Life Cycle Assessment of Olive Pomace as a Reinforcement in Polypropylene and Polyethylene Biocomposite Materials: A New Perspective for the Valorization of This Agricultural By-Product

: The main environmental impact of olive oil production is the disposal of residues such as pomace and water vegetation. During the olive oil extraction process, the olive stone is milled and discharged within the olive pomace. However, olive stone ﬂour can be valorized as ﬁller for polymeric composites. A life cycle assessment of the olive pomace valorization was carried out by focusing on the manufacturing process of a biocomposite made of two different thermoplastic matrices, i.e., polyethylene and polypropylene. The functional unit is the production of 1 m 2 of a lath made of an olive pomace-based biocomposite. The analysis was carried out with the SimaPro PhD 9.1.1.1 software, and the database used for the modeling was Ecoinvent 3.6. The obtained results reveal that the hotspot of the whole process is the twin-screw compounding of the olive stone fraction, with the polymeric matrix and coupling agent, and that human health is the most affected damage category. It represents 89% for both scenarios studied: olive stone fraction/polypropylene (OSF/PP) and olive stone fraction/polyethylene (OSF/PE). Further research directions include the use of biosourced polymer matrices, which could reduce the impact of olive pomace-based composite manufacturing.


Introduction
Olive oil is one of the main agricultural products in the Mediterranean countries. The organoleptic and healthy properties of olive oil associated with its high consumption level have made the cultivation of olive trees expand worldwide, along with its consumption trends.
The production of olive oil includes several phases. First, the olives are washed in order to remove the impurities collected during the harvesting (e.g., leaves, twigs, stones, etc.). After washing, the olives are crushed to facilitate the release of the oil from the vacuoles. Then, the crushed olives are subjected to a malaxation process, where the paste is mixed, allowing small oil droplets to combine into bigger ones. The last step is the separation of the oil from the rest of the olive components. The oil can be extracted by mechanical pressing (i.e., a discontinuous process) or centrifugation (i.e., a continuous process) [1,2].
It is worth noting that the pressing method is the oldest system for olive oil extraction, known as the traditional method. Nevertheless, it is still used in some small mills and has a processing extraction yield of around 86-90% [3].
The centrifugation method covers the need for a continuous extraction process. This method works on the basis of centrifugal force, where the less dense liquid phase forms a concentric inner layer, whereas the denser solid particles are pushed against the wall of the rotating bowl [3]. This extraction process presents two operation alternatives: the three-phase and the two-phase horizontal centrifugation methods.
The difference between the two-phase and three-phase horizontal centrifugation is not whether or not water is added, as it is often mistaken. The difference lies in the number of output streams that the decanter has: • On the one hand, the three-phase centrifuge has as an output for olive oil, vegetable water, also known as olive mill wastewater (OMW) (alpechin in Spanish) and pomace (orujo in Spanish).

•
On the other hand, the two-phase centrifuge has as an output for olive oil, and other for wet pomace (alperujo, contraction of alpechin and orujo in Spanish).
It should be noted that the two-phase decanter requires a minimum moisture content of the olive paste (about 50%) to facilitate the separation process. If the olive paste is too dry before being introduced into the decanter, it will be necessary to incorporate a certain amount of water until the moisture level required for a proper operation of the decanter is reached [4]. For this reason, water can be added to the two-phase centrifuge system as well. Compared to the traditional method, the three-phase centrifugation device increases water utilization (from 1.25 to 1.75 times more) [3]. Moreover, valuable components, especially natural antioxidants, can be lost in the water phase (OMW), thus reducing the olive oil quality.
The rising popularity of olive oil has increased the generation of its by-products: the olive pomace (OP), a general term used to refer to the pomace obtained from all the different olive oil extraction processes, and an effluent known as OMW, derived from traditional pressing and from the three-phase system, as mentioned before [5,6].
This OP is a mixture of residual skin, pulp, and fragments of the crushed olive stone [7]. The main components of this solid residue are cellulose, hemicelluloses, and lignins. Residual fat and proteins are also present in noteworthy quantities. The moisture content of the solid residues is 22-25% for traditional pressed olive pomace, 65-74% for pomace from a two-phase system, and 40-50% for that from a three-phase one [1,5]. On the other hand, OMW is a red-to-black colored acidic liquid, with 83-92% content of water, its main components being phenolic compounds, sugars, and organic acids. OMW also reveals an important quantity of potassium [5].
On average, olive fruit contains 20 wt.% of oil, and the remaining 80 wt.% together with the added water form OP [8]. Olive oil processing is considered inefficient due to the high volume of waste generated [9]. This particular industry has a seasonal production, which generates a high amount of waste in a short period of time. The olive oil industry causes many environmental impacts in terms of resource depletion, land degradation, air emissions, and waste generation. Moreover, the management of olive oil residues is an economic burden to producers [10][11][12][13][14]. In Europe, the production of OP reaches approximately 6.8 million tons per year [15].
Currently, olive oil by-products are discharged on agricultural land by controlled spreading [5,10,16]. Due to its high content in phenolic and lipidic constituents, organic acids, low pH, and salinity, OP should not be used as agricultural spreading [17]. Moreover, OP is resistant to bacterial degradation, which makes it a significant source of environmental pollution [17]. Another use of OP has been in animal nutrition. As an example, it is used in Tunisia in mixture with bran or even cactus to feed dromedaries or sheep. In countries such as Italy and Greece, cows are fed with OP. However, it can cause digestive problems in animals due to its high degree of lignification [18]. On the other hand, OP has also been used for composting, or to produce a non-phytotoxic product through biological conversion (bioremediation), which can be used as a fertilizer [5,19,20].
Over the years, many other methods have been proposed for olive oil waste disposal and valorization. These techniques include thermo-chemical processes, anaerobic digestion, fermentation, blending, and chemical extraction of bioactive compounds [1,[21][22][23]. Valorization routes also include the production of activated carbons, cosmetic applications, the production of polyols, and the improvement of the thermal properties of cement mortar [24][25][26].
In the most recent years, research has focused on the valorization of OP on the biocomposite field [7,17,23,[27][28][29][30][31][32][33]. Due to their natural richness in lignocellulosic fibers, this sector uses agricultural wastes (or by-products) as renewable fillers for polymeric matrices. The obtained results from olive stone flour have confirmed its viability as a cheap reinforcing filler for the polypropylene matrix, thus opening new perspectives for the use of this by-product [32]. The developed composites could find applications in buildings, in the automotive industry, and as outdoor products, e.g., deck floors, furniture, park benches, etc. Specific examples of this application are those from the GO-OLIVA project (Spain), which developed Olipast, a new sustainable packaging material from olive pits [34], and from the Biolive company, which commercializes the Bio-Pura product, used for the manufacture of television components (Turkey). The Biolive company is also working to produce shrink wrap for beer can from this material; and other end products for various applications, including consumer electronic casings, automotive interiors, toys, and packaging. Approximately 3.5 tons of bioplastics can be transformed from 5 tons of locally sourced olive seeds [35,36].
Since 2015, French authorities have developed "the Energy Transition Law for Green Growth". This law has focused on waste management as an essential pillar to ensure the transition to a circular economy model [37]. Moreover, the use of the circular economy is becoming increasingly important, especially in the field of agriculture, one of the main suppliers of waste. In particular, much research is being carried out to transform agricultural residues by sustainable processes.
For all these reasons, it is crucial to solve the waste management issues generated by OP and to explore the alternatives to convert this by-product into a co-product. Previous publications, like the one by Espadas-Aldana et al. [12] compiled the studies of environmental life cycle assessment of olive oil and some waste management techniques. Several authors have focused on the life cycle assessment of olive oil extraction waste treatment [23,[38][39][40][41][42]. Here, the current case study is on the valorization of the olive pomace and its life cycle assessment, focusing on the manufacturing process of a biocomposite. To the authors' knowledge, this is the first environmental life cycle assessment study made on biocomposites from olive pomace in order to innovate on the by-product valorization from olive oil production.
The aim of this article is to evaluate the environmental performance of a biocomposite composed of olive pomace reinforcement and a polymeric matrix. Data for the compounding process come from a pilot scale experiment to produce lath for terraces. Two scenarios were investigated which are differentiated by the polymeric matrix used: i.e., one made from polyethylene and the other from polypropylene.

Materials and Methods
Life cycle assessment (LCA) is defined as "a tool to assess the potential environmental impacts and resources used throughout a product's life cycle" [43]. The ISO 14040 [44] standard states that the LCA framework includes four phases: Goal and scope definition, Inventory analysis, Impact assessment, and Interpretation.

Goal and Scope of the Study
The following LCA focuses on the manufacturing process of a biocomposite made of olive stone fraction (OSF), which is part of the olive pomace (OP), and two different polymeric matrices: polypropylene (PP) and polyethylene (PE).
The goal of this LCA is to analyze and compare the environmental impacts of the different scenarios and to identify the unit process with the strongest environmental impacts, in order to improve the current valorization of olive pomace.

Functional Unit
In order to build the production inventory and set the scope of the study, the functional unit is defined. Based on similar works [45][46][47] and EN 15804 [48], the functional unit chosen is the production of 1 m 2 of lath (used as building material) made from the olive pomace-based composite. Figure 1a,b show a diagram of the lath and its dimensions.

System Boundary
The ISO 14044 [49] states that the system boundary is a "set of criteria specifying which unit processes are part of a product system". In order to focus on the impacts related to the development of a new biocomposite made from OP as filler, and PP or PE, respectively, as thermoplastic matrix, a "cradle-to-gate" approach life cycle assessment was carried out. This study is centered on the generation of the raw materials and manufacturing of the biocomposites. In Figure 2, system A shows the completed life cycle of the biocomposite; system B comprehends the generation of the raw materials, and the manufacturing process of the composite; system C1 shows the production of the raw materials used in the process; system C2 shows the manufacturing process of the product and the necessary pretreatment (i.e., drying, milling, etc.) to prepare the OP fraction. Finally, system C3 includes the use and end of life of the product. It is important to mention that system B comprehends the complete system boundary of the LCA herein. Namely, the system studied takes into account the production of all the raw materials needed (i.e., OP, PP, PE, and the coupling agents added to the compound to reinforce the matrix/filler interface), and the production of both composites. Several hypotheses must be considered in the actual approach in order to avoid overlaps in the decision-making process:

•
The necessary infrastructure is not taken into account, consequently excluding their manufacture as well as their dismantling, • The electricity is considered to come from the mixed French energy supply, • The cleaning of the devices used in the process is neglected, • The transportation of the olive pomace is not taken into account.
The current study presents two different scenarios, which correspond to the mixture of the olive stone and the two different polymeric matrices ( Table 1). The polymeric matrices studied are PP and PE. The OSF acts as a filler in the polymeric matrix [27,28].

Life Cycle Inventory Analysis
The life cycle inventory (LCI) collects and compiles all data on elementary flows from all processes in the studied product system(s) drawing on a combination of different sources. The output is a compiled inventory of elementary flows that is used as the basis of the subsequent life cycle impact assessment phase.

Process Tree
Based on the analysis of various publications [7,17,28,[30][31][32]50], all the manufacturing processes of olive pomace-based composites presented similar unit operations. First, crude olive pomace is dried in an oven at 60 • C for 24 h. Then, crude olive pomace is milled in a ball mill device at ambient temperature, 86 rpm for 30 min [7].
The powder passes into an electric sieving machine (RITEC, model 400, Signes, France) through a 1.25 mm mesh for 10 min. Two fractions are obtained, the fine fraction corresponds to the pulp-rich fraction (PF) and is recovered at the bottom of the sieve; whereas, the coarse fraction is retained in the sieve [31].
The coarse fraction is further ground in a knife mill (SM 300, Retch, Haan, Germany), with a speed of 1500 rpm and a grid size of 1 mm [7]. Then, the ground powder is sieved through a 0.4 mm mesh to separate the OSF from the intermediate fraction [7]. Polymer granules and the OP-based filler were then blended into a twin-screw extrusion compounding device. The coupling agents used are PE-g-MA (polyethylene-grafted-maleic anhydride) and PP-g-MA (polypropylene-grafted-maleic anhydride) agents, for the PE and PP thermoplastic matrices, respectively.
The presence of dust during the grinding process is very common. The main particle size present is PM10 (particles with the size smaller than 10 µm); nevertheless there are also particles with smaller size, such as PM2.5 (particles with the size smaller than 2.5 µm). Regardless of the milling method, organic dust is always produced when lignocellulosic materials are ground [51]. Dust is harmful to the working environment. Therefore, the particulate matter (i.e., the smallest particles) have to be recovered by a cyclone, and the content conveyed to a dry storage bin [52]. The equipment used for grinding includes a cyclone that recovers all the particulates, and collects them directly on a container [53].
The development of the biobased lath is part of a confidential work carried out by the Laboratoire de Chimie Agro-industrielle (Université de Toulouse, Toulouse, France) on behalf of a biosourced plastics industrialist [54]. Composites had been produced by mixing the OP (60% filler) in two polymeric matrices: PE and PP. The addition of a coupling agent has also been carried out to reinforce the matrix/fiber interface. As a result, adding OP to the polymeric matrices showed a mechanical reinforcement of the material, which was illustrated by the increase of the elastic modulus simultaneously with the decrease of the elongation at break, both in tensile and in bending. Figure 3 itemizes the process tree of the manufacturing of the olive stone composite, with the different stages of the process and their flows.

Data Collection
Inputs: Raw Materials

•
Olive pomace OP is a mixture of different fractions, the pulp-rich fraction (PF), stone-rich fraction (OSF) and intermediate fraction, whose percentage weights are 31.3, 56.4, and 11.7%, respectively [7]. The moisture of the crude olive pomace considered for the process is 53%, which is close to a three-phase system pomace. The moisture of the material is then decreased to 9% thanks to a drying process [7]. The energy consumption linked to the drying, crushing, and sieving of the olive pomace comes from the technical data of the machinery used and literature data [53,[55][56][57]. The grinding of the olive husk gave 80% of the weight of the sample [58]. This value was used in the milling of the coarse fraction due to missing data. For the modeling of "Crude olive pomace 53% moisture", the olive pomace dataset was adapted from the AGRIBALYSE v3.0 database according to Avadí [59].
The above-mentioned database considers that the impact of olive cultivation is attributed only to olive oil. Nevertheless, a part of the impact of olive oil production is attributed to the virgin olive pomace at an economic allocation of 2.32%. These characteristics belong to the "Olive pomace" file presented in Table 2. Then, this virgin olive pomace follows a new extraction process to obtain pomace oil and de-oiled pomace. There again, a part of the impact is attributed to the de-oiled pomace with an economic allocation of 9.47%, named "Olive pomace, processed" ( Table 2). Table 2. Background data for the modeling of olive pomace, processed. Adapted from [59].

Process Input/Output Amount Comment
Olive pomace

• Polymeric matrices
The word "composite" indicates that two or more separate materials are combined on a macroscopic scale to form a structural unit for various engineering applications. The composite is constituted by the reinforcement (olive stone) and the matrix. Polymers with thermoplastic behavior are usually used as matrix materials in composites [61].
In the present study, the polymers considered for the matrices are PP and PE, as they are very common thermoplastic polymers used for many applications. Being able to originate from petrol just as from renewable resources, PE is produced through radical polymerization, anionic polymerization, and cationic polymerization, while PP is obtained from high temperature cracking of petroleum hydrocarbons and propane. The properties of PP are almost similar to those of PE. However, PP does not present stress-cracking problems, and it offers electrical and chemical resistance at high temperatures. Besides, it has a little lower density, and its structure is hard and more rigid [62].
The product studied is 1 m 2 of lath made of olive pomace-based composite. The dimensions of the profile are 10 cm × 3 cm on the outside, and 1.72 cm × 1.8 cm for the 4 interior spaces, and 1 m in length, as shown in Figures 1 and 2. For a superficial area of 1 m 2 , the total quantity of profiles used is 10. The total area is 0.0174 m 2 , and the volume of 1 m 2 of lath (building material) is 0.0174 m 3 . For the latter calculation, the hypothesis of lath contiguous (no space between them) was supposed. Table 3 shows the density of each composite and the mass needed for the production of 1 m 2 of lath. The density of the composites was taken from the extrapolation of the results of Uitterhaegen et al. [54]. Table 3. Density and mass for the production of 1 m 2 of lath made of olive pomace-based composite. Adapted from [54].

Composite
Density ( The coupling agent improves the compatibility between the natural fiber and the polymeric matrix. The main incompatibility cause of natural fibers and polymer inside composites is due to the hydrophilic properties of natural fibers and the hydrophobic ones of the thermoplastic matrices. To improve the reinforcement effect of the filler, and especially to ensure efficient load transfer from the matrix to the filler, some authors [27,28,32] used a polymer-based coupling agent to improve the mechanical properties, especially the maximal strengths, of lignocellulosic-plastic composites. In the present study, polypropylene-grafted-maleic anhydride (PP-g-MA) and polyethylenegrafted-maleic anhydride (PE-g-MA) were used as coupling agents. The percentage used in the formulation of the composite was 6 wt.% Table 4 shows the data used in the modelling of the coupling agents. In particular, the percentages of maleic anhydride of each compound were taken from the formulation of the commercial compound. Table 4. Data for the modeling of the coupling agents (PP-g-MA, PE-g-MA).

Process
Input/Output Amount Comment Ref.

Input
---Maleic anhydride 0.09 kg 8-10%wt, an average between the two values was taken as reference. [63] The data considered for the modeling is the formulation of the commercial compound. - The data considered for the modeling is the formulation of the commercial compound.
-Outputs: By-Products of the Olive Stone Composite Manufacturing The by-products obtained during the processing of the composite (Figure 3), such as olive stone dust and intermediate and fine fractions, can be used as biofuels. The most common waste management approach for the by-products is incineration [28]. As with other fuels, the heating value depends on the moisture content and ranges from around 17 MJ/kg (moisture 10%) to 20 MJ/kg (moisture 6%) [65]. Incineration of natural fibers results in recovery of energy and carbon credits [66]. Another common waste management approach is composting [23,40].

•
Boiler combustion of olive stone dust Olive mills used combustion to obtain thermal or electric energy, due to the high calorific power of the dried olive husk (4000 kcal/kg) [67]. However, the energy obtained by combustion is used for dryness of the fresh two-phase olive waste mill, which decreases the total energy recovery [10,68].
Wood lower heating values (LHVs) range between 10.5 MJ/kg for wet wood and 18.6 MJ/kg for dry wood [69].
The properties of the olive pomace present more advantages than other biomass. Indeed, it has a low sulfur content between 0.12% and 0.26%, and an LHV in the range of 16.4-18.6 MJ/kg [10]. Moreover, the LHV of olive stone presents similar values in the range of 16.2-19.2 MJ/kg. Table 5 shows some LHVs of olive stone found in the literature. It is worth mentioning that olive pit is another term used to refer to the olive stone. For the modeling of the "boiler combustion" on SimaPro (PhD 9.1.1.1, PRé Sustainability, Amersfoort, The Netherlands), the combustion of natural wood chips from forest (Heat production, untreated waste wood, at a furnace 1000-5000 kW CH) was chosen as process reference. Included activities start from the delivery of waste wood to the combustion of untreated waste wood chips. It comprises the infrastructure (dust collector, furnace), the wood requirements (LHV), the emissions to air, the electricity needed for its operation, and the disposal of the ashes. The LHV of wood used in the file was 14.0 MJ/kg.
On the other hand, the LHV of olive stone is bigger than that of wood. Therefore, a corrective factor between the olive stone and wood was used in order to adjust the modeling.
The following data were used for comparing the olive stone per kg of wood. The LHV of wood is 14.0 MJ/kg and the average LHV of an olive pit is 17.5 MJ/kg. After comparing these values, the amount of olive pit that would replace the wood in the boiler is 0.80 kg olive pit per kg of wood.
An example is the milling process, where the quantity of olive pit dust produced is 0.20 kg. This value was replaced by 0.25 kg of wood as a factor of 0.80 kg olive pit/kg wood was used for this calculation.

•
Composting of pulp-rich fraction The main by-product of the "Sieving 1" process is the olive pulp. For the treatment of this waste, the industrial composting of biowaste process was chosen (Biowaste {CH}|treatment of biowaste, industrial composting|Cut-off, U). The composting treatment is a process of controlled decomposition and humidification of biodegradable materials under managed conditions, which is aerobic and which allows the development of temperatures suitable for mesophilic and thermophilic bacteria as a result of biologically produced heat. The inventory refers to 1 kg of fresh weight of biogenic waste.
The activities of the process include energy demand for operating a compost plant as well as process emissions, infrastructure of the compost plant, and transports related to the collection of the biogenic waste.

Inventory Tables
Pretreatment data were obtained from the literature. Pre-industrial scale trials carried out in the Laboratoire de Chimie Agro-industrielle (Université de Toulouse, Toulouse, France) have provided the data of the compounding process [54].
The tables below show the data used for the completed modeling of the process. Table 6 shows the Global LCI data corresponding to the foreground system for the production of the olive pomace-based composite. The data of each process are reported per 1 kg of output. Table 7 shows the description of the main background processes from Ecoinvent 3.6 considered in this study, and Table 8 shows the LCI data corresponding to the production of an olive pomace-based composite reported per functional unit. Table 6. Global life cycle inventory data corresponding to the foreground system for the production of the olive-based composite. Data of each process are reported per 1 kg of output.

Life Cycle Impact Assessment
The system scenarios were developed and analyzed with SimaPro PhD 9. . The methodology takes into account the midpoint indicators from CML, and the endpoint indicators from Ecoindicator [76]. The database used for the modeling was Ecoinvent 3.6.
Modeling elements are used to link midpoint indicators to one or more endpoint indicators, which are representative of different topics or "areas of protection" (AoP) that "defend" our interests as a society with regards to human health, ecosystems or ecosystem services and resources [43]. The ReCiPe 2016 methodology includes 18 midpoint impact categories, and three areas of protection or endpoints [77]. The different midpoint indicators contribute to a small set of endpoint indicators as can be observed in Figure 4.  6 show the result of the LCA of 1 m 2 of lath (building material) made of OSF/PE and OSF/PP composites, respectively. As we can observe in both production processes, the main hotspot is the compounding process, which affects all the impact categories, the most affected ones being global warming (88%), freshwater eutrophication (87%), and fossil resource scarcity (95%). Inside the compounding process, the main hotspot is the production of PE and PP. Fossil resource scarcity is the most affected midpoint indicator, due to the production of ethylene and propylene (in the petrochemical industry). Another impact category that is highly affected by compounding is human carcinogenic toxicity, which reaches values of 86% and 82% for OSF/PE and OSF/PP composites, respectively.   Figure 7 shows the pie chart of the OSF/PE and OSF/PP compounding processes. From the three damage categories, the most influenced is human health, with a value of 88%, follow by ecosystems and resources availability, with 6% in both categories. In the human health category, the main contributor is the polymeric matrix (PE and PP) (83%), whereas the coupling agent (PP-g-MA and PE-g-MA) contributed 15% of the impact in the mentioned category of each scenario. The electricity need for the process has the lowest contribution, i.e., only 2%.

Figures 5 and
From Tables 9 and 10, it is possible to observe the main input and substance that contribute to the pollution of each process. The contribution percentages of each input are expressed based on 100% of each midpoint indicator. The substance percentages are first calculated from the total of all substances of each process, and the percentage expressed in the table is the percentage that corresponds only to the input mentioned (e.g., in the drying process, 85% of the global warming is due to the input of "Olive pomace, processed" and the remaining 15% is due to "Electricity"). A total of 92% of the substances are from "Carbon dioxide, fossil" and this breaks down to 79% from "Olive pomace, processed" and 13% from "Electricity". Table 9 details the pollutants corresponding to drying, milling and sieving processes, which are similar for both scenarios. Table 10 details the pollutants corresponding to the compounding process in both scenarios. As mentioned before, freshwater eutrophication is highly impacted by the compounding process. This indicator shows that along the process the main impacts are produced by consumption of energy (electricity) from the machines, the combustion and composting process of the waste, and the impacts coming from the polymeric matrices (PP, PE) in both cases. Tables 9 and 10 show that the main pollutant in human carcinogenic toxicity is Chromium VI in water. The values of this midpoint indicator were 721 g 1,4-DCB for the OSF/PE composite, and 574 g 1,4-DCB for the OSF/PP one. Terrestrial ecotoxicity is one of the main contributors to pollution in the case study. The production of 1 FU of the OSF/PE composite released 61.4 kg 1,4-DCB, while the production of the OSF/PP one released 58.8 kg 1,4-DCB. The two main metals emitted during the life cycle of the product were zinc and copper, which generated damages on the ecosystems, especially the soil [78]. The results show that fossil resource scarcity indicator is similar in both cases, with 13.2 kg oil eq for the OSF/PE composite and 13.3 kg oil eq for the OSF/PP one. The mineral resources scarcity indicator (Table 10) shows that the polymeric matrices (PE and PP) depleted the environment with different substances: the OSF/PE composite mostly drains gold, while the OSF/PP one mainly drains titanium. All the results for each impact category for both biocomposites are presented in Table 11.     Figure 8 represents the single score result of the LCA production of 1 m 2 of the OSF/PE and OSF/PP laths, respectively. It is worth mentioning that the score used in the charts is called eco-points (Pt). One eco-point can be interpreted as one thousandth of the annual environmental load of one average European inhabitant [79]. In both scenarios, the most impactful process was compounding, where human health was the more affected area of protection. The results show similar values for the compounding of OSF/PE and OSF/PP composites, 574 and 548 mPt, respectively. The human health category repeated along the different processes. Therefore, it can be identified as an area of concern. The contribution for this endpoint category was 89% for both scenarios. Ecosystems and resources availability had a small impact in comparison with human health, their total values being 53.7 mPt (6%) and 36.5 mPt (4%), respectively, for the OSF/PE composite, and 52.5 (6%) mPt and 37.1 mPt (5%), respectively, for the OSF/PP composite. As mention before, the main contributor to these damage categories was the compounding process. For ecosystems, the contribution of this process to the total damage category was 76% for both scenarios, while compounding represented 96% of the resources availability category.

Comparison with a Conventional Lath
For comparing the performance of the herein biocomposites made of olive stone flour and its application as a building material, it is important to compare it with a business-asusual scenario for this type of application. A common material used for this is "PVC decking".
This term is used to refer to plastic decking that uses cellular polyvinyl chloride (PVC) as the building material of the lath. Cellular PVC is lighter than standard PVC due to the addition of a foaming agent throughout the manufacturing process [80]. The authors reported that the production of 9.3 m 2 of installed PVC decking in service for 25 years produces 426 kg CO 2 eq. That project considered the full life cycle of the decking product, starting from the raw material extraction to the final disposal in a municipal solid waste landfill [80]. The preliminary results (cradle-to-gate) of this project reported the emission of 368 kg CO 2 eq. This translates into 39.6 kg CO 2 eq for 1 m 2 of PVC decking. In contrast, the herein work results show that the production of 1 m 2 of OSF/PE and OSF/PP lath releases 20.5 kg CO 2 eq and 20.3 kg CO 2 eq, respectively. This may indicate that the pollution caused by PVC decking is almost two times bigger than that caused by the olive pomace-based composites.
What is certain is that PVC is considered carcinogenic and environmentally hazardous due to the presence of organochlorines. In contrast, PP and PE are chlorine-free plastics [81].

Biosourcing the Matrix
The most common polymeric matrices used for biocomposites are produced from petrochemicals and are not biodegradable. This type of polymer generates long-term negative impacts on the environment and human health [17]. It should nevertheless be noted here that biosourced polyolefins exist on the market, especially BioPE, which is produced from sugar cane waste, and, to a much lesser extent, BioPP.
Biodegradable and biosourced polymers are raising great interest, due to the growing environmental concerns and the decline of the fossil resources [30]. Among the mentioned polymers, PLA (poly(lactic acid)) and polyhydroxyalkanoates (PHAs) (e.g., PHB (polyhydroxybutyrate), PHV (polyhydroxyvalerate), PHBV (polyhydroxy-butyrate-co-valerate)) are commercially available polymers, produced in large scale and able to compete with more traditional petroleum-based plastics [17,30,82]. The environmental assessment of this biodegradable composite reinforced with OP can be the objective for further studies.

Impact of the Diversion of the Olive Pomace from Its Original Use
It is important to contemplate the consequences of diverting the olive pomace from its original use.
The conventional uses of olive oil by-products explained earlier (1. Introduction) are their controlled spreading, their use as a mixture in animal nutrition, and composting.
Olive wastes are frequently discharged on soil. The production of 1 L of extra virgin olive oil (EVOO) leads to the emission of around 57 g CO 2 eq. This practice is widespread around the European Community as it is supported by the law in many countries [6,83].
Duman et al. [23] studied the composting scenario in Turkey, and found that 2.25 kg of OP in a mixture with 0.34 kg of wheat straw and 0.67 kg of poultry manure can produce 2.09 kg of compost and release to the atmosphere 6.82 kg CO 2 eq, with nitrous oxide as the main emission [23].
For the production of the herein functional unit (1 m 2 of lath (building material) made of olive pomace-based composite), an average of 46.7 kg OP is used. Compared with the results of Duman et al. [23], the composting of the same quantity of OP would liberate to the environment 141.5 kg CO 2 eq, which is almost seven times higher than the pollution caused by the olive pomace-based composites.
The controlled spreading of those 46.7 kg OP would liberate to the environment 0.665 kg CO 2 eq. This is taking into account that, on average, olive fruit contains 20 wt.% of oil, and the remaining 80 wt.% together with the water added during the olive oil extraction process form OP. The production of 1 L of EVOO generates 4 kg of OP. The controlled spreading of OP is about thirty times less polluting than the production of 1 m 2 of olive pomace-based composites. Nevertheless, the direct application of this olive oil by-product can cause negative effects on soil due to its high mineral salt content, low pH and presence of polyphenols [6].

Carbon Sequestration
To deepen the information obtained on this work, the importance of an expected benefit of biocomposites can be discussed, namely long-term carbon sequestration.
The U.S. Environmental Protection Agency defines biogenic CO 2 emissions as CO 2 emissions associated with the natural carbon cycle, together with the emissions resulting from the combustion, harvest, digestion, fermentation, decomposition, or processing of biologically based materials [84]. Products and residues of the olive orchard cultivation contain biogenic carbon derived from the uptake of CO 2 by the crop [85].
When talking about olive oil production, the biogenic carbon from the agricultural phase (olive tree permanent components, especially taking into account the longevity of olive groves) does not become part of the product (olive oil). Therefore, in accordance with PAS 2050, the assessment of biogenic carbon should be taken into account when performing an LCA that considers this phase within its system boundaries [12]. Storing carbon during a long lifespan (composite decking can last between 25 and 30 years) can mitigate climate change because of the delay in the carbon emissions into the technosphere. This advantage, however, could not be quantified with the static LCA approach used in this study. A rough estimation of biogenic carbon, based on the work herein presented, shows that 1 FU of the olive pomace based-composite could contribute to delaying the emission of over 32.5 kg CO 2 (considering a humidity content of OP of 53% and a percentage of total carbon for a three-phase centrifugation of 29%).

Conclusions
In this study, the valorization of an olive pomace-based biocomposite was evaluated through the environmental criteria, with the LCA method. The functional unit is the production of 1 m 2 of a lath (building material) made of an olive pomace-based biocomposite. Two scenarios with different thermoplastic matrices (PE, PP) were assessed. In both cases, the twin-screw compounding process contributed the major burden in most of the midpoint impact categories. Compounding is mainly affected by the production of the respective polymers. When comparing the OSF/PE and OSF/PP materials, the impacts are relatively similar. Therefore, a further study at the end of life of the material should be carried out to conclude which of the proposed biocomposites is the less polluting one.
The results obtained showed that human health is the most affected area of protection; it represented 89% for both scenarios, i.e., OSF/PP and OSF/PE. The main contributors to this damage category are energy, carbon dioxide and sulfur dioxide, used and produced in the manufacturing process. Ecosystems and resources availability represented a lower contribution to the total impact. Scenarios presented values of 6% and 4.5% for ecosystems and resources availability, respectively.
The comparison of the olive pomace-based-composite with the business-as-usual scenario shows that the biocomposite released half of the pollution produced by the PVC decking, when considering the same FU. Besides, given the long lifespan of the biocomposites, the CO 2 stored on it can mitigate climate change because of the delay in the carbon emissions into the technosphere.
This case study evaluates a new path for olive pomace-based composites as an alternative eco-material for the building sector, based on environmental criteria. Future works can include the use of biosourced polymer matrices, which could reduce the impact of the production of olive pomace-based composites.

Conflicts of Interest:
The authors declare no conflict of interest.