The Influence of New and Artificial Aged Microplastic and Leachates on the Germination of Lepidium sativum L.

With the increase in environmental monitoring and assessing, we are gaining insight into the extent of microplastic pollution in our environment. The threat posed by microplastics to biota could come, e.g., from leached substances. As some plastic materials have been decaying in nature for extended periods already, the toxic effects of leaching compounds need to be investigated. It is furthermore essential to understand the adverse effects of new plastic and how these effects differ from the effects elicited by old plastic material. Therefore, in the present study, the effects of exposure to leachates from new and artificial aged polycarbonate as well as new and aged polycarbonate granules on various germination parameters of Lepidium sativum were studied. Germination, root, and shoot length, as well as the calculated germination rate index as a measure for germination speed, was negatively influenced in substrate-free and substrate containing exposures. From an ecological and agricultural point of view, this implies possible yield losses with less germinating seeds, slower plant germination speed, and smaller seedlings in general.


Introduction
Most human activities nowadays are based on or influenced by plastics and plastic products. Plastic is essential in nearly all aspects of human life. Due to intensive production, around 8.3 million metric tons of virgin plastic were produced in 2015 [1]. Due to its ubiquitous use, low cost, and the single-use throwaway culture, plastic pollution has become a severe environmental problem [2]. Plastic debris as a source of waste and chemical pollution is detected not only in oceans, forming huge swirling patches in areas, but also soil, sediment, freshwater bodies, and even human stool [3,4].
The threats posed by microplastics (MP) in nature need to be investigated. However, a standardized definition of what can be defined as MPs in terms of size classification is still under debate, and numerous Plants 2020, 9,339 3 of 18 constitutes three principal processes: the imbibition, the activation, and the intra-seminal growth, leading to the embryo protrusion [21]. During germination, the plant is most vulnerable to dissolved toxic substances because the seeds imbibe plenty of water from its surroundings through pores in the seed capsule [22]. Therefore, the effects, primarily on germination, was considered as leached substances in water could affect the plants (leachates) or MP particles could alter soil properties affecting water availability (granules).

Germination in Substrate-Free System with Leachates
Using germination as a test parameter in substrate-free exposures, the leachate solution from the new PC material (new-PC-leachate), in the two dilutions 1:10 and 1:1, as well as non-diluted, significantly inhibited the germination of L. sativum compared to the control (p < 0.05) ( Figure 1A). After seven days of exposure, the germination was inhibited by 20% in the 1:10 diluted leachate, 54% in the 1:1 diluted leachate, and by 77% using the non-diluted leachate compared to untreated controls. A strong inhibitory effect compared to untreated controls was seen using the artificially aged PC leachate (aged-PC-leachate) (p < 0.05), for which the germination was inhibited by 6% using 1:10 diluted leachate, 13% using 1:1 diluted leachate, and 18% using the non-diluted leachate. ( Figure 1B). Comparing the inhibitory effect on germination in the presence of the new-PC-leachate with the aged-PC-leachate, it is evident that ageing decreased the ecotoxicity of the plastic material. For example, the non-diluted aged-PC-leachate inhibited the germination less than the 1:10 diluted new-PC-leachate. Exposure of the seeds to three different concentrations of BPA (10,50, and 100 mg/L), a primary component of PC and also a known endocrine-disrupting chemical [23], exhibited inhibitory effects on the germination after seven days. The inhibition with exposure to 10 mg/L BPA was 13%, using 50 mg/L BPA 17% inhibition, and using 100 mg/L 33% inhibition was observed ( Figure 1C). The degree of inhibition on the germination by BPA falls between the results of the new-PC-leachate and the aged-PC-leachate, suggesting that the adverse effects resulting from the new-PC-leachate are the sum of numerous harmful substances leaching from the PC. Dogan et al. [24] reported that BPA at concentrations of 10 mg/L and 50 mg/L did not cause inhibited germination of chickpea (Cicer arietinum L. cv. Ispanyol); however, a BPA concentration of 50 mg/L was able to reduce the germination of Triticum aestivum L. cv. Sagittario significantly by 43% in a substrate-free system [25]. It is possible that like T. aestivum, L. sativum is more sensitive to BPA exposure than C. arietinum. Exposure of Lens culinaris seeds to 10, 50, and 100 mg/L BPA in a substrate-free system also caused inhibited germination [26]. These observed discrepancies illustrate that different plants have different sensitivities to the effects of MP, which is a theory previously suggested by Rillig et al. [27].

Germination in a Substrate-System with Exposure to Leachates
The same experimental set-up detailed above was repeated in a substrate. The new-PC-leachate in different dilutions (1:10, 1:1, and non-diluted) exhibit a lower, but still significant (p < 0.05) inhibition of germination. After seven days, using the 1:10 diluted leachate, the germination of L. sativum was inhibited by 21% compared to the controls. The inhibition was 30% in comparison to untreated controls using the 1:1 diluted leachate and 61% using the non-diluted leachate (Figure 2A). With aged-PC-leachate, the inhibition of the germination from untreated controls after seven days was 3% using the 1:10 diluted leachate, 10% using the 1:1 diluted leachate, and 19% with the non-diluted leachate ( Figure 2B). By ageing the plastic, the inhibitory effect of the used plastic leachate was diminished by one third. Exposures with the three concentrations of BPA in substrate revealed significant inhibition of the germination (p < 0.05) by 13% with exposure to 10 mg/L, by 18% using 50 mg/L and by 36% 100 mg/L from untreated controls ( Figure 2C). In addition, in exposures with the leachates and BPA in the substrate systems, the severity of the germination inhibition caused by BPA fell between the values of new-PC-leachate and aged-PC-leachate. seemed to buffer the effects of the leachates, the combined effects of both MP and the leachates should be taken into account to understand the entirety of the effects on plants.
Polycyclic aromatic hydrocarbons (PAHs) are commonly detected in soils as xenobiotics and was previously found to inhibit the germination of L. sativum by > 84% and < 25%, at exposure concentrations of 1000 and 50 mg/kg, respectively [28]. Relating this to the results found in the present study, exposure to non-diluted PC leachate roughly elicits the same effect as exposure to between 50 and 1000 mg/kg PAHs.  The buffer function of the substrate is evident for exposures to the new-PCand aged-PC-leachate showing in most cases slightly lower germination inhibitions. Yet, in exposures using BPA, the inhibitory effect in both systems was nearly the same. However, Rillig et al. [27] pointed out that in nature, the natural microbiota may be affected by the presence of plastics in soil and thus the toxic substances associated with and leaching from MP. Therefore, even though the substrate system seemed to buffer the effects of the leachates, the combined effects of both MP and the leachates should be taken into account to understand the entirety of the effects on plants.

Germination in a Substrate-System with MP Granules
The inhibitory effect on the germination of L. sativum was also measured in exposures using new-PC-granules without prior leaching, mixed in the substrate in three different percentages (w/w) ( Figure 3A). The germination was inhibited (p < 0.05) from the first day. After seven days of exposure to 0.1% of new-PC-granules in the substrate, the inhibition of the germination was 16%, in substrate containing 1% new-PC-granules it was 27%, and 55% in substrate containing 10% of new-PC-granules compared to untreated controls. Polycyclic aromatic hydrocarbons (PAHs) are commonly detected in soils as xenobiotics and was previously found to inhibit the germination of L. sativum by > 84% and < 25%, at exposure concentrations of 1000 and 50 mg/kg, respectively [28]. Relating this to the results found in the present study, exposure to non-diluted PC leachate roughly elicits the same effect as exposure to between 50 and 1000 mg/kg PAHs.

Germination in a Substrate-System with MP Granules
The inhibitory effect on the germination of L. sativum was also measured in exposures using new-PC-granules without prior leaching, mixed in the substrate in three different percentages (w/w) ( Figure 3A). The germination was inhibited (p < 0.05) from the first day. After seven days of exposure to 0.1% of new-PC-granules in the substrate, the inhibition of the germination was 16%, in substrate containing 1% new-PC-granules it was 27%, and 55% in substrate containing 10% of new-PC-granules compared to untreated controls.
Using aged-PC-granules without prior leaching, mixed in the substrate in three different percentages (w/w) ( Figure 3B), the germination was inhibited (p < 0.05) from the first day. However, with exposure to 0.1% aged-PCgranules mixed in the substrate, the germination was not significantly influenced compared to the control from day 1 to 4 (p > 0.05).
Comparing the inhibitory effect of new-PC-granules and aged-PC-granules, the inhibition was lowered by 44% (0.1% granules in substrate), 59%, (1% granules in substrate), and 56% (10% granules in substrate), respectively, using the aged granules, clearly showing that ageing reduced the adverse effect on the germination of L. sativum in all granule percentages used in substrate.
Previously, Bosker et al. [29], found that MP particles (10 3 -10 7 particles/mL) in a substrate-free system caused significant inhibition, up to 83% after 8 h, on L. sativum germination; however, the seeds recovered after 24 h resulting in up to 100% germination. The inhibition was said to be due to a physical blockage of the pores in the seed capsule. In the present study, the inhibition was constant over a period of seven days, and the seeds did not recover as in the case of Bosker et al. [29]. However, their experimental system was conducted in a soil-free system. It is possible that the soil wrapped the seed and MP together with no movement and therefore the MP continued to block the pores. Wan et al. [30] reported that plastics could lead to the formation of channels in the soil, which could, in turn, lead to faster drying. This could have a negative impact not only on the water availability for germinating seed but also on the soil microbe composition [30] and may have been another factor contributing to the continued inhibition seen in the present study.
The same setup using previously leached granules from new-PC and aged-PC showed in the cases of the leached new-PC-granules (p < 0.05) an inhibition of germination of 7% growing seedlings in 0.1% plastic containing substrate, 17% and 24% inhibition of germination in substrate containing 1% and 10% plastic granules compared to untreated controls ( Figure 3C). Using leached aged-PC-granules, the inhibition was not significant compared to untreated controls and ranged between 2% (with 0.1 and 1% plastic in the substrate) and 5% (with 10% plastic in the substrate) ( Figure 3D). Comparing the inhibitory effect on germination between new-PC-granules leached and aged-PC-granules leached, the inhibitory effect was lowered by 29% (0.1% granules in the substrate), 12% (1% granules in the substrate), and 21% (10% granules in the substrate) using the aged leached granules. This again supports the previous observation that ageing reduced the adverse effect on germination of L. sativum but also that leaching prior to exposure reduced the adverse effect.
Leaching per se in all granule percentages used in the substrate from new-PC-granules showed a reduced inhibitory potential from leached granules by 63% (in 0.1% granules in soil), 20% (in 1% granules in the substrate), and 38% (10% granules in the substrate). There is a variation in the reduced inhibitory effect; however, clearly, pre-leaching reduced the adverse effect of the plastic particles. Considering the aged-PC-granules and comparing the leached granules versus the non-leached granules, it indicates that the inhibitory effect was reduced by 29% (0.1% granules in the substrate), 13% (1% granules in the substrate), and 17% (10% granules in the substrate). In correspondence with the previously attained results, leaching of aged-PC-granules is reducing the adverse effect. This suggests that the compounds leaching from MP plays a significant role in the effects seen on germination. Plants 2020, 9,

Root and Seedling Length in Substrate-Free Exposures
Measurement of the root and seedling length, as sub-lethal endpoints, in substrate-free exposures resulted in a concentration-dependent inhibition using the new-PC-leachate, the aged-PCleachate, and BPA ( Figure 4A). In general, the root length was reduced in all exposures (p < 0.05). The root growth reduction is concentration-dependent with leachates originating from new-PC and aged-

Root and Seedling Length in Substrate-Free Exposures
Measurement of the root and seedling length, as sub-lethal endpoints, in substrate-free exposures resulted in a concentration-dependent inhibition using the new-PC-leachate, the aged-PC-leachate, Plants 2020, 9, 339 8 of 18 and BPA ( Figure 4A). In general, the root length was reduced in all exposures (p < 0.05). The root growth reduction is concentration-dependent with leachates originating from new-PC and aged-PC, as well as using different BPA concentrations. Using the non-diluted new-PC-leachate, the reduction compared to the untreated controls is 64%. Similarly, with the non-diluted aged-PC-leachate, the root growth was inhibited by 63%. The highest reduction was observed in exposures with non-diluted leachate and 100 mg/L BPA (p < 0.05). The inhibition of root growth in seedlings exposed to BPA in high concentrations (17.2 or 50 mg/L) was also detected in soybean, wheat, and lettuce after seven days of growth [31,32]. The most provoked effect was measured in exposures with 100 mg/L BPA showing 52% smaller seedlings, compared to untreated controls. In soybean seedlings, the root length was reduced when exposed to 17.2 and 50 mg/L BPA [31]. The seedling length was adversely affected in all treatments (p < 0.05) in respect to untreated controls, which was concentration-dependent using new-PC-leachate, aged-PC-leachate, as well as in the BPA exposures. Using the new-PC-leachate, growth was reduced by 23% using the 1:10 and the 1:1 dilutions of the leachate and by 66% with the non-diluted leachate compared to untreated controls. With age-PC-leachate, the inhibition of seedling length was 13%, 56%, and 67% for exposure to the dilutions 1:10, 1:1 and non-diluted leachate in relation to untreated controls. Exposures to BPA showed a reduced seedling length of 50%, 57%, and 77% compared to the untreated control seedlings. Results indicated that there are adverse effects on root and total seedlings growth under the influence of plastic leachates. Especially with a higher leachate concentration (non-diluted), the adverse effects on smaller length was mostly over 66% in respect to untreated controls. As stated by Nicola [33], the root architecture is most vital for plant productivity. Therefore, the good growth of the primary root length of seedlings may determine the optimum root systems and influence the entire life cycle of this plant. For agriculturally used plants, this may also determine the later yield of this plant [34].

Root and Seedling Length in Substrate Exposures
In substrate systems, with exposure to new-PC-leachate, aged-PC-leachate, and BPA, a similar effect on the growth inhibition on primary root length and the seedling length was visible compared to untreated controls ( Figure 4B). Root length was reduced using new-PC-leachate with 1:10, 1:1 diluted leachate, and non-diluted leachate. The growth inhibition was significant only in 1:1 and non-diluted exposures showing 71% and 76% reduction from untreated controls (p < 0.05). Using the aged-PC-leachate the growth inhibition in respect to untreated controls were 20% (1:10 diluted leachate), 28% (1:1 diluted leachate), and 49% (non-diluted leachate) respectively ( Figure 4B). Exposure to BPA in the substrate system showed a reduced root length of 42% using 10 mg/L BPA, 55% with 50 mg/L BPF, and 74% with 100 mg/L BPA compared to untreated controls (p < 0.05) ( Figure 4B). For T. aestivum variant Sagittario, BPA decreased the root length by 19.6% at an exposure concentration of 50 mg/L [25].
The leachates of new-PC and aged-PC concentration-dependently reduced the seedling length. Using new-PC-leachate the reductions were 14% (1:10 diluted leachate), 24% (1:1 diluted leachate), and 46% (non-diluted leachate) (p < 0.05) compared to the untreated control seedlings ( Figure 4B). Lesser reductions concerning seedling length was seen using aged-PC-leachate; i.e., by 8% (1:10 diluted leachate), 17% (1:1 diluted leachate), and 22% (non-diluted leachate) (p < 0.05). Exposure to BPA showed a reduced seedling length of 4% using 10 mg/L BPA and 14% using both 50 mg/L and 100 mg/L BPA (p < 0.05) ( Figure 4B). A decrease in shoot length was observed in exposures using 50 mg/L BPA with 26.6% in T. aestivum [25]. This adverse effect might be explained by the possible inhibition of cell elongation and cell division, as suggested by Ferrara et al. [31].   Testing the different PC granules, new-PC, aged-PC, and already leached new-PC and aged-PC-granules in substrate system exposures ( Figure 5) exhibited inhibitory effects on root length and total seedling length. Compared to the untreated controls, exposure to the new-PC-granules mixed in substrate resulted in the root growth being inhibited by 35% (0.1% new-PC-granules mixed in the substrate), 71%, and 76% (1% and 10% new-PC-granules mixed in the substrate) (p < 0.05). Artificially aged-PC-granules exhibit a lesser inhibition of 8% (0.1% aged-PC-granules mixed in substrate) and 17% as well as 22% (1% and 10% aged-PC-granules mixed in substrate) (p < 0.05). The same experimental set up using previously leached granules from new-PC and aged-PC batches revealed a root growth inhibition of 4%, 14%, and 14% respectively. Rillig et al. [27] proposed that MP in soil could lead to reduced roots penetration resistance, as well as better soil aeration, which would promote root growth [35]. However, in the present study, this was not the case, presumably because the effects of substances leaching from the MP was greater than the added benefits of MP.

Germination Rate Index Calculation
The germination rate index (GRI) expresses the percentage of germination on each day during the seven days germination periods (Table 1). Higher GRI values indicate higher and faster germination of the seeds [36]. Compared to controls exhibiting a GRI of 1.59 in substrate-free exposures, exposures to new-PC-leachate and aged-PC-leachate, as well as in exposures with BPA resulted in a reduced GRI (p < 0.05) and indicated lower and slower germination of the seeds in the respective treatments. Using the new-PC-leachate, this inhibition was 23%, 61%, and 86% for the three dilutions 1:10, 1:1, and undiluted respectively, compared to untreated controls. Whereas the aged-PCleachate exhibit a GRI lowered by 6%, 14%, and 30% using the different leachate concentrations (p < 0.05). Exposure to the three different BPA concentrations revealed GRI's lowered by 8%, 16%, and 42% compared to controls (p < 0.05). In the substrate-free exposures, the most substantial adverse effect was seen with new-PC-leachate, followed by BPA exposure followed by aged-PC-leachate.  Average root length and seedlings length of L. sativum exposed to granules of new-PC and aged-PC mixed in the substrate in three different concentrations (w/w), as well as already leached granules from new-PC and age-PC, ± standard deviation (n = 50). Significance (p < 0.05) is represented by a) for root length and b) for seedling length.

Germination Rate Index Calculation
The germination rate index (GRI) expresses the percentage of germination on each day during the seven days germination periods (Table 1). Higher GRI values indicate higher and faster germination of the seeds [36]. Compared to controls exhibiting a GRI of 1.59 in substrate-free exposures, exposures to new-PC-leachate and aged-PC-leachate, as well as in exposures with BPA resulted in a reduced GRI (p < 0.05) and indicated lower and slower germination of the seeds in the respective treatments. Using the new-PC-leachate, this inhibition was 23%, 61%, and 86% for the three dilutions 1:10, 1:1, and undiluted respectively, compared to untreated controls. Whereas the aged-PC-leachate exhibit a GRI lowered by 6%, 14%, and 30% using the different leachate concentrations (p < 0.05). Exposure to the three different BPA concentrations revealed GRI's lowered by 8%, 16%, and 42% compared to controls (p < 0.05). In the substrate-free exposures, the most substantial adverse effect was seen with new-PC-leachate, followed by BPA exposure followed by aged-PC-leachate. Calculations of GRI in exposures using the substrate-system revealed, in general, using the new-PC-leachate resulted in a GRI lowered by 25%, 34%, and 71% compared to the control (p < 0.05). Using the aged-PC-leachate, the GRI has reduced with exposure to the 1:1 diluted leachate by 26% and with non-diluted leachate by 39%. Compared to the new-PC-leachate, this shows that the aged-PC-leachate has a reduced potential to influence the germination speed of the seeds adversely. In substrate, exposure to BPA exhibited a feeble inhibitory effect significant in treatments using 50 mg/L (13%) and 100 mg/L (24%) BPA compared to untreated controls (p < 0.05).
Treatments using the PC granules exhibited a lower GRI using the new-PC-granules mixed in the substrate in three percentages by 15%, 30%, and 65% from untreated controls (p < 0.05). As seen with the aged-PC-leachate, also the aged-PC granules showed a weaker influence on the GRI as it was reduced by 6%, 20%, and 35%. Using already leached new-PC granules, the reduction of GRI compared to untreated controls was nearly halved to 8%, 19%, and 34% also compared to the results from the respectively used leachate samples. Already leached aged-PC granules showed a non-significant GRI reduction by 1%, 2%, and 8% from untreated controls.
In most of the treatments, the GRI and therefore the germination speed of the L. sativum seeds were reduced when exposed to leachates or PC granules material. A possible ecological implication is that crop yield might be reduced if the agricultural soil contains too many plastic particles, which are able to influence the GRI, by delayed growth and seed production.
In soil, fertilizers made from recycled waste, as well as street runoff, including abrasions from tires and breaks may be a source of MP [37]. The presence of MP could change soil structure and behavior [14,15]; nevertheless, the main effect seems to be the chemicals leaching out of the plastic material.

Lepidium sativum (L.) Seeds
Garden cress (Lepidium sativum L.) seeds (Art. No. G250) were purchased from Bingenheimer Saatgut AG (Echzell, Germany). Seeds were carefully selected by removing small seeds or any deformed or damaged seeds. The seeds were then washed in distilled water to remove possible impurities. The batch used for all experiments exhibited a germination percentage of 99%. Germination experiments were performed at 25 • C ± 1 • C under 1500 lux light and a light-dark cycle of 12:12 h for seven days in total.

Microplastics, Aged Microplastics and Plastic Leachates
For the experiments, commercially available colorless polycarbonate granules (PC) (Goodfellow GmbH, Hamburg, Germany) with an average size of 3 mm ± 1 mm were used. The plastic material was washed with ISO reconstituted water (pH 7.2) [38] and dried at 25 • C before use to remove any superfine particles.
Accelerated ageing of the PC material was done according to Fejdyś et al. [39] making use of PN-EN 12280-1:2002. In short, artificial ageing was done in a thermal chamber (TK 720 Binder GmbH, Tuttlingen, Germany) with a heating effect at a temperature of 70 • C ± 0.5 • C and < 1.5% humidity for 80 days.
The PC was subjected to treatment to induce leaching according to the Swedish standard 12457: 2003 [40], with some modifications. Leaching time was increased from 24 h to 72 h and a temperature of 50 • C was used to increase leaching and to simulate a more realistic scenario; i.e., that the surface of plastic material in the environment may reach this temperature and even above when exposed to sunlight outdoors [41]. The leaching was accomplished by mixing 200 g of the PC material with ISO reconstituted water (pH 7.2) [38] to reach a liquid-to-solid ratio (L/S) of 10. The complete leaching process was done in darkness in round bottom flasks on a rotary mixer (Hei-VAP Valve, Heidolph-Instruments, Schwabach, Germany) at 21 rpm. The liquid and solids were separated by vacuum filtration on Whatman borosilicate glass microfiber filters (grade GF/F; particle retention 0.7 µm). This filter is approved in the EPA method TCLP 1311 for toxicity characteristic leaching procedure.
For the substrate-free exposures ( Figure 6A), the new PC (new-PC-granules) material was used. Parts of the new PC material was artificially aged (aged-PC-granules) as described above. Both batches were then separately leached, as described above, to gain a leaching solution for the substrate-free experiments (new-PC-leachate; aged-PC-leachate). The leaching solution was diluted with ISO reconstitutes water 1:10, 1:1, and also non-diluted was used. For the substrate-based exposures ( Figure 6B), new PC granules were used directly and mixed in the substrate in a ratio of 0.1%, 1.0%, and 10% (w/w). Parts of the new PC material was leached to gain a leaching solution (new-PC-leachate) and leached PC material (new-leached-PC). The leaching solution was diluted 1:10 and 1:1, as well as non-diluted, were used for the exposures. The leached PC material was mixed in the substrate in the ratio of 0.1%, 1.0%, and 10% (w/w). A batch of the new PC material was again artificially aged. Parts of this material was directly mixed in the substrate in the ratio of 0.1%, 1.0%, and 10% (w/w). Another part was leached to gain leached, aged PC material (aged-leached-PC) and the leaching solution of aged PC material (aged-PC-leachate). Leaching solution was diluted 1:10, 1:1, and also non-diluted were used for the exposures. The leached, aged PC material was mixed in the substrate in the ratio of 0.1%, 1.0%, and 10% (w/w).

Bisphenol A
Bisphenol A (BPA) is known to be an important chemical widely used as a monomer in the production of plastics. Analytical grade solid bisphenol A was obtained from Sigma-Aldrich Inc. (USA). BPA was solved in 96% ethanol to final concentrations of 10 mg/L, 50 mg/L, and 100 mg/L [24,26]. Concentrations were checked on a UPLC-MS/MS system (Acquity UPLC, Quattro Premier, Micromass, Waters GmbH, Eschborn, Germany) using the method of Vela-Soria et al. [42]. Ethanol concentration in all samples, including controls were less than 10%.

Control for Plastic Leachate and BPA Exposures
To investigate whether controls without and with ethanol could be grouped, ten independent substrate-free exposures with 50 seeds each of L. sativum was set up using ISO reconstitute water and ten independent exposures with ISO water [38] containing ethanol, to see possible effects caused by the solvent. The ethanol concentration in the medium did not exceed 0.05% (v/v). Germination was determined after seven days as well as the root length of the seedlings. Both exposures with ISO water and with water-containing ethanol (0.05%, v/v) exhibited a germination percentage of 99% ± 1%. Average root lengths of 25.1 mm ± 1.3 mm and 25.3 mm ± 1.1 mm were achieved using ISO water [38] and water containing 0.05% ethanol, respectively. As both groups were the same (p > 0.05), they were combined as one control for all exposures.

Experimental Design
All experimental setups were performed in two sets; i.e., substrate-free ( Figure 6A) and substrate environment ( Figure 6B) for direct comparison and a possible link to real agricultural situations.

Substrate-Free Experiments
Seeds were sown on a Whatman filter GF/D (WH 1823-055) in glass crystallizing dishes with 5 mL of ISO reconstituted water [38] at pH 7.2 (control). Exposure solutions contained a mixture of the respective leaching solutions from new PC and aged PC material in a ration of 1:10, 1:1, and non-diluted leaching solution. Three concentrations of BPA (10.5 mg/L, 51.4 mg/L, and 103 mg/L) were used for exposures in parallel. Ten replicates with 50 seeds each were used for all exposures. The experimental set consisted of six treatments of 10 replicates (50 seeds each) and one control set with ten replicates (50 seeds each).

Substrate Experiments
A turf-free soil-based substrate was purchased from MeinWoody (Grub am Forst, Germany) and consisted of 20% lingo fibers, 35% cocopeat washed, 10% spelt fermented, and 35% substrate compost. The substrate had a pH of 7 ± 0.5. Glass crystallizing dishes were used containing 6 g of the substrate per replicate, respectively. Exposure was done carefully mixing the respective PC material (new, aged, and leached) into the substrate until a visually homogeneous mixture was achieved in a percentage of 0.1%, 1.0%, and 10% (w/w). Before sowing the seeds, the substrate was watered with 4 mL of ISO reconstituted water [38], which had a pH 7.2; for all treatments. The different leaching solutions from newand aged-PC-granules were directly applied onto the substrate as non-diluted or diluted with ISO reconstituted water (pH 7.2) [38] in a ratio of 1:10 and 1:1. The same three concentrations of BPA (10.5 mg/L, 51.4 mg/L, and 103 mg/L) were again applied in parallel. Each treatment had ten replicates with 50 seeds each. Every second day 500 µL of ISO reconstituted water was added for each replicate to ensure that the soil did not dry out.
During all stages of experimental set-up and analysis, attention was paid to avoid self-contamination [43].

Experimental End Points
The evaluation criterion for germination was the opening of the seed cover and the emergence of a 3 mm primary root. In all experiments, the following parameters were determined: (a) Germination percentage (GP) is determined by calculating the level of cumulative seed germination percentage as shown in Equation (1): Ng is the number of germinated seeds, and N t represents the total number of seeds used in the particular batch. Germination is operationally defined as radicle emergence. The completion of germination is actually observed. The unit for GP is percentage (%) and measures the germination capacity [44][45][46][47][48].
(b) Mean total seedlings length, and radicle length was measured in mm after seven days of germination with a digital caliper. (c) Germination rate index (Speed of germination; GRI) is expressed as the germination in terms of the total number of seeds germinating in a time interval in%/time as per Equation (2): N1, N2, . . . N7 are the numbers of germinated seeds observed at time (days) T1, T2, . . . T7 after sowing.
No accumulated numbers but only seeds that germinated at the specific time [48,49].

Statistics
IBM ® SPSS ® statistics 25 (2018) was used to perform a descriptive analysis based on means of each germination index. Results are expressed as mean ± standard deviation. Data were submitted to one-way analysis of variance (ANOVA). When the overall F statistic was significant, pair-wise comparisons to controls were performed by Tukey-Kramer test [50]. The 0.05 level of significance was used.

Conclusions
Previous research has demonstrated the adverse effects of MP on animals; however, plants can be affected by MP-containing irrigation water or simply by MP in the substrate. The results of the present study showed that ageing of MP reduced the adverse effects on the germination of L. sativum, conceivably as harmful chemicals were leached out. Similar reduced effects were seen in the presence of substrate, where the substrate serves as a buffer and likely adsorbs the leached chemicals. Whether MP as a whole is toxic is questionable; however, leached chemicals seem to have significant adverse effects, especially in germinating seeds that soak up leachate contaminated water. In addition, it should be noted that the adverse effects might also be due to surface-bound chemicals [6] or even due to metabolic products from surface biofilms formed during the several years in the environment or a combination and should be investigated in future.