Morphology Development of Polymer Blend Fibers along Spinning Line

Melt spinning is an efficient platform to continuously produce fiber materials with multifunctional and novel properties at a large scale. This paper briefly reviews research works that reveal the morphology development of immiscible polymer blend fibers during melt spinning. The better understanding of the formation and development of morphology of polymer blend fibers during melt spinning could help us to generate desired morphologies and precisely control the final properties of fiber materials via the melt spinning process.


Introduction
The blend method has been considered a promising way to achieve an in situ composite by simply mixing different components.The addition of the second component not only brings the original properties of the additive to the polymer blend but also creates new properties by tuning the structure of the polymer blend.The final properties of polymer materials rely on the morphology produced under the action of hydrodynamic and interfacial tension during melt processing.The strategy of tailoring the morphology of polymer blends aims to create a dispersed phase or second component at the desired scale and to distribute it in the desired position [1][2][3][4][5][6].Melt spinning is a simple and efficient way to produce polymer blend fibers.However, the rheological behavior, heat transmission, force equilibrium, dynamics and crystallization of polymers are quite complex during the melt spinning of fibers.So far, the precise control of the morphology of polymer blend fibers is still a challenge.
The purpose of this paper is to review studies related to the morphology development of immiscible polymer blend fibers during melt spinning.The formation mechanism of the disperse-matrix morphology of blend fibers during melt spinning, regarding droplet deformation, break-up and coalescence, is also briefly addressed.In this case, the microrheological behavior and an extensive overview are given by Janssen [7].Since most commonly used commercial polymers are not miscible, the situation becomes more complicated when the strong interaction between components is taken into consideration [8,9].Therefore, we only consider fully immiscible polymer-polymer mixtures in this review.
The supramolecular structure evolution, regarding the crystal structure and orientation of polymer fibers during melt spinning, has been systemically studied by researchers based on on-line small-angle and wide-angle X-ray scattering techniques [10][11][12][13][14][15][16][17][18][19][20][21].As far as we know, the effect that the second phase has on the supramolecular structure evolution during melt spinning is not yet fully understood; however, is beyond the scope of this review.

Morphology Development along the Spinning Line
Once the polymer melt is removed from the spinneret, it is quenched in cooling media (e.g., water and air), where the morphology of fibers is mainly controlled by the elongational force of the take-up action during the melt spinning process.The temperature of running filament decreases gradually along the spinning line, and the variation of temperature and temperature-related parameters (e.g., viscosity) play a vital role in the development of morphology during spinning [22].Fundamental equations (1-D model), describing the axial distributions of diameter, velocity, temperature, stress and structures of the fiber during the melt spinning process, was proposed by Ziabicki [22], Kase et al. [23] and Han et al. [24][25][26][27] in the 1960s, and was later developed further and modified by other authors [28,29].
To study the evolution of the morphology and structure of polymer blend fibers, it is necessary to detect the second phase inside the fiber matrix, which is not easy due to the limitation of on-line measurement methods.Thus, a high-speed camera was used to record the flow of biphasic fluid and monitor the morphology evolution in a transparent tube [30].However, optical recognition of the second phase in a polymeric matrix is not possible when the matrix is not transparent, which is common in most fiber materials.Furthermore, this technique is quite limited to the concentration of the second phase and the reflection index between polymer components.Therefore, in most research, the evaluation of the morphology development of polymer blend fibers is executed by collecting samples from the original position (usually by quenching extrudate in a low-temperature bath, and once removed, the capillary die) and take-up position.Recently, our group [31] and Tran et al. [32] both used a self-made fiber capturing device (see Figure 1), which allowed the capture of the running filament at different spinning line positions and quenched the structure of the filament at a low temperature.This was done in order to study the morphology development of blend fibers at a high resolution.

Morphology Development along the Spinning Line
Once the polymer melt is removed from the spinneret, it is quenched in cooling media (e.g.water and air), where the morphology of fibers is mainly controlled by the elongational force of the takeup action during the melt spinning process.The temperature of running filament decreases gradually along the spinning line, and the variation of temperature and temperature-related parameters (e.g.viscosity) play a vital role in the development of morphology during spinning [22].Fundamental equations (1-D model), describing the axial distributions of diameter, velocity, temperature, stress and structures of the fiber during the melt spinning process, was proposed by Ziabicki [22], Kase et al. [23] and Han et al. [24][25][26][27] in the 1960s, and was later developed further and modified by other authors [28,29].
To study the evolution of the morphology and structure of polymer blend fibers, it is necessary to detect the second phase inside the fiber matrix, which is not easy due to the limitation of on-line measurement methods.Thus, a high-speed camera was used to record the flow of biphasic fluid and monitor the morphology evolution in a transparent tube [30].However, optical recognition of the second phase in a polymeric matrix is not possible when the matrix is not transparent, which is common in most fiber materials.Furthermore, this technique is quite limited to the concentration of the second phase and the reflection index between polymer components.Therefore, in most research, the evaluation of the morphology development of polymer blend fibers is executed by collecting samples from the original position (usually by quenching extrudate in a low-temperature bath, and once removed, the capillary die) and take-up position.Recently, our group [31] and Tran et al. [32] both used a self-made fiber capturing device (see Figure 1), which allowed the capture of the running filament at different spinning line positions and quenched the structure of the filament at a low temperature.This was done in order to study the morphology development of blend fibers at a high resolution.The initial morphology of polymer blend fibers usually comes from melt extrusion.The melting and mixing process can generate morphologies ranging from dispersed drops to fibers to lamella to co-continuous structures [33], see Figure 2. The initial morphology of immiscible polymer blend fibers is usually represented as a droplet-matrix or fibril-matrix morphology [31,32,[34][35][36][37][38][39][40][41][42][43][44][45][46][47][48][49][50][51][52].The strategy to produce lamellae and other morphologies is more difficult than that required for the droplet-matrix morphology since the interfacial tension tends to minimize the surface of the second phase [7].Moreover, the formation mechanism of such a morphology during processing is not yet clear.The initial morphology of polymer blend fibers usually comes from melt extrusion.The melting and mixing process can generate morphologies ranging from dispersed drops to fibers to lamella to co-continuous structures [33], see Figure 2. The initial morphology of immiscible polymer blend fibers is usually represented as a droplet-matrix or fibril-matrix morphology [31,32,[34][35][36][37][38][39][40][41][42][43][44][45][46][47][48][49][50][51][52].The strategy to produce lamellae and other morphologies is more difficult than that required for the droplet-matrix morphology since the interfacial tension tends to minimize the surface of the second phase [7].Moreover, the formation mechanism of such a morphology during processing is not yet clear.The morphology development of polymer blend fibers during melt spinning is controlled by dynamic factors (e.g.elongational force and strain rate, which are mainly dependent on the take-up action) and thermal conditions (e.g.cooling system, which affects the heat conduction and transfer of polymer blend melts) [22].Dynamic simulation studies [22,53,54] have shown that the axis velocity and stress of the filament increase gradually along the spinning line and continue until they almost reach the point of solidification, where the polymer blend fiber is converted from the molten to the solid state.This indicates that the second phase undergoes a gradually increased elongational force in the region between the spinneret and the solidification point.Ultimately, the morphology evolution of the second phases are strongly affected by the elongational force in the fiber formation region.Experimental studies [31,32,35,36,55] have shown that the second phase is continuously stretched along the spinning line and the diameter of the second phase decreases with increasing the take-up speed due to the increasing elongational stress.A sphere or rod-like second phase can be easily stretched into a fibril-like morphology under this elongational flow field.Tran and co-authors reported the morphology development of a poly (vinyl alcohol) (PVA) and poly (lactic acid) (PLA) blend filament (the weight ratio of PVA to PLA was 70/30, the zero shear viscosity ratio of PVA to PLA was 13.3) taken-up at 50 m/min during melt spinning [32].Figure 3 presents the morphology of the PLA phase after removing the PVA matrix at different spinning line locations.The spherical/ellipsoidal PLA domains were gradually formed into long continuous nanofibrillar structures due to the gradually increased elongational force along the spinning line.The formation of fibrillar structures is essential for the improvement of the mechanical properties of polymer blend fibers [35].Precise morphology studies-performed in our previous studies [31,36,50]-based on the morphology analysis of cross and longitudinal sections of blend fibers revealed that the dispersed phase deformed from ellipse to nano-scale fibrils along the spinning line, as shown in Figure 4.The break-up phenomenon was observed when the interfacial tension was not strong enough to maintain the dispersed phase under the equilibrium with viscous force [36,56].The morphology development of polymer blend fibers during melt spinning is controlled by dynamic factors (e.g., elongational force and strain rate, which are mainly dependent on the take-up action) and thermal conditions (e.g., cooling system, which affects the heat conduction and transfer of polymer blend melts) [22].Dynamic simulation studies [22,53,54] have shown that the axis velocity and stress of the filament increase gradually along the spinning line and continue until they almost reach the point of solidification, where the polymer blend fiber is converted from the molten to the solid state.This indicates that the second phase undergoes a gradually increased elongational force in the region between the spinneret and the solidification point.Ultimately, the morphology evolution of the second phases are strongly affected by the elongational force in the fiber formation region.Experimental studies [31,32,35,36,55] have shown that the second phase is continuously stretched along the spinning line and the diameter of the second phase decreases with increasing the take-up speed due to the increasing elongational stress.A sphere or rod-like second phase can be easily stretched into a fibril-like morphology under this elongational flow field.Tran and co-authors reported the morphology development of a poly (vinyl alcohol) (PVA) and poly (lactic acid) (PLA) blend filament (the weight ratio of PVA to PLA was 70/30, the zero shear viscosity ratio of PVA to PLA was 13.3) taken-up at 50 m/min during melt spinning [32].Figure 3 presents the morphology of the PLA phase after removing the PVA matrix at different spinning line locations.The spherical/ellipsoidal PLA domains were gradually formed into long continuous nanofibrillar structures due to the gradually increased elongational force along the spinning line.The formation of fibrillar structures is essential for the improvement of the mechanical properties of polymer blend fibers [35].Precise morphology studies-performed in our previous studies [31,36,50]-based on the morphology analysis of cross and longitudinal sections of blend fibers revealed that the dispersed phase deformed from ellipse to nano-scale fibrils along the spinning line, as shown in Figure 4.The break-up phenomenon was observed when the interfacial tension was not strong enough to maintain the dispersed phase under the equilibrium with viscous force [36,56].During melt spinning, the polymer melt flow presents as an unsteady flow with a shrinking fiber matrix.In some cases, the shrinking matrix compresses the droplets to enable them to migrate from the surface to the center of the matrix fiber [31].Meanwhile, the shrinking boundary also makes the coalescence of the dispersed phase much more frequent.He and co-authors [31,57] found that there is a coalescence region combined with the droplet deformation region under the condition of high   During melt spinning, the polymer melt flow presents as an unsteady flow with a shrinking fiber matrix.In some cases, the shrinking matrix compresses the droplets to enable them to migrate from the surface to the center of the matrix fiber [31].Meanwhile, the shrinking boundary also makes the coalescence of the dispersed phase much more frequent.He and co-authors [31,57] found that there is a coalescence region combined with the droplet deformation region under the condition of high During melt spinning, the polymer melt flow presents as an unsteady flow with a shrinking fiber matrix.In some cases, the shrinking matrix compresses the droplets to enable them to migrate from the surface to the center of the matrix fiber [31].Meanwhile, the shrinking boundary also makes the coalescence of the dispersed phase much more frequent.He and co-authors [31,57] found that there is a coalescence region combined with the droplet deformation region under the condition of high take-up velocity, as shown in Figures 5 and 6.In this coalescence region, the diameter of polystyrene (PS) dispersed phases in polypropylene (PP)/PS blend fibers increased along the spinning line.This indicates that the diameter of the second phase is not always decreasing along the spinning line under elongational flow.The increase in the diameter of the dispersed phase due to the coalescence also make the elongation of the dispersed phase more pronounced and facilitates fibril formation [31,58].

Slide rail & Scale
Fibers 2019, 7, x FOR PEER REVIEW 5 of 14 take-up velocity, as shown in Figures 5 and 6.In this coalescence region, the diameter of polystyrene (PS) dispersed phases in polypropylene (PP)/PS blend fibers increased along the spinning line.This indicates that the diameter of the second phase is not always decreasing along the spinning line under elongational flow.The increase in the diameter of the dispersed phase due to the coalescence also make the elongation of the dispersed phase more pronounced and facilitates fibril formation [31,58].The equilibrium between the break-up and coalescence of droplets makes the morphology and its development along the spinning line more complicated, especially in high concentrations and particle-particle interaction systems [9,[58][59][60].Tran and co-authors [32] showed that the dispersed phase tends to coalesce with the adjacent dispersed phase in order to form continuous long micro-or nanofibrils.When they investigated the morphological evolution of thermoplastic PVA/PLA blend filaments along the spinning line, a random morphology of the dispersed PLA phase was observed in the earlier stage, when the equilibrium between the break-up and coalescence of droplets was in a delicate balance status, which may be due to the not fully developed morphology in the extrusion capillary.Furthermore, this irregularly dispersed PLA was also stretched into micro-or nanofibrils.Yang's study [40] showed that the fibrils or droplets at the surface of polymer blend fibers can coalesce into a continuous layer or network during melt spinning when the drawdown ratio (DDR) is high enough.Despite the axis temperature difference, it is known that there is a non-uniform distribution of temperature along the radial direction in the melt spinning of fibers due to the heat transfer from the molten fiber to the surrounding medium [50].The radial temperature difference in turn affects the radial viscosity and stress fields in the running filament, which can generate a hierarchical structure-such as a skin-core structure [61,62].Furthermore, the temperature difference also influences the microrheological behavior of the second phase in polymer blend fibers [31,36,50].Our previous research [36,38,50,63,64] found that, if a polymer blend fiber with gradient structures was produced by using this radial gradient temperature during melt spinning, it could be achieved with great ease.The gradient morphology of PP/PS blend fibers could be tailored by tuning the take-up speed and the viscosity ratio (p) of the polymer blend, as shown in Figure 7. Gradient structures with large droplets near the surface region of PP/PS blend fibers and small droplets in the center can be produced in PP/PS blend fibers with high viscosity ratios, and was found to accelerate the dye absorption of PP fiber [36].However, a relatively uniform morphology was obtained in a matched viscosity ratio system (p ≈ 1) [64].The dynamics of the melt spinning of PP/PS blend fibers showed that the polymer melt jets exit the spinneret at uniform temperatures [53].As the polymer melt jets were drawn down, the polymer melt jets were cooled, with a temperature gradient in the radial direction of fiber.The transition from the central region with high temperatures to the surface region with low temperatures is shown in Figure 8.The maximum radial temperature gradients varied from 5.6 × 10 4 to 12.4 × 10 4 • C/m at the spinning line positions from 11.4 to 32.7 cm with regard to the various take-up velocities.The PS droplets, with higher viscosity than the PP matrix, in the center region tended to have smaller diameters than those in the surface region [31].This radial diameter gradient was found to be a result of the radial temperature gradient since the droplets in the center region with high temperatures have a higher possibility and more time to deform into more stretched droplets or fibrils [50].This radial diameter gradient was strengthened along the spinning line and slightly strengthened by the increasing take-up speed.However, the drastic coalescence of droplets in the center of fibers at a high take-up speed results in a weakening of the radial gradients of droplets.The dispersed phases near the surface region can act as a functional additive to improve the surface properties of normal fibers.Dan and co-authors [6] showed that PS dispersed phases near the fiber surface were aligned along the fiber axis and formed nano-channels after removing said PS phases, as shown in Figure 9.This could be a possible way to produce a functional fiber with good surface properties and novel optical properties.

Mechanism of Morphology Development
An essential aspect of the formation mechanism of a dispersed-matrix morphology in polymer blends is the dispersion of one liquid in another.The morphology of polymer blend fibers highly depends on the microrheological behavior of the second phase, including deformation, break-up, coalescence and migration under the action in elongational flow.In particular, the time scales of the distinct microrheological processes have to be considered to verify whether the available process time suffices for a specific event to occur [7].
The deformation of a dispersed droplet is governed by the viscosity ratio p, the ratio of the viscosity of dispersed phase η d to the viscosity of matrix η m and the capillary number Ca, which expresses the ratio between viscous force and interfacial tension, according to Taylor's theory [65,66].
ε is the elongational rate, R 0 is the radius of the initial droplet and α the interfacial tension between two polymers.The deformation degree of the dispersed phase is usually defined as: where L is the length of the major axis, B is the length of the minor axis.Taylor presented two cases of the deformation expressions-when interfacial forces dominate and when viscous effects dominate.
Cox [67] then extended Taylor's theory to the full range of the viscosity ratio under elongational flow: where A is the flow type constant, A = 2 in plane hyperbolic flow fields, A = 1 in the uniaxial elongational flow field.However, Taylor and Cox's theories are limited to small deformation cases with medium or high viscosity ratio systems.When discussing low viscosity ratio polymer blends, the dispersed phases can be stretched into fine fibrils.Meanwhile, the small deformation theory cannot predict the deformation and break-up of fibrils precisely [68].In 1964, Taylor proposed a large deformation theory intended to describe a slender droplet in four roller axisymmetric extension fields.However, this large deformation theory is limited to low viscosity ratio and low Ca cases.Acrivos et al. [69] extended the large deformation theory into droplet deformation in uniaxial elongational flow, for which the relation between Ca and droplet deformation can be expressed as: When the droplet deformation is similar to the deformation of the matrix, as shown in Figure 10, the affine deformation of droplet can be described as: where ε (ε = .ε•t) is the elongation stress.
Fibers 2019, 7, x FOR PEER REVIEW 9 of 14 with medium or high viscosity ratio systems.When discussing low viscosity ratio polymer blends, the dispersed phases can be stretched into fine fibrils.Meanwhile, the small deformation theory cannot predict the deformation and break-up of fibrils precisely [68].In 1964, Taylor proposed a large deformation theory intended to describe a slender droplet in four roller axisymmetric extension fields.However, this large deformation theory is limited to low viscosity ratio and low  cases.Acrivos et al. [69] extended the large deformation theory into droplet deformation in uniaxial elongational flow, for which the relation between  and droplet deformation can be expressed as: When the droplet deformation is similar to the deformation of the matrix, as shown in Figure 10, the affine deformation of droplet can be described as: where  ( =  ⋅ ) is the elongation stress.Above a critical number,  , the viscous force overrules the interfacial tension and no stable equilibrium droplet shape exists.The droplet is stretched and finally breaks apart. can be experimentally determined by increasing the elongational rate to evaluate whether or not the droplet shape remains stable for a considerable period of time [7].The  of the droplet in the elongational flow is a function of the viscosity ratio and can be expressed as Equation (6) according to Grace's study [70].
There are three types of break-up that can be found in experimental studies: stepwise, transient, and edge break-up mechanisms as shown in Figure 11 [71,72].Stepwise break-up usually happens in the case of low , wherein the mother droplet break-up converts into two same droplets when  > Ca c .The deformation and break-up of droplets can be predicted when the reduced capillary number (see Equation ( 7)) based on Huneault's criteria [73] is taken into account.According to Huneault's certificate, droplets cannot deform in the case of  * < 0.1.Droplets deform but not break-up in the case of 0.1 <  * < 1; droplets deform and then split into two primary droplets for 1 <  * < 4; and droplets deform into fibrils and disintegration when 4 <  * .Above a critical number, Ca c , the viscous force overrules the interfacial tension and no stable equilibrium droplet shape exists.The droplet is stretched and finally breaks apart.Ca c can be experimentally determined by increasing the elongational rate to evaluate whether or not the droplet shape remains stable for a considerable period of time [7].The Ca c of the droplet in the elongational flow is a function of the viscosity ratio and can be expressed as Equation (6) according to Grace's study [70].
There are three types of break-up that can be found in experimental studies: stepwise, transient, and edge break-up mechanisms as shown in Figure 11 [71,72].Stepwise break-up usually happens in the case of low Ca, wherein the mother droplet break-up converts into two same droplets when Ca > Ca c .
The deformation and break-up of droplets can be predicted when the reduced capillary number (see Equation ( 7)) based on Huneault's criteria [73] is taken into account.According to Huneault's certificate, droplets cannot deform in the case of Ca * < 0.1.Droplets deform but not break-up in the case of 0.1 < Ca * < 1; droplets deform and then split into two primary droplets for 1 < Ca * < 4; and droplets deform into fibrils and disintegration when 4 < Ca * .
During the break-up of extended fibrils, the waves of distorted interfacial surfaces are continuously stretched.Break-up occurs as soon as the amplitude of a disturbance of interface is magnified to such an extent that it equals the continuously decreasing mean thread radius [7].The total break-up time t * b is expressed as: where t * c is the critical time where the thread radius has decreased to the critical radius R c of break-up and t * g is the growth time from critical time to the moment break-up occurs.e f is the stretching efficiency, e f = .γ, R c and e f t * g can be determined by using the method described in Reference [7].
The above models suggest that the morphology of polymer blend fibers could be predicted based on the melt spinning dynamics simulated under some simple conditions [50,56,68,74].The droplet deformation theory was first adopted by Padsalgikar et al. [68] to simulate the diameter of dispersed PP droplets along the spinning line in PS/PP blend fibers based on Taylor and Cox's theories.The simulated values correlated with the measured values at the low take-up speed range from 125 to 250 m/min.Song et al. [56] adopted similar methods and predicted the diameter of Liquid crystalline polymer (LCP) droplets in polyester (PET)/LCP blend fibers.The simulated values were found to be about 12% to 33% smaller than the measured diameter.Pan et al. [50] studied the PS droplet deformation in a PP matrix during melt spinning.Delaby's affine deformation model [75][76][77] was selected to simulate the diameter of the dispersed PS phase, based on Huneault's certificate, and again displayed signs of correlation between predicted and measured values at relatively low take-up velocities.However, the prediction of the morphology of polymer blend fibers becomes much more challenging when the strong interaction between the dispersed phases is taken into consideration.He et al. [74] also studied the deformation, coalescence and breakup of thermotropic liquid-crystalline polymer (TLCP) drops in poly(ethylene naphthalate) (PEN)/TLCP Vectra A950 blend at the take-up speed of 300 m/min by using affine deformation theory.However, neither the degree of TLCP droplets deformation nor the fundamental question of the difference between simulated and measured morphology was further illustrated.From the existing few papers related to the simulation of the morphology of polymer blend fibers, droplet deformation theory enables the prediction of the diameter of the dispersed phase at low take-up velocities.However, when the coalescence effect is non-negligible, the precise predict of droplet morphology is not possible.
The flow-induced coalescence of droplets is a complex phenomenon and is mostly studied in shear flow, where droplets with different coordinates in the direction of the velocity gradient collide [9], as shown in Figure 12.The course of coalescence usually has three steps: (1) the approach and collision of droplets; (2) the rupture of the matrix film between two approaching droplets; (3) the drainage of the matrix film.It is difficult to find further research on the coalescence of droplets in elongational flow.However, the current coalescence theory of droplets is limited to a low shear rate range and low concentration blends.Many problems have not yet been studied, and most theories focus on the coalescence between sphere droplets, which is not common in the elongational flow.Most research neglects the effect of other droplets on the collision droplet pairs [9].
where  * is the critical time where the thread radius has decreased to the critical radius  of breakup and  * is the growth time from critical time to the moment break-up occurs. is the stretching efficiency,  = 1 2 ⁄ in 2-D elongational flow and  = 2 3 ⁄ in 3-D elongational flow. ,  and   * can be determined by using the method described in Reference [7].The above models suggest that the morphology of polymer blend fibers could be predicted based on the melt spinning dynamics simulated under some simple conditions [50,56,68,74].The droplet deformation theory was first adopted by Padsalgikar et al. [68] to simulate the diameter of dispersed PP droplets along the spinning line in PS/PP blend fibers based on Taylor and Cox's theories.The simulated values correlated with the measured values at the low take-up speed range from 125 to 250 m/min.Song et al. [56] adopted similar methods and predicted the diameter of Liquid crystalline polymer (LCP) droplets in polyester (PET)/LCP blend fibers.The simulated values were found to be about 12% to 33% smaller than the measured diameter.Pan et al. [50] studied the PS droplet deformation in a PP matrix during melt spinning.Delaby's affine deformation model [75][76][77] was selected to simulate the diameter of the dispersed PS phase, based on Huneault's certificate, and again displayed signs of correlation between predicted and measured values at relatively low takeup velocities.However, the prediction of the morphology of polymer blend fibers becomes much more challenging when the strong interaction between the dispersed phases is taken into consideration.He et al. [74] also studied the deformation, coalescence and breakup of thermotropic liquid-crystalline polymer (TLCP) drops in poly(ethylene naphthalate) (PEN)/TLCP Vectra A950 blend at the take-up speed of 300 m/min by using affine deformation theory.However, neither the degree of TLCP droplets deformation nor the fundamental question of the difference between simulated and measured morphology was further illustrated.From the existing few papers related to the simulation of the morphology of polymer blend fibers, droplet deformation theory enables the prediction of the diameter of the dispersed phase at low take-up velocities.However, when the coalescence effect is non-negligible, the precise predict of droplet morphology is not possible.
The flow-induced coalescence of droplets is a complex phenomenon and is mostly studied in shear flow, where droplets with different coordinates in the direction of the velocity gradient collide [9], as shown in Figure 12.The course of coalescence usually has three steps: (1) the approach and collision of droplets; (2) the rupture of the matrix film between two approaching droplets; (3) the drainage of the matrix film.It is difficult to find further research on the coalescence of droplets in elongational flow.However, the current coalescence theory of droplets is limited to a low shear rate range and low concentration blends.Many problems have not yet been studied, and most theories focus on the coalescence between sphere droplets, which is not common in the elongational flow.Most research neglects the effect of other droplets on the collision droplet pairs [9].

Conclusions and Outlooks
In this brief and introductory review, we have expressed current understandings of the morphology development of polymer blend fibers during melt spinning.Yet, current studies do not supply sufficient knowledge to cover all conditions, e.g. the full range of the viscosity ratio and the volume fraction, or the wide range of the take-up speed, due to the limitations of the precise characterization of morphology.In order to gain more insight into the formation mechanisms of morphology during melt spinning, we have drawn attention to the microrheological behavior of the second phase in elongational flow.Current research demonstrates that the microrheological theory will continue to evolve and become more popular in morphology simulation during melt processing.However, for more concentrated systems and high strain rate conditions, a complete understanding of morphology development in elongational flow has not yet been obtained.That being said, with the progress in theoretical and experimental techniques, it will perhaps be possible to design polymer materials with novel structures at desired scales and positions in the future.

Conclusions and Outlooks
In this brief and introductory review, we have expressed current understandings of the morphology development of polymer blend fibers during melt spinning.Yet, current studies do not supply sufficient knowledge to cover all conditions, e.g., the full range of the viscosity ratio and the volume fraction, or the wide range of the take-up speed, due to the limitations of the precise characterization of morphology.In order to gain more insight into the formation mechanisms of morphology during melt spinning, we have drawn attention to the microrheological behavior of the second phase in elongational flow.Current research demonstrates that the microrheological theory will continue to evolve and become more popular in morphology simulation during melt processing.However, for more concentrated systems and high strain rate conditions, a complete understanding of morphology development in elongational flow has not yet been obtained.That being said, with the progress in theoretical and experimental techniques, it will perhaps be possible to design polymer materials with novel structures at desired scales and positions in the future.

Figure 1 .
Figure 1.Schematic diagram of the capture device made by our group.

Figure 1 .
Figure 1.Schematic diagram of the capture device made by our group.

Figure 2 .
Figure 2. Schematic of morphologies which can produced by polymer-polymer melt blending [33].Reused with permission from W. Macosko Christopher, Macromolecular Symposia; published by John Wiley and Sons, 2000.

Figure 2 .
Figure 2. Schematic of morphologies which can produced by polymer-polymer melt blending [33].Reused with permission from W. Macosko Christopher, Macromolecular Symposia; published by John Wiley and Sons, 2000.

Figure 3 .
Figure 3. SEM images of poly (lactic acid) (PLA) domains at different spinning line positions according to the schematic view of the filament capturing diagram, which was shown on the right side of Figure 3: P0 (A and B), P2 (A and B), P3 (C and D), P4 (E and F), P5 (G and H), P6 (I and J) [32].Reproduced with permission from Tran, N.H.A.; Brünig, H.; Boldt, R.; Heinrich, G., Polymer; published by Elsevier, 2014.

Figure 4 .
Figure 4. SEM micrographs of polypropylene (PP)/polystyrene (PS) extrudate fiber and blend fiber taken at 500 m/min from (a1 and a2) a longitudinal section and (b1 and b2) a cross section after removing the dispersed PS phased in solvent.The dark spots on the cross section represent PS phases.The weight percent of PS phase in blend fiber is 8%; the zero-shear viscosity ratio of PS/PP is 10.8 [31].Reproduced with permission from He, H.; Chen, L.; Zhang, Y.; Hong, S.; Zhou, Y.; Zhu, M., Fibers and Polymers; published by Springer Nature, 2014.

Figure 3 .
Figure 3. SEM images of poly (lactic acid) (PLA) domains at different spinning line positions according to the schematic view of the filament capturing diagram, which was shown on the right side of Figure 3: P0 (A and B), P2 (A and B), P3 (C and D), P4 (E and F), P5 (G and H), P6 (I and J) [32].Reproduced with permission from Tran, N.H.A.; Brünig, H.; Boldt, R.; Heinrich, G., Polymer; published by Elsevier, 2014.

Fibers 14 Figure 3 .
Figure 3. SEM images of poly (lactic acid) (PLA) domains at different spinning line positions according to the schematic view of the filament capturing diagram, which was shown on the right side of Figure 3: P0 (A and B), P2 (A and B), P3 (C and D), P4 (E and F), P5 (G and H), P6 (I and J) [32].Reproduced with permission from Tran, N.H.A.; Brünig, H.; Boldt, R.; Heinrich, G., Polymer; published by Elsevier, 2014.

Figure 4 .
Figure 4. SEM micrographs of polypropylene (PP)/polystyrene (PS) extrudate fiber and blend fiber taken at 500 m/min from (a1 and a2) a longitudinal section and (b1 and b2) a cross section after removing the dispersed PS phased in solvent.The dark spots on the cross section represent PS phases.The weight percent of PS phase in blend fiber is 8%; the zero-shear viscosity ratio of PS/PP is 10.8 [31].Reproduced with permission from He, H.; Chen, L.; Zhang, Y.; Hong, S.; Zhou, Y.; Zhu, M., Fibers and Polymers; published by Springer Nature, 2014.

Figure 4 .
Figure 4. SEM micrographs of polypropylene (PP)/polystyrene (PS) extrudate fiber and blend fiber taken at 500 m/min from (a1 and a2) a longitudinal section and (b1 and b2) a cross section after removing the dispersed PS phased in solvent.The dark spots on the cross section represent PS phases.The weight percent of PS phase in blend fiber is 8%; the zero-shear viscosity ratio of PS/PP is 10.8 [31].Reproduced with permission from He, H.; Chen, L.; Zhang, Y.; Hong, S.; Zhou, Y.; Zhu, M., Fibers and Polymers; published by Springer Nature, 2014.

Figure 5 .
Figure 5. Morphology evolution of PP/PS blend fibers at various take-up velocities (v) along the spinning line (x).The weight percent of the PS phase in the blend fiber is 8%; the zero-shear viscosity ratio of PS/PP is 16.7.

Figure 5 .
Figure 5. Morphology evolution of PP/PS blend fibers at various take-up velocities (v) along the spinning line (x).The weight percent of the PS phase in the blend fiber is 8%; the zero-shear viscosity ratio of PS/PP is 16.7.

Figure 5 .
Figure 5. Morphology evolution of PP/PS blend fibers at various take-up velocities (v) along the spinning line (x).The weight percent of the PS phase in the blend fiber is 8%; the zero-shear viscosity ratio of PS/PP is 16.7.

Figure 6 .
Figure 6.Number-average diameter of droplet versus distance from spinneret.Error bars show the maximum and minimum of the number-average diameter, and open symbols show the average diameter of the analyzed SEM micrographs of samples captured at each spinning line position.Symbols are connected with B-Spline solid lines [31].Reproduced with permission from He, H.; Chen, L.; Zhang, Y.; Hong, S.; Zhou, Y.; Zhu, M., Fibers and Polymers; published by Springer Nature, 2014.

Fibers 2019, 7 , 35 8 of 15 1 Figure 9 .
Figure 9. Atom force microscopy images of the surface patterns of PP/PS gradient fibers after hot-drawing, before (left column) and after (right column) dissolving PS.The upper and lower rows show the surfaces of the fibers processed with v = 30 m/min and aspect ratio of capillary AR = 2 and 57, respectively.The weight percent of PS is 20% and the viscosity ratio of PS/PP is 2.45.Arrows indicate the fiber axis [6].Reused with permission from Pan, D.; Hufenus, R.; Qin, Z.; Chen, L.; Gooneie, A., Macromolecular Materials and Engineering; published by John Wiley and Sons, 2018.

Figure 10 .
Figure 10.Schematic representation of the affine deformation of a single drop in matrix before and after deformation. and λ are the initial and final lengths of the specimen, respectively. is the initial drop diameter and λ is the major axis of the elongated droplet.

Figure 10 .
Figure 10.Schematic representation of the affine deformation of a single drop in matrix before and after deformation.L 0 and λL 0 are the initial and final lengths of the specimen, respectively.D 0 is the initial drop diameter and λD 0 is the major axis of the elongated droplet.

Fibers 2019, 7 , 14 Figure 12 .
Figure 12.Collision of two droplets in simple shear flow with drainage of the film in between.

Figure 12 .
Figure 12.Collision of two droplets in simple shear flow with drainage of the film in between.