Green Solid-State Chemical Reduction of Graphene Oxide Supported on a Paper Substrate

: The reduction of graphene oxide (GO) thin ﬁlms deposited on substrates is crucial to achieve a technologically useful supported graphene material. However, the well-known thermal reduction process cannot be used with thermally unstable substrates (e.g., plastics and paper), in addition photo-reduction methods are expensive and only capable of reducing the external surface. Therefore, solid-state chemical reduction techniques could become a convenient approach for the full thickness reduction of the GO layers supported on thermally unstable substrates. Here, a novel experimental procedure for quantitative reduction of GO ﬁlms on paper by a green and low-cost chemical reductant (L-ascorbic acid, L-aa) is proposed. The possibility to have an e ﬀ ective mass transport of the reductant inside the swelled GO solid (gel-phase) deposit was ensured by spraying a reductant solution on the GO ﬁlm and allowing it to reﬂux in a closed microenvironment at 50 ◦ C. The GO conversion degree to reduced graphene oxide (r-GO) was evaluated by Fourier transform infrared spectroscopy (FT-IR) in attenuated total reﬂectance (ATR) mode and X-ray Di ﬀ raction (XRD). In addition, morphology and wettability of GO deposits, before and after reduction, were conﬁrmed by digital USB microscopy, scanning electron microscopy (SEM), and contact angle measurements. According to these structural characterizations, the proposed method allows a bulky reduction of the coating but leaves to a GO layer at the interface, that is essential for a good coating-substrate adhesion and this special characteristic is useful for industrial exploitation of the material.


Introduction
In recent decades, graphene and its derivatives have attracted great interest because of their excellent mechanical, electrical, thermal, and optical properties [1][2][3][4][5]. On this basis, graphite oxide, first reported over 150 years ago [6], has re-emerged with an intense research interest due to its possible role as a precursor for a cost-effective mass-production of graphene-based materials. Reduced graphene oxide (r-GO) has mechanical, electrical, and optical properties quite similar to graphene because it has a slightly heterogeneous structure made of graphene-like planes, decorated by a few oxygen-containing chemical groups. Owing to the graphene-like properties, r-GO is a convenient material for many technological fields (e.g., catalysis, energy-storage, electronics, etc.) [7,8]. Several GO synthesis methods, which are alternatives to the original Hammer's method [9][10][11][12], and new chemical reduction schemes are being proposed [13][14][15][16][17][18][19][20][21][22][23][24][25][26][27]. The GO conversion to r-GO usually requires some reducing agents or a high temperature [13][14][15][16][17][18]. Among these reduction strategies, the chemical approach is very promising for bulk production of r-GO at low cost. Unfortunately, most of the widely used chemical reductants such as hydrazine or hydrazine hydrate are highly toxic and/or explosive, which can potentially induce environmental and safety risks [19]. Moreover, the chemical reduction process of GO usually occurs under liquid-phase conditions by dissolving reducing agent and GO in

Materials and Methods
GO was synthesized by a modified Hummers' method [11,27], that was based on the oxidation of graphite nanoplatelets (GNP) by KMnO 4 (≥99%) and KNO 3 (≥99%) solution in absolute H 2 SO 4 and after ca. 1 h the reaction was stopped by adding H 2 O 2 (30%). The raw reaction product was repeatedly washed by distilled water. All reactants were provided by Sigma-Aldrich. Then, the concentrated aqueous solution of GO was cast onto a paper substrate and this system was allowed to dry in air at room temperature. A Whatman ® quantitative filter grade paper, 42 circles, diameter 42.5 mm, was selected as substrate.
The GO supported on paper was placed inside a closed Petri dish (Pyrex), and thermostated at a temperature of 50 • C by using a hot plate. The sample was periodically sprayed by L-ascorbic acid (L-aa, Sigma-Aldrich, St. Louis, MO, USA, 99%) aqueous solution to reduce GO (see Figure 1). Such treatment lasted for ca. 48 h. In these experimental conditions, an effective mass-transport diffusion of the L-aa reductant was possible inside the GO layer swelled by water. To remove all possible reduction by-products, at the end of treatment, the samples were washed by spraying distilled water on them. The surface of samples was analyzed by digital USB-microscope (Dino-lite). In order to establish the time required for a complete reduction, the GO supported on paper samples were characterized by FT-IR spectroscopy, before and after the reduction treatment. FT-IR spectra were recorded in ATR mode in the 4000-700 cm −1 range by using a spectrophotometer (PerkinElmer Frontier NIR, Milan, Italy).
The paper substrate and GO supported on paper samples, before and after the reduction treatment, were structurally characterized by XRD (PANalytical-X'PERT PRO diffractometer, with CuKα radiation (λ = 0.154 nm)) in the range of 2θ = 5°-60°, scan step = 0.0130°, and full scan time = 18.9 s.
The surface and the cross-sections morphologies of the coating layer were visualized by a SEM (FEI Quanta 200 FEG, Hillsboro, OR, USA) equipped with an energy dispersive X-Ray (EDS) microanalyzer (Inca Oxford 250, High Wycombe, UK). Cross-sections were obtained by cutting the system with a scalpel.
The surface wettability of GO supported on paper, before and after the reduction treatment, was evaluated by contact angle measurements. In particular, the sessile drop method, that considers the shape of the small liquid test drop to be a truncated sphere, was used. The sessile drop contact angles were measured by a Dataphysics mod. OCA 20, using 1 μL as volume sampling. Each measurement was repeated ten times at room temperature and the achieved contact angle values were statistically treated.
The chemical structures have been drawn by ACD/ChemSketch Freeware Software, version 2019.2.1, Advanced Chemistry Development, Inc., Toronto, ON, Canada, www.acdlabs.com. Figure 2 shows the images of a typical sample made of GO supported on paper, before and after the treatment with L-aa aqueous solution. As visible, the GO uniformly covers the surface of the paper substrate and its color changes from a light-brown (see Figure 2a) to black (see Figure 2b), as a consequence of the chemical reduction, thus proving that the GO has been converted to reduced graphene oxide (r-GO). The very uniform black color distribution in the coating layer suggests a complete chemical reduction of the GO into the r-GO. In addition, the coating does not show any defect (e.g., cracks, fractures, pores, etc.) and does not evidence any de-bonding of the substrate, before and after the chemical treatment. Further, the paper substrate was not modified by contacting the acid.  The surface of samples was analyzed by digital USB-microscope (Dino-lite). In order to establish the time required for a complete reduction, the GO supported on paper samples were characterized by FT-IR spectroscopy, before and after the reduction treatment. FT-IR spectra were recorded in ATR mode in the 4000-700 cm −1 range by using a spectrophotometer (PerkinElmer Frontier NIR, Milan, Italy).

Results and Discussion
The paper substrate and GO supported on paper samples, before and after the reduction treatment, were structurally characterized by XRD (PANalytical-X'PERT PRO diffractometer, with CuKα radiation (λ = 0.154 nm)) in the range of 2θ = 5 • -60 • , scan step = 0.0130 • , and full scan time = 18.9 s.
The surface and the cross-sections morphologies of the coating layer were visualized by a SEM (FEI Quanta 200 FEG, Hillsboro, OR, USA) equipped with an energy dispersive X-Ray (EDS) microanalyzer (Inca Oxford 250, High Wycombe, UK). Cross-sections were obtained by cutting the system with a scalpel.
The surface wettability of GO supported on paper, before and after the reduction treatment, was evaluated by contact angle measurements. In particular, the sessile drop method, that considers the shape of the small liquid test drop to be a truncated sphere, was used. The sessile drop contact angles were measured by a Dataphysics mod. OCA 20, using 1 µL as volume sampling. Each measurement was repeated ten times at room temperature and the achieved contact angle values were statistically treated.
The chemical structures have been drawn by ACD/ChemSketch Freeware Software, version 2019.2.1, Advanced Chemistry Development, Inc., Toronto, ON, Canada, www.acdlabs.com. Figure 2 shows the images of a typical sample made of GO supported on paper, before and after the treatment with L-aa aqueous solution. As visible, the GO uniformly covers the surface of the paper substrate and its color changes from a light-brown (see Figure 2a) to black (see Figure 2b), as a consequence of the chemical reduction, thus proving that the GO has been converted to reduced graphene oxide (r-GO). The very uniform black color distribution in the coating layer suggests a complete chemical reduction of the GO into the r-GO. In addition, the coating does not show any defect (e.g., cracks, fractures, pores, etc.) and does not evidence any de-bonding of the substrate, before and after the chemical treatment. Further, the paper substrate was not modified by contacting the acid. The surface of samples was analyzed by digital USB-microscope (Dino-lite). In order to establish the time required for a complete reduction, the GO supported on paper samples were characterized by FT-IR spectroscopy, before and after the reduction treatment. FT-IR spectra were recorded in ATR mode in the 4000-700 cm −1 range by using a spectrophotometer (PerkinElmer Frontier NIR, Milan, Italy).

Results and Discussion
The paper substrate and GO supported on paper samples, before and after the reduction treatment, were structurally characterized by XRD (PANalytical-X'PERT PRO diffractometer, with CuKα radiation (λ = 0.154 nm)) in the range of 2θ = 5°-60°, scan step = 0.0130°, and full scan time = 18.9 s.
The surface and the cross-sections morphologies of the coating layer were visualized by a SEM (FEI Quanta 200 FEG, Hillsboro, OR, USA) equipped with an energy dispersive X-Ray (EDS) microanalyzer (Inca Oxford 250, High Wycombe, UK). Cross-sections were obtained by cutting the system with a scalpel.
The surface wettability of GO supported on paper, before and after the reduction treatment, was evaluated by contact angle measurements. In particular, the sessile drop method, that considers the shape of the small liquid test drop to be a truncated sphere, was used. The sessile drop contact angles were measured by a Dataphysics mod. OCA 20, using 1 μL as volume sampling. Each measurement was repeated ten times at room temperature and the achieved contact angle values were statistically treated.
The chemical structures have been drawn by ACD/ChemSketch Freeware Software, version 2019.2.1, Advanced Chemistry Development, Inc., Toronto, ON, Canada, www.acdlabs.com. Figure 2 shows the images of a typical sample made of GO supported on paper, before and after the treatment with L-aa aqueous solution. As visible, the GO uniformly covers the surface of the paper substrate and its color changes from a light-brown (see Figure 2a) to black (see Figure 2b), as a consequence of the chemical reduction, thus proving that the GO has been converted to reduced graphene oxide (r-GO). The very uniform black color distribution in the coating layer suggests a complete chemical reduction of the GO into the r-GO. In addition, the coating does not show any defect (e.g., cracks, fractures, pores, etc.) and does not evidence any de-bonding of the substrate, before and after the chemical treatment. Further, the paper substrate was not modified by contacting the acid.  The coating surface morphology, before and after chemical reduction, was investigated by digital USB-microscopy. This type of microscopy is very sensible to the sample reflectivity because the observation takes place under reflected light. As visible in Figure 3, the reflectivity of the two samples significantly differs: the GO sample in Figure 2a does not reflect light and appears mostly brown, differently the r-GO sample in Figure 2b has a much higher reflectivity and includes even silvery areas. It is well known that graphite, similarly to the metals, has a glossy appearance, as a consequence also r-GO resembles graphite and have a mirror-like aspect. The higher reflectivity of the r-GO surface allows to better evidence the presence of an open porosity in the coating layer (dark areas uniformly distributed in the silvery phase).

Results and Discussion
Coatings 2020, 10, x FOR PEER REVIEW 4 of 13 The coating surface morphology, before and after chemical reduction, was investigated by digital USB-microscopy. This type of microscopy is very sensible to the sample reflectivity because the observation takes place under reflected light. As visible in Figure 3, the reflectivity of the two samples significantly differs: the GO sample in Figure 2a does not reflect light and appears mostly brown, differently the r-GO sample in Figure 2b has a much higher reflectivity and includes even silvery areas. It is well known that graphite, similarly to the metals, has a glossy appearance, as a consequence also r-GO resembles graphite and have a mirror-like aspect. The higher reflectivity of the r-GO surface allows to better evidence the presence of an open porosity in the coating layer (dark areas uniformly distributed in the silvery phase).  Figure 4 shows the FT-IR spectra in ATR mode of paper substrate (green line), GO before (black line), and after (red line) the treatment with L-aa aqueous solution. The spectrum of paper (green line) shows peaks in the range of 3700-3000 cm −1 that can be referred to the resonance vibration of hydroxyl groups (-OH), a peak at ca. 2700 cm −1 that is due to the C-H stretching vibration, and other peaks in the range of 1500-900 cm −1 which could be due a C-O functional groups. As visible, the GO spectrum includes six main peaks that can be attributed to the resonance vibrations of: (i) the oxygencontaining groups and (ii) the carbon skeleton. In particular, the very strong and broad peak at 3171 cm −1 can be referred to the resonance vibration of hydroxyl groups (-OH), the peak at 1735 cm −1 to the resonance vibration of carbonyl groups (C=O), the peak at 1227 cm −1 to the alloy groups (C-O-H) and the peak at 1061 cm −1 to the epoxide groups (C-O-C). In addition, the stretching absorption of C=C groups is also clearly visible in the spectrum at 1621 cm −1 , and the band centered at 2840 cm −1 is due to the C-H stretching vibration [44]. The spectrum of GO after the chemical reduction (red line in Figure 4) shows a decrease of absorption band number and intensities, thus confirming the formation of r-GO by the removal of most oxygen-containing functional groups. In particular, the C-O stretching resonance completely disappears, and the C=C stretching vibration slightly attenuates and shifts from 1621 to 1590 cm −1 ,  Figure 4 shows the FT-IR spectra in ATR mode of paper substrate (green line), GO before (black line), and after (red line) the treatment with L-aa aqueous solution. The spectrum of paper (green line) shows peaks in the range of 3700-3000 cm −1 that can be referred to the resonance vibration of hydroxyl groups (-OH), a peak at ca. 2700 cm −1 that is due to the C-H stretching vibration, and other peaks in the range of 1500-900 cm −1 which could be due a C-O functional groups. As visible, the GO spectrum includes six main peaks that can be attributed to the resonance vibrations of: (i) the oxygen-containing groups and (ii) the carbon skeleton. In particular, the very strong and broad peak at 3171 cm −1 can be referred to the resonance vibration of hydroxyl groups (-OH), the peak at 1735 cm −1 to the resonance vibration of carbonyl groups (C=O), the peak at 1227 cm −1 to the alloy groups (C-O-H) and the peak at 1061 cm −1 to the epoxide groups (C-O-C). In addition, the stretching absorption of C=C groups is also clearly visible in the spectrum at 1621 cm −1 , and the band centered at 2840 cm −1 is due to the C-H stretching vibration [44].
Coatings 2020, 10, x FOR PEER REVIEW 4 of 13 The coating surface morphology, before and after chemical reduction, was investigated by digital USB-microscopy. This type of microscopy is very sensible to the sample reflectivity because the observation takes place under reflected light. As visible in Figure 3, the reflectivity of the two samples significantly differs: the GO sample in Figure 2a does not reflect light and appears mostly brown, differently the r-GO sample in Figure 2b has a much higher reflectivity and includes even silvery areas. It is well known that graphite, similarly to the metals, has a glossy appearance, as a consequence also r-GO resembles graphite and have a mirror-like aspect. The higher reflectivity of the r-GO surface allows to better evidence the presence of an open porosity in the coating layer (dark areas uniformly distributed in the silvery phase).  Figure 4 shows the FT-IR spectra in ATR mode of paper substrate (green line), GO before (black line), and after (red line) the treatment with L-aa aqueous solution. The spectrum of paper (green line) shows peaks in the range of 3700-3000 cm −1 that can be referred to the resonance vibration of hydroxyl groups (-OH), a peak at ca. 2700 cm −1 that is due to the C-H stretching vibration, and other peaks in the range of 1500-900 cm −1 which could be due a C-O functional groups. As visible, the GO spectrum includes six main peaks that can be attributed to the resonance vibrations of: (i) the oxygencontaining groups and (ii) the carbon skeleton. In particular, the very strong and broad peak at 3171 cm −1 can be referred to the resonance vibration of hydroxyl groups (-OH), the peak at 1735 cm −1 to the resonance vibration of carbonyl groups (C=O), the peak at 1227 cm −1 to the alloy groups (C-O-H) and the peak at 1061 cm −1 to the epoxide groups (C-O-C). In addition, the stretching absorption of C=C groups is also clearly visible in the spectrum at 1621 cm −1 , and the band centered at 2840 cm −1 is due to the C-H stretching vibration [44]. The spectrum of GO after the chemical reduction (red line in Figure 4) shows a decrease of absorption band number and intensities, thus confirming the formation of r-GO by the removal of most oxygen-containing functional groups. In particular, the C-O stretching resonance completely disappears, and the C=C stretching vibration slightly attenuates and shifts from 1621 to 1590 cm −1 , The spectrum of GO after the chemical reduction (red line in Figure 4) shows a decrease of absorption band number and intensities, thus confirming the formation of r-GO by the removal of most oxygen-containing functional groups. In particular, the C-O stretching resonance completely disappears, and the C=C stretching vibration slightly attenuates and shifts from 1621 to 1590 cm −1 , because of the conjugation extension in the graphene plane [44]. The Optimized 3-D images of GO and r-GO are available in the Supplementary Information in Figure S1. Figure 5 shows XRD diffractograms of: pristine paper substrate, GO, and r-GO supported on paper. The paper substrate has the typical semi-crystalline cellulose diffraction pattern (see Figure 5a), which includes diffraction peaks at 2θ values of: 14.7 • , 16.8 • , and 22.7 • , corresponding respectively to the 110 , (110), and (200) crystallographic planes of type I monolithic cellulose (PDF files: 000561717, 000561718, and 000561719) [34]. The XRD patterns of GO and r-GO supported on paper are shown in Figure 5b,c. As visible in Figure 5b, the untreated GO deposit XRD diffractogram includes, in addition to the paper substrate XRD pattern, the presence of a peak at 2θ = 10.62 • , referred to the GO (002) plane [14]. The XRD diffractogram of r-GO deposit, shown in Figure 5c, includes, in addition to the paper substrate pattern, a peak of low intensity at 2θ = 11.53 • , referred to the GO (002) plane, and two peaks at 25.39 • and 43.02 • , belonging to r-GO [14]. Other peaks present in the XRD diffractogram can be referred to the presence of inorganic/organic crystalline solid phases (i.e., residual L-aa, calcium salts, etc.) present in the sample at an impurity level. As known, the d-spacing of the GO is higher than the corresponding value of graphite, because of the presence of oxygen-containing functional groups attached on both sheet sides, and of the atomic-scale roughness, arising from structural defects (e.g., sp 3 carbon atoms). It is possible to evaluate this d-spacing by the Bragg's law [45][46][47]: where λ is the wavelength of the X-ray (Cu-K α1 = 1.5481 Å), θ is half of the corresponding scattering angle, n is an integer number, representing the diffraction peak order, d is the inter-plane distance of the lattice, and (hkl) are the Miller's indices. According to Equation (1), such increased value of the d-spacing, calculated by a GO peak analysis, results: d (002) = 8.32 Å for the untreated GO deposit, while it results 7.67 Å, after the chemical treatment (see Table 1). The calculated d-spacing values were more than twice compared to that of pristine graphite (d (002) = 3.54 Å), thus confirming the expansion of graphitic stack during oxidation. Moreover, Scherrer's equation can be used to obtain the average crystal thickness, i.e., the size perpendicular to the (002) plane (2θ = 10.62 • for GO and 2θ = 25.39 • for r-GO) and the in-plane crystallite average size that can be expressed in terms of in-plane periodicity peak (2θ = 43.02 • for the (100) plane) [30][31][32] as follows: where FWHM is the full-width-at-half-maximum in radians obtained by a Gaussian fit of the peak, K is a constant depending on the crystallite shape, and it is taken as 0.89 to evaluate the average in-plane thickness (i.e., L (002) ), and 1.84, to evaluate the in-plane size (i.e., L (100) ) [47].  Figure 5. X-ray Diffraction (XRD) diffractogram of the paper substrate (a) and GO supported on paper before (b) and after (c) the treatment with L-aa aqueous solution. The inset in Figure 4c represents a magnification of the r-GO peak (100).
The average number of the graphene layers (n) per crystalline domain can be calculate from the XRD peak broadening by using a combination of Scherrer's and Bragg's equations, that provides the following expression: n = (L(002)/d) + 1 (3) Table 1 summarizes the results of these calculations for the system before and after chemical treatment. The (002) peak area of the GO is significantly reduced (68% of the initial area), the average thickness of the GO crystallites before chemical reduction resulted 11.72 nm, while the same thickness was 19.95 nm after the chemical treatment. A thickness value of 27.21 nm was found by analyzing the r-GO peak at 2θ = 25.39.
The morphologies of the paper substrate and the GO supported on paper, before and after the chemical reduction, were investigated by SEM, as shown in Figure 6. As visible in the two micrographs showing the substrate microstructure at different magnifications (Figure 6a,b), the substrate was made of compacted cellulose microfibers having a diameter in the 20-50 μm range. Several pores, with a size of ca. 2.5 μm, were uniformly distributed on the substrate surface. After coating the paper substrate by GO and drying this system in air, according to the SEM-micrographs shown in Figure 6c,d, a continuous and uniform coverage of both the cellulose fibers and pores by a thin GO layer was obtained. Obviously, the observed roughness in the GO surface has to be ascribed to the substrate fibrous morphology that is perfectly reproduced because of the conformational flexibility of GO chemical structure for the presence of the sp 3 -hybridized carbon atoms. Owing to the chemical affinity between the GO layer and the cellulose fibers, related to the presence of hydroxyl groups in both solid phases, a strong interfacial adhesion (i.e., absence of peeling off in the GO coating layer), with complete filling of the pores, was possible. As visible in Figure 6e,f, the coating The average number of the graphene layers (n) per crystalline domain can be calculate from the XRD peak broadening by using a combination of Scherrer's and Bragg's equations, that provides the following expression: n = (L (002) /d) + 1 (3) Table 1 summarizes the results of these calculations for the system before and after chemical treatment. The (002) peak area of the GO is significantly reduced (68% of the initial area), the average thickness of the GO crystallites before chemical reduction resulted 11.72 nm, while the same thickness was 19.95 nm after the chemical treatment. A thickness value of 27.21 nm was found by analyzing the r-GO peak at 2θ = 25.39.
The morphologies of the paper substrate and the GO supported on paper, before and after the chemical reduction, were investigated by SEM, as shown in Figure 6. As visible in the two micrographs showing the substrate microstructure at different magnifications (Figure 6a,b), the substrate was made of compacted cellulose microfibers having a diameter in the 20-50 µm range. Several pores, with a size of ca. 2.5 µm, were uniformly distributed on the substrate surface. After coating the paper substrate by GO and drying this system in air, according to the SEM-micrographs shown in Figure 6c,d, a continuous and uniform coverage of both the cellulose fibers and pores by a thin GO layer was obtained. Obviously, the observed roughness in the GO surface has to be ascribed to the substrate fibrous morphology that is perfectly reproduced because of the conformational flexibility of GO chemical structure for the presence of the sp 3 -hybridized carbon atoms. Owing to the chemical affinity between the GO layer and the cellulose fibers, related to the presence of hydroxyl groups in both solid phases, a strong interfacial adhesion (i.e., absence of peeling off in the GO coating layer), with complete filling of the pores, was possible. As visible in Figure 6e,f, the coating morphology slightly changed after the chemical reduction treatment, indeed the surface roughness reduced significantly, and all deep grooves and folds are not visible anymore because of the increased stiffness of the graphene coating layer, which consist manly sp 2 -hybridized carbon atoms. Such a lower roughness of the sample surface that follows to the chemical treatment proves a complete conversion of GO sheets to r-GO, near the coating top.
Coatings 2020, 10, x FOR PEER REVIEW 7 of 13 morphology slightly changed after the chemical reduction treatment, indeed the surface roughness reduced significantly, and all deep grooves and folds are not visible anymore because of the increased stiffness of the graphene coating layer, which consist manly sp 2 -hybridized carbon atoms. Such a lower roughness of the sample surface that follows to the chemical treatment proves a complete conversion of GO sheets to r-GO, near the coating top. A further SEM investigation was carried out on the cross-section of the GO and r-GO supported on paper samples (see Figure 7). According to these images, the GO and r-GO solid phases do not permeate the substrate fibrous structure. Figure 7a,b shows that the thickness of the paper substrate was ca. 120 μm, while the average thickness of GO layer was ca. 3 μm. As visible in Figure 6b, the coating layer appeared as quite compact and cavities or other defects were not present in this layer. In addition, a good interfacial adhesion resulted between the GO substrate and the fibrous coating. The SEM micrographs of the r-GO sample shown in Figure 7c,d suggests the formation of air cavities inside the layer as a consequence of the reduction treatment, and the layer thickness became ca. 50 μm. Probably, such cavities have been produced by the formation of gaseous by-products (mostly H2O) during the reduction process.
In order to establish the coating layer purity an EDS analysis of the sample, before and after the chemical reduction treatment, has been performed. The EDS spectrum of both GO and r-GO sample is shown in Figure 8. According to this EDS characterization, sulfur impurities (0.75%) and a little amount of silicon (0.20%) were present in the GO coating. However, such impurities completely disappear after the reduction treatment. Owing to the presence of a cellulose substrate, C and O signals remain mostly unchanged by the reduction treatment. A further SEM investigation was carried out on the cross-section of the GO and r-GO supported on paper samples (see Figure 7). According to these images, the GO and r-GO solid phases do not permeate the substrate fibrous structure. Figure 7a,b shows that the thickness of the paper substrate was ca. 120 µm, while the average thickness of GO layer was ca. 3 µm. As visible in Figure 6b, the coating layer appeared as quite compact and cavities or other defects were not present in this layer. In addition, a good interfacial adhesion resulted between the GO substrate and the fibrous coating. The SEM micrographs of the r-GO sample shown in Figure 7c,d suggests the formation of air cavities inside the layer as a consequence of the reduction treatment, and the layer thickness became ca. 50 µm. Probably, such cavities have been produced by the formation of gaseous by-products (mostly H 2 O) during the reduction process.  The variation of the GO coating wettability, as a consequence of the chemical reduction, was quantified by measuring the contact angle of this layer before and after treatment. The "sessile drop method" was used according to the literature [48]; this method considers the shape of the small water test drop as a truncated sphere and measures the angle between the surface of the liquid and the outline of contact surface by image analysis. An example the achieved values of the contact angle are given in Figure 9. The average contact angle value for a pristine GO layer is 53° ± 1.1°, however, it is possible to observe that the values on the two drop sides are not exactly equal, for example in Figure  9a, on the left side, the average value was 52.6°, while on the right side it was 55.8° and such a discrepancy is related to the high roughness that characterizes the layer surface. This low value of the contact angle confirms the high wettability (hydrophilic nature) of the GO coating. Differently, the average contact angle of a water drop located on the r-GO layer shows higher average values and precisely ca. 97° ± 1.5° (see Figure 9b), thus confirming the low wettability (hydrophobic nature) of In order to establish the coating layer purity an EDS analysis of the sample, before and after the chemical reduction treatment, has been performed. The EDS spectrum of both GO and r-GO sample is shown in Figure 8. According to this EDS characterization, sulfur impurities (0.75%) and a little amount of silicon (0.20%) were present in the GO coating. However, such impurities completely disappear after the reduction treatment. Owing to the presence of a cellulose substrate, C and O signals remain mostly unchanged by the reduction treatment.  The variation of the GO coating wettability, as a consequence of the chemical reduction, was quantified by measuring the contact angle of this layer before and after treatment. The "sessile drop method" was used according to the literature [48]; this method considers the shape of the small water test drop as a truncated sphere and measures the angle between the surface of the liquid and the outline of contact surface by image analysis. An example the achieved values of the contact angle are given in Figure 9. The average contact angle value for a pristine GO layer is 53° ± 1.1°, however, it is possible to observe that the values on the two drop sides are not exactly equal, for example in Figure  9a, on the left side, the average value was 52.6°, while on the right side it was 55.8° and such a discrepancy is related to the high roughness that characterizes the layer surface. This low value of Figure 8. Energy dispersive X-ray spectra of the GO coating layer on paper substrate before (a) and after (b) the chemical reduction treatment by L-aa (insets give the elemental compositions of the layer).
The variation of the GO coating wettability, as a consequence of the chemical reduction, was quantified by measuring the contact angle of this layer before and after treatment. The "sessile drop method" was used according to the literature [48]; this method considers the shape of the small water test drop as a truncated sphere and measures the angle between the surface of the liquid and the outline of contact surface by image analysis. An example the achieved values of the contact angle are given in Figure 9. The average contact angle value for a pristine GO layer is 53 • ± 1.1 • , however, it is possible to observe that the values on the two drop sides are not exactly equal, for example in Figure 9a, on the left side, the average value was 52.6 • , while on the right side it was 55.8 • and such a discrepancy is related to the high roughness that characterizes the layer surface. This low value of the contact angle confirms the high wettability (hydrophilic nature) of the GO coating. Differently, the average contact angle of a water drop located on the r-GO layer shows higher average values and precisely ca. 97 • ± 1.5 • (see Figure 9b), thus confirming the low wettability (hydrophobic nature) of the same layer after chemical reduction. This significant increase in the contact angle as a consequence of the chemical treatment shows the efficiency of the proposed method in the removal of most oxygen-containing groups from the GO surface [49].
Coatings 2020, 10, x FOR PEER REVIEW 9 of 13 the same layer after chemical reduction. This significant increase in the contact angle as a consequence of the chemical treatment shows the efficiency of the proposed method in the removal of most oxygen-containing groups from the GO surface [49]. Finally, this chemical technique is based on the possibility to convert the solid GO phase in an aqueous gel, where molecular transport by diffusion easily takes place exposing this hydrophilic substance to water vapor [50]. In particular, the hydrophilic surface of the GO sheets is easily solvated by water molecules that also accumulate at inter-layer, thus generating a continuous liquid phase interpenetrating the GO layers. The use of a temperature close to 50 °C allows a fast diffusion of the L-aa reductant molecules, periodically distributed by spraying a L-aa aqueous solution on the GO layer surface, inside the gel-phase. The mild temperature, selected for the experimental process, allowed to favor the L-aa molecule migration inside the gel-phase, without causing an early thermal degradation of the reductant. The schematic representation of the involved diffusion path is summarized in Figure 10. This process also allowed a solid-state removal of different by-products (e.g., dehydroascorbic acid) by spraying water on the produced r-GO layer. Concerning the chemical mechanism taking place in the gel-phase during GO reduction, the investigated system should approximately behave as reported in the literature for the reduction of single GO units dispersed in liquid-phase [51,52]. Owing to the slow diffusion rate of L-aa molecules, which always characterizes a gel-phase reduction, a lower value for the reaction rate is expected. Actually, the exact mechanism of the chemical reaction between GO and L-aa is not completely clear, but two different reactions should be involved in the interaction between L-aa and GO epoxy groups or L-aa and GO vicinal-hydroxyl groups. The reaction pathway is schematically indicated in Figure  11 (3-D images were not energetically optimized). As visible, both reactions require the formation of a good leaving group, which is a hydroxyl group, in the case of epoxies, and a water molecule, in the case of vicinal-hydroxyl groups. These types of leaving group are generated by protonation of the cited GO reactive groups. In particular, the electron withdrawing from five-membered ring of L-aa makes its hydroxyls more acidic, consequently the L-aa is ready to dissociate two protons, that are Finally, this chemical technique is based on the possibility to convert the solid GO phase in an aqueous gel, where molecular transport by diffusion easily takes place exposing this hydrophilic substance to water vapor [50]. In particular, the hydrophilic surface of the GO sheets is easily solvated by water molecules that also accumulate at inter-layer, thus generating a continuous liquid phase interpenetrating the GO layers. The use of a temperature close to 50 • C allows a fast diffusion of the L-aa reductant molecules, periodically distributed by spraying a L-aa aqueous solution on the GO layer surface, inside the gel-phase. The mild temperature, selected for the experimental process, allowed to favor the L-aa molecule migration inside the gel-phase, without causing an early thermal degradation of the reductant. The schematic representation of the involved diffusion path is summarized in Figure 10. This process also allowed a solid-state removal of different by-products (e.g., dehydroascorbic acid) by spraying water on the produced r-GO layer.
Coatings 2020, 10, x FOR PEER REVIEW 9 of 13 the same layer after chemical reduction. This significant increase in the contact angle as a consequence of the chemical treatment shows the efficiency of the proposed method in the removal of most oxygen-containing groups from the GO surface [49]. Finally, this chemical technique is based on the possibility to convert the solid GO phase in an aqueous gel, where molecular transport by diffusion easily takes place exposing this hydrophilic substance to water vapor [50]. In particular, the hydrophilic surface of the GO sheets is easily solvated by water molecules that also accumulate at inter-layer, thus generating a continuous liquid phase interpenetrating the GO layers. The use of a temperature close to 50 °C allows a fast diffusion of the L-aa reductant molecules, periodically distributed by spraying a L-aa aqueous solution on the GO layer surface, inside the gel-phase. The mild temperature, selected for the experimental process, allowed to favor the L-aa molecule migration inside the gel-phase, without causing an early thermal degradation of the reductant. The schematic representation of the involved diffusion path is summarized in Figure 10. This process also allowed a solid-state removal of different by-products (e.g., dehydroascorbic acid) by spraying water on the produced r-GO layer. Concerning the chemical mechanism taking place in the gel-phase during GO reduction, the investigated system should approximately behave as reported in the literature for the reduction of single GO units dispersed in liquid-phase [51,52]. Owing to the slow diffusion rate of L-aa molecules, which always characterizes a gel-phase reduction, a lower value for the reaction rate is expected. Actually, the exact mechanism of the chemical reaction between GO and L-aa is not completely clear, but two different reactions should be involved in the interaction between L-aa and GO epoxy groups or L-aa and GO vicinal-hydroxyl groups. The reaction pathway is schematically indicated in Figure  11 (3-D images were not energetically optimized). As visible, both reactions require the formation of a good leaving group, which is a hydroxyl group, in the case of epoxies, and a water molecule, in the case of vicinal-hydroxyl groups. These types of leaving group are generated by protonation of the cited GO reactive groups. In particular, the electron withdrawing from five-membered ring of L-aa makes its hydroxyls more acidic, consequently the L-aa is ready to dissociate two protons, that are transferred to GO, thus generating the nucleophilic species (the oxyanion of L-aa, C6H7O6 − ). After this Concerning the chemical mechanism taking place in the gel-phase during GO reduction, the investigated system should approximately behave as reported in the literature for the reduction of single GO units dispersed in liquid-phase [51,52]. Owing to the slow diffusion rate of L-aa molecules, which always characterizes a gel-phase reduction, a lower value for the reaction rate is expected. Actually, the exact mechanism of the chemical reaction between GO and L-aa is not completely clear, but two different reactions should be involved in the interaction between L-aa and GO epoxy groups or L-aa and GO vicinal-hydroxyl groups. The reaction pathway is schematically indicated in Figure 11 (3-D images were not energetically optimized). As visible, both reactions require the formation of a good leaving group, which is a hydroxyl group, in the case of epoxies, and a water molecule, in the case of vicinal-hydroxyl groups. These types of leaving group are generated by protonation of the cited GO reactive groups. In particular, the electron withdrawing from five-membered ring of L-aa makes its hydroxyls more acidic, consequently the L-aa is ready to dissociate two protons, that are transferred to GO, thus generating the nucleophilic species (the oxyanion of L-aa, C 6 H 7 O 6 − ). After this preliminary acid-base reaction, an SN2 step follows. In this SN2 step, the nucleophilic agent attacks the sp 2 -carbon of the epoxy group or the Sp 3 -carbon of the alcoholic groups, and hydroxyl or water results as by-product, respectively. In the case of the reaction involving epoxy, a further condensation by SN2 mechanism follows. Then, this intermediate undergoes a thermally induced redox reaction, that leads to formation of reduced graphene (r-GO) and dehydroascorbic acid [51,52]. Optimized 3-D images of different reaction intermediate and some more structural information about the kinetic mechanism are available in the Supplementary Information in Figure S2.
Coatings 2020, 10, x FOR PEER REVIEW 10 of 13 by SN2 mechanism follows. Then, this intermediate undergoes a thermally induced redox reaction, that leads to formation of reduced graphene (r-GO) and dehydroascorbic acid [51,52]. Optimized 3-D images of different reaction intermediate and some more structural information about the kinetic mechanism are available in the Supplementary Information in Figure S2.

Conclusions
The possibility to reduce thin GO deposits on paper substrate by a non-toxic, eco-friendly, and low-cost chemical reductant, like L-aa aqueous solution, has been investigated and according to the achieved results, a uniform and bulky layer of highly reduced r-GO can be obtained. This process requires to reflux the L-aa aqueous solution in presence of the GO deposit in a closed microenvironment for 48 h at a temperature of ca. 50 °C. In these experimental conditions, GO forms a gel-phase where the reductant diffusion can easily take place. According to the SEM investigation, a structural modification of coating surface follows to the chemical reduction treatment, mainly consisting in an increase of the coating flatness. According to the infrared spectroscopy (FT-IR) most of the oxygen-containing groups present in the GO layer were removed, thus determining a significant variation of the wettability of the material, that changes from hydrophilic (contact angle: 53°) to hydrophobic (contact angle: 97°). The XRD results show the presence of the main peaks of the r-GO pattern combined with signals of residual GO, thus confirming the spectroscopic results concerning r-GO formation in presence of a very thin residual GO layer at the interface with paper. In particular, the obtained r-GO coating is composed of graphite platelets, with the average thickness of ca. 27 nm and a width of ca. 40 nm, which are aligned parallel to the interfacial plane and show

Conclusions
The possibility to reduce thin GO deposits on paper substrate by a non-toxic, eco-friendly, and low-cost chemical reductant, like L-aa aqueous solution, has been investigated and according to the achieved results, a uniform and bulky layer of highly reduced r-GO can be obtained. This process requires to reflux the L-aa aqueous solution in presence of the GO deposit in a closed microenvironment for 48 h at a temperature of ca. 50 • C. In these experimental conditions, GO forms a gel-phase where the reductant diffusion can easily take place. According to the SEM investigation, a structural modification of coating surface follows to the chemical reduction treatment, mainly consisting in an increase of the coating flatness. According to the infrared spectroscopy (FT-IR) most of the oxygen-containing groups present in the GO layer were removed, thus determining a significant variation of the wettability of the material, that changes from hydrophilic (contact angle: 53 • ) to hydrophobic (contact angle: 97 • ). The XRD results show the presence of the main peaks of the r-GO pattern combined with signals of residual GO, thus confirming the spectroscopic results concerning r-GO formation in presence of a very thin residual GO layer at the interface with paper. In particular, the obtained r-GO coating is composed of graphite platelets, with the average thickness of ca. 27 nm and a width of ca. 40 nm, which are aligned parallel to the interfacial plane and show good graphitic quality. This structural characteristic is relevant to achieve a high flexible r-GO layer, supported on paper substrate because of the excellent GO-paper interface adhesion, which is strictly necessary for an industrial exploitation of this system.

Supplementary Materials:
The following are available online at http://www.mdpi.com/2079-6412/10/7/693/s1, Figure S1: Optimized 3-D images of GO and r-GO. Figure S2: Optimized 3-D images of different reaction intermediate and some more structural information about the kinetic mechanism.