by the present model is consistent with that obtained by numerical simulation., and the diffusion range of slurry gradually increases with time and tends to be stable at 30 s. In addition, it is observed that the time-consuming of slurry expansion and the diffusion stage is not related to the grouting quantity. When the grouting quantity is 125 g, 250 g and 170 g, the slurry stops diffusion at about 30 s. At this time, the slurry stops expanding and reaches the maximum diffusion range, which is the effective diffusion area of the slurry. It can also be seen from the figure that the effective diffusion area of the slurry is directly proportional to the grouting volume. Figure 7 shows the simulation results of the change of slurry volume fraction with time. It can be seen from the figure that the slurry diffusion form of single crack grouting In this paper, 3 types of polymer material are selected, and the grouting amount is 125 g, 250 g and 370 g. The initial density of slurry ρ 0 is 1172.86 kg/m 3 . The initial radius R 0 calculated by Formula (32) is 0.11 m, 0.15 m and 0.18 m, respectively.
The UDFs function (user-defined functions) is used to edit the user-defined function of the attribute change of slurry fluid, so as to realize the real-time adjustment of density parameters in the process of slurry expansion.

Numerical Verification of Diffusion Model
The reliability of the grouting model is verified by comparing the numerical solution with the analytical solution. Figure 6 shows the theoretical curve and simulation curve of diffusion radius with time under different grouting quantities. It can be seen from the figure that the curve obtained by the present model is consistent with that obtained by Mathematics 2021, 9, 2907 9 of 18 numerical simulation., and the diffusion range of slurry gradually increases with time and tends to be stable at 30 s. In addition, it is observed that the time-consuming of slurry expansion and the diffusion stage is not related to the grouting quantity. When the grouting quantity is 125 g, 250 g and 170 g, the slurry stops diffusion at about 30 s. At this time, the slurry stops expanding and reaches the maximum diffusion range, which is the effective diffusion area of the slurry. It can also be seen from the figure that the effective diffusion area of the slurry is directly proportional to the grouting volume. is circular, and gradually diffuses outward in concentric circular form with time, finally reaching the effective diffusion area of slurry, which is consistent with the diffusion form assumed by the present theoretical model.   Figure 7 shows the simulation results of the change of slurry volume fraction with time. It can be seen from the figure that the slurry diffusion form of single crack grouting is circular, and gradually diffuses outward in concentric circular form with time, finally reaching the effective diffusion area of slurry, which is consistent with the diffusion form assumed by the present theoretical model. Table 1 shows the simulation results and analytical results of the pressure distribution with time at 2 cm away from the grouting hole when the grouting amount is 250 g. It can be seen from the Table 1 that the diffusion pressure gradually increases with time and finally tends to be stable. The maximum relative error between the numerical solution and the analytical solution is 0.9%, and the average relative error is 0.28%.    Table 2 shows the simulation results and analytical results of pressure radial distribution with distance when the grouting amount is 250 g and the time is 30 s. It can be seen in Table 2 that the diffusion pressure gradually decreases with the increase of radial distance. The maximum relative error between the numerical solution and the analytical solution is 1.4%, and the average relative error is 1%. It can be seen that the theoretical solutions in Tables 1 and 2 are in good agreement with the numerical solutions. Table 2. Simulation results and analytical results of radial pressure distribution at different positions.

Time t (s) Position r (cm) Diffusion Pressure (KPa) Relative Error Numerical Solution
Theoretical Solution  Figures 8 and 9 show the temporal and spatial distribution characteristics of the slurry pressure field. Figure 8 shows the variation curve of pressure with diffusion distance at different times. It can be seen from the figure that the farther away from the grouting hole, the smaller the diffusion pressure. Figure 9 shows the variation curve of pressure with time at different distances. It can be seen from the figure that the pressure at different positions increases slowly with time and finally ends up being stable, and the pressure values at different positions are basically the same.   Figure 10 shows the variation curve of pressure with time under different grouting quantities at the radius r = 2 cm. It can be seen from the figure that the pressure increases slowly with time, and finally the pressure tends to be stable. Figure 11 shows the relationship curve between the maximum pressure and the grouting amount. It can be seen from Figures 10 and 11 that the diffusion pressure is directly proportional to the grouting amount. Figure 12 shows the change of pressure with time under different crack opening, and Figure 13 shows the relationship curve between the maximum pressure and crack opening. It can be seen from Figures 12 and 13 that the diffusion pressure is inversely proportional to the grouting volume, and the diffusion pressure is very sensitive to the change in the crack opening. When the crack decreases from 4 mm to 2 mm, the pressure increases rapidly, the crack opening decreases from 8 mm to 2 mm, and the maximum pressure value increases by a factor of 20. Figure 14 shows the change curve of pressure with time under different expansion ratios, and Figure 15 shows the relationship curve   Figure 10 shows the variation curve of pressure with time under different grouting quantities at the radius r = 2 cm. It can be seen from the figure that the pressure increases slowly with time, and finally the pressure tends to be stable. Figure 11 shows the relationship curve between the maximum pressure and the grouting amount. It can be seen from Figures 10 and 11 that the diffusion pressure is directly proportional to the grouting amount. Figure 12 shows the change of pressure with time under different crack opening, and Figure 13 shows the relationship curve between the maximum pressure and crack opening. It can be seen from Figures 12 and 13 that the diffusion pressure is inversely proportional to the grouting volume, and the diffusion pressure is very sensitive to the change in the crack opening. When the crack decreases from 4 mm to 2 mm, the pressure increases rapidly, the crack opening decreases from 8 mm to 2 mm, and the maximum pressure value increases by a factor of 20. Figure 14 shows the change curve of pressure with time under different expansion ratios, and Figure 15 shows the relationship curve   Figure 10 shows the variation curve of pressure with time under different grouting quantities at the radius r = 2 cm. It can be seen from the figure that the pressure increases slowly with time, and finally the pressure tends to be stable. Figure 11 shows the relationship curve between the maximum pressure and the grouting amount. It can be seen from Figures 10 and 11 that the diffusion pressure is directly proportional to the grouting amount. Figure 12 shows the change of pressure with time under different crack opening, and Figure 13 shows the relationship curve between the maximum pressure and crack opening. It can be seen from Figures 12 and 13 that the diffusion pressure is inversely proportional to the grouting volume, and the diffusion pressure is very sensitive to the change in the crack opening. When the crack decreases from 4 mm to 2 mm, the pressure increases rapidly, the crack opening decreases from 8 mm to 2 mm, and the maximum pressure value increases by a factor of 20. Figure 14 shows the change curve of pressure with time under different expansion ratios, and Figure 15 shows the relationship curve between the maximum pressure and expansion ratio. It can be seen from Figures 14 and 15 that the diffusion pressure is directly proportional to the grouting amount. In general, the grouting volume, the crack opening and the expansion ratio are three key factors affecting the slurry pressure field.

Analysis of Slurry Pressure Field
Mathematics 2021, 9, 2907 12 of 19 between the maximum pressure and expansion ratio. It can be seen from Figures 14 and  15 that the diffusion pressure is directly proportional to the grouting amount. In general, the grouting volume, the crack opening and the expansion ratio are three key factors affecting the slurry pressure field.  between the maximum pressure and expansion ratio. It can be seen from Figures 14 and  15 that the diffusion pressure is directly proportional to the grouting amount. In general, the grouting volume, the crack opening and the expansion ratio are three key factors affecting the slurry pressure field.  Grouting amount Q (g) Figure 11. Relation curve between maximum pressure and grouting volume. Table 3 shows the flow velocity values at different positions on the fracture section when t = 20 s, which can be described as an intuitive three-dimensional distribution of flow velocity, as shown in Figure 16. It can be seen from Table 3 and Figure 16 that the farther the fracture section is from the grouting hole and the fracture wall, the greater the diffusion pressure is. Figures 17 and 18 show the velocity on temporal and spatial distribution characteristics of slurry. Figure 17 shows the velocity variation of slurry with radial distance at different times. It can be seen from the Figure 17 that the slurry velocity increases along the radial direction, and the velocity reaches the maximum at the interface between slurry and air. Figure 18 shows the velocity variation curve of slurry along the z-axis direction at different times. It can be seen from Figure 18 that the slurry velocity presents a parabolic distribution in the z-axis direction, and the velocity reaches the maximum at the midpoint of the fracture (z = 0) and reaches the minimum at the fracture wall, and the velocity is zero. It can also be seen from Figures 17 and 18 that the slurry flow rate gradually decreases with time and finally becomes zero. Figures 19 and 20 are the time-varying curves of flow velocity at the interface between slurry and air under different grouting amounts and expansion ratios. It can be seen from Figures 19 and 20 that the greater the grouting amount and expansion ratio, the greater the interface flow velocity; the grouting amount and expansion ratio are the key factors affecting the flow velocity.    Maximun Pressure(KPa)

Analysis of Slurry Diffusion Flow Field
Crack width h (mm)      Table 3 shows the flow velocity values at different positions on the fracture section when t = 20 s, which can be described as an intuitive three-dimensional distribution of flow velocity, as shown in Figure 16. It can be seen from Table 3 and Figure 16 that the farther the fracture section is from the grouting hole and the fracture wall, the greater the diffusion pressure is. Figures 17 and 18 show the velocity on temporal and spatial distribution characteristics of slurry. Figure 17 shows the velocity variation of slurry with radial distance at different times. It can be seen from the Figure 17 that the slurry velocity increases along the radial direction, and the velocity reaches the maximum at the interface between slurry and air. Figure 18 shows the velocity variation curve of slurry along the zaxis direction at different times. It can be seen from Figure 18 that the slurry velocity presents a parabolic distribution in the z-axis direction, and the velocity reaches the maximum at the midpoint of the fracture (z = 0) and reaches the minimum at the fracture wall, and the velocity is zero. It can also be seen from Figures 17 and 18 that the slurry flow rate gradually decreases with time and finally becomes zero. Figures 19 and 20 are the time-   Table 3 shows the flow velocity values at different positions on the fracture section when t = 20 s, which can be described as an intuitive three-dimensional distribution of flow velocity, as shown in Figure 16. It can be seen from Table 3 and Figure 16 that the farther the fracture section is from the grouting hole and the fracture wall, the greater the diffusion pressure is. Figures 17 and 18 show the velocity on temporal and spatial distribution characteristics of slurry. Figure 17 shows the velocity variation of slurry with radial distance at different times. It can be seen from the Figure 17 that the slurry velocity increases along the radial direction, and the velocity reaches the maximum at the interface between slurry and air. Figure 18 shows the velocity variation curve of slurry along the zaxis direction at different times. It can be seen from Figure 18 that the slurry velocity presents a parabolic distribution in the z-axis direction, and the velocity reaches the maximum at the midpoint of the fracture (z = 0) and reaches the minimum at the fracture wall, and the velocity is zero. It can also be seen from Figures 17 and 18 that the slurry flow rate gradually decreases with time and finally becomes zero. Figures 19 and 20 are the time-

Conclusions
(1) In this paper, the effects of grouting volume, crack opening, radial distance, time, expansion ratio and other factors were fully considered. The radial diffusion model of polymer grouting in a single crack was theoretically deduced, and the theoretical model was verified by the numerical simulation of slurry in parallel plate cracks. The variation laws of slurry diffusion radius and pressure at different times are basically consistent with

Conclusions
(1) In this paper, the effects of grouting volume, crack opening, radial distance, time, expansion ratio and other factors were fully considered. The radial diffusion model of polymer grouting in a single crack was theoretically deduced, and the theoretical model

Conclusions
(1) In this paper, the effects of grouting volume, crack opening, radial distance, time, expansion ratio and other factors were fully considered. The radial diffusion model of polymer grouting in a single crack was theoretically deduced, and the theoretical model was verified by the numerical simulation of slurry in parallel plate cracks. The variation laws of slurry diffusion radius and pressure at different times are basically consistent with the analytical solution, (2) The amount of grouting, the expansion ratio and the crack opening have a great influence on the diffusion law of polymer crack grouting. The diffusion pressure is directly proportional to the grouting amount and expansion ratio, and inversely proportional to the crack opening. In addition, the greater the grouting amount and expansion ratio, the greater the interfacial velocity.
(3) The diffusion pressure is directly proportional to the grouting volume and expansion multiple, and inversely proportional to the crack width. In addition, diffusion pressure decreases with the increase of diffusion distance, and the pressure at the corresponding distance increases slowly with time, eventually reaching stability.