Lubrication and Anti-Rust Properties of Jeffamine-Triazole Derivative as Water-Based Lubricant Additive

: With the worldwide concern of environmental protection, water-based lubricants exhibit extensive potential applications due to their advantages of energy-conservation, innocuity, and competitive price. Nonetheless, the common lubricating additives currently available in the market are mainly oil-based, while multifunctional water lubricants are rare. This paper reports a sulfur-and phosphorus-free multifunctional additive with high water-solubility, which is applicable for multitype material surfaces. Speciﬁcally, through the Mannich reaction method, a Jeffamine-triazole derivative was synthesized from olyetheramine and benzotriazole. Compared with distilled water, the derivative exhibited superior friction reduction and wear resistance properties in water, with the friction reduction rate up to 72.7% and 70.2% for steel/steel and steel/aluminum contacts, respec-tively, when the concentration of the JD2000 is 2 wt.%. Remarkably, the wear resistance property for steel/aluminum contact is improved by 88.2%. Moreover, the additive showed corrosion inhibition on the metal surface by 75.5%. We further revealed the lubrication and anti-rust mechanisms: the additives are adsorbed on the surfaces through nitrogen atoms, and the long-chain structure of polyether can cover the sliding surfaces, forming a stable viscoelastic ﬁlm to prevent the severe damages caused by the direct contact between rough friction pairs. Concurrently, the dense protective ﬁlm can resist the corrosion of environmental media on the metal surface and delay the metal rust. This research may provide a candidate for an ecofriendly multifunctional water-based lubricating additive. Jeffamine D2000 g, 37 wt.% formaldehyde solution under The was to 90 ◦ and the sulfuric acid aqueous solution (80 reaction continues for 10 h at 90 ◦ C. the diaphanous viscous the Jeffamine-triazole derivatives (JD2000) repeated throughout the friction testing process, making the friction curve of the distilled and a lower concentration of the JD2000 aqueous solutions periodically. When the concentrations of the JD2000 increased to 1 and 2 wt.%, it was observed that the friction curve had no obvious ﬂuctuation and remained at the lowest point. The friction coefﬁcient of the 2 wt.% JD2000 aqueous solutions was very stable and stayed at the lowest value, showing that the JD2000 had the best anti-friction property at 2 wt.%. When the concentration of the JD2000 was increased to 4 wt.%, the friction curve resumed its periodic ﬂuctuation, and the friction coefﬁcient also increased. It is speculated that this was because the appropriate concentration of the JD2000 could well cover the surface of the aluminum plates, forming a stable friction ﬁlm and preventing the direct contact of the rough surface. When the amount of additive continued to increase, the thickness of the lubrication ﬁlm increased, which tended to form an agglomeration of molecular chains. This led to an increase in the friction coefﬁcient. that this molecule was a JD2000 long chain that lost C 6 H 4 N 3 CH 2 NH– and CH 3 –, and its degrees of polymerization were 7 and 12. When the m / z value was near 649, the corresponding molecule was the additive long chain with the lost C 6 H 4 N 3 CH 2 NH– structure, and the degree of polymerization was 8. The results show that the chain of the JD2000 molecule broke and formed chains with different molecular weights during the friction process. This then ﬁlled in the wear track to prevent direct contact with the uneven metal surface.


Introduction
With the severe situation of environmental problems and the worldwide shortage of oil resources [1], traditional lubricants and greases are facing serious challenges. It is imperative to develop new strategies of realizing multifunctional "green" lubrications. As a novel type of ecofriendly lubrication method, water lubrication exhibits a wide application prospect in drilling equipment, tail bearing, metal tool processing, etc. due to its advantages of low cost, high thermal conductivity, high fluidity, and environment friendliness [2]. However, the development of water-based lubrications is limited by the problems of low viscosity, poor lubrication performance, and serious corrosion [3]. Additionally, most lubricating additives are applicable for oil or greases, while water-based additives are relatively few [4]. Commonly used water-based additives have some unavoidable shortcomings. Borate, for example, has poor solubility in water and cannot play a good role in lubrication. Sulfur and phosphorus additives contain active elements, which can easily cause environmental pollution, such as water eutrophication. Relevant environmental laws and regulations have clearly banned the use of phosphorus compounds [5]. In addition, the preparation of nano-water-soluble additives is generally complicated and costly. Therefore, it is very important to promote the development of water-based lubricants to obtain green 100 mL). Then, a Jeffamine D2000 (21.05 g, 10 mmol) and 37 wt.% formaldehyde solution (0.85 g, 10 mmol) were added under magnetic stirring. The mixture was heated to 90 • C, and the sulfuric acid aqueous solution (80 wt.%, 8 mL) was introduced into the mixture. The reaction continues for 10 h at 90 • C. Finally, the mixture was cooled to a yellowish diaphanous viscous liquid, and the Jeffamine-triazole derivatives (JD2000) were obtained. The reaction formula and structural formula of the JD2000 are shown in Figure 1.

Preparation of the JD2000
The JD2000 derivative were prepared via the following procedures. First, the benzotriazole (1.25 g, 10 mmol) was introduced into the sodium hydroxide solution (8 wt.%, 100 mL). Then, a Jeffamine D2000 (21.05 g, 10 mmol) and 37 wt.% formaldehyde solution (0.85 g, 10 mmol) were added under magnetic stirring. The mixture was heated to 90 °C, and the sulfuric acid aqueous solution (80 wt.%, 8 mL) was introduced into the mixture. The reaction continues for 10 h at 90 °C. Finally, the mixture was cooled to a yellowish diaphanous viscous liquid, and the Jeffamine-triazole derivatives (JD2000) were obtained. The reaction formula and structural formula of the JD2000 are shown in Figure 1.

Pretreatment of the Friction Pair
In practical use, different friction pairs often appear in different working conditions. Due to its high tensile strength and low cost, steel is used in buildings, infrastructure, tools, ships, trains, cars, machines, electrical appliances, and weapons. With the properties of low density, non-toxicity, easy recovery, electrical conductivity, and heat transfer, the recycling of aluminum alloys has been shown to provide major economic benefits and has been widely used in aerospace, automation, and advanced machinery. To meet the needs of different conditions and expand the usage of the products, 304 stainless steel and 6061 aluminum alloy substrates were selected as the lower stationary block in the friction pairs. Before the friction test, steel and aluminum plates were immersed in a mixture of petroleum ether (analytical pure, Sinopharm Chemical Reagent Co., Ltd., Shanghai, China) and ethanol (analytical pure, purity 99%, Sinopharm Chemical Reagent Co., Ltd., Shanghai, China). Afterwards, ultrasonication was performed in a water bath for 15 min to remove the surface impurities and contaminants. The surface was then blow-dried using nitrogen gas flow. The resulting steel and aluminum plates were retained for tribological testing.

Friction and Wear Tests
A Bruker UMT-tribolab tester (Bruker, Billerica, MA, USA) was used to evaluate the tribological performance of the additive. The tests were performed in a ball-on-block configuration. Contact between the friction pairs was achieved by applying pressure to the upper running ball (8 mm in diameter, GCr15 steel, hardness of approximately 59-61 HRC) against the lower stationary block in the reciprocating mode. The variation in friction force and displacement with time during the test were controlled using a computer, and the entire process was recorded. The test was under a load of 7 N at a frequency of 4 Hz at room temperature (25 °C) and ambient humidity (30.2%) for 30 min. Distilled water and solutions with different concentrations of the JD2000 were adopted as the lubricants. All of the tests were repeated three times.

Pretreatment of the Friction Pair
In practical use, different friction pairs often appear in different working conditions. Due to its high tensile strength and low cost, steel is used in buildings, infrastructure, tools, ships, trains, cars, machines, electrical appliances, and weapons. With the properties of low density, non-toxicity, easy recovery, electrical conductivity, and heat transfer, the recycling of aluminum alloys has been shown to provide major economic benefits and has been widely used in aerospace, automation, and advanced machinery. To meet the needs of different conditions and expand the usage of the products, 304 stainless steel and 6061 aluminum alloy substrates were selected as the lower stationary block in the friction pairs. Before the friction test, steel and aluminum plates were immersed in a mixture of petroleum ether (analytical pure, Sinopharm Chemical Reagent Co., Ltd., Shanghai, China) and ethanol (analytical pure, purity 99%, Sinopharm Chemical Reagent Co., Ltd., Shanghai, China). Afterwards, ultrasonication was performed in a water bath for 15 min to remove the surface impurities and contaminants. The surface was then blow-dried using nitrogen gas flow. The resulting steel and aluminum plates were retained for tribological testing.

Friction and Wear Tests
A Bruker UMT-tribolab tester (Bruker, Billerica, MA, USA) was used to evaluate the tribological performance of the additive. The tests were performed in a ball-on-block configuration. Contact between the friction pairs was achieved by applying pressure to the upper running ball (8 mm in diameter, GCr15 steel, hardness of approximately 59-61 HRC) against the lower stationary block in the reciprocating mode. The variation in friction force and displacement with time during the test were controlled using a computer, and the entire process was recorded. The test was under a load of 7 N at a frequency of 4 Hz at room temperature (25 • C) and ambient humidity (30.2%) for 30 min. Distilled water and solutions with different concentrations of the JD2000 were adopted as the lubricants. All of the tests were repeated three times.

Corrosion Tests
The JB/T 9189-2016 method was applied to evaluate the anti-rust performance of the JD2000. In the experiment, cast iron scraps of the same quality were evenly spread on the filter paper in two culture dishes, and the same amount of water and additive solution were removed with a dropper to evenly wet the iron scraps. After the culture dish was covered, it was kept away from light and humidity for 2 h at room temperature. After the experiment, we removed the iron scraps, rinsed the filter paper with toluene, and dried it in the air. The number and area of rust spots on the filter paper were visually checked to determine the corrosion grade of the additive.

Water Contact Angle Measurements
The DSA30R interfacial rheometer (KRÜSS, Hamburg, Germany) was applied to measure the water contact angle of the additive on different metal surfaces. We first submerged the steel plates and aluminum plates used in the tribological test in pure water with or without 2 wt.% JD2000 additive for half an hour at room temperature. The plates were rinsed with toluene and dried in the air, generating the plates for tests. The change of contact angle with time was recorded, and the adsorption rate of lubricant on metal surface was obtained.

Adsorption Behavior Test of the JD2000 on Metal Surface
Q-sense 401 quartz crystal microbalance with dispersion (QCM-D, Biolinscientific, Gothenburg, Sweden) was used to investigate the adsorption behavior of the JD2000 on the metal surface. Compared with iron wafers, which are prone to chemical reactions during the pre-cleaning process and may affect test results, gold wafers can avoid such problems. At the same time, related studies showed that the adsorption behaviors of samples on these two surfaces are consistent. Hence, we adopted the metallographic wafer as the adsorption surface for testing in this study.
During the process, the cleaned wafer was placed on the O ring of the QCM-D flow cell and connected to the device. Then, the dodecane solution flowed throughout it at a rate of 80 µL/min. When the ∆F and ∆D curves were stable, we established a baseline and applied the 2 wt.% JD2000 aqueous solution. After the absorption was stable, we waited another 30 min and removed the sample, which then had dodecane flow through it again for about 15 min. At the end of the experiment, the instrument was cleaned with petroleum ether, ethanol, and deionized water. All the data were real-time recorded.

Characterization of Product Structure and Investigation of Worn Surface
To verify the product structure, the Fourier transform infrared (FTIR) spectra were collected using Paragon 1000 (PerkinElmer, Inc., Waltham, MA, USA) with the attenuated total reflection (ATR) attachment scanning from 4000 to 650 cm −1 . Nuclear magnetic data were collected with a Bruker AVANCE III HD spectrometer (Bruker, Billerica, MA, USA) in CDCl 3 with trimethylsilane as the reference. Measurements were performed with MALDI-TOF MS (Bruker autoflex III, Bruker, Billerica, MA, USA) equipped with a pulsed N 2 laser (337 nm). An accelerating voltage of 20 kV was used. The Malvenpanako (Viscotek GPC/SEC, Viscotek Corp, Houston, TX, USA) was used to measure the molecular weight distribution of the additive. The Contour GT (Bruker, Billerica, MA, USA) was used to investigate the morphology (WLI) of the worn surfaces and the wear degree. Prior to the study, the plates were cleaned in an ultrasonic bath with petroleum ether for 10 min and lightly mopped with a clean tissue. To analyze the chemical composition on the worn scars, the X-ray photoelectron spectroscopy (XPS) data were obtained from thermo scientific Escalab 250xi (ESCALAB250Xi, Thermo Fisher Scientific, Waltham, MA, USA) with Al Kα radiation, and the vacuum degree of the analysis chamber was 8 × 10 −10 Pa. Scanning electron microscopy (SEM) and energy-dispersive X-ray spectroscopy were conducted on AZtec X-MaxN 80 (Oxford, Abingdon, UK), and the Raman spectra were collected using Thermo DXR 2xi (Thermo Fisher Scientific, Waltham, MA, USA) in a range from 3500 to 50 cm −1 with a 532 nm laser source.  Figure 2a shows the FTIR spectra of the JD2000. Sharp peaks near 3030 cm −1 were observed in the FTIR spectra of the JD2000, which were assigned to the stretching vibration peak of the C-H bond of the benzene ring. The peaks near 1600 cm −1 were due to the stretching vibration of the -CH 3 bond. The stretching vibration peak near 1100 cm −1 was assigned to the N=N double bond. The strongest peak at 1170 cm −1 was the stretching vibration peak of the C-O-C single bond, proving the existence of the ether bond appearing in the spectra of the JD2000. The FTIR results demonstrate that the JD2000 was successfully produced from benzotriazole and formaldehyde. Figure 2b shows the 1 H NMR spectra of the JD2000. The chemical shifts of 7.79 and 7.34 ppm represent the hydrogen atoms in the benzene ring, the chemical shifts of 4.45 ppm represent the signal of the active methylene group, and a new peak was produced. The peaks of 1.0 and 3.86 ppm represent the methyl and methylene signals on the polyether chain. The nuclear magnetic resonance data show that the product contained benzotriazole and polyether chains, and the target product, JD2000, was successfully obtained. collected using Thermo DXR 2xi (Thermo Fisher Scientific, Waltham, MA, USA) in a range from 3500 to 50 cm −1 with a 532 nm laser source. Figure 2a shows the FTIR spectra of the JD2000. Sharp peaks near 3030 cm −1 were observed in the FTIR spectra of the JD2000, which were assigned to the stretching vibration peak of the C-H bond of the benzene ring. The peaks near 1600 cm −1 were due to the stretching vibration of the -CH3 bond. The stretching vibration peak near 1100 cm −1 was assigned to the N=N double bond. The strongest peak at 1170 cm −1 was the stretching vibration peak of the C-O-C single bond, proving the existence of the ether bond appearing in the spectra of the JD2000. The FTIR results demonstrate that the JD2000 was successfully produced from benzotriazole and formaldehyde. Figure 2b shows the 1 H NMR spectra of the JD2000. The chemical shifts of 7.79 and 7.34 ppm represent the hydrogen atoms in the benzene ring, the chemical shifts of 4.45 ppm represent the signal of the active methylene group, and a new peak was produced. The peaks of 1.0 and 3.86 ppm represent the methyl and methylene signals on the polyether chain. The nuclear magnetic resonance data show that the product contained benzotriazole and polyether chains, and the target product, JD2000, was successfully obtained. The structure of the JD2000 product was analyzed using mass spectrometry, as shown in Figure 3. The peak at 2334 m/z is the derivative of Jeffamine-triazole at n = 34. The disparity of m/z between the adjacent peaks is approximately 58, which represents the difference of a -C3H6O structure. GPC results are shown in the inset's table. The number average molecular weight (Mn) is 1055, and the weight average molecular weight (Mw) is 2234. The degree of dispersion (Mw/Mn) is 2.117. It can be seen that the molecular weight of the JD2000 is concentrated around 2234, and the main degree of polymerization is 34. The results show that the synthesized product had a polyether chain structure and was a mixture of derivatives with different degrees of polymerization. The structure of the JD2000 product was analyzed using mass spectrometry, as shown in Figure 3. The peak at 2334 m/z is the derivative of Jeffamine-triazole at n = 34. The disparity of m/z between the adjacent peaks is approximately 58, which represents the difference of a -C 3 H 6 O structure. GPC results are shown in the inset's table. The number average molecular weight (Mn) is 1055, and the weight average molecular weight (Mw) is 2234. The degree of dispersion (Mw/Mn) is 2.117. It can be seen that the molecular weight of the JD2000 is concentrated around 2234, and the main degree of polymerization is 34. The results show that the synthesized product had a polyether chain structure and was a mixture of derivatives with different degrees of polymerization.

Configuration and Stability Test of the JD2000 Water-Based System
Due to the inclusion of various ions and impurities in tap water, which may affec the tribological behavior of an aqueous solution, the water used in this experiment was distilled water. The JD2000 was introduced into the distilled water and ultrasonically dispersed in a water bath for 30 s to obtain a uniformly dispersed water solution. In this experiment, the JD2000 aqueous solutions with mass fractions of 0.25, 0.5, 1, 2, and 4 wt.% were prepared. As shown in Figure 4a, the aqueous solutions of the JD2000 with differen concentrations were all clear and diaphanous, and they gradually became pale yellow with increasing concentration. To observe their solubility stabilities in water, the JD2000 aqueous solutions with different concentrations were left for one month. The results are shown in Figure 4b. The JD2000 aqueous solutions with different concentrations re mained clear and diaphanous, and no precipitation phenomenon occurred. The results show that the JD2000 stably dissolved in water, and the JD2000 aqueous solutions with different concentrations were obtained.

Configuration and Stability Test of the JD2000 Water-Based System
Due to the inclusion of various ions and impurities in tap water, which may affect the tribological behavior of an aqueous solution, the water used in this experiment was distilled water. The JD2000 was introduced into the distilled water and ultrasonically dispersed in a water bath for 30 s to obtain a uniformly dispersed water solution. In this experiment, the JD2000 aqueous solutions with mass fractions of 0.25, 0.5, 1, 2, and 4 wt.% were prepared. As shown in Figure 4a, the aqueous solutions of the JD2000 with different concentrations were all clear and diaphanous, and they gradually became pale yellow with increasing concentration. To observe their solubility stabilities in water, the JD2000 aqueous solutions with different concentrations were left for one month. The results are shown in Figure 4b. The JD2000 aqueous solutions with different concentrations remained clear and diaphanous, and no precipitation phenomenon occurred. The results show that the JD2000 stably dissolved in water, and the JD2000 aqueous solutions with different concentrations were obtained.

Configuration and Stability Test of the JD2000 Water-Based System
Due to the inclusion of various ions and impurities in tap water, which may affect the tribological behavior of an aqueous solution, the water used in this experiment was distilled water. The JD2000 was introduced into the distilled water and ultrasonically dispersed in a water bath for 30 s to obtain a uniformly dispersed water solution. In this experiment, the JD2000 aqueous solutions with mass fractions of 0.25, 0.5, 1, 2, and 4 wt.% were prepared. As shown in Figure 4a, the aqueous solutions of the JD2000 with different concentrations were all clear and diaphanous, and they gradually became pale yellow with increasing concentration. To observe their solubility stabilities in water, the JD2000 aqueous solutions with different concentrations were left for one month. The results are shown in Figure 4b. The JD2000 aqueous solutions with different concentrations remained clear and diaphanous, and no precipitation phenomenon occurred. The results show that the JD2000 stably dissolved in water, and the JD2000 aqueous solutions with different concentrations were obtained.

Friction Reduction and Anti-Wear Properties of the Steel Plates
To test the anti-friction property of water with JD2000 concentrations ranging from 0 to 4 wt.% on the steel plates, the tribological test was conducted on the UMT-tribolab tester. The test results of the average friction coefficients (COF) of the different concentrations of the JD2000 aqueous solutions are shown in Figure 5a. It can be seen that the COF of the distilled water was 0.481. After adding the lubricant, the COF decreased obviously with increasing amounts of the additive. When the JD2000 concentration was 2 wt.%, the COF was 0.185 compared with the distilled water, and the anti-friction property was improved by 61.4%. When the concentration further increased to 4 wt.%, the COF of the system was 0.182, and the anti-friction property was improved by 62.1%. The COF reduction was not obvious compared with the case of 2 wt.%. The results show that the lubrication effect of the JD2000 was sensitive to its concentration. The low concentration JD2000 did not form tribofilms. In this study, a JD2000 concentration of 2 wt.% was applicable for the JD2000 to exert its lubrication ability.
trations of the JD2000 aqueous solutions are shown in Figure 5a. It can be seen that the COF of the distilled water was 0.481. After adding the lubricant, the COF decreased obviously with increasing amounts of the additive. When the JD2000 concentration was 2 wt.%, the COF was 0.185 compared with the distilled water, and the anti-friction property was improved by 61.4%. When the concentration further increased to 4 wt.%, the COF of the system was 0.182, and the anti-friction property was improved by 62.1%. The COF reduction was not obvious compared with the case of 2 wt.%. The results show that the lubrication effect of the JD2000 was sensitive to its concentration. The low concentration JD2000 did not form tribofilms. In this study, a JD2000 concentration of 2 wt.% was applicable for the JD2000 to exert its lubrication ability.
To further analyze the variation in the friction coefficient during the friction process, the real-time friction coefficient curves of the steel plates lubricated using the JD2000 aqueous solutions are shown in Figure 5b. It can be seen that the friction coefficient of the distilled water was very unstable and always fluctuated at a higher value. When the JD2000 was added, the friction coefficient and the fluctuation of the friction curve decreased. The average friction coefficient decreased with increasing amounts of the additions, and the stability of the curve increased with increasing concentrations. The wear conditions of the steel plates lubricated using the JD2000 aqueous solutions with different concentrations are shown in Figure 6. It can be seen that the wear scar width and depth of the distilled water were 0.36 mm and 4.03 μm, respectively, being the smallest of all the samples. With an increase of the JD2000 concentrations, the width and depth of the wear mark increased gradually. The results show that the water-based lubricant JD2000 had no anti-wear property on the 304 steel plate. To further analyze the variation in the friction coefficient during the friction process, the real-time friction coefficient curves of the steel plates lubricated using the JD2000 aqueous solutions are shown in Figure 5b. It can be seen that the friction coefficient of the distilled water was very unstable and always fluctuated at a higher value. When the JD2000 was added, the friction coefficient and the fluctuation of the friction curve decreased. The average friction coefficient decreased with increasing amounts of the additions, and the stability of the curve increased with increasing concentrations.
The wear conditions of the steel plates lubricated using the JD2000 aqueous solutions with different concentrations are shown in Figure 6. It can be seen that the wear scar width and depth of the distilled water were 0.36 mm and 4.03 µm, respectively, being the smallest of all the samples. With an increase of the JD2000 concentrations, the width and depth of the wear mark increased gradually. The results show that the water-based lubricant JD2000 had no anti-wear property on the 304 steel plate.  Figure 7a shows the COF of the different concentrations of the JD2000 aqueous solutions. The COF of distilled water was 0.361. In comparison, with the addition of 0.25, 0.5, 1, 2, and 4 wt.% JD2000, the COF decreased to 0.180, 0.181, 0.145, 0.129, and 0.205, respectively. It can be seen that, with the JD2000 concentration of 2 wt.%, the anti-friction property was improved by 64% compared with the distilled water. However, when the concentration was further increased to 4 wt.%, the COF of the system increased. The results show that the low JD2000 concentrations were unable to form tribofilms, while a high additive concentration caused an excess of long chains in the water that generated the aggregation complication and increased friction. Therefore, in this study, the JD2000 with concentration of 2 wt.% was applicable for the JD2000 to exert its lubrication ability.

Friction Reduction and Anti-Wear Properties of the Aluminum Plates
To further analyze the variation in the friction coefficient during the friction process, the real-time friction coefficient curves lubricated using the JD2000 aqueous solutions on the surface of the steel plates are shown in Figure 7b. It can be seen that the friction coefficient of the distilled water was very unstable and always fluctuated at a higher value. When a small amount of the JD2000 (0.25 and 0.5 wt.%) was introduced into the distilled water, the fluctuation and the friction coefficient of the aqueous solutions decreased. This can be attributed to the aluminum plate being less rigid than the steel balls. During the friction process, the rough surface directly contacted and sheared mutually under the squeezing action, making the soft aluminum plate easily produce metal debris. This led  Figure 7a shows the COF of the different concentrations of the JD2000 aqueous solutions. The COF of distilled water was 0.361. In comparison, with the addition of 0.25, 0.5, 1, 2, and 4 wt.% JD2000, the COF decreased to 0.180, 0.181, 0.145, 0.129, and 0.205, respectively. It can be seen that, with the JD2000 concentration of 2 wt.%, the anti-friction property was improved by 64% compared with the distilled water. However, when the concentration was further increased to 4 wt.%, the COF of the system increased. The results show that the low JD2000 concentrations were unable to form tribofilms, while a high additive concentration caused an excess of long chains in the water that generated the aggregation complication and increased friction. Therefore, in this study, the JD2000 with concentration of 2 wt.% was applicable for the JD2000 to exert its lubrication ability.

Friction Reduction and Anti-Wear Properties of the Aluminum Plates
To further analyze the variation in the friction coefficient during the friction process, the real-time friction coefficient curves lubricated using the JD2000 aqueous solutions on the surface of the steel plates are shown in Figure 7b. It can be seen that the friction coefficient of the distilled water was very unstable and always fluctuated at a higher value. When a small amount of the JD2000 (0.25 and 0.5 wt.%) was introduced into the distilled water, the fluctuation and the friction coefficient of the aqueous solutions decreased. This can be attributed to the aluminum plate being less rigid than the steel balls. During the friction process, the rough surface directly contacted and sheared mutually under the squeezing action, making the soft aluminum plate easily produce metal debris. This led to abrasive and adhesive wear, and the friction coefficient increased rapidly. Then, a portion of the debris was extruded from the friction orbit and entered the surrounding aqueous solution system, and the friction coefficient decreased accordingly. This process was repeated throughout the friction testing process, making the friction curve of the distilled water and a lower concentration of the JD2000 aqueous solutions change periodically. When the concentrations of the JD2000 increased to 1 and 2 wt.%, it was observed that the friction curve had no obvious fluctuation and remained at the lowest point. The friction coefficient of the 2 wt.% JD2000 aqueous solutions was very stable and stayed at the lowest value, showing that the JD2000 had the best anti-friction property at 2 wt.%. When the concentration of the JD2000 was increased to 4 wt.%, the friction curve resumed its periodic fluctuation, and the friction coefficient also increased. It is speculated that this was because the appropriate concentration of the JD2000 could well cover the surface of the aluminum plates, forming a stable friction film and preventing the direct contact of the rough surface. When the amount of additive continued to increase, the thickness of the lubrication film increased, which tended to form an agglomeration of molecular chains. This led to an increase in the friction coefficient.
PEER REVIEW 9 of 20 stayed at the lowest value, showing that the JD2000 had the best anti-friction property at 2 wt.%. When the concentration of the JD2000 was increased to 4 wt.%, the friction curve resumed its periodic fluctuation, and the friction coefficient also increased. It is speculated that this was because the appropriate concentration of the JD2000 could well cover the surface of the aluminum plates, forming a stable friction film and preventing the direct contact of the rough surface. When the amount of additive continued to increase, the thickness of the lubrication film increased, which tended to form an agglomeration of molecular chains. This led to an increase in the friction coefficient. The 3D topography and the profile depth curve of the wear marks on the surface of the aluminum plates after the friction test are shown in Figure 8. It can be clearly observed that the surface of the aluminum plates was heavily worn after the distilled water friction, with a width of approximately 3.1 mm and a depth of 92.5 μm. After the addition of the JD2000 lubricant, the wear amount decreased significantly, and the width and depth of wear marks decreased gradually with an increase in the JD2000 addition. With the addition of the 2 wt.% JD2000 in water, the width and depth of the abrasion mark were 0.7 mm and 2.3 μm, which were reduced by 77.4% and 97.5%, respectively, compared with that of the distilled water, greatly improving the friction and wear phenomenon of the water system. With this result combined with the real-time friction coefficient curves, it can be concluded that the 2 wt.% JD2000 water dispersion had the best comprehensive lubrication performance of all the samples. The 3D topography and the profile depth curve of the wear marks on the surface of the aluminum plates after the friction test are shown in Figure 8. It can be clearly observed that the surface of the aluminum plates was heavily worn after the distilled water friction, with a width of approximately 3.1 mm and a depth of 92.5 µm. After the addition of the JD2000 lubricant, the wear amount decreased significantly, and the width and depth of wear marks decreased gradually with an increase in the JD2000 addition. With the addition of the 2 wt.% JD2000 in water, the width and depth of the abrasion mark were 0.7 mm and 2.3 µm, which were reduced by 77.4% and 97.5%, respectively, compared with that of the distilled water, greatly improving the friction and wear phenomenon of the water system. With this result combined with the real-time friction coefficient curves, it can be concluded that the 2 wt.% JD2000 water dispersion had the best comprehensive lubrication performance of all the samples.
The wear volume at the wear mark on the aluminum plates with different concentrations of the JD2000 water solutions after the tribological experiment were calculated. The results are as shown in Figure 9. With an increase in the concentration of the additive, the wear volume gradually decreased. It can be seen that the wear volume of the distilled water was 0.034 mm 2 . With the addition of 2 wt.% JD2000 in the water, the wear volume of the abrasion mark was 0.004 mm 2 , which was reduced by 88.2% compared with that of the distilled water. Therefore, the JD2000 had an excellent anti-wear property on the aluminum plate. The wear volume at the wear mark on the aluminum plates with different concentrations of the JD2000 water solutions after the tribological experiment were calculated. The results are as shown in Figure 9. With an increase in the concentration of the additive, the wear volume gradually decreased. It can be seen that the wear volume of the distilled water was 0.034 mm 2 . With the addition of 2 wt.% JD2000 in the water, the wear volume of the abrasion mark was 0.004 mm 2 , which was reduced by 88.2% compared with that of the distilled water. Therefore, the JD2000 had an excellent anti-wear property on the aluminum plate. The wear volume at the wear mark on the aluminum plates with different concentrations of the JD2000 water solutions after the tribological experiment were calculated. The results are as shown in Figure 9. With an increase in the concentration of the additive, the wear volume gradually decreased. It can be seen that the wear volume of the distilled water was 0.034 mm 2 . With the addition of 2 wt.% JD2000 in the water, the wear volume of the abrasion mark was 0.004 mm 2 , which was reduced by 88.2% compared with that of the distilled water. Therefore, the JD2000 had an excellent anti-wear property on the aluminum plate.

Anti-Corrosion and Anti-Rust Property
The results of corrosion tests are shown in Figure 10. Corrosion grades were assigned according to the JB/T 9189-2016. It can be observed that, when the distilled water was used as anti-rust solution, the surface rust area of filter paper was more than 5%, which belongs to severe corrosion. When the 2 wt.% JD2000 aqueous solution was used as antirust solution, the surface rust area of filter paper was between 1% and 5%, belonging to moderate corrosion. Comparing the area of rust spots produced by the two kinds of anti-rust solutions, it can be seen that the addition of the JD2000 can reduce the corrosion degree by about 75.5%, which has significant anti-rust performance. signed according to the JB/T 9189-2016. It can be observed that, when the distilled water was used as anti-rust solution, the surface rust area of filter paper was more than 5%, which belongs to severe corrosion. When the 2 wt.% JD2000 aqueous solution was used as anti-rust solution, the surface rust area of filter paper was between 1% and 5%, belonging to moderate corrosion. Comparing the area of rust spots produced by the two kinds of anti-rust solutions, it can be seen that the addition of the JD2000 can reduce the corrosion degree by about 75.5%, which has significant anti-rust performance.

Analysis of Water Contact Angle Measurements Results
The ability to adsorb onto a metal surface is essential to the effectiveness of additives. Water contact angle measurements were performed to evaluate the adsorption behavior of polar molecules on the metal surface (Figure 11a-d). The results show that the contact angles of the surfaces decreased with the addition of the JD2000 additive, which contained multiple surface active nitrogen atoms [9]. This is because the nitrogen atoms can combine with the metal surface elements, forming a firm adsorption layer, which can still exist on the metal surface after rinsing. In the contact angle test, the hydrophilic group of the JD2000 can combine with water, and the water spreads out on the metal surface, resulting in the reduction of contact angles. The adsorption curve ( Figure  11e) shows that the JD2000 lubricant spreads faster on the metal surface and forms a film rapidly (as illustrated in the inset), which verifies the conjecture of adsorption film.

Analysis of Water Contact Angle Measurements Results
The ability to adsorb onto a metal surface is essential to the effectiveness of additives. Water contact angle measurements were performed to evaluate the adsorption behavior of polar molecules on the metal surface (Figure 11a-d). The results show that the contact angles of the surfaces decreased with the addition of the JD2000 additive, which contained multiple surface active nitrogen atoms [9]. This is because the nitrogen atoms can combine with the metal surface elements, forming a firm adsorption layer, which can still exist on the metal surface after rinsing. In the contact angle test, the hydrophilic group of the JD2000 can combine with water, and the water spreads out on the metal surface, resulting in the reduction of contact angles. The adsorption curve (Figure 11e) shows that the JD2000 lubricant spreads faster on the metal surface and forms a film rapidly (as illustrated in the inset), which verifies the conjecture of adsorption film.

Analysis of Water Contact Angle Measurements Results
The ability to adsorb onto a metal surface is essential to the effectiveness of additives. Water contact angle measurements were performed to evaluate the adsorption behavior of polar molecules on the metal surface (Figure 11a-d). The results show that the contact angles of the surfaces decreased with the addition of the JD2000 additive, which contained multiple surface active nitrogen atoms [9]. This is because the nitrogen atoms can combine with the metal surface elements, forming a firm adsorption layer, which can still exist on the metal surface after rinsing. In the contact angle test, the hydrophilic group of the JD2000 can combine with water, and the water spreads out on the metal surface, resulting in the reduction of contact angles. The adsorption curve ( Figure  11e) shows that the JD2000 lubricant spreads faster on the metal surface and forms a film rapidly (as illustrated in the inset), which verifies the conjecture of adsorption film.

Analysis of Adsorption Behavior Results
The change in frequency (∆f) depends on the quantity of the molecules adsorbed on the surface of the wafer. It can be seen that, with the adsorption of the JD2000 on the surface, ∆f of the wafer surface increased significantly (Figure 12a), indicating that the adsorption rate was greater than the desorption rate; the curve was stable after 15,000 s, indicating that the absorption/desorption rate had reached equilibrium at this time. After the surface was rinsed with dodecane, the curve had no obvious change, implying that the adsorption of the JD2000 on the metal surface was highly stable. The change in energy dissipation factor (∆D) reflects the internal viscoelasticity and structural changes of the substance. When ∆D < 10 −6 , it means that a rigid film is formed on the surface, and when ∆D > 10 −6 , a viscoelastic film is formed on the surface. As shown in Figure 12b, after adsorption on the surface, the elastic modulus of the JD2000 increased and far exceeded 10 −6 , showing that the JD2000 formed a typical viscoelastic film on the surface, which kept the film intact without fracture under the action of experimental load and provided long-term lubrication protection for the metal surface.
adsorption rate was greater than the desorption rate; the curve was stable after 15,000 s, indicating that the absorption/desorption rate had reached equilibrium at this time. After the surface was rinsed with dodecane, the curve had no obvious change, implying that the adsorption of the JD2000 on the metal surface was highly stable. The change in energy dissipation factor (∆D) reflects the internal viscoelasticity and structural changes of the substance. When ∆D < 10 −6 , it means that a rigid film is formed on the surface, and when ∆D > 10 −6 , a viscoelastic film is formed on the surface. As shown in Figure 12b, after adsorption on the surface, the elastic modulus of the JD2000 increased and far exceeded 10 −6 , showing that the JD2000 formed a typical viscoelastic film on the surface, which kept the film intact without fracture under the action of experimental load and provided long-term lubrication protection for the metal surface.

Analysis of the Worn Surfaces of Steel Plates
To further investigate the wear surfaces of the aluminum plates, the overall SEM images were recorded, as shown in Figure 13. Figure 13a1-a3 shows the surface morphology of the wear marks with different water lubrication under different magnifications. Figure 13b1-b3 shows the surface morphologies of the wear marks under different magnifications with the 2 wt.% JD2000 lubrication. The SEM of the wear surface with a higher magnification is shown on the left side to give more details of the wear surface. When the SEM images of the wear surfaces were viewed at the same magnification, it was clearly shown that the JD2000 corresponded to a smaller wear volume compared with the distilled water. It can be seen that the surfaces of the steel plates were severely worn under the distilled water lubrication, with obvious grooves and bumps. In addition, tiny metal fragments were distributed on the wear track. The surfaces were very coarse because of the experimental load. Direct contact between the surfaces of the friction pairs resulted in mutual shearing, and the friction between the rough surfaces made the surface particles peel off. This in turn led to the wear of the abrasive particles, resulting in a higher friction coefficient. With the addition of the additive, the surface quality was improved, and smooth surfaces with no metal debris, basically no grooves and bumps, and only slight scratches were obtained. In addition, the marks of the tribofilms filling can be observed. This could be attributed to the better adsorption of the

Analysis of the Worn Surfaces of Steel Plates
To further investigate the wear surfaces of the aluminum plates, the overall SEM images were recorded, as shown in Figure 13. Figure 13a 1 -a 3 shows the surface morphology of the wear marks with different water lubrication under different magnifications. Figure 13b 1 -b 3 shows the surface morphologies of the wear marks under different magnifications with the 2 wt.% JD2000 lubrication. The SEM of the wear surface with a higher magnification is shown on the left side to give more details of the wear surface. When the SEM images of the wear surfaces were viewed at the same magnification, it was clearly shown that the JD2000 corresponded to a smaller wear volume compared with the distilled water. It can be seen that the surfaces of the steel plates were severely worn under the distilled water lubrication, with obvious grooves and bumps. In addition, tiny metal fragments were distributed on the wear track. The surfaces were very coarse because of the experimental load. Direct contact between the surfaces of the friction pairs resulted in mutual shearing, and the friction between the rough surfaces made the surface particles peel off. This in turn led to the wear of the abrasive particles, resulting in a higher friction coefficient. With the addition of the additive, the surface quality was improved, and smooth surfaces with no metal debris, basically no grooves and bumps, and only slight scratches were obtained. In addition, the marks of the tribofilms filling can be observed. This could be attributed to the better adsorption of the active elements in the JD2000 on the surfaces, which formed a sheared film during the friction process and avoided direct contact between the metal surfaces of the friction pair.
To analyze the formation of the friction film on the steel surface under the 2 wt.% JD2000 lubrication condition, the MS of the JD2000 (Figure 4) and the friction-tested steel plates ( Figure 14) were compared. When the m/z values appeared near 567 and 854, it was speculated that this molecule was a JD2000 long chain that lost C 6 H 4 N 3 CH 2 NHand CH 3 -, and its degree of polymerization was 7 and 12, respectively. When the m/z value appeared near 642, the corresponding molecule was the additive long chain with a lost C 6 H 4 N 3 CH 2 NH-structure, and the degree of polymerization was 8. The results show that the chemical bonds of the JD2000 molecular long chain broke and formed long chains with different molecular weights. These would cover the worn surface and further participate in the formation of the lubricating film, filling the wear marks. Hence, during the friction process, they would play a protective role in preventing metal debris and more serious wear. active elements in the JD2000 on the surfaces, which formed a sheared film during the friction process and avoided direct contact between the metal surfaces of the friction pair. To analyze the formation of the friction film on the steel surface under the 2 wt.% JD2000 lubrication condition, the MS of the JD2000 (Figure 4) and the friction-tested steel plates ( Figure 14) were compared. When the m/z values appeared near 567 and 854, it was speculated that this molecule was a JD2000 long chain that lost C6H4N3CH2NH-and CH3-, and its degree of polymerization was 7 and 12, respectively. When the m/z value appeared near 642, the corresponding molecule was the additive long chain with a lost C6H4N3CH2NHstructure, and the degree of polymerization was 8. The results show that the chemical bonds of the JD2000 molecular long chain broke and formed long chains with different molecular weights. These would cover the worn surface and further participate in the formation of the lubricating film, filling the wear marks. Hence, during the friction process, they would play a protective role in preventing metal debris and more serious wear. The different element contents of the wear marks were obtained using EDS, as shown in Table 1. It can be observed that, when the distilled water was used as the lubricant, the most abundant element in the wear marks was Fe, which came from the metal  To analyze the formation of the friction film on the steel surface under the 2 wt.% JD2000 lubrication condition, the MS of the JD2000 (Figure 4) and the friction-tested steel plates ( Figure 14) were compared. When the m/z values appeared near 567 and 854, it was speculated that this molecule was a JD2000 long chain that lost C6H4N3CH2NH-and CH3-, and its degree of polymerization was 7 and 12, respectively. When the m/z value appeared near 642, the corresponding molecule was the additive long chain with a lost C6H4N3CH2NHstructure, and the degree of polymerization was 8. The results show that the chemical bonds of the JD2000 molecular long chain broke and formed long chains with different molecular weights. These would cover the worn surface and further participate in the formation of the lubricating film, filling the wear marks. Hence, during the friction process, they would play a protective role in preventing metal debris and more serious wear. The different element contents of the wear marks were obtained using EDS, as shown in Table 1. It can be observed that, when the distilled water was used as the lubricant, the most abundant element in the wear marks was Fe, which came from the metal Figure 14. The MS spectra of the friction-tested steel plates lubricated by the 2 wt.% JD2000 aqueous solution.
The different element contents of the wear marks were obtained using EDS, as shown in Table 1. It can be observed that, when the distilled water was used as the lubricant, the most abundant element in the wear marks was Fe, which came from the metal material of the friction pair and the wear debris produced during the friction process. C, Si, Cr, Ni, and Mn came from the inner material of the friction pair. When the JD2000 was introduced into the water, the worn surface containing N and O elements was derived from the JD2000, showing that the long chain JD2000 passed through the reactive elements and reacted with the metal surface. They then adhered to the surface stably and formed the protective film. In addition, the Mn element was only produced during the process of water friction, while its existence was not detected under the JD2000 lubrication. This indicated that the friction pair under water lubrication was seriously worn, and the wear was reduced after the addition of the JD2000. To further investigate the chemical composition of the tribofilms and illustrate the changes in the chemical states of the several typical elements on the worn surfaces, the composition of the wear marks on the steel plate after the friction test was analyzed using XPS. Figure 15 shows the high-resolution XPS spectra of C1s, O1s, Fe2p, and N1s. All of the XPS spectra were fitted using the Lorentzian-Gaussian method. The C1s spectra of the surface have a weak peak at 285.1 eV, which represents the C-O chemical bond. There are two new peaks in the C1s spectra of the lubricating film formed by the JD2000, and the peaks at 288.5 and 286.1 eV represent the C=O and C-C bonds of the lubricating film, respectively. These results indicate that the hydrocarbon compounds were absorbed tribo-physically on the worn surface. The peak of O1s at 531.0 eV came from the SiO 2 , and the additive-containing lubricant also contained NiO bonds in the friction film formed during friction. The peak of the Fe2p spectra at 708.3 eV corresponds to the binding energy of FeOOH. In addition, the binding energy peak at 705.7 and 718.8 eV correspond to Fe2p3 and Fe2p1, respectively, while the new signal peak at 76.5 eV is assigned to the Fe 2 O 3 , which was one of the components of the surface friction film. The spectra results of the N elements show that the active nitrogen elements in the additive also adsorbed on the surface of the steel plate, producing the binding energy peak of the N-O bond at 399.3 eV. This made the long chain in the JD2000 bind tightly to the surface of the steel plate during the friction process, and thus it played a protective role to prevent direct contact between the metal friction pairs. To further investigate the wear surfaces of aluminum plates, the SEM images o surface wear of the aluminum plates obtained by lubrication with distilled water an 2 wt.% JD2000 were compared under the same test conditions. Figure 16a1-a3 show

Analysis of the Worn Surfaces of Aluminum Plates
To further investigate the wear surfaces of aluminum plates, the SEM images of the surface wear of the aluminum plates obtained by lubrication with distilled water and the 2 wt.% JD2000 were compared under the same test conditions. Figure 16a 1 -a 3 shows the surface morphologies of the wear marks with the water lubrication under different magnifications. It can be seen that, under the distilled water lubrication, the surface of the aluminum plates was severely worn, and there were a large amount of wear debris and obvious cutting pits in the wear track. The surface was very rough, showing that the direct contact of the rough friction pairs caused surface particles to peel off and contribute a large amount of metal debris. This led to the deep and wide cutting pits. Figure 16b 1 -b 3 shows the wear marks of the 2 wt.% JD2000 lubrication under different magnifications. After adding the additive, the surface of the wear marks was smooth, with no obvious metal debris particles and grooves. However, it can be observed that the surface of the aluminum plates was covered with a thin layer of film, and the spalling lubricating film fragments can be clearly seen at a large multiple. This indicated that the JD2000 reacted with the metal surface during the friction process and produced the protected film. The fragments were produced when the chemical film was sheared during the friction process, which filled in the abrasion mark, avoided direct contact with the metal surface, and played an obvious lubrication role.  Figure 17 shows the MS of the friction-tested aluminum plates under the 2 wt.% JD2000 lubrication condition. It can be seen that the polymer can be detected at the wear place of the aluminum plates after lubrication with the JD2000, and the results are very similar to those of the steel plates. When the m/z values were near 569 and 855, it was speculated that this molecule was a JD2000 long chain that lost C6H4N3CH2NH-and CH3-, and its degrees of polymerization were 7 and 12. When the m/z value was near 649, the corresponding molecule was the additive long chain with the lost C6H4N3CH2NHstructure, and the degree of polymerization was 8. The results show that the chain of the JD2000 molecule broke and formed chains with different molecular weights during the friction process. This then filled in the wear track to prevent direct contact with the uneven metal surface.  Figure 17 shows the MS of the friction-tested aluminum plates under the 2 wt.% JD2000 lubrication condition. It can be seen that the polymer can be detected at the wear place of the aluminum plates after lubrication with the JD2000, and the results are very similar to those of the steel plates. When the m/z values were near 569 and 855, it was speculated that this molecule was a JD2000 long chain that lost C 6 H 4 N 3 CH 2 NH-and CH 3 -, and its degrees of polymerization were 7 and 12. When the m/z value was near 649, the corresponding molecule was the additive long chain with the lost C 6 H 4 N 3 CH 2 NHstructure, and the degree of polymerization was 8. The results show that the chain of the JD2000 molecule broke and formed chains with different molecular weights during the friction process. This then filled in the wear track to prevent direct contact with the uneven metal surface. speculated that this molecule was a JD2000 long chain that lost C6H4N3CH2NH-and CH3-, and its degrees of polymerization were 7 and 12. When the m/z value was near 649, the corresponding molecule was the additive long chain with the lost C6H4N3CH2NHstructure, and the degree of polymerization was 8. The results show that the chain of the JD2000 molecule broke and formed chains with different molecular weights during the friction process. This then filled in the wear track to prevent direct contact with the uneven metal surface. Figure 17. The MS spectra of the friction-tested aluminum plates lubricated using the 2% JD2000 aqueous solution.
The wear marks obtained by lubrication with the distilled water and 2 wt.% JD2000 under the same test conditions of the aluminum plates were analyzed using EDS, and the different element contents of the friction film were obtained. The results are shown in Table 2. When the distilled water was used as the lubricating fluid, the content of Al in the wear mark was as great as 74.2%, which is the primary component of the wear mark surface. In addition, it also contained a small amount of O and Mg, which came from the water and friction material, respectively. When the JD2000 was added into the water, the primary elements of the abrasion mark were Al, O, and C, and a portion of the C and O elements came from the JD2000. In addition, the primary composition of the friction film The wear marks obtained by lubrication with the distilled water and 2 wt.% JD2000 under the same test conditions of the aluminum plates were analyzed using EDS, and the different element contents of the friction film were obtained. The results are shown in Table 2. When the distilled water was used as the lubricating fluid, the content of Al in the wear mark was as great as 74.2%, which is the primary component of the wear mark surface. In addition, it also contained a small amount of O and Mg, which came from the water and friction material, respectively. When the JD2000 was added into the water, the primary elements of the abrasion mark were Al, O, and C, and a portion of the C and O elements came from the JD2000. In addition, the primary composition of the friction film on the aluminum plate was the stable chemical bond, which formed due to the reaction of the O and C elements in the JD2000 with the metal surface. To further investigate the chemical composition of the tribofilms and describe the lubrication mechanism of the JD2000, the compositions of the wear marks on the aluminum plates after the friction test were analyzed using XPS. Figure 18 shows the high-resolution XPS spectra of O1s, Al2p, C1s and N1s, illustrating the changes in the chemical states of several typical elements on the worn surfaces. All the high-resolution XPS spectra were fitted using the Lorentzian-Gaussian method. The Al2p and O1s spectra of the worn surfaces under the two lubrication types were analogous. The weak peaks at 74.2 eV for Al2p and Al2p signal intensity of the JD2000 were slightly stronger, which came from the reaction of the Al element with O during the friction process. The O in the JD2000 molecule promoted the formation of a more stable Al-O bond on the metal surface. The O1s spectra of both were at 531 eV, and the signal peaks at 532.8 and 532.8 eV were from Mg-O and Al-O, respectively. The peak of the JD2000 was slightly higher, which indicated that the oxygen element in the JD2000 also participated in the formation of the chemical bond. The peaks of the C1s spectra of the JD2000 at 284.6 and 285.6 eV came from the C-C and C-O bonds, respectively. The spectra of the N elements showed that the active nitrogen elements in the additive reacted with aluminum to produce the binding energy peak of the Al-N bond at 398.2 eV. This makes the long chain in the JD2000 bind tightly to the surface of the steel plate during the friction process and play a protective role in preventing direct contact between the metal friction pairs. This demonstrated that the long chain structure of the JD2000 molecules was part of the friction film, which filled in the wear marks and played a protective role during the friction process.
oatings 2021, 11, x FOR PEER REVIEW 18 Figure 18. The XPS spectra of (a) O1s, (b) Al2p, (c) C1s and (d) N1s on the wear scar of the a num ball lubricated using the 2 wt.% JD2000 aqueous solution as measured using the UMT meter.

Discussion
Based on the presence of tribo-oxides on the worn surfaces, the essential mechanism of this study was oxidative wear [17]. In the oxidative wear mechanism metal surface under mild wear condition had a typical single-layer of tribo-oxides. U severe wear condition, the multilayer layers of tribo-oxides were sheared off from surface during the friction process, leading to large plastic deformation. In this stud worn surface lubricated by distilled water suffered wide furrows and severe plast formation, resulting in the weak XPS signals of Fe2O3 and SiO2 on the surface from plates and aluminum plates [18]. It can be speculated that the multilayer tribo-o detached from the worn surface during sliding. The addition of the JD2000 led t slight scratches and few plastic deformation, and the strong XPS signals of oxide nitrides were detected on the surface. The QCM-D test confirmed the formation o coelastic film by studying the adsorption behavior of the JD2000 molecules on surface. The measurement of water contact angle further confirmed that the JD molecules can achieve stable adsorption on the metal surface through active nit element. The MS test results show that the adsorption membrane contains a large ber of polymers of different molecular weights. Therefore, combining multiple te sults, the lubrication and anti-rust mechanism of the JD2000 can be obtained. The

Discussion
Based on the presence of tribo-oxides on the worn surfaces, the essential wear mechanism of this study was oxidative wear [17]. In the oxidative wear mechanism, the metal surface under mild wear condition had a typical single-layer of tribo-oxides. Under severe wear condition, the multilayer layers of tribo-oxides were sheared off from the surface during the friction process, leading to large plastic deformation. In this study, the worn surface lubricated by distilled water suffered wide furrows and severe plastic deformation, resulting in the weak XPS signals of Fe 2 O 3 and SiO 2 on the surface from steel plates and aluminum plates [18]. It can be speculated that the multilayer tribo-oxides detached from the worn surface during sliding. The addition of the JD2000 led to the slight scratches and few plastic deformation, and the strong XPS signals of oxides and nitrides were detected on the surface. The QCM-D test confirmed the formation of viscoelastic film by studying the adsorption behavior of the JD2000 molecules on metal surface. The measurement of water contact angle further confirmed that the JD2000 molecules can achieve stable adsorption on the metal surface through active nitrogen element. The MS test results show that the adsorption membrane contains a large number of polymers of different molecular weights. Therefore, combining multiple test results, the lubrication and anti-rust mechanism of the JD2000 can be obtained. The schematic diagram is shown in Figure 19. It can be hypothesized that the molecules of the JD2000 can be adsorbed on the metal surface by the active element N, and the long-chain molecules can well cover the surface of the plate under the appropriate concentration to form a stable tribofilms and prevent direct contact with rough surfaces. In this situation, the friction state is boundary friction. The shear action appears on the lubricating film to keep the minimum friction coefficient. It also effectively reduces the occurrence of groove and abrasive wear, which can obtain a smoother surface. Therefore, compared with other water-based lubricants, the JD2000 has excellent lubrication performance. Xiangyuan Ye et al. [19] prepared a functionalized fluorinated graphene, which can only reduce the wear volume by 64% compared with that of the distilled water. The water solid carbon nanotube prepared by Xiaowei Pei et al. [20] can reduce the wear volume and COF by 40% and 46%, respectively. At the same time, the dense protective film can resist the corrosion of the surrounding media and delay the corrosion reaction. Most of the water-based additives have no obvious anti-rust performance and even accelerate the corrosion of metals.

EER REVIEW
19 of 20 et al. [19] prepared a functionalized fluorinated graphene, which can only reduce the wear volume by 64% compared with that of the distilled water. The water solid carbon nanotube prepared by Xiaowei Pei et al. [20] can reduce the wear volume and COF by 40% and 46%, respectively. At the same time, the dense protective film can resist the corrosion of the surrounding media and delay the corrosion reaction. Most of the water-based additives have no obvious anti-rust performance and even accelerate the corrosion of metals.

Conclusions
In this study, a polyether Jeffamine-triazole derivative which can be used as a water-based multifunctional ecofriendly lubricant additive on different material surfaces was synthesized, characterized, and investigated. The following conclusions can be drawn.
1. The preparation method is simple, and the raw materials are cheap and accessible.
The product can exert the excellent properties of raw materials without environmental pollution. Therefore, it can be used as an ecofriendly water-based additive. 2. The JD2000 was proved to be a multifunctional additive. It has excellent tribological properties compared with other water-based lubricants. The addition of the 2 wt.% JD2000 led to a reduction of 72.7% and 70.2% in friction for steel/steel and steel/aluminum contacts, respectively, relative to the distilled water, and the wear volume of the JD2000 reduced by 88.2% for steel/aluminum contact. The test also improved the anti-rust property of the JD2000 by 75.5%, while some water-based lubricants do not reduce or even enhance the degree of metal corrosion. 3. The adsorption behavior of the JD2000 on metal surface and the formation of viscoelastic film were confirmed by adsorption behavior test and water contact angle tests. Worn surface analysis further determined the structure of tribofilms, which were composed of nitrogen-containing substances, metal oxides, and even polymer deposition. It is speculated that the nitrogen atoms in the JD2000 are first adsorbed on the metal surfaces and then form tribofilms. As the third body, the tribofilms improve the tribological properties by preventing straight asperity contact from the sliding surfaces. Meanwhile, this stable viscoelastic film can resist the corrosion of the metal from the external environment and reduce the corrosion degree of the metal.

Conclusions
In this study, a polyether Jeffamine-triazole derivative which can be used as a waterbased multifunctional ecofriendly lubricant additive on different material surfaces was synthesized, characterized, and investigated. The following conclusions can be drawn.

1.
The preparation method is simple, and the raw materials are cheap and accessible. The product can exert the excellent properties of raw materials without environmental pollution. Therefore, it can be used as an ecofriendly water-based additive.

2.
The JD2000 was proved to be a multifunctional additive. It has excellent tribological properties compared with other water-based lubricants. The addition of the 2 wt.% JD2000 led to a reduction of 72.7% and 70.2% in friction for steel/steel and steel/aluminum contacts, respectively, relative to the distilled water, and the wear volume of the JD2000 reduced by 88.2% for steel/aluminum contact. The test also improved the anti-rust property of the JD2000 by 75.5%, while some water-based lubricants do not reduce or even enhance the degree of metal corrosion.

3.
The adsorption behavior of the JD2000 on metal surface and the formation of viscoelastic film were confirmed by adsorption behavior test and water contact angle tests. Worn surface analysis further determined the structure of tribofilms, which were composed of nitrogen-containing substances, metal oxides, and even polymer deposition. It is speculated that the nitrogen atoms in the JD2000 are first adsorbed on the metal surfaces and then form tribofilms. As the third body, the tribofilms improve the tribological properties by preventing straight asperity contact from the sliding surfaces. Meanwhile, this stable viscoelastic film can resist the corrosion of the metal from the external environment and reduce the corrosion degree of the metal.

4.
This research can broaden the application of this Jeffamine-triazole derivative in the additives field and validates its application potential as a water-based lubricating and anti-rust additive on different metal surfaces. Concurrently, it also provides an effective method for the preparation and application of an ecofriendly water-soluble polymer-based additive.