After-Machining Surface Layer of Composite Coatings Obtained by Thermal Spraying

: The surface of machine elements is changed to improve their mechanical properties. Ceramic-metal composite coatings are mainly used to increase the durability of machine parts. Therefore, new materials are constantly searched for application in the future development of metal and ceramic composites. The nickel and iron elements are usually used as a base and Al 2 O 3 as tough particles. The welding technology for applying alloy and composite coatings is widely used. The common technology used to apply composite coatings is thermal spraying. It is a simple technology and very useful for the production or regeneration of machines. The surface layer is very rough and porous after applying the coating by thermal spraying. In order to obtain the proper surface quality of alloy and composite coatings, after-machining should be used. Many parts of machines strive to achieve an accurate surface. Therefore, a certain roughness is often required. The arithmetic mean of the ordinates of the surface roughness proﬁle was (Ra = 0.16–1.25 µ m). The article presents the inﬂuence of ﬁnishing on the roughness of the surface layer of the coating. After plastic working and machining, the roughness of the surface layer of the coating was reduced. However, it can be seen that, after plastic working, there is a strengthening of the surface layer of the coating and most of the pores were closed.


Introduction
The engineering materials such as metals, polymers, ceramics and composites are constantly used in the production and regeneration of machine parts. Composite materials are of great interest in mechanical engineering. One of the widely used groups of composites are those based on metals and ceramics. Composites are used in the energy, electronics, petrochemical, military, automotive, aviation, shipbuilding and other industries. Coatings can also be distinguished among composites. The composite coatings obtained by thermal spraying have a large surface roughness. Therefore, these coatings must be subjected to finishing. The most commonly used machining types are finishing, turning and grinding. Flame spray coatings are applied taking into account the allowance for finishing. Aftermachining should ensure not only adequate coating thickness associated with the nominal size of an object but also to obtain the required surface roughness and waviness. Surface texture is very important where it has a direct influence on the quality of the elements' machine parts. Therefore, it has to be defined as precisely as possible with the help of standardized surface texture parameters. The best tool contour and angles and shape and grade inserts should be selected to obtain a minimum surface roughness.
The coatings are applied and often reflect the shape of the actual surface of the substrate. The structure of thermal sprayed coatings is characterized by, among other things, high porosity and considerable roughness. Thermal spraying is a technology that does not allow for precise control of the thickness of the coatings. Due to these considerations, coatings obtained by thermal spraying require the use of an after-machining. The coatings

Materials and Methods
The composite coatings are characterized by oxide inclusions, porosities, and the presence of a strongly developed surface after being flame sprayed. The finishing coats should be used in order to obtain the appropriate surface texture. For this purpose, burnishing, rolling, turning or grinding can be applied. Ni-Al alloy and Ni-Al-Al 2 O 3 composite coatings, obtained by flame spraying, were investigated. The samples with shafts shape of steel C45 (ArcelorMittal, Dąbrowa Górnicza, Poland) (C-0.45%, Cr-0.4%, Mo-0.1%, Mn-0.7%, Si-0.3%, Ni-0.4%, P-0.045%, S-0.045%) [26] and spraying coatings were researched. The flame sprayed coatings were characterized by appreciable value of surface roughness. The surface roughness obtained by flame spraying was not satisfactory with respect to the service qualities because large values were reached. The tests were carried out on nickel alloy and nickel composite coatings on a C45 steel matrix using the subsonic flame spray method. The coatings were prepared with such materials as powder ProXon 21021 (Ni-94%, Al-5%, B-1%) and its combination with powder MetaCeram 28020 (Al 2 O 3 -97.7%, TiO 2 -2.2%, SiO 2 -0.1%), the powders were produced by Castolin Eutectic (Kriftel, Germany) [27][28][29]. Strengthening of the coatings based on ProXon 21021 may take place as a result of introducing a reinforcing phase into its structure in the form of dispersion ceramic particles. The material used as reinforcement was MetaCeram 28020, consisting of almost 100% Al 2 O 3 particles with an average particle diameter of 60 µm. A few percent admixture of titanium oxide increases the impact strength of the material. Aluminum oxide is resistant to corrosion, tribological wear and has a low coefficient of friction. The evaluated materials of the composite coatings contained 15% and 30% of the volume fraction of the MetaCeram 28020 powder. The structure of the coatings (porosity and the proportion of oxides) was assessed by quantitative metallography based on graphical models of thermally sprayed coatings. The porosity of the sprayed coatings based on Ni-Al and Ni-Al-Al 2 O 3 , depending on the proportion of the ceramic phase (the so-called reinforcement) and the technology used, was in a wide range from 5% to 30%. The porosity depends on the composition of the sprayed coating material. With the proportion of the reinforcing phase to the value of 30%, the porosity of the coatings increases even threefold. Concentrations of non-metallic compound Al 2 O 3 in the obtained coatings: 15% and 30%.
The coatings were sprayed with the following parameters: • Research methodology of finishing coatings by machining and plastic working was made. Machining parameters of alloy and composite nickel coatings on the steel substrate obtained by flame spraying, through preliminary study, were developed for high-precision turning. Turning has been realized with cutting speed (v c = 45-214 m/min), feed rate (f = 0.06-0.20 mm/rev) and depth of cut (a p = 0.05-0.30 mm). To research appropriate holder and edge of tungsten, carbide and cubic boron nitride were chosen (Table 1). Table 1. The shape, type and grade of inserts to turning for nickel matrix composite coatings.
The microhardness test was carried with a Vickers Hardness Tester FM-800 (Gnehm Härteprüfer AG, Thalwil, Switzerland) according to PN-EN ISO 6507-1: 2018. The load of 0.49 N for 10 s at room temperature was applied. In accordance with the principle, five measurements were made for each measuring point. The surface roughness was measured with the Hommel Tester T1000 profilometer (The Sempre Group Ltd., Gloucester, UK), with the assumed measuring section lengths of 4.8 mm and the sampling section of 0.8 mm. The roughness measurements were made worthy in accordance with the principles contained in standards EN ISO 4287:1997. The mean arithmetic deviation of the roughness profile was determined.
Visual assessment of the coating structure was performed with the use of optical microscope Axiovert 25 (ZEISS, Oberkochen, Germany) at 100× 200× magnification. Adhesion of the alloy and composite coatings was assessed accordingly using the following two qualitative methods: scratch and temperature change methods. Evaluation was made by observing the surface with an SZX16 stereoscopic microscope (Olympus, Tokyo, Japan) at 5× magnification. Coating adhesion was considered good if bubbles or exfoliation and amination were not observed.
The corrosion resistance of the coatings was performed by an electrochemical test in a three-electrode system. The surface area of 0.75 cm 2 was degreased with acetone and then placed in a vessel containing 500 cm 3 of 0.01 M H 2 SO 4 at the ambient temperature together with a polarising electrode made of platinum coated titanium and the saturated calomel electrode. Electrochemical polarization testing is a classic corrosion method that is relatively well known and widely used. Measurements of potential and corrosion current were made using the direct current (polarization curves) and alternating current method [30]. The specimens had been exposed to an electrolyte for one hour to enable stabilisation of corrosion potential. The duration of the experiments and polarisation curves i = f(E) were recorded in the range ±150 mV from the corrosion potential. During the entire time that the measurement lasted, the electrolyte was constantly stirred. The first curve of cathodic was recorded and then an anodic one. In all cases, the potential change rate was 10 mV/min. Tests for electrochemicals by ATLAS 0931 device (ATLAS-SOLLICH, Banino, Poland) were performed.

Finishing Results of the Surface Layer of Composite Coatings
The results are presented in a graphic form. The technologies of plastic working and machining were compared with each other. A new feature is the addition of burnishing.

Results of Research for Machining Nickel Matrix Composite Coatings
The research allowed for resolution, that there is a relation between the surface of alloy and composite coatings and the type of grade used and the shape of the inserts. Trigon insert WNMG 080 408 S01030A and round insert N123J1-0600-RE 7015 of cubic boron nitride (CBN), were characterized by a smaller flank wear as compared to a square insert with SNGA 120 408 S01030A 7015 of CBN (presented in Table 1).
The surface roughness of turned alloy coatings insert round (Ra = 0.3 µm) and insert trigon (Ra = 0.4 µm) is nearly three times smaller than the roughness of the coatings for a square insert (Ra = 0.9 µm).
The trigon insert made of tungsten carbide, which determined that the minimum surface roughness of alloy coatings is obtained for grade GC3215 (Ra = 0.5 µm), was used.
The turning of composite coatings with square insert SNGA120408S01030A 7015 specifies that the arithmetical mean deviation of the assessed profile reached a lower value of Ra = 1.1 µm in comparison to the roughness of the surface with the trigon insert made of the same grades CB7015 and also with the trigon of tungsten carbide (about the grades: GC2015, GC3205, GC3210, GC3215) and tungsten carbide for triangular inserts (for grades: GC4015, H10F).
Lowest surface roughness Ra = 0.7 µm is achieved for composite coating turned insert round N123J1-0600-RE 7015. Round insert after turning composite coatings is characterized by the lowest flank wear related to the square, trigon and triangular. Figure 1 shows the roughness parameter Ra of the assessed profile for alloy and composite coatings after turning for type inserts. grades: GC2015, GC3205, GC3210, GC3215) and tungsten carbide for triangular inserts (for grades: GC4015, H10F).
Lowest surface roughness Ra = 0.7 μm is achieved for composite coating turned insert round N123J1-0600-RE 7015. Round insert after turning composite coatings is characterized by the lowest flank wear related to the square, trigon and triangular. Figure 1 shows the roughness parameter Ra of the assessed profile for alloy and composite coatings after turning for type inserts.  (Table 1).
The parameter Rpk of the reduced peak height, which should be the lowest, is characteristic for the upper surface layer that quickly undergoes abrasion after the start of i.e., engine running. Reduced depth of roughness profile valley is described by Rvk parameter, which should be the highest. It is a measure of the working surface ability to keep the lubricant in the valleys created mechanically. The parameter Rk defines the core roughness depth, which should be the lowest in Table 2, and it was presented in Table 3. After turning the cylindrical steel samples with coating of alloys and composites, it was determined that there were relationships between surface texture and the type of material used and the shape of the tool inserts. Based on the analysis of test results, it was determined, due to the smaller surface roughness of the alloy coatings, that it was desirable to use trigon inserts made of GC3215 grade tungsten carbide and trigon inserts made of GC3215 grade tungsten carbide, cubic boron nitride grade CB7015 and round inserts CB7015.
The roughness of the surface nickel coating subjected to turning by trigon insert with CBN is three times smaller than the roughness of the nickel coatings by a square insert. Therefore, it is advisable not use square inserts for machining alloy coatings. Based on analysis of experimental results after finishing composite coatings, it can be determined that the roughness profile parameters and parameter values of the bearing area curve reached the lowest values for samples.  (Table 1).
The parameter Rpk of the reduced peak height, which should be the lowest, is characteristic for the upper surface layer that quickly undergoes abrasion after the start of i.e., engine running. Reduced depth of roughness profile valley is described by Rvk parameter, which should be the highest. It is a measure of the working surface ability to keep the lubricant in the valleys created mechanically. The parameter Rk defines the core roughness depth, which should be the lowest in Table 2, and it was presented in Table 3. After turning the cylindrical steel samples with coating of alloys and composites, it was determined that there were relationships between surface texture and the type of material used and the shape of the tool inserts. Based on the analysis of test results, it was determined, due to the smaller surface roughness of the alloy coatings, that it was desirable to use trigon inserts made of GC3215 grade tungsten carbide and trigon inserts made of GC3215 grade tungsten carbide, cubic boron nitride grade CB7015 and round inserts CB7015.  The roughness of the surface nickel coating subjected to turning by trigon insert with CBN is three times smaller than the roughness of the nickel coatings by a square insert. Therefore, it is advisable not use square inserts for machining alloy coatings. Based on analysis of experimental results after finishing composite coatings, it can be determined that the roughness profile parameters and parameter values of the bearing area curve reached the lowest values for samples. Figure 2 shows an example of the surface topography of the composite coatings for inserts with WNMG 080408 S01030A CB7015.

Results of Experiments by Plastic Working
The introduction of the ceramic dispersed phase itself increases hardness of the coatings base. Hence, plastic working as the strengthening finishing is advisable mainly for alloy coatings. After pressing, an increase in alloy coating hardness even up to 80% is observed, whereas, for composite coatings with 15% content of Al 2 O 3 , the coating base hardness rises by 50%. In the case of cold rolling, even greater hardening ratios for both alloy and composite coatings (93% for Ni-Al coating and 66% for coating Ni-Al-Al 2 O 3 ) are attainable.
Draft and unit pressure applied in plastic working of the steel specimens with alloy and composite coatings caused only plastic strain of the coating material. In the base steel, no structure change testifying to its plastic strain was observed. The metallographic study showed reduction in the porousness of the alloy and composite coatings subjected to plastic working ( Figure 3). Application of plastic working for thermal sprayed coatings results in a significant improvement of the surface quality. After plastic working, the average arithmetic roughness profile is twenty times smaller than the average arithmetic roughness profile of the coating before plastic working. As a result of rolling, parameter Ra reaches much lower values compared to the roughness profile deviation after pressing. Flamesprayed alloy coatings were characterised by a greatly developed real surface. The average arithmetic roughness Ra = 13.0 µm. The applied methods of plastic working allowed a significant reduction of the value of the parameter considered. The minimum value of Ra = 0.3 µm for ε h = 12% was achieved for cold rolled coatings, whereas the pressing process allowed for obtaining the surface roughness of the order of Ra = 1.2 µm. Loads applied within plastic working of the steel specimens with alloy and composite coatings caused only plastic strain of the coating material. coatings base. Hence, plastic working as the strengthening finishing is advisable mainly for alloy coatings. After pressing, an increase in alloy coating hardness even up to 80% is observed, whereas, for composite coatings with 15% content of Al2O3, the coating base hardness rises by 50%. In the case of cold rolling, even greater hardening ratios for both alloy and composite coatings (93% for Ni-Al coating and 66% for coating Ni-Al-Al2O3) are attainable.
Draft and unit pressure applied in plastic working of the steel specimens with alloy and composite coatings caused only plastic strain of the coating material. In the base steel, no structure change testifying to its plastic strain was observed. The metallographic study showed reduction in the porousness of the alloy and composite coatings subjected to plastic working ( Figure 3). Application of plastic working for thermal sprayed coatings results in a significant improvement of the surface quality. After plastic working, the average arithmetic roughness profile is twenty times smaller than the average arithmetic roughness profile of the coating before plastic working. As a result of rolling, parameter Ra reaches much lower values compared to the roughness profile deviation after pressing. Flame-sprayed alloy coatings were characterised by a greatly developed real surface. The average arithmetic roughness Ra = 13.0 μm. The applied methods of plastic working allowed a significant reduction of the value of the parameter considered. The minimum value of Ra = 0.3 µ m for εh = 12% was achieved for cold rolled coatings, whereas the pressing process allowed for obtaining the surface roughness of the order of Ra = 1.2 μm. Loads applied within plastic working of the steel specimens with alloy and composite coatings caused only plastic strain of the coating material.   Figure 4 shows the influence of the ceramic dispersion in the nickel matrix composite coatings on corrosion current density after being flame sprayed and after plastic working. Corrosion current density for the composite coatings after plastic working is twice as low compared to the alloy coatings. This may prove that a lower rate of electrochemical corrosion ( Figure 5) shows the influence of the ceramic dispersion in the composite coatings on corrosion potential after spraying and plastic working. The corrosion potential for composite coatings that has been treated with plastic working is three times smaller than for the alloy and composite coatings after spraying. An increase of  low compared to the alloy coatings. This may prove that a lower rate of electrochemical corrosion ( Figure 5) shows the influence of the ceramic dispersion in the composite coatings on corrosion potential after spraying and plastic working. The corrosion potential for composite coatings that has been treated with plastic working is three times smaller than for the alloy and composite coatings after spraying. An increase of ceramic dispersion reduces the corrosion potential and therefore increases the capacity of electrochemical corrosion. Electrochemical corrosion tests proved that the proposed finishing methods aimed at reducing the roughness of flame sprayed coatings resulted in the corrosion potential value shift towards the anodic values.
(e) (f)  Figure 4 shows the influence of the ceramic dispersion in the nickel matrix composite coatings on corrosion current density after being flame sprayed and after plastic working. Corrosion current density for the composite coatings after plastic working is twice as low compared to the alloy coatings. This may prove that a lower rate of electrochemical corrosion ( Figure 5) shows the influence of the ceramic dispersion in the composite coatings on corrosion potential after spraying and plastic working. The corrosion potential for composite coatings that has been treated with plastic working is three times smaller than for the alloy and composite coatings after spraying. An increase of ceramic dispersion reduces the corrosion potential and therefore increases the capacity of electrochemical corrosion. Electrochemical corrosion tests proved that the proposed finishing methods aimed at reducing the roughness of flame sprayed coatings resulted in the corrosion potential value shift towards the anodic values.   The purpose of the polarization test in a corrosive environment is to record the current-potential relationships in a specific range of potential or current. Figure 6 shows potentiostatic polarization curves on the nickel matrix composite coatings for Vcdp = 15%Al2O3 ceramic dispersion after plastic working. The powder manufacturer recommends using it for the regeneration of machine parts operating in tribological nodes. The alloy of nickel and aluminum may be operated in conditions which may lead to chemical  The purpose of the polarization test in a corrosive environment is to record the currentpotential relationships in a specific range of potential or current. Figure 6 shows potentiostatic polarization curves on the nickel matrix composite coatings for V cdp = 15%Al 2 O 3 ceramic dispersion after plastic working. The powder manufacturer recommends using it for the regeneration of machine parts operating in tribological nodes. The alloy of nickel and aluminum may be operated in conditions which may lead to chemical and electrochemical corrosion. Aluminum oxide is resistant to corrosion, tribological wear and has a low coefficient of friction. The presence of the Al 2 O 3 phase improves the protective properties of the thermal sprayed coatings.
Coatings 2022, 12, x FOR PEER REVIEW 10 of 14 Figure 6. The curves' potentiostatic polarization for composite coatings with volume fraction ceramic dispersed phase Vcdp = 15%Al2O3 after plastic working for pressing and rolling. Figure 7 indicates that, the greater content of dispersion phase in composite coatings, the greater roughness is achieved. In addition, the surface roughness reduction ratio reaches its greatest values for alloy coatings. The lowest values of the roughness reduction ratio occur for composite coatings with 30% content of Al2O3.  The application of pressing increased the coating corrosion rate j corr and potential corrosion E corr compared to that before plastic working. A lower value of corrosion current density can provide a lower rate of electrochemical corrosion in the case of plastic working treated alloy and composite coatings. A lower value of the corrosion potential may be characterized by a greater ability to act electrochemical corrosion. Corrosion investigation made in 0.01 M H 2 SO 4 showed that, in most cases of plastic working operations, there was an increase in the corrosive current density accompanied by the drop in the corrosion potential. In an acid environment, the corrosion rate of composite coatings is very much limited by the presence of the dispersion phase, and the porosity is reduced by rolling, pressing and burnishing. The burnishing process for the analyzed material increases the corrosion resistance of the coatings. Due to the reduction in surface roughness and waviness, a reduction in the actual surface area after burnishing is achieved compared to machining. Figure 7 indicates that, the greater content of dispersion phase in composite coatings, the greater roughness is achieved. In addition, the surface roughness reduction ratio reaches its greatest values for alloy coatings. The lowest values of the roughness reduction ratio occur for composite coatings with 30% content of Al 2 O 3 . Figure 6. The curves' potentiostatic polarization for composite coatings with volume fraction ceramic dispersed phase Vcdp = 15%Al2O3 after plastic working for pressing and rolling. Figure 7 indicates that, the greater content of dispersion phase in composite coatings, the greater roughness is achieved. In addition, the surface roughness reduction ratio reaches its greatest values for alloy coatings. The lowest values of the roughness reduction ratio occur for composite coatings with 30% content of Al2O3. The experiments allowed for determination-based on the measurements of microhardness and roughness profile after flame spraying and after plastic working-that the dispersion phase content in the composite coating has a significant effect on The experiments allowed for determination-based on the measurements of microhardness and roughness profile after flame spraying and after plastic working-that the dispersion phase content in the composite coating has a significant effect on strengthening and smoothness of the coating surface. The dependency of the ratio of relative strengthening of the composite coating on the nickel base, on the volume content of non-metallic material Al 2 O 3 , is shown in Figure 8. It shows that an increase in the percentage content of alumina is accompanied by a decrease in the coating strengthening ratio after plastic working. Another important thing is that after rolling, and also after pressing, the specimens with alloy coatings gain much greater microhardness compared to the specimens with composite coating. Therefore, the lower content of dispersion phase results in greater strengthening of the coating base. strengthening and smoothness of the coating surface. The dependency of the ratio of relative strengthening of the composite coating on the nickel base, on the volume content of non-metallic material Al2O3, is shown in Figure 8. It shows that an increase in the percentage content of alumina is accompanied by a decrease in the coating strengthening ratio after plastic working. Another important thing is that after rolling, and also after pressing, the specimens with alloy coatings gain much greater microhardness compared to the specimens with composite coating. Therefore, the lower content of dispersion phase results in greater strengthening of the coating base. Introduction of the dispersion phase itself increases hardness of the coatings base. Hence, plastic working as the strengthening is advisable mainly for Ni-Al alloy coatings. In the case of cold rolling, even greater hardening ratios for both alloy and composite coatings (Su = 93% for Ni-Al coating and Su = 66% for coating Ni-Al-Al2O3) are attainable. The obtained results of hardness measurements showed that all the proposed methods of plastic working caused strengthening of the investigated coatings. The greatest ratio of Figure 8. The influence of volume fraction ceramic dispersed phase V cdp in achieved composite coatings on relative strengthening ratio after plastic working, 1-pressing, 2-rolling, 3-burnishing. Introduction of the dispersion phase itself increases hardness of the coatings base. Hence, plastic working as the strengthening is advisable mainly for Ni-Al alloy coatings.
In the case of cold rolling, even greater hardening ratios for both alloy and composite coatings (S u = 93% for Ni-Al coating and S u = 66% for coating Ni-Al-Al 2 O 3 ) are attainable. The obtained results of hardness measurements showed that all the proposed methods of plastic working caused strengthening of the investigated coatings. The greatest ratio of coating strengthening occurred in the cold rolled and cold pressed specimens, whereas, in hot rolled specimens, the strengthening ratio was the least. The flame sprayed alloy coatings were characterized by a greatly developed actual surface. The applied methods of plastic working allowed for significant reduction of the value of the parameter in question. The minimum value of Ra = 0.3 µm was achieved for hot rolled coatings at actual draft ε h = 12%, whereas the pressing process allowed for obtaining the surface roughness of the order of Ra = 1.2 µm. Figure 9 shows an example of the surface roughness topography, the amplitude distribution of the surface roughness profile and the material share of Ni-Al alloy coatings and Ni-Al-Al 2 O 3 thermal sprayed composite coatings. The production and regeneration of products with applied coating are recognized among engineers. Composite coatings increased the performance characteristics of the surface layer (strength, tribological and corrosion resistance). These composite coatings are used in such as: aerospace, electronics, energy, industry, defense, automotive, aviation, shipbuilding and more. Based on a review, in the study, composite coatings based on nickel or aluminium were proposed.

Summary and Conclusions
The article presents the problems that can arise when producing coatings by thermal projection. It is important to obtain a low roughness. It can be seen that machining is most often performed and then material is lost.
An innovative approach to the problem is the proposition of plastic working (without material loss) as after-machining.
(1) After turning of alloy and composite coatings, it was determined that, due to obtaining the smallest surface roughness, with the least wear on the insert flank face and tool face, for a constant length of spiral cutting, round inserts with borazon were targeted to be used.
(2) It can be argued that, due to the surface quality coatings and durability of the turning inserts, for turning, shafts of centrifugal pumps with a coating alloy would need to be round and trigon inserts with borazon and trigon with tungsten carbide; for turning shafts of centrifugal pumps with composite coatings, round inserts with borazon should be applied.
(3) Based on experimental data, the ceramic dispersion content in the composite coating has a significant effect on strengthening and quality of the coating subjected to plastic working. The production and regeneration of products with applied coating are recognized among engineers. Composite coatings increased the performance characteristics of the surface layer (strength, tribological and corrosion resistance). These composite coatings are used in such as: aerospace, electronics, energy, industry, defense, automotive, aviation, shipbuilding and more. Based on a review, in the study, composite coatings based on nickel or aluminium were proposed.

Summary and Conclusions
The article presents the problems that can arise when producing coatings by thermal projection. It is important to obtain a low roughness. It can be seen that machining is most often performed and then material is lost.
An innovative approach to the problem is the proposition of plastic working (without material loss) as after-machining.
(1) After turning of alloy and composite coatings, it was determined that, due to obtaining the smallest surface roughness, with the least wear on the insert flank face and tool face, for a constant length of spiral cutting, round inserts with borazon were targeted to be used.
(2) It can be argued that, due to the surface quality coatings and durability of the turning inserts, for turning, shafts of centrifugal pumps with a coating alloy would need to be round and trigon inserts with borazon and trigon with tungsten carbide; for turning shafts of centrifugal pumps with composite coatings, round inserts with borazon should be applied.
(3) Based on experimental data, the ceramic dispersion content in the composite coating has a significant effect on strengthening and quality of the coating subjected to plastic working.
(4) Application of plastic working as a strengthening method of finishing is advisable mainly for alloy coatings, where significant strengthening occurs, and the ratios of coating strengthening are 45%-after burnishing, 80%-after pressing, and 93%-after rolling.
(5) Application of plastic working as a strengthening finish method is also advisable for composite coatings with 15% content of Al 2 O 3 where hardness of the coating base increases by 30%-after burnishing, 50%-after pressing and by 66%-after rolling; minimum values of the surface roughness are obtained after rolling. (6) The coating subjected to plastic working gained a more homogeneous structure as most of the pores, which had occurred after flame spraying, were closed. (7) The lower value of corrosion potential in the coating plastic working composite shows that the increase of ceramic dispersion Al 2 O 3 can affect the ability to increase the occurrence of electrochemical corrosion in the composite coatings. (8) The smaller value of corrosion current density can provide a lower rate of electrochemical corrosion in the case of composite coatings after plastic working; the lowest corrosion current density occurs in the composite coatings containing 15%Al 2 O 3 ceramic dispersion after rolling, burnishing and pressing.
(9) After the analysis of the results of plastic working and machining of alloy and composite coatings, it can be concluded that the technologies presented in the article may be recommended for surface chip-less forming of coatings.