Aptamer Trimode Biosensor for Trace Glyphosate Based on FeMOF Catalytic Oxidation of Tetramethylbenzidine

The stable and highly catalytic Fe metal–organic framework (FeMOF) nanosol was prepared and characterized by electron microscopy, and energy and molecular spectral analysis. It was found that FeMOF strongly catalyzed the oxidation of 3,3’,5,5’-tetramethylbenzidine (TMB) by H2O2 to produce TMBox, which had a fluorescence (FL) peak at 410 nm. When silver nanoparticles were added, it exhibited strong resonance Rayleigh scattering (RRS) activity and surface-enhanced Raman scattering (SERS) effect. This new FeMOF nanocatalytic trimode indicator reaction was combined with the glyphosate aptamer reaction to establish a new SERS/RRS/FL trimode biosensor for glyphosate. The sensor can be used for the analysis of environmental wastewater, and a new method for detecting glyphosate content in wastewater is proposed. The linear range of the sensor is 0.1–14 nmol/L, the detection limit is 0.05 nmol/L, the recovery is 92.1–97.5%, and the relative standard deviation is 3.6–8.7%.


Introduction
Metal-organic frameworks (MOFs) are crystalline porous materials with periodic network structures formed by the self-assembly of transition metal ions and organic ligands. It has the advantages of high porosity, low density, large specific surface area, regular pore channels, adjustable pore size, diversity, and tailorability of the topological structure, and is widely used in gas storage, pharmacology, chemical sensing, pollutant separation and chemical catalysis [1][2][3][4]. Therefore, the preparation and application of MOFs have attracted much attention. Manuel et al. prepared Zn-, Mg-, Mn-, Ni-, and Co-modified MOFs by the aqueous phase method at room temperature using terephthalic acid as a precursor. The results show that the properties of MOFs can be enhanced by reducing the crystal size to nanometer level [5]. Tan et al. proved that copper-based MOF (HKUST-1) exhibits peroxidase activity, using thiamine (TH) as the peroxidase substrate. Based on the peroxidase-like activity of HKUST-1, a simple and sensitive FL detection method for TH was developed. The detection limit was as low as 1 µmol/L and the linear range was 4-700 µmol/L [6]. Zhang et al. synthesized ZIF-8 graphene oxide (ZIF-8 GO) via a simple wet chemical process, and then fixed it onto AuPtNPs by the reduction method to prepare AuPt/ZIF-8 rGO. The peroxidase activity of AuPt/ZIF-8 rGO was used to electrochemically detect 100 nmol/L −18 mmol/L H 2 O 2 with a detection limit (DL) of 19 nmol/L [7]. Wang designed a biomolecular sensing platform based on the peroxidase catalytic activity of MOFs, and established a method for the detection of thrombin according to the significant colorimetric changes, with the DL as low as 0.8 nmol/L. Iron is a common and stable MOF material [8]. Patricia et al. successfully prepared MIL-100 (Fe) by the hydrothermal method. It was proven that the catalytic performance of MIL-100 (Fe) is attributed to the redox characteristics of Fe 2+ and Fe 3+ , which is similar to the properties of many iron-containing solid catalysts [9]. Zhang et al. prepared Fe-doped metal-organic framework material provides three methods for selection. As far as we know, there is no report on the synthesis of FeMOF with high catalytic activity, or the nanocatalytic amplification of the H 2 O 2 -TMB indicator reaction and its coupling with highly selective aptamers to establish trimode detection. In this study, a novel trimode SERS method for the determination of trace GLY was developed by combining the highly selective aptamer reaction with the sensitive FeMOF nanocatalytic H 2 O 2 -TMB trimode indicator reaction. It has the advantages of convenient operation, good selectivity, high sensitivity, and can provide trimodal options. The SERS method was applied to the determination of GLY in wastewater with satisfactory results.

Apparatus
The resonance Rayleigh scattering spectrum was scanned by Hitachi F-7000 fluorescence spectrophotometer (Hitachi Hi-tech Company, Hitachi, Japan), and the absorption spectrum was scanned by Tu-1901 dual-beam ultraviolet-visible spectrophotometer (Beijing Pusan General Instrument Co., Ltd., Beijing, China). The DXR smart Raman spectrometer (Thermo, Waltham, MA, USA) has a laser wavelength of 633 nm, a laser power of 0.5 mw, a slit of 2.5 µm, and an intelligent background scanning mode to obtain SERS spectra, which includes a scanning electron microscope (SEM, JSM-6380LV, Hitachi, Japan, Chiyoda, Tokyo, Japan) and a transmission electron microscope (FEI Talos 200S, Thermo, Waltham, MA, USA). An FD-1C-50 vacuum freeze dryer (Hangzhou Jutong Electronics Co., Ltd., Hangzhou, China) was used to prepare solid samples, and the infrared spectra were obtained by scanning with a Fourier transform infrared spectrometer (Shanghai Platinum Elmer Co., Ltd., Shanghai, China). The size spectra of nanomaterials were obtained by Nano-2s nanoparticles (Malverm Co., Malverm, UK). Other instruments include an HH-S2 electrothermal constant-temperature water bath (Jintan Dadi Automation Instrument Factory, Jintan, China), used for heating the reaction system, and a KQ3200DB numerical control ultrasonic cleaner with ultrasonic power of 150 w and operating frequency of 40 KHz (Kunshan Ultrasonic Instrument Co., Ltd., Kunshan, China), used for cleaning the required equipment for the experiment.

Preparation of Silver Nanoparticles
Into a conical flask, 44 mL water, 2 mL 1.7 g/L AgNO 3 , 2.0 mL 100 mmol/L sodium citrate, 600 µL 30% H 2 O 2 , and 600 µL 0.1 mol/L NaBH 4 were added in sequence while stirring, the black nanosilver colloid was quickly stirred to obtain a black color. The black nanosilver colloid was immediately transferred to the light wave furnace, and the orange-red transparent nanosilver colloid was obtained by 250 • C light wave for 10 min.
After natural cooling, the water was fixed to 50 mL for standby. The concentration was 68 mg/L AgNPs. The reagents used were all analytical pure, and the experimental water was sub-boiling water.

Preparation of FeMOF/CoMOF/CuMOF/NiMOF
First, 0.53 g NaOH was added into the round-bottom flask and dissolved in 13 mL water, after which 0.735 g H 3 btc was added to the flask in batches and dissolved by ultrasound. Subsequently, 1.5 g FeSO 4 ·7H 2 O was weighed and dissolved in a 100 mL round-bottom flask with 27 mL H 2 O ultrasonically. Under ultrasonic stirring, FeSO 4 solution was slowly added to the H 3 btc solution at room temperature, and continuously stirred for 12 h to obtain a red-brown suspension. The suspension was centrifuged at 12,000 r/min to obtain red-brown products, and then the products were washed three times with deionized water and anhydrous ethanol, respectively. Then, the red-brown solid was obtained by high-speed freezing centrifugation (12,000 r/min). Finally, the product was vacuum freeze-dried for 24 h to obtain red-brown powder, namely FeMOF. The preparation of CoMOF/CuMOF/NiMOF followed the same steps as that of FeMOF, except replacing 1.5 g FeSO 4 ·7H 2 O with CoCl 2 ·6H 2 O, CuSO 4 ·H 2 O, and NiCl 2 ·6H 2 O of the same mass. A 0.01 g/L FeMOF solution was prepared with water.

Experimental Procedure
Into a 5.0 mL test tube, 150 µL 0.01 g/L FeMOF, 200 µL 0.1 µmol/L Apt GLY , and a certain concentration of glyphosate solution were added. The test tube was then placed in an 80 • C water bath for 5 min to allow the Apt to combine with the catalyst, after which was then added 100 µL 0.5 mmol/L TMB solution, 90 µL 0.1 mmol/L H 2 O 2 solution, and 90 µL 0.1 mol/L Tris-HCl buffer. Subsequently, the solution was diluted to 2.0 mL with water, and mixed. After bathing at 45 • C for 30 min, the reaction was terminated in ice water, and 400 µL 68 mg/L AgNPs were added. The solution was placed into a quartz cell, and the Raman spectrum was recorded under the condition of 1 mW light source power and a 25.0 µm slit. The SERS intensity at 1607 cm −1 was measured, and the blank (I 1607 cm −1 ) 0 was not mixed with GLY. The value of ∆I 1607 cm −1 = I 1607 cm −1 − (I 1607 cm −1 ) 0 was calculated.

Analysis Principles
FeMOF can catalyze the oxidation of TMB by H 2 O 2 to produce TMBox. TMBox can make AgNPs aggregate, and its SERS activity and RRS effect are greatly enhanced. When Apt is added, it can be adsorbed onto the surface of FeMOF to inhibit its catalytic effect. The TMBox generated in the system decreases, and the SERS/RRS/FL signals decrease. When the target molecule GLY is added, it forms a stable complex with Apt and leaves the nanosurface. Its catalytic effect is enhanced, and the TMBox generated by the system is increased, and the SERS/RRS/FL signal is linearly enhanced. Accordingly, a new Apt-mediated FeMOF catalytic amplification RRS/SERS/FL trimode quantitative detection method for GLY can be established using the Raman spectrometer (Raman) and fluorescence instrument (FM) (Figure 1).  Figure 2A shows the absorption spectra of FeMOF, indicating that FeMOF has a wide absorption band at 300-650 nm. With the increase in FeMOF concentration, the absorbance gradually increases, and an absorption peak appears at 375 nm. The resonance Rayleigh scattering spectra (RRS, volt = 350 V, excited slit = emission slit = 5 nm) of FeMOF were obtained by fluorescence synchronous scanning technique. It is obvious that the RRS signal at 440 nm increases with the increase in FeMOF concentration, indicating that FeMOF has an RRS signal, which lays a foundation for the establishment of subsequent RRS analysis method ( Figure 2B). The prepared FeMOF powder was ground uniformly in an agate bowl and placed into a Petri dish. The FeMOF powder was dried again in the oven at 50 °C for 2 h to remove the moisture that may have been absorbed during the transfer process. The powder was pressed by the tablet press. The tablet was placed into the infrared spectrometer to scan and obtain the corresponding spectrum. The infrared spectra showed that for FeMOF, strong infrared spectral peaks were mainly generated at 1622.1 cm −1 , 1383.5 cm −1 , 1109.8 cm −1 , 1044.9 cm −1 , 943.6 cm −1 , 759.6 cm −1 , and 710.2 cm −1 , respectively. The broad peak, 3445 cm −1 , belongs to the hydroxyl -OH peak, the peaks at 1622.1 cm −1 , 1383.5 cm −1 , 1109.8 cm −1 , and 1044.9 cm −1 belong to the stretching vibration peak of C=O, the bending vibration peak of hydroxyl, and the stretching vibration peak of C-O, respectively. Peaks at 759.6 cm −1 and 710.2 cm −1 belong to the fingerprint peak of FeMOF and the structure of Fe 3+ oxide, respectively. It was proven that FeMOF was successfully prepared. In order to prove that the synthesized material is FeMOF, the crystal structure was analyzed by X-ray powder diffraction (XRD). Figure 2D presents the XRD pattern of FeMOF powder synthesized in aqueous phase at room temperature for 12 h and 24 h. When the visible reaction proceeded, as displayed in Figure 2C, to 12 h, the diffraction peak intensity of the spectrum was high, and the diffraction characteristic peak of FeMOF appeared, especially in the range of 3-5°. The main diffraction peaks corresponded to the peak position of FeMOF reported in literature, indicating that FeMOF was successfully synthesized. When the reaction proceeded to 24 h, the intensity of diffraction peak decreased, indicating that the crystallinity of FeMOF decreased. Therefore, the reaction time of 12 h is the optimal time for the synthesis of FeMOF powder, and the prepared FeMOF has a good crystal form. The particle size distribution of nanoparticles in FeMOF  Figure 2A shows the absorption spectra of FeMOF, indicating that FeMOF has a wide absorption band at 300-650 nm. With the increase in FeMOF concentration, the absorbance gradually increases, and an absorption peak appears at 375 nm. The resonance Rayleigh scattering spectra (RRS, volt = 350 V, excited slit = emission slit = 5 nm) of FeMOF were obtained by fluorescence synchronous scanning technique. It is obvious that the RRS signal at 440 nm increases with the increase in FeMOF concentration, indicating that FeMOF has an RRS signal, which lays a foundation for the establishment of subsequent RRS analysis method ( Figure 2B). The prepared FeMOF powder was ground uniformly in an agate bowl and placed into a Petri dish. The FeMOF powder was dried again in the oven at 50 • C for 2 h to remove the moisture that may have been absorbed during the transfer process. The powder was pressed by the tablet press. The tablet was placed into the infrared spectrometer to scan and obtain the corresponding spectrum. The infrared spectra showed that for FeMOF, strong infrared spectral peaks were mainly generated at 1622.1 cm −1 , 1383.5 cm −1 , 1109.8 cm −1 , 1044.9 cm −1 , 943.6 cm −1 , 759.6 cm −1 , and 710.2 cm −1 , respectively. The broad peak, 3445 cm −1 , belongs to the hydroxyl -OH peak, the peaks at 1622.1 cm −1 , 1383.5 cm −1 , 1109.8 cm −1 , and 1044.9 cm −1 belong to the stretching vibration peak of C=O, the bending vibration peak of hydroxyl, and the stretching vibration peak of C-O, respectively. Peaks at 759.6 cm −1 and 710.2 cm −1 belong to the fingerprint peak of FeMOF and the structure of Fe 3+ oxide, respectively. It was proven that FeMOF was successfully prepared. In order to prove that the synthesized material is FeMOF, the crystal structure was analyzed by X-ray powder diffraction (XRD). Figure 2D presents the XRD pattern of FeMOF powder synthesized in aqueous phase at room temperature for 12 h and 24 h. When the visible reaction proceeded, as displayed in Figure 2C, to 12 h, the diffraction peak intensity of the spectrum was high, and the diffraction characteristic peak of FeMOF appeared, especially in the range of 3-5 • . The main diffraction peaks corresponded to the peak position of FeMOF reported in literature, indicating that FeMOF was successfully synthesized. When the reaction proceeded to 24 h, the intensity of diffraction peak decreased, indicating that the crystallinity of FeMOF decreased. Therefore, the reaction time of 12 h is the optimal time for the synthesis of FeMOF powder, and the prepared FeMOF has a good crystal form. The particle size distribution of nanoparticles in FeMOF solution was analyzed by Nano-2s particle size analyzer. The laser scattering size distribution of FeMOF solution was recorded by the nanoparticle size and potential analyzer. The size distribution was from 820 nm to 1200 nm, with an average size of 955 nm ( Figure 2E), which is consistent with the particle size range of FeMOF obtained by SEM. FeMOF was prepared according to the experimental method, and 10 mg was dissolved in water and ultrasonically dispersed to obtain 10 mL of yellow suspension. After 10-fold dilution, 5 µL solution was placed on the silicon wafer and recorded by scanning electron microscopy (SEM). From Figure 2F, it can be seen that FeMOF tends to be a cubic sheet structure, and the average particle size is between 500 nm −1 µm.

Characterization of FeMOF
Biosensors 2022, 12, 920 6 of 17 solution was analyzed by Nano-2s particle size analyzer. The laser scattering size distribution of FeMOF solution was recorded by the nanoparticle size and potential analyzer. The size distribution was from 820 nm to 1200 nm, with an average size of 955 nm ( Figure  2E), which is consistent with the particle size range of FeMOF obtained by SEM. FeMOF was prepared according to the experimental method, and 10 mg was dissolved in water and ultrasonically dispersed to obtain 10 mL of yellow suspension. After 10-fold dilution, 5 μL solution was placed on the silicon wafer and recorded by scanning electron microscopy (SEM). From Figure 2F, it can be seen that FeMOF tends to be a cubic sheet structure, and the average particle size is between 500 nm −1 μm.

SERS Spectra
In pH 4.0 Tris-HCl buffer solution, AuNPs, AgNPs, HPR, CoMOF, CuMOF, NiMO, and FeMOF can catalyze the oxidation of TMB by H2O2 at 45 °C in a water bath. The catalytic product, TMBox, has a SERS effect ( Figure 3). The results show that the catalyst concentration was linear to the SERS peak intensity at 1607 cm −1 ( Figure S1). The catalytic effect was best when FeMOF was used as the catalyst, thus FeMOF was selected as the catalyst. After adding Apt, FeMOF can be wrapped, which inhibits the catalytic ability of FeMOF, reduces the generated TMBox, and weakens the SERS intensity. When the target molecule, GLY, was added, GLY specifically bound with Apt and released FeMOF, and its catalytic activity was restored. Ag nanoparticle has the properties of surface effect, volume effect, quantum size effect, and the macroquantum tunneling effect of general metal nanomaterials, and also has the special effect of surface plasmon resonance. When the Ag nanoparticle was irradiated by the laser, the very small scale of Ag nanoparticle makes the nanosphere cavity array cooperate with surface plasmon resonance and optical coupling, resulting in the enhancement of electromagnetic field. Therefore, the Raman signal of adsorbed molecules on the Ag nanosurface is 10 6 times, or even stronger, than that of normal molecules, which makes it one of the best SERS metal substrates. When a certain

SERS Spectra
In pH 4.0 Tris-HCl buffer solution, AuNPs, AgNPs, HPR, CoMOF, CuMOF, NiMO, and FeMOF can catalyze the oxidation of TMB by H 2 O 2 at 45 • C in a water bath. The catalytic product, TMBox, has a SERS effect (Figure 3). The results show that the catalyst concentration was linear to the SERS peak intensity at 1607 cm −1 ( Figure S1). The catalytic effect was best when FeMOF was used as the catalyst, thus FeMOF was selected as the catalyst. After adding Apt, FeMOF can be wrapped, which inhibits the catalytic ability of FeMOF, reduces the generated TMBox, and weakens the SERS intensity. When the target molecule, GLY, was added, GLY specifically bound with Apt and released FeMOF, and its catalytic activity was restored. Ag nanoparticle has the properties of surface effect, volume effect, quantum size effect, and the macroquantum tunneling effect of general metal nanomaterials, and also has the special effect of surface plasmon resonance. When the Ag nanoparticle was irradiated by the laser, the very small scale of Ag nanoparticle makes the nanosphere cavity array cooperate with surface plasmon resonance and optical coupling, resulting in the enhancement of electromagnetic field. Therefore, the Raman signal of adsorbed molecules on the Ag nanosurface is 10 6 times, or even stronger, than that of normal molecules, which makes it one of the best SERS metal substrates. When a certain concentration of photo-silver nanoparticles was added, the system showed strong Raman peaks at 1184 cm −1 , 1332 cm −1 , and 1607 cm −1 , respectively. Among them, the SERS peak at 1607 cm −1 had the most obvious change and good linearity. Therefore, the SERS peak at 1607 cm −1 was selected for the detection of glyphosate, and the signal intensity was linear with the added amount of GLY. concentration of photo-silver nanoparticles was added, the system showed strong Raman peaks at 1184 cm −1 , 1332 cm −1 , and 1607 cm −1 , respectively. Among them, the SERS peak at 1607 cm −1 had the most obvious change and good linearity. Therefore, the SERS peak at 1607 cm −1 was selected for the detection of glyphosate, and the signal intensity was linear with the added amount of GLY.

RRS and Fluorescence Spectra
RRS and fluorescence spectra were obtained by fluorescence spectrophotometer. The former adopted synchronous scanning technology, and the latter fixed excitation wave-

RRS and Fluorescence Spectra
RRS and fluorescence spectra were obtained by fluorescence spectrophotometer. The former adopted synchronous scanning technology, and the latter fixed excitation wavelength to scan emission wavelength. In pH 4.0 Tris-HCl buffer solution, FeMOF can catalyze the oxidation of TMB by H 2 O 2 to generate TMBox in a 45 • C water bath. The oxidation product TMBox can make silver nanoparticles aggregate. With the increase in TMBox, the RRS signal of the system gradually increases (Figures 4A and S2A). After the addition of Apt to GLY, Apt wrapped FeMOF, thereby inhibiting the catalytic ability of FeMOF ( Figure 4B). The generated TMBox decreased, thus the RRS strength decreased accordingly. For the H 2 O 2 -TMB-Tris-HCl reaction system, the target GLY specifically binds to Apt, FeMOF is released, and the catalytic activity is gradually restored. The signal intensity of RRS spectrum is linear with the amount of GLY ( Figure 4C). The fluorescence spectra in Figure 4D show that FeMOF had a strong catalytic effect on the reduction of TMB by H 2 O 2 . Moreover, with the increase in FeMOF concentration, the signal value is stronger and has an obvious linear relationship ( Figure S2B). Apt GLY has a strong inhibitory effect on the nanocatalytic system; with the increase in Apt GLY concentration, the stronger the inhibition. Figure 4F shows that the aptamer-mediated FeMOF catalysis fluorescence can determine glyphosate. Furthermore, with the increase in GLY concentration, the signal value is stronger, and therefore has an obvious linear relationship.
Biosensors 2022, 12, 920 10 of 17 RRS signal of the system gradually increases (Figures 4A and S2A). After the addition of Apt to GLY, Apt wrapped FeMOF, thereby inhibiting the catalytic ability of FeMOF (Figure 4B). The generated TMBox decreased, thus the RRS strength decreased accordingly. For the H2O2-TMB-Tris-HCl reaction system, the target GLY specifically binds to Apt, FeMOF is released, and the catalytic activity is gradually restored. The signal intensity of RRS spectrum is linear with the amount of GLY ( Figure 4C). The fluorescence spectra in Figure 4D show that FeMOF had a strong catalytic effect on the reduction of TMB by H2O2. Moreover, with the increase in FeMOF concentration, the signal value is stronger and has an obvious linear relationship ( Figure S2B). AptGLY has a strong inhibitory effect on the nanocatalytic system; with the increase in AptGLY concentration, the stronger the inhibition. Figure 4F shows that the aptamer-mediated FeMOF catalysis fluorescence can determine glyphosate. Furthermore, with the increase in GLY concentration, the signal value is stronger, and therefore has an obvious linear relationship.

Transmission Electron Microscopy (TEM) and Laser Scattering of the Analytical System
The system reaction liquid was obtained according to the following test method: place the liquid into a 2 mL centrifuge tube, centrifugate at 10,000 rpm/g for 5 min; take the supernatant, add 1.5 mL deionized water, and centrifugate twice; the precipitation of 1.5 mL deionized water occurs via ultrasonic dispersion; take 5 μL solution and drop onto the silicon wafer, commence scanning electron microscopy. It can be seen from the TEM images that AgNPs are relatively dispersed with an average particle size of about 30 nm ( Figure 5A). For the analysis system, when glyphosate was not detected, AgNPs continued to exist in the form of dispersion ( Figure 5B), and the particle size was about 30 nm. When glyphosate was added into the reaction system, more TMBox was generated, which made AgNPs aggregate into larger particles ( Figure 5C), with a particle size of about 50 nm. The Nano-2s particle size analyzer was used to determine the particle size distribution of the nanoparticles in the system. After adding glyphosate, glyphosate formed a stable complex with AptGLY and released encapsulated FeMOF particles. The catalytic activity of FeMOF was restored, and the TMBox generated in the system was gradually increased, and the aggregation of TMBox-AgNPs was enhanced. The particle sizes of the H2O2-TMB-Tris-HCl-FeMOF-AptGLY system and the H2O2-TMB-Tris-HCl-FeMOF-AptGLY-GLY system were 38 nm and 460 nm, respectively ( Figure 5D), and the particle sizes showed an increasing trend. The two particle sizes of glyphosate system are quite

Transmission Electron Microscopy (TEM) and Laser Scattering of the Analytical System
The system reaction liquid was obtained according to the following test method: place the liquid into a 2 mL centrifuge tube, centrifugate at 10,000 rpm/g for 5 min; take the supernatant, add 1.5 mL deionized water, and centrifugate twice; the precipitation of 1.5 mL deionized water occurs via ultrasonic dispersion; take 5 µL solution and drop onto the silicon wafer, commence scanning electron microscopy. It can be seen from the TEM images that AgNPs are relatively dispersed with an average particle size of about 30 nm ( Figure 5A). For the analysis system, when glyphosate was not detected, AgNPs continued to exist in the form of dispersion ( Figure 5B), and the particle size was about 30 nm. When glyphosate was added into the reaction system, more TMBox was generated, which made AgNPs aggregate into larger particles ( Figure 5C), with a particle size of about 50 nm. The Nano-2s particle size analyzer was used to determine the particle size distribution of the nanoparticles in the system. After adding glyphosate, glyphosate formed a stable complex with Apt GLY and released encapsulated FeMOF particles. The catalytic activity of FeMOF was restored, and the TMBox generated in the system was gradually increased, and the aggregation of TMBox-AgNPs was enhanced. The particle sizes of the H 2 O 2 -TMB-Tris-HCl-FeMOF-Apt GLY system and the H 2 O 2 -TMB-Tris-HCl-FeMOF-Apt GLY -GLY system were 38 nm and 460 nm, respectively ( Figure 5D), and the particle sizes showed an increasing trend. The two particle sizes of glyphosate system are quite different; this is because TEM is a solid-state imaging method, laser scattering measurement is the average value of the solution state.

Nanocatalytic Mechanism of FeMOF
Generally speaking, the smaller the particle size of nanoparticles, the stronger the catalysis. The results of the electron microscopy and laser scattering particle size distribution experiments show that FeMOF has a large particle size, but it still has a strong catalytic effect on the oxidation of TMB to TMBox by H2O2. This is related to the porous structure and nanopore size of FeMOF. That is, its nanopores can provide more nanosurface electrons. It is usually difficult to react when H2O2 oxidizes TMB. When FeMOF is added, H2O2 will react with TMB, and with the increase in nanocatalyst concentration, the catalytic capacity will increase, and the amount of TMBox generated by catalysis will increase. After adding a certain concentration of silver nanoparticles (AgNPs) sol, TMBox can make AgNPs aggregate, and enhance its SERS activity and RRS effect. The large specific surface area of FeMOF provides a large number of reaction sites for the reaction between H2O2 and TMB. The porous structure of FeMOF can adsorb the reactants to the nanosurface of the nanomaterial, the electrons on the nanopores speed up the redox electron transfer to enhance the H2O2-TMB reaction. At the same time, Fe(II) on the catalyst surface will activate hydrogen peroxide to generate ·OH radicals and Fe(III) [28,29], Fe(III)MOF will

Nanocatalytic Mechanism of FeMOF
Generally speaking, the smaller the particle size of nanoparticles, the stronger the catalysis. The results of the electron microscopy and laser scattering particle size distribution experiments show that FeMOF has a large particle size, but it still has a strong catalytic effect on the oxidation of TMB to TMBox by H 2 O 2 . This is related to the porous structure and nanopore size of FeMOF. That is, its nanopores can provide more nanosurface electrons. It is usually difficult to react when H 2 O 2 oxidizes TMB. When FeMOF is added, H 2 O 2 will react with TMB, and with the increase in nanocatalyst concentration, the catalytic capacity will increase, and the amount of TMBox generated by catalysis will increase. After adding a certain concentration of silver nanoparticles (AgNPs) sol, TMBox can make AgNPs aggregate, and enhance its SERS activity and RRS effect. The large specific surface area of FeMOF provides a large number of reaction sites for the reaction between H 2 O 2 and TMB. The porous structure of FeMOF can adsorb the reactants to the nanosurface of the nanomaterial, the electrons on the nanopores speed up the redox electron transfer to enhance the H 2 O 2 -TMB reaction. At the same time, Fe(II) on the catalyst surface will activate hydrogen peroxide to generate ·OH radicals and Fe(III) [28,29], Fe(III)MOF will further react with H 2 O 2 to generate HO 2 · and Fe(II)MOF, and the circulation of Fe(II)MOF and Fe(III)MOF on the catalyst surface plays the role of a nanocatalyst ( Figure 6).

Preparation Conditions of FeMOF
The preparation conditions of FeMOF were selected by single-factor transformation. The three factors of trimellitic acid, sodium hydroxide, and ferrous sulfate hexahydrate were investigated ( Figure S2). Based on the I1607 cm −1 of the H2O2-TMB system, FeMOF was prepared by heating 0.398 g, 0.585 g, 0.735 g, and 0.815 g trimellitic acid to room temperature, and stirring for 12 h according to the method. The effect of trimellitic acid addition on the catalytic effect of H2O2-TMB system was investigated. With the increase in trimellitic acid content, SERS signal value first increased and then decreased. When the addition amount of trimellitic acid was 0.735 g, I1607 cm −1 was the largest. Therefore, the amount of trimellitic acid added was 0.735 g. The effects of 0.2 g, 0.36 g, 0.53 g, and 0.84 g sodium hydroxide on the catalytic effect of H2O2-TMB system were investigated. With the increase in sodium hydroxide content, SERS signal value first increased and then decreased. When the addition amount of sodium hydroxide was 0.53 g, I1607 cm −1 was the largest. Therefore, the addition amount of sodium hydroxide was 0.53 g. The effects of 0.6 g, 1.2 g, 1.5 g, and 2.1 g ferrous sulfate heptahydrate on the catalytic effect of H2O2-TMB system were investigated. With the increase in ferrous sulfate heptahydrate content, the SERS signal value first increased and then decreased. When the addition amount of fer-

Preparation Conditions of FeMOF
The preparation conditions of FeMOF were selected by single-factor transformation. The three factors of trimellitic acid, sodium hydroxide, and ferrous sulfate hexahydrate were investigated ( Figure S2). Based on the I 1607 cm −1 of the H 2 O 2 -TMB system, FeMOF was prepared by heating 0.398 g, 0.585 g, 0.735 g, and 0.815 g trimellitic acid to room temperature, and stirring for 12 h according to the method. The effect of trimellitic acid addition on the catalytic effect of H 2 O 2 -TMB system was investigated. With the increase in trimellitic acid content, SERS signal value first increased and then decreased. When the addition amount of trimellitic acid was 0.735 g, I 1607 cm −1 was the largest. Therefore, the amount of trimellitic acid added was 0.735 g. The effects of 0.2 g, 0.36 g, 0.53 g, and 0.84 g sodium hydroxide on the catalytic effect of H 2 O 2 -TMB system were investigated. With the increase in sodium hydroxide content, SERS signal value first increased and then decreased. When the addition amount of sodium hydroxide was 0.53 g, I 1607 cm −1 was the largest. Therefore, the addition amount of sodium hydroxide was 0.53 g. The effects of 0.6 g, 1.2 g, 1.5 g, and 2.1 g ferrous sulfate heptahydrate on the catalytic effect of H 2 O 2 -TMB system were investigated. With the increase in ferrous sulfate heptahydrate content, the SERS signal value first increased and then decreased. When the addition amount of ferrous sulfate heptahydrate was 1.5 g, I 1607 cm −1 was the largest. Therefore, the addition amount of ferrous sulfate heptahydrate was 1.5 g.

Analysis Conditions
The analytical conditions were examined. The effect of H 2 O 2 concentration on the SERS signal of the system was investigated. When 4.5 × 10 −3 mmol/L H 2 O 2 was added, ∆I reached the maximum; therefore, 4.5 × 10 −3 mmol/L H 2 O 2 was selected ( Figure S5A). The effect of TMB concentration on the SERS signal of the system was investigated. When 0.025 mmol/L TMB was added, ∆I reached the maximum, this this concentration was chosen ( Figure S5B). The effect of Tris-HCl buffer solution concentration on the SERS signal of the system was investigated. When 0.45 mmol/L Tris-HCl buffer solution was added, ∆I reached the maximum level, therefore, this concentration is the optimal concentration ( Figure S5C). The effect of Apt GLY concentration on the SERS signal of the system was investigated. When 8 nmol/L Apt GLY was added, ∆I reached the maximum, hence 8 nmol/L AptGLY was selected ( Figure S5D). The effect of reaction temperature on the SERS signal of the system was investigated. When the reaction time is 50 • C, ∆I reached the maximum level, thus the optimum temperature is 50 • C ( Figure S5E). The effect of reaction time on the SERS signal was considered. When the reaction time is 30 min, ∆I reached the maximum level, and thus, 30 min was chosen ( Figure S5F).

Working Curve
Under the selected experimental conditions, for the H 2 O 2 -TMB-FeMOF-Apt GLY -GLY-AgNPs SERS system, in the concentration range of 0.1-14 nmol/L GLY ( Figure 7A), the SERS intensity change ∆I 1607 cm −1 was linear to the concentration of GLY, and the linear equation was ∆I 1607 cm −1 = 722C − 49.2. The linear correlation coefficient, R 2 , was 0.9947, and the DL was 0.05 nmol/L. For the H 2 O 2 -TMB-FeMOF-Apt GLY -GLY-AgNPs RRS system, in the concentration range of 1-10 nmol/L GLY, the change of RRS intensity ∆I at 370 nm was linear with the concentration of GLY. The linear equation was ∆I 370 nm = 82.2C + 18.1, the coefficient R 2 was 0.9950, and the DL was 0.5 nmol/L ( Figure 7B). For the FL analysis system, in the concentration range of 2.0-10 nmol/L GLY, the FL intensity change ∆F at 410 nm was linearly related to the GLY concentration. The linear equation was ∆F 410 nm = 68.9C + 12, the coefficient R 2 was 0.9748, and the DL was 1.0 nmol/L ( Figure 7C). With the trimode method, the SERS was most sensitive and the linear range was the widest, the RRS was second, and the equipment cost was lower that the Raman meter. In addition, the FM can be finished the RRS/FL dimode detection. Table 1 lists the reported methods for determination of glyphosate, including the method, detection limit, recovery, and analysis sample. This SERS method was sensitive. at 410 nm was linearly related to the GLY concentration. The linear equation was ΔF410 nm = 68.9C + 12, the coefficient R 2 was 0.9748, and the DL was 1.0 nmol/L ( Figure 7C). With the trimode method, the SERS was most sensitive and the linear range was the widest, the RRS was second, and the equipment cost was lower that the Raman meter. In addition, the FM can be finished the RRS/FL dimode detection. Table 1 lists the reported methods for determination of glyphosate, including the method, detection limit, recovery, and analysis sample. This SERS method was sensitive.

Influence of Coexisting Substances
According to the experimental method, the effect of interfering substances on the determination of 2.5 ng/L glyphosate was detected. The results presented in Table S1 show that when the relative error is less than ±10%, the common inorganic ions and organic compounds have little effect on the measurement results of glyphosate, indicating that the method has good selectivity.

Analysis of Samples
The wastewater sample was filtered by 100 mL, and the supernatant was diluted to obtain the sample solution. According to the experimental method, 100 μL sample solution was taken to determine glyphosate content (Table S2). The SERS analytical results were in agreement with the HPLC results. The relative standard deviation (RSD) was 3.6-8.7%, and the recovery was 92.1-97.5%. This indicates that this SERS assay was accurate

Influence of Coexisting Substances
According to the experimental method, the effect of interfering substances on the determination of 2.5 ng/L glyphosate was detected. The results presented in Table S1 show that when the relative error is less than ±10%, the common inorganic ions and organic compounds have little effect on the measurement results of glyphosate, indicating that the method has good selectivity.

Analysis of Samples
The wastewater sample was filtered by 100 mL, and the supernatant was diluted to obtain the sample solution. According to the experimental method, 100 µL sample solution was taken to determine glyphosate content (Table S2). The SERS analytical results were in agreement with the HPLC results. The relative standard deviation (RSD) was 3.6-8.7%, and the recovery was 92.1-97.5%. This indicates that this SERS assay was accurate and reliable.

Conclusions
In this study, FeMOF prepared by aqueous phase method at room temperature exhibited good catalytic performance, which can facilitate TMB oxidization by H 2 O 2 to produce more TMBox probe molecules. Through the regulation of nucleic acid aptamers, an effective SERS/RRS/FL trimode detection method for GLY in soil and water environments was established. This method combines the characteristics of SERS detection with low DL and good accuracy of RRS detection, and can be applied to the detection of GLY in actual samples. The recovery rate is between 92.1% and 97.5%, and the results are satisfactory. In addition, a reasonable nanocatalytic mechanism was proposed, that the surface electrons on FeMOF nanopores enhanced the redox electron transfer efficiency.
Supplementary Materials: The following supporting information can be downloaded at: https: //www.mdpi.com/article/10.3390/bios12110920/s1, Figure S1: The relationship between SERS peak intensity and catalyst/GLY concentration; Figure S2: The relationship between RRS/fluorescence intensity and FeMOF/GLY; Figure S3: Transmission electron microscopy and laser scattering of FeMOF analytical system; Figure S4: Effect of preparation conditions on FeMOF; Figure S5: Influence of the analysis conditions; Table S1: Effect of coexistence substance on the SERS de-termination of GLY; Table S2. SERS results of GLY in wastewater samples.