Seismic Performance Enhancement of RC Columns Using Thin High-Strength RC Jackets and CFRP Jackets

: The existing non-ductile RC structures built prior to the 1960s–1970s were mainly con-ceived to carry only vertical loads. As a result, the columns of these structures demonstrate poor overall hysteresis behavior during strong earthquakes, dominated by brittle shear or/and premature excessive slipping of the inadequately lap-spliced reinforcement. In the present study, the effectiveness of two different strengthening systems (including either the wrapping of the columns by carbon-ﬁber-reinforced polymer textile or the use of thin high-strength reinforced concrete jackets), was experimentally and analytically investigated. The main variables examined were the strengthening material, the length of the lap splices and the amount of conﬁnement provided by the jackets. Three cantilever column specimens were constructed without incorporating modern design code requirements for preserving seismic safety and structural integrity. Subsequently, the specimens were strengthened and subjected to earthquake-type loading. Their hysteresis performances were compared, while also evaluated with respect to the response of two similar original specimens and the behavior of a control one with continuous reinforcement, tested in a previous study. The predictions of the proposed analytical formulation for the hysteresis behavior of the strengthened specimens were satisfactorily veriﬁed by the experimental results.


Introduction
The poor overall hysteresis performance of existing RC structures built in the 1960-1970s or earlier is invariably highlighted in the aftermath of every moderate-to-strong seismic event worldwide [1][2][3]. Meanwhile, the catastrophic partial or/and general collapse of these structures, which form the majority of the building stoke in most countries, is extremely common, with immense social and economic impact. This has triggered the continuous reformation of modern codes for the design of RC structures over recent decades, to incorporate parameters related to the controllable and hierarchically developed damage control philosophy (capacity design approach). Moreover, various conventional or innovative materials and strengthening schemes were used to improve the seismic behavior of the poorly designed structural members, while securing the ductile overall response of the strengthened structures.
Among other materials, fiber-reinforced polymers (FRPs) have been used for retrofitting, mainly for providing additional external flexural or shear reinforcement to RC columns [4][5][6][7], beams [8][9][10][11], beam-column joints [12][13][14][15][16][17] and slabs [18,19]. Seifi et al. [20] studied the effectiveness of the NSM technique for the flexural strengthening of columns, as well as the effectiveness of FRP jackets for the seismic retrofitting of beam-column joints. They concluded that the seismic performance of old framed RC structures was significantly improved when retrofitted, showing increased dissipating energy and lateral capacity. In the experimental work of Yalçin et al. [21], the effectiveness of the CFRP strengthening technique was examined, both for columns with continuous longitudinal reinforcement concrete jackets of 25 and 35 mm thickness for repairing and strengthening damaged RC columns of various cross-sectional dimensions. A group of specimens was retrofitted using RC jackets of normal concrete strength, while another group of columns was jacketed using ultra-high-performance, fiber-reinforced, self-compacting concrete with steel reinforcement. The response of the retrofitted columns of both groups showed a significant improvement with respect to the behavior of the original specimens.
As vertical members of the structural bearing system, the columns are exceptionally important for preserving the structural integrity, especially in the case of non-ductile framed RC structures. Moreover, the seismic behavior of the columns involves the influence of complex interacting phenomena which are not easily well understood, such as bond, lap splicing, confinement and shear. The influence of the aforementioned parameters becomes even more crucial in the case of the existing non-ductile RC structures, because they are coupled with significant structural deficiencies, such as the use of concrete with low compressive strength, plain steel reinforcement, inadequate lap splice length and poor confinement [28,29]. For this reason, the efficiency, reliability and range of application of the strengthening schemes depend on the satisfactory confrontation of these structural deficiencies. The authors have previously examined the seismic performance of CFRPstrengthened RC columns [7]. In the present research, the effectiveness of both the thin high-strength RC jacketing system and the CFRP jacketing system in improving the hysteresis performance of existing RC columns is experimentally and analytically investigated. The critical parameters studied herein were the strengthening material, the lap splice length (which was increased in the case of the CFRP-strengthened column with respect to previous research) and the amount of confinement provided by the jackets. Furthermore, an analytical formulation proposed by Kalogeropoulos and Tsonos [3,7] is used, to allow for the precise calculation of the ultimate shear capacity of the lap splice region and the prediction of the hysteretic behavior of the enhanced specimens.

Materials and Methods-Experimental Program and Strengthening Interventions
The columns of RC structures are indisputably critical members of the bearing system, and their resistance to both axial and horizontal (seismic) loads is directly related to their ultimate capacity and to the preservation of structural integrity. Therefore, during the reversed inelastic lateral deformations of strong seismic excitations, the columns of both the modern RC structures and the strengthened ones should ideally remain elastic or, at least, exhibit a ductile dissipating hysteresis response, characterized by flexural yielding of reinforcement in the plastic hinges. Damage to the beam-column joint regions should definitely be precluded, as well.
However, the aforementioned desirable seismic behavior can only be achieved if adequate confinement is provided to the column critical regions, to allow for the overstrength development before shear failure or/and premature slipping of the lap-spliced bars occurs. Nevertheless, this is not possible for most of the existing RC structures built prior to the 1960s-1970s, due to the poor confinement of the columns and the inadequate length of the lap splices. Furthermore, the concurrent use of plain steel bars and of concrete with a low compressive strength adversely affects the inelastic cyclic response. Thus, in earthquake prone areas, the pre-1960s-1970s RC structures are particularly vulnerable to exhibiting a rapidly degrading hysteresis behavior, dominated by brittle failure modes related to catastrophic partial or general collapse.
This can be effectively prevented by improving the shear capacity, ductility and deformability of the existing columns by means of external confinement. Along these lines, the effectiveness of CFRP jackets and of thin RC jackets of high strength was experimentally and analytically investigated herein. In particular, the efficiency of both retrofit schemes was evaluated by comparing the failure mode of the strengthened specimens with that of the corresponding original ones (which were tested in a previous work [3]), as well as by measuring the developed steel micro-strain values of the lap-spliced bars, which should exceed the steel yield stress to ensure that premature bar slipping is satisfactorily prevented and the nominal flexural moment capacity is eventually developed.
An experimental program was, therefore, conducted for three cantilever column specimens of 1:1.5 scale. The specimens were designated S 2 , G 1 and G 2 , while incorporating poor seismic details, typical of those found in columns of pre-1960s-1970s RC structures. The columns had S220 plain steel lap-spliced bars, poor shear reinforcement consisted of S220 90-degrees hook end ties of 8mm diameter spaced at 200 mm and concrete of low compressive strength. The latter was measured by using 150 × 300 mm 2 cylinder compression tests. Strength values of the concrete after twenty-eight days are shown in Table 1, while in Figure 1 and in Table 2 the dimensions and cross-section details of the specimens are illustrated. Moreover, the length of the lap splices equaled 200 mm in the case of specimen G 1 , and 240 mm in the case of specimens S 2 and G 2 . Specimen S 2 was pre-earthquake retrofitted by CFRP textile-wrapping of the column's critical region, while for the strengthening of specimens G 1 and G 2, a thin, high-strength RC jacket was used to provide the necessary external confinement to the critical region. The enhanced specimens were designated FS 2 , RG 1 and RG 2 , respectively. It should be noted that the hysteresis performance of FS 2 , RG 1 and RG 2 , was compared to the seismic response of two similar original column specimens, O 1 and O 2, and to that of a control specimen with continuous reinforcement, C 1 , which were tested in a previous work [3], to evaluate the effectiveness of the two strengthening schemes. Details about specimens O 1 , O 2 and C 1 are given in Tables 1 and 2, and in Section 3 of the present study.    The strengthening of specimen FS 2 required careful smoothening of the column surface. In particular, a spinning wheel was used to rub the surface in the circumference of the column along the critical height (600 mm) (see Figure 2c,d) and improve the contact with the CFRP textile, while also preventing potential damage to the textile from surface imperfections and protrusions. Furthermore, the column edges were curved with a radius of two and a half times the width of the concrete cover [30] to prevent tearing of the CFRP textile (see Figure 2c). Thereafter, the surface of the column was cleaned with air pressure and covered with epoxy resin. The textile was subsequently applied in the transverse direction with the fibers perpendicular to the column axis, to secure the effective Fibers 2021, 9, 29 6 of 24 confinement of the column's critical region (see Figure 2d). A trowel was used to press the CFRP textile to the surface of the column and removing the captured air. Thus, full integration of the textile to the resin matrix was achieved. The length of the CFRP jacked equaled 1700 mm, while the jacket started 20 mm above the foundation block of the specimen, to avoid potential damage to the CFRP textile layers during cycling [30,31]. The properties of the CFRP textile and of the epoxy resin are illustrated in Table 3. The required width, t J , of the CFRP jacket for providing the necessary confining stress to the critical region of the column, was calculated using Equation (1), which is introduced by the Greek Code for Interventions (GCI 2017) [31]. It was found that two layers of the CFRP textile should be wrapped around the column. In Equation (1), t J is the width of the CFRP jacket; A J is the cross-section area of the jacket; s w is the distance between stirrups or FRP strips; f yk is the yield stress of the plain lap-spliced bars; l s is the lap splice length; γ Rd , λ s , β and µ are coefficients equal to 1.5, 0, 1.0 and 1.0, respectively; σ Jd = Eε Jd is the design stress, which is equal to the yield stress σ Jd,max for the CFRP textile used to improve the load transfer mechanism between the lap-spliced bars; A b is the diameter of one lap-spliced bar.
In the case of specimens RG 1 and RG 2 , the necessary external confinement for ensuring yielding of the columns' inadequately lap-spliced reinforcement was provided by a thin RC jacket of high strength. Using a jack hammer, the concrete cover along the column critical height was chipped-away prior to the construction of the jacket. Subsequently, B500C steel bars of 8 mm diameter were placed in touch with the initial column, while they were formed as closed ties spaced at equal distances of 50 mm (see Figure 2a,b). Eventually, eleven ties were used to confine the critical column height (600 mm). Moreover, electrical resistant strain gages were attached to the ties of the jacket to allow for the measuring of the of steel strain value variations during cycling and ascertain if yielding of reinforcement was achieved. Then, the premixed, rheoplastic, non-shrink and non-segregating concrete of high strength was poured into the wooden formwork, which was constructed around the column of each specimen. The material characteristics of the thin RC jacket of high strength are illustrated in Tables 1 and 2. The seismic response of the enhanced columns, FS 2 , RG 1 and RG 2 was thoroughly experimentally investigated by conducting seismic tests in the test setup, which is located at the Laboratory of Reinforced Concrete and Masonry Structures of the Aristotle University of Thessaloniki (see Figure 3). The earthquake-type loading was intentionally performed with a strain rate corresponding to static conditions, which is lower than that of a dynamic earthquake event. As a result, the column specimens exhibited somewhat lower strengths with respect to the strengths they would exhibit if subjected to displacement histories similar to actual seismic events [32][33][34]. Two post-tensioned bars (bolts) were used to fix the strong foundation block of each column specimen to the reaction frame. Thus, both the horizontal and the vertical displacement, as well as the rotation of the foundation block, were effectively precluded (see Figure 3). Subsequently, the reversed lateral loading was applied by slowly displacing the column free end of the specimen. This was achieved by Fibers 2021, 9, 29 7 of 24 using a two-way actuator perpendicular to the column axis. The reversed inelastic deformations causes cumulative damage, while the seismic performance of the column is mainly demonstrated by the envelope curves. Thus, a constantly ascending lateral displacement history with one cycle per amplitude of displacement was adopted (see Figure 4) without considerable influence in the seismic performance of the specimens [35][36][37]. Meanwhile, a compressive axial force was applied to the column by a one-way actuator, which was laying on a rolling carrier (see Figure 3). The axial force was controlled to remain constant during cycling, equal to 150 kN. The seismic response of the enhanced columns, FS2, RG1 and RG2 was thoroughly experimentally investigated by conducting seismic tests in the test setup, which is located at the Laboratory of Reinforced Concrete and Masonry Structures of the Aristotle University of Thessaloniki (see Figure 3). The earthquake-type loading was intentionally performed with a strain rate corresponding to static conditions, which is lower than that of a dynamic earthquake event. As a result, the column specimens exhibited somewhat lower strengths  ing the seismic performance of the columns. For instance, the development of post-yield steel strain values presupposes that the bonding between the concrete and the steel bars is adequate to prevent early slipping of reinforcement. This, in turn, demonstrates the effectiveness of the strengthening scheme in improving the bond stress by means of the applied external confinement. Contrarily, the descending strain values during the consecutive cycles of lateral displacement are related to premature bond-slip failure and, hence, to the slipping of the lap-spliced bars.

Results
The cyclic response of the enhanced column specimens, FS2, RG1 and RG2, was thoroughly investigated, both experimentally and analytically, to assess the efficiency of the retrofit schemes examined herein, which included the CFRP-wrapping or the thin RC jacketing of the column critical region. Thus, the perceived lateral strength, peak-to-peak stiffness and energy dissipation capacity are subsequently evaluated based on the data acquired during the seismic tests (see Figures 5-7).

Interpretation of the Seismic Performance of the Strengthened Specimens
Due to numerous and significant structural deficiencies (for instance, the use of plain steel reinforcement and concrete of low compressive strength, the inadequacy of confinement and the short length of the lap splices which are located in the potential plastic hinge region), the columns found in RC structures of the 1950s-1970s possess poor deformability and low ductility, while also exhibiting a rapidly degrading hysteresis performance, related to catastrophic partial or general collapse. Thus, the efficiency and reliability of the applied retrofit scheme is primarily and inseparably related to the satisfactory transformation of the brittle failure mode to a more ductile one, by securing the full exploitation of the material properties and, hence, the development of the column's nominal flexural moment capacity.
For this purpose, it was considered of particular interest to evaluate the effectiveness The lateral displacement values of the column's load point were measured using a calibrated linear variable differential transducer (LVDT) throughout testing. Moreover, the resisted shear force values were constantly recorded to a data acquisition system by using a load cell (see Figure 3). Thereupon, the hysteresis loops of the specimens were drawn. The latter fully reflect the performance of the columns, while allowing for the interpretation of their seismic behavior. Furthermore, electrical resistant strain gages were installed on the inadequately lap-spliced bars of the columns, as well as on the ties of the thin, high-strength RC jackets. This instrumentation was used for measuring the variation in the steel strain values and to ascertain if yielding or/and strain-hardening of reinforcement occurs or not. This is crucial for evaluating the effectiveness of the retrofitting scheme in improving the seismic performance of the columns. For instance, the development of post-yield steel strain values presupposes that the bonding between the concrete and the steel bars is adequate to prevent early slipping of reinforcement. This, in turn, demonstrates the effectiveness of the strengthening scheme in improving the bond stress by means of the applied external confinement. Contrarily, the descending strain values during the Fibers 2021, 9, 29 9 of 24 consecutive cycles of lateral displacement are related to premature bond-slip failure and, hence, to the slipping of the lap-spliced bars.

Results
The cyclic response of the enhanced column specimens, FS 2 , RG 1 and RG 2 , was thoroughly investigated, both experimentally and analytically, to assess the efficiency of the retrofit schemes examined herein, which included the CFRP-wrapping or the thin RC jacketing of the column critical region. Thus, the perceived lateral strength, peak-to-peak stiffness and energy dissipation capacity are subsequently evaluated based on the data acquired during the seismic tests (see . The column specimen RG1 was pre-earthquake strengthened with a thin RC jacket of high-strength and it was subsequently subjected to eleven cycles of lateral displacement increments. The amount of confinement provided by the ties of the jacket was calculated using Equation (1), while the width of the jacket equaled 15 mm. The seismic behavior of RG1 is clearly reflected in the hysteresis loops shown in Figure 5a. The lateral bearing strength and peak-to-peak stiffness showed a mild reduction during cycling, while the cumulative hysteresis dissipated energy progressively increased significantly (see Figure 6).
During the first cycle of the earthquake-type loading, the main flexural crack was formed at the base of the column. This crack gradually dilated with the increase in lateral

Interpretation of the Seismic Performance of the Strengthened Specimens
Due to numerous and significant structural deficiencies (for instance, the use of plain steel reinforcement and concrete of low compressive strength, the inadequacy of confinement and the short length of the lap splices which are located in the potential plastic hinge region), the columns found in RC structures of the 1950s-1970s possess poor deformability and low ductility, while also exhibiting a rapidly degrading hysteresis performance, related to catastrophic partial or general collapse. Thus, the efficiency and reliability of the applied retrofit scheme is primarily and inseparably related to the satisfactory transformation of the brittle failure mode to a more ductile one, by securing the full exploitation of the material properties and, hence, the development of the column's nominal flexural moment capacity. Thereupon, excessive slipping of the lap-spliced reinforcement dominated the cyclic response of the specimen, causing a degrading overall hysteresis response.
(a) (b) Figure 6. (a) Peak-to-peak stiffness and (b) energy dissipation capacity of the strengthened specimens RG1, RG2 and FS2 with respect to specimens O1, O2 and C1 which were tested previously [3].
(a) (b) Figure 7. Plots of (a) load point displacement-versus-strength ratio for peak displacement of each cycle and (b) load point displacement-versus-energy dissipation ratio for peak displacement of each cycle of the strengthened specimens RG1, RG2 and FS2 with respect to specimens O1 and O2 [3]. Figure 6. (a) Peak-to-peak stiffness and (b) energy dissipation capacity of the strengthened specimens RG 1 , RG 2 and FS 2 with respect to specimens O 1 , O 2 and C 1 which were tested previously [3]. Thereupon, excessive slipping of the lap-spliced reinforcement dominated the cyclic response of the specimen, causing a degrading overall hysteresis response.
(a) (b) Figure 6. (a) Peak-to-peak stiffness and (b) energy dissipation capacity of the strengthened specimens RG1, RG2 and FS2 with respect to specimens O1, O2 and C1 which were tested previously [3].
(a) (b) Figure 7. Plots of (a) load point displacement-versus-strength ratio for peak displacement of each cycle and (b) load point displacement-versus-energy dissipation ratio for peak displacement of each cycle of the strengthened specimens RG1, RG2 and FS2 with respect to specimens O1 and O2 [3]. For this purpose, it was considered of particular interest to evaluate the effectiveness of the two examined strengthening schemes (which include either the CFRP-wrapping of the columns or the use of thin high-strength RC jackets) by comparing the hysteresis behavior of the strengthened columns with the seismic response of two corresponding original column specimens with inadequate lap splices, O 1 and O 2 , as well as with that of a control specimen with continuous reinforcement, C 1 , which were all tested in a previous work [3]; see Figures 5d, 6 and 7. The original columns, O 1 and O 2 , with lap splices of 200 and 240 mm length, respectively, demonstrated poor seismic performance dominated by premature excessive slipping of the inadequately lap-spliced bars, while they eventually collapsed due to the loss of axial load-carrying capacity. Contrariwise, the control specimen, C 1 , performed in a ductile manner when subjected to the same history of reversed inelastic lateral displacements. The column specimen RG 1 was pre-earthquake strengthened with a thin RC jacket of high-strength and it was subsequently subjected to eleven cycles of lateral displacement increments. The amount of confinement provided by the ties of the jacket was calculated using Equation (1), while the width of the jacket equaled 15 mm. The seismic behavior of RG 1 is clearly reflected in the hysteresis loops shown in Figure 5a. The lateral bearing strength and peak-to-peak stiffness showed a mild reduction during cycling, while the cumulative hysteresis dissipated energy progressively increased significantly (see Figure 6).
During the first cycle of the earthquake-type loading, the main flexural crack was formed at the base of the column. This crack gradually dilated with the increase in lateral displacement, resulting in increased post-yield strain of the lap-spliced steel bars. Nevertheless, no other crack was observed on the jacket surface until the end of testing (drift angle equal to R = 6.63%), as can be observed from the failure mode depicted in Figure 8a. Eventually, the specimen maintained 82.75% and 69.44% of its initial lateral bearing strength in the case of the push-half cycles and the pull half-cycles, respectively. Moreover, the confinement provided by the thin high-strength RC jacket effectively restrained the slipping of the longitudinal column reinforcement. The latter is clearly reflected in the plots of resisted shear force-versus-displacement, illustrated in Figure 5a, where it can be observed that increasing values of lateral strength are required for further displacing the column free end. For lateral drift angle values, R, higher than 4.59%, the unloading (lower) branch of the push half-cycles and the unloading (upper) branch of the pull half-cycles become almost horizontal, causing slight pinching of the hysteresis loops. This is attributed to the P-δ effect and the significant influence of the axial load.
During the first two cycles of the earthquake-type loading, the peak-to-peak stiffness of specimen RG 1 deteriorated sharply due to the concrete cracking, showing a reduction of 27.19%. Thereupon, the deterioration rate was slower, while, at the end of testing, the column maintained almost 18% of its initial stiffness (see Figure 6a).
The strengthened specimen RG 1 also showed a remarkable dissipating hysteresis behavior with constantly increasing values of dissipated seismic energy during the consecutive cycles of loading. In particular, the amount of dissipated seismic energy during the eleventh cycle of loading was increased by almost 318% with respect to the corresponding value during the first cycle (Figures 6b and 9c).
Ultimately, the strengthening scheme applied to specimen RG 1 effectively prevented the premature bond-slip failure and excessive bar slipping, while also securing the desirable ductile seismic performance of the column. Furthermore, the thin high-strength RC jacket substantially increased the lateral bearing strength of the enhanced column, RG 1 , with respect to the strength of the corresponding original column, O 1 , as can be observed in the plots of strength ratio for peak displacement of each cycle-versus-load point displacement, shown in Figure 7a. For instance, for lateral displacement of 45mm the strength ratio value RG 1 /O 1 equals 6.9 and 6.1 for the push half-cycle and the pull half-cycle, respectively. The same is also true in the case of the energy dissipation capacity of specimen RG 1 with respect to that of O 1 . In particular, as was obtained in the plots of energy dissipation ratio for peak displacement of each cycle-versus-load point displacement (see Figure 7b), the energy dissipation ratio value RG 1 /O 1 ranged from 1.74 for the first cycle of loading to 4.0 for the seventh cycle, when the original column, O 1 , literally collapsed.
It is worth noting that the hysteresis performance of the strengthened column, RG 1 , was also improved with respect to that of the control specimen, C 1 . In fact, RG 1 showed significantly increased lateral strength values with respect to specimen C 1 (see Figure 5d), due to the additional ties and the high-strength concrete of the thin RC jacket. An increase of almost 25% in the peak-to-peak stiffness values was also observed throughout testing (see Figure 6a). This results from the slight increase in the dimensions of the strengthened column's cross-section, but is mainly caused by the additional confinement provided by the thin high-strength RC jacket. Moreover, during the eleven cycles of the earthquake-type loading the mean value of the energy dissipation ratio, RG 1 /C 1 , equaled to 1.36. The latter According to the capacity design approach, RC structures should be able to withstand increased values of inelastic cyclic deformations during strong seismic excitations, to allow for the dissipation of a significant amount of kinetic energy through damping. Therefore, the structures should possess adequate displacement ductility to develop acceptable damage in the plastic hinges, while preserving the structural integrity and preventing partial or general collapse. Thus, the equivalent viscous damping is highly related to the deformability, while consisting of both the elastic and the hysteretic damping. The latter is crucial for the seismic response of RC structures and depends on the post-yielding characteristics of the structural members. Furthermore, the desirable ductile seismic performance requires an adequate energy dissipation capacity of the members, which, in turn, results in higher equivalent viscous damping ratios. Contrarily, the RC structural members with low energy dissipation capacity exhibit poor hysteresis behavior, while being susceptible to collapse due to the cumulative dissipated energy under small deformations. The enhanced specimen RG 2 was retrofitted similarly to the RG 1 . From the plots of resisted shear force-versus-displacement of RG 2 (see Figure 5b), it can be observed that both the lateral strength and the peak-to-peak stiffness showed a mild reduction during testing, while the energy dissipation capacity of the column gradually increased significantly during the consecutive cycles of the earthquake-type loading. The main flexural crack was formed at the base of the column during the first cycle. Thereafter, this crack dilated progressively with the increase in the reversed lateral displacements of RG 2 , causing excessive deformation of the lap-spliced column reinforcement. For a drift angle value equal to R = 4.59% a hairline flexural crack was formed on the jacket surface at the exact location where the lap splices of the reinforcement end, namely at a distance of 240 mm from the foundation block of the specimen. Propagation of this crack occurred in the circumference of the thin high-strength RC jacket, due to the gradual increase in lateral displacement values until the end of testing (see Figure 8b). However, no significant further dilation of this crack or disintegration of the concrete was observed. Thus, the thin RC jacket satisfactorily confined the column's critical region to prevent early bond-slip failure and excessive slipping of the bars, while the enhanced column, RG 2 , exhibited a ductile dissipating hysteresis behavior.
result, the cumulative equivalent viscous damping coefficient values of specimen RG1 were higher than the corresponding ones of column RG2, because the latter showed a lower energy dissipation capacity with respect to RG1 (see Figures 6b and 9b-d). Additionally, it is worth noting that specimen FS2, which was strengthened by CFRP-wrapping, dissipated an almost similar amount of seismic energy with specimen RG2 during the first five loading cycles (up to a drift angle ratio equal to 3.57%) (see Figure 6b). However, the shear resistance of FS2 was a portion of that of RG2 (see Figures 5b,c). As a result, the elastic strain energy values of FS2 were significantly lower with respect to the ones of RG2. Consequently, the values of cumulative equivalent viscous damping coefficient of specimen FS2 appear to be slightly increased when compared to the corresponding ones of RG2 (see Figures 9b,d).

Monitoring of the Steel Bar Micro-Strain
The seismic performance of existing RC structures, built prior to the 1960s-1970s, is mainly dominated by brittle failures of the columns and beam-to-column joints, which are related to loss of structural integrity and catastrophic partial or general collapse. Therefore, the applied retrofitting schemes should effectively prevent the occurrence of brittle failure modes, such as shear failure and/or premature excessive slipping of the lap-spliced reinforcing bars, while also securing, at least, the yielding of the columns' longitudinal reinforcement and the development of the nominal flexural moment capacity. Accordingly, a thorough analysis of the reinforcement's strain value variations during the reversed increments of inelastic lateral displacement would provide valuable information regarding the effectiveness of the applied retrofit scheme. Similar work can be found in the literature [37,38], where the transverse reinforcement and fiber hoop strains were monitored experimentally.
For this reason, electrical resistant strain gages were attached to the lap-spliced bars The slipping of reinforcement was effectively restricted, and it was not before the ninth push half-cycle when bar slipping showed a considerable increase. The latter is perceived in the hysteresis loops of RG 2 by the less steep (almost horizontal) upper branch of the push half-cycles (see Figure 5b). Notably, this is not true for the pull half-cycles, where the continuously ascending lower branch of the hysteresis loops reveals that increasing values of lateral shear force are required to further displace the column's free end.
Eventually, after eleven cycles of the earthquake-type loading, the strengthened column specimen, RG 2 , maintained 68% (push half-cycles) and 80% (pull half-cycles) of its initial lateral strength (see Figure 5b). Moreover, the peak-to-peak stiffness values of RG 2 were similar to those of the enhanced column RG 1 , as shown in Figure 6a. The energy dissipation capacity of RG 2 is illustrated in Figure 6b. As can be observed, the strengthened column showed a remarkable dissipating hysteresis behavior, with constantly increasing values of dissipated seismic energy during testing. The lower vales of the seismic energy dissipated by specimen RG 2 with respect to specimen RG 1 are reflected by the slightly reduced area of the hysteresis loops of RG 2 compared to the loops of RG 1 . The latter is primarily caused by the slipping of reinforcement after the seventh push half-cycle of RG 2 and, apparently, by the increased influence of the axial loading (P-δ effect). This influence is clearly demonstrated by the almost stable values of the resisted shear force, which are required for displacing the column's free end backwards from the peak displacement of each push half-cycle (see Figure 5b). Nevertheless, the amount of dissipated seismic energy during the eleventh cycle of loading of specimen RG 2 was increased by almost 220% with respect to the value of the first cycle, while also corresponding to almost 70% of the amount of energy dissipated by specimen RG 1 during the eleventh cycle.
A substantial increase in the lateral-bearing strength of specimen RG 2 with respect to the strength of the corresponding original column, O 2 , was also achieved. The latter is clearly demonstrated in the plots of strength ratio for peak displacement of each cycleversus-load point displacement, illustrated in Figure 7a. In particular, for drift angle value R = 4.59%, the strength ratio value RG 2 /O 2 equals 7.97 and 3.54 for the push halfcycle and the pull half-cycle, respectively. Accordingly, the peak-to-peak stiffness of the enhanced column RG 2 was significantly improved with respect to that of the original specimen, O 2 . During the first cycle of the earthquake-type loading, the strengthened column RG 2 showed an 16.5% increase in the peak-to-peak stiffness value with respect to specimen O 2 . Thereafter, RG 2 demonstrated a slower stiffness degradation rate during the consecutive cycles of loading. For lateral displacement value of 40 mm the original column, O 2 , collapsed due to the loss of axial load carrying capacity, while specimen RG 2 retained 32.9% of its initial stiffness. Furthermore, after eleven cycles of inelastic lateral displacement amplitudes (drift angle value, R, equal to 6.63%), specimen RG 2 maintained 16.65 % of its initial stiffness value shown during the first cycle. In Figure 7b the energy dissipation capacity ratio for peak displacement of each cycle-versus-load point displacement is presented. As can be observed, a significant improvement in the dissipating hysteresis performance of RG 2 with respect to O 2 was indisputably achieved, due to the external confinement provided by the thin high-strength RC jacket. Indeed, the energy dissipation ratio RG 2 /O 2 ranged from 1.29 to 2.40 during testing. Therefore, the strengthened column, RG 2 , exhibited a ductile overall seismic response, which was almost similar to the behavior of the control specimen, C 1 , with the continuous longitudinal reinforcing bars (see Figures 5d and 6b). In particular, RG 2 showed significantly higher values of lateral bearing strength than the specimen C 1 , while also achieving an increase of almost 25% in the peak-to-peak stiffness values. As with specimen RG 1 , this resulted from the slight increase in the dimensions of the strengthened column's cross-section, but is mainly caused by the additional confinement provided by the thin highstrength RC jacket. Furthermore, the mean value of the energy dissipation ratio, RG 2 /C 1 , during testing, equaled 0.98. Consequently, the strengthening interventions implemented on specimen RG 2 effectively secured the satisfactory ductile seismic performance of the enhanced column and, thus, were proved to constitute a reliable and efficient strengthening scheme for improving the seismic behavior of columns found in existing pre-1960s-1970s RC structures.
Specimen FS 2 was strengthened pre-earthquake by wrapping two layers of CFRP textile around the critical column region. The number of the required layers was determined using Equation (1). The column eventually exhibited brittle failure due to excessive slipping of the lap-spliced bars. In particular, during the first cycle of the earthquake-type loading, the main flexural crack was formed at the column base. The damage gradually evolved with the increase in lateral displacement values during the subsequent cycles, while progressive slipping of the lap-spliced reinforcement also occurred. As a result, the cracking at the column base sequentially dilated, and disconnection of the column from the strong foundation block of the specimen eventuated for drift angle values, R, was greater than 4.08 % (see Figure 8c). At the end of testing of FS 2 (after eight cycles of reversed inelastic lateral displacements), the pullout of the column's longitudinal reinforcing bars was apparent. The excessive slipping of the bars was also ascertained from the data acquired from strain gages, which were attached to the bars, showing almost stable steel strain values during the consecutive loading cycles (see Figure 11e) [23]. In Figure 8c, the failure mode of specimen FS 2 is depicted, characterized by excessive residual deformation and rotation of the column. From the plots of energy dissipation capacity-versus-load point displacement (see Figure 6b), it can be observed that the strengthened column, FS 2 , performed similarly to specimens C 1 and RG 2 during the first five cycles of the reversed inelastic lateral displacements (drift angle, R, equal to 3.57%), while subsequently showing a degrading hysteresis behavior similar to that of the corresponding original column specimen, O 2 . The latter is also clearly demonstrated on the hysteresis loops of FS 2 (see Figure 5c). For instance, rapid deterioration of lateral bearing strength and peakto-peak stiffness, intensive pinching of the hysteresis loops around the axes, horizontal branches showing excessive bar slipping and poor energy dissipation capacity dominated the hysteresis behavior of the column after the sixth push half-cycle and the fifth pull half-cycle of the seismic loading. The peak-to-peak stiffness of specimen FS 2 deteriorated more sharply during the first three cycles, while it subsequently deteriorated with a slower rate. For a lateral drift angle, R, equal to 5.10%, the peak-to-peak stiffness of FS 2 equaled only 1% of its initial value during the first cycle of loading (see Figure 6a). The hysteretic energy dissipation capacity of specimen FS 2 was similar to the capacities of C 1 and RG 2 for up to a drift angle value, R, equal to 3.57%, while afterwards it was rapidly reduced due to the excessive slipping of reinforcement (see Figure 6b). Nevertheless, the confinement provided by wrapping the two layers of the CFRP textile around the column of specimen FS 2 improved the failure mode of the specimen with respect to that of the corresponding original specimen, O 2 [3]. In particular, the evolution of damage was delayed, since excessive disintegration of the core concrete and loss of the concrete cover were effectively restricted. The strengthened column FS 2 initially showed a dissipating hysteresis behavior until the fifth cycle of the seismic loading. Thereupon, excessive slipping of the lap-spliced reinforcement dominated the cyclic response of the specimen, causing a degrading overall hysteresis response.
According to the capacity design approach, RC structures should be able to withstand increased values of inelastic cyclic deformations during strong seismic excitations, to allow for the dissipation of a significant amount of kinetic energy through damping. Therefore, the structures should possess adequate displacement ductility to develop acceptable damage in the plastic hinges, while preserving the structural integrity and preventing partial or general collapse. Thus, the equivalent viscous damping is highly related to the deformability, while consisting of both the elastic and the hysteretic damping. The latter is crucial for the seismic response of RC structures and depends on the post-yielding characteristics of the structural members. Furthermore, the desirable ductile seismic performance requires an adequate energy dissipation capacity of the members, which, in turn, results in higher equivalent viscous damping ratios. Contrarily, the RC structural members with low energy dissipation capacity exhibit poor hysteresis behavior, while being susceptible to collapse due to the cumulative dissipated energy under small deformations.
In order to evaluate the capacity of RC structural members for dissipating seismic energy, Equation (2) was used [38]. According to this equation, the equivalent viscous damping coefficient, ζ eq , is expressed as the ratio of the dissipated energy within a given cycle of the earthquake-type loading (represented by the area S ABCDEFA ) to the elastic strain energy associated with the maximum force and displacement of the given hysteresis loop (represented by the areas S OCC and S OFF ) (see Figure 9a). The energy dissipation capacity and the equivalent viscous damping coefficient, ζ eq , per cycle of loading are depicted in Figures 6b and 9b, while in Figure 9c,d, the cumulative dissipated energy and the cumulative equivalent viscous damping coefficient of specimens FS 2 , RG 1 and RG 2 for different drift ratio values are illustrated.
The enhanced columns RG 1 and RG 2 showed similar lateral resistance throughout testing and, therefore, similar elastic strain energy values (see Figure 5a,b and Figure 9a). As a result, the cumulative equivalent viscous damping coefficient values of specimen RG 1 were higher than the corresponding ones of column RG 2 , because the latter showed a lower energy dissipation capacity with respect to RG 1 (see Figures 6b and 9b-d). Additionally, it is worth noting that specimen FS 2 , which was strengthened by CFRP-wrapping, dissipated an almost similar amount of seismic energy with specimen RG 2 during the first five loading cycles (up to a drift angle ratio equal to 3.57%) (see Figure 6b). However, the shear resistance of FS 2 was a portion of that of RG 2 (see Figure 5b,c). As a result, the elastic strain energy values of FS 2 were significantly lower with respect to the ones of RG 2 . Consequently, the values of cumulative equivalent viscous damping coefficient of specimen FS 2 appear to be slightly increased when compared to the corresponding ones of RG 2 (see Figure 9b,d).

Monitoring of the Steel Bar Micro-Strain
The seismic performance of existing RC structures, built prior to the 1960s-1970s, is mainly dominated by brittle failures of the columns and beam-to-column joints, which are related to loss of structural integrity and catastrophic partial or general collapse. Therefore, the applied retrofitting schemes should effectively prevent the occurrence of brittle failure modes, such as shear failure and/or premature excessive slipping of the lap-spliced reinforcing bars, while also securing, at least, the yielding of the columns' longitudinal reinforcement and the development of the nominal flexural moment capacity. Accordingly, a thorough analysis of the reinforcement's strain value variations during the reversed increments of inelastic lateral displacement would provide valuable information regarding the effectiveness of the applied retrofit scheme. Similar work can be found in the literature [39,40], where the transverse reinforcement and fiber hoop strains were monitored experimentally.
For this reason, electrical resistant strain gages were attached to the lap-spliced bars of the column specimens, as well as to the ties of the thin high-strength RC jackets of RG 1 and RG 2 , to allow the monitoring of steel stain variations during the earthquaketype loading and ascertain if yielding of the bars was achieved. The exact location of the strain gages is illustrated in Figure 10, while in Figures 11 and 12 the plots of the load point displacement-versus-strain of reinforcement and the plots of maximum steel strain per cycle of loading are illustrated, respectively. Based on the strain analysis (see Figures 10-12), it was concluded that the continuously increasing strain values of the lapspliced reinforcement of strengthened specimen RG 1 resulted from both the confinement offered by the additional ties and from the high-strength concrete of the jacket, which replaced the concrete of low compression strength in the lap splice region. This dual contribution of the jacket substantially increased the bond stress between the bars and the concrete along the inadequate lap splice length and allowed for a satisfactory load transfer between the lap-spliced reinforcement. Therefore, yielding of reinforcement (ε s > ε y = 1.87‰) was eventually achieved (see Figure 11b,c and Figure 12). Moreover, it was clearly demonstrated that only minor steel strain (significantly lower than the yielding strain ε y = 2.50‰) was developed in the ties of the RC jacket (see Figure 11a,d and Figure 12). The latter was further substantiated by the failure mode of specimen RG 1 , which did not include any damage to the thin RC jacket (no increase in volume of the core concrete or loss of the concrete cover were observed). Consequently, it was evinced that the strengthened specimen RG 1 exhibited a ductile dissipating hysteresis response due to the satisfactory performance of the thin high-strength RC jacket. The same is also true for specimen RG 2 . The CFRP-strengthened column, FS 2 , showed increasing strain values of the lap-spliced reinforcement during the consecutive cycles of loading. This continuous increase in steel strain values up to the fifth cycle of loading indicates an absence of bar slipping for a drift angle ratio of up to 3.57% [36]. However, the strain values remained lower than steel yielding strain ε y = 1.87‰ (see Figure 11e). Thus, from the measurements of the strain gages, it was demonstrated that the confinement provided by the CFRP jacket was insufficient to allow yielding of the lap-spliced bars. The latter is attributed to the unexpected failure of the jacket, which, in turn, caused loss of the confinement provided to the lap splice region, while triggering brittle bond-slip failure and slipping of the bars. were observed). Consequently, it was evinced that the strengthened specimen RG1 exhibited a ductile dissipating hysteresis response due to the satisfactory performance of the thin high-strength RC jacket. The same is also true for specimen RG2. The CFRP-strengthened column, FS2, showed increasing strain values of the lap-spliced reinforcement during the consecutive cycles of loading. This continuous increase in steel strain values up to the fifth cycle of loading indicates an absence of bar slipping for a drift angle ratio of up to 3.57 % [34]. However, the strain values remained lower than steel yielding strain 1.87‰ (see Figure 11e). Thus, from the measurements of the strain gages, it was demonstrated that the confinement provided by the CFRP jacket was insufficient to allow yielding of the lap-spliced bars. The latter is attributed to the unexpected failure of the jacket, which, in turn, caused loss of the confinement provided to the lap splice region, while triggering brittle bond-slip failure and slipping of the bars. were observed). Consequently, it was evinced that the strengthened specimen RG1 exhibited a ductile dissipating hysteresis response due to the satisfactory performance of the thin high-strength RC jacket. The same is also true for specimen RG2. The CFRP-strengthened column, FS2, showed increasing strain values of the lap-spliced reinforcement during the consecutive cycles of loading. This continuous increase in steel strain values up to the fifth cycle of loading indicates an absence of bar slipping for a drift angle ratio of up to 3.57 % [34]. However, the strain values remained lower than steel yielding strain 1.87‰ (see Figure 11e). Thus, from the measurements of the strain gages, it was demonstrated that the confinement provided by the CFRP jacket was insufficient to allow yielding of the lap-spliced bars. The latter is attributed to the unexpected failure of the jacket, which, in turn, caused loss of the confinement provided to the lap splice region, while triggering brittle bond-slip failure and slipping of the bars.

Theoretical Conciderations
Kalogeropoulos and Tsonos [3,7] recently proposed a modified version of the analytical model proposed by Tsonos [39][40][41], to predict the seismic performance of RC columns of both existing pre-1960-1970s and modern RC structures. The latter can be achieved by controlling the adequacy of length of the lap-spliced reinforcement. Furthermore, the for-

Theoretical Conciderations
Kalogeropoulos and Tsonos [3,7] recently proposed a modified version of the analytical model proposed by Tsonos [39][40][41], to predict the seismic performance of RC columns of both existing pre-1960-1970s and modern RC structures. The latter can be achieved by controlling the adequacy of length of the lap-spliced reinforcement. Furthermore, the for-

Theoretical Conciderations
Kalogeropoulos and Tsonos [3,7] recently proposed a modified version of the analytical model proposed by Tsonos [41][42][43], to predict the seismic performance of RC columns of both existing pre-1960-1970s and modern RC structures. The latter can be achieved by controlling the adequacy of length of the lap-spliced reinforcement. Furthermore, the formulation is used to precisely determine the necessary confinement which should be provided by the strengthening material during the retrofitting of existing RC structures, in order to prevent early failure of the lap splices. Thus, the implementation of the proposed methodology ensures the satisfactory design of the retrofit schemes, which allows for the yielding of the inadequately lap-spliced bars and the development of the column's nominal flexural moment capacity.
In Figures 13 and 14, the details of the lap-spliced column reinforcing bars are depicted. As can be observed, the shear forces, acting on a 45 degree angle [44], are resisted by the concrete compression struts that act between diagonally opposite corners of each rectangular section "abcd". The diagonal compression strut mechanism depends on the concrete strength and, therefore, failure of the concrete causes a limitation of the strength of the lap splice, due to the gradual crushing along the cross-diagonal cracks, and especially along the potential failure plane, KLMN (see Figure 14b). Meanwhile, slipping of the bars occurs.
23 similar experiments found in the literature [5,28,[44][45][46] (see Figure 15). In Table 4, the shear capacities and the predicted actual values of the lap splice shear stress are shown. In particular, the value of actual shear stress in the potential failure plane between the lapspliced bars when yielding of the bars occurs is τ γ f . Thus, γ is calculated when the tension force acting in the bar, V A f , equals the bond force developed between the bar and the concrete along the lap splice, V γ f A, where A 3 • d • l is the area of the potential failure plane. The coeficient γ is calculated from Equations 3 -7, and the ultimate shear stress is subsequently given by the expression τ γ f . The value of γ is calculated from the expression A σ γ f A, where σ is the stress value calculated according to the Hook's law (σ Eε ) using the maximum measured steel strain value, ε , . The latter is measured experimentally by strain gages attached to the steel bar (ε ε , ). If the measured maximum strain, ε , , exceeds the yielding strain, ε , then ε is used to calculate the developed stress (ε ε since the Hook' law is not applied in the post-yielding range. According to the analytical formulation when the calculated shear stress is lower than the ultimate strength, τ γ f τ , then the predicted actual value of the lap splice shear stress will be near τ , because the lap splice permits the yielding of reinforcement τ τ . Contrarily, when τ τ lap, splice failure occurs prior to the yielding of reinforcement and τ τ . In the case of specimens RG1 and RG2, it was demonstrated that the implementation of the analytical model ensured the satisfactory design of the thin RC jackets, which provided adequate confinement to the lap splice region and allowed for the yielding of the inadequately lapspliced bars. • 1 • (7) Table 4. Predicted values of the concrete shear stress in the potential failure plane. According to the proposed methodology, which was presented in detail in previous works [3,7], the ultimate strength of the lap splice is given by Equation (3), where the values of x and ψ are given by Equations (4) and (5), respectively and the aspect ratio value α = h/b is always equal to 1.0. The increased value of the concrete compressive strength, f c , due to the confinement provided by the jacket, is calculated using Equations (6) and (7) [45].
The validity of the proposed analytical model was checked using experimental data from 13 column specimens tested in the Laboratory of Reinforced Concrete Structures and Masonry Buildings of the Aristotle University of Thessaloniki [3,7], as well as data from 23 similar experiments found in the literature [5,30,[46][47][48] (see Figure 15). In Table 4, the shear capacities and the predicted actual values of the lap splice shear stress are shown. In partic-ular, the value of actual shear stress in the potential failure plane between the lap-spliced bars when yielding of the bars occurs is τ cal = γ cal f c . Thus, γ cal is calculated when the tension force acting in the bar, V u = A s f y , equals the bond force developed between the bar and the concrete along the lap splice, V n = γ cal f c A, where A = 3·d b ·l s is the area of the potential failure plane. The coeficient γ ult is calculated from Equations (3)- (7), and the ultimate shear stress is subsequently given by the expression τ ult = γ ult f c . The value of γ exp is calculated from the expression A s σ s = γ exp f c A, where σ s is the stress value calculated according to the Hook's law (σ s = Eε exp ) using the maximum measured steel strain value, ε s,max . The latter is measured experimentally by strain gages attached to the steel bar (ε exp = ε s,max ). If the measured maximum strain, ε s,max , exceeds the yielding strain, ε y , then ε y is used to calculate the developed stress (ε exp = ε y ) since the Hook' law is not applied in the post-yielding range. According to the analytical formulation when the calculated shear stress is lower than the ultimate strength, τ cal = γ cal f c < τ ult , then the predicted actual value of the lap splice shear stress will be near τ cal , because the lap splice permits the yielding of reinforcement τ pred = τ cal . Contrarily, when τ cal > τ ult lap, splice failure occurs prior to the yielding of reinforcement and τ pred = τ ult . In the case of specimens RG 1 and RG 2 , it was demonstrated that the implementation of the analytical model ensured the satisfactory design of the thin RC jackets, which provided adequate confinement to the lap splice region and allowed for the yielding of the inadequately lap-spliced bars. (

Conclusions
In the present study, the effectiveness of two strengthening schemes in improving the overall hysteresis performance of RC columns with poor seismic details was experimentally and analytically investigated. Three column specimens of 1:1.5 scale were constructed, designed for gravity loads only. The main structural deficiencies of the columns included the use of concrete with low compressive strength, plain steel reinforcement,

Conclusions
In the present study, the effectiveness of two strengthening schemes in improving the overall hysteresis performance of RC columns with poor seismic details was experimentally and analytically investigated. Three column specimens of 1:1.5 scale were constructed, designed for gravity loads only. The main structural deficiencies of the columns included the use of concrete with low compressive strength, plain steel reinforcement, widely spaced ties and inadequate length of the lap splices of reinforcement. Subsequently, these specimens were enhanced by either wrapping layers of CFRP textile along the critical column height (specimen FS 2 ) or by using high-strength concrete to confine the critical region with a thin RC jacket (specimens RG 1 and RG 2 ). The strengthened columns were then subjected to a large number of incremental amplitudes of lateral displacement under constant axial loading, to simulate the equivalent effect of strong earthquake motions. The examined variables were the strengthening material, the length of the lap splices and the amount of confinement provided by the jackets. Based on both the experimental data acquired during the seismic tests and the implementation of the proposed analytical formulation, a comprehensive analysis of the hysteresis response of the specimens was attempted. Moreover, the seismic behavior of the strengthened columns was further evaluated with respect to the cyclic performance of two corresponding original specimens, O 1 and O 2, and the response of a control one, C 1 , with continuous reinforcement, which were tested in a previous work [3].
It was clearly demonstrated that the thin RC jackets of high strength provided adequate confinement to the critical region of specimens RG 1 and RG 2 , where the lap splices of reinforcement are located, and hence, satisfactorily improved the load transfer mechanism between the lap-spliced bars. Meanwhile, premature lap splice failure and excessive bar slipping were effectively precluded. Consequently, the strengthening interventions applied to specimens RG 1 and RG 2 allowed for the development of the columns' nominal flexural moment capacities, while securing a ductile dissipating hysteresis behavior. Thus, RG 1 and RG 2 showed an indisputably superior hysteresis behavior with respect to the seismic response of the original columns, O 1 and O 2 , which was mainly dominated by bond-slip failure and excessive slipping of the lap-spliced reinforcement which, eventually, resulted in the collapse of the specimens due to the loss of axial load-carrying capacity. It is also worth noting that the application of the aforementioned strengthening scheme is relatively easy and requires limited labor work with respect to the application of conventional RC jacketing. Furthermore, due to the limited dimensions of the thin high-strength RC jacket, only minimal impact is caused in the exploitation of the available floor space. Ultimately, the use of a thin high-strength RC jacket was proved to be an efficient, cost-effective and competitive strengthening scheme which can be easily applied, while able to secure a satisfactory seismic performance of the strengthened non-ductile RC columns when implementing the proposed analytical formulation to define the necessary confinement. The strengthened specimen FS 2 showed almost similar values of dissipated hysteresis energy with specimen RG 2 for a drift angle ratio up to 3.57 %, which were also increased with respect to the corresponding values of the original column, O 2 . Moreover, the confinement provided by the CFRP jacket improved the failure mode of FS 2 with respect to that of specimen O 2 , since excessive disintegration of the core concrete and loss of the concrete cover were not observed in the case of FS 2 . However, due to the unexpected premature failure of the CFRP jacket, column FS 2 exhibited a rapidly degrading hysteresis behavior, dominated by the excessive slipping of the lap-spliced bars. This indicates the severe consequences of the brittle failure of the CFRP jacket in the seismic response of the strengthened column. In particular, the cracking of the CFRP jacket triggered immediate loss of the provided confining stress, which resulted in the slipping of the inadequately lap-spliced reinforcement. Contrarily, specimen RG 2 showed a continuous increase in the energy dissipation capacity during the consecutive cycles of the earthquake-type loading until the end of testing, despite the cracking formed in the circumference of the thin high-strength RC jacket. This is attributed to the beneficial influence of the jacket's ties in the confinement of the existing column. Eventually, it was concluded that wrapping layers of CFRP textile around the column's critical region may also be a cost-effective and easy-to-apply strengthening scheme with negligible influence on the dimensions of the column [7], which can satisfactorily improve the seismic response of the column only if premature failure of the CFRP jacket is successfully precluded to allow for the yielding of the lap-spliced bars.