In Situ Biosynthesis of Reduced Alpha Hematite (α-Fe2O3) Nanoparticles by Stevia Rebaudiana L. Leaf Extract: Insights into Antioxidant, Antimicrobial, and Anticancer Properties

In the present study, we utilized Stevia rebaudiana L. (SRLe) extract to in situ biosynthesize nanoscale alpha hematite (α-Fe2O3) nanoparticles (NPs) with potent antioxidant, antimicrobial, and anticancer properties. SRLe-α-Fe2O3 was characterized using physiochemical analyses, including UV/Vis, FTIR, XRD, DLS, EDX, SEM, and TEM studies. Among tested solvents, CHCl3/MeOH (2:1 v/v) SRL extract (least polar solvent) contained the highest EY, TPC, and antioxidant capacity of ~3.5%, ~75 mg GAE/g extract, and IC50 = 9.87 ± 0.7 mg/mL, respectively. FTIR confirmed the engagement of coating operation to the colloidal α-Fe2O3 NPs. TEM, SEM, and DLS revealed that SRLe-α-Fe2O3 has a spherical shape, uniform size distribution with aggregation for an average size of ~18.34 nm, and ζ = −19.4 mV, forming a repulsive barrier that helped to improve stability. The synthesized nanoparticles displayed considerable antibacterial activity against E. coli and S. aureus bacterial growth, and exhibited superior activity against the A549 lung cancer cell lines. These findings indicate that the increased availability of bioactive substances with antioxidant properties of SRLe makes it a potentially interesting material for the preparation of biologically active compounds and green synthesis of nanoparticles.


Introduction
Plants are a treasure trove of natural bioactive compounds represented in their secondary metabolites and antioxidants [1]. Stevia rebaudiana L. (S. rebaudiana) is a perennial herb [2]; its leaves have rich contents of phenolic compounds such as phenolic acids, flavonoids, proteins, vitamins, and essential and nonessential fatty acids [3]. Various studies have reported new phenol and polyphenol compounds identified as flavonoids and glycosides in Stevia leaves, indicating the importance of the nutritive structure of S. rebaudiana (Figure 1) [4].
Phenolic compounds are amphipathic molecules, having a peculiar chemical composition with at least one aromatic ring, in addition to one or more attached hydroxyl groups. They have variable molecular weights, with a huge number of subgroups distinguished as The availability of bioactive substances with antioxidant/reducing properties makes S. rebaudiana a potentially interesting raw material for the preparation of bioactive compounds and green synthesis of nanoparticles [8]. On the other hand, in recent years, magnetite NPs, mainly Fe 3 O 4 , have generated extreme interest in biomedical applications for magnetic separation and resonance imaging, drug delivery, engineering of tissue, tracking of cells, bio-separation, and magnetic hyperthermia [9].
Several studies have proven that attached antioxidants on the nanoparticle surface increase antioxidant activity and bioavailability for long periods. Thus, the nanoparticles must have biocompatibility and a high saturation of magnetic and surface interaction [10]. Moreover, Fe 3 O 4 nanoparticles are comparatively safe, do not accumulate in bio-organs. and are quickly eliminated from the body, as shown by in vivo studies [11].
Magnetic IONPs have prominent antioxidant activity against oxidative damage-related diseases [12,13]. However, the antioxidant activity of nanomaterials is strongly influenced by many factors, such as chemical composition, particle size, surface charge, and coating of the surface [14,15]. The surface coating should be nontoxic and biocompatible, enabling delivery of the targeted drug [16,17]. Studies have elucidated that antioxidants attached to the surface of nanomaterials induce antioxidant activity and bioavailability [10,18].
Furthermore, the antioxidant activity of either single or bimetallic combination synthesized nanocomposites via chemical or green techniques utilizing various phytochemicals (leaf extracts) was also evaluated [19]. Nanoparticles present many advantages compared to traditional antioxidant delivery methods, which include raising the bioavailability and environmental protection of the bioactive components, targeted delivery of antioxidants, and controlled freeing at the site of action [15]. Engineered nanostructured particles have recently been considered an innovative strategy to provide novel antioxidants with enhanced characteristics. Nanoparticles enhance the natural antioxidant enzyme activity by providing increased target delivery of compounds that show poor permeation across cell membranes and inadequate cell internalization [20]. However, limited studies are available regarding the biological synthesis of nanoscale alpha hematite (α-Fe 2 O 3 ) and its application as an antimicrobial and anticancer agent. Hence, this study aims to investigate the size-controlled green synthesis process using SRLe and the surface functionalization synthesis of nanoscale alpha hematite (α-Fe 2 O 3 ) NPs via in situ oxidation-precipitation methods, along with the prediction of biological activities, antimicrobial activities, and anticancer. Furthermore, this is the ever first report to elucidate the phytochemicals in S. rebaudiana plant extract and to synthesize S. rebaudiana leaf extract-mediated α-Fe 2 O 3 NPs with provden antibacterial and anticancer efficacy. A schematic representation of the present study is clearly depicted in Figure 2. zyme activity by providing increased target delivery of compounds that show poor permeation across cell membranes and inadequate cell internalization [20]. However, limited studies are available regarding the biological synthesis of nanoscale alpha hematite (α-Fe2O3) and its application as an antimicrobial and anticancer agent. Hence, this study aims to investigate the size-controlled green synthesis process using SRLe and the surface functionalization synthesis of nanoscale alpha hematite (α-Fe2O3) NPs via in situ oxidationprecipitation methods, along with the prediction of biological activities, antimicrobial activities, and anticancer. Furthermore, this is the ever first report to elucidate the phytochemicals in S. rebaudiana plant extract and to synthesize S. rebaudiana leaf extract-mediated α-Fe2O3 NPs with provden antibacterial and anticancer efficacy. A schematic representation of the present study is clearly depicted in Figure 2.

Effect of Solvent Polarity on Extraction Yield (EY) and TPC of S. Rebaudiana L. Extracts (SRLe)
It is well known that the EY of bioactive chemical compounds relies on various factors, including the types of solvents with varying polarities, pH, time, and extraction temperature, in addition to the chemical installation of the basic samples. Under the same time and temperature conditions, the solvent and the chemical properties of the sample are the two most important factors [21]. In this study, three solvents were tested to estimate the EY and TPC from various SRLe parts (leaves, stems, and roots). The results are shown in Table 1 and Figure 3A, B. Among the tested solvents, CHCl3/MeOH (2:1 v/v) leaf extract (least polar solvent) contained the highest EY and TPC of ~3.5% and ~75 mg GAE/g extract. AcOH root extract (most polar solvent) contained the lowest EY and TPC of ~2.2% and ~55.6 mg GAE/g extract. EtOAc stem extract exhibited an EY and TPC of ~2.7% and

Effect of Solvent Polarity on Extraction Yield (EY) and TPC of S. rebaudiana L. Extracts (SRLe)
It is well known that the EY of bioactive chemical compounds relies on various factors, including the types of solvents with varying polarities, pH, time, and extraction temperature, in addition to the chemical installation of the basic samples. Under the same time and temperature conditions, the solvent and the chemical properties of the sample are the two most important factors [21]. In this study, three solvents were tested to estimate the EY and TPC from various SRLe parts (leaves, stems, and roots). The results are shown in Table 1 and Figure 3A, B. Among the tested solvents, CHCl 3 /MeOH (2:1 v/v) leaf extract (least polar solvent) contained the highest EY and TPC of~3.5% and~75 mg GAE/g extract. AcOH root extract (most polar solvent) contained the lowest EY and TPC of~2.2% and~55.6 mg GAE/g extract. EtOAc stem extract exhibited an EY and TPC of~2.7% and~64 mg GAE/g extract, respectively. These outcomes are consistent with previously reported results by Kim et al. [22]. However, these findings also indicate that the extraction efficiency depends on the polarity of the solvents. The significant modifications in the content of TPC in Stevia extract confirmed that the chemical polarity properties of the solvent influenced the qualitative structure and physicochemical activity of the extracts, as confirmed in a previous report by Bęben et al. [23]. vent influenced the qualitative structure and physicochemical activity of the extracts, as confirmed in a previous report by Bęben et al. [23].

Antioxidant Activity
Extraction solvents affect the EY and the TPC, thus significantly affecting the biological activity of the extract [24]. The antioxidant activities of SRLe were indexed according to the DPPH radical-scavenging activity ( Figure 3C). The inferences showed that all samples possessed varying antioxidant and free-radical-scavenging activities. Among the

Antioxidant Activity
Extraction solvents affect the EY and the TPC, thus significantly affecting the biological activity of the extract [24]. The antioxidant activities of SRLe were indexed according to the DPPH radical-scavenging activity ( Figure 3C). The inferences showed that all samples possessed varying antioxidant and free-radical-scavenging activities. Among the tested extracts, CHCl 3 /MeOH (2:1 v/v) leaf extract had significantly higher radical-scavenging activity with an IC 50 value of 12.87 ± 0.7mg/mL as compared to the EtOAc leaf extract, while AcOH root extract exhibited significantly lower radical-scavenging activity with IC 50 values of 20.07 ± 1.2 mg/mL and 36.54 ± 1.1 mg/mL, respectively, compared to the control (ascorbic acid, IC 50 = 11.2 ± 0.6 µg/mL). This behavior is similar to that reported by Criado et al. [25], Furthermore, Ruiz et al. [26] investigated the free-radical-scavenging activity of S. rebaudiana extracts at various doses. S. rebaudiana extract's radical-scavenging efficacy improved with increasing dose (25-625 mg/mL). The IC50 value was determined to be 335.94 g/mL. These findings suggest that the CHCl 3 /MeOH (2:1 v/v) extract of S. rebaudiana is a potentially strong antioxidant agent for the improvement of additional drugs. According to Kähkönen et al., S. rebaudiana extract may have higher antioxidant activities since it has a larger TPC [27].

Identification of Bioactive Phenolic Compounds of SRLe Using HPLC
HPLC currently represents the most popular and reliable technique for the analysis of phenolic compounds. Various supports and mobile phases are available for the analysis of phenolics including anthocyanin, proanthocyanins, hydrolysable tannins, flavonols, flavan-3-ols, flavanones, flavones, and phenolic acids in different plant extracts and food samples [28]. Under the current conditions, CHCl 3 /MeOH (2:1 v/v) of SRLe had a slightly higher phytochemical content accumulation than stems and roots. The peaks in the HPLC chromatogram of CHCl 3 /MeOH (2:1 v/v) leaf extract were identified by comparing the retention time and UV spectra of bioactive phenolic compounds in the sample with standards within 10 min. The HPLC results of bioactive phenolic content are listed in Table 2. Eight phenolic compounds were identified in the CHCl 3 /MeOH (2:1 v/v) extract according to HPLC chromatograms: ferulic acid, syringic acid, protocatechuic, catechin, coumaric acid, caffeic acid, gallic acid, and chlorogenic acid. As indicated in Table 2 and Figure 4, a substantial peaks of gallic acid, syringic acid, and coumaric acid, with concentrations of 13.483 µg/mL, 7.825 µg/mL, and 6.154 µg/mL, respectively, were found. According to Mynit et al. (2020), chlorogenic acids, isochlorogenic acids, and other hydroxycinnamic acids, make up the majority of the potential polyphenols in the leaves of S. rebaudiana (Bertoni) [29]. Many bioactive phenolic compounds have also been found in stevia leaves [4,30], presenting potential bioactivities, such as coumaric acid [4], catechin, gallic acid, syringic acid, and caffeic acid [31].
Antibiotics 2022, 11, x FOR PEER REVIEW 6 of 20 acids, make up the majority of the potential polyphenols in the leaves of S. rebaudiana (Bertoni) [29]. Many bioactive phenolic compounds have also been found in stevia leaves [4,30], presenting potential bioactivities, such as coumaric acid [4], catechin, gallic acid, syringic acid, and caffeic acid [31].  Dynamic light scattering (DLS) was used to measure the PS, PDI, and ζ-potential of bare SRLe-αFe2O3. The mean values recorded for all the systems showed a PS distribution in nanometers as shown in Figure 5. The size of SRLe-αFe2O3 was about ~19.60 ± 3.8 nm,  Dynamic light scattering (DLS) was used to measure the PS, PDI, and ζ-potential of bare SRLe-αFe 2 O 3 . The mean values recorded for all the systems showed a PS distribution in nanometers as shown in Figure 5. The size of SRLe-αFe 2 O 3 was about~19.60 ± 3.8 nm, while the PDI was 0.237 ( Figure 5A). Furthermore, a very narrowly distributed particle possesses PDI values of about 0.01-0.3, which is ideal for stability and uniformity of dispersion [32]. The stability of nanoparticles is generally predicted from their ζ-potential values; here, the ζ-potential value was determined to be −18.1 ± 1.6 mV for SRLe-αFe 2 O 3 ( Figure 5B). A ζ-potential value higher than −30 mV is considered to be stable due to electrostatic balance [33]. The negative ζ-potential charge of SRLe-αFe 2 O 3 could be attributed to the ionization of the phenolic hydroxyl groups in the capping moieties at alkaline pH [34], indicating good coating of magnetite iron surface cations through Fe-O linkage [35]. The high negative charge formed a repulsive barrier that helped to avoid the aggregation and improve the colloidal stability of SRLe-αFe 2 O 3.

Fourier-Transform Infrared Spectroscopy (FT-IR)
The FTIR showed a different vibration according to functional groups with a characteristic absorption in the IR region. FTIR spectroscopy is useful for detecting the characteristic peaks and functional groups of compounds. The FTIR spectrum of the extract is shown in Figure 6. The spectrum showed an -OH band in the frequency range 3200-3600 cm −1 , C-H stretching in the frequency range 2800-3000 cm −1 , C=O stretching at the frequency of 1628 cm −1 , and C-O stretching in the frequency range of 1050-1400 cm −1 . The presence of the -OH band and C=O stretching suggests that the constituents in the extract had -OH and C=O groups as functional groups. Phenolic and flavonoid compounds are compounds containing hydroxyl and carbonyl groups as functional groups [36]. These annotations affirm the existence of -OH moieties, which are capable of terminating the propagation of chain carrying radicals by acting as an H-atom donor. The C-OH group of phenols was responsible for the peak at 1160 cm −1 , indicating the presence of polyphenols such as terpenoids and flavonoids, which may also operate as bio-reducing agents. As a result, proteins can serve as both stabilizing and reducing agents. Fe-O nanoparticles were responsible for the peak at 770 cm −1 . These functional groups were observed on the surface of SRLe-αFe 2 O 3 NPs produced from leaf extracts of stevia plants. These results are in line with previous studies on green nanoparticle synthesis [37].
Antibiotics 2022, 11, x FOR PEER REVIEW 7 of 20 ( Figure 5B). A ζ-potential value higher than −30 mV is considered to be stable due to electrostatic balance [33]. The negative ζ-potential charge of SRLe-αFe2O3 could be attributed to the ionization of the phenolic hydroxyl groups in the capping moieties at alkaline pH [34], indicating good coating of magnetite iron surface cations through Fe-O linkage [35]. The high negative charge formed a repulsive barrier that helped to avoid the aggregation and improve the colloidal stability of SRLe-αFe2O3.

Fourier-Transform Infrared Spectroscopy (FT-IR)
The FTIR showed a different vibration according to functional groups with a characteristic absorption in the IR region. FTIR spectroscopy is useful for detecting the characteristic peaks and functional groups of compounds. The FTIR spectrum of the extract is shown in Figure 6. The spectrum showed an -OH band in the frequency range 3200-3600 cm −1 , C-H stretching in the frequency range 2800-3000 cm −1 , C=O stretching at the frequency of 1628 cm −1 , and C-O stretching in the frequency range of 1050-1400 cm −1 . The presence of the -OH band and C=O stretching suggests that the constituents in the extract had -OH and C=O groups as functional groups. Phenolic and flavonoid compounds are compounds containing hydroxyl and carbonyl groups as functional groups [36]. These annotations affirm the existence of -OH moieties, which are capable of terminating the propagation of chain carrying radicals by acting as an H-atom donor. The C-OH group of phenols was responsible for the peak at 1160 cm −1 , indicating the presence of polyphenols such as terpenoids and flavonoids, which may also operate as bio-reducing agents. As a result, proteins can serve as both stabilizing and reducing agents. Fe-O nanoparticles were responsible for the peak at 770 cm −1 . These functional groups were observed on the surface of SRLe-αFe2O3 NPs produced from leaf extracts of stevia plants. These results are in line with previous studies on green nanoparticle synthesis [37].

UV/Visible (UV/Vis) Spectroscopy Analysis
The coordination complex was validated as the absorption peak was identified at 390 nm using the UV/visible spectral analysis of the synthesized SRLe-αFe2O3 NPs ( Figure  7A). Our result coincides with previously published results [38,39]. Additionally, the single and strong peak at 390 nm in the UV/Vis absorption spectrum confirmed that the SRLe-αFe2O3 NPs had a spherical shape, similar to the findings of Kumar et al. (2022) [40].

XRD Analysis
The degree of crystallinity of the synthesized SRLe-αFe2O3 NPs was determined via powder XRD analysis. Figure 7B

UV/Visible (UV/Vis) Spectroscopy Analysis
The coordination complex was validated as the absorption peak was identified at 390 nm using the UV/visible spectral analysis of the synthesized SRLe-αFe 2 O 3 NPs ( Figure 7A). Our result coincides with previously published results [38,39]. Additionally, the single and strong peak at 390 nm in the UV/Vis absorption spectrum confirmed that the SRLe-αFe 2 O 3 NPs had a spherical shape, similar to the findings of Kumar et al. (2022) [40].

XRD Analysis
The degree of crystallinity of the synthesized SRLe-αFe 2 O 3 NPs was determined via powder XRD analysis. Figure 7B  The degree of crystallinity of the synthesized SRLe-αFe2O3 NPs was determined via powder XRD analysis. Figure 7B

Surface Properties
The size distribution and morphology are illustrated in Figures 8 and 9. SRLe-αFe2O3 was analyzed using TEM ( Figure 8A,B) and SEM ( Figure 9A-C) microscopy images matched to those obtained using DLS. Each TEM and SEM image showed particles with a spherical shape, uniform size distribution, and aggregation. The SRLe-αFe2O3 size distribution for functionalized magnetite NPs was uniform with an average size of ~18 ± 2.7 nm. Similar sizes of green synthesized silver nanoparticles using fresh Sida cordifolia

Surface Properties
The size distribution and morphology are illustrated in Figures 8 and 9. SRLe-αFe 2 O 3 was analyzed using TEM ( Figure 8A,B) and SEM ( Figure 9A-C) microscopy images matched to those obtained using DLS. Each TEM and SEM image showed particles with a spherical shape, uniform size distribution, and aggregation. The SRLe-αFe 2 O 3 size distribution for functionalized magnetite NPs was uniform with an average size of~18 ± 2.7 nm. Similar sizes of green synthesized silver nanoparticles using fresh Sida cordifolia extract were reported, with typical size diameters ranging from 15 to 18 nm [42]. Overall, prior results confirm that utilizing aqueous leaf extract of SRLe to synthesize alpha hematite nanoparticles is an eco-friendly and high-efficiency approach, as demonstrated in our current investigation.
Using energy0dispersive X-ray spectroscopy (EDX), the elemental mapping of the biogenic SRLe-αFe 2 O 3 was discovered. Oxygen (34.44%) and iron (65.56%) were both detected through EDX analysis, as shown in Figure 9C. Additionally, a strong peak at 6.44 keV was seen, suggesting the presence of iron (Fe), while another peak at 7.02 keV was attributed to the presence of iron (Fe) [43]. According to previous research, several elements discovered through EDX analysis, such as Si, Fe, and Cl, were revealed to behave as capping agents of biogenic αFe 2 O 3 [44].
Antibiotics 2022, 11, x FOR PEER REVIEW 9 of 20 extract were reported, with typical size diameters ranging from 15 to 18 nm [42]. Overall, prior results confirm that utilizing aqueous leaf extract of SRLe to synthesize alpha hematite nanoparticles is an eco-friendly and high-efficiency approach, as demonstrated in our current investigation. Using energy0dispersive X-ray spectroscopy (EDX), the elemental mapping of the biogenic SRLe-αFe2O3 was discovered. Oxygen (34.44%) and iron (65.56%) were both detected through EDX analysis, as shown in Figure 9C. Additionally, a strong peak at 6.44 keV was seen, suggesting the presence of iron (Fe), while another peak at 7.02 keV was attributed to the presence of iron (Fe) [43]. According to previous research, several elements discovered through EDX analysis, such as Si, Fe, and Cl, were revealed to behave as capping agents of biogenic αFe2O3 [44].

Antimicrobial Activity of SRLe-αFe 2 O 3 NPs According to Agar Well Diffusion Assay
Green synthesized nanoparticle suspensions of various concentrations were tested for antibacterial activity against E. coli and S. aureus using the well diffusion method. The ability of the antibacterial agent (NPs) is shown in Figure 10A,B, revealing that the synthesized nanoparticles clearly displayed antibacterial properties. The maximum effect was noted for S. aureus, while the minimum effect was noted for E. coli in a dose-dependent manner. For S. aureus, the zones of inhibition were 13 ± 0.4 mm and 18 ± 0.5 mm for the 10 mg/mL and 15 mg/mL doses, respectively, which almost doubled to an inhibition zone of 21.5 ± 0.8 mm for 30 mg/mL. No inhibition was detected at the 5 mg/mL dose. It has been reported that iron nanoparticles possess antibacterial properties due to their nanoscale size, which enables them to accumulate and deposit on the surface of bacteria during testing [45,46]. Additionally, plant extracts are also likely to possess antibacterial properties due to their high phytochemical content [47]. The activity against both Grampositive and Gram-negative bacteria of hematite (α-Fe 2 O 3 ) NPs can be explained by several possible mechanisms such as stability in an ambient environment, generation of ROS (superoxide radical anions (O 2 −), hydroxyl radicals (OH−), etc.), oxidative stress, and release of ions by nanoparticles reacting with the bacteria's thiol groups (-SH), which can alter the cellular structure of microorganisms, thus interrupting DNA reproduction and inhibiting enzyme and protein synthesis [48,49]. Furthermore, the NPs exhibited a moderate effect on both E. coli strains with inhibition zones of approximately 11 ± 1.3 mm and 16.5 ± 1.4 mm, respectively, at doses of 15 mg/mL and 30 mg/mL. At the same time, no inhibitions were detected at doses of 5 mg/mL and 10 mg/mL. These results were significantly similar to those of Bhuiyan et al. (2020), who reported no antibacterial efficiency for α-Fe 2 O 3 synthesized using a leaf extract of Carica papaya against E. coli strains at a concentration of 5 (mg/disc) [50]. A negatively charged bacterial surface might be disrupted and destabilized by the positively charged metal ions released by NPs, resulting in cell death. [51]. As a result, the nanoparticles were shown to have greater effectiveness against Gram-positive bacteria as compared to Gram-negative bacteria, potentially due to Gram-negative bacteria having an extra layer of lipopolysaccharide and peptidoglycan on top of their cell walls, granting them the ability to resist the damage caused by nanoparticles.
inhibitions were detected at doses of 5 mg/mL and 10 mg/mL. These results were significantly similar to those of Bhuiyan et al. (2020), who reported no antibacterial efficiency for α-Fe2O3 synthesized using a leaf extract of Carica papaya against E. coli strains at a concentration of 5 (mg/disc) [50]. A negatively charged bacterial surface might be disrupted and destabilized by the positively charged metal ions released by NPs, resulting in cell death. [51]. As a result, the nanoparticles were shown to have greater effectiveness against Grampositive bacteria as compared to Gram-negative bacteria, potentially due to Gram-negative bacteria having an extra layer of lipopolysaccharide and peptidoglycan on top of their cell walls, granting them the ability to resist the damage caused by nanoparticles.

Cytotoxicity Study
The cell viability and cytotoxic effect of different concentrations of SRLe-αFe 2 O 3 nanoparticles at 31.25 to 250 µg/mL was observed against A549 cells and Vero-derived kidney epithelia isolated from green monkeys; the results are shown in Figure 11A,B. The results clearly show that, in the absence of SRLe-αFe 2 O 3 NPs synthesized from the green species, 100% of the cell lines survived the damage. The treatment of A549 lung cancer cell lines with SRLe-αFe 2 O 3 NPs inhibited the proliferation of cell lines in a time-dependent and dose-dependent manner. It was observed that the morphology was not effectively destroyed when SRLe-αFe 2 O 3 NPs were used at low concentrations, with a complete loss of cells occurring at higher concentrations [52]. Nevertheless, the synthesized NPs exhibited high toxicity against the A459 cell line, with only 5.4% (IC 50 = 51.2 µg/mL) of the cells surviving after 48 h. Approximately similar results of synthesized αFe 2 O 3 nanoparticles using L-ascorbic acid as a reducing agent were reported by Kumar et al. (2022), with an IC 50 ≤30 µg/mL [53]. These outcomes may be explained by the usage of higher dosages of SRLe-αFe 2 O 3 NPs, leading to excessive production of ROS-mediated oxidative stress in the cell and, thus, DNA damage, as presented in previous investigations [54]. Furthermore, approximately 20-25% (IC 50 = 117.5 µg/mL) of the Vero cells survived when given the same SRLe-αFe 2 O 3 NPs up to a dose of 250 µg/mL. These results are similar to those of Bhuiyan et al. [50]. This suggests that cancer cells may be more vulnerable to ROS than normal cells and that ROS-mediated processes may be used to target cancer cells [55]. Because iron-based nanoparticles are a potent inducer of ROS, a sufficient quantity can selectively destroy tumor cells while also inhibiting their development. A459 cells are isolated from lung cancer cells; thus, nanoparticles can be utilized to cure cancer, as cancer cells have greater amounts of ROS and more oxidative DNA damage than normal cells in the same regions of tissue. Overall, the results of our investigation confirm that utilizing an aqueous leaf extract of Stevia rebaudiana L. to synthesize SRLe-αFe 2 O 3 NPs is an ecofriendly and high-efficiency approach.
The present study had some limitations that need to be addressed in the future. Firstly, the in vitro effect of the designed formulations needs to be evaluated on pre-established biofilms. Secondly, a lack of funding precluded the completion of an antibiotic resistance experiment on both bacteria tested. Future investigations will reveal whether the biosynthesized alpha hematite Fe 2 O 3 from Stevia leaf extract can exhibit synergism and disruptive effects on biofilm-based infection as a result of its effective antibacterial activity against established in this study. In addition, we recommend undertaking in vivo studies to demonstrate the efficacy of our designed formulations.
Antibiotics 2022, 11, x FOR PEER REVIEW The present study had some limitations that need to be addressed in the fut Firstly, the in vitro effect of the designed formulations needs to be evaluated on pre tablished biofilms. Secondly, a lack of funding precluded the completion of an antibi resistance experiment on both bacteria tested. Future investigations will reveal whe the biosynthesized alpha hematite Fe2O3 from Stevia leaf extract can exhibit synerg and disruptive effects on biofilm-based infection as a result of its effective antibacte activity against established in this study. In addition, we recommend undertaking in v studies to demonstrate the efficacy of our designed formulations.

Preparation of S. rebaudiana Samples
The S. rebaudiana materials were washed several times using ddH 2 O, and all parts (leaves, stems, and roots) were dried in the open air at room temperature. Lastly, a powder was obtained by grinding all parts mechanically before storing in polyethylene bags in a freezer at −4 • C until use.

Extraction of Phenolic Compounds from S. rebaudiana
TPCs were extracted following the method of Anokwuru et al. [56] with some modifications. Briefly, 10 g of each dried powder part was soaked in 100 mL of ethyl acetate, acetone, or CHCl 3 /MeOH (2:1 v/v) in conical flasks for 72 h at room temperature with shaking (Thermo Scientific™, MaxQ™ 420HP). Then, all samples were filtered through Whitman filter paper No 42 and concentrated under reduced pressure using a rotary evaporator in vacuo at 45 • C. Finally, the extracts were preserved in sterilized airtight, labeled bottles in a refrigerator at 4 • C until required for analysis.

Determination of Extraction Yield (EY)
The extraction yield (EY) was calculated as using the following formula: where WE is the weight of the extract after evaporating the solvent and freeze-drying, and DW is the dry weight of the sample.

Evaluation of TPC Using Folin-Ciocâlteu Assay
The TPC of the S. rebaudiana extracts was defined using the Folin-Ciocâlteu assay [57]. In brief, 200 µL of extract (10 mg/mL) was added to 2.0 mL of a solution of 10 mL of Na 2 CO 3 (2% w/v), 0.1 mL of CuSO 4 , and 0.1 mL of sodium and potassium tartrate, before mixing. Then, 0.4 mL of NaOH (0.5 M) was added after 4 min to the mixture, while 0.2 mL of Folin-Ciocâlteu reagent (1:1 v/v) was added after 10 min. Next, the solution was left for 30 min, and its absorbance was estimated using a UV/Vis spectrophotometer at 750 nm. The TPC was calculated as mm GAE using a GA standard curve.

Evaluation of Antioxidant Activity
The 2,2-diphenyl-1-picryl-hydrazyl (DPPH) radical-scavenging assay was carried out according to a previously reported method [58]. Briefly, 0.4 mL of Stevia extract was mixed with 3.6 mL of a methanol solution of DPPH (0.1 mM). An equal amount of 0.4 mL of methanol (0.004% w/v) was used as a blank with 3 mL of DPPH solution. All samples were evaluated in triplicate, vortexed for 3 min, and incubated in the dark for 35 min at 37 • C. The reduction in absorbance of each sample was measured against methanol as a blank on a UV spectrophotometer (Miltton Roy, Spectronic 1201) at 515 nm, and the data were recorded every minute for 16 min. The PI of the DPPH antioxidant activity was calculated using the following formula: Percentage inhibition (PI) = AC at t = 0 min − AT at t = 16 min AC at t = 0 min (2) where AC is the absorbance of the control, and AT is the absorbance of the sample + DPPH. The results were reported as the IC 50 value, with a lower value representing stronger DPPH scavenging capacity. An ascorbic acid standard curve was used as a positive control.

Evaluation of Total Phenolic Compound Using HPLC Assay
HPLC was carried out using a GBC 1100 Series HPLC system equipped with a UV detector [59]. Bioactive phenolic components were identified in SRLe using a C18 column (250 mm × 4.6 mm; 5 µm). The mobile phase consisted of 10.2% acetic acid in 2 mm sodium acetate (solvent A) and acetonitrile (solvent B). The flow rate was kept constant at 1 mL/min for a total run time of 10 min at 25 • C. The system was run with an isocratic program (70:30 B/A) The injection volume was 50 µL of CHCl 3 /MeOH (2:1 v/v) extract.

Biosynthesis of SRLe-αFe 2 O 3 Nanoparticles
SRLe-αFe 2 O 3 NPs were synthesized using ferric chloride (FeCl 3 ·6H 2 O), as described in [60]. Briefly, 40 mL of ferric chloride (2 mM) was placed in an Erlenmeyer flask and stirred for more than 1 h. SRLe solution (4 mL) was then added dropwise into the ferric chloride solution with vigorous stirring (200 rpm) at ambient room temperature (25-27 • C) for 4 h to allow the formation of SRLe-αFe 2 O 3 . Then, 1 M of NaoH was added until attaining pH 11. The solution eventually turned cloudy black. Subsequently, the solution was centrifuged at 12,000 rpm for 10 min and washed with dH 2 O to remove any impurities or absorbed ions. Finally, the product was dried at 60-70 • C for 48 h using a fan-assisted oven ( Figure 1A,B). The mean PS and ZP of the formulations were measured using DLS (Malvern Instruments, UK). For size estimation, 3 mL of bare SRLe-αFe 2 O 3 NPs were diluted in deionized water, placed in a cell cuvette, and scanned four times to get an average reading. The mean ± SD was obtained after three measurements.

Surface Morphology
The SRLe-αFe 2 O 3 NPs samples were imaged using transmission electron microscopy (TEM; TOPCON002B; Tokyo, Japan). Thin SRLe-αFe 2 O 3 NPs films were created on a carbon-coated copper grid by simply dropping a small quantity of sample on the grid, before blotting away any excess solution using blotting paper [61]. The optimized samples were imaged using scanning electron microscopy (SEM) (JSM 6390 ® , JEOL DATUM Ltd., Tokyo, Japan). A drop of SRLe-αFe 2 O 3 NPs was dried onto an aluminum grid under a mercury lamp for 5 min to obtain a coating thickness of 400 Å.

X-ray Fdiffraction (XRD)
XRD patterns of the as-synthesized SRLe-αFe 2 O 3 NPs were determined using a Rigaku D/Max-lllC X-ray diffractometer (Rigaku Int. Corp., Tokyo, Japan) at a voltage of 40 kV and a current of 40 kA. The patterns were recorded as a function of the 2θ angle in the range of 10 • −80 • with a step size of 0.01 • at a scanning rate of 0.02 steps/s with the help of a monochromatized X-ray beam with a copper filter (CuKα, λ = 1.54178 Å).

FTIR
The optical properties of SRLe-αFe 2 O 3 NPs were characterized using an FTIR spectrometer (JASCO FT-IR 4100 spectrometer, Hachioji, Tokyo, Japan) to inspect the functional groups contained in the prepared samples. Potassium bromide (KBr) was mixed with the prepared samples. A disc was loaded at high pressure and measured at a wavelength of 400-4000 cm −1 with a resolution of 4.0 cm −1 .

Antimicrobial Activity According to Agar Well Diffusion Assay
The well diffusion method was performed in triplicate according to the method in [63]. Briefly, the bacterial suspension was prepared and spread on Mueller-Hinton agar using a swab and then left for 5 min to dry. Next, five holes were created, with one of the pits containing the standard control erythromycin, while 100 µL of SRLe-αFe 2 O 3 NPs were added to each pit at successive concentrations (5, 10, 15, and 30 mg/mL), before incubating for 24 h at 37 • C. After incubation, zones of growth inhibition were measured to the nearest millimeter to determine the antimicrobial potency of the screened antimicrobial substances [64]. The results are expressed as the mean ± standard deviation (SD).

Cytotoxicity and Anticancer Studies
The cytotoxic assessment of A459 cells derived from lung cancer cells (ATCC CCL-185) and Vero cells isolated from kidney epithelia extracted from African green monkeys (ATCC CCL-81) were evaluated using the MTT assay (5 mg/mL in PBS). The medium from the wells was evacuated after incubation. Then, MTT (20 µL) was incorporated into each well along with 25 µL of SRLe-αFe 2 O 3 NPs (autoclaved). The cells were dissolved in 200 µL of DMSO (dimethyl sulfoxide). The absorbance spectra of the specimens were distinguished by recording the optical density at 560 nm and subtracting the background at 620 nm using a microplate reader [65].
where test denotes the cells exposed to the SRLe-αFe 2 O 3 NP sample, control denotes the control sample, and blank denotes the wells without Vero cells and A549 cells [66].

Statistical Analysis
Each experiment was carried out at least in triplicate, and all data were presented as the mean ± SD. Analysis of statistical significance was performed using one-way ANOVA and the post-hoc Tukey test (p < 0.05). All analysis was conducted using SAS 9.4 for Windows x64 from the SAS Institute (Cary, North Carolina), and graphical outputs were generated using GraphPad Prism software (Version 8, GraphPad Software Inc., San Diego, CA, USA).

Conclusions
This study focused on the green synthesis of alpha hematite αFe 2 O 3 NPs from S. rebaudiana leaf extract, which was efficaciously implemented as an antimicrobial and anticancer agent. DLS, UV/Vis, XRD, EDX, and FTIR analyses were used to determine the features, size, shape, and thermal stability of SRLe-αFe 2 O 3 NPs nanoparticles, while TEM and SEM microscopic methods were utilized to detect the morphological qualities of the surfaces of the green synthesized nanoparticles. The results showed that the SRL extract with CHCl 3 /MeOH (2:1 v/v) (least polar solvent) contained the highest EY and TPC of~3.5% and~75 mg GAE/g extract, respectively, along with an antioxidant radicalscavenging activity of IC 50 = 12.87 ± 0.7 mg/mL. These phenolic compounds played an important role in increasing the stability of SRLe-αFe 2 O 3 NPs. The antibacterial efficacy of synthesized NPs toward isolated Gram-negative and Gram-positive bacteria was moderate. Although nanoparticles were toxic at high concentrations, they demonstrated remarkable effectiveness (eliminating almost 94% of cancer cells) against the A549 lung cancer cell line, indicating that they might be a viable choice for eradicating tumor cells at optimal doses. However, further research is needed to discover the exact doses and reaction conditions needed to employ nanoparticles for these purposes.