UV-Accelerated Photocatalytic Degradation of Pesticide over Magnetite and Cobalt Ferrite Decorated Graphene Oxide Composite

Pesticides are one of the main organic pollutants as they are highly toxic and extensively used worldwide. The reclamation of wastewater containing pesticides is of utmost importance. For this purpose, GO-doped metal ferrites (GO-Fe3O4 and GO-CoFe2O4) were prepared and characterized using scanning electron microscopy, X-ray diffraction and Fourier transform infrared spectroscopic techniques. Photocatalytic potentials of catalysts were investigated against acetamiprid’s degradation. A detailed review of the parametric study revealed that efficiency of overall Fenton’s process relies on the combined effects of contributing factors, i.e., pH, initial oxidant concentration, catalyst dose, contact time, and acetamiprid load. ~97 and ~90% degradation of the acetamiprid was achieved by GO-CoFe2O4 and GO-Fe3O4, respectively during the first hour under UV radiations at optimized reaction conditions. At optimized conditions (i.e., pH:3, [H2O2]: 14.5 mM (for Fe3O4, GO-Fe3O4, and GO-CoFe2O4) and 21.75 mM (for CoFe2O4), catalysts: 100 mgL−1, time: 60min) the catalysts exhibited excellent performance, with high degradation rate, magnetic power, easy recovery at the end, and efficient reusability (up to 5 cycles without any considerable loss in catalytic activity). A high magnetic character offers its easy separation from aqueous systems using an external magnet. Moreover, the combined effects of experimental variables were assessed simultaneously and justified using response surface methodology (RSM).


Introduction
Pesticides have been widely used worldwide to meet the food demands, but these exhibit persistency, bioaccumulation, and easy transportation over long distances from their sources, thus posing a serious threat to environmental habitats [1]. Neonicotinoid is a fast-growing class of commercialized pesticides. They are derived from nicotine and are used as alternatives to synthetic, extremely hazardous pesticides [2]. The extensive use of these pesticides would cause serious threats to the terrestrial and aquatic environment [3]. These are water-soluble, photo-stable, and persistent to biological degradation. The active compounds and major by-products enable their transference in surface water as well as underground water. The extensive use of pesticides in the agriculture sector not only cide, pH, catalyst dose, oxidant concentration, and UV-light exposure time were studied to enhance the process's efficiency. Ferrites and their GO composites were magnetically separable, and their reusability was studied for the degradation of pollutants cyclically. Further, three kinetic models were chosen for degradation study including the 1st order kinetic model, 2nd order kinetic model, and BMG kinetic model. The central composite design for response surface methodology was used as a statistical tool to understand the mutual effects of influencing parameters like catalysts dose, oxidant dose, and pesticide concentration.
This study aims to present useful scientific information on the effectiveness of magnetic composite based AOPs for the remediation of recalcitrant organic compounds especially neonicotinoid pesticide.

Results Characterization
Characterization (SEM, XRD, and FTIR) of magnetite and its GO-based catalyst, sonochemical synthesized, was precisely reported earlier [5]. As explained before, moderate ultrasonic irradiation involved in co-precipitation reaction, yielded smaller sized, magnetically improved Fe 3 O 4 particles with narrow size distribution. Figure 1a,b shows the SEM images of CoFe 2 O 4 and GO-CoFe 2 O 4 respectively, exhibiting the comparative morphologies of both (CoFe 2 O 4 and its composite). It is quite clear from the SEM images that the composite is formed due to the firm linkage of embedded ferrite cubical particles on the highly exposed surface of exfoliated graphene oxide. Successful composite synthesis is also supported by XRD peaks (Figure 1c) and FTIR spectra (Figure 1d). In the XRD pattern of CoFe 2 O 4 , the characteristic peaks at 35.64 • and 62.77 • corresponds to the (311) and (440) crystal planes of copper ferrite, whereas in GO-CoFe 2 O 4 , a broad shift of plane can be observed. The disappearance of GO peak in GO-CoFe 2 O 4 may be due to the reduction of rGO, or it may be due to the destruction of regular stacking of GO sheets by the crystal growth of CoFe 2 O 4 between the layers [26,27].
FTIR also confirmed the developed metal-oxygen bonds during the formation of ferrites. Two absorption bands appearing below 600 cm −1 are characteristic features of ferrites. The bands at higher and lower frequencies are assigned to stretching vibrations of tetrahedral metal ion-oxygen ion (M tet -O) and octahedral metal ion-oxygen ion (M Oct -O), respectively. While in composite, the band near 3400 cm −1 endorses the stretching vibration of the hydroxyl group present on the GO surface.
UV-Visible spectroscopy was carried out to check the bandgap energies of catalysts using Tauc plot method. The results obtained are presented in Figure 2. The band gap energies (in eV) of Fe 3 O 4 , GO-Fe 3 O 4 , CoFe 2 O 4 , and GO-CoFe 2 O 4 were found to be 2.35, 2.76, 2.56, and 2.97, respectively. The increase in band gap energies from metal ferrites to their graphene oxide composites was observed [28,29]. This ensures the better charge (electron hole pair) separation in the composites and results in improved photocatalysis as compared to the pristine metal ferrites.  Considering pH as one of the influential parameters in catalysis, 7 Acetamiprid solutions (10ppm each) with pH values determined initially (2 to 8) were selected. The pH of different solutions was maintained using 0.1 M hydrochloric acid and 0.1 M sodium hydroxide solutions. In Figure 3a, the obtained results in terms of % degradation as a function of pH have been presented. It can be noticed that all the catalysts (Fe 3 O 4 , GO-Fe 3 O 4 , CoFe 2 O 4 , and GO-CoFe 2 O 4 ) put their maximum degradation potential at 3 pH (highly acidic condition). The catalyst's degradation potentials (in all cases) have been dropped when approaching alkaline pH from pH 3 (e.g., in case of Fe 3 O 4 57% (at pH 3) to 21% (at pH ≥ 4), GO-Fe 3 O 4 65% (at pH 3) to 18% (at pH 8), CoFe 2 O 4 40% (at pH 3) to 18% (at pH 6), and GO-CoFe 2 O 4 27% (at pH 3) to 5% (at pH ≥ 7)). At higher pH (more than 7), a gradual decrease in catalytic activity is due to the unwanted reaction of ferrous ions and excess hydroxyl ions (present in the solution (Equation (1)). This reaction will lead to the formation of yellowish-brown ferric hydroxide sludge, which ultimately will cover the active catalyst' sites and hence contribute to the reduction of overall efficiency. This is the situation when surface-bound-transportation of molecules and other charge carriers is hindered.
Moreover, hydrogen peroxide molecules, at alkaline pH, would more likely be auto decomposed (Equations (2) and (3)). Therefore, no more active reagents (such as catalyst and hydroxyl radicals) would be available to conduct the degradation reaction effectively Moreover, hydrogen peroxide molecules, at alkaline pH, would more likely be auto decomposed (Equations (2) and (3)). Therefore, no more active reagents (such as catalyst and hydroxyl radicals) would be available to conduct the degradation reaction effectively [5].
when hydrogen ion concentration is very high in the pesticide solution, at acidic conditions (pH closer to 3), more hydroxyl radicals are susceptible to be attacked upon by H + ions present in the solution, forming a relatively stable specie H 3 O 2 + . Consequently here, during Fenton's reaction, the catalyst's performance is retarded, because hydroxyl radicals become limiting reactants. It is evident from Figure 3a that acetamiprid's degradation is highest at pH 3 so, it is taken as optimized pH (in all cases).

Effect of Oxidant Dose
In the heterogeneous photo-Fenton process, the role of oxidant (H 2 O 2 ) is also very decisive because it acts as an accelerator for the photocatalysts. The effect of oxidant was investigated using hydrogen peroxide (H 2 O 2 ) dose-ranging from 1.16 to 58 mM. The results are represented in Figure 3b. Here before the discussion, two opposing factors must be considered, i.e., (a) If oxidant in the photochemical reaction is added in a sufficient amount, it will absorb photons from the environment and help in promoting the rate of photolysis reaction occurring at the catalyst's surface (Equation (5)). Consequently, more hydroxyl radicals would be available for pollutant degradation. Hydrogen peroxide not only enhances the Fenton's reaction but also promotes the reusability of the catalyst (Equation (6)).
(b) On the other hand, hydroxyl radicals can efficiently react with hydrogen peroxide, so the excess of hydrogen peroxide will act as a hydroxyl radical scavenger (Equation (7)), which will lead to a decline in catalytic potential.
In the case of all catalysts ( (21.75 mM) was needed, because it has to struggle against the fast recombination of electron-hole pair (e --h + pair), owing to its lower bandgap (than magnetite). At the beginning of the reaction (from 1.16 mM of oxidant to its optimized value), with the increase in H 2 O 2 concentration, there is a gradual enhancement in the rate of reaction. While the further increase in the oxidant dose decreased the degradation rate due to the scavenging of · OH radicals by H 2 O 2 (not needed stoichiometrically) (Equation (8)). Peroxyl radicals formed in the equation do not have enough oxidation potential required for efficient Fenton process, as their rate constant is 2 × 10 4 M -1 s -1 . Therefore, they will lead to a negligible contribution to the degradation process.

Effect of Catalyst Dose
The influence of catalyst concentration on its degradation efficiency is represented in Figure 3c. In the present work, variable doses (0-200 mg/L) of catalysts have been studied to achieve optimum degradation. From Figure 3c, it has been observed that a higher value of degradation (for Fe 3 O 4 76%, for GO-Fe 3 O 4 85%, for CoFe 2 O 4 75%, and for GO-CoFe 2 O 4 90%) has been achieved at a catalyst dose of 100 mg/L (for each of four catalysts). Initially, a rapidly increasing trend of acetamiprid's degradation was observed by increasing the photocatalysts up to 100 mg/L, above which it did not promote the degradation potential of catalysts. From 0 to 100 mg/L dose range of catalysts, pesticide removal efficiency increases considerably. As with the increasing concentration of catalyst in the pesticide solution, more active sites will be available for the adsorption (accelerator and target molecule), modifications, and catalytic performance. Enhanced production of hydroxyl radicals and good accommodation of target molecules will be assisted on the grounds of more active sites (Equation (9)). Thus, it can be assumed that at 100 mg/L catalyst dose, there is a perfect balance attained among the three major components of the system (i.e., oxidant concentration, catalyst dose, and pesticide load).
After this, further increase approaching 200 mg/L of catalyst, the degradation rate was decreased because of the catalyst's agglomeration at its higher concentration. At this point, catalyst sheets start stacking over each other, thus leading to the presence of unexposed active sites, giving no contribution to Fenton's process. Moreover, this excessive addition of catalysts may lead to the blockage of photon penetration into the solution. In this case, photocatalytic activators have no more appropriate access to light, thus resulting in a negative impact on degradation. Moreover, if the amount of catalyst is enhanced too much and the balance between catalysts to pollutant ratio is disturbed, the in situ produced radicals are scavenged by excess catalytic species.
Graphene oxide-based composites proved more efficient even at a high dosage of catalyst because graphene oxide not only provided conductive support to ferrites but also prevented the catalysts from agglomeration [30].

Effect of Pesticide Load
As ppm levels of pesticide were proved hazardous, a degradation study was also conducted on small amounts (ppm level) of acetamiprid. For this purpose, varying concentrations of acetamiprid (2 to 16 ppm), added in simulated wastewater, were treated using catalysts individually. Results are reported in Figure 3d. Catalysts effectively (80%) degrade 10 ppm solution of pesticide. Nearly 100% of degradation was achieved in the case of 2 to 8 ppm of acetamiprid as reflected by Figure 3d. As the short-lived hydroxyl radicals (lifetime = a few nanoseconds) can only react where they are produced in solution, there will be an enhanced probability of collision between pesticide molecule and the activator when there is an increase in Acetamiprid molecules per unit volume. However, as pesticide dose exceeds beyond 10ppm up to 16ppm, the rate of degradation sharply declines. Because more pollutant molecules are added in wastewater, more active sites are occupied, giving no space for the reaction responsible for the formation of surface-bound reactive oxygen species. Secondly, photons uptake by more concentrated pesticide solution will decrease the availability of photons for activation of catalyst surface (production of hydroxyl radicals over the surface of catalyst). It will also disturb the proper balance in oxidant to pollutant ratio, which imparts a negative impact on degradation reaction. Secondly, the molar extinction coefficient of Acetamiprid is 25 × 10 3 Lmol −1 cm −1 , so increasing Acetamiprid concentration will lead to wastage of incident light for pesticide molecule excitation. Ultimately, the solution will become impermeable to the coming photons.

Effect of Irradiation Time
Up till now, acetamiprid's degradation reaction conditions, other than time, have been optimized, to get the highest output in terms of degradation. Now, the time, for which pesticide solution is irradiated by UV (254 nm), should be optimized, enhancing the economic feasibility of the process. It is investigated under optimized conditions of pH, oxidant dose, pesticide load, and catalyst dose, by varying irradiation time from 15 to 120 min. At these fixed time intervals, specified in Figure 3e, the aliquots (of treated samples) were taken out and their absorbances reflected the extent of acetamiprid's degradation. It is clear from Figure 3e that, at the initial stage rate of the degradation process, it sharply increases, but as the process proceeds, the rate becomes slower. Thus, the specific time needed by the active sites to fully degrade the pollutant is 60 min (in the case of all catalysts). The declining rate of reaction reflects that with time during the reaction, (a) hydroxyl radicals are being consumed speedily, while are being regenerated in situ through a slower process; (b) more hydroxyl ions are generated in the medium which affects pH; (c) these generated hydroxyl ions react with ferrous ions and suppress the original Fenton reaction because of limited available active sites on the surface of catalyst; and (d) if ferrous ions are rapidly being oxidized to ferric ions, Fe(OH) 3 sludge will be produced. This sludge along with other negative impacts will hinder the photon penetration into the solution and their proper access to the catalyst's surface (where degradation is carried on) [5].

Reusability and Stability of Catalysts
The extraordinary performance of these selected catalysts is also linked to their magnetic property, durability, low catalyst deterioration leading to metal leaching in water bodies, and efficient reusability. The stability of catalysts was investigated by performing successive trials of the used catalysts separately. To do so, used catalysts were magnetically separated by applying an external magnetic field, washed thoroughly with distilled water and ethanol, dried in an oven at 60 • C, weighed, and tested against untreated pesticide solution. The results are shown in Figure 3f. It is evident from the Figure that the catalytic activities of all catalysts (especially GO-based composites) did not drop considerably even after 5 runs. Moreover, the GO-supported catalysts (GO-Fe 3 O 4 , GO-CoFe 2 O 4 ) showed enhanced stability and efficiency (more than 65% catalytic power at the 5th run). Thus, the GO-based composite formation enhanced their efficiency, magnetic recoverability, stability, and reusability against acetamiprid remediation. The iron leaching of all catalysts, after each reusability run, was checked using atomic absorption spectroscopy, and the results obtained are presented in Table 1. The low iron leaching values (far below the European Union Standard i.e., 2.0 mg/L [12]) suggest that the heterogeneous catalysts are stable towards metal leaching from solid to liquid state.

Radical Scavenging Test
The photodegradation of organic pollutants is carried out with reactive species like hydroxyl radicles, holes, electron, etc. Therefore, radical scavenging experiment was performed to find out the key radicals involved in photodegradation of pesticide [31][32][33][34]. The 5 mM of each DMSO (dimethyl sulfoxide), EDTA (ethylene-diamine-tetra-acetate), and K 2 Cr 2 O 7 (potassium dichromate) were used to scavenge OH radicals, holes, and electron, respectively. The experiments were carried out under UV irradiations. The results obtained are presented in  Depending upon the effectiveness of hydroxyl radicals, the possible mechanism for the heterogeneous photo-Fenton reaction is as follows: First of all, pollutants present in wastewater are chemisorbed onto the surface of the catalyst. Hydrogen peroxide reacts with the catalyst's iron species, and as a result, highly reactive hydroxide radicals are produced (Equations (11) and (12)). These produced hydroxide radicals attack the surface-linked pollutant molecules, resulting in their photocatalytic degradation (Equation (13)).
OH + organics chemisorbed → degraded products The photo-Fenton-like catalytic process is based on the traditional Fenton process assisted with light radiations. The enhanced acceleration of OH ions produced during the Fenton reaction (Equation (11)) can be achieved with the introduction of the light source, which benefits from the synergistic effect of photocatalysis and the Fenton process [35,36].

Kinetics of Photo-Degradation Reaction
Three kinetic models first-order, second-order, and BMG were studied for the degradation of acetamiprid via the Fenton oxidation process (FOP) [37]. These three kinetic models are usually reported for the degradation of organic pollutants owing Fenton oxidation processes (FOP). Gallard and De Laat [38] suggested that FOP should be a simple first order kinetic process, whereas Guedes [39] reported that it should be the second order process. Behnajady and coworkers [40] proposed the mathematical model to predict the chemical reaction kinetics and the performance of FOP under different conditions.
The expression for each model is presented in Equations (14)- (16). The model graphs are presented in Figure 5. The values of correlation coefficient and rate constants are presented in Table 2.  Considering the correlation coefficient values of the reaction under FOP, the BMG model fitted best to the experimental data as the highest R 2 was obtained if compared with first-order and second-order models. It can be concluded from Table 2 that the corresponding regression results with a high correlation coefficient (R 2 ), from 0.8474 (first order) to 0.9971 (BMG) and 0.8397 (first order) to 0.9911 (BMG) for GO-Fe 3 O 4 and GO-CoFe 2 O 4 best suited for BMG kinetic model.
The oxidative degradation of organic pollutants by the Fenton process usually occurs in two steps: the fast and the slower ones. The fast reactive stage was initiated by the availability of hydroxyl radicals, which consumed vigorously during the reaction. In the later stage, ferric ions also react with hydrogen peroxide, and consequently, peroxyl radicals were formed. Peroxyl radicals are other weaker radicals. Apparently, in the reaction hydrogen peroxide is the limiting reactant because with time hydrogen peroxide is consumed rapidly. Here, the rate of formation of hydroxyl radical is slower than its consumption. As the reaction followed two-step patterns, i.e., the very fast and the slower one, neither first-order nor second-order kinetic model could describe the reaction kinetics perfectly. The value of the regression coefficient (R 2 ) (0.9971 and 0.9911 GO-Fe 3 O 4 and GO-CoFe 2 O 4 ) justified the fitness of the BMG model.

Optimization through Response Surface Methodology (RSM)
Optimized ranges of influential (selected) parameters were also found out using Response Surface Methodology (RSM). It is a comprehensive statistical tool that helps in identifying the possible interactions among selected parameters. Central Composite Design (CCD) was selected to evaluate the interactive influence of three selected variables (oxidant dose, catalyst dose, and pesticide load) [5]. Ranges of variables were set as predicted by conventional optimization study (single factor influence).  Table 4 (in the case of GO-CoFe 2 O 4 ). These represent the individual effects of linear (A, B, and C) and quadratic terms (A 2 , B 2 , C 2 ) as well as the first-order interaction effects (AB, AC, and BC). A high correlation between the observed and predicted values is reflected by adjusted R 2 values (closer to 1) [5]. The influence of parameters individually as well as in combination, on the degradation of the acetamiprid is clear from response surfaces and ANOVA. The adequacy of the model to present the experimental results were justified by significantly large values of R 2 and adj R 2 . A non-significant lack of fit (p-value > 0.05) warranted the reliability of the proposed CCD model. Based on the CCD matrix, different combinations of selected independent variables (catalyst dose (mg/L), oxidant dose (mM), and pesticide load (ppm)) were set to perform a photo-degradation experiment. The response (%age degradation) is reported along with 3D response surfaces ( Figure 6). The response (% degradation) varied from 11.6 to 88% (in the case of GO-Fe 3  where Y is the response (in terms of % degradation), and A, B, and C represent three selected independent variables, i.e., catalyst dose, oxidant dose, and pesticide concentration, respectively.  The study of contour and response surface plots helped in comprehending the optimization and effects of the selected independent variables on the degradation process. The results are shown in Figure 6a,b. The combined effect of oxidant dose and catalyst dose is shown in Figure 6a. Here, the third variable is kept at an optimized value. It depicts in both cases that there is a threshold value of oxidant to catalyst ratio, above and below which catalysts do not perform efficiently. However, the general trend is that the optimum point (maximum degradation) seemed to be in the mid of the selected ranges. With an increase in catalyst dose, degradation of acetamiprid was increased at moderate oxidant concentration. Very high and very low oxidant doses impart severely low degradation efficiency even if the amount of catalyst is high [5]. The mutual effect of catalyst dose and acetamiprid concentration on the degradation process was studied and reported in Figure 6c,d, keeping oxidant dose fixed. The oxidation potentials of catalysts were enhanced with an increase in catalyst dose and a decrease in acetamiprid concentration. A combined effect in numerical value was also given in terms of the polynomial quadratic, coded equation, as a coefficient. To further enhance the degradation efficiency, more oxidant is required to initiate the oxidative reaction on the surface of the passive catalyst. An interactive study of impacts of oxidant dose and pesticide concentration on degradation of acetamiprid has been represented in Figure 6e

Preparation of Graphene Oxide and Catalysts
Modified Hummer's method was used for the synthesis of Graphene oxide, as reported earlier [5]. Here, the graphitic oxide was used as a carbon source, and KMnO 4 , H 2 O 2 , H 2 SO 4 were used as oxidizing agents. The catalyst was synthesized by ultrasonic impregnation of ferrite particles using Graphene Oxide (GO) as support material where FeCl 3 .6H 2 O and FeSO 4 .7H 2 O act as iron precursors (Fe 3+ and Fe 2+ , respectively) [41]. Onepot ultrasonically assisted reverse co-precipitation method was followed for the synthesis of magnetite. For this purpose, a fixed amount of ultra-sonicated GO was added into the mixed solution of iron precursors having Fe 2+ /Fe 3+ mole ratio of 0.5. Under highly alkaline conditions, GO-Fe 3 O 4 precipitates were prepared. For comparison, Fe 3 O 4 nanoparticles were also prepared following a similar procedure without addition of GO [42,43]. CoFe 2 O 4 -GO was prepared by adopting one-pot hydrothermal method in the presence of GO suspension [43,44].

Characterization of Catalysts
Catalysts (Fe 3 O 4, GO-Fe 3 O 4, CoFe 2 O 4, GO-CoFe 2 O 4 ) were characterized using XRD, FTIR, and SEM analysis. Powder x-ray diffractometer (PW1398, Philips, The Netherlands) with Cu-Kα radiation (λ = 1.5418 Å) was used for XRD analysis. Chemical bonding within the composites was determined by Fourier Transform Infrared spectroscopy (FT-IR, Thermo Nicolet). Scanning Electron Microscope (SEM; JSM5910 JEOL JAPAN) at E = 30 KV was used to investigate microstructures and morphologies of catalysts. The band gap energies of the prepared materials were estimated from the data obtained by UV-Visible spectrophotometer using Tauc plot method.

Degradation Experiment
The photocatalytic experiments were conducted under Ultraviolet light irradiation. UV (254nm) lamps (8 × 18 W) were used as a UV-light source (ZamZam micro technologies ZM144W) for the photo-Fenton degradation of organic compounds at room temperature. The solution samples were placed in an orbital shaker, and the distance between the lamp and test solution was fixed, to maintain constant intensity. Typically, 100 mL of test solution was used in the degradation experiments. The absorbances of pesticide solutions during the photo-Fenton process were measured individually, at regular intervals, using a double beam spectrophotometer. Different parameters like effect of pH (2-8), oxidant concentration (1.16-58 mM), catalyst dose (0-200mg/L), pesticide concentration (2-16 ppm), and contact time (15-120 min), for enhanced degradation of pesticide, were optimized. The range of influencing parameters was selected based on some preliminary experiments and from the literature already reported. The percentage (%) degradation was calculated by using the following formula: where C o and C refer to the initial and final concentrations of acetamiprid, respectively.

Kinetic Study of Degradation Reaction
Heterogeneous Fenton-like processes are quite complicated due to the involvement of multiple steps that contribute to the overall degradation reaction [45]. Three kinetic models were applied to the experimental data, i.e., first order, second order, and Behnajady-Modirashahla-Ghanbery (BMG).
Different kinetic models were derived in the form of a linear quadratic equation. First-order kinetics ln Second-order kinetics Behnajaday-Modrishahla-Ghanbery model Here, C t , C o , k 1 , k 2 , t, m, and b are the concentration of pesticide at the time "t", at the time "0"; the rate constant for the first-order reaction, for second-order reaction; time and constants in BMG models which are related to the maximum oxidation capacity and kinetics of the reaction, respectively. The fitness of the model was justified through Linear regression analysis (R 2 value).

Optimization Using Response Surface Methodology (RSM)
Interactions among the influential parameters (classically studied and observed in this paper) were studied through RSM. It is an amalgamated tool involving statistical and mathematical techniques, which empirically evaluates the correlation among several controllable experimental parameters and their reproducible results simultaneously. It is a modeling technique that assists in predicting the simultaneous impact of two or more variables (a) performing statistically designed experiments, (b) estimating the coefficients in a mathematical model, (c) predicting the cumulative response, and (d) checking the adequacy of the model. Central Composite Design (CCD) sufficiently informs about data fitness with a relatively lesser number of runs, so by reducing the overall cost of the experiment [5]. Three independent variables, as oxidant concentration, catalyst dose, and pesticide load, were chosen independent variables, based on the classical study and %age Acetamiprid's degradation was the dependent response, while other parameters like pH, irradiation time, and UV light were kept constant. There was a total of seventeen experimental runs, consisting of eight factorial points, three central points, and six axial points. Five levels were chosen for each independent variable (i.e., xi = −1.68, −1, 0, 1 and 1.68). Correlation between independent and response variables was interpreted by the Least Square Method (LSM) following the second-order model.
where Y is the response, β 0 is a coefficient with a specific numerical value, βi, βii, and βij belong to the coefficients regarding linear, quadratic, and interaction effects, respectively, while n is the number of independent variables and ε (Epsilon) is random error. Statistical computation of F-value, at probability (p) of 0.05, reflects the validity and suitability of polynomial models. Fitness of regression coefficients represented in Analysis of Variance (ANOVA).

Conclusions
Acetamiprid was selected as a model pollutant. The co-precipitation method has opted for the synthesis of magnetic Fe 3 O 4 particles, and the hydrothermal method has opted for the synthesis of CoFe 2 O 4. While respective composite was prepared by doping graphene oxide, prepared by Hummer's method. Magnetite was proved as a potential catalyst, but composite enhanced its degradation potential. As a result of composite formation, the catalytic activity was enhanced by inhibiting the magnetite's agglomeration, and thus, active sites are exposed to oxidant as well as pollutants present in water. It also leads to the catalyst's uniform dispersion. Moreover, the efficient separation was conducted by applying an external magnetic field. This easy post-treatment made it an attractive and feasible technique in terms of large-scale applicability. Thus, the development of such a promising catalyst offers not only high degrading activity to complete mineralization. Low iron leaching, complying with the European Union directives for the discharge of treated waters, contributes to the catalyst's stability and reusability. Mineralization of 100% can be achieved by focusing on the development of coupled/merged techniques of AOPs, light, and acoustic cavitation because these will help in minimizing the shielding effect, and consequently, light penetration will be enhanced. Thus, wastewater remediation using magnetically assisted separation is an important consideration for cost-effectiveness and less time consumption.