E ﬀ ect of Sodium Phosphate and Calcium Nitrate Sealing Treatment on Microstructure and Corrosion Resistance of Wire Arc Sprayed Aluminum Coatings

: Aluminum coating was deposited by arc thermal spraying process onto the steel substrate for the corrosion protection in aggressive environment. However, the arc thermal sprayed coating possesses defects in the coating. Thus, it is important to reduce the defects and enhance the corrosion resistance properties of the deposited coating using post-treatment. In the present study, we have used di ﬀ erent concentrations of sodium phosphate mono basic (NaH 2 PO 4 ) with 0.1 molar (M) calcium nitrate [Ca(NO 3 ) 2 ] as post-treatment solution to ﬁll out the defects of the Al coating. It was observed by scanning electron microscopy (SEM) that 1 M NaH 2 PO 4 with 0.1 M Ca(NO 3 ) 2 treated sample exhibited 71% reduction in defects compared to as coated samples. X-ray di ﬀ raction (XRD) was performed to determine the phases formed on the coating surface after treatments. XRD conﬁrms the formation of sodium aluminum hydrogen phosphate (Na 3 Al(OH)(HPO 4 )(PO 4 )) and brushite (Ca(HPO 4 )(H 2 O) 2 ) as composite oxides on the Al coating. Electrochemical results show that 0.5 M NaH 2 PO 4 with 0.1 M Ca(NO 3 ) 2 treated sample has exhibited the highest charge transfer resistance and the lowest corrosion current density after 89 days of exposure in 3.5 wt.% NaCl solution. The enhancement in corrosion resistance of 0.5 M NaH 2 PO 4 with 0.1 M Ca(NO 3 ) 2 treated sample attributed to the formation of adherent, sparingly soluble, and stable corrosion products. The volume fraction result of the corrosion products formed on 0.5 M NaH 2 PO 4 with 0.1 M Ca(NO 3 ) 2 treated sample after 89 days of exposure in 3.5 wt.% NaCl using XRD conﬁrms the highest amount of Bayerite ( α -Al(OH) 3 ) deposition, thus, the corrosion rate of this sample was the lowest. voltage in triplicate number of samples. The DC potentiodynamic polarization was performed by changing the impressed current from − 0.4 to + 0.8 V versus Ag / AgCl at a 1 mV / s scan rate. The analysis of the obtained results was performed by Metrohm Autolab Nova 1.10 software.


Introduction
The economic loss of the most advanced countries due to corrosion is estimated to be about 3%-4% of gross domestic product [1][2][3]. The building and infrastructures can be protected from

Treatment of the Coatings
The treatment solution was prepared by dissolving analytical grade sodium phosphate mono basic (NaH 2 PO 4 ) and calcium nitrate [Ca(NO 3 2 were abbreviated as SPCN1, SPCN2, and SPCN3, respectively. The pH of the treatment solution was measured at 25 ± 1 • C and it was found to be 3.52, 3.40, and 3.13 for SPCN1, SPCN2, and SPCN3, respectively. The treatment of Al coating was performed at 25 ± 1 • C three times using a nylon brush up to 24 h at every 8 h interval. After the treatment of samples, they were kept for drying at 25 ± 1 • C up to 24 h in laboratory. After drying, the samples were subsequently kept in a humidity chamber for 7 days at 50 • C and 95% relative humidity for the formation of natural oxides [33][34][35]. It is well known that when the coating is exposed to harsh atmospheric conditions where humidity and temperature are very high, there will be a probability of forming natural oxide. Thus, we have kept the samples in the humidity chamber to form natural oxide prior to immersion in NaCl solution.

Corrosion Studies
The corrosion studies of as coated (AC) Al samples as well as treated coatings were performed by dissolving analytical grade of 3.5 wt.% NaCl salt in distilled water. It was carried out by VersaSTAT potentiostat (Princeton Applied Research, Oak Ridge, TN, USA) using a three electrode system where the coated/treated sample acted as the working electrode, the platinum wire as the counter electrode, and the silver-silver chloride (Ag/AgCl) as the reference electrode. The electrochemical impedance spectroscopy (EIS) of the samples were carried out from 100 kHz to 0.01 Hz with a 10 mV sinusoidal voltage in triplicate number of samples. The DC potentiodynamic polarization was performed by changing the impressed current from −0.4 to +0.8 V versus Ag/AgCl at a 1 mV/s scan rate. The analysis of the obtained results was performed by Metrohm Autolab Nova 1.10 software.

Characterization of the Coatings and Corrosion Products
The surface morphology of the AC, treated, and corrosion products was carried out by scanning electron microscopy (SEM, MIRA3, TESCAN, Brno, Czech Republic) operated at 15 kV and elemental analysis by energy-dispersive X-ray spectroscopy (EDS). The porosity of the samples considering cross sectional area was calculated by ImageJ software (version 1.52n).
The formation of phases on AC, treated, and corrosion products was performed by X-ray diffraction (XRD, Rigaku, Tokyo, Japan) using Cu Kα radiation (λ = 1.54059 Å) generated at 40 kV and 100 mA. The volume fraction (%) of each phase formed on the samples was analyzed by JADE2016 software.

Coating Thickness and Bond Adhesion Analysis
The thickness of the coatings was measured at three different locations using Elcometer456 and the average value was taken as a result. The average thickness of AC and SPCN1 was found to be 100 ± 5 µm whereas SPCN2 and SPCN3 were found to be 110 and 140 ± 5 µm, respectively, attributed to the deposition of composite oxide after treatment. The average bond adhesion value of the coatings was 4.86 ± 0.08 MPa for four consecutive samples [19,31,[33][34][35].

Scanning Electron Microscopy (SEM) of the Coatings
SEM images of the coatings are shown in Figures 1 and 2. The top surface SEM image of the AC sample shows lamellar particles owing to the sudden cooling of melted metal droplets during deposition of the coating using arc thermal spray process. The approximate size of the lamellae is found to be 5-10 µm, but in between two lamellae some defects and cracks can be observed (Figure 1a). The cracks have originated horizontally from the upper layer of the coating and in depth which encourages the ingress of harmful gases and solutions from the atmosphere. Once the coating was treated with solution, the surface morphology has changed dramatically owing to the deposition of oxide film which covers the surface and fills out the defects of the coatings. When the coating was treated with SPCN1 ( Figure 1b) solution, it exhibits filamentous and clusters of needle particles. However, it shows defects and non-homogenous deposition owing to the lower concentration of NaH 2 PO 4 solution [35]. The influential effect of 0.1 M Ca(NO 3 ) 2 is observed when it was mixed with NaH 2 PO 4 [34]. Moreover, 0.1 M NaH 2 PO 4 and 0.1 M Ca(NO 3 ) 2 i.e., SPCN1 is not enough to make proper film. Thus, it is required to increase NaH 2 PO 4 concentration with 0.1 M Ca(NO 3 ) 2 from 0.1 to 0.5 and 1 M. The improvement in morphology is observed when coating was treated with 0.5 M NaH 2 PO 4 and 0.1 M Ca(NO 3 ) 2 i.e., SPCN2 (Figure 1c). The surface is covered by needle like oxide particles which is smaller in size and combined to each other (Figure 1c). The number of defects and area is reduced compare to AC and SPCN1. A bunch of needle like particles are filled out the defects and enhances the morphology of coating owing to the precursor effect by calcium [44]. As the concentration was increased from 0.5 to 1 M NaH 2 PO 4 with 0.1 M Ca(NO 3 ) 2 i.e., SPCN3, the surface become homogeneous (Figure 1d) rather than needle like morphology. It means higher concentration of NaH 2 PO 4 along with 0.1 M Ca(NO 3 ) 2 improve the quality of coating in regards of surface morphology. However, it contains net like morphology with micro-cracks owing to the higher concentration of NaH 2 PO 4 which enhances the formation of crack on surface [35]. The net like composite oxides and micro-cracks allow the ingress of aggressive ions easily which later enhances the deterioration of coating.
cross sectional SEM images and it is found to be 31%, 25%, 19%, and 9% for AC, SPCN1, SPCN2, and SPCN3, respectively. The defect is gradually decreased as the amount of NaH2PO4 increased with 0.1 M Ca(NO3)2 solution. The defect is approximately reduced by 19%, 38%, and 71% for SPCN1, SPCN2, and SPCN3, respectively, compared to the AC sample.
The EDS analysis of coating (Table 1) shows that as the concentration of NaH2PO4 is increased, the amount of Na, P, and O increased. The N and Ca amount is found to be between 1.35%-1.44% and 7.71%-7.95%, respectively. The amount of O is found to be 2.20% in the AC sample.    The cross sectional SEM images of the coatings are shown in Figure 2. It can be seen from Figure 2a that the AC sample shows defects at the coating/substrate interface as well as cracks at the outer surface of the coating. These cracks and defects are interconnected and correlate to the results of the top surface morphology (Figure 1a). However, once the treatment was applied, the coating exhibits less defects compared to the AC sample owing to the filling ability of the treatment solution. Figure 2b shows that the defects are found to be pronounced at the coating/substrate interface which is attributed to the incomplete penetration of the treatment solution. However, AC and SPCN1 samples exhibit around 100 ± 5 µm coating thickness. After the treatment with SPCN1, there is no influential effect of the treatment solution in coating thickness owing to the formation of less amount of oxide film. As the concentration of NaH 2 PO 4 is increased from 0.1 to 0.5 M with 0.1 M Ca(NO 3 ) 2 solution, the area of defects decreased attributed to the formation of composite oxide film. It can be seen from Figure 2c that the SPCN2 sample shows uniform film (Figure 2c) owing to the penetration of treatment solution through the spaces of lamellae as observed in the AC sample, which encourages the formation of composite oxide. Hence, the defect area is very less observed in SPCN2 (marked by the circle in Figure 2c) compared to AC and SPCN1. The coating thickness after treatment is found to be approximately 115 µm, which is greater than AC, owing to the formation of composite oxide film. SPCN3 sample exhibits defect free surface (Figure 2d) compared to the other samples attributed to the greater filling ability of 1 M NaH 2 PO 4 and 0.1 M Ca(NO 3 ) 2 solution. The coating thickness is increased up to 140 µm owing to the formation of greater volume of composite oxide which participated in the coating thickness.
The defect area of the coating was calculated using ImageJ software after treatment considering cross sectional SEM images and it is found to be 31%, 25%, 19%, and 9% for AC, SPCN1, SPCN2, and SPCN3, respectively. The defect is gradually decreased as the amount of NaH 2 PO 4 increased with 0.1 M Ca(NO 3 ) 2 solution. The defect is approximately reduced by 19%, 38%, and 71% for SPCN1, SPCN2, and SPCN3, respectively, compared to the AC sample.
The EDS analysis of coating (Table 1) shows that as the concentration of NaH 2 PO 4 is increased, the amount of Na, P, and O increased. The N and Ca amount is found to be between 1.35%-1.44% and 7.71%-7.95%, respectively. The amount of O is found to be 2.20% in the AC sample. The identification of phases deposited on coating surface after treatment as well as AC sample was analyzed by XRD and results are shown in Figure 3. The full scan i.e., 2θ = 10 • -90 • XRD result is shown in Figure 3a whereas lower angle scan i.e., 2θ = 10 • -30 • is shown in Figure 3b. The most intense and strong peak is Al phase (Figure 3a) owing to the coating materials. Once the treatment was performed, the intensity of Al decreased owing to the participation of another phases. After treatment of Al coating with NaH 2 PO 4 and 0.1 M Ca(NO 3 ) 2 , the following reaction may occur [34,35]: Coatings 2020, 10, 33

of 22
The volume fraction (%) was calculated using JADE software (2016) and the results are shown in Table 2. As the concentration of NaH2PO4 is increased with 0.1 M Ca(NO3)2, the volume fraction of BR and SAHP increased gradually. This result suggests that Al might be highly reactive with NaH2PO4 resulting in deposition of SAHP film, while NaH2PO4 reacts with 0.1 M Ca(NO3)2 and forms BR [34,[45][46][47]. AC sample shows 100% Al which indicates that during deposition of the coating there was no new phase formation.   Figure 4 shows the complex-plane impedance plots of the coatings at different exposure periods in 3.5 wt.% NaCl solution. As the concentration of NaH2PO4 increased with 0.1 M Ca(NO3)2, the magnitude of the real and imaginary  [34,[45][46][47]. The SAHP reaction of Al with phosphate ion [35,48] is shown in Equation (1). From Equation (1), it can be seen that H + ion releases during the reaction which make the solution acidic, thus the pH of the treatment solution was reduced to 3.52, 3.40, and 3.13 for SPCN1, SPCN2, and SPCN3, respectively. However, SAHP is soluble in water and makes the solution acidic owing to it being acidic in nature [49][50][51]. However, SAHP is brittle [52], thus when the concentration of NaH 2 PO 4 is increased, some micro-and nano-cracks have been observed on the surface of the coating (Figure 1d). Due to the high intensity of Al peaks, Brushite and SAHP peaks are suppressed, thus we have plotted it again and shown it in Figure 3b at 2θ = 10 • -30 • . As the concentration of NaH 2 PO 4 is increased, the intensity of brushite and SAHP is increased owing to the greater deposition of these phases.
The volume fraction (%) was calculated using JADE software (2016) and the results are shown in Table 2. As the concentration of NaH 2 PO 4 is increased with 0.1 M Ca(NO 3 ) 2 , the volume fraction of BR and SAHP increased gradually. This result suggests that Al might be highly reactive with NaH 2 PO 4 resulting in deposition of SAHP film, while NaH 2 PO 4 reacts with 0.1 M Ca(NO 3 ) 2 and forms BR [34,[45][46][47]. AC sample shows 100% Al which indicates that during deposition of the coating there was no new phase formation.  Figure 4 shows the complex-plane impedance plots of the coatings at different exposure periods in 3.5 wt.% NaCl solution. As the concentration of NaH 2 PO 4 increased with 0.1 M Ca(NO 3 ) 2 , the magnitude of the real and imaginary components of impedance increased gradually after 1 h of exposure ( Figure 4a) attributed to the treatment [53]. The AC sample exhibits a smaller magnitude semi-circle compared to treated coating Coatings 2020, 10, 33 8 of 22 owing to the presence of defects on the surface (Figures 1a and 2a) which allows the ingress of the NaCl solution through the defects and causes a localized attack. At the lower studied frequency, all samples exhibit scattering in data which attributed either due to capacitive properties of the coatings or presence of defective film (after treatment) [35]. As it is observed in the SEM images (Figure 1), AC as well as treated coating contains defects which act as capacitance. This result confirms that AC and SPCN3 contain two electrical equivalent circuits (EEC). In the case of AC, after 1 h of exposure in 3.5 wt.% NaCl solution it might be starting to corrode owing to the presence of defects and cracks on the coating surface. During the reaction of Al coating with NaCl solution, there is possibility to deposit the corrosion products onto the surface which fill out the defects. On the other hand, SPCN3 contains brittle film of the SAHP layer which allows the penetration of the solution, thus corrosion would start on the treated film as well as the coating surface. Moreover, SPCN1 and SPCN2 exhibit a needle like microstructure (Figure 1b,c) which firstly reacts with the NaCl solution thereafter allowing the penetration of the solution towards the coating surface. Once the solution comes in contact with treated surface of SPCN1 and SPCN2, BR and SAHP film stifle the penetration of the solution owing to the barrier type of protection provided by them [54,55]. Therefore, only one EEC can be observed. components of impedance increased gradually after 1 h of exposure ( Figure 4a) attributed to the treatment [53]. The AC sample exhibits a smaller magnitude semi-circle compared to treated coating owing to the presence of defects on the surface (Figures 1a and 2a) which allows the ingress of the NaCl solution through the defects and causes a localized attack. At the lower studied frequency, all samples exhibit scattering in data which attributed either due to capacitive properties of the coatings or presence of defective film (after treatment) [35]. As it is observed in the SEM images ( Figure 1), AC as well as treated coating contains defects which act as capacitance. This result confirms that AC and SPCN3 contain two electrical equivalent circuits (EEC). In the case of AC, after 1 h of exposure in 3.5 wt.% NaCl solution it might be starting to corrode owing to the presence of defects and cracks on the coating surface. During the reaction of Al coating with NaCl solution, there is possibility to deposit the corrosion products onto the surface which fill out the defects. On the other hand, SPCN3 contains brittle film of the SAHP layer which allows the penetration of the solution, thus corrosion would start on the treated film as well as the coating surface. Moreover, SPCN1 and SPCN2 exhibit a needle like microstructure (Figure 1b,c) which firstly reacts with the NaCl solution thereafter allowing the penetration of the solution towards the coating surface. Once the solution comes in contact with treated surface of SPCN1 and SPCN2, BR and SAHP film stifle the penetration of the solution owing to the barrier type of protection provided by them [54,55]. Therefore, only one EEC can be observed. As the exposure periods are extended up to 11 days, the magnitude of complex-plane impedance plots increased (Figure 4b) which indicate that coating would provide protection against corrosion in 3.5 wt.% NaCl solution. In the case of the AC sample, the corrosion products might be deposited in defects whereas treated coating containing BR and SAHP film might be transformed into other phases [34,56]. SPCN1 exhibits semi-circle which indicate that treated film might be dissolved and coating surface contributed in the corrosion reaction. AC, SPCN2, and SPCN3 show a semi-circle at higher to middle frequency, attributed to the charge transfer resistance between treated film/corrosion products and solution interface whereas at lower frequency, one tail can be seen which causes a resistance by oxide layer at corrosion products/coating interface in NaCl solution [57][58][59]. As the exposure periods are extended up to 11 days, the magnitude of complex-plane impedance plots increased (Figure 4b) which indicate that coating would provide protection against corrosion in 3.5 wt.% NaCl solution. In the case of the AC sample, the corrosion products might be deposited in defects whereas treated coating containing BR and SAHP film might be transformed into other phases [34,56]. SPCN1 exhibits semi-circle which indicate that treated film might be dissolved and coating surface contributed in the corrosion reaction. AC, SPCN2, and SPCN3 show a semi-circle at higher to middle frequency, attributed to the charge transfer resistance between treated film/corrosion products and solution interface whereas at lower frequency, one tail can be seen which causes a resistance by oxide layer at corrosion products/coating interface in NaCl solution [57][58][59].
pH reduction of the studied solution. However, in the case of SPCN3, the amount of these phases were the maximum and active in nature which might be dissolved in the studied solution and result in lowering of pH as well as impedance value. The SPCN2 sample steadily dissolve and uniformly cover the surface thus, higher total impedance is observed at 0.01 Hz (Figure 5d). The total impedance value of AC, SPCN1, and SPCN2 is found to be increased by 11, 8, and 12 times compared to SPCN3 sample, respectively. The phase-frequency Bode plots of the coatings with exposure periods in 3.5 wt.% NaCl solution are illustrated in Figure 6. It is observed that SPCN1 and SPCN2 exhibit one time constant around −52° on 11 and 71 Hz, respectively, owing to the deposition of treatment film while AC and SPCN3 show two different time constants at different frequencies ( Figure 6a). Middle frequency attributed to the treatment/corrosion products while lower frequency shows the characteristics of the coating [34,[60][61][62][63]]. The SPCN3 sample shows highest shifting in phase angle maxima at −62° on 120 Hz while at lower frequency i.e., 0.03 Hz exhibit at −13°. The AC sample shows 20° phase angle shifting on 0.01 Hz which reveals that the coating is defective and the crack bearing surface enhances the ingress of aggressive ions from atmosphere/solution. As the exposure periods are extended from 1 h to 11 d, the phase angle maxima are shifted towards a higher angle in the middle frequency range (Figure 6b) owing to the deposition of corrosion products onto the surface. AC sample shows two time constants; one at −33° on 70 Hz attributed to the corrosion products while another at −38° on 0.32 Hz owing to the coating characteristics. This result suggests that coating as well as corrosion products of AC sample strengthen their properties with exposure periods in NaCl solution. Thus, increment in the impedance is observed compared to 1 h of exposure (Figure 5b). The treated coatings show shifting of maxima at a higher angle. The SPCN1 shows only one time constant in middle frequency ranges around −58° attributed to the treatment or deposition of corrosion products. Although, in middle frequency ranges, scattering in data is observed owing to the defective corrosion products which causes capacitance. The SPCN2 and SPCN3 show two phase angle maxima, one at middle and another at lower frequency. The SPCN2 exhibit broadening in maxima at −43° from 1800 to 18 Hz owing to the deposition of uniform corrosion products after reaction of BR and SAHP film with NaCl solution. At lower frequency i.e., 0.017 Hz, the phase angle maxima are shifted from −0.5° to −7.5° for 1 h to 11 days, respectively. It means the reaction of BR and SAHP help in improving the properties of coating as well as corrosion products. The SPCN3 shows the maxima around −58° at 31 Hz with scattering which reveals that treatment/corrosion products are defective and causes capacitance. But broadening in the time constant is observed which helps in improvement of the impedance. However, the decrease in maxima after 11 days compared to 1 h is owing to the dissolution of defective BR and SAHP film during reaction with NaCl solution. It might be corrosion products distributed all over the surface but being defective at longer durations of exposure causes deterioration. As the exposure periods are extended from 11 to 41 days, the phase angle maxima of all samples shifted towards higher angles except SPCN3 (Figure 6c). The decrease in phase angle maxima of SPCN3 owing to the dissolution of BR and SAHP film as well as deposition of defective corrosion products which was started to dissolve after 11 days of exposure. Thus, the coating itself is participating in the corrosion reaction. It is also observed that the phase angle maxima at lower frequency i.e., 0.01 Hz, is decreased compared to 11 days of exposure. This result indicates that BR and SAHP film is completely dissolved and the coating has started to participate in the corrosion As the exposure periods are increased up to 41 days, the magnitude of complex-plane impedance plots of AC, SPCN1, and SPCN2 increased dramatically while SPCN3 decreased compare to earlier exposure periods (Figure 4c). The decrease in magnitude of complex-plane impedance plot of SPCN3 attributed to the presence of high amount of SAHP ( Figure 3 and Table 2) which dissolved at longer duration of exposure and made the studied solution acidic. On the other hand, it might be that the AC sample contains protective corrosion product after 41 days of exposure which fill out the defects whereas SPCN1 and SPCN2 transformed the BR and SAHP into a protective film. Thus, there are two semi-circles observed at different studied frequencies. One small semi-circle at higher frequency and another big from middle to lower frequency was observed. In earlier exposure periods, at higher frequency a bigger semi-circle was observed whereas at lower frequency a smaller one was observed. It is attributed to the reaction of NaCl solution with coating/treated surface. Up to 11 days of exposure, coating/treated surfaces participated in the corrosion reaction but at a longer duration of exposure, the treated layer might be dissolved or transformed into corrosion products. It means that at longer duration of exposure corrosion products have contributed in the corrosion reaction rather than the coating or treated film, thus the coatings provide protection against corrosion.
After 89 days of exposure in 3.5 wt.% NaCl solution, SPCN1 and SPCN3 decreased the magnitude of complex-plane impedance plots owing to the deterioration. In case of SPCN1, the thin layer of treated film has dissolved and formed less stable corrosion products thus, a decrease in magnitude is observed but it is higher than SPCN3. BR and SAHP phases were the lowest amount in SPCN1 ( Figure 3 and Table 2) and non-uniformly distributed with some spaces between two needle particles of treated film (Figure 1b) which was dissolved as well as there is possibility that the corrosion products are porous. The SPCN3 shows the lowest magnitude in the complex-plane impedance plots among all coatings owing to the dissolution of BR and SAHP film. SAHP film is acidic in nature and reduced the pH of NaCl solution which enhances the dissolution of coating as well as corrosion products. Thus, it shows deterioration of coatings at a longer duration of exposure. On the other hand, SPCN2 dramatically enhances the corrosion resistance properties as observed in complex-plane impedance plots (Figure 4d) after 89 days of exposure might be attributed to the transformation of corrosion products/film into adherent and protective film which stifle the ingress of aggressive ions while in the case of AC sample, the protective corrosion products fill out the porosity and do not allow to ingress the solution. The magnitude of two semicircles i.e., a smaller one at higher frequency and bigger one from middle to lower studied frequency. A second semi-circle at lower frequency, the magnitude in the complex-plane impedance plots of AC, SPCN1, and SPCN2 is greater attributed to the nature of corrosion products than the first semi-circle which reveal the characteristics of coating. Thus, it can be proposed that a corrosion reaction occurred via coating/treated and solution interface as well as corrosion products/solution interface. It means the corrosion phenomena consists of two EECs. It will be described in subsequence paragraphs.
The modulus-frequency Bode plots of the coating with exposure periods in 3.5 wt.% NaCl solution are shown in Figure 5. From Figure 5a it is found that AC shows the lowest total impedance value at 0.01 Hz but as the concentration of NaH 2 PO 4 is increased with 0.1 M Ca(NO 3 ) 2 , the impedance value increased gradually after 1 h of exposure in 3.5 wt.% NaCl solution. The treated coatings exhibit almost 2 times higher impedance values compared to the AC sample. It is attributed to the filling ability of defects by BR and SAHP film which reduces the ingress of the solution. SPCN3 shows highest impedance values (Figure 5a) after 1 h of exposure at 0.01 Hz owing to the deposition of thicker film as shown in the SEM image (Figures 1d and 2d). As the exposure periods are extended from 1 h to 11 days, the total impedance values at 0.01 Hz of the coatings increased two times (Figure 5b). For the reaction of coating/treated sample, it requires some time to react with the solution. Therefore, 11 days is the duration when all samples properly reacted and form the corrosion products.
It is observed that after 41 days of exposure, all samples exhibit increases in the impedance values except SPCN3 (Figure 5c). SPCN3 shows the lowest impedance value exposed to 3.5 wt.% NaCl solution owing to the dissolution of SAHP film which make the solution acidic. AC, SPCN1, and SPCN2 exhibit more than 11 times higher impedance compared to SPCN3. The increase in impedance values of AC samples is attributed to the deposition of stable and uniform corrosion products which fill out the pores and reduce the ingress of solution towards the surface. Once the exposure periods are extended up to 89 days, the total impedance value of AC and SPCN2 increased dramatically due to the deposition of sparingly soluble corrosion products onto the coating surface which stifle the ingress of the solution while SPCN1 is decreased (Figure 5d) compared to 41 days. In the case of SPCN1, there is a possibility that BR and SAHP have dissolved and deposited the defective corrosion products onto the coating surface. Therefore, the total impedance value is less compared to AC and SPCN2. The amount of BR and SAHP in SPCN1 was minimum which did not influence in pH reduction of the studied solution. However, in the case of SPCN3, the amount of these phases were the maximum and active in nature which might be dissolved in the studied solution and result in lowering of pH as well as impedance value. The SPCN2 sample steadily dissolve and uniformly cover the surface thus, higher total impedance is observed at 0.01 Hz (Figure 5d). The total impedance value of AC, SPCN1, and SPCN2 is found to be increased by 11, 8, and 12 times compared to SPCN3 sample, respectively.
The phase-frequency Bode plots of the coatings with exposure periods in 3.5 wt.% NaCl solution are illustrated in Figure 6. It is observed that SPCN1 and SPCN2 exhibit one time constant around −52 • on 11 and 71 Hz, respectively, owing to the deposition of treatment film while AC and SPCN3 show two different time constants at different frequencies ( Figure 6a). Middle frequency attributed to the treatment/corrosion products while lower frequency shows the characteristics of the coating [34,[60][61][62][63]]. The SPCN3 sample shows highest shifting in phase angle maxima at −62 • on 120 Hz while at lower frequency i.e., 0.03 Hz exhibit at −13 • . The AC sample shows 20 • phase angle shifting on 0.01 Hz which reveals that the coating is defective and the crack bearing surface enhances the ingress of aggressive ions from atmosphere/solution. As the exposure periods are extended from 1 h to 11 d, the phase angle maxima are shifted towards a higher angle in the middle frequency range (Figure 6b) owing to the deposition of corrosion products onto the surface. AC sample shows two time constants; one at −33 • on 70 Hz attributed to the corrosion products while another at −38 • on 0.32 Hz owing to the coating characteristics. This result suggests that coating as well as corrosion products of AC sample strengthen their properties with exposure periods in NaCl solution. Thus, increment in the impedance is observed compared to 1 h of exposure (Figure 5b). The treated coatings show shifting of maxima at a higher angle. The SPCN1 shows only one time constant in middle frequency ranges around −58 • attributed to the treatment or deposition of corrosion products. Although, in middle frequency ranges, scattering in data is observed owing to the defective corrosion products which causes capacitance. The SPCN2 and SPCN3 show two phase angle maxima, one at middle and another at lower frequency. The SPCN2 exhibit broadening in maxima at −43 • from 1800 to 18 Hz owing to the deposition of uniform corrosion products after reaction of BR and SAHP film with NaCl solution. At lower frequency i.e., 0.017 Hz, the phase angle maxima are shifted from −0.5 • to −7.5 • for 1 h to 11 days, respectively. It means the reaction of BR and SAHP help in improving the properties of coating as well as corrosion products. The SPCN3 shows the maxima around −58 • at 31 Hz with scattering which reveals that treatment/corrosion products are defective and causes capacitance. But broadening in the time constant is observed which helps in improvement of the impedance. However, the decrease in maxima after 11 days compared to 1 h is owing to the dissolution of defective BR and SAHP film during reaction with NaCl solution. It might be corrosion products distributed all over the surface but being defective at longer durations of exposure causes deterioration.
As the exposure periods are extended from 11 to 41 days, the phase angle maxima of all samples shifted towards higher angles except SPCN3 (Figure 6c). The decrease in phase angle maxima of SPCN3 owing to the dissolution of BR and SAHP film as well as deposition of defective corrosion products which was started to dissolve after 11 days of exposure. Thus, the coating itself is participating in the corrosion reaction. It is also observed that the phase angle maxima at lower frequency i.e., 0.01 Hz, is decreased compared to 11 days of exposure. This result indicates that BR and SAHP film is completely dissolved and the coating has started to participate in the corrosion reaction. It is attributed to the high amount of BR and SAHP which makes the studied solution acidic. The phase angle maxima of SPCN1 sample is around −62 • on 1.25 Hz which reveals that coating is providing protection rather than corrosion products. It might be due to less amount of BR and SAHP film which was dissolved and fill out the defects of the coating, but the corrosion products are not too protective. Thus, at longer durations of exposure i.e., 89 days, the impedance is decreased (Figure 5d) compared to 41 days. The AC and SPCN2 samples exhibit phase angle maxima in middle frequency ranges at −59 • which show the characteristics of corrosion products. But, SPCN2 shows broadening in maxima from 271 to 2 Hz which reveals that corrosion products are uniformly distributed. The phase maxima of AC and SPCN2 at 0.01 Hz shifted towards higher angles compared to earlier exposure periods. This result suggests that the deposition of corrosion products on these two samples strengthen the coating properties. After 89 days of exposure, the phase angle maxima of SPCN3 shifted at a lower angle around −34 • with broadening ( Figure 6d) which indicates that corrosion products are not helping anymore to stifle the penetration of solution. On the other hand, SPCN1 shows identical phase angle maxima around −62 • on 1.25 Hz (Figure 6d) as obtained after 41 days of exposure. It means there is no improvement in corrosion characteristics of the SPCN1 sample. AC and SPCN2 exhibit phase angle maxima around −61 • on 14 Hz and −57 • on 31 Hz after 89 days of exposure in 3.5 wt.% NaCl solution (Figure 6d) but at lower studied frequency i.e., 0.01 Hz, it is found to be around −33 • and −32 • , respectively. The shifting in maxima of AC, SPCN1, and SPCN2 at higher angles in middle frequency provide protection due to corrosion products while the lower studied frequency i.e., 0.01 Hz, is due to coating. The shifting in maxima of AC and SPCN2 at higher angle on 0.01 Hz would provide protection attributed to the coating. This result suggests that corrosion products as well as coating are participating in corrosion resistance. Thus, AC and SPCN2 show higher impedance compared to SPCN1 and SPCN3.
The electrical equivalent circuit (EEC) of the coatings exposed in 3.5 wt.% NaCl solution are shown in Figure 7. In Figure 7a, R s , R c/t , and CPE c/t represent the solution resistance, coating/treatment resistance, and constant phase element of coating/treatment, respectively. This EEC is suitable for SPCN1 after 1 h and 11 days as well as SPCN2 for 1 h of exposure in 3.5 wt.% NaCl solution whereas once the exposure periods are extended, another EEC would be involved because the treated layer and corrosion product both have participated in the corrosion reaction at the coating/solution interface. In the case of the AC sample, once the coating comes in contact with the solution, immediately it starts to deteriorate due to the presence of defects on the surface. Thus, two EECs would participate. One EEC for coating which causes resistance for coating (R c ) while another for charge transfer resistance (R ct ). This EEC is shown in Figure 7b. In this EEC, CPE ct is in series with R c/t while R ct is parallel (Figure 7b).   After fitting of EIS data in suitable EEC, electrochemical parameters were determined. The electrochemical parameters after fitting of EIS data in suitable EEC are shown in Table 3 and Figure 8. From Table 3, it can be seen that R s is found to be in between 16-31 Ω·cm 2 for all samples at different exposure periods. Due to the presence of defects on AC as well as treated coatings, constant phase element (CPE) is involved instead of pure capacitance. Thus, the effective CPE (Q eff ) can be calculated by imaginary impedance when n 1 [64]: where n, Z j , and f are the CPE exponent, imaginary impedance, and frequency, respectively. But, when n = 1 then Q eff becomes a capacitance (C eff ), and Equation (2) can be rewritten as: Thus, the corrosion characteristics of the coating between interfacial capacitance and the CPE coefficient (Q) can be calculated by Brug's equation [65] and others [66,67]: From Figure 8, it can be seen that R c/t of all samples is gradually increased with exposure periods except SPCN3 which shows a decrease in its value after 41 days of exposure. The detrimental nature of SPCN3 after 41 days of exposure might be attributed to the dissolution of BR and SAHP film in NaCl solution which makes the solution acidic thus, at longer duration of exposure R ct is also decreased ( Table 3). After 41 days of exposure, AC shows a higher R c value compared to SPCN1 and SPCN3 owing to the greater filling ability of defects by corrosion products which strengthen the coating properties. In the case of SPCN1, it can be said that the thin layer of BR and SAHP films have dissolved and the corrosion products have deposited onto the coating surface and simultaneously due to the dissolution of film, the solution become slightly acidic which hinders the formation of a stable corrosion product. Thus, R ct is decreased after 89 days of exposure in 3.5 wt.% NaCl solution ( Table 3). The resistance to treatment (R t ) value of SPCN2 is highest among all samples after 41 days of exposure ( Figure 8) and might be owing to the transformation of BR and SAHP film into a stable corrosion product. Thus, it can be said that 0.5 M NaH 2 PO 4 with 0.1 M Ca(NO 3 ) 2 i.e., SPCN2 is the optimum amount to give the highest corrosion resistance of Al coating. In this case, the formed BR and SAHP is neither higher nor lower to give the negative effect on corrosion of Al coating. It can be said that 0.1 M Ca(NO 3 ) 2 has the synergistic effect to get an adherent and stable oxide layer which protects the coating from corrosion. As the R c/t is increased, the C eff is decreased simultaneously (Figure 8). C eff represents the defectiveness of the coating surface. It can be seen from SEM images (Figures 1a and  2a) that initially the AC sample was highly defective, thus C eff is very high (Figure 8) for 1 h but once the exposure periods are increased, this value is decreased owing to the deposition of stable corrosion products which fill out the defects. Due to the greater filling ability of the coating after treatment, R t is very high in SPCN3 for 1 h and 11 days of exposure but this value is decreased from 41 to 89 days, thus C eff is increased (Figure 8). After 41 days of exposure, SPCN2 exhibited the highest R t and lowest C eff therefore, this treatment is the optimum for corrosion protection of Al coating at longer duration of exposure in 3.5 wt.% NaCl solution. Moreover, it can be suggested that during the initial period of exposure, the protection can be defined by filling ability of the coating but at longer duration it can be determined by nature of corrosion products. Thus, it is very important to characterize the nature of the corrosion product using SEM and XRD. The SEM and XRD results will be described in next section i.e., characterization of corrosion products. and SAHP is neither higher nor lower to give the negative effect on corrosion of Al coating. It can be said that 0.1 M Ca(NO3)2 has the synergistic effect to get an adherent and stable oxide layer which protects the coating from corrosion. As the Rc/t is increased, the Ceff is decreased simultaneously (Figure 8). Ceff represents the defectiveness of the coating surface. It can be seen from SEM images (Figures 1a and 2a) that initially the AC sample was highly defective, thus Ceff is very high (Figure 8) for 1 h but once the exposure periods are increased, this value is decreased owing to the deposition of stable corrosion products which fill out the defects. Due to the greater filling ability of the coating after treatment, Rt is very high in SPCN3 for 1 h and 11 days of exposure but this value is decreased from 41 to 89 days, thus Ceff is increased (Figure 8). After 41 days of exposure, SPCN2 exhibited the highest Rt and lowest Ceff therefore, this treatment is the optimum for corrosion protection of Al coating at longer duration of exposure in 3.5 wt.% NaCl solution. Moreover, it can be suggested that during the initial period of exposure, the protection can be defined by filling ability of the coating but at longer duration it can be determined by nature of corrosion products. Thus, it is very important to characterize the nature of the corrosion product using SEM and XRD. The SEM and XRD results will be described in next section i.e., characterization of corrosion products.
The nc/t gives some information about the surface homogeneity of coating/treatment. Initially, the nt value of SPCN3 is higher due to uniform and homogenous deposition of treated film, but it is gradually decreased with exposure periods due to the dissolution of film (Table 3). AC exhibits the lowest nc value during initial periods of exposure which indicates that the surface is non-uniform, uneven and non-homogenous. On the other hand, nc/t value of AC, SPCN1, and SPCN2 is gradually increased with exposure periods and it is found that SPCN2 shows 0.79 after 89 days of exposure which reveals that the coating becomes homogenous. The Rct of SPCN3 is gradually increased up to 11 days due to deposition of corrosion product but nct is lower which indicates that corrosion products are defective and it might enhance the deterioration at a longer duration of exposure. It is observed from Table 3 that Rct and nct of SPCN3 is decreased after 41 days of exposure. The Rct and nct value of AC and SPCN2 are increased as well as Qct decreased after 11 days of exposure owing to the deposition of protective, uniform, and homogenous corrosion products.  The n c/t gives some information about the surface homogeneity of coating/treatment. Initially, the n t value of SPCN3 is higher due to uniform and homogenous deposition of treated film, but it is gradually decreased with exposure periods due to the dissolution of film (Table 3). AC exhibits the lowest n c value during initial periods of exposure which indicates that the surface is non-uniform, uneven and non-homogenous. On the other hand, n c/t value of AC, SPCN1, and SPCN2 is gradually increased with exposure periods and it is found that SPCN2 shows 0.79 after 89 days of exposure which reveals that the coating becomes homogenous. The R ct of SPCN3 is gradually increased up to 11 days due to deposition of corrosion product but n ct is lower which indicates that corrosion products are defective and it might enhance the deterioration at a longer duration of exposure. It is observed from Table 3 that R ct and n ct of SPCN3 is decreased after 41 days of exposure. The R ct and n ct value of AC and SPCN2 are increased as well as Q ct decreased after 11 days of exposure owing to the deposition of protective, uniform, and homogenous corrosion products.

Potentiodynamic Polarization Results
The potentiodynamic polarization plots of coatings after 89 days of exposure in 3.5 wt.% NaCl solution are shown in Figure 9. SPCN3 sample shows hydrogen evolution reaction at cathodic side might be owing to dissolution of SAHP film which is acidic in nature. The oxygen reduction reaction can be seen in AC, SPCN1, and SPCN2 due to deposition of oxide films/corrosion products onto the surface. The highest cathodic current density is observed in SPCN3 while the lowest is observed in SPCN2. It is attributed to the nature of corrosion products where the stable oxide film blocks the cathodic reaction [45]. There is sudden increment in anodic current density found on SPCN3 after corrosion potential (E corr ) which indicates that there is a possibility to form a heavy pit. The correlation of this statement will be described on the basis of SEM results of corrosion products. It can be seen from Figure 9 that SPCN3 shows mass transfer resistance caused on 400 µA·cm −2 from −0.386 V to 0.021 V vs. Ag/AgCl where anodic current density is stabilized. The anodic current density of SPCN1 is increased on active open circuit potential (OCP). AC, SPCN1, and SPCN2 samples show passive behavior at anodic scanning due to the deposition of stable corrosion products/oxide layer. The formation of passive film is more prominent on SPCN2 followed by AC and SPCN1 which might be attributed to the transformation of unstable corrosion products into stable oxide. The anodic current density of SPCN2 is the lowest then followed by AC, SPCN1, and SPCN3 which indicates that SPCN3 is more active to corrosion at a longer duration of exposure in 3.5 wt.% NaCl solution. The potentiodynamic polarization plots of coatings after 89 days of exposure in 3.5 wt.% NaCl solution are shown in Figure 9. SPCN3 sample shows hydrogen evolution reaction at cathodic side might be owing to dissolution of SAHP film which is acidic in nature. The oxygen reduction reaction can be seen in AC, SPCN1, and SPCN2 due to deposition of oxide films/corrosion products onto the surface. The highest cathodic current density is observed in SPCN3 while the lowest is observed in SPCN2. It is attributed to the nature of corrosion products where the stable oxide film blocks the cathodic reaction [45]. There is sudden increment in anodic current density found on SPCN3 after corrosion potential (Ecorr) which indicates that there is a possibility to form a heavy pit. The correlation of this statement will be described on the basis of SEM results of corrosion products. It can be seen from Figure 9 that SPCN3 shows mass transfer resistance caused on 400 µA·cm −2 from −0.386 V to 0.021 V vs. Ag/AgCl where anodic current density is stabilized. The anodic current density of SPCN1 is increased on active open circuit potential (OCP). AC, SPCN1, and SPCN2 samples show passive behavior at anodic scanning due to the deposition of stable corrosion products/oxide layer. The formation of passive film is more prominent on SPCN2 followed by AC and SPCN1 which might be attributed to the transformation of unstable corrosion products into stable oxide. The anodic current density of SPCN2 is the lowest then followed by AC, SPCN1, and SPCN3 which indicates that SPCN3 is more active to corrosion at a longer duration of exposure in 3.5 wt.% NaCl solution. The electrochemical parameters are extracted after the fitting of potentiodynamic polarization plots into Tafel slopes and the results are shown in Table 4. The corrosion potential (Ecorr) of the SPCN3 is found to be −0.722 V vs. Ag/AgCl. This result suggests that almost all treated film has dissolved after 89 days of exposure in 3.5 wt.% NaCl solution. It is attributed to the highly acidic nature of the treated film. The amount of BR and SAHP is highest in the SPCN3 sample among all treated coating which make the 3.5 wt.% NaCl solution acidic resultant to dissolution of Al coating. Al is amphoteric in nature, thus it can be dissolved in acidic medium. Therefore, at the cathodic side, a hydrogen evolution reaction is observed (Figure 9). On the other hand, it is observed that SPCN1 and SPCN2 show Ecorr around −1.0 V vs. Ag/AgCl which is more active compared to SPCN3. This result suggests that 1 M NaH2PO4 with 0.1 Ca(NO3)2 i.e., SPCN3, is not beneficial for corrosion resistance at a longer duration of exposure in 3.5 wt.% NaCl solution but at a shorter duration i.e., up to 11 days it has shown highest impedance ( Figure 5) owing to the greater filling ability of defects. It is reported that if the coating shows Ecorr at −0.870 V vs. Ag/AgCl then such type of coating is considered as a sacrificial coating [68]. Since, in the present study, AC, SPCN1, and SPCN2 exhibit more than −0.870 V vs. Ag/AgCl, it indicates that these coatings are providing sacrificial protection to the steel even after 89 days of exposure in 3.5 wt.% NaCl solution. The corrosion current density (Icorr) of the SPCN3 is found to be highest among all coatings whereas SPCN2 shows the lowest in value (Table 4). The electrochemical parameters are extracted after the fitting of potentiodynamic polarization plots into Tafel slopes and the results are shown in Table 4. The corrosion potential (E corr ) of the SPCN3 is found to be −0.722 V vs. Ag/AgCl. This result suggests that almost all treated film has dissolved after 89 days of exposure in 3.5 wt.% NaCl solution. It is attributed to the highly acidic nature of the treated film. The amount of BR and SAHP is highest in the SPCN3 sample among all treated coating which make the 3.5 wt.% NaCl solution acidic resultant to dissolution of Al coating. Al is amphoteric in nature, thus it can be dissolved in acidic medium. Therefore, at the cathodic side, a hydrogen evolution reaction is observed (Figure 9). On the other hand, it is observed that SPCN1 and SPCN2 show E corr around −1.0 V vs. Ag/AgCl which is more active compared to SPCN3. This result suggests that 1 M NaH 2 PO 4 with 0.1 Ca(NO 3 ) 2 i.e., SPCN3, is not beneficial for corrosion resistance at a longer duration of exposure in 3.5 wt.% NaCl solution but at a shorter duration i.e., up to 11 days it has shown highest impedance ( Figure 5) owing to the greater filling ability of defects. It is reported that if the coating shows E corr at −0.870 V vs. Ag/AgCl then such type of coating is considered as a sacrificial coating [68]. Since, in the present study, AC, SPCN1, and SPCN2 exhibit more than −0.870 V vs. Ag/AgCl, it indicates that these coatings are providing sacrificial protection to the steel even after 89 days of exposure in 3.5 wt.% NaCl solution. The corrosion current density (I corr ) of the SPCN3 is found to be highest among all coatings whereas SPCN2 shows the lowest in value (Table 4). Table 4. Electrochemical parameters of coatings extracted after fitting of potentiodynamic plots in Tafel regions exposed to 3.5% NaCl solution. The corrosion rate of the sample was calculated using following equation [69]:

Sample ID
where I corr , E.W., and d represent corrosion current density (µA/cm 2 ) obtained from dividing the total surface area of the working electrode by the corrosion current (µA), the equivalent weight (g/mol), and the density (g/cm 3 ) of Aluminum, respectively. The corrosion rate (µm·year −1 ) of the coatings is shown in Table 4. From this table it is confirmed that SPCN3 has the highest corrosion rate i.e., 208.52 µm·year −1 and lowest to be found on SPCN2. The corrosion rate of SPCN2 is 30% lower whereas SPCN1 and SPCN3 exhibited 21.53% and 379.47% higher, respectively compared to AC. Thus, it can be suggested that 0.5 M NaH 2 PO 4 with 0.1 M Ca(NO 3 ) 2 i.e., SPCN2 is the optimum amount for corrosion resistance of Al coating deposited by arc thermal spray coating process. The highest and lowest corrosion rate of the coatings can be correlated with morphology and phases present in corrosion products. Therefore, in the subsequent paragraphs, we have characterized the corrosion products using SEM and XRD.

SEM of the Corrosion Products
The SEM of the corrosion product formed onto the coating surface after potentiodynamic polarization studies are shown in Figure 10. It can be seen from Figure 10a that AC sample contain regular and condensed globular particles of corrosion products which covered all over the surface, but some cracks can be observed because potentiodynamic polarization is a destructive experiment where the development of crack is possible. Thus, it shows cracks on the surface. The SEM images of corrosion products formed on treated samples are shown in Figure 10b-d. Figure 10b shows that corrosion products are coagulated in the center but in periphery of the corrosion products, space is observed which causes to ingress of solution. Thus, corrosion rate is higher compare to AC. Once the NaH 2 PO 4 concentration is increased from 0.1 to 0.5 M with 0.1 M Ca(NO 3 ) 2 i.e., SPCN2, the corrosion products are uniformly distributed over the surface of coating (Figure 10c) with compact and adherent in nature characteristics which stifle the attack of aggressive ions from solution and atmosphere. The particle size of the corrosion products is smaller compare to AC and SPCN1 which completely cover all over the surface thus, the lowest corrosion rate is observed. It is attributed to the transformation of BR and SAHP into stable corrosion products. On the other hand, SPCN3 exhibits very big cracks perpendicular to the coating (Figure 10d) which allows the penetration of the solution and reaches towards the steel substrate and causes heavy corrosion. This result correlates with potentiodynamic polarization results (Figure 9) where the anodic current density was suddenly increased during anodic scanning which attributed to the pits formation. The diameter of the cracks is around 10 µm where the smaller particles of corrosion products are filled. After the treatment of Al coating with SPCN3, fine cracks were developed (Figure 1d) but once it was exposed to NaCl solution, the cracks are propagated and enhanced the corrosion rate at a longer duration. Thus, highest corrosion rate is observed after 89 days of exposure in 3.5 wt.% NaCl solution (Table 4).
Ca(NO3)2 is remaining in the corrosion products which might help in the transformation of corrosion products. It means Ca(NO3)2 has a synergistic effect on transformation of corrosion products into a stable form. The amount of Cl in SPCN3 and SPCN1 is very high which causes pitting corrosion, thus, SEM images of the corrosion products of these treated coatings exhibit pit formation (Figure 10b,d). P and Ca in corrosion products of SPCN2 are the highest which means that these elements are entrapped in corrosion products and help in formation of stable corrosion products. The presence of Na and Cl shows that NaCl was deposited in corrosion products of all coatings. However, the P and Ca amount is reduced (Table 5) in corrosion products of all treated samples compared to treatment (Table 1). This result suggests that BR and SAHP have dissolved and transformed into another form. High amounts of O reveal that corrosion products contain either Al2O3 or Al(OH)3. Thus, XRD is performed to know the phases formed in corrosion products. The EDS analysis of the corrosion products formed on coating surfaces are shown in Table 5. The element present on corrosion products of AC sample contain O, Al, Na, and Cl. Na and Cl are attributed to the NaCl solution whereas O and Al are owing to the corrosion products. This result suggests that the corrosion products contain NaCl, Al, and oxides or hydroxides of Al. Therefore, XRD is needed to characterize the corrosion products which will be described in subsequent paragraph. N is found to be between 1.24% to 1.31% in corrosion products of all treated coatings. This amount is almost identical as found after treatment (Table 1). This result suggests that N from Ca(NO 3 ) 2 is remaining in the corrosion products which might help in the transformation of corrosion products. It means Ca(NO 3 ) 2 has a synergistic effect on transformation of corrosion products into a stable form. The amount of Cl in SPCN3 and SPCN1 is very high which causes pitting corrosion, thus, SEM images of the corrosion products of these treated coatings exhibit pit formation (Figure 10b,d). P and Ca in corrosion products of SPCN2 are the highest which means that these elements are entrapped in corrosion products and help in formation of stable corrosion products. The presence of Na and Cl shows that NaCl was deposited in corrosion products of all coatings. However, the P and Ca amount is reduced (Table 5) in corrosion products of all treated samples compared to treatment (Table 1). This result suggests that BR and SAHP have dissolved and transformed into another form. High amounts of O reveal that corrosion products contain either Al 2 O 3 or Al(OH) 3 . Thus, XRD is performed to know the phases formed in corrosion products. XRD results of the corrosion products are shown in Figure 11. It is found that all samples show Al, NaCl, and α-Al(OH) 3 . Al is present due to the coating whereas NaCl is found because the coating was exposed in 3.5 wt.% NaCl solution. Thus, there is possibility to deposit the NaCl in corrosion products. The presence of α-Al(OH) 3 in treated coating might have occurred via the following reaction [32,33] XRD results of the corrosion products are shown in Figure 11. It is found that all samples show Al, NaCl, and α-Al(OH)3. Al is present due to the coating whereas NaCl is found because the coating was exposed in 3.5 wt.% NaCl solution. Thus, there is possibility to deposit the NaCl in corrosion products. The presence of α-Al(OH)3 in treated coating might have occurred via the following reaction [32,33] The BR and SAHP react with water and form Al(OH)3, NaOH, Ca(OH)2, and H3PO4. Al(OH)3 is identified as α-Al(OH)3 (bayerite). Bayerite is thermodynamically stable which plays an important role in the reduction of corrosion rate. Thus, it is important to determine the volume fraction of phases present in the corrosion products. Volume fraction of each phase identified by XRD in corrosion products are shown in Table 6. AC sample shows higher NaCl compared to SPCN1 and SPCN2 owing to the absence of treatment layer. In this case, there is the possibility that corrosion products and NaCl both fill out the defects of the coating. The SPCN2 sample exhibits 43.95% α-Al(OH)3 which is highest compared to the others. Thus, it shows the least corrosion rate ( Table 4). The SPCN3 shows least percentage of α-Al(OH)3 thus, it shows highest corrosion rate. AC sample shows the lowest Al owing to the deposition of NaCl and α-Al(OH)3 in the corrosion products. The amount of α-Al(OH)3 is greater than SPCN1 and SPCN3 and lesser than SPCN2. Therefore, it shows lesser corrosion rate compared to SPCN1 and SPCN3.  The BR and SAHP react with water and form Al(OH) 3 , NaOH, Ca(OH) 2 , and H 3 PO 4 . Al(OH) 3 is identified as α-Al(OH) 3 (bayerite). Bayerite is thermodynamically stable which plays an important role in the reduction of corrosion rate. Thus, it is important to determine the volume fraction of phases present in the corrosion products. Volume fraction of each phase identified by XRD in corrosion products are shown in Table 6. AC sample shows higher NaCl compared to SPCN1 and SPCN2 owing to the absence of treatment layer. In this case, there is the possibility that corrosion products and NaCl both fill out the defects of the coating. The SPCN2 sample exhibits 43.95% α-Al(OH) 3 which is highest compared to the others. Thus, it shows the least corrosion rate ( Table 4). The SPCN3 shows least percentage of α-Al(OH) 3 thus, it shows highest corrosion rate. AC sample shows the lowest Al owing to the deposition of NaCl and α-Al(OH) 3 in the corrosion products. The amount of α-Al(OH) 3 is greater than SPCN1 and SPCN3 and lesser than SPCN2. Therefore, it shows lesser corrosion rate compared to SPCN1 and SPCN3.

Conclusions
From the above results and discussion the following conclusions can be drawn: • The treatment of Al coating exhibited reduction in defects by 19%, 38%, and 71% for SPCN1, SPCN2, and SPCN3, respectively compared to AC.

•
After treatment with different concentrations of NaH 2 PO 4 and 0.1 M Ca(NO 3 ) 2 , brushite and sodium Aluminum hydrogen phosphate (SAHP) composite oxide film was formed on the coating surface. Due to the formation of SAHP film on treated coating, it exhibits cracking.

•
The EIS results show that initially SPCN3 exhibited highest R t value followed by SPCN2, SPCN1, and AC, but at longer durations of exposure it shows least in value owing to the dissolution of the treated film. High amounts of SAHP make the solution acidic which enhances the deterioration of the coating in 3.5 wt.% NaCl solution.

•
After 89 days of exposure, SPCN2 shows highest R t and R ct values whereas SPCN3 is the lowest owing to the deposition of stable and protective corrosion products. • SPCN2 shows lowest corrosion rate whereas SPCN3 is the highest. Funding: There is no external funding for this research.