Synthesis of Polypyrrole / V 2 O 5 Composite Film on the Surface of Magnesium Using a Mild Vapor Phase Polymerization (VPP) Method for Corrosion Resistance

: The vapor phase polymerization (VPP) method is a conventional strategy for synthesizing conducting polymers (CPs) on the surfaces of various materials. However, the current VPP method performed on a metal surface usually requires harsh reaction conditions, such as high temperature and low vacuum. In this paper, a polypyrrole (PPy) and vanadium pentoxide (V 2 O 5 ) composite ﬁlm was synthesized on the surface of Mg using a mild VPP method. Here, V 2 O 5 was used as an oxidant, and it was found that the oxidation of pyrrole (Py) vapor on the surface of V 2 O 5 , which had been previously coated on the surface of Mg, could be performed at room temperature under normal atmospheric pressure. The formation of the PPy / V 2 O 5 composite was veriﬁed by Fourier transform infrared spectroscopy (FTIR) and energy dispersive X-ray (EDX) spectroscopy. A thermogravimetric analyzer (TGA) was used to study the thermal stability of the composite. Subsequent corrosion tests showed that the PPy / V 2 O 5 composite ﬁlm could slow down the corrosion of Mg in 3.5 wt% NaCl. It is expected that the mild VPP method may ﬁnd great potential in the ﬁelds of synthesis of CPs and the corrosion protection of reactive metals. , where the two positive peaks in the intermediate frequency region gradually divide into three positive peaks from 0.5 to 96 h. The third peak appeared at 72 h. The presence of such conductive behavior in the intermediate region suggests that the ﬁlm has corrosion protection for the substrate. As time prolonged (after 72 h), the position of the positive peak changed, indicating the degradation of the ﬁlm and new chemical reaction. A similar Bode-phase plots characteristic was found in the PPy / V 2 O 5 composite ﬁlm sample. The impedance of the composite ﬁlm is higher and more stable than those of the previous two samples (bare Mg and V 2 O 5 ). This conductive behavior indicates an improved anticorrosion protection from the PPy ﬁlm. All results show that the PPy / V 2 O 5 composite ﬁlm possesses the best anticorrosion ability.


Introduction
Metals are of industrial interest as structural material due to their high density and high strength to weight ratio. However, their poor corrosion resistance limits their applications. Metal anticorrosion is a process of inhibiting corrosion through physical and chemical means, which is of great significance for many aspects, such as industrial production and biomedical materials. In the last two decades, with the development of metal chemistry, alloying effects, and the electrochemical and polymer field, research has produced many options for the improvement of the corrosion resistance of metals, such as electrochemistry [1,2], chemical coatings [3], electroplating [4], and chemical oxidation anticorrosion [5]. Among them, coating technology is a very common method. Anticorrosive coatings include organic polymers [6], metal oxide [7], and graphene-containing composites [8]. Among them, conducting polymers (CPs) are one of the most important coating materials due to their electronic conductivity, optical transparency, and mechanical flexibility [9][10][11][12].
However, CPs, particularly those formed from unfunctionalized monomers, are often insoluble or require solvents which are unsafe and costly [13]. Therefore, chemical vapor deposition methods 2 of 11 such as vapor phase polymerization (VPP) have been developed for the synthesis of CPs on a variety of substrate surfaces [14][15][16][17]. The main advantage of these methods is that they require no solvents. VPP is a two-step process. The first step is to precoat the oxidant onto the substrate, usually using a wet chemistry method. The second step is to expose the pretreated sample to monomer vapor in a vacuum chamber [18]. This technique is a useful deposition method for fabricating CPs because of its unique characteristics, including its solvent-free synthesis, uniformity of growth, mechanical flexible film, and industrial scale-up. However, the current VPP method performed on a metal surface usually requires harsh reaction conditions, such as high temperature and low vacuum, and conducting polymer anticorrosive coatings synthesized by the VPP method is mainly performed on the inert metal surface [19][20][21]. To the best of our knowledge, there are no reports on the synthesis of CPs on the surface of reactive metals (such as Mg) using the VPP method.
In this article, we report a mild VPP method for synthesizing CP polypyrrole (PPy) and vanadium pentoxide (V 2 O 5 ) composite films on the surface of reactive metal Mg at room temperature under normal atmospheric pressure. The morphology of PPy-based composite films was characterized by Fourier transform infrared spectroscopy (FTIR), a scanning electron microscope (SEM), and energy dispersive X-ray (EDX) spectroscopy. Nanowires with a diameter of about 50 nm were observed. Thermogravimetric analysis (TGA) was used to study the differences among products synthesized at different temperatures. The conductivity of composite films reached 1.22 S/cm. Eventually, we got acceptable corrosion resistance results from the Mg samples covered by the composite films through an electrochemical test.

Test Materials
Magnesium foil (99.99%) was provided by Hui-Ye Magnesium Marketing Co., Ltd. (Shizuishan, China), which was cut into 15 mm × 15 mm pieces. The sample of Mg foil was polished by silicon carbide papers (800-2000 mesh), cleaned in ethanol for 10 min within the ultrasonic bath; after that, the Mg foil was dried in warm air. Pyrrole (Py) was purchased from Sinopharm Chemical Reagent Co., Ltd. (Shanghai, China), distilled under the protection nitrogen gas, and stored in −20 • C. V 2 O 5 hydrogel having a solid content of 1.2 to 1.8 wt% as reported in the literature [22] was used, and other solvents and reagents were analytically pure level and purchased from Sinopharm Chemical Reagent Co., Ltd. (Shanghai, China).

Synthesis of PPy/V 2 O 5 Film on the Surface of Mg
The preparation of PPy/V 2 O 5 nanostructures on Mg foil was carried out at room temperature in a sealed wide-mouth bottle. The exposed area of Mg is 15 mm × 15 mm. Before transferring the sample, we added a Py monomer into the bottle and kept it sealed for 30 min for forming Py vapor pressure. The V 2 O 5 hydrogel-coated Mg foil was immediately put into the prepared Py atmosphere. After 12 h of polymerization reaction, the Mg foil was taken out and dried at room temperature.

Performance Test
Surface morphological characteristics of all samples were observed by a field emission scanning electron microscope (SEM, SU-70, Hitachi, Tokyo, Japan). The element composition analysis was performed using an energy dispersive X-ray detector (EDX, SU-70, Hitachi, Tokyo, Japan). The composition of the film was characterized by attenuated total reflection-Fourier transform infrared reflection (FTIR, is10, Nicolet, Madison, WI, USA) spectroscopy. The thickness of the deposited film sample was detected by a step height profiler (ST, ET150, Kosaka, Tokyo, Japan). The measured samples were PPy/V 2 O 5 composites on Mg substrates (15 mm × 15 mm). The conductivity is calculated after a two-step experiment. In the first step, the multi position film thickness of five samples was measured by an ET150 step meter (Kosaka, Tokyo, Japan). The path length was 500 µm, and different positions were selected for measurement. The final thickness of one sample was the average of all data. In the second step, the resistances of the five samples were measured by an RTS-9 four-probe conductivity tester (4PT, RTS-9, 4PROBES TECH, Guangzhou, China), and the resistances were measured at different points. Four orders of magnitude of a two-way voltage of 0.01, 0.10, 1.00, and 10.0 mV were applied. Thermogravimetric analysis (TGA) was carried out on the SDT Q600 thermogravimetric analyzer (TA Instruments, New Castle, DE, USA) with a heating rate of 20 • C/min in the oxygen condition. The electrochemical impedance spectrum (EIS) was carried out in a 3.5 wt% NaCl solution at 25 • C with an Autolab-Nova electrochemical workstation (PGSTAT 302 N, Metrohm Autolab, Utrecht, Netherlands) using a 5 mV alternating current (AC) sinusoid signal at a frequency range from 1000 kHz to 0.1 Hz. All electrochemical experiments were performed using a conventional three-electrode system at room temperature.

Reaction Process
The process of preparing PPy on the Mg surface by the VPP method is shown in Figure 1. The reaction steps are as follows: Firstly, 20 µL of a Py monomer is added dropwise into a wide-mouth bottle with a ground glass stopper, in which a cylindrical Teflon block was placed. Because the vapor pressure of the Py monomer is 12.2 Torr at 25 • C (for comparison, the vapor pressure of 3,4-ethoxylenedioxythiophene (EDOT) is 0.278 Torr at 25 • C) [18], it is beneficial to form a saturated vapor pressure in a closed space. Secondly, 65 µL of V 2 O 5 hydrogel is uniformly coated on the pretreated substrate, and then the V 2 O 5 -coated Mg is transferred promptly into the bottle, placed on the surface of the Teflon block. V 2 O 5 , which is the oxidant in the reaction, can oxidize the Py vapor into PPy, thereby obtaining a PPy/V 2 O 5 composite film on the Mg surface. All the above steps are performed at normal temperature and in a vacuum. After 12 h, the sample is taken out from the bottle, washed, and dried at room temperature.
Coatings 2020, 10, x FOR PEER REVIEW 3 of 10 resistances were measured at different points. Four orders of magnitude of a two-way voltage of 0.01, 0.10, 1.00, and 10.0 mV were applied. Thermogravimetric analysis (TGA) was carried out on the SDT Q600 thermogravimetric analyzer (TA Instruments, New Castle, DE, USA) with a heating rate of 20 °C/min in the oxygen condition. The electrochemical impedance spectrum (EIS) was carried out in a 3.5 wt% NaCl solution at 25 °C with an Autolab-Nova electrochemical workstation (PGSTAT 302 N, Metrohm Autolab, Utrecht, Netherlands) using a 5 mV alternating current (AC) sinusoid signal at a frequency range from 1000 kHz to 0.1 Hz. All electrochemical experiments were performed using a conventional three-electrode system at room temperature.

Reaction Process
The process of preparing PPy on the Mg surface by the VPP method is shown in Figure 1. The reaction steps are as follows: Firstly, 20 μL of a Py monomer is added dropwise into a wide-mouth bottle with a ground glass stopper, in which a cylindrical Teflon block was placed. Because the vapor pressure of the Py monomer is 12.2 Torr at 25 °C (for comparison, the vapor pressure of 3,4ethoxylenedioxythiophene (EDOT) is 0.278 Torr at 25 °C) [18], it is beneficial to form a saturated vapor pressure in a closed space. Secondly, 65 μL of V2O5 hydrogel is uniformly coated on the pretreated substrate, and then the V2O5-coated Mg is transferred promptly into the bottle, placed on the surface of the Teflon block. V2O5, which is the oxidant in the reaction, can oxidize the Py vapor into PPy, thereby obtaining a PPy/V2O5 composite film on the Mg surface. All the above steps are performed at normal temperature and in a vacuum. After 12 h, the sample is taken out from the bottle, washed, and dried at room temperature.  Figure 2a is the SEM image of V2O5 on the surface of Mg. Nanowire morphology can be observed. Figure 2b shows the morphologies of the PPy film. It can be seen clearly that after VPP, the surface of Mg was covered with the deposited PPy. The color quickly changed from dark red to black, which means Py polymerizes into PPy film on the surface of Mg. Figure 2c is the digital photo of the sample in Figure 2b. The EDX of nanowires formed on the surface of Mg is shown in Figure 1d. In the spectrogram, the vanadium element was derived from the oxidant V2O5, the carbon elements were derived from PPy, and the magnesium was derived from the substrate. The oxygen element was observed, which is widely present in PPy and V2O5. It is concluded from the SEM and the EDX spectrogram that composite nanowires of PPy and V2O5 have been successfully synthesized on the surface of Mg foil with a diameter of about 50 nm.  Figure 2a is the SEM image of V 2 O 5 on the surface of Mg. Nanowire morphology can be observed. Figure 2b shows the morphologies of the PPy film. It can be seen clearly that after VPP, the surface of Mg was covered with the deposited PPy. The color quickly changed from dark red to black, which means Py polymerizes into PPy film on the surface of Mg. Figure 2c is the digital photo of the sample in Figure 2b. The EDX of nanowires formed on the surface of Mg is shown in Figure 2d. In the Coatings 2020, 10, 402 4 of 11 spectrogram, the vanadium element was derived from the oxidant V 2 O 5 , the carbon elements were derived from PPy, and the magnesium was derived from the substrate. The oxygen element was observed, which is widely present in PPy and V 2 O 5 . It is concluded from the SEM and the EDX spectrogram that composite nanowires of PPy and V 2 O 5 have been successfully synthesized on the surface of Mg foil with a diameter of about 50 nm.

FTIR Spectroscopic Analysis
The FTIR spectrum of V2O5 and the PPy/V2O5 composite are shown in Figure 3a. The red curve shows the FTIR spectrum of V2O5 with absorption bands at 971, 837, and 554 cm −1 . The band at 971 cm −1 is due to V=O stretching [23,24]. Bands at 837 and 554 cm −1 are assigned to V-O-V deformation modes [24,25]. V2O5 is transition metal oxide, and the vibration of vanadium oxygen group is concentrated in the range of 400-1000 cm −1 . The band 1500 cm −1 is mostly caused by residual water molecules in the early stage of reaction, which is not V2O5's own characteristic peak.
Bands at 705 cm −1 are assigned to the V-OH2 stretching mode due to the H2O in the structure [24]. The FTIR spectrum also shows the characteristic peaks of PPy/V2O5 composites. The band at around 1595 cm −1 is allocated to a stretching vibration of C=C in the Py ring [23][24][25][26]. The absorption band at 1337 cm −1 is related to C-H in plane deformation modes [23][24][25][26]. The characteristic absorption bands at 1213 and 1050 cm −1 are due to the stretching vibrations of C-N and C-H of PPy, respectively [23]. The peak at 979 cm −1 is due to the =CH out of plane vibration. Bands at 801 cm −1 are due to the stretching vibration of V=O in the remaining V2O5 in the composite product. The peak of 560 cm −1 is due to the vanadate ion bond in the composites [27]. The SEM and EDX experiments confirmed that the synthesized product is a composite containing PPy and V2O5.

FTIR Spectroscopic Analysis
The FTIR spectrum of V 2 O 5 and the PPy/V 2 O 5 composite are shown in Figure 3a. The red curve shows the FTIR spectrum of V 2 O 5 with absorption bands at 971, 837, and 554 cm −1 . The band at 971 cm −1 is due to V=O stretching [23,24]. Bands at 837 and 554 cm −1 are assigned to V-O-V deformation modes [24,25]. V 2 O 5 is transition metal oxide, and the vibration of vanadium oxygen group is concentrated in the range of 400-1000 cm −1 . The band 1500 cm −1 is mostly caused by residual water molecules in the early stage of reaction, which is not V 2 O 5 's own characteristic peak.

Thermogravimetric Analysis
The thermal stability of the PPy/V2O5 composite was studied via thermogravimetric analysis (TGA). Figure 3b shows four thermogravimetric curves of film synthesizing at different temperatures (room temperature, 60, 120, and 180 °C). The test was performed from room temperature to 600 °C. From the curves, three distinct temperature changes can be observed. The weight loss of about 5.0%-10.0% before 220 °C in the curves is due to the release of adsorbed water, crystallization water, and residual intercalated water molecules in the V2O5 interlayer [28]. The second stage, which starts at 220 °C and ends at 450 °C, is the main part of weight loss, indicating that the PPy in the PPy/V2O5 composites begins to decompose, and the PPy long chain collapses. After 450 °C, the weight of the sample grew about 2%. Since the reduced product of V2O5 is vanadate ion, vanadate may be oxidized to higher valence and higher weight in oxygen at high temperature. In general, the thermogravimetric experiments show that the PPy content of the composites obtained by VPP at different temperatures is similar. The weight loss proceeded quite steadily, with a residue of about 78% at 450 °C.

Conductivity
The conductivity is calculated by the following two-step experiments; our PPy/V2O5-covered Mg substrates (15 mm × 15 mm) are the same as the electrochemical test sample substrates. In the first step, after many times of measurement, the thickness data were concentrated at a value of 20-40 μm, so the film thicknesses of 20, 30 and 40 μm were taken. In the second step, the resistances of five samples in the same batch were measured by a RTS-9 four-probe tester (Guangzhou four probe technology Co. Ltd., Guangzhou, China). After the electrical conductivity was obtained from the resistivity, the average value was calculated: For the thickness of 20 μm, the conductivity range of all samples is 0.39~1.22 S/cm; for the thickness of 30 μm, the conductivity range of all samples is 0.26~0.82 S/cm; for the thickness of 40 μm, the conductivity range of all samples is 0.20-0.24 S/cm (Figure 4). Bands at 705 cm −1 are assigned to the V-OH 2 stretching mode due to the H 2 O in the structure [24]. The FTIR spectrum also shows the characteristic peaks of PPy/V 2 O 5 composites. The band at around 1595 cm −1 is allocated to a stretching vibration of C=C in the Py ring [23][24][25][26]. The absorption band at 1337 cm −1 is related to C-H in plane deformation modes [23][24][25][26]. The characteristic absorption bands at 1213 and 1050 cm −1 are due to the stretching vibrations of C-N and C-H of PPy, respectively [23]. The peak at 979 cm −1 is due to the =CH out of plane vibration. Bands at 801 cm −1 are due to the stretching vibration of V=O in the remaining V 2 O 5 in the composite product. The peak of 560 cm −1 is due to the vanadate ion bond in the composites [27]. The SEM and EDX experiments confirmed that the synthesized product is a composite containing PPy and V 2 O 5 .

Thermogravimetric Analysis
The thermal stability of the PPy/V 2 O 5 composite was studied via thermogravimetric analysis (TGA). Figure 3b shows four thermogravimetric curves of film synthesizing at different temperatures (room temperature, 60, 120, and 180 • C). The test was performed from room temperature to 600 • C. From the curves, three distinct temperature changes can be observed. The weight loss of about 5.0%-10.0% before 220 • C in the curves is due to the release of adsorbed water, crystallization water, and residual intercalated water molecules in the V 2 O 5 interlayer [28]. The second stage, which starts at 220 • C and ends at 450 • C, is the main part of weight loss, indicating that the PPy in the PPy/V 2 O 5 composites begins to decompose, and the PPy long chain collapses. After 450 • C, the weight of the sample grew about 2%. Since the reduced product of V 2 O 5 is vanadate ion, vanadate may be oxidized to higher valence and higher weight in oxygen at high temperature. In general, the thermogravimetric experiments show that the PPy content of the composites obtained by VPP at different temperatures is similar. The weight loss proceeded quite steadily, with a residue of about 78% at 450 • C.

Conductivity
The conductivity is calculated by the following two-step experiments; our PPy/V 2 O 5 -covered Mg substrates (15 mm × 15 mm) are the same as the electrochemical test sample substrates. In the first step, after many times of measurement, the thickness data were concentrated at a value of 20-40 µm, so the film thicknesses of 20, 30 and 40 µm were taken. In the second step, the resistances of five samples in the same batch were measured by a RTS-9 four-probe tester (Guangzhou four probe technology Co. Ltd., Guangzhou, China). After the electrical conductivity was obtained from the resistivity, the average value was calculated: For the thickness of 20 µm, the conductivity range of all samples is 0.39~1.22 S/cm; for the thickness of 30 µm, the conductivity range of all samples is 0.26~0.82 S/cm; for the thickness of 40 µm, the conductivity range of all samples is 0.20-0.24 S/cm (Figure 4). 220 °C and ends at 450 °C, is the main part of weight loss, indicating that the PPy in the PPy/V2O5 composites begins to decompose, and the PPy long chain collapses. After 450 °C, the weight of the sample grew about 2%. Since the reduced product of V2O5 is vanadate ion, vanadate may be oxidized to higher valence and higher weight in oxygen at high temperature. In general, the thermogravimetric experiments show that the PPy content of the composites obtained by VPP at different temperatures is similar. The weight loss proceeded quite steadily, with a residue of about 78% at 450 °C.

Conductivity
The conductivity is calculated by the following two-step experiments; our PPy/V2O5-covered Mg substrates (15 mm × 15 mm) are the same as the electrochemical test sample substrates. In the first step, after many times of measurement, the thickness data were concentrated at a value of 20-40 μm, so the film thicknesses of 20, 30 and 40 μm were taken. In the second step, the resistances of five samples in the same batch were measured by a RTS-9 four-probe tester (Guangzhou four probe technology Co. Ltd., Guangzhou, China). After the electrical conductivity was obtained from the resistivity, the average value was calculated: For the thickness of 20 μm, the conductivity range of all samples is 0.39~1.22 S/cm; for the thickness of 30 μm, the conductivity range of all samples is 0.26~0.82 S/cm; for the thickness of 40 μm, the conductivity range of all samples is 0.20-0.24 S/cm (Figure 4). Kim [29] prepared a composite film of polymethyl methacrylate (PMMA)/PPy by spin coating. The composite film can passivate the iron substrate through oxidation-reduction chemistry to provide corrosion protection. The electrical conductivity of the composite material is in the range of 0.30-1.84 S/cm −1 .
Jadhav [27] reported a PPy coating doped with vanadate and tungstate. With the degradation of PPy in the composite coating, the doped anions were released along with it, becoming a corrosion inhibitor in the system and slowing the corrosion of the aluminum substrate. The conductivity of PPy composite reached 0.05 S/cm −1 .
Feng Li [30] pointed out that the copolymer coating doped with sodium molybdate (PPy-PAnimolybdate) can promote the formation of passivation film on stainless steel substrate; we believe that PPy doped with vanadate anions has a similar effect.
Generally, the conductivity of Mg is 22 × 10 6 S·m −1 . If the measured resistivity is a parallel resistance, the resulting parallel resistivity should be less than that of pure Mg, and the resulting conductivity should be much greater than 22 × 10 6 S·m −1 . However, the results prove that the obtained conductivity is similar to the reported PPy/V 2 O 5 conductivity, and it has not increased sharply, so what we measured is the conductivity of the composites. Meanwhile, the results prove that the conductivity of the final product PPy/V 2 O 5 (0.20-1.22 S/cm −1 ) is higher than the V 2 O 5 conductivity (0.05 S/cm −1 ) prepared by the same method [22], which is attributed to the PPy being doped.

Tracing Quasistationary Polarization
Corrosion tests of the nanostructured PPy/V 2 O 5 composite were investigated in order to evaluate its ability for regulating the degrade rate of Mg. Figure 5 shows the polarization curves of the bare Mg, V 2 O 5 -coated Mg, and PPy/V 2 O 5 -coated Mg foils soaking in 3.5 wt% sodium NaCl for 6 h.
Compared to bare Mg and V 2 O 5 -coated Mg, the Tafel plots of the PPy/V 2 O 5 -coated sample gave a much more positive corrosion potential (Ecorr) and a lower corrosion current (Icorr). The Tafel extrapolations revealed that the presence of PPy/V 2 O 5 film caused a positive shift in the corrosion potential compared to the bare Mg and V 2 O 5 -coated Mg foil, indicating that the anticorrosion performance of Mg has been improved by the PPy deposits. By contrast, the anticorrosion ability of the V 2 O 5 -coated sample was only slightly better than that of bare Mg.

Tracing Quasistationary Polarization
Corrosion tests of the nanostructured PPy/V2O5 composite were investigated in order to evaluate its ability for regulating the degrade rate of Mg. Figure 5 shows the polarization curves of the bare Mg, V2O5-coated Mg, and PPy/V2O5-coated Mg foils soaking in 3.5 wt% sodium NaCl for 6 h. Compared to bare Mg and V2O5-coated Mg, the Tafel plots of the PPy/V2O5-coated sample gave a much more positive corrosion potential (Ecorr) and a lower corrosion current (Icorr). The Tafel extrapolations revealed that the presence of PPy/V2O5 film caused a positive shift in the corrosion potential compared to the bare Mg and V2O5-coated Mg foil, indicating that the anticorrosion performance of Mg has been improved by the PPy deposits. By contrast, the anticorrosion ability of the V2O5-coated sample was only slightly better than that of bare Mg.

Electrochemical Impedance Spectroscopy
Since Mg is very sensitive, electrochemical impedance spectroscopy (EIS) is also carried out to characterize the corrosion resistance of different samples from 0.5 to 96 h in a 3.5 wt% NaCl solution ( Figure 6). In general, the negative peak in the Bode-phase plots indicates the electrical conductivity between the films and the substrate. Meanwhile, the positive peak in the plots represents the unique inductive response of Mg. In addition, a high corrosion-resistant system should have a slow decreasing resistance. Based on the changes of these EIS parameters, the corrosion damage of a film system can be estimated [31]. Figure 6a shows that the bare Mg has two positive peaks (upward) at the intermediate frequency region (10-10 4 Hz). In the Bode-impedance plot (Figure 6d), we find the impedance at 0.1 Hz of bare Mg experiences a fluctuation process. This phenomenon means that the passivation film is gradually destroyed in the NaCl solution, and Cl − invades the Mg substrate; pitting is getting worse after 24 h. Figure 6b shows the samples covering V 2 O 5 , where the two positive peaks in the intermediate frequency region gradually divide into three positive peaks from 0.5 to 96 h. The third peak appeared at 72 h. The presence of such conductive behavior in the intermediate region suggests that the film has corrosion protection for the substrate. As time prolonged (after 72 h), the position of the positive peak changed, indicating the degradation of the film and new chemical reaction. A similar Bode-phase plots characteristic was found in the PPy/V 2 O 5 composite film sample. The impedance of the composite film is higher and more stable than those of the previous two samples (bare Mg and V 2 O 5 ). This conductive behavior indicates an improved anticorrosion protection from the PPy film. All results show that the PPy/V 2 O 5 composite film possesses the best anticorrosion ability. decreasing resistance. Based on the changes of these EIS parameters, the corrosion damage of a film system can be estimated [31]. Figure 6a shows that the bare Mg has two positive peaks (upward) at the intermediate frequency region (10-10 4 Hz). In the Bode-impedance plot (Figure 6d), we find the impedance at 0.1 Hz of bare Mg experiences a fluctuation process. This phenomenon means that the passivation film is gradually destroyed in the NaCl solution, and Cl − invades the Mg substrate; pitting is getting worse after 24 h.

Mechanism of the Corrosion Resistance
At present, there are many explanations for the mechanism of metal corrosion protection by PPy, but there is no final conclusion in the academic field. The main mechanisms include the anodic protection theory, controlled inhibitor release mechanism, conductive mechanism, etc. As for the composite film deposited by our VPP method, its corrosion protection can be explained in two periods.
In the first stage (before 24 h), the physical barrier effect is dominant. Actually, the film of the nanowires has a large specific surface area and cannot be absolutely pinhole-free, but the coating

Mechanism of the Corrosion Resistance
At present, there are many explanations for the mechanism of metal corrosion protection by PPy, but there is no final conclusion in the academic field. The main mechanisms include the anodic protection theory, controlled inhibitor release mechanism, conductive mechanism, etc. As for the composite film deposited by our VPP method, its corrosion protection can be explained in two periods.
In the first stage (before 24 h), the physical barrier effect is dominant. Actually, the film of the nanowires has a large specific surface area and cannot be absolutely pinhole-free, but the coating thickness ranges from 20 to 40 µm, which is enough for the physical barrier effect to provide limited corrosion protection in a short period. In the second stage (after 24 h), the conductive mechanism and anodic protection are dominant. On the one hand, because the Mg's reduction potential (−2.37 V) is lower than PPy's (−0.1-+0.3 V), the surface of Mg will react with PPy to form a passivation layer (a mixture of Mg hydroxide and oxide), which increases the overall potential. In addition, the PPy/V 2 O 5 composite film and the Mg substrate can be regarded as a whole due to their conductivity. When Mg loses electrons, it does not gather in the defect area; it can be transferred to other parts, which slows down the occurrence of pitting and corrosion.
We acknowledge that there is still a gap between the present VPP method and commercial anticorrosion methods, but it can be used as a new idea for corrosion protection. Mg is a promising biodegradable metal and has important application prospects in the biomedical field. However, its corrosion resistance is quite poor, which leads to rapid degradation within the human body and thus greatly limits the application in vivo. Therefore, it is of both great scientific and technical significance to slow down the degradation rate of Mg. The use of PPy as a coating material can provide an effective way to meet this requirement.
3.8. The Role of V 2 O 5 V 2 O 5 plays the role of an oxidant and a template in our VPP method, and vanadate anion as the reduction product of V 2 O 5 is a dopant for the composite. The specific reasons we chose V 2 O 5 are as follows. First, the film formation of PPy is greatly affected by V 2 O 5 hydrosol. If the storage time and the storage temperature are appropriate, the final nanostructure morphology will be complete.
Second, unlike other oxidants (such as Fe (III) sulfonates) in VPP, V 2 O 5 does not need to be heated to crystallization and thus without the requirement of high temperature and low vacuum because it can maintain excellent oxidizability under normal temperature and pressure. Third, after the polymerization of Py, the V 2 O 5 was reduced to vanadate ion, which exists in the composites as dopant.
3.9. The Limitations of Our VPP PPy exposed to atmospheric conditions will gradually degrade. Our VPP method deposited PPy on V 2 O 5 nanowires, so there is also the possibility of degradation. There are two factors that have a great influence on the degradation of VPP: (1) exposure to air, as the reaction of the PPy main chain with oxygen in the air leads to irreversible loss of conjugated structure; and (2) the loose porous structure leads to PPy adsorbing water in the air, leading to a reversible or partially reversible hydrolysis of a conjugated structure. If the next step is to carry out in-depth research on the application of metal anti-corrosion, these two points must be given attention.
V 2 O 5 could remain in the reaction product. Whether V 2 O 5 is present in the final product depends on the amount of pyrrole (Py) and the reaction time. If the amount of Py is excessive and time is long enough, V 2 O 5 will be completely reacted, and there will be no residue in the product. If the amount of pyrrole is insufficient or the reaction time is short, a part of V 2 O 5 will remain in the final product. If V 2 O 5 is not removed by acid, there could be potential safety hazards.

Conclusions
In summary, a mild VPP method has been successfully developed for the synthesis of a PPy/V 2 O 5 composite film on the reactive metal Mg. The microstructure of the composite film exhibits wire-like morphology with a diameter of about 40-50 nm. FTIR and EDX tests confirmed that the film is a composite of PPy and V 2 O 5 , with conductivity in the range of 0.20-1.22 S/cm. The TGA tests showed that the composites synthesized at different temperatures (room temperature, 60, 120, 180 • C) had a similar thermal stability and decomposition content. Electrochemical tests revealed that the corrosion resistance of bare Mg was improved due to the deposition of the composite films. Compared with the current existing VPP method for the formation of CPs, our method was a more convenient and cost-effective method because the VPP reaction could be carried out at room temperature under normal atmospheric pressure, and thus, there is no complex equipment required. Furthermore, the present mild method also could be applied to synthesize PPy-based composite film on the surface of reactive metal, which is impossible for the conventional VPP methods. These unique properties make the present mild VPP method very attractive for a variety of applications, such as the synthesis of CP-based composites and corrosion protection of the reactive metal.