Phytosynthesis of Zinc Oxide Nanoparticles Using Ceratonia siliqua L. and Evidence of Antimicrobial Activity

Carob (Ceratonia siliqua L.) is a tree crop cultivated extensively in the eastern Mediterranean regions but that has become naturalized in other regions as well. The present study focused on the green synthesis of zinc oxide nanoparticles (ZnONPs) from Carob and their evaluation for antimicrobial activity in bacteria and fungi. The synthesized ZnONPs showed strong antibacterial activity against Staphylococcus aureus ATCC 25 923 (92%). The NPs inhibited the growth of pathogenic yeast strains, including Candida albicans ATCC90028, Candida krusei ATCC6258, and Candida neoformans ATCC14116, by 90%, 91%, and 82%, respectively, compared to the control. Fungal inhibition zones with the ZnONPs were 88.67% and 90%, respectively, larger for Aspergillus flavus 15UA005 and Aspergillus fumigatus ATCC204305, compared to control fungal growth. This study provides novel information relevant for plant-based development of new and potentially antimicrobial ZnONPs based on extracts. In particular, the development and application of phytogenic nanoparticles enhances the biocompatibility of nano-scale materials, thereby allowing to tune effects to prevent adverse outcomes in non-target biological systems.


Introduction
Engineered nanomaterials existing in dimensions ranging between 1-100 nanometers (nm) have shown novel applicability in different fields, including food, agriculture, and medicine. Nanoparticles (NPs) possess unique physical properties such as small size, large surface area to volume ratio, electric conductivity, biomimetic property with enhanced catalytic reactivity, thermal conductivity, and non-linear optical performance [1,2]. In particular, the property of increased reactivity has raised the question of whether there are risks of potential toxicity to human and environmental health, and what environmental factors influence such toxicity [3,4]. Therefore, the biosynthesis of NPs has emerged as a preferred approach due to being safer, more cost-effective, biocompatible and eco-friendly, relative to chemically synthesized NPs [5]. The biological pathway for NP synthesis involves use of microorganisms (bacteria, fungi, yeast and algae) and plants. However, compared to Carob bean (Ceratonia siliqua L.) belongs in the Caesalpinioideae sub-family of the legume family, Fabaceae. The carob tree grows to a height of 12-15 m, with a productive life span of more than one hundred years. This legume is an evergreen tree known for its economic and environmental values in the coastal regions of Mediterranean basin and southwest Asia [18]. It has an annual worldwide production of over 315,000 tons of carob products [18]. The Carob pod consists of pulp (90%) and seeds (10%) by weight. In the US, carob is adapted to USDA zones 9-11, which encompass the area between Texas and Florida, and also Hawaii. In much of these places, it is considered a "neglected" crop in the context of contemporary crop science and agronomic research. Carob fruit, flour and syrup have been shown to be rich sources of carbohydrates, proteins and minerals [19]. Carob pulp is rich in antioxidant compounds and nutrients such as fructose, sucrose, glucose and maltose (48-56%), fibers such as cellulose and hemicellulose (18%), and condensed tannins (16-20%) [20]. The plant can be a source of biologically active substances with proven health properties for inclusion in the human diet [18]. Isolated galactomannan from seed gum (30-40% by weight) is indeed used as a valuable stabilizing and thickening additive in the food, pharmaceutical and biotechnology industries [21,22]. In addition, derived products such as laxatives and diuretics are used in medicine [20]. Therefore, carob plant may contain significant amounts of phytochemicals utilizable for the synthesis or development of products with application in agriculture, such as nanoscale agrochemicals. To the best of our knowledge, studies on the use of C. siliqua L. pods for the green synthesis of ZnONPs are lacking. Given the rich phytochemical profile of carob and the relevance of Zn in microbial metabolism, the objectives of this study were the biosynthesis of ZnONPs using carob pods, the evaluation of the chemical composition of the carob precursor material, and investigation of the antimicrobial activity of the bio-generated ZnONPs.

Phytosynthesis and Characterization of Zinc Oxide Nanoparticles
Bio-ZnONPs were synthesized using Zinc acetate as a precursor. The bio-ZnONPs were characterized using several techniques. The biosynthesis of ZnONPs from C. siliqua was confirmed by UV-vis absorption ( Figure 1). The biosynthesized ZnONPs showed an absorption peak at 360 nm. FTIR spectroscopy ( Figure 2) showed the presence of organic functional groups, including carbonyls and hydroxyls attached to the surface of the NPs, as well as other surface chemical residues showing peaks at the range of 400-4500 cm −1 at a resolution of 4 cm −1 . FTIR analysis allowed to ascertain the presence of phytochemicals and functional groups in the plant extract, such as flavones, alcohols, phenols, amines, carboxylic acids, sugars, and ketones, which can interact with the particle surface, and aid in the stabilization of the ZnONPs. The absorption peaks of FTIR spectra at (1) 3550-3200 cm −1 , (2) 1685-1596 cm −1 , (3) 1400-1300 cm −1 , (4) 1415-1380 cm −1 and (5) 1000-960 cm −1 imply respectively the stretching vibrations of (1) O-H (alkene), (2) C=C stretching, and also (3) N-O stretching, (4) S=O stretching ( Figure 1). The peak registered for ZnONP at about 1680 cm −1 implies alkene (C=C) stretching, while the peak recorded at 1500 cm −1 is assigned to the aromatic bending vibration of alkane group (C-H).
In addition, TEM images revealed particles with round morphology and having an average size of 200 µm (Figure 3). EDAX confirmed the main peaks for Zn and O, in addition to peaks corresponding to C and Na, presumably originating from the plant extract ( Figure 4A). Electron paramagnetic resonance (EPR) analysis showed that bio-ZnONPs did not demonstrate any magnetic properties ( Figure 4B). Further, the particles contained amounting to 8.576 ppm ± 1.239, in addition to other minerals, including Na (4.157 ppm ± 0.969), and Ca (2.719 ppm ± 0.304) ( Table 1). did not demonstrate any magnetic properties ( Figure 4B). Further, the particles contained amounting to 8.576 ppm ± 1.239, in addition to other minerals, including Na (4.157 ppm ± 0.969), and Ca (2.719 ppm ±0.304) ( Table 1).

Determination of the Chemical Profile of C. siliqua Pods by HPLC-MS.
As this study pioneers the biosynthesis of any metal oxide NPs using C. siliqua as the starting plant material, it was important to analyze the chemical composition of the plant material. Figure 5 shows the presence of proteins, sugars, as well as the macronutrients P, Ca, K, Mg, and Na, and the micronutrients Cu, Zn, Fe and Mn. The highest nutrient levels were recorded, in a decreasing order, for Na, Ca, Fe, K, and Zn ( Figure 5).

Determination of the Chemical Profile of C. siliqua Pods by HPLC-MS
As this study pioneers the biosynthesis of any metal oxide NPs using C. siliqua as the starting plant material, it was important to analyze the chemical composition of the plant material. Figure 5 shows the presence of proteins, sugars, as well as the macronutrients P, Ca, K, Mg, and Na, and the micronutrients Cu, Zn, Fe and Mn. The highest nutrient levels were recorded, in a decreasing order, for Na, Ca, Fe, K, and Zn ( Figure 5).

Evaluation of the Antimicrobial Activity of bioZnONP
An assessment of the antimicrobial potential of the C. siliqua-based ZnONPs was conducted on bacterial and fungal strains. Table 3 showed the antibacterial activity against Staphylococcus aureus ATCC 25 923 (Gram-positive) (zone of inhibition: 12 mm), versus no antibacterial activity against Micrococcus luteus NCIMB 8166 (Gram-positive), Salmonella enterica serotype Typhimurium ATCC 1408 (Gram-negative) and Escherichia coli ATCC35218 (Gram-negative). As with bacterial strains, the Bio-ZnONP showed strong inhibitory activity against all tested yeast strains, including Candida albicans ATCC90028 and Candida krusei ATCC6258 (zone of inhibition: 14 mm) and Candida neoformans ATCC14116 (zone of inhibition: 13 mm). Moreover, antifungal effects were recorded against Aspergillus flavus 15UA005 with a larger zone of inhibition (17 mm), compared with Aspergillus fumigatus ATCC204305 (15 mm), whereas no antifungal activity was observed against Aspergillus niger 15UA006 (Table 3).

Discussion
Plant extracts act as reducing and stabilizing agents in the production of NPs with antimicrobial potential, enabling cost-effective and environment-friendly operations, compared to conventional physical and chemical approaches to synthesizing NPs. In this study we synthesized ZnONPs from carob pods and demonstrated antimicrobial activity with the biosynthesized NPs. The FTIR data indicates that the observed functional groups on the NP surface are the capping ligands derived from C. siliqua. The main role of capping ligands is to stabilize the NPs to prevent further growth and agglomeration which modulates their bioactivity [23]. The capping process by the functional groups can also occur during the green synthesis process, thereby controlling growth in situ [24]. In this case, the phytochemicals such as favones, alcohols, phenols, amines, carboxylic acids, sugars and ketones can interact with the zinc surface and aid in the stabilization of NPs. Water soluble phytoconstituents such as flavones, quinones, and organic acids that are available in the plant extract could have contributed towards an instantaneous reduction of zinc ions in the synthesis process. Overall, the stretching vibrations in FTIR spectra of bioZnONPs, confirm that C. siliqua phytocompounds serve as coating, capping, and stabilizing agents for ZnONPs; and that the Zn-O frequencies observed for the bioZnONP are in accordance with values in the literature [25,26]. Besides, the relative chemical composition of the plant material suggests that sugars from plants may be responsible for the reduction of metal salts into the NPs, a likelihood corroborated by previous findings with other metallic NPs [27,28]. However, amino acids and proteins may also be involved, but likely to a lesser degree. In addition, bio-capping may be achieved by the carboxylic and phenolic acids present in the carob pod extract. These capping agents are important for preventing agglomeration and controlling the biosynthesis. Also, Zinc reduction achieved through the phytoconstituents (flavonoids or other polyphenols) present in C. siliqua may be considered as an important progress in this path. In this regard, the screening of the polyphenols and phenolic acids present in C. siliqua suggests some of the main phenolic compounds that may have been involved in the capping and stabilization of NPs, notably flavonoids and phenolic compounds.
Findings on the antimicrobial activity of the biosynthesized ZnONPs agree with other reports on the efficacy of green synthesized metal oxide NPs, including ZnONPs, as antibacterial agents [29][30][31][32][33]. Gupta [30] who showed that biologically synthesized silver NPs (AgNPs) exhibited antibacterial activity against Staphylococcus aureus and E. coli, with larger inhibition zone formation against S. aureus (9.25 mm), compared with that of E. coli (6.75 mm), in addition to antifungal activity against Aspergillus flavus and Candida albican (with superior inhibition against A. flavus (zone of inhibition: 7 mm) compared with C. albicans (zone of inhibition: 5.75 mm). Similar antimicrobial and anticancer activities were reported for ZnONPs and AgNPs [12,35,36]. Notably, Aspergillus flavus is a plant pathogen; research to understand the effect of the carob-synthesized ZnONPs is ongoing in an Aspergillus-plant pathosystem, which would demonstrate the applicability of work reported in this manuscript in plant production.
Drug or agrochemical resistance by strains of human and plant pathogenic microbes have increased in recent times. Hence, alternative strategies to control microbial infections in biological systems are required. In this wise, studies to establish nanoscale materials such as ZnONPs as viable options for novel antimicrobials have gained prominence in recent times. Taken together, therefore, data from the current study contribute to the search for enhanced efficiency biogenic antibacterial and antifungal agents. Increasingly, NPs continue to be assessed as antibiotics because of their strong antimicrobial activities [37], while plant extract have already been used as reducing antibacterial and antifungal agents [22]. The combination of NPs and plant derived extracts therefore provides a synergy among specific plant constituents and nanosized particles for biological activity. The biosynthesized plant extract-derived metal/metal oxide NPs may act via their ability to inhibit key enzymes, such as bacterial DNA gyrase and fungal cytochrome P450 (C. albicans) and dihydrofolate reductase (A. flavus), thus resulting in inactivation of bacterial or fungal microorganisms [34].
The fundamental shortcoming of research in the field of phytosynthesis of NPs is that findings are sometimes conflicting, and there are no consistent outcomes. This is because to a considerable extent, the findings differ substantially because phytochemical composition and quantities vary from plant to plant. Additionally, the size and morphology of NPs are controlled by certain phytochemicals and chemistry of the specific precursor salt. To clarify the mechanism, it is necessary to identify the exact phytochemicals participating in the NP biosynthesis process. However, in attempting to understand the correlations between the plant extract composition, the phytosynthesis, and NP morphology and surface chemistry, there is a lack of appropriate plant extract characterization in accordance with the common phytoconstituents. In this regard, there is need, as demonstrated in the current work, to identify plants with superior biochemical arsenals that can be appropriately characterized, quantified and deployed in NP synthesis to provide novel agrochemicals that can be applied in improving and sustaining crop production in the face of increased events of disease outbreaks that devastate crop yield.

Biosynthesis and Characterization of Biosynthesized C. siliqua L. Bio-ZnONPs
Carob (C. siliqua L.) pods were dried at room temperature for one month. Subsequently, pods were crushed mechanically using a kibbler, and separated from seeds. Pods were then ground into powder in a mixer. 5-10 g of the pod powder was added to distilled water for 1 h under heating at 60 • C, followed by filtration using Whatman filter paper (diameter 0.9 cm) and the filtrate was stored at 4 • C. A volume of 100 mL of plant broth was mixed with 0.1 M zinc acetate dehydrate (v/v). The mixture was incubated in a boiling water bath at 80 • C for 2 h. The formed bio-ZnONPs precipitates were collected by centrifugation at 8000× g for 10 min. Supernatants were eliminated, and pellets were collected and washed 3 times with distilled water to remove impurities. This product I hereinafter referred as "C. siliqua. bio-ZnONPs". Characterization of synthesized materials was done using standardized analytical techniques. The formation of bio-ZnONPs was confirmed by measuring UV-visible absorption spectrum using a Spectra Max M2 spectrophotometer. Fourier Transform Infra-Red (FTIR) spectra was recorded by using a Bruker Equinox 55 spectrometer. The particle size distribution and the surface area of the samples were determined at the wavelength of 400-4000 cm −1 , and a resolution of 2 cm −1 using a laser analyzer Malvern Mastersizer 2000. Dynamic light-scattering (DLS) was used to determine the particle size distribution, and the zeta potential, which represents the charge on the NPs' surface. Transmission electron microscopy (TEM) images was used to characterize particle morphology and size (Hitachi HT 7800, 120 kV). EDX analysis was performed using a FEI Quanta 200 environmental scanning electron microscopy (SEM; Leuven Belgium, PHILIPS/FEI), operating at 20 kV. For magnetic properties of NPs, EPR spectra were obtained at room temperature on a Bruker ER-200D spectrometer operating at 9.8 GHz X-Band frequencies with modulation amplitude of 0.2 mT, modulation frequency of 100 khz, sweep width of 210 mT and microwave power of 63 mW.

Elemental Analysis of Bio-ZnONPs
The content of Zn and other mineral elements in C. siliqua pods was measured using inductively coupled plasma optical emission spectroscopy (iCAP 6000; DAC0083, Thermo Fisher Scientific). ICP-OES method was validated using blank, 0.1 ppm, 1 ppm, and 10 ppm standard solutions (quality control standard 7 and 21, SPEX CertiPrep, Metuchen, NJ, USA; prepared in 2% nitric acid). Yttrium (10 ppm) was used as an internal standard. A 30 s rinse with DI water was carried out between samples, and continuing calibration verification sample was done each 15 samples. Results were expressed in ppm.

Determination of Dry Biomass (DM), Organic Biomass (OM), Mineral Biomass (MM) and Total Nitrogen
Fresh pods were placed at 40 • C for 24 h to obtain dry biomass (DM). Mineral biomass (MM), referred as ash, was determined after combustion at 550 • C in oven for 6 h and expressed as a percentage of the DM. Organic biomass (OM) was calculated using the formula DM-MM.
The total nitrogen content in dry pods (0.5 g of DM) was determined using Kjeldahl [38], and used as a surrogate for protein content. A control reaction (in the absence of sample) was included as a reference. The percentage of nitrogen was calculated as %N = 100 × (VHCl for sample-V0) × 0.1 (N) × 0.140/m (g), where V0 refers to the volume of HCl used in titration. The concentration of crude proteins was then calculated as CP = %N × 6.25.

Elemental Analysis
Determination of mineral elements by atomic absorption spectrometry (AAS). Pods of C. siliqua were dried at 120 • C in oven and ground in a mortar. One gram of dry biomass was subjected to mineralization at 500 • C in oven for 6 h. The obtained ashes were solubilized in HCl (4:1, concentrated HCl: distilled H 2 O) under heating at approximately 200 • C. Homogenates were then filtered twice with ash-free filter papers and the final volumes of filtrates were adjusted to 50 mL. Atomic absorption spectrometry (AAS; Thermo SCIENTIFIC, Type iCE3500AA System, NC942350023500, Ser No C103500104) was used to determine the contents of essential mineral elements in the pods. Total phosphorus was estimated using the vanado-molybdic reaction solution [39]. The solution consisted of 50 mL of ammonium heptamolybdate (NH 4 ) 6 Mo 7 O 24 .4H 2 O (5 g dissolved in H 2 O and 0.5 mL ammoniac (d: 0.91)), 50 mL ammonium monovanadate NH 4 VO 3 (0.1175 g) and 3.35 mL nitric acid (HNO 3 ) in 200 mL total volume. A mass of 0.1175 g of ammonium monovanadate (NH 4 VO 3 ) was dissolved in 20 mL of hot H 2 O. Potassium dihydrogen phosphate (KH 2 PO 4 ) was used to prepare standard concentrations up to 40 µg/mL. Pods were dried at 120 • C, then mixed with 1 mL of vanado-molybdic reactional solution. After homogenization, the mixture was allowed to stand for 10 min at 20 • C, after which absorbance was read at 730 nm using a UV-VIS spectrophotometer (Model T80, 25-1884-01-0002, 180W).

Measurement of Pod Fiber Content
The protocol of ANKOM 220 Fiber bag method [ANKOM Technology [Filter Bag Technique in Feeds (for A200 and A200I)] was used for the determination of fiber contents in cell walls (cellulose, hemicellulose and lignin); Acid Detergent Fiber (ADF) (cellulose and lignin); Neutral Detergent Fiber (NDF) (cellulose, hemicellulose, and lignin); and Acid Detergent Lignin (ADL). The levels of cellulose, hemicellulose, lignin, crude cellulose (CB), NDF, and ADF were estimated using the method of Van Soest [40]. To measure ADF, an acid detergent solution (ADS) was used, in which 20 g of cetyltrimethyl ammonuim bromure (CTAB) was dissolved in H 2 SO 4 (1 N). Subsequently, one gram of dry C. siliqua pods (Pe) was boiled with ADS for 60 min, followed by filtration and rinsing with acetone, and drying at 105 • C for 24 h (1st desiccation) (P1). A volume of 30 mL of ADSL (acid detergent lignin solution) prepared by placing sample bags in a flask containing 350 mL of sulfuric acid H 2 SO 4 72% by weight. After 3 h, the mixture was filtered and rinsed with hot distilled water, then dried at 105 • C for 24 h (2nd desiccation) (P2). Samples were then oven-dried at 500 • C for 3 h (incineration) P3. Calculations were made using the following formulas (manufacturer instructions): With; W1: bag tare weight; W 2 : sample weight; W3: dried weight of bag with fiber after extraction process; and C1: blank bag correction (running average of final oven dried weight divided by original blank bag weight. With: W 1 : bag tare weight; W 2 : sample weight; W 3 : weight after extraction process; W 4 : weight of organic matter (OM) (weight loss on ignition of bag and fiber residue); C 1 : blank bag correction (final oven_dried weight/original blank bag weight); C 2 : ash corrected blank bag (loss of weight on ignition of bag/original blank bag); MD: dry matter.
To measure NDF, sodium dodecyl sulfate (SDS; C12H25NaSO4), a neutral detergent solution (NDS) was used, in which one gram of biomass (Pe) was added to 100 mL de solution NDS, and boiled for 60 min, after which the homogenate was filtered and rinsed with distilled H 2 O, and bags were placed in a flask containing pure acetone. The mixture was then dried at 105 • C for 24 h (desiccation) (P1), then in an oven at 500 • C for 3 h (incineration) (P2). % NDF (as_received basis) = [100 × (W 3 − (W 1 × C 1 ))]/W 2 .
With; W1: bag tare weight; W 2 : sample weight; W3: dried weight of bag with fiber after extraction process; and C1: blank bag correction (running average of final oven dried weight divided by original blank bag weight.

Assay of Free Amino Acids and Total Soluble Sugars
Fresh carob pods were extracted and stored at −20 • C. Subsequently, homogenization (1:10, w/v) was performed in 80% ethanol at 70 • C (1:10, w/v), followed by centrifugation at 8000× g for 20 min at 4 • C. The obtained supernatant speculated to contain free amino acids and total soluble sugars were analyzed to quantify these compounds. For free amino acids, an aliquot of extract was added to 0.9 M citric acid (pH 5.2) and ninhydrin solution 1.5% (prepared in ethanol 60% /H 2 O, v/v, in the presence of ascorbic acid). The reaction mixture was incubated at 100 • C for 15 min and then allowed to cool at 4 • C for 5 min.
After the immediate addition of ethanol 60%, absorbance of the mixture was read at 570 nm using glycine as standard [41]. For total soluble sugars, an aliquot of the extract was mixed with a 0.2% anthrone solution in concentrated sulfuric acid. After incubation at 100 • C for 15 min and cooling at 4 • C for 5 min, absorbance was measured at 625 nm using glucose as standard [42].

Determination of the Phenolic Compounds by HPLC-MS
Dried carob pods were ground into powder, after which a powder mass of 5 g was homogenized in 80% methanol (1:10, w/v), centrifuged at 8000× g for 20 min, and the supernatants filtered through a 0.45 µm cellulose acetate filter (Millipore). Phenolic compounds were analyzed by Liquid Chromatography-Mass Spectrometry using a Shimadzu UFLC XR system (Kyoto, Japan), consisting of a CTO-20 AC column, a LC-20ADXR binary pump and a quadrupled 2020 detector system. The chromatography was performed using an Inertial ODS-4 C18 3 µm column L150 × 3.0 mm i.d, at column temperature set at 40 • C. The injection volume was 20 µL, and the flow rate was 0.5 mL min −1 . The mobile phases were: (A) 5% methanol, containing 0.15% acetic acid and (B) 50% ACN, containing 0.15% acetic acid. Elution proceeded in a linear gradient system of 0.01-14 min from 10% to 20% (B); 14-27 min from 20% to 55% (B); 27-37 min from 55% to 100% (B); 37-45 min with 100% (B), followed by column washing and equilibration for 45-50 min with 10% (B). Dissolving line temperature was 275 • C, mobilizing gas flow was 1.50 mL/min, the drying gas was set at 15.00 mL/min, and Temperature of Heat block was set at 450 • C. LC-ESI (-) MS mass spectra [M-H]-were acquired using Lab Solutions software. Phenolic acids were identified by comparison with retention time of the standards of polyphenolic compounds. The lab standards used were LGC and Sigma Aldrich.

Evaluation of the Antibacterial Activity of bioZnONP
The bacteria for the evaluation consisted of Gram positive (Staphylococcus aureus ATCC 25 923 and Micrococcus luteus NCIMB 8166) and Gram negative (Salmonella enterica serotype Typhimurium ATCC 1408 and Escherichia coli ATCC35218) strains. Bacterial culture was carried out on nutritive gelose at 37 • C for 24 h. Subsequently, selected colonies were inoculated into suspensions of 10 mL volume of sterile physiologic water and then mixed for 5 min. Growth was monitored by measuring the optic density (OD) of the culture at 600 nm and adjusted up to OD value 0.5. A volume of 1 mL of the bacterial culture was used on Muller Hinton gelose in a petri dish. Then, 100 µL (10 mg/mL) of carob Bio-ZnONPs was added into 6 mm diameter of wells. Petri dishes were incubated at 37 • C for 24 h. The diameter of inhibition zone was measured using digital caliper. These experiments were carried out in triplicates under sterile conditions.

Evaluation of Activity against Yeast Growth
Yeast strains consisting of Candida albicans ATCC90028, Candida krusei ATCC6258 and Candida neoformans ATCC14116 were used for this evaluation. Culture was performed on Sabouraud gelose at 37 • C for 48 h. Selected colonies were inoculated into suspensions of 10 mL volume of sterile physiologic water and mixed for 5 min. Growth was monitored by measuring the optic density (OD) of the culture at 600 nm and adjusted up to OD value 0.5. One mL of the yeast suspension was inoculated on Sabouraud gelose and grown for 30 min at 37 • C. Then, 6 mm of diameter wells were prepared on gelose. A volume of 1 mL of the bacterial culture was used on Muller Hinton gelose in a petri dish. Then, 100 µL (10 mg/mL) of carob Bio-ZnONPs was added into 6 mm diameter of wells. Following incubation for growth at 37 • C for 48 h, diameters of inhibition zone surrounding the sample zone were measured and expressed in mm. Three replicates were involved with experiments conducted under sterile conditions.

Evaluation of Antifungal Activity
The fungal strains, Aspergillus flavus 15UA005, Aspergillus niger 15UA006 and Aspergillus fumigatus ATCC204305 were cultured on Sabouraud gelose in Falcon tubes of 15 mL at 25 • C for 7 days. Spores of the fungal strain were transferred into suspensions of peptone water and counted up to 106 spores/mL. One mL of fungal suspension was inoculated on Sabouraud gelose in petri dish and incubated for growth at 25 • C for 30 min. Then, 6 mm of diameter wells were prepared on gelose. A volume of 100 µL (10 mg/mL) of the Bio-ZnONPs sample was added into the wells. Following incubation for yeast growth at 25 • C for 48 h, the diameters of inhibition zone surrounding the sample zone was determined and expressed in mm. The test was carried out in triplicates under sterile conditions.

Statistical Analysis
Statistical analyses were carried out using SPSS 20.0 and Xlstat version 9.0 software 2014 SPSS(Statistical Product and Service Solutions) developed by SPSS Inc. under IBM company, Chicago, Illinois. Data were subjected to analysis of variance (two ways) ANOVA at α = 0.05%. Means were compared using Duncan multi-range test at 5%.

Conclusions
We demonstrate for the first time that extracts from the carob plant, C. siliqua L., can be used for the synthesis if ZnONPs; and that the ZnONPs can effectively be used as an alternative antimicrobial agent. These results portend a demonstration of a novel tool for developing more efficient solutions against antibacterial and antimicrobial resistance in both human and plant pathogens. However, further research is required to assess the mechanisms of action and toxicity of the phytosynthesized NPs, including for untargeted microbes, especially in plant-pathosystems. Also, studies to establish optimal dose are required, compared to conventional antimicrobials. Furthermore, a rapid, cost-effective, environmentally-friendly method for ZnONPs synthesis was demonstrated, which can be used as a rapid screening strategy agent against different microbial species with relevance in human and agricultural health. Funding: The authors declare that no funds, grants, or other support were received during the preparation of this manuscript.

Data Availability Statement:
The datasets generated during and/or analyzed during the current study are available from the corresponding author upon reasonable request.