The Study of POSS/Polyurethane as a Consolidant for Fragile Cultural Objects

: Moisture-curable polyurethane (MCPU) is a speciﬁcally designed material for the consolidation of fragile cultural objects in high-humidity environments. In order to solve the problem of its susceptibility to yellowing due to heat ageing, polyhedral oligomeric silsesquioxane (POSS) was added to the MCPU to prepare POSS/MCPU. The appearance, stability and mechanical properties of the POSS/MCPU ﬁlms were characterized using a UV–Vis spectrophotometer, a gloss meter, a colorimeter, a thermal analyzer and a universal material testing machine. The results showed that the ﬁlms are colorless and transparent and have a light transmission of over 80%. The addition of POSS has almost no effect on the chromaticity of the MCPU, while the thermal stability of the POSS/MCPU is improved compared to the pristine MCPU. The modiﬁed ﬁlm is 2.50 times more resistant to yellowing by heat. The addition of POSS also simultaneously enhances the strength and toughness of the ﬁlm. Using POSS/MCPU to reinforce the fragile object, the material was found to be signiﬁcantly effective, indicating it has the potential to be used during the extraction of fragile cultural objects from archaeological sites. rate of POSS/MCPU exceeded that of the pristine MCPU. This suggests that the addition of POSS somewhat inhibits decomposition at low temperatures and raises the decomposition temperature of the polymer. This may be related to the fact that POSS contains Si–O, Si–C bonds and Si–O–Si networks, which have larger bond energies and are less prone to breakage. The side chain groups of POSS may also reduce the molecular mobility of the PU polymer [21,28], as well as reducing the rate of release of volatiles [21], both of which contribute to a lower rate of thermal decomposition of the polymer.


Introduction
Cultural objects are physical carriers of human civilization and are a key to revealing the lost history of mankind. After thousands of years of burial, cultural objects, especially organic ones, often become fragile and are subject to destruction. The organic objects found in archaeological sites are often too fragile to be extracted. It is therefore essential to take appropriate measures to increase the strength of these objects.
Consolidation with chemical materials is an effective means of enhancing the strength of fragile objects. Acrylates [1][2][3][4], polyethylene and its derivatives [5], epoxy resins [6,7] and silicones [8][9][10] are commonly used as consolidants for cultural objects at normal atmospheric humidity. The environments at archaeological sites such as tombs and caves are often very humid, however, with relative humidity sometimes reaching over 90%. In such environments, acrylates, polyethylene and their derivatives blanch severely or even fail to cure [11]. Epoxy resin has a high mechanical strength and is generally used for stone relics rather than fragile organic cultural objects. Silicone has poor adhesive properties and does not provide sufficient bonding for fragile organic objects. Menthol [12,13], cyclododecane and veratraldehyde [14][15][16] perform excellently when used for the extraction of fragile organic objects, but their use as temporary reinforcement materials generally requires secondary treatment, which can be damaging to fragile objects. In summary, there are few materials suitable for use in high-humidity environments.
A novel moisture-curable polyurethane has been developed specifically to address the challenges of extracting fragile organic cultural objects in high-humidity environments [17]. The material can be cured at 30-100% relative humidity to form a colorless, transparent film with a flat surface and excellent mechanical properties. It is effective for the reinforcement of fragile organic objects but is susceptible to yellowing under UV light and heat conditions. In a previous study, we enhanced the yellowing resistance of the films under UV ageing by introducing hindered amine light stabilizers [18]. However, the issues of thermal stability and yellowing susceptibility to thermal ageing have not yet been addressed.
Inorganic-organic hybrids have a high thermal and oxidative stability due to the synergy between the inorganic and organic components. Polyhedral oligomeric silsesquioxane (POSS), a class of inorganic-organic nanohybrid materials with a backbone composed partly of Si-O-Si, can be dispersed into other materials at the molecular or nano level, which can effectively improve the stability of these materials [19][20][21][22][23][24]. Lewicki et al. [25] carried out thermogravimetric analysis (TGA) and thermal volatilization analysis (TVA) on the thermal degradation properties of POSS/PU hybrid elastomers. They found that the modified PU was more thermally stable and had significantly lower volatile degradation products, with a 30 • C increase in degradation onset temperature. Pielichowski et al. [21] incorporated POSS into PU. They found that the modified polymers had the highest thermal stability when the POSS content was between 4 and 6 wt.%. Lu et al. [26] used octaphenyl POSS and vinyl POSS as modifiers for polyurethane elastomers (PUE). The best mechanical properties of POSS/PUE were obtained when POSS was added at 3%. Their group also found that when the octaphenyl POSS content was 5 wt.%, a large number of agglomerates appeared with high-speed shear dispersion and few agglomerates appeared when using ultrasonic dispersion, indicating that the latter was more effective in dispersing the POSS [27].
The above studies demonstrated the potential of POSS to improve the thermal stability of PU, but further exploration is still required for moisture-curable polyurethane, which is the focus of this study. The impact of POSS on heritage is also an element of interest. Therefore, this study proposes to use epoxy POSS (POSS) to modify MCPU. The effect of its application to delicate samples is also investigated.

Preparation of MCPU and POSS/MCPU
Synthesize MCPU with a 3:1:0.01 M ratio of IPDI/PEG600/DBTDL. Preheat PEG600 and DBTDL at 40 °C for 0.5 h in a three-necked flask equipped with a mechanical stirrer,

Preparation of MCPU and POSS/MCPU
Synthesize MCPU with a 3:1:0.01 M ratio of IPDI/PEG600/DBTDL. Preheat PEG600 and DBTDL at 40 • C for 0.5 h in a three-necked flask equipped with a mechanical stirrer, a condenser tube and a temperature sensor. Then, add IPDI. Continue to react at 60 • C for 3 h until a white, thick production of MCPU develops. [17] Then, dissolve the prepolymer in ethyl acetate to get a 20 wt.% MCPU solution.
Add 8 wt.% POSS to the MCPU prepolymer solution and ultrasonically disperse it for 1 h at 70 • C using a KQ2200DB ultrasonic shaker (Kunshan Ultrasonic Instruments Co., Ltd., Kunshan, China) to prepare the POSS/MCPU.

Preparation and Ageing of MCPU and POSS/MCPU Films
Drop 3 mL of a 10 wt.% MCPU solution of ethyl acetate onto a slide. Let it stand in an environment with a relative humidity of 100% to obtain an MCPU film. Prepare the POSS/MCPU film by using the same method.
Place MCPU and POSS/MCPU films in a DHG-9015A oven (Yiheng Instruments Co., Ltd., Shanghai, China) for thermal ageing with the temperature set at 120 • C.

Light Transmission Test
The transmittance of the films was measured using an Hitaichi U2001 UV-Visible spectrophotometer (Hitachi, Ltd., Tokyo, Japan) in the wavelength range of 190 to 1100 nm.

Chromaticity Test
Characterization of the appearance of the sample was conducted using a VS 450 colorimeter (X-rite, Inc., Grand Rapids, MI, USA). The CIE L*a*b* color system was adopted, where L* indicates luminosity; a* from positive to negative indicates colors from red to green; and b* from positive to negative indicates colors from yellow to blue. The color difference ∆E was calculated by using the following formula. ∆E = (∆L * ) 2 + (∆a * ) 2 + (∆b * ) 2 ∆L*, ∆a* and ∆b* are the changes of L*, a* and b*, respectively. Each sample was measured three times and averaged.

Thermogravimetric Analysis
The thermal properties of the films were tested using a TGA/DSC 3+ simultaneous thermal analyzer (Mettler Toledo, Zurich, Switzerland) with a heating rate of 15 • C·min −1 , a temperature range of 50 to 1000 • C and a nitrogen atmosphere with a flow rate of 50 mL·min −1 .

Mechanical Property Tests
The tensile strength of the film was measured using a QT-1176 testing machine (Gaotai Testing Instruments Co., Ltd., Dongguan, China) with a sample size of 45 mm × 25 mm and a standard distance of 20 mm, at a constant speed of 10 mm·min −1 .

Scanning Electron Microscope Analysis
The microstructures of films were observed by a Quanta 450 FEG thermal field emission ESEM (FEI Technologies, Inc., Hillsboro, OR, USA) after brittle failure of sampled liquid nitrogen. The voltage was 20 kV and the magnification was 2500 times. The imaging mode was high vacuum secondary electron imaging.

Simulation Experiments
Spray an appropriate amount of distilled water onto the surface of the aged silk samples to simulate the condition of silk artefacts excavated in humid environments. After the sample has dried, draw up an amount of 8 wt.% POSS/MCPU ethyl acetate solution to treat the aged silk samples. Leave them to stand in a plexiglass box. The plexiglass box should hold a sufficient amount of water at the bottom and the sample should be placed on the upper layer. The relative humidity inside the box should be 90% or more.

Film Performance Results
As shown in Figure 2, the light transmission of MCPU and POSS/MCPU films were both greater than 80% in the spectral range of 400 to 800 nm, which is consistent with our previously published data [17]. In addition, there was little difference in the L*, a* and b* values of the films. The color-difference value ∆E between the two films was 0.72, which is unrecognizable to the naked eye. The modification has little or no effect on the color of the film. liquid nitrogen. The voltage was 20 kV and the magnification was 2 mode was high vacuum secondary electron imaging.

Simulation Experiments
Spray an appropriate amount of distilled water onto the surfa ples to simulate the condition of silk artefacts excavated in humid e sample has dried, draw up an amount of 8 wt.% POSS/MCPU e treat the aged silk samples. Leave them to stand in a plexiglass b should hold a sufficient amount of water at the bottom and the sa on the upper layer. The relative humidity inside the box should b

Film Performance Results
As shown in Figure 2, the light transmission of MCPU and P both greater than 80% in the spectral range of 400 to 800 nm, whic previously published data [17]. In addition, there was little differe values of the films. The color-difference value ∆E between the tw is unrecognizable to the naked eye. The modification has little or the film.   After the addition of POSS, the initial and terminal decomposition temperatures of the films were increased from 316 to 319 • C and from 402 to 418 • C, respectively. This indicates an increase in the thermal stability of the film. It is worth noting that the maximum rate temperatures of the POSS/MCPU are slightly shifted toward lower temperatures, which contradicts previous research [21]. Despite this, the decomposition rate of POSS/MCPU remained smaller than that of the pristine MCPU until 394 • C, when the decomposition Coatings 2022, 12, 153 5 of 10 rate of POSS/MCPU exceeded that of the pristine MCPU. This suggests that the addition of POSS somewhat inhibits decomposition at low temperatures and raises the decomposition temperature of the polymer. This may be related to the fact that POSS contains Si-O, Si-C bonds and Si-O-Si networks, which have larger bond energies and are less prone to breakage. The side chain groups of POSS may also reduce the molecular mobility of the PU polymer [21,28], as well as reducing the rate of release of volatiles [21], both of which contribute to a lower rate of thermal decomposition of the polymer. mum rate temperatures of the POSS/MCPU are slightly shifted toward lower te tures, which contradicts previous research [21]. Despite this, the decomposition POSS/MCPU remained smaller than that of the pristine MCPU until 394 °C, wh decomposition rate of POSS/MCPU exceeded that of the pristine MCPU. This s that the addition of POSS somewhat inhibits decomposition at low temperatur raises the decomposition temperature of the polymer. This may be related to the f POSS contains Si-O, Si-C bonds and Si-O-Si networks, which have larger bond e and are less prone to breakage. The side chain groups of POSS may also reduce t lecular mobility of the PU polymer [21,28], as well as reducing the rate of release tiles [21], both of which contribute to a lower rate of thermal decomposition of th mer.   The energy barriers that need to be crossed for thermal decomposition are higher. As a result, thermal decomposition becomes more difficult and the thermal stability of the material increases. Similarly, Vyazovkin used clay to modify polystyrene polymer; the composite materials obtained had an increased resistance to thermo-oxidative degradation and greater activation energy [28].
The most obvious change in the MCPU during thermal ageing is yellowing, so the ∆b* value representing the change in yellow color in the CIE L*a*b* system was used as an indicator to represent the degree of ageing of the samples. Figure 4 shows the variation of ∆b* values for MCPU and POSS/MCPU with ageing time under 120 • C ageing conditions. The degree of yellowing is positively correlated with the ageing time in both cases (the fitted equations have been included in the figures). The two critical values for the colordifference values are generally considered to be 3 and 6, representing recognizable color change and significant color differences, respectively. According to the Lambert-Beer law, the color difference is proportional to the thickness. Since the thickness of the experimental sample is much greater than the thickness in actual use, ∆b* = 6 was chosen as the ageing endpoint in this experiment. The MCPU and POSS/MCPU reached their ageing endpoints at approximately 8.32 and 20.78 h respectively, with the latter being 2.50 times more resistant to yellowing than the former. POSS significantly improved the yellowing resistance of the MCPU.
Based on the kinetics calculations of thermal decomposition [18], the decomp activation energy was increased from 125.25 to 165.71 kJ·mol −1 with the addition of The energy barriers that need to be crossed for thermal decomposition are highe result, thermal decomposition becomes more difficult and the thermal stability of t terial increases. Similarly, Vyazovkin used clay to modify polystyrene polymer; th posite materials obtained had an increased resistance to thermo-oxidative degra and greater activation energy [28].
The most obvious change in the MCPU during thermal ageing is yellowing Δb* value representing the change in yellow color in the CIE L*a*b* system was u an indicator to represent the degree of ageing of the samples. Figure 4 shows the va of Δb* values for MCPU and POSS/MCPU with ageing time under 120 °C ageing tions. The degree of yellowing is positively correlated with the ageing time in bot (the fitted equations have been included in the figures). The two critical values color-difference values are generally considered to be 3 and 6, representing recog color change and significant color differences, respectively. According to the La Beer law, the color difference is proportional to the thickness. Since the thickness experimental sample is much greater than the thickness in actual use, Δb* = 6 was as the ageing endpoint in this experiment. The MCPU and POSS/MCPU reache ageing endpoints at approximately 8.32 and 20.78 h respectively, with the latter bei times more resistant to yellowing than the former. POSS significantly improved t lowing resistance of the MCPU.  As shown in Figure 5, the tensile strengths of the MCPU and POSS/MCPU films were 11.63 and 14.81 MPa, respectively, an increase of 27.34%. Maximum elongations were 344.97% and 370.15%, respectively, an improvement of 25.18%. The incorporation of nano-POSS increased the strength and toughness of the films. This is consistent with the results of previous research [24].  Figure 6 shows the SEM images of the fracture surfaces of the MCP POSS/MCPU films. The fracture surface of the original MCPU film is flat, while tha POSS/MCPU film is covered with striated grooves. After POSS incorporation, as of the ultrasonic assistance, a well-dispersed inorganic-organic phase is formed polymer. When the film fractures, as a single-component polymer, the original film produces a relatively flat surface, whereas the POSS/MCPU film has both in and organic phases and tends to form a rough structure. The grooved structure in the bonding force at the fracture interface, which is responsible for the increases strength and maximum elongation of the film. In summary, the introduction of POSS does not affect the surface appearanc film and, meanwhile, improves the heat resistance of the MCPU. This makes it m sistant to yellowing during heat ageing. In addition, the strength and toughness film are simultaneously increased.  Figure 6 shows the SEM images of the fracture surfaces of the MCPU and POSS/MCPU films. The fracture surface of the original MCPU film is flat, while that of the POSS/MCPU film is covered with striated grooves. After POSS incorporation, as a result of the ultrasonic assistance, a well-dispersed inorganic-organic phase is formed in the polymer. When the film fractures, as a single-component polymer, the original MCPU film produces a relatively flat surface, whereas the POSS/MCPU film has both inorganic and organic phases and tends to form a rough structure. The grooved structure increases the bonding force at the fracture interface, which is responsible for the increases in the strength and maximum elongation of the film.  Figure 6 shows the SEM images of the fracture surfaces of the MCPU and POSS/MCPU films. The fracture surface of the original MCPU film is flat, while that of the POSS/MCPU film is covered with striated grooves. After POSS incorporation, as a result of the ultrasonic assistance, a well-dispersed inorganic-organic phase is formed in the polymer. When the film fractures, as a single-component polymer, the original MCPU film produces a relatively flat surface, whereas the POSS/MCPU film has both inorganic and organic phases and tends to form a rough structure. The grooved structure increases the bonding force at the fracture interface, which is responsible for the increases in the strength and maximum elongation of the film. In summary, the introduction of POSS does not affect the surface appearance of the film and, meanwhile, improves the heat resistance of the MCPU. This makes it more resistant to yellowing during heat ageing. In addition, the strength and toughness of the film are simultaneously increased.

Treatment Results
The silk fabric samples were processed using POSS/MCPU. It penetrates well as a reinforcement, which enhances the overall strength of fragile artefacts. The GPC results showed that the corresponding number-average molecular weights were 1894 and 4842, which are much lower than those of Paraloid B72, resulting in better permeability of POSS/MCPU. In summary, the introduction of POSS does not affect the surface appearance of the film and, meanwhile, improves the heat resistance of the MCPU. This makes it more resistant to yellowing during heat ageing. In addition, the strength and toughness of the film are simultaneously increased.

Treatment Results
The silk fabric samples were processed using POSS/MCPU. It penetrates well as a reinforcement, which enhances the overall strength of fragile artefacts. The GPC results showed that the corresponding number-average molecular weights were 1894 and 4842, which are much lower than those of Paraloid B72, resulting in better permeability of POSS/MCPU.
As a general rule, any treatments should not alter the appearance of the cultural objects. Therefore, the color change before and after treatment was tested. As shown in Figure 7, the chromaticity of the silk samples before and after treatment remained almost unchanged, with an average color difference of ∆E of 1.49 (unrecognizable to the naked eye), which is in line with the requirements of conservation.
Coatings 2022, 12, x FOR PEER REVIEW 8 of 10 As a general rule, any treatments should not alter the appearance of the cultural objects. Therefore, the color change before and after treatment was tested. As shown in Figure 7, the chromaticity of the silk samples before and after treatment remained almost unchanged, with an average color difference of ∆E of 1.49 (unrecognizable to the naked eye), which is in line with the requirements of conservation. The tensile strength and maximum elongation of the untreated and treated silk samples were tested contrastingly ( Figure 8). After treatment, the tensile strength of the silk samples increased from 46.52 to 80.51 MPa, an increase in strength of 73.07%. The maximum elongation increased from 5.53% to 7.30%, an increase of 1.77%. It shows that the treatment of fragile samples with POSS/MCPU simultaneously enhanced their strength and toughness. Therefore, the POSS/MCPU is a potential material for the extraction of fragile organic samples excavated from archaeological sites. Overall, the treatment of fragile-artefact samples with POSS/MCPU does not affect the appearance of the samples but does increase their strength and toughness, which is important for the extraction of fragile samples. The newly prepared POSS/MCPU is a suitable material with high performance for the conservation of cultural objects. The tensile strength and maximum elongation of the untreated and treated silk samples were tested contrastingly ( Figure 8). After treatment, the tensile strength of the silk samples increased from 46.52 to 80.51 MPa, an increase in strength of 73.07%. The maximum elongation increased from 5.53% to 7.30%, an increase of 1.77%. It shows that the treatment of fragile samples with POSS/MCPU simultaneously enhanced their strength and toughness. Therefore, the POSS/MCPU is a potential material for the extraction of fragile organic samples excavated from archaeological sites.
Coatings 2022, 12, x FOR PEER REVIEW 8 o As a general rule, any treatments should not alter the appearance of the cultural jects. Therefore, the color change before and after treatment was tested. As shown in F ure 7, the chromaticity of the silk samples before and after treatment remained alm unchanged, with an average color difference of ∆E of 1.49 (unrecognizable to the nak eye), which is in line with the requirements of conservation. The tensile strength and maximum elongation of the untreated and treated silk sa ples were tested contrastingly ( Figure 8). After treatment, the tensile strength of the s samples increased from 46.52 to 80.51 MPa, an increase in strength of 73.07%. The ma mum elongation increased from 5.53% to 7.30%, an increase of 1.77%. It shows that treatment of fragile samples with POSS/MCPU simultaneously enhanced their stren and toughness. Therefore, the POSS/MCPU is a potential material for the extraction fragile organic samples excavated from archaeological sites. Overall, the treatment of fragile-artefact samples with POSS/MCPU does not aff the appearance of the samples but does increase their strength and toughness, which important for the extraction of fragile samples. The newly prepared POSS/MCPU is a su Overall, the treatment of fragile-artefact samples with POSS/MCPU does not affect the appearance of the samples but does increase their strength and toughness, which is important for the extraction of fragile samples. The newly prepared POSS/MCPU is a suitable material with high performance for the conservation of cultural objects.

Conclusions
MCPU was modified with POSS as a stabilizer to produce POSS/MCPU, which exhibited excellent thermal stability and good reinforcement properties. The results showed that the addition of POSS improves the thermal stability, resistance to yellowing by heat and the strength and toughness of the film, without affecting its appearance. Satisfactory results were also achieved with the POSS/MCPU-reinforced fragile samples. The newly prepared material has potential to be used for the extraction of fragile organic cultural objects from archaeological sites.