Enhancing the Performance of GaN-Based Light-Emitting Diodes by Incorporating a Junction-Type Last Quantum Barrier

: In this paper, an n-i-p-type GaN barrier for the final quantum well, which is closest to the p-type GaN cap layer, is proposed for nitride light-emitting diodes (LEDs) to enhance the confinement of electrons and to improve the efficiency of hole injection. The performances of GaN-based LEDs with a traditional GaN barrier and with our proposed n-i-p GaN barrier were simulated and analyzed in detail. It was observed that, with our newly designed n-i-p GaN barrier, the performances of the LEDs were improved, including a higher light output power, a lower threshold voltage, and a stronger electroluminescence emission intensity. The light output power can be remarkably boosted by 105% at an injection current density of 100 A/cm 2 in comparison with a traditional LED. These improvements originated from the proposed n-i-p GaN barrier, which induces a strong reverse electrostatic field in the n-i-p GaN barrier. This field not only enhances the confinement of electrons but also improves the efficiency of hole injection.


Introduction
Nitride light-emitting diodes (LEDs) have garnered increasing attention and extensive amounts of research due to their low power consumption and compact size [1][2][3].One common problem facing GaN-based LEDs is that the electrons can be easily injected from the active regions into the p-GaN region, which decreases the recombination of the carriers within the active regions, owing to the high mobility and small effective mass of the electrons.This issue significantly limits these devices' performances.To solve this problem, a novel electron-blocking layer (EBL) made of AlGaN with a wide band gap was inserted among the active regions and the p-type GaN cap region [4][5][6][7][8].However, this method alone is not effective in suppressing the injection of the electrons to the p-type GaN cap layer.Moreover, it creates an obstruction within the movement of holes from the p-type GaN cap layer towards the active regions.To enhance the efficacy of hole injection from the p-GaN region into the active regions, concepts such as AlInGaN EBL [9], undope BGaN/BAlN EBL [10,11], Graded EBL [12,13], quantum barrier [14], triangular EBL [15], and band offset [16] devices have been reported.These works focused on finding a proper EBL, which in general required an additional hetero epitaxial deposition, making them difficult to realize due to the lattice mismatch.The EBL is primarily utilized for engineering the energy band of the multiple quantum wells (MQWs) in close proximity to the p-GaN cap layer, thereby enhancing both electron and hole concentrations and subsequently improving the electrical and optical characteristics of nitride LEDs [17][18][19][20].
The aforementioned studies show that researchers have enhanced the carrier injection efficiency by improving wider-bandgap EBL, but for GaN-based LEDs, it is not sufficient to optimize a single p-EBL.Alternatively, it is conceivable that a favorable polarization charge may exist at the interface where the final quantum barrier meets the EBL with a wider bandgap.This occurrence can be attributed to a negative difference in heterointerface polarization [21].The existence of this positive charge has an effect on bending the last quantum barrier bands, leading to a reduction in the effective electron barrier and an increase in the effective hole barrier.Consequently, it may significantly compromise both the electron blocking and hole injection processes, ultimately resulting in a diminished optical power and efficiency [22].As a result, many strategies aimed at improving the amount of droop utilize either an Al composition gradient [23][24][25] or a final barrier with a different thickness [23,26,27] as a workaround for this issue.In a previous study we reported highperformance green LEDs employing heterojunction-type last quantum barrier layers [28].However, the realization of this process is difficult due to lattice structure mismatch.Further investigations are necessary to determine a straightforward device structure that exhibits a mechanism that clearly leads to enhanced carrier injection and reduced current leakage.
In this study, we introduce a novel n-i-p-type GaN barrier to engineer the energy band structure.This n-i-p barrier is used for the last quantum well (QW) only, which is nearest to the p-type GaN cap region.The improvements in the hole injection efficiency and electron confinement of the LED with our newly designed barrier are demonstrated in simulations.In addition, this method can avoid any additional hetero epitaxial growth, which makes it easy to apply in practice.

Device Structure and Parameters
In this study, the InGaN/GaN MQW LED with a traditional GaN barrier developed in Ref. [29] was used as a reference.Its schematic cross section is shown in Figure 1.From the bottom to the top, the device structure consists of a sapphire substrate, an n-type GaN/Si layer with a concentration of 5 × 10 18 cm −3 and a thickness of 2 µm, five periods of GaN (12 nm)/In 0.15 Ga 0.85 N (3 nm) MQW regions, subsequently accompanied by a p-type Al 0.25 Ga 0.75 N:Mg EBL with a density of 3 × 10 17 cm −3 and a thickness of 25 nm, and a 0.12 µm p-type GaN/Mg cap layer with a density of 3 × 10 17 cm −3 .The dimensions of the device are 60 µm × 60 µm, forming a square shape.When the GaN barrier in the final QW is substituted with n-GaN (1 × 10 18 cm −3 )-i-GaN-p-GaN (5 × 10 18 cm −3 ), an LED with our proposed n-i-p GaN barrier is then formed, as shown in Figure 1.The thicknesses of the n, I, and p layers in the proposed barrier are identical at 4 nm.Therefore, the only structural difference between these two types of LEDs is the type of barrier used for the last QW.
heterointerface polarization [21].The existence of this positive charge has an effect on bending the last quantum barrier bands, leading to a reduction in the effective electron barrier and an increase in the effective hole barrier.Consequently, it may significantly compromise both the electron blocking and hole injection processes, ultimately resulting in a diminished optical power and efficiency [22].As a result, many strategies aimed at improving the amount of droop utilize either an Al composition gradient [23][24][25] or a final barrier with a different thickness [23,26,27] as a workaround for this issue.In a previous study we reported high−performance green LEDs employing heterojunction−type last quantum barrier layers [28].However, the realization of this process is difficult due to lattice structure mismatch.Further investigations are necessary to determine a straightforward device structure that exhibits a mechanism that clearly leads to enhanced carrier injection and reduced current leakage.
In this study, we introduce a novel n−i−p−type GaN barrier to engineer the energy band structure.This n−i−p barrier is used for the last quantum well (QW) only, which is nearest to the p−type GaN cap region.The improvements in the hole injection efficiency and electron confinement of the LED with our newly designed barrier are demonstrated in simulations.In addition, this method can avoid any additional hetero epitaxial growth, which makes it easy to apply in practice.

Device Structure and Parameters
In this study, the InGaN/GaN MQW LED with a traditional GaN barrier developed in Ref. [29] was used as a reference.Its schematic cross section is shown in Figure 1.From the bottom to the top, the device structure consists of a sapphire substrate, an n−type GaN/Si layer with a concentration of 5 × 10 18 cm −3 and a thickness of 2 µm, five periods of GaN (12 nm)/In0.15Ga0.85N(3 nm) MQW regions, subsequently accompanied by a p-type Al0.25Ga0.75N:MgEBL with a density of 3 × 10 17 cm −3 and a thickness of 25 nm, and a 0.12 µm p−type GaN/Mg cap layer with a density of 3 × 10 17 cm −3 .The dimensions of the device are 60 µm × 60 µm, forming a square shape.When the GaN barrier in the final QW is substituted with n−GaN (1 × 10 18 cm −3 )−i−GaN−p−GaN (5 × 10 18 cm −3 ), an LED with our proposed n−i−p GaN barrier is then formed, as shown in Figure 1.The thicknesses of the n, I, and p layers in the proposed barrier are identical at 4 nm.Therefore, the only structural difference between these two types of LEDs is the type of barrier used for the last QW.To examine the impact of the n-i-p GaN barrier on the device's performance, models of these two types of LEDs were built in Silvaco ATLAS software (version 5.19.20.R), and simulations of the band diagrams, the carrier concentrations, the light output power, the I-V curve, and the electroluminescence spectra were performed.In the calculations, an approximate value of 1 ns was assigned to the Shockley-Read-Hall (SRH) lifetime of the quantum wells (QWs).The coefficient for Auger recombination was assumed to be around 3.0 × 10 −29 cm 6 /s.The offset caused by fixed defects and additional interface charges was taken into account in 30% of the theoretical values.
The simulation model incorporates a k•p-Schrödinger solver for the examination of luminescence and carrier distribution in the quantum wells, alongside a semi-classical drift diffusion transport solver [30,31].It has undergone improvements to accurately capture the luminescence and transport characteristics specific to GaN-based MQW LEDs.A Newton solver is employed to achieve a combined solution of models in both real and energy domains.The Gummel iteration guarantees adherence to the k•p-Schrödinger model by ensuring self-consistency.
The equations that generally dictate the calculation of band gap energies in InGaN and AlGaN are provided below [32].
The determination of the permittivity of nitrides can be achieved by employing linear interpolations, which rely on the values obtained for binary compounds, to establish a relationship with the composition fraction denoted as x [35].
Polarization modeling is of the utmost importance in the evaluation of GaN-based devices' performance.Their highly polar nature results in a significant accumulation of fixed charges at the interfaces, leading to the generation of a substantial static field which is present within the LED.The overall macroscopic polarization P of InGaN (AlGaN) is defined as the combination of the spontaneous polarization P SP in the equilibrium lattice and the piezoelectric polarization P Pi induced by strain.The total polarization, P, is given by: P = P SP + P Pi where P SP is specified in Table 1.Ternary material values are obtained through linear interpolation based on the values of the binary materials.The piezoelectric polarizations of InGaN and AlGaN are contingent upon the strains present within the materials, which can be mathematically expressed as follows [36,37]: where e 31 and e 33 represent piezoelectric constants, C 13 and C 33 denote the elastic constants, and a 0 corresponds to the wurtzite lattice constant (a s is the substrate value).The material parameters for binary compounds are provided in Table 1.In the case of ternary compounds, a linear interpolation method can be employed to estimate these values.
The physical parameters set in our simulation are justified by reproducing the experimental results in [29], as shown in Figure 2. The simulated results align harmoniously with the measurements, thereby validating the chosen physical parameters.The physical parameters set in our simulation are justified by reproducing the experimental results in [29], as shown in Figure 2. The simulated results align harmoniously with the measurements, thereby validating the chosen physical parameters.

Light Output Power
The light output power performances of these two types of LEDs have been calculated and compared, as depicted in Figure 3.It is evident that the incorporation of an n−i−p GaN barrier greatly enhances the luminous output capability of the LED, across all levels of current injection.With an n−i−p GaN barrier, the output power density of the LED is increases by 105% in contrast with the traditional one at an injection current density of 100 A/cm 2 .

Light Output Power
The light output power performances of these two types of LEDs have been calculated and compared, as depicted in Figure 3.It is evident that the incorporation of an n-i-p GaN barrier greatly enhances the luminous output capability of the LED, across all levels of current injection.With an n-i-p GaN barrier, the output power density of the LED is increases by 105% in contrast with the traditional one at an injection current density of 100 A/cm 2 .

Energy Band Diagrams
To investigate the carrier transport in LEDs, simulations of the band diagram have been performed.The band diagrams of the LEDs, both with a traditional GaN barrier and an n−i−p GaN barrier, were simulated and results obtained at an injection current density of 40 A/cm 2 , as depicted in Figure 4.It is evident that, in the case of a traditional GaN barrier, the effective valence band barrier height for the holes is 312 meV, as depicted in Figure 4a.And in the case of an n−i−p GaN barrier, the barrier height for the holes in the

Energy Band Diagrams
To investigate the carrier transport in LEDs, simulations of the band diagram have been performed.The band diagrams of the LEDs, both with a traditional GaN barrier and an n-i-p GaN barrier, were simulated and results obtained at an injection current density of 40 A/cm 2 , as depicted in Figure 4.It is evident that, in the case of a traditional GaN barrier, the effective valence band barrier height for the holes is 312 meV, as depicted in Figure 4a.And in the case of an n-i-p GaN barrier, the barrier height for the holes in the valence band is found to be 285 meV, as depicted in Figure 4b.This means that the holes encounter a much lower barrier height in the LED with an n-i-p GaN barrier than in the traditional GaN barrier.Therefore, with an n-i-p GaN barrier, the holes can move from the cap layer to the active regions easier, resulting in a higher efficiency of injecting holes.It is clear that incorporating an n-i-p GaN barrier leads to an increased effective potential barrier height being experienced by the electrons in the conduction band.This increased electron barrier height can effectively suppress the electron leakage from the QWs to the p-type cap region.In summary, the LED with an n-i-p GaN barrier shows significantly improved carrier transport not only in the confinement of electron but also in the injection of holes.
barrier for the last quantum well.

Energy Band Diagrams
To investigate the carrier transport in LEDs, simulations of the band diagram have been performed.The band diagrams of the LEDs, both with a traditional GaN barrier and an n−i−p GaN barrier, were simulated and results obtained at an injection current density of 40 A/cm 2 , as depicted in Figure 4.It is evident that, in the case of a traditional GaN barrier, the effective valence band barrier height for the holes is 312 meV, as depicted in Figure 4a.And in the case of an n−i−p GaN barrier, the barrier height for the holes in the valence band is found to be 285 meV, as depicted in Figure 4b.This means that the holes encounter a much lower barrier height in the LED with an n−i−p GaN barrier than in the traditional GaN barrier.Therefore, with an n−i−p GaN barrier, the holes can move from the cap layer to the active regions easier, resulting in a higher efficiency of injecting holes.It is clear that incorporating an n−i−p GaN barrier leads to an increased effective potential barrier height being experienced by the electrons in the conduction band.This increased electron barrier height can effectively suppress the electron leakage from the QWs to the p−type cap region.In summary, the LED with an n−i−p GaN barrier shows significantly improved carrier transport not only in the confinement of electron but also in the injection of holes.

Carrier Concentration
From the above band diagram analysis, it can be inferred that the n-i-p GaN barrier enhances hole injection.To verify this, we have studied the carrier concentrations in the active regions and compared the distributions of holes and electrons under DC bias. Figure 5 shows the calculated hole and electron distributions of these two types of LEDs at a current density of 40 A/cm 2 .The reference point for the relative position is established at the uppermost layer of p-GaN, directed in a downward vertical orientation towards the MQWs.As expected, the LED featuring an n-i-p GaN barrier exhibits significantly elevated hole and electron concentrations compared to the LED employing a traditional GaN barrier.In the case of an n-i-p GaN barrier, the peak hole concentration can reach 6.0 × 10 18 cm −3 in the first QW.However, in the case of a traditional GaN barrier, the peak hole concentration is only 2.2 × 10 18 cm −3 in the first QW, as depicted in Figure 5.It is evident that the electron concentrations in the first QW are also improved with the n-i-p GaN barrier.Similar trends were observed for the other four QWs, although these are not shown in this paper.
active regions and compared the distributions of holes and electrons under DC bias.Fig-ure 5 shows the calculated hole and electron distributions of these two types of LEDs at a current density of 40 A/cm 2 .The reference point for the relative position is established at the uppermost layer of p−GaN, directed in a downward vertical orientation towards the MQWs.As expected, the LED featuring an n−i−p GaN barrier exhibits significantly elevated hole and electron concentrations compared to the LED employing a traditional GaN barrier.In the case of an n−i−p GaN barrier, the peak hole concentration can reach 6.0 × 10 18 cm −3 in the first QW.However, in the case of a traditional GaN barrier, the peak hole concentration is only 2.2 × 10 18 cm −3 in the first QW, as depicted in Figure 5.It is evident that the electron concentrations in the first QW are also improved with the n−i−p GaN barrier.Similar trends were observed for the other four QWs, although these are not shown in this paper.The insert in Figure 5 shows the profiles of leaked electronics for a traditional LED and our proposed LED.The traditional LED exhibits a significant electron current leakage, which is about three times higher than our proposed LED.Based on the results shown in Figure 6, it is evident that the electron leakage of the LED utilizing the n-i-p GaN final barrier is significantly lower compared to that of the conventional structure LED.This means that the electron reflection is much stronger than the electron crossing at the EBL.Consequently, our proposed LED structure exhibited a superior performance, as can be seen in Figure 3.The electron-blocking capabilities of the n-i-p GaN barrier were significantly enhanced, leading to a substantial reduction in leakage rate.These data validate that the incorporation of the n-i-p GaN barrier effectively suppresses electron leakage and enhances hole injection efficiency.Therefore, the active regions experienced a simultaneous rise in the concentrations of both electrons and holes.The insert in Figure 5 shows the profiles of leaked electronics for a traditional LED and our proposed LED.The traditional LED exhibits a significant electron current leakage, which is about three times higher than our proposed LED.Based on the results shown in Figure 6, it is evident that the electron leakage of the LED utilizing the n−i−p GaN final barrier is significantly lower compared to that of the conventional structure LED.This means that the electron reflection is much stronger than the electron crossing at the EBL.Consequently, our proposed LED structure exhibited a superior performance, as can be seen in Figure 3.The electron−blocking capabilities of the n−i−p GaN barrier were significantly enhanced, leading to a substantial reduction in leakage rate.These data validate that the incorporation of the n−i−p GaN barrier effectively suppresses electron leakage and enhances hole injection efficiency.Therefore, the active regions experienced a simultaneous rise in the concentrations of both electrons and holes.

Current-Voltage Curves
Figure 7 shows the I-V curves of these two types of LEDs.It is evident that the LED featuring an n-i-p GaN final barrier exhibits a reduced turn-on voltage, indicating an improved carrier transport.These results align with the analysis of the band diagram.When the biased forward voltage increases to approximately 4.0 V, the corresponding current densities of traditional and our proposed LED reach 17.4 and 42.212 A/cm 2 , respectively.Due to the reduced series resistance of the n-i-p GaN final barrier in our proposed LED, the current density of this new structure LED is higher than that of traditional one.It was found that the electrical characteristics were hampered by adding the n-i-p-type doping from our proposed LED.
Electronics 2024, 13, x FOR PEER REVIEW

Radiative Recombination Rates
Figure 8 presents the carrier radiative recombination rate of the two LEDs, helps identify the confinement of carriers within the active region caused by the inc of a last GaN barrier layer with an n−i−p configuration.Compared to the traditiona the radiative recombination rates of our proposed LED were increased to 623%, 507%, 281%, and 248% in QW5, QW4, QW3, QW2, and QW1, respectively, at a c injection density of 40 A/cm 2 .When a significant quantity of holes, each contain equivalent number of electrons, are introduced into the active region, the trapped c will experience accelerated recombination within the MQWs.This phenomenon is ularly evident in the final quantum well (QW5), which is located closer to th n−i−p−type GaN barrier and AlGaN EBL.These findings align closely with the afor tioned results.We can infer that the carrier injection and transport in our propose structure are effectively enhanced by the last barrier being n−i−p−type GaN, leadin accelerated recombination process towards the final quantum well (QW5).It is no thy that, while the increase in radiative recombination rate in QW4 is the highest, stitutes a relatively minor proportion compared to the final quantum well (QW5) in of the overall radiative recombination.Consequently, the final quantum well (QW5) the most significant influence.

Radiative Recombination Rates
Figure 8 presents the carrier radiative recombination rate of the two LEDs, which helps identify the confinement of carriers within the active region caused by the inclusion of a last GaN barrier layer with an n-i-p configuration.Compared to the traditional LED, the radiative recombination rates of our proposed LED were increased to 623%, 906%, 507%, 281%, and 248% in QW5, QW4, QW3, QW2, and QW1, respectively, at a current injection density of 40 A/cm 2 .When a significant quantity of holes, each containing an equivalent number of electrons, are introduced into the active region, the trapped carriers will experience accelerated recombination within the MQWs.This phenomenon is particularly evident in the final quantum well (QW5), which is located closer to the last n-ip-type GaN barrier and AlGaN EBL.These findings align closely with the aforementioned results.We can infer that the carrier injection and transport in our proposed LED structure are effectively enhanced by the last barrier being n-i-p-type GaN, leading to an accelerated recombination process towards the final quantum well (QW5).It is noteworthy that, while the increase in radiative recombination rate in QW4 is the highest, it constitutes a relatively minor proportion compared to the final quantum well (QW5) in terms of the overall radiative recombination.Consequently, the final quantum well (QW5) exerts the most significant influence.
thy that, while the increase in radiative recombination rate in QW4 is the highest, it stitutes a relatively minor proportion compared to the final quantum well (QW5) in te of the overall radiative recombination.Consequently, the final quantum well (QW5) ex the most significant influence.

Electroluminescence Spectra
The calculated electroluminescence (EL) spectra for both devices at current densities of 40 A/cm 2 , 60 A/cm 2 , and 80 A/cm 2 are depicted in Figure 9.A stronger EL intensity is observed for the LED with an n-i-p GaN barrier than for the LED with a traditional GaN barrier under all three current injection density conditions.In contrast to the conventional LED, the maximum intensities of our new structure LED rise to 124.6%, 111.6%, and 113.1% at current injection densities of 40 A/cm 2 , 40 A/cm 2 , and 40 A/cm 2 , respectively.The enhanced EL intensity can be attributed to the enhanced carrier transport across the GaN barrier in the n-i-p structure.
Electronics 2024, 13, x FOR PEER REVIEW

Electroluminescence Spectra
The calculated electroluminescence (EL) spectra for both devices at current de of 40 A/cm 2 , 60 A/cm 2 , and 80 A/cm 2 are depicted in Figure 9.A stronger EL inten observed for the LED with an n−i−p GaN barrier than for the LED with a traditiona barrier under all three current injection density conditions.In contrast to the conven LED, the maximum intensities of our new structure LED rise to 124.6%, 111.6% 113.1% at current injection densities of 40 A/cm 2 , 40 A/cm 2 , and 40 A/cm 2 , respectivel enhanced EL intensity can be attributed to the enhanced carrier transport across th barrier in the n−i−p structure.

Electric Fields
In order to understand the underlying mechanism of carrier concentration distributions, it is necessary to analyze the electrostatic field in the final GaN barrier and the AlGaN EBL within these LED structures.The zoomed-in electric fields and energy band diagrams of the LEDs with an n-i-p GaN barrier and a traditional barrier at 40 A/cm 2 are depicted in Figure 10.The energy band at the last GaN barrier and AlGaN EBL interface undergoes a downward shift due to the influence of polarization effect, resulting from the presence of strong electric fields in conventional LEDs.This leads to an increase in the effective barrier height for hole injection and a decrease in that for electron injection, which may contribute to the less-than-optimal efficiency of hole injection and the noticeable electron leakage observed in GaN-based MQW LEDs.However, the downward band bending at the interface between the last barrier and AlGaN EBL is significantly reduced as a result of the opposing electric field generated by the n-i-p junction in the GaN layers of the final barrier.It is evident that the barrier height experienced by holes is decreased while that for electrons is enhanced, which improves the hole injection efficiency and suppresses the electron leakage.In summary, the above results indicate that the introduction of an n-i-p GaN barrier can dramatically improve the GaN-based LED's performance.

Conclusions
In summary, a comprehensive numerical analysis and comparison have been conducted on two distinct categories of GaN−based LEDs.One is an LED with a traditional GaN barrier for the last quantum well, and the other is an LED with our newly proposed n−i−p GaN barrier for the last quantum well.The light output power of the LED with the n−i−p GaN last quantum barrier is significantly improved by 105% when exposed to an injection current density of 100 A/cm 2 .Our research findings suggest that, by employing an n−i−p GaN barrier as the final quantum well, it is possible to enhance hole injection efficiency from the p−type GaN cap region into the active regions and effectively mitigate electron leakage from the active regions.Therefore, the carrier confinement within the active regions is improved.As a result, our newly devised barrier design exhibits remarkable enhancements in various aspects such as increased light output power, reduced turn−on voltage, and intensified EL emission intensity.The results obtained in this study present a novel approach for enhancing the efficiency of GaN−based LEDs.The suggested design can be easily implemented during the fabrication process of LEDs, eliminating any challenges associated with lattice mismatching that may arise during additional heterostructure growth.

Figure 1 .
Figure 1.Schematic diagrams depicting the LEDs with (a) a traditional GaN barrier and (b) an n−i−p GaN barrier for the last quantum well.

Figure 1 .
Figure 1.Schematic diagrams depicting the LEDs with (a) a traditional GaN barrier and (b) an n-i-p GaN barrier for the last quantum well.

Figure 2 .
Figure 2. Simulated and experimentally measured optical power of a reference InGaN/GaN LED as a function of injection current.

Figure 2 .
Figure 2. Simulated and experimentally measured optical power of a reference InGaN/GaN LED as a function of injection current.

Figure 3 .
Figure 3.Light output power for the LEDs with a traditional GaN barrier and with an n−i−p GaN barrier for the last quantum well.

Figure 3 .
Figure 3.Light output power for the LEDs with a traditional GaN barrier and with an n-i-p GaN barrier for the last quantum well.

Figure 4 .
Figure 4. Energy band diagrams of the LEDs with a traditional GaN barrier (a) and with an n-i-p barrier GaN (b) at 40 A/cm 2 .

Figure 5 .
Figure 5.The calculated hole and electron concentrations of the LEDs with a traditional GaN barrier and with an n−i−p GaN barrier at a current density of 40 A/cm 2 .

Figure 5 .
Figure 5.The calculated hole and electron concentrations of the LEDs with a traditional GaN barrier and with an n-i-p GaN barrier at a current density of 40 A/cm 2 .

Figure 6 .
Figure 6.Simulated electron and hole current density profiles of the LEDs at 40 A/cm 2 with and without the last n−i−p GaN barrier.

Figure 7
Figure 7 shows the I−V curves of these two types of LEDs.It is evident that the LED featuring an n−i−p GaN final barrier exhibits a reduced turn−on voltage, indicating an improved carrier transport.These results align with the analysis of the band diagram.When the biased forward voltage increases to approximately 4.0 V, the corresponding cur-

Figure 6 .
Figure 6.Simulated electron and hole current density profiles of the LEDs at 40 A/cm 2 with and without the last n-i-p GaN barrier.

Figure 7 .
Figure 7. I-V curves for the LEDs with a traditional GaN barrier and with an n−i−p GaN bar the last quantum well.

Figure 7 .
Figure 7. I-V curves for the LEDs with a traditional GaN barrier and with an n-i-p GaN barrier for the last quantum well.

Figure 8 .
Figure 8. Carrier relative radiative recombination rate at a current density of 40 A/cm 2 .

Figure 8 .
Figure 8. Carrier relative radiative recombination rate at a current density of 40 A/cm 2 .

Figure 9 .
Figure 9. Simulated EL spectra for the LEDs with a traditional GaN barrier and with an n−i− barrier for the last QW at a current density of 40 A/cm 2 ,60 A/cm 2 , and 80 A/cm 2 , respectively

Figure 9 .
Figure 9. Simulated EL spectra for the LEDs with a traditional GaN barrier and with an n-i-p GaN barrier for the last QW at a current density of 40 A/cm 2 ,60 A/cm 2 , and 80 A/cm 2 , respectively.

Electronics 2024 , 12 Figure 10 .
Figure 10.Zoomed−in energy band diagrams and electric fields of the LEDs with an n−i−p GaN barrier and a traditional barrier at a current density equivalent to 40 A/cm 2 .