The Preparation and Properties of Multilayer Cu-MTa2O5 Composite Coatings on Ti6Al4V for Biomedical Applications

For the enhancement of the anticorrosion and antibacterial performance of the biomedical alloy Ti6Al4V, a novel Cu incorporated multilayer Ta2O5ceramic composite coating Cu-Ta2O5/Ta2O5/Ta2O5-TiO2/TiO2/Ti (coating codeCu-MTa2O5) was developed by radio frequency (RF) and direct current (DC) reactive magnetron sputtering. Meanwhile, to better display the multilayer Ta2O5 coating mentioned above, a monolayer Ta2O5 ceramic coating was deposited onto the surface of Ti6Al4V alloy as a reference. The surface morphology, microstructure, phase constituents, and elemental states of the coating were evaluated by atomic force microscopy, scanning electron microscopy, X-ray diffraction, and X-ray photoelectron spectroscopy, respectively. The adhesion strength, wettability, anticorrosion and antibacterial properties of the coating were examined by a scratch tester, contact angle measurement, electrochemical workstations, and plate counting method, respectively. The results showed that the deposited coatings were amorphous and hydrophobic. Cu doped into the Ta2O5 coating existed as CuO and Cu2O. A Ta2O5-TiO2/TiO2/Ti multi-interlayer massively enhanced the adhesion strength of the coating, which was 2.9 times stronger than that of the monolayer Ta2O5coating. The multilayer Cu-MTa2O5 coating revealed a higher corrosion potential and smaller corrosion current density as compared to the uncoated Ti6Al4V, indicating the better anticorrosion performance of Ti6Al4V. Moreover, a 99.8% antibacterial effect of Cu-MTa2O5 coated against Staphylococcus aureuswas obtained.


Introduction
Ti6Al4V titanium alloy, as a medical implant material, has been commonly applied in dentistry, orthopedics, and other fields due to its excellent corrosion resistance, mechanical properties, and biocompatibility [1][2][3][4]. However, clinical studies have indicated that Ti6Al4V titanium alloy-related implants would be corroded by body fluids, releasing toxic and side-effectmetal ionssuch as V 5+ and Al 3+ [5,6], and causing local immune dysfunction [7], inflammation, and cytotoxic reactions in the human body [8]. During operations, bacteria will adhere to the surface of the implant, then propagate and form biofilms, resulting in postoperative infection, and in severe cases resulting in amputation and of Cu/a-C:H coating was also reported. Also, Rosenbaum et al. [49] demonstrated that titanium had no antibacterial activity, while the antibacterial rate of a Cu-TiO 2 coating on E. coli and S. aureus can reach 100%. Unfortunately, the doped copper may reduce the corrosion resistance of the copper-bearing coating in chloride media because of the release of the Cu ions, leading to the premature failure of the coating [50,51].
Based on the above situation, this paper aims at improving the anticorrosion and antibacterial properties of a Ti6Al4V titanium alloy medical implant, whereby a novel copper doped multilayer tantalum oxide composite coating Cu-Ta 2 O 5 /Ta 2 O 5 /Ta 2 O 5 -TiO 2 /TiO 2 /Ti (coating code Cu-MTa 2 O 5 ) was deposited on the Ti6Al4V substrate by magnetron sputtering. The surface morphology, microstructure, and phase composition of the coating were analyzed by scanning electron microscopy (SEM), atomic force microscopy (AFM), X-ray diffraction (XRD), energy-dispersive spectroscopy (EDS), and X-ray photoelectron spectroscopy (XPS). The wettability, bonding strength, corrosion resistance, and antibacterial property of the coating were determined by a contact angle measuring instrument, scratch tester, electrochemical workstation, and plate counting method, respectively. For comparison, these investigations were also performed on monolayer Ta 2 O 5 coating samples. The findings from this study are expected to provide a valuable reference for the surface modification of titanium alloy implant materials.  Figure 1, the Cu-MTa 2 O 5 coating contains five layers of film, wherein the first to third layers are a Ti film, TiO 2 film, and TiO 2 -Ta 2 O 5 composite film, respectively. These three films serve as the interlayer, in which elements of adjacent layers penetrate each other in reducing the interface stress and enhance the bonding property of the coating. The fourth layer of the Ta 2 O 5 ceramic film is an anticorrosion layer, and the fifth layer (outer layer) is Ta 2 O 5 doped with Cu, which has an antibacterial effect. Nanomaterials 2019, 9, x FOR PEER REVIEW 3 of 19 decrease of 81.9%. Chan et al. [48] reported a nearly 40% antibacterial rate of an a-C:H coating on Escherichia coli, while 99.9% of the antibacterial rate of Cu/a-C:H coating was also reported. Also, Rosenbaum et al. [49] demonstrated that titanium had no antibacterial activity, while the antibacterial rate of a Cu-TiO2coating on E. coli and S. aureus can reach 100%. Unfortunately, the doped copper may reduce the corrosion resistance of the copper-bearing coating in chloride media because of the release of the Cu ions, leading to the premature failure of the coating [50,51]. Based on the above situation, this paper aims at improving the anticorrosion and antibacterial properties of a Ti6Al4V titanium alloy medical implant, whereby a novel copper doped multilayer tantalum oxide composite coating Cu-Ta2O5/Ta2O5/Ta2O5-TiO2/TiO2/Ti (coating code Cu-MTa2O5) was deposited on the Ti6Al4V substrate by magnetron sputtering. The surface morphology, microstructure, and phase composition of the coating were analyzed by scanning electron microscopy (SEM), atomic force microscopy (AFM), X-ray diffraction (XRD), energy-dispersive spectroscopy (EDS), and X-ray photoelectron spectroscopy (XPS). The wettability, bonding strength, corrosion resistance, and antibacterial property of the coating were determined by a contact angle measuring instrument, scratch tester, electrochemical workstation, and plate counting method, respectively. For comparison, these investigations were also performed on monolayer Ta2O5 coating samples. The findings from this study are expected to provide a valuable reference for the surface modification of titanium alloy implant materials. Figure 1 depicts the structures of the Cu-MTa2O5 coating. As shown in Figure 1, the Cu-MTa2O5coating contains five layers of film, wherein the first to third layers are a Ti film, TiO2 film, and TiO2-Ta2O5 composite film, respectively. These three films serve as the interlayer, in which elements of adjacent layers penetrate each other in reducing the interface stress and enhance the bonding property of the coating. The fourth layer of the Ta2O5 ceramic film is an anticorrosion layer, and the fifth layer (outer layer) is Ta2O5 doped with Cu, which has an antibacterial effect. A Ti6Al4V alloy (BAOTI Group Co., Ltd., Baoji, Shanxi, China) with a size of 10 mm × 10 mm × 0.6 mm and silicon wafers (10 mm × 10 mm × 2 mm) were used as substrates. The chemical compositions of the Ti6Al4V alloy are shown in Table 1. The Ti6Al4V substrates were mechanically ground using SiC sandpaper (240-2000 grit) and polished with aqueous alumina solution to gain a surface roughness of 5 nm. The silicon wafer and polished Ti6Al4V were ultrasonically cleaned in acetone and ethanol for 15 min, respectively, and vacuum-dried. A Ti6Al4V alloy (BAOTI Group Co., Ltd., Baoji, Shanxi, China) with a size of 10 mm × 10 mm × 0.6 mm and silicon wafers (10 mm × 10 mm × 2 mm) were used as substrates. The chemical compositions of the Ti6Al4V alloy are shown in Table 1. The Ti6Al4V substrates were mechanically ground using SiC sandpaper (240-2000 grit) and polished with aqueous alumina solution to gain a surface roughness of 5 nm. The silicon wafer and polished Ti6Al4V were ultrasonically cleaned in acetone and ethanol for 15 min, respectively, and vacuum-dried. A JCP-450 high-vacuum magnetron sputtering coating system (BJTN, Beijing, China) was employed for plasma cleaning and coating deposition. Before deposition, the substrates and targets were separately cleaned by plasma cleaning for 20 min to remove the surface contaminants and improve the surface activity. Afterward, Cu-MTa 2 O 5 coatings were prepared on the substrates by successively depositing a Ti metal film, TiO 2 ceramic film, Ta 2 O 5 -TiO 2 ceramic composite film, Ta 2 O 5 ceramic, and Cu-Ta 2 O 5 composite film. Cu-MTa 2 O 5 coatings deposited on Si substrates were employed to characterize the microstructure of the cross-section of the coating, while those on Ti6Al4V substrates were used to evaluate properties such as adhesion strength, wettability, corrosion resistance, and antibacterial behavior. The purity of the Ta 2 O 5 , Ti, and Cu targets (ZNNM, Beijing, China) with a size of ϕ75 mm × 5 mm was 99.99%. Argon and oxygen with 99.99% purity were used as the sputtering gas and reaction gas, respectively. A monolayer Ta 2 O 5 coating was prepared on Ti6Al4V substrate as a control. Table 2 lists the details of the coating preparation parameters.

Coatings Characterization
The crystal structure of the coatings was investigated by XRD (Ultima IV, Rigaku Corporation, Tokyo, Japan) analysis. The surface and fractured cross-sectional morphology, elemental composition, and map of the coatings were characterized by SEM (SU8000, Hitachi Group, Tokyo, Japan) equipped with EDS. The roughness of the coated surface was detected with AFM (EasyScan2, Nanosurf, Basel, Switzerland). The elemental chemical states in Cu-MTa 2 O 5 coatings were determined by XPS (EscaLab 250Xi, Thermo Fisher Scientific Inc., Waltham, MA, US).

Scratch Test
The scratch test is the most common method to quantitatively evaluate the adhesion strength of a coating [36]. In this work, MFT-4000 multifunctional surface test equipment (LICP, Lanzhou, China) was employed to investigate the bonding strength of a coating deposited on the surface of a Ti6Al4V alloy. During the measurement, a diamond indenter with a radius of 200 µm was applied to the coating surface with a normal load ranging from 0 to 20 N and moved with a loading rate of 10 N/min and a scratch length of 6.0 mm. Meanwhile, the changes of the acoustic emission, friction force, friction coefficient, and normal force with the scratch distance were continuously recorded. The critical load (L c ) was determined by comprehensively analyzing the changes in friction force and microscopic observation. Two critical loads of L c1 and L c2 were used to characterize the failure mode of the coating. L c1 denotes the load required for initial chipping in the scratch track or next to the scratch track, while L c2 denotes the load required for complete failure and represents the coating adhesion strength [52]. To determine the failure position and failure mode of the coating, an ultra-depth of field optical microscope (KH-7700, Seika Corporation, Tokyo, Japan) was used to observe the morphology of the scratch.

Contact Angle Measurements
The water contact angle is usually used to evaluate the wettability of the material [53]. The contact angles of uncoated and coated Ti6Al4V alloy were detected by a JC20001 contact angle goniometer (POWEREACH, Shanghai, China) with the sessile drop method (using a 2-µL distilled water droplet). The droplet images were obtained by the optical system of the goniometer and the contact angle was measured from the images.

Electrochemical Experiments
Electrochemical experiments were performed using an SP-15/20A electrochemical workstation (Bio-logic Scientific Instruments, Seyssinet-Pariset, France) with a typical three-electrode configuration. A saturated Ag/AgCl electrode was used as the reference electrode (RE), and a platinum sheet was used as the counterelectrode (CE). The uncoated and coated Ti6Al4V were employed as the working electrodes (WE), which were fully coated with epoxy resin, except for a 1-cm 2 area for exposure to SBF solution. Simulated body fluid (SBF) electrolyte with a 7.4 pH was used [54]. Potentiodynamic polarization curves were recorded using a scanning rate of 1 mV/s from −0.3 V to +2.0 V. The corrosion potential (E corr) and corrosion current density (I corr ) were obtained from the polarization curves using the Tafel extrapolation method.

Antibacterial Tests
The plate counting technique is usually employed for investigating the antibacterial activity of modified coatings [55]. Gram-positive S. aureus is one of the most common pathogens causing biomaterial-centered infection (BCI) and peri-implant inflammation [56]. In this study, S. aureus strain ATCC 6538 obtained from Guangzhou Industrial Microorganism Testing Center (Guangzhou, China) was used to evaluate the antibacterial activity of the coatings with the plate counting method. Before the tests, all the specimens were sterilized at 121 • C, 0.1 MPa for 30 min. A sterilized 0.9% NaCl solution was used to modulate the concentration of the bacterial suspension.
The sterilized sample was placed in a centrifuge tube containing 10 7 CFU/mL bacterial suspension of 4 mL and incubated at 37 • C for 24 h. After incubation, the specimen was taken out and the bacterial suspension was fully mixed by a mixer. Then 100 µL of the mixed bacterial suspension were inoculated in Luria-Bertani (LB) agar plates and cultivated at 37 • C for 24 h. Finally, the bacterial colonies grown were counted by an automatic colony detection instrument (Sphere Flash, Barcelona, Spain). The antimicrobial rate (P) was obtained by Equation (1) [40]: where X and Y are the number of living bacteria observed on the uncoated and coated Ti6Al4V, respectively.

Statistical Analysis
Each experiment was carried out in triplicate and the result is expressed as mean ± standard deviation (SD). To investigate the statistical significance between various sample groups, one-way analysis of variance was applied and p < 0.05 was regarded as statistically significant.

Microstructural Characterization
The surface topographies of the coated Ti6Al4V samples are displayed in Figure 2. The surface of the Ta 2 O 5 coating was flat, smooth, and the grain size was uniform (Figure 2a). In contrast, the grain of the Cu-Ta 2 O 5 coating surface ( Figure 2c) is larger (10-100 nm), with clear grain boundariesand larger grain gaps, indicating the lower compactness of the outer layer. The increase in the grain size of the Cu-MTa 2 O 5 coating relates to the doping amount of Cu [57]. Three-dimensional AFM topographies with an area of 5 µm × 5 µm showed that the main features of both coating surfaces were characterized by peak-type particles (Figure 2b,d). The particles size of Ta 2 O 5 coating was small, with an average roughness Ra value of 3.48 ± 0.3 nm, while the roughness of the Cu-MTa 2 O 5 coating was 30 ± 0.8 nm. A low element doping amount in the coating can increase the compactness of the coating and reduce the surface roughness, while a high doping amount increases the surface roughness [58]. Nanomaterials 2019, 9, x FOR PEER REVIEW 6 of 19

Microstructural Characterization
The surface topographies of the coated Ti6Al4V samples are displayed in Figure 2. The surface of the Ta2O5 coating was flat, smooth, and the grain size was uniform ( Figure 2a). In contrast, the grain of the Cu-Ta2O5 coating surface ( Figure 2c) is larger (10-100 nm), with clear grain boundariesand larger grain gaps, indicating the lower compactness of the outer layer. The increase in the grain size of the Cu-MTa2O5 coating relates to the doping amount of Cu [57]. Three-dimensional AFM topographies with an area of 5 μm × 5 μm showed that the main features of both coating surfaces were characterized by peak-type particles (Figure 2b,d). The particles size of Ta2O5 coating was small, with an average roughness Ra value of 3.48 ± 0.3 nm, while the roughness of the Cu-MTa2O5 coating was 30 ± 0.8 nm. A low element doping amount in the coating can increase the compactness of the coating and reduce the surface roughness, while a high doping amount increases the surface roughness [58].    content in the coating mainly connects with the preparation parameters such as sputtering power, oxygen flow rate, and ratio of oxygen to argon.    1085 nm, and 410 nm, respectively. Depending on the structure ( Figure 1) and preparation parameters ( Table 2) of the Cu-MTa 2 O 5 coating, it was deduced that the S1, S2, and S3 regions corresponded to the Ti film, TiO 2 -Ta 2 O 5 /Ta 2 O 5 film, and Cu-Ta 2 O 5 film, respectively. In the S2 region, there was no observable interface between the TiO 2 -Ta 2 O 5 film and Ta 2 O 5 film, and there were no microspores and cracks observed. This contributes to the lowering of the interfacial stress and improves the adhesion of the coating. In addition, the density of the S3 region was significantly lower than that of the S2 region, which was related to a large amount of Cu incorporation. thicknesses of 162 nm, 1085 nm, and 410 nm, respectively. Depending on the structure ( Figure 1) and preparation parameters (Table 2) of the Cu-MTa2O5 coating, it was deduced that the S1, S2, and S3 regions corresponded to the Ti film, TiO2-Ta2O5/Ta2O5 film, and Cu-Ta2O5 film, respectively. In the S2 region, there was no observable interface between the TiO2-Ta2O5 film and Ta2O5 film, and there were no microspores and cracks observed. This contributes to the lowering of the interfacial stress and improves the adhesion of the coating. In addition, the density of the S3 region was significantly lower than that of the S2 region, which was related to a large amount of Cu incorporation.    thicknesses of 162 nm, 1085 nm, and 410 nm, respectively. Depending on the structure ( Figure 1) and preparation parameters (Table 2) of the Cu-MTa2O5 coating, it was deduced that the S1, S2, and S3 regions corresponded to the Ti film, TiO2-Ta2O5/Ta2O5 film, and Cu-Ta2O5 film, respectively. In the S2 region, there was no observable interface between the TiO2-Ta2O5 film and Ta2O5 film, and there were no microspores and cracks observed. This contributes to the lowering of the interfacial stress and improves the adhesion of the coating. In addition, the density of the S3 region was significantly lower than that of the S2 region, which was related to a large amount of Cu incorporation.    Figure 6 shows the XRD spectrum of the uncoated and coated Ti6Al4V specimens. There were no characteristic peaks of the Cu and Ta2O5 in the XRD spectrum of the coating (Figure 6a), indicating that the Cu and Ta2O5 in the coating are amorphous structures [59]. The appearance of an amorphous structure relates to factors such as low deposition temperature and small sputtering power [60,61]. The previous study found that a Ta2O5 film deposited at room temperature begins to crystallize above an annealing temperature of about 800 °C [62], while the crystallization temperature of the Cu film was above 300 °C [20].
Additionally, the diffraction peaks of Ti appeared in the XRD pattern of the coatings, which may be the diffusion of the Ti from the intermediate layer or the substrate due to the porous structure and small thickness of the coating. Compared with the Ta2O5 coating, the Cu-MTa2O5 coating had a bigger thickness and weaker Ti peak strength. Analyzing the XRD high-resolution diagram (Figure 6b), a hump in the range of 20-40°of 2θ was observed, and its position was consistent with the interval diffraction peak of the Ta2O5 (JCPDS card No. 25-0922). The chemical valence of the elements in the coating should be further determined using XPS.  Figure 6 shows the XRD spectrum of the uncoated and coated Ti6Al4V specimens. There were no characteristic peaks of the Cu and Ta 2 O 5 in the XRD spectrum of the coating (Figure 6a), indicating that the Cu and Ta 2 O 5 in the coating are amorphous structures [59]. The appearance of an amorphous structure relates to factors such as low deposition temperature and small sputtering power [60,61]. The previous study found that a Ta 2 O 5 film deposited at room temperature begins to crystallize above an annealing temperature of about 800 • C [62], while the crystallization temperature of the Cu film was above 300 • C [20].  Figure 7 shows the XPS spectrum of the Cu-MTa2O5 coating. As shown in Figure 7a, the Ta 4f, O 1s, and Cu 2p spectra appear in the XPS survey spectrum of the coating, revealing the existence of O, Cu, and Ta in the Cu-MTa2O5 coatings.The Ta4f spectrum displayed in Figure 7b contains two peaks at the binding energies of 25.8 eV and 27.7 eV, corresponding to Ta 4f7/2 and Ta 4f5/2, respectively, indicating that Ta exists in the Cu-MTa2O5 coating in the form of Ta2O5, which is consistent with a previous report [63]. Figure 7c shows the XPS spectrum of the Cu 2p that was used to analyze the chemical bonds of  Additionally, the diffraction peaks of Ti appeared in the XRD pattern of the coatings, which may be the diffusion of the Ti from the intermediate layer or the substrate due to the porous structure and small thickness of the coating. Compared with the Ta 2 O 5 coating, the Cu-MTa 2 O 5 coating had a bigger thickness and weaker Ti peak strength. Analyzing the XRD high-resolution diagram (Figure 6b), a hump in the range of 20-40 • of 2θ was observed, and its position was consistent with the interval diffraction peak of the Ta 2 O 5 (JCPDS card No. 25-0922). The chemical valence of the elements in the coating should be further determined using XPS.
relates to CuO, while the peak at 932 eV relates to Cu or Cu2O [49]. In the deconvolution diagram of Cu 2p1/2 (Figure 7e), the 951.8 eV peak comes from copper or Cu2O, while the 953.7eV peak comes from CuO. Furthermore, two other shake-up peaks belong to CuO [46], which further confirms the presence of CuO in Ta2O5 [64]. The doped Cu exists in the Cu-MTa2O5 coating in the oxidation state of copper because copper can easily be oxidized [65].
The high-resolution XPS spectrum of O1s, shown in Figure 7c, contains three deconvoluted peaks. The large peak with the binding energy of 531.3 eV was assigned to Ta2O5 [66], while the peaks with a binding energy of 530.2 eV and 529.8 eV correspond to Cu2O and CuO, respectively [67,68]. The above results indicate that Ta exists in the Cu-MTa2O5 coatings in the form of Ta2O5, while Cu exists in CuO and Cu2O. Ta2O5 affects the enhancement of the anticorrosion and biocompatibility of the metal implant materials [3,28], while Cu plays an important role in enhancing the antibacterial activity of the Cu-MTa2O5 coating [69].  Figure 8 displays the scratch curves and scratch track images of the scratch test. As shown in Figure 8a, the initial chipping appeared on the Ta2O5 coatings at a distance of 0.01 mm with a corresponding load (Lc1) of 0.03 N. When the diamond indenter moved 0.828 mm, the Ta2O5 coating completely fell off with an applied load of 2.76 N, indicating that the critical load Lc2 of Ta2O5 was 2.76 N. Figure 8b shows that the critical loads Lc1 and Lc2 for initial fragmentation and continuous  Figure 7 shows the XPS spectrum of the Cu-MTa 2 O 5 coating. As shown in Figure 7a, the Ta 4f, O 1s, and Cu 2p spectra appear in the XPS survey spectrum of the coating, revealing the existence of O, Cu, and Ta in the Cu-MTa 2 O 5 coatings.The Ta4f spectrum displayed in Figure 7b contains two peaks at the binding energies of 25.8 eV and 27.7 eV, corresponding to Ta 4f 7/2 and Ta 4f 5/2 , respectively, indicating that Ta exists in the Cu-MTa 2 O 5 coating in the form of Ta 2 O 5 , which is consistent with a previous report [63]. Figure 7c shows the XPS spectrum of the Cu 2p that was used to analyze the chemical bonds of Cu species. It was observed that the broad Cu 2p 3/2 and Cu2p 1/2 peaks can both be deconvoluted into two peaks, as shown in Figure 7d,e, respectively. In the Cu2p 3/2 spectrum, the peak at 933.9 eV relates to CuO, while the peak at 932 eV relates to Cu or Cu 2 O [49]. In the deconvolution diagram of Cu 2p 1/2 (Figure 7e), the 951.8 eV peak comes from copper or Cu 2 O, while the 953.7eV peak comes from CuO. Furthermore, two other shake-up peaks belong to CuO [46], which further confirms the presence of CuO in Ta 2 O 5 [64]. The doped Cu exists in the Cu-MTa 2 O 5 coating in the oxidation state of copper because copper can easily be oxidized [65].

Adhesion Strength
The high-resolution XPS spectrum of O1s, shown in Figure 7c, contains three deconvoluted peaks. The large peak with the binding energy of 531.3 eV was assigned to Ta 2 O 5 [66], while the peaks with a binding energy of 530.2 eV and 529.8 eV correspond to Cu 2 O and CuO, respectively [67,68]. The above results indicate that Ta exists in the Cu-MTa 2 O 5 coatings in the form of Ta 2 O 5 , while Cu exists in CuO and Cu 2 O. Ta 2 O 5 affects the enhancement of the anticorrosion and biocompatibility of the metal implant materials [3,28], while Cu plays an important role in enhancing the antibacterial activity of the Cu-MTa 2 O 5 coating [69].

Wettability
Wettability is one of the important surface properties that affect the response of cells/bacteria to implant materials [71]. The wettability of the surface of the material will be better and the biological activity will be higher due to the smaller contact angle [72]. Figure 9 shows the water contact angle data and water droplet images on uncoated Ti6Al4V, Ta2O5, and Cu-MTa2O5 coated Ti6Al4V. The The bonding mechanism between the coating and the substrate is complicated, and the bonding strength can be affected by many factors, such as the surface state of the substrate, preparation parameters, substrate temperature, intermediate layer, coating thickness, post-heat treatment [1,4,29,70], etc. For a multilayer Cu-MTa 2 O 5 coating, its adhesion strength is higher than that of the single layer Ta 2 O 5 coating due to the introduction of the multiple intermediate layers of Ta 2 O 5 -TiO 2 /TiO 2 /Ti. This is mainly because the element content in the Cu-MTa 2 O 5 coating sample gradually changed from the Ti6Al4V substrate to the outer layer of the coating after the addition of the intermediate multilayer, which reduces the performance mismatch and interfacial stress between the Ta 2 O 5 coating and the Ti6Al4V substrate, and enhances the bonding strength of the coating. Of course, the bonding strength of the Cu-MTa 2 O 5 coating is not sufficient for clinical applications. In the future, it will be further improved by optimizing the preparation parameters, increasing the coating thickness, and performing post-heat treatment.

Wettability
Wettability is one of the important surface properties that affect the response of cells/bacteria to implant materials [71]. The wettability of the surface of the material will be better and the biological activity will be higher due to the smaller contact angle [72]. Figure 9 shows the water contact angle data and water droplet images on uncoated Ti6Al4V, Ta 2 O 5 , and Cu-MTa 2 O 5 coated Ti6Al4V. The uncoated Ti6Al4V showed a contact angle of 73 ± 1 • , indicating a hydrophilic surface. The coated sample had a larger contact angle than the uncoated samples, wherein the Cu-MTa 2 O 5 coating sample exhibited the largest contact angle (105.5 ± 1.5 • ), showing hydrophobicity. It is well known that the greater the roughness of the material surfaces, the greater the water contact angle [73]. The surface roughness value of the Cu-MTa 2 O 5 coating was about 8 times larger than that of the Ta 2 O 5 coating (Figure 2), and thus exhibits a larger contact angle. For medical implant materials, a hydrophobic surface is considered helpful in stopping early bacterial adherence and forming microbial membranes, thus improving the anticorrosion properties of the materials [74].

Wettability
Wettability is one of the important surface properties that affect the response of cells/bacteria to implant materials [71]. The wettability of the surface of the material will be better and the biological activity will be higher due to the smaller contact angle [72]. Figure 9 shows the water contact angle data and water droplet images on uncoated Ti6Al4V, Ta2O5, and Cu-MTa2O5 coated Ti6Al4V. The uncoated Ti6Al4V showed a contact angle of 73 ± 1°, indicating a hydrophilic surface. The coated sample had a larger contact angle than the uncoated samples, wherein the Cu-MTa2O5 coating sample exhibited the largest contact angle (105.5 ± 1.5°), showing hydrophobicity. It is well known that the greater the roughness of the material surfaces, the greater the water contact angle [73]. The surface roughness value of the Cu-MTa2O5coating was about 8 times larger than that of the Ta2O5 coating (Figure 2), and thus exhibits a larger contact angle. For medical implant materials, a hydrophobic surface is considered helpful in stopping early bacterial adherence and forming microbial membranes, thus improving the anticorrosion properties of the materials [74].

Corrosion Behavior
Anticorrosion property is one of the critical indicators to evaluate the safety of metal implant materials. Figure 10 displays the potentiodynamic polarization curves acquired from uncoated Ti6Al4V and the coating specimens in SBF. The corrosion parameters such as corrosion potential (E corr ) and corrosion current density (I corr ) were derived by Tafel extrapolation of the polarization curves and listed in Table 2. The E corr expresses the tendency to corrode and the I corr shows the corrosion rate [75]. The E corr of the Ti6Al4V was about −0.42 V vs. Ag/AgCl in SBF, while the values of Ta 2 O 5 and Cu-MTa 2 O 5 coating specimens moved toward the positive potential, which was −0.25 V and −0.08V, respectively, suggesting that corrosion of Ti6Al4V in SBF is retarded by the Ta 2 O 5 coating and the Cu-MTa 2 O 5 coating. The I corr values of the Cu-MTa 2 O 5 and Ta 2 O 5 coating samples were 0.74 µA/cm 2 and 0.48 µA/cm 2 , respectively, which are lower than those of Ti6Al4V (1.07 µA/cm 2 ). These results signify that the I corr of Cu-MTa 2 O 5 and Ta 2 O 5 coating samples is reduced about 1.5-fold and 2-fold, respectively, compared with the Ti6Al4V substrate in SBF. The polarization resistance R p is usually used to evaluate the corrosion difficulty of materials [76]. As shown in Table 3, the R p value of the coated sample was approximately 222% to 362% larger than that of Ti6Al4V. It is well accepted that high E corr , low I corr , and high R p indicate the good anticorrosion property of the material [3]. Therefore, among the three samples, Ta 2 O 5 coating samples show the best corrosion resistance, followed by Cu-MTa 2 O 5 coating samples and uncoated Ti6Al4V titanium alloy.
composition and structure of materials, surface state, environmental conditions [77,78], etc. Compared with the bare Ti6Al4V samples, the improvement in corrosion resistance of the coated Ti6Al4V samples may be mainly attributed to the high stability of the Ta2O5 ceramic coating. Previous studies have shown that Ta2O5 films exhibit extreme resistance to dissolution over all combinations of pH and potential encountered in biomedical applications [79], effectively preventing corrosive ions from eroding the substrate. The reduction in corrosion resistance of Cu-MTa2O5 may be due in part to the low density of the outer Cu-Ta2O5 film (Figure 2b), which makes it easy for the corrosive medium to reach the surface of the Ti6Al4V substrate through the coating defects and corrode the substrate. On the other hand, Cu2O in the coating easily reacts with the chloride ions in the solution as follows [80]: The product CuCl2 of Equation (2) readily dissolves and releases Cu 2+ ions, leading to the destruction of surface integrity and the reduction of the compactness of the coating, thus aggravating the corrosion of the substrate.  Figure 10. Potentiodynamic polarization curves of the coated specimens and Ti6Al4V. Table 3. Corrosion parameters obtained from the polarization curves shown in Figure 10. There are many factors that influence the corrosion behavior of materials, such as the composition and structure of materials, surface state, environmental conditions [77,78], etc. Compared with the bare Ti6Al4V samples, the improvement in corrosion resistance of the coated Ti6Al4V samples may be mainly attributed to the high stability of the Ta 2 O 5 ceramic coating. Previous studies have shown that Ta 2 O 5 films exhibit extreme resistance to dissolution over all combinations of pH and potential encountered in biomedical applications [79], effectively preventing corrosive ions from eroding the substrate. The reduction in corrosion resistance of Cu-MTa 2 O 5 may be due in part to the low density of the outer Cu-Ta 2 O 5 film (Figure 2b), which makes it easy for the corrosive medium to reach the surface of the Ti6Al4V substrate through the coating defects and corrode the substrate. On the other hand, Cu 2 O in the coating easily reacts with the chloride ions in the solution as follows [80]:

Specimen
The product CuCl 2 of Equation (2) readily dissolves and releases Cu 2+ ions, leading to the destruction of surface integrity and the reduction of the compactness of the coating, thus aggravating the corrosion of the substrate.

Antibacterial Property
The antibacterial properties of the Ti6Al4V alloy, Ta 2 O 5 , and Cu-MTa 2 O 5 coatings against S. aureus colonies were investigated. Figure 11 showed the quantitative results of the live bacteria after 24 hours of culture at 37 • C on LB agar plates. A large number of bacterial colonies were observed on the surface of Ti6Al4V-and Ta 2 O 5 -coated Ti6Al4V, while there were only two bacterial colonies on the Cu-MTa 2 O 5 coating surface. The results showed that the Cu-MTa 2 O 5 coating had strong antibacterial activity against S. aureus with an antibacterial rate of 99.8± 2%, while polished Ti6Al4V alloy did not possess antimicrobial activity.
dissolved from the coating surface and diffused into the bacterial solution. Then, the copper ions were adsorbed on the bacterial cell wall by electrostatic action, limiting the bacterial activity and resulting in its metabolic disorder and death [81]. Moreover, after bacterial contact, copper ions pierced the cell membrane and entered the cell's interior, destroying the integrity of the cell wall and causing bacterial death due to the loss of substances such as protein and reducing sugar [82]. In addition, copper ions entering the cells destroyed the respiratory chain of the bacteria, produced high levels of reactive oxygen species (ROS), degraded DNA, proteins and lipids, and eventually led to bacterial death [11,83]. Due to the complex mechanism of the bactericidal activity conferred by copper, the antibacterial activity of Cu-MTa2O5 coating may also come from the nanostructure of the coating surface, and its antibacterial mechanism may be a combination of various mechanisms, which need to be studied further.
The experimental results also showed that the Ta2O5 coating had a certain bactericidal ability, with an antibacterial rate of 30.1± 5%. The antibacterial activity of Ta2O5 coating was related to its amorphous structure [84] and the release of Ta 5+ ions [85]. At present, there are very few studies on the antibacterial mechanism of Ta2O5, and detailed work needs to be carried out.

Conclusions
In summary, a multilayer composite coating with excellent antibacterial and anticorrosion properties was successfully deposited on a biomedical alloy, Ti6Al4V, using magnetron sputtering. The coatings, with a total thickness of about 1657 nm, were uniform, amorphous, and hydrophobic. The bond strength of the multilayer coating increased by 198% compared to the single-layer Ta2O5 coating. Moreover, the corrosion resistance and antibacterial properties of the Cu-MTa2O5 coating samples were significantly improved compared to the uncoated Ti6Al4V. Therefore, this study The antibacterial activity of the Cu-MTa 2 O 5 coating closely relates to the copper ions released from the coating surface [49]. When the coating was exposed to the bacterial solution, copper ions dissolved from the coating surface and diffused into the bacterial solution. Then, the copper ions were adsorbed on the bacterial cell wall by electrostatic action, limiting the bacterial activity and resulting in its metabolic disorder and death [81]. Moreover, after bacterial contact, copper ions pierced the cell membrane and entered the cell's interior, destroying the integrity of the cell wall and causing bacterial death due to the loss of substances such as protein and reducing sugar [82]. In addition, copper ions entering the cells destroyed the respiratory chain of the bacteria, produced high levels of reactive oxygen species (ROS), degraded DNA, proteins and lipids, and eventually led to bacterial death [11,83]. Due to the complex mechanism of the bactericidal activity conferred by copper, the antibacterial activity of Cu-MTa 2 O 5 coating may also come from the nanostructure of the coating surface, and its antibacterial mechanism may be a combination of various mechanisms, which need to be studied further.
The experimental results also showed that the Ta 2 O 5 coating had a certain bactericidal ability, with an antibacterial rate of 30.1± 5%. The antibacterial activity of Ta 2 O 5 coating was related to its amorphous structure [84] and the release of Ta 5+ ions [85]. At present, there are very few studies on the antibacterial mechanism of Ta 2 O 5 , and detailed work needs to be carried out.

Conclusions
In summary, a multilayer composite coating with excellent antibacterial and anticorrosion properties was successfully deposited on a biomedical alloy, Ti6Al4V, using magnetron sputtering. The coatings, with a total thickness of about 1657 nm, were uniform, amorphous, and hydrophobic. The bond strength of the multilayer coating increased by 198% compared to the single-layer Ta 2 O 5 coating. Moreover, the corrosion resistance and antibacterial properties of the Cu-MTa 2 O 5 coating samples were significantly improved compared to the uncoated Ti6Al4V. Therefore, this study provides an alternative medical function coating for a titanium alloy surface. However, further work such as optimization of the preparation parameters, improvement of the bond strength, evaluation of the biocompatibility, in vivo experiments, etc., needs to be carried out.