Nano-Structured Optical Fibers Made of Glass-Ceramics, and Phase Separated and Metallic Particle-Containing Glasses

: For years, scientists have been looking for different techniques to make glasses perfect: fully amorphous and ideally homogeneous. Meanwhile, recent advances in the development of particle-containing glasses (PCG), defined in this paper as glass-ceramics, glasses doped with metallic nanoparticles, and phase-separated glasses show that these “imperfect” glasses can result in better optical materials if particles of desired chemistry, size, and shape are present in the glass. It has been shown that PCGs can be used for the fabrication of nanostructured fibers—a novel class of media for fiber optics. These unique optical fibers are able to outperform their traditional glass counterparts in terms of available emission spectral range, quantum efficiency, non-linear properties, fabricated sensors sensitivity, and other parameters. Being rather special, nanostructured fibers require new, unconventional solutions on the materials used, fabrication, and characterization techniques, limiting the use of these novel materials. This work overviews practical aspects and progress in the fabrication and characterization methods of the particle-containing glasses with particular attention to nanostructured fibers made of these materials. A review of the recent achievements shows that current technologies allow producing high-optical quality PCG-fibers of different types, and the unique optical properties of these nanostructured fibers make them prospective for applications in lasers, optical communications, medicine, lighting, and other areas of science and industry.


Introduction
The ground-breaking discovery done in the 1960s by Charles K. Kao on fibers of very pure glass possessing very low absorption losses allowed fiber optics to transfer from the theoretical to the practical. High purity silica-glass fibers with losses of about 0.2 dB/km led to the development of fiber-optic communications, which nowadays connect millions of people all over the world. Optical fibers became a perfect host for laser development. They can be used to measure strain, temperature, and pressure just to cite a few applications. Despite this tremendous success, the fiber-optics is still a rapid and active developing area of science.
Made of glass, optical fibers inherited all positive and negative properties of this material. Glasses are easy and inexpensive to produce on any scale and in any shape, they can possess high chemical stability and mechanical strength, and have high transparency. However, they could hardly compete, for example, with crystalline materials in thermal conductivity, or rare-earth elements' absorption, emission crosssections, and available transparency range. Recent advances in glass science showed that properties of this material can be significantly improved if some additional phases are formed or impregnated in the glass. In particular, advances have been achieved in the development of particle-containing glasses: glass-ceramic materials, glasses doped with metallic nanoparticles, and phase-separated glasses. To date, these particlecontaining glasses have become quite common and actively used in case of the bulk materials, but are still rather new for fiber optics.
The purpose of this review is to summarize recent advances in the fabrication of structured fibers made of particle-containing glasses, their potential benefits, their actual properties, and their potential applications. The review covers three types of particle-containing glasses (PCG): crystalline dielectric particles, i.e., glass-ceramics; metallic nanoparticles (MeNPs); and dielectric amorphous particles, i.e., phase-separated glasses.
First, we consider properties of the PCG bulk materials, their potential benefits over the homogenous materials (Section 2), their fabrication (Section 3), characterization methods (Section 4) and factors influencing the transparency of these materials (Section 5). Since to a large extent we deal with the same material when referring to bulk glass and their corresponding optical fibers, ideas and methods used for the bulk materials can be applied to fibers too. Nevertheless, there are, of course, many peculiarities during the fiber fabrication process, which are considered in Section 6. The last part of the review is focused on the recent experimental advances in the fabrication of PCG fibers, their properties, and their applications available in the scientific literature (Section 7).

Glass-Ceramics
The first glass-ceramic (GC) was discovered in the 1960s by Stookey who defined GCs this way: "Glass-ceramics are made by first melting and forming special glasses containing nucleating agents and then causing controlled crystallization of the glass" [1]. Since then, interest in novel GCs has increased. New GCs with promising properties have been developed in the past six decades leading to new knowledge and fundamental understanding of the nucleation and growth mechanisms in glasses and so to an updated definition for GC: "Glass-ceramics are inorganic, non-metallic materials prepared by controlled crystallization of glasses via different processing methods. They contain at least one type of functional crystalline phase and a residual glass. The volume fraction crystallized may vary from ppm to almost 100%" [2].
Glass-ceramics possess various advantages compared to glasses. They possess better mechanical and thermal properties than glasses. As the transparency of the first GC was sufficiently good (up to 90% in the visible wavelength range), imaging through short path lengths was possible, leading to the commercial cookware application [3]. This work became a baseline and led to discovery of many new transparent glassceramic systems [4][5][6], just to cite the first transparent GCs. It was shown that glass-ceramics could be easily treated and also drawn into fibers [7]. enhancement factor depends on the emission wavelength: the closer is an optical transition to the localized surface plasmon resonance (LSPR) band, the higher is the increase [24]. Nevertheless, a significant effect can be observed even far from the resonance frequencies, as it was demonstrated for Er 3+ 4 I13/2 → 4 I15/2 transition (~1.54 µm) in presence of Ag- [25] and Au-NPs [26]. The presence of MeNPs can also affect and enhance the up-conversion efficiency in Er 3+ -MeNPs co-doped materials [20,27].
To understand mechanisms laying behind these phenomena, many experiments with precise control of fluorophore-metal distances at the nanometre scale have been performed [28][29][30][31][32][33]. Today it is commonly accepted that there are three possible mechanisms responsible for the MEF effect. (1) The first is the enhancement of the local incident field in the presence of the metal particles in the proximity of the emitting centre [34]. The incoming electromagnetic waves excite collective oscillations of the nanoparticles' conduction band electrons, known as LSPRs, producing electrical fields that are locally concentrated. In this case, metals operate like a nanoscale antenna allowing one to achieve the local field intensity enhancement up to ~12,000 [35], subsequently increasing the rate of excitation of the fluorophore [34]. (2) The second possible mechanism is that the metal in the vicinity of a fluorophore can influence its radiative decay rate [34]. This gives a possibility to control the decay rate; i.e., so-called radiative decay engineering. Theory predicts that the increase in the decay rate can be up to 10 6 -fold. This should result in the quantum yield of the fluorophore near unity and very short emission lifetime [36]. (3) The last possible mechanism is fluorophore-metal resonance energy transfer. In this case, after excitation the fluorophore can induce oscillations in the metal and excite plasmons; i.e., the fluorophore-metal couple can be considered in terms of a donor-acceptor pair concept. The optical emission occurs not from the fluorophore but from the excited plasmon. However, in contrast to a classical donor-acceptor pair, the plasmon emission can match precisely with the usual emission spectrum of the fluorophores [37]. Thus, if the transfer is efficient and fast, the overall emission quantum yield becomes equal to the quantum yield of the plasmons, which can quench and enhance the emission of the system. The typical lifetimes of plasmons are very short (~10 fs), and this mechanism results in a decrease of the emission lifetime.
The dominant MEF mechanism depends on many factors. However, one of the key factors for different systems is fluorophore-metal distance. Excessive proximity often leads to a significant quenching of luminescence [33,38]. To achieve the maximum effect both the fluorophore and MeNPs should be at some optimal distance, which varies depending on the system from nm to tens of nm [32,39]. Recent research considers that the quenching is not fundamentally obligatory and mostly depends only on the ability of the induced surface plasmons to emit (or not) the light. Besides these three mechanisms, it is also proposed that the MeNPs could serve as chemical absorbents of OH-groups, increasing the number of hydroxyl-free optical centres; e.g., Er 3+ ions [26].
The effect of local electromagnetic field enhancement due to LSPR in presence of MeNPs can be used for different types of surface-enhanced spectroscopies. In particular, surface-enhanced Raman scattering (SERS) is characterized by enhancements of up to 10 8 in the Raman cross-section of analytes bound to MeNPs [40,41]. The resonance wavelength of the LSPR depends on many factors, including the particle size and shape, chemical composition, and their dielectric environment [41][42][43][44]. The latter makes it possible to follow the changes in the MeNPs environment, controlling the LSPR band properties. Therefore, the effects observed in the presence of MeNPs are widely used for surface-enhanced spectroscopies techniques and sensing applications.
The local enhancement of the electromagnetic field close to the surface of the MeNPs also modifies the linear and nonlinear optical properties of the glasses. Particularly, the value of their Kerr coefficient can be enhanced by several orders of magnitude in comparison to the same host medium without the MeNPs [45]. It is suggested that the high optical nonlinearity is due to an increase of the electron temperature caused by the incident laser beam, which determines short response fast relaxation times of several to tens of picoseconds [45,46]. These features make MeNP-doped glasses attractive for optical switching and computing.

Preparation of Particle-Containing Glasses
Glass-ceramics are usually fabricated using a two-step process. (1) The first step consists of preparing a homogeneous glass, which can be done using several methods, with the conventional melt-quench technique being the most common one. However, significant fluorine loss can occur when melting an oxyfluoride glass at high temperature (1400-1700 °C), limiting the fluorine content in the glass [47]. High metal content silicate glasses, for example, glasses within the ZrO2-SiO2, HfO2-SiO2, and La2O3-SiO2 systems, have high melting temperatures (>1700 °C) [48], and their melts tend to demix or crystallize upon quenching [49]. The sol-gel technique is an alternative process to prepare glasses, especially oxyfluoride [50] and metal-silicate compositions [51,52]. It allows the preparation of novel glasses at a lower temperature compared to the conventional melt-quench process, achieving a wider range of compositions, in particular, a high amount of fluorine in the glass with better dispersion of the components. Additionally, the sol-gel technique is handy, flexible, and quite cheap. (2) The second step in the fabrication of glassceramics includes the heat treatment of the starting glasses under specific heating conditions. The heattreatment can lead to surface and/or volume precipitation of the dielectric crystals (hereinafter just "crystals"), but volume crystallization is desirable for the preparation of transparent GCs. In most of the GCs, this volume crystallization can be favoured by adding nucleation agents. Usually, the heat-treatment is done using a two-step process. During the first heat treatment, the formation of the precursors of the crystalline phases, i.e., nucleation, is happening. The temperature during this step should be high enough to achieve mobility of the ions in the glass matrix, but not too high, to avoid dissolution of the nuclei or extensive growth of the crystals. After, the nucleated glass is heat-treated at a higher temperature so that the nuclei can grow into larger crystals. The temperature during the growth step should be close to the crystallization temperature of the glass, that the heat treatment leads to the precipitation of crystalline particles within the glass matrix. During this step, the nuclei grow continuously, and their volume increases, until they are impeded by neighbouring crystals. Then, secondary growth is observed, resulting in the fusion of smaller crystals to larger ones. The size and concentration of the crystals are determined by the temperature and the duration of the thermal treatments and by the chemical composition of the glass.
The heat treatment can lead to phase separation and to devitrification of the glass, resulting in the formation of amorphous or crystalline (dielectric or metallic) particles in the bulk material. Although these processes have been described in various papers and books [53][54][55][56], this conventional heat-treatment method is very complex to control experimentally. Phase separation in glass is a phenomenon in which a homogeneous glass separates into two or more glass phases of different compositions [57]. This effect is observed only for glasses of the compositions within an immiscibility gap. The binodal or spinodal mechanism of the demixing depends on the composition of the glass and usually results in the formation of isolated droplets or interconnected structures, respectively. For the moment, these ranges are rather wellknown for borates [58], borosilicates [59], metal oxide-silica [60], tellurite [61,62], and other glass systems. Usually, the decomposition is performed in a single step by an isothermal heat-treatment at a temperature above the glass transition temperature (Tg). The degree of the demixing depends on time and temperature of the heat treatment and chemical composition. For more detailed information on the decomposition of the glasses, its mechanisms, and its nature, please refer to the reviews [57,63].
For the formation of the MeNPs, a glass should contain ions of the desired metal in their composition. Besides conventional melt-quenching and sol-gel techniques, the ions can be introduced by ion-exchange [64][65][66]. Not all metals tend to form clusters and can be easily reduced to metal under heat treatment. Therefore, the most common metals to form MeNPs in glass are gold and silver, sometimes copper, and nickel. The growth and nucleation of MeNPs can be controlled through subsequent annealing procedure above the glass transition temperature, which is usually done by a single step isothermal heat-treatment. It is important to note, that being at the beginning in the form of ions, the metals need to be reduced to form MeNPs. This may require the introduction of additional polyvalent ions, such as antimony [67] or iron [66], capable of serving as an electron donor, limiting the yield of the MeNPs formed.
Unfortunately, as of today, there is no general and precise empirical or theoretical model, that would allow one to predict of the crystallization process or phase separation for a glass a given chemical composition. Phase separation, the formation of metallic nanoparticles and/or crystallization could occur simultaneously during the heat-treatment, having a huge influence of the resulting material. In particular, the influence of the phase separation on the crystallization behaviour of the glasses can enhance or suppress the devitrification depending on the composition and is still under active investigation. The formation of MeNPs could be accompanied by the precipitation of some dielectric crystals, as it was found by da Silva et al. [20]. Phase diagrams can be used to design and estimate the crystals precipitating in novel GCs. Numerical tools are also under development to simulate the formation of the nanoparticles. For instance, molecular dynamics allow simulating the formation of phase-separated nanoparticles in oxide [68], aluminosilicate [69], and oxyfluoride [70] glass optical fibers. Reviews on the preparation methods and properties of transparent glass-ceramics can be found in [71,72].
To overcome the limits of the classical heat-treatment approach, alternative methods and some modifications in the preparation technique have been proposed. MeNPs can be formed by direct ion implantation in the glass. This was demonstrated for Ag [73], Au [74,75], Cu [76,77], Ni [78], and for different metal pairs [77,79]. Commonly, positive ions are used for the implantation, which after requiring a charge compensation for the formation of the neutral particles, may cause glass elements migration [73]. Alternatively, the use of negative ions allows obtaining the charge balance due to the secondary electron emission from the sample [76,78]. Ion implantation makes it possible to achieve a concentration of Meatoms higher than the solubility limit in target materials without any heat treatment. The technique is suitable and versatile since virtually any element can be introduced in the glass, and moreover, the method allows material direct patterning.
It was demonstrated that silver particles in ion-exchanged glasses could be obtained by electron-beam irradiation, allowing higher yield and concentration, speed and reproducibility, a homogeneous arrangement of particles, and a narrow distribution in size of the particles [80]. Laser irradiation also can cause reduction of the ions. It was found that the irradiation of Au2O3-doped silicate glass samples with a femtosecond laser could locally reduce Au + to metal, which can serve as the nuclei for the formation of the MeNPs during the subsequent heat-treatment [81]. This allows controlling the formation of the MeNPs inside a bulk sample with a high spatial resolution.
Lasers and electron beams (E-beams) have been also used to precipitate crystals within the glass matrix [82,83]. However, these techniques are not easy to use, as most of the glasses are stable against crystallization. GCs have been also obtained from controlled cooling of the melt which was found to be an alternative, effective approach to fabricate transparent GCs [84]. A REE-doped phosphosilicate transparent GC was obtained by melting followed by a devitrification during cooling [85]. Nakanishi and Tanabe prepared GCs using the ''frozen sorbent method" [86]; the GC was prepared by quenching a melt of a composition outside the glass-forming region. Several oxide GCs were successfully prepared using this technique. These methods do not require additional isothermal treatment steps.
GCs can also be prepared by sintering glass powders. A variety of low-melting glasses, including borate and heavy metal oxide-based glasses, have been under investigation due to their sufficient chemical stability. Borosilicate glass was successfully sintered with the Y3Al5O12: Ce 3+ (YAG: Ce 3+ ) crystals [87]. However, it is important to note that the transparency levels of the GCs prepared using this technique are typically less compared to the GCs prepared by heat-treatment of the glasses, due to the scattering from the remaining pores and grain boundaries.
Another approach to prepare glass-ceramics is to incorporate REE-doped nanocrystals, also called active nanoparticles (NPs), in the glass. This approach provides a host lattice structure for rare-earth ions and specified, tuneable luminescence properties [88]. In this approach, the glass is prepared with active nanoparticles, so the rare-earth ions are uninfluenced from the host network [89]. Such glass combines the low cost and the mechanical stability of the glass and the augmented luminescence properties of the NPs. The crystalline nanoparticles can be dispersed in the doping solution when preparing a glass using the modified vapor chemical deposition technique or in the glass batch when using the standard melting process. However, an insufficient dispersion of the NPs was reported in melted glass [90]. The dissolution of the NPs can also occur in the glass melt [91,92]. The direct doping of NPs into glass melts was developed as an advanced modification of this technique [93]. In this approach, the NPs are added in the glass batch after the melting at a lower temperature than was used during the melting process. The temperature at which the NPs are added and the dwell time before quenching the glass melt need to be optimized to ensure the survival and dispersion of the NPs in the glass [94,95]. As reported in [96], the survival of the particles depends on the melting conditions and on the composition of the glass and the NPs.

Characterization of PCGs
Various techniques can be used applied to characterize the micro and nanostructures, the chemical compositions, and the optical properties of PCGs.
For the GC and MeNPs, X-ray diffraction (XRD) can be used to determine the crystalline phases formed in the material and the unit cell parameters. The Scherrer equation also allows one to calculate the average size of the crystals [97]. This equation takes into account the broadening of the corresponding Xray diffraction lines due to finite size of coherent scattering area. As the XRD technique acquires the signal from a macro-sized sample, i.e., measuring an average over the sample, this technique does not allow one to characterize the morphology and distribution of the particles formed in the glass.
Detailed structural characterizations of the PCGs can be done using Raman scattering spectroscopy. The spectra are determined by the short-order structure of the materials; i.e., sensitive to amorphous and crystalline inclusions. The minimal spatial resolution of the method can achieve about 200 nm when using a confocal Raman microscope with a UV-laser excitation source [98]; even higher resolution (~50 nm) can be obtained using a nano-Raman implementation of the method [99]. This allows one to image sub-micron crystalline [99,100] and amorphous particles [101,102] in the PCGs. Raman scattering can be also applied to characterize the phase-separated glasses, where sizes of the structures can be well below 100 nm. However, no information about the spatial distribution of the phases can be obtained in this case [103,104].
The nanostructure of the PCGs can be obtained using transmission electron microscopy (TEM) and its high-resolution analogue (HRTEM), as it is demonstrated in [105][106][107][108]. In particular, HRTEM can be used to reveal the lattice planes and the crystal-size distribution. An example of such analysis is shown in Figure  1a-c. Scanning electron microscopy (SEM) is also commonly used to image the surface of the PCGs from nano-to micrometre scale depending on the size of the crystallites and the resolution of the instrument. SEM can also provide information about the composition of the nanophase when combined with energy dispersive X-ray spectroscopy accessory (EDX) [17,[109][110][111][112]. An example of combined a SEM/EDX analysis is shown in Figure 1d. In the case of REE-doped materials, important information can be obtained by the use of absorption and fluorescence optical spectroscopies. Optical characterizations are very useful to discriminate the location of REE-ions as their emission and absorption spectra are strongly affected by the local environment of the REE: in the crystalline environment, the spectra consist of sharp peaks while they are broader when the REE is located in a glassy environment. Fluorescence spectroscopy can reach a sub-micron resolution if a confocal microscope is used for the measurement, allowing one to follow the changes in the optical properties between different phases in the PCGs, especially in the GCs. Similarities in the equipment needed for the Raman and photoluminescence spectroscopies make it possible to use a Raman confocal microscope to measure both the structural and the emission properties in the same area with high spatial resolution [104]. In this case, the type of signal depends on the wavelength of the excitation laser ( Figure  2). Special attention is paid to the determination of the nonlinear properties at 1.55 µm. In the case of the fibers, this is commonly done by the resonant optical nonlinearity measurement using a long-period fiber grating pair, initially proposed by Kim et al. [114]. The method is based on the fact that the change in the refractive index of the fiber core is related to the shift in wavelength arising from the interference between the core mode and the cladding mode of the fiber through the long-period fiber grating pair. For a more detailed description of this method, please refer to the original work [114].

Raman spectroscopy Photoluminescence
The methods mentioned above have become commonly available nowadays in many laboratories. Additional characterization can be done using some more rare methods. X-ray absorption spectroscopy (XAS) can be used to determine the local environment and the redox of a specific element after a heattreatment or in situ [113,[115][116][117][118]. Small-angle neutron scattering (SANS) examines the structure of the PCGs with a characteristic scale of 1-100 nm [119][120][121]. Secondary ion mass spectrometry (SIMS) imaging can be used to characterize the chemical composition with high spatial resolution (60 nm). In particular, SIMS has been applied to evidence the partitioning of P, Mg, and Er elements in phase-separated nanoparticles formed in a silica-based optical fiber [122]. More recently, atom probe tomography (APT) has been employed to characterize, with a sub-nm spatial resolution, the composition of nanoparticles embedded in a glassy matrix [123].

Control of PCGs Transparency
One of the most important requirements when preparing transparent optical PCGs is the light scattering, including Rayleigh scattering, which should be minimized. When the size of the particles is close to the wavelength of the excitation radiation, micro-inhomogeneity occurs, leading to Mie scattering. Therefore, the size of the particles formed should be controlled. In the case of dielectric particles, the inclusions should have a refractive index similar to that of the host glass. According to Hopper [124] nanocrystals with a size <30 nm and a difference between the refraction coefficients of crystalline and glassy phases <0.3 can lead to transparent GCs.
In [125], four empirically determined requirements for ultra-transparency, as expected for optical fiber, were proposed: (i) particle size must be less than 15 nm, (ii) separation between the particles must be comparable to their size, (iii) particle size distribution must be narrow, and (iv) there must be no clustering of particles. Tick suggested that the transmission loss could be, also, minimized of the order of tens of decibels per kilometre by removing all the impurities. Later, Tick et al. demonstrated that the increase in the losses after heat treatment of fiber could be related to the different particle size distribution in the fibers and not to the mean particle size [126].
All these considerations on the characteristics of the nanoparticles aim to design a "transparent" fiber laser or amplifier; i.e., where nanoparticles would have a negligible impact on light scattering. However, light propagation in highly scattering media is a very active research area, leading to tailored light propagation in such media. For instance, by using a spatial light modulator (SLM) to shape the wavefront of the incident beam, light transmitted through a scattering medium can be focused at the output [127] or focused inside the scattering medium [128]. This approach opens new opportunities to promote nanoparticles-doped optical fiber lasers or amplifiers but necessitates one to use free space components such as SLMs which may impede their applications.
Scatterers can also be intentionally embedded in the fiber core to manage light properties during its propagation. For instance, the random fiber laser is a well-known example of photonic devices based on disordered-induced light scattering developed during the last decade. A random laser is a mirrorless laser where the properties of the light generated are defined by random multiple scattering of photons in the optical gain medium. Various configurations have been investigated, such as the dispersion of TiO2 particles in a rhodamine 6G solution [129] or of polyhedral oligomeric silsesquioxanes nanoparticles and laser dye pyrromethene 597 in carbon disulphide [130], injected in the hollow core of a photonic crystal. In conventional telecommunications fiber, the intrinsic disorder (density and refractive index heterogeneities) has been exploited [131]. For a recent review on random fiber lasers, one can read [132]. When the size of the scatterers is about the wavelength, the light can be trapped between these randomly disordered heterogeneities through the Anderson localization mechanism [133]. If the transverse random distribution is longitudinally invariant along the fiber, the light can be guided through the transverse Anderson localization [134]. In such fiber, there is no core-cladding structure. As any location across the transverse section of the fiber guides the light, it can be used to transport an image [135]. One of the main issues related to this class of fiber relies on the ability to prepare long fiber length with invariant transverse random distribution. Several approaches are under investigation and reviewed in this paper [136].

Fiber Fabrication Methods
Most of the PCG fibers are drawn using the rod-in-tube technique [137]. In this technique, the prepared bulk glass is first made into a cylindrical rod through cold working and inserted into a prepared hollow glass tube with a sealed bottom to form a preform. Usually, clad and core glasses have similar compositions and the fiber is drawn near the core glass softening temperature. The use of bulk glasses for the preform preparation ensures tremendous versatility in the chemical composition of the fibers. Nevertheless, contamination on the surface of fiber core and cladding and residual surface defects can restrain its practicability. Moreover, the softening temperature of the core glass is typically higher than its crystallization temperature, making it hard to control the crystallization process during the drawing step, which may result in the growth of large crystals and so in high transmission losses.
The preform can be, also, obtained by the modified chemical vapor deposition (MCVD) technique (see Figure 3), which is the most common process used to prepare special optical fibers in industry. First described by MacChesney et al. from AT&T Bell Laboratories [138], the method is based on the successive deposition of vitreous layers inside a silica glass tube (Figure 3). The chemical composition of the layers can be controlled by use of different reactive gases (mainly SiCl4, GeCl4, and POCl3 and a fluorine carrier, such as C2F6, SF6, or SiF4), which are carried in the tube by oxygen. However, due to the absence of volatile precursors for many elements, the "pure" MCVD technique is mostly used for the fabrication of passive high-silica fibers with common dopants, such as Ge, P, B, and F [139]. Alternatively, the solution doping method can be used to introduce additive elements, among which are rare-earth elements, aluminium, and other modifiers [140]. In this method a porous silica layer, which is formed by MCVD at relatively low temperature, is soaked with a solution (alcoholic or aqueous) of salts of metal chlorides (ErCl3, AlCl3, etc.). When the solution is removed, the porous layer is first dried, and, after, densified and vitrified at a high temperature (up to 1800 °C). It is also possible to introduce a crystalline phase during the doping step, e.g., using a "slurry doping method," which is similar to the solution doping technique [141]. After, during socalled collapse step (at a temperature above 2000 °C), the tube is closed and a preform ready for the fiber drawing is obtained. The particle formation in the glass can be done before, after, or during the fiber drawing step, which is mostly dictated by the composition, type of the end-fiber, and particles to be stabilized. The optical preform is drawn into a fiber on a draw tower at the temperatures above the softening temperature of the glass, which is typically associated with high temperatures; e.g., around 2000 °C for high-silica glasses.
The additional heat-treatment steps, such as drawing (also vitrification and collapsing in the case of MCVD process), can change, drastically, the properties of a PCG: high temperature can lead to devitrification/demixing of the glass, transformation of the crystalline phases, and corrosion or dissolution of the particles. It can also affect the particles' sizes and shapes. Therefore, in many cases, to avoid these uncontrollable effects, it is preferable and easier to perform an additional heat-treatment step after the drawing of a glass fiber. However, even this additional step can reduce the mechanical strength of the fiber, if surface or too-extensive a crystallization is induced.
To ensure the formation of glass (not PCG) during the drawing, the fiber can be obtained directly from a melt. This can be done using the double crucible technique. The optical fiber is fabricated by melting the core and cladding materials in two joint concentric crucibles and the fiber is drawn from the combined melted glass. As shown in Figure 4, the core and cladding glasses are melted in the inner and outer crucibles, respectively. A somewhat intermediate method, which shares some resemblance with the rod in tube and double crucible methods is the melt-in-tube technique. Instead of using clad and core glasses of similar compositions, it is possible to use a combination of glasses. At the drawing temperature, the core is molten, whereas the clad glass is only softened [143], allowing one to avoid the undesirable crystallization of the fiber core glass. The duration of the heat treatment of the glass fiber also needs to be optimized to avoid the distortion of the fiber during the heat treatment.  Since the light in the traditional core-clad fiber propagates mostly along the core, it is not sensitive to the environment of the fiber itself. Therefore, for sensing applications, it is necessary to form the MeNPs not in the bulk, but on the surface of the fiber. If no relevant charge compensation is provided under the heat-treatment of the glass the MeNPs can precipitate at the surface [144]; i.e., a standard post-annealing is capable of producing MeNPs at the surface. However, for better control of the precipitated MeNPs usually, the particles can be deposited at the surface separately. This can be done chemically. In this case, the glass surface is dipped into a solution with pre-synthesized MeNPs for the formation of a self-assembled monolayer of MeNPs on the surface [145][146][147]. Using this approach, it is not only possible to deposit MeNPs on the outer surfaces, but also to form layers of selected MeNPs inside the channels of microstructured optical fibers [146]. The MeNPs can be also obtained by the sputtering technique: first, a Me nano-layer is formed on the glass surface; then a subsequent annealing allows one to transform the layer into nanoparticles and nano-islands [148], whereas the size of the MeNPs depends on the thickness of the initial Melayer and the subsequent heat-treatment procedure.

Glass-Ceramics Fibers
One of the first GC fibers was successfully obtained by Zheng, Hu, and Mackenzie in Bi-Ca-Sr-Cu-O system [149,150]. Slight modification of the glass properties by co-coping with Al or V decreased the crystallization tendency, whereas the drawing from a glass preform at the temperature above the crystallization temperature allowed the authors to avoid full devitrification of the materials during this step. The devitrification occurring during the drawing led to precipitation of only very fine particles inside the fibers, whereas a large number of spherical Bi2(Sr, Ca)2CuOx crystals with an average size of 0.5 µm formed on the surface of the fibers [150]. These crystals did not affect the fiber drawing process. The final ceramization was done by heat-treatment of the fibers. Heat treatment of the Al-containing fiber at 825 °C for 12 h in air atmosphere led to the formation of the Bi4Ca3Sr3Cu4Oy crystals.
For optical applications, silicate GCs are the most popular among GC materials due to their unique thermo-mechanical properties, such as very low thermal expansion coefficients, combined with outstanding optical characteristics, as it is possible to stabilize small enough nanocrystals and in this way avoid the light scattering and achieve high optical transmission even in the UV-blue region. Examples of typical crystals formed in silicate glasses can be found in [71]. The first report on an GC silicate fiber laser was reported in 2001 by Samson et al. [151]. Using the double-crucible and rod-in-tube techniques, NdF3doped GC fiber laser within the SiO2-AlO3/2-CdF2-PbF2-YF3-ZnF2 system was successfully prepared. It was possible to obtain the Nd-doped fluoride crystals in the core of the single-mode optical fiber by its heat-treating at 450 °C for 30 min. The presence of the Nd-doped crystals in the fiber compromised the efficiency of the GC fibers. Such GC fibers could be obtained with low scattering losses as the crystal size was ~10 nm. The work was then focused on transition-metal-doped GC fibers and especially on Cr 4+ -doped forsterite nanocrystalline fiber which displayed luminescence similar to that of a single crystal [152]. This GC combines the radiative properties of Cr 4+ -doped crystals with the advantages of glasses. Later, Samson et al. developed novel Ni 2+ -doped nanocrystalline GC fibers within the SiO2-Ga2O3-Al2O3-K2O-Na2O-Li2O system [153]. The preform was obtained using the rod-in-tube method. Heat treatment of the glass fiber at 850 °C for 2 h led to the precipitation of gallate-rich aluminogallate spinel crystals homogeneously dispersed in the silicate glass matrix. In 2015, Ni 2+ doped GC fiber was successfully prepared using the melt-in-tube method [143]. The temperature of 1830 °C was used to fabricate the fiber; the core glass melted while the clad glass was softened. No signs of element inter-diffusion or crystallization were found in the as-drawn glass fibers and the GC fiber was obtained by heat-treating the glass fibers; LiGa5O8 crystals were found to precipitate in the fiber using a heat treatment at 800 °C for 10 h.
The melt-in-tube method was used recently to prepare GC optical fiber containing Ba2TiSi2O8 crystals as the fabrication of such GC fiber using other techniques is challenging [154]. The authors noted that it was impossible to draw the fiber using the rod-in-tube technique due to the high crystallization rate of the materials (see Figure 5, left panel). In the case of the amorphous fiber, Ba2TiSi2O8 nanocrystals could precipitate in the fiber core evenly with a diameter between 1.0 and 6.0 nm to ensure low transmission loss using a heat treatment at a temperature of about 850 °C for 5 h (see Figure 5, right panel). These studies clearly show that the melt-in-tube fabrication method is a promising new process to obtain GC fibers, which cannot be fabricated using the conventional rod-in-tube method.
Yb-doped GC fiber was also successfully drawn from yttria-alumina-silica GC preform prepared using MCVD [118]. The collapsing step led to the formation of a phase-separated glass with two regions of different compositions. A heat treatment above 1300 °C led to the precipitation of nano-sized particles of YbPO4, which were evidenced by X-ray absorption spectroscopy and by the shape of the emission band which was typical of a structurally ordered phase.
Sakamoto and Yamamoto demonstrated that for Li2O-Al2O-SiO2 it is possible to draw the fibers using pre-crystallized preforms [155]. In this work, it was shown that the drawing step could change the crystalline phase (from β-spodumene to β-quartz) and could reduce the crystallinity. Nevertheless, under optimized parameters, it was possible to get a GC fiber of good quality with a high amount of the crystalline phase. Despite many successes for the silica glass, REEs do not incorporate well into the silicate glass structure. The low solubility of REE in silica glass directly results in a high probability of phase aggregation and even crystallization [156]. Clusters give rise to luminescence quenching at REE concentrations greater than 100 ppm [157]. Silica glass has relatively high phonon energy that increases the probability of nonradiative relaxation of the luminescent ions. As a consequence, this may decrease the emission quantum yield of certain optical transitions [158]. Then, several glasses were developed over time [159], such as, chalcogenides [160] and fluorides [161] which exhibit improved REE solubility and lower phonon energy. However, these glasses are prone to crystallization during the fiber making process. Additionally, they are not as compatible as silicates with the current common optical fiber cable network. In this context, oxyfluoride GC fibers have been also of great interest for the development of efficient amplifiers or lasers in glass-ceramics, as the fluoride environment is beneficial for the rare-earth ions keeping the chemical and thermal stability and the good mechanical properties of the oxide matrix [162]. The first oxyfluoride GC in bulk form having high transparency was reported for the composition 30SiO2-15AlO1.5-24PbF2-20CdF2-10YbF3-1ErF3. This GC was found to possess efficient up-conversion, which was up to several orders higher when compared to the mother fluoride [9]. Since then, there has been much interest in developing novel transparent oxyfluoride glass-ceramics containing REE-doped fluoride crystals. Reviews on transparent oxyfluoride GCs in bulk form can be found in [163] and [108]. Some of the first transparent oxyfluoride GC fibers were with the composition of 48SiO2-11Al2O3-7Na2CO3-10CaO-10PbO-11PbF2-3ErF3 and 48SiO2-11Al2O3-7Na2CO3-10CaO-10PbO-10PbF2-3YbF3-1ErF3 [105]. They were obtained by heat-treating of the glassy fiber at 700°C for various periods of time. The transparent GCs could be obtained when using the treatment shorter than 32 h. Transparent GCs fibers with SrF2 and LaF3 crystals possessing intense Nd 3+ emission were obtained within SiO2-Al2O3-ZnO-Na2O-SrF2 and SiO2-Al2O3-ZnF2-Na2O-LaF3 systems [164]. In this work, Reben et al. showed that the most important parameters to control during fiber drawing were temperature and heating time during the drawing, leading to precipitation of SrF2 nanocrystals in the core of the fiber.
Recently, transparent oxyfluoride Nd 3+ doped fibers with the composition 55SiO2-20Al2O3-15Na2O-10LaF3 GCs were successfully prepared using a single crucible method [165]. After drawing, fibers of 5-10 cm in length were heat-treated between 620 and 680 °C for 5 to 120 h in order to precipitate Nd 3+ doped LaF3 crystals with a size of 10-20 nm. The fibers exhibit a slower crystallization rate than the parent bulk glass, and therefore, the fibers needed to be heat treated at a higher temperature than the parent bulk glass in order to precipitate crystals with similar size and similar crystal fraction. After, the GC fibers were covered with SiO2 cladding using the sol-gel method. In this way, a multimode fiber with losses of about 20 dB/m at 633 nm at the doping level of 0.1% NdF3 was obtained.
Ytterbium-doped oxyfluoride GC fibers were also obtained within the SiO2-Al2O3-CdF2-PbF2-YF3 [166]. It was shown that partial devitrification of the glass occurs during the conventional glass preform drawing process. Alternatively, the glass fiber could be obtained directly from the melt, whereas the crystallization was done by an additional controlled heat-treatment step. The latter approach was found to be preferable to produce transparent GCs with nanocrystals homogeneously distributed along the fiber, as the drawing of a GC preform did not allow fine tailoring of the crystals' sizes, shapes, and distribution along the fiber. Pb1-x-y-zCdxYyYbzF2 (x + y + z ≈ 0.3-0.4) nanocrystals with an average size of ~10 nm were found to precipitate in the fiber heat-treated at 460 °C for 20 h, increasing the photoluminescence quantum yield in the nearinfrared region compared with the glass-fiber.
GCs oxyfluoride fibers with remarkably enhanced Er 3+ 2.7 µm emission under 980 nm excitation were first reported in [167]. The fibers with the core composition 40B2O3-25SiO2-18Na2O-7NaF-10YF3-2ErF3 were obtained using melt in tube technique. Heat treatment at 470-500 °C for 5 h led to precipitation of NaYF4: Er 3+ nanocrystals in the core. The increase in the transmission loss values at 1310 nm from 7.44 to 11.81 dB/m after heat treatment was related to the scattering caused by the precipitated nanocrystals.
Efforts have been also focused on the preparation of GCs transparent up to 12 µm using chalcogenide glasses. The crystallization of chalcogenide glasses has been of great interest [168][169][170][171][172][173][174]. However, the crystallization of these glasses is difficult to control, as reported in [173]; Zhang et al. reported that, as for oxide glasses, the control of the nucleation and crystal growth is very sensitive to temperature and to the glass composition. The temperature of the heat treatment should not be too high so the crystal growth can be controlled. If not controlled, the GC loses its transparency. A reasonable nucleation rate was obtained by varying the duration of the treatment, which could last for up to 15 days in order to observe a significant decrease of the expansion coefficient of the final glass-ceramics. In [175], Zhang et al. reported that it is possible to draw the GC with the composition Ga5Sb10Ge25Se60 into infrared transmitting GC fibers. During the fiber drawing, they noticed that the crystals in the GCs continue to grow. Although the scattering losses in short wavelengths increased, the transmission of the GC fibers beyond 6 µm remained unchanged despite the growth of the crystals during the fiber drawing.
The other technique developed to control the rare-earth optical response independently of the host glass composition involves the incorporation of rare-earth-doped nanoparticles in a glass. This new nanoparticle doping MCVD-process was implemented to fabricate REE-doped fibers. Use of erbium-doped nanoparticles allows one to control better Er 3+ local environment, decreasing the probability of the pairformation and up-conversion level, providing longer luminescence lifetimes; achieving high homogeneity of the dopant along the fiber length erbium-doped fibers; and reducing light attenuation level in the fiber [176][177][178][179]. This approach also works for other REEs [179,180]. Fibers have been prepared by adding other NPs, such as REE-doped Y3Al5O12 (YAG) [181] and LaF3 [182,183] nanocrystals. These nanocrystals, used as precursors, allow one to improve the REE luminescence properties. However, direct proof of the existence of the initial nanocrystals in the final fiber is rarely presented. In the case of LaF3 nanoparticles, it has been clearly demonstrated that the integrity of these nanocrystals is not maintained during the MCVD process [183]. Fluor ions react with silicon and form the gaseous SiF4 compound. Even if the nanoparticles could be imaged in the fiber, their composition was La-silicate, not LaF3. Summary information about various nanoparticles suitable host material composition and their characteristics can be found in [184].

Phase-Separated Fibers
Fabrication of phase-separated fibers is a quite novel area, still having a lot of things to discover. Advances in this area were achieved by the group of W. Blanc. During the fabrication of the silica core using the MCVD process, the sintering of the soaked porous core layer, the collapsing of the tube, and the preform drawing steps require many thermal cycles with temperatures up to more than 2000 °C. These thermal cycles last for only a few seconds to a few minutes at each pass or step at specific point of the fiber. Nevertheless, due to this thermal treatment, inherent to the MCVD process, nanoparticles can be formed in situ through the phase separation mechanism by introducing, through the doping solution, alkaline earth elements, such as magnesium [185], calcium [186], or scandium and yttrium ions [187], resulting in the particles of nm-range size. Later, phase separation was obtained for Mg and La-doped silicate fibers [188,189]. The small size of the nanoparticles allows one to ensure low scattering losses, and at the same time, a significant broadening of the Er 3+ emission spectrum was observed (Figure 6a). It is important to note, that the formation of the nanoparticles in these works did not require additional post-heat treatment of the fibers as the nanoparticles formed during the collapsing step of the MCVD process [190]. The particles survive the high-temperature drawing process. However, from the geometrical considerations, it is clear that their shape should evolve. Recently, to shed more light on this question, Vermillac et al. studied the morphologies of oxide particles in optical fibers [191,192]. It was found that during the drawing step, the spherical particles present in the preform could be elongated and even broken up into smaller particles (Figure 6b). The break-up phenomenon can be favoured by decreasing the drawing temperature (increasing drawing tension). This top-down approach (starting from "big" particles in the preform and finishing with "small" nanoparticles in the fiber) opens a new strategy to control the final size of the nanoparticles in the fibers. The size control of nanophases in fibers provides a great opportunity for new applications. One of the most trivial examples is the development of the light-diffusing fibers used for illumination [193]. In these fibers, the scatterers (which can be air bubbles with a typical size of 50-500 nm) are located in a ring around the fiber core. Despite the apparent simplicity of this approach, one of the main issues relies on the ability to keep the scattered light intensity constant all along the fiber [194]. Sensors were recently developed, based on the enhanced nanoparticle-induced backscattered light and the optical backscatter reflectometry. The fabrication method for these sensors is simplified since there is no need for inscribing reflective elements (such as fiber Bragg gratings) or fabricating microstructures in the fiber. A fiber-optic refractive index sensor was demonstrated by simply etching a high-scattering nanoparticle-doped fiber in hydrofluoric acid [195,196]. A setup for multiplexed distributed optical fiber sensors, which are capable to measure temperature in the range of up to 140 °C (of interest for biomedical applications such as thermotherapy) with a spatial resolution of 2.5 mm over the several fibers simultaneously, has been reported in [197]. Finally, this approach is also applicable for strain measurements and 3D shape sensing [198,199].

MeNP-Containing Fibers
To date, most of the efforts have been focused on the fabrication of MeNP-doped silica fibers. Temperatures of about 2000 °C used for the drawing of high silica fibers are lower than the boiling point but high above the melting point of most of the metals. Therefore, MeNPs can survive, and the precipitation of the MeNPs is often performed by heat-treating the preform before the drawing; however, the drawing can change the nanoparticle characteristics dramatically. It is complicated to control the particle size and distribution, making the fabrication of the fibers with particular optical properties more challenging. Ju et al. demonstrated that the MCVD technique can be used for fabrication of Au-NP-doped silica-fibers, but, a shift of the Au-resonance absorption band was observed after the drawing when compared to the preform [200]. This shift was attributed to the recrystallization of the Au metal at high temperatures. Recently de Oliveira et al. studied different ways to produce Au-NP-doped silica fibers in detail, and mentioned that the drawing of a preform, that already has MeNPs inside (see Figure 7a), could result in the fluctuations in the NPs concentration over the length of the fiber, with the formation of regions with higher concentrations of gold clusters. These gold clusters are highly scattered and increase optical losses [201]. Several studies showed that this problem could be solved by co-doping with Al, which was found to lead to a better dispersion of Au-NPs in the final fiber and so to better optical performance [200][201][202].
In the recent work of de Oliveira et al. [201] it was demonstrated that annealing of the fiber under reducing conditions results in the particles similar to the case for nanoparticles formed in the preform, allowing one to reach the concentration of the Au-NPs with resonance absorption band intensity >800 dB/m. At the same time, the fiber is fully spliceable and can be handled in a common way. Better control of the NPs growth process can be achieved if the fiber is exposed to local heating using a CO2 laser instead of being heat-treated in a furnace. The IR irradiation is well absorbed by silicate glasses, allowing one to locally change the temperature and to achieve resolution in the NPs nucleation regions of about 100 µm in fiber length. Changes in the laser power and in the number of scans can be used to precisely control the process of the MeNPs formation via one or two-step procedure, producing fibers with different NP concentrations and size distributions (see Figure 7b).
Despite the difficulties in the fabrication of MeNPs containing fibers, potential enhancement in the luminescence properties inspires scientists to improve the spectroscopic properties of REE-doped fibers using MeNPs. Significant efforts in the development of MeNP-doped optical fibers were performed by the group of W.-T. Han [203][204][205]. In particular, it was demonstrated that co-doping of Er 3+ -doped germanosilicate optical fiber with Au-NPs allowed increasing the emission intensity under 980 nm excitation about 20% [203]. Authors ascribed the observed enhancement to the absorption of hydroxyl groups by Au-NPs. However, the MeNPs co-doping also can lead to a decreased radiative emission rate; i.e., suppressing the REE luminescence [206]. The other possible reasons for this are the extensive scattering and the additional losses caused by the high MeNPs concentration [206,207].  In comparison to traditional surface sensing systems based on the plasmon resonance effect and including an optical prism in the setup, sensing configuration based on an optical fiber allows one to fabricate a small sensing element with a simplified optical design, which requires only a small sample volume and has great potential for use as disposable fiber-optic sensors and the capability for use in remote sensing [208]. For a sensor fabrication, an unclad region of the fiber can be coated with metal-layer or MeNPs. Commonly, the sensing is based on the evanescent light field absorption in the fiber, which is analogous to attenuated total reflection (ATR) spectroscopy. The sensitivity of the method depends on the length of the sensing (modified) part of the fiber [145] and the morphology of the deposited nanoparticles [209]. A LSPR-sensor based on a modified standard telecommunication single-mode fiber can achieve the sensitivity of about 10 −5 RIU [210].
As an alternative to the outer surface, the MeNPs can be deposited on the inner surfaces of a microstructured fiber-the theoretical consideration of such a configuration has predicted its high sensitivity [211]. This approach was successfully realized in the work of A. Csaki et al. [146]. In this study, Ag and Au nanoparticles of different sizes and shapes were deposited inside the channels of microstructured optical fibers with high coating uniformity (see Figure 8). Experimental results agreed well with the theoretical calculations. Moreover, a proof-of-principle sensing experiment demonstrated high sensitivity (up to 78 nm RIU −1 ) of the obtained sensor and its potential. Nowadays NIR lasers based on different REEs dominate various practical applications. In particular, Er-doped lasers and amplifiers emitting at around 1.55 µm are used for telecommunications-the application area where the MeNP-doped fibers could be used for optical switching. It is important to note here that the enhancement of the nonlinear properties is the most pronounced for the laser wavelengths, which are in resonance with the plasmon modes of the MeNPs [212]. For the most common Au and Ag particles, the resonance band is typically observed in the visible range. The position of the resonance band can be controlled by the size of the MeNPs and the precipitation of bigger particles can shift the resonance band towards lower energies. The broader tunability range of the resonance can be achieved by an extensive control of the particles geometry and using multipolar plasmon oscillations. In particular, it was demonstrated that the resonance band in the region up to 1 µm can be achieved with a change in length of the Ag nanorods [213]. Nevertheless, even far from the resonance frequencies, e.g., at 1064 nm, nonlinear susceptibilities of the MeNPs in colloids are in order of 10 −14 ESU [212], which is about two orders higher when compared to amorphous SiO2 at the same wavelength [214]. Therefore, the properties of the MeNPs will determine the final nonlinear susceptibility when embedded in commonly used optical glasses, such as silica.
In practice, it was demonstrated that the formation of Au-NPs in silica glass fiber permits one to achieve the nonlinear refractive index (n2) of about 10 −16 m 2 /W, which is several times higher in comparison to the reference fiber without the MeNPs [215]. To date, it has been shown that the final nonlinearity depends on the chosen metal, the concentration, and the dispersion of the NPs [202,216,217]. As was already mentioned above, co-doping with Al usually improves the dispersion of the MeNPs in the fiber and can enhance the nonlinear properties [202]. However, this is not always the case. According to Lin et al., high resonant nonlinearity in Ag-NP-doped fibers can be obtained in Al-free fibers [216]. Later, the authors demonstrated that this level of nonlinearity is enough for all-optical switching applications at 1.55 µm [217]. In more recent study on Au-NP-doped fibers it was demonstrated that a higher concentration of the nanoparticles can be achieved in the fiber, resulting in n2 = (6.75 ± 0.55) × 10 −15 m 2 /W; i.e., five orders of magnitude higher than that of silica glass [201].

Conclusions
It is proven that particle-containing glasses, i.e., glass-ceramics, glasses doped with metallic nanoparticles, and phase-separated glasses, provide additional freedom degrees in the tuning of material properties compared to the traditional glasses. Moreover, these materials can be obtained in fiber form, resulting in novel materials for fiber optics-nanostructured fibers. These PCG-fibers have demonstrated a significant enhancement of the spectroscopic properties, increase in detection sensitivity, higher nonlinearities, and other advances over traditional glass fibers. However, only PCGs with desired chemistry, size, and shape of particles in the glass have a positive impact on glass properties.
This review demonstrates that today, the synthesis of nanostructured PCG-fibers is still a challenging task. Different methods of the PCG-fibers' fabrication are considered. It is shown that nanostructured fibers, with the compositions close to SiO2 glass, can be obtained by modification of the common MCVD process. At the same time, other fiber drawing techniques like rod-in-tube, melt-in-tube, or double crucible methods allow one to broaden the possible chemical composition spectrum and provide extensive control of the formation of the nanoparticles. Recent advances show that, in many cases, additional processing steps during the fiber drawing change the properties of the particles present in the material-being in most cases a negative effect, leading, for example, to extensive crystallization of the fiber and high scattering losses; sometimes, it can be also used as a benefit, making it possible to synthesize the nanoparticles in situ or modify the particle size and shape during the drawing step.
Even though in many cases PCG-fibers still require significant improvement in terms of the optical quality, it has been shown these fibers can possess unique optoelectronic characteristics, which could be useful for many practical applications, such as lasing, optical communications, medicine, lighting, sensing, and others. Further development of the nanostructured fibers requires a search of novel chemical formulations, cutting-edge fabrication, and characterization techniques and a fundamental understanding of the theoretical and technological problems. Nevertheless, the potential benefits of using these unique materials for everyday life, science, and industry are clearly worth the trouble of investigating nanostructured PCG-fibers.
Author Contributions: This article has been written by the following authors. A.V.: MeNP-doped glasses and fibers; L.P.: glass-ceramic materials; Z.L., M.V., F.P., and W.B.: phase-separated glasses and fibers. All authors are aware of its content and approved its submission.
Funding: A.V. and L.P. would like to thank the Academy of Finland (Flagship Programme, Photonics Research and Innovation (PREIN-320165) and Academy Project Numbers 326418, 316483) for funding of this research.