Hexosomes with Undecylenic Acid Efficient against Candida albicans

Due to the growing issues with fungal infections, especially with Candida, there is still a need to develop novel anti-Candida materials. One of the known antifungal agents is undecylenic acid (UA), which still cannot be efficiently used due to its oily nature, and thus limited solubility. By taking advantage of the properties of UA, we developed an emulsion with hexagonal phase, i.e., hexosomes, whose structure and morphology was studied by small-angle X-ray scattering and cryo-electron microscopy, respectively. The presence of UA in the hexosome was confirmed by spectroscopy. Moreover, we studied the anti-Candida effect of hexosomes and their cytotoxicity toward human cells. The minimal inhibitory concentration for the 50% and 90% Candida-growth reduction was found at 0.01 and 0.16 wt % hexosomes, respectively (i.e., 2 and 32 pghex/C.a.cell, respectively). The percentage of metabolically active Candida was reduced by 72–96% at hexosome concentrations of 1.0–8.2 pghex/C.a.cell as compared to untreated Candida. Furthermore, at the same concentration range the embedded filamentation test after 24 and 48 h showed the inhibition of both the filamentation and growth of Candida, while the preliminary toxicity test showed that hexosomes were nontoxic for human cells. All these render the here-developed hexosomes with UA efficient and promising anti-Candida agents.


Introduction
Fungal infections are recognized as one of the major health issues affecting millions of people worldwide [1,2] and Candida is among the four fungal species that pose the largest issue [1]. There are numerous Candida species, but Candida albicans (C.a.) is among those most found in clinical cases [3]. Therefore, numerous studies have been dedicated to combat C.a. [3][4][5][6][7][8][9][10][11]. In fact, the current state-of-the-art clinical treatments, which are mainly based on echinocandins and fluconazole, still cannot combat candidiasis, and the mortality from systemic candidiasis still remains~50% [1]. Among the numerous factors which contribute to the pathogenicity of C.a., the ability to switch between yeast and hyphal growth forms (dimorphism) is recognized as the most critical one [6,12]. Thus, novel anti-Candida materials, which would ideally inhibit both the C.a. growth and the yeast-to-hyphae transition are urgently need [4,6,9,12,13].
There are numerous drug delivery systems, but lipid-based liquid crystals (LLC) are one of the most promising and, consequently, there is increasing interest in their use and development. LLC are The obtained emulsion had a negative surface potential with a ζ of −31 ± 1 mV. Moreover, the emulsions, stored at 4 • C, were stable over one month and the average hydrodynamic diameters, D h , obtained by three measurements by DLS, were 286 ± 14 nm and 342 ± 50 nm in intensity and volume weighted distributions, respectively (see Supplementary Figure S1).
All of the lipid components as well as the final LLC were investigated using FTIR spectroscopy ( Figure 1). The region between 1500 and 900 cm −1 is often referred to as the fingerprint region, related to both C-O-C stretching and C-H bending [33]. The strong peak in the region at 1700-1800 cm −1 in DU and UA spectra can be attributed to carbonyl (C=O) stretching vibration mode (saturated aliphatic esters or carboxylic acid, respectively). In the case of UA, a prominent additional peak is observed at 1640 cm −1 and is assigned to C=C vibration mode. This peak is very weak in the case of DU. The strong bands in the region 2800-3000 cm −1 may be indicative of symmetrical and asymmetrical stretching of C-H bonds in -CH 3 and -CH 2 . Finally, the O-H stretch appears as a broad peak between 3000 and 3500 cm −1 for both DU and LLC. The analysis of FTIR spectra showed that both UA and DU are present in the final LLC particles. However, since LLC contain 70% of DU and 30% of UA in their nanostructure, the most prominent vibration bands on the spectrum are those of DU. All of the lipid components as well as the final LLC were investigated using FTIR spectroscopy ( Figure 1). The region between 1500 and 900 cm −1 is often referred to as the fingerprint region, related to both C-O-C stretching and C-H bending [33]. The strong peak in the region at 1700-1800 cm −1 in DU and UA spectra can be attributed to carbonyl (C=O) stretching vibration mode (saturated aliphatic esters or carboxylic acid, respectively). In the case of UA, a prominent additional peak is observed at 1640 cm −1 and is assigned to C=C vibration mode. This peak is very weak in the case of DU. The strong bands in the region 2800-3000 cm −1 may be indicative of symmetrical and asymmetrical stretching of C-H bonds in -CH3 and -CH2. Finally, the O-H stretch appears as a broad peak between 3000 and 3500 cm −1 for both DU and LLC. The analysis of FTIR spectra showed that both UA and DU are present in the final LLC particles. However, since LLC contain 70% of DU and 30% of UA in their nanostructure, the most prominent vibration bands on the spectrum are those of DU.   Figure S2). The DU/water system is known to form a Pn3m cubic mesophase in excess of water [19]. However, the molecular packing of the DU (composed of ~60% of monolinolein) can be affected by the hydrocarbon chain space obtained upon the solubilization of an additive component [16,34]. In our case, due to the hydrophobic nature of UA, its addition to DU led to an increase of the negative curvature and to the formation of hexosomes, as observed by cryo-TEM. The hexagonal phase can be clearly identified by the presence of curved striations (Figure 2c Figure S2). The DU/water system is known to form a Pn3m cubic mesophase in excess of water [19]. However, the molecular packing of the DU (composed of~60% of monolinolein) can be affected by the hydrocarbon chain space obtained upon the solubilization of an additive component [16,34]. In our case, due to the hydrophobic nature of UA, its addition to DU led to an increase of the negative curvature and to the formation of hexosomes, as observed by cryo-TEM. The hexagonal phase can be clearly identified by the presence of curved striations (Figure 2c) or hexagonal periodicity (Figure 2b) commonly observed in liquid crystalline nanoparticles characterized by reverse hexagonal symmetry.
LLC mesophases are readily identified through SAXS, Figure 2d, where each phase can be identified by its characteristic Bragg peak positions. The H 2 phase is identified by reflections at 1: bicontinuous cubic phase (Im3m), the Bragg peaks occur at q = √ 2: √ 4: √ 6: √ 8. This mixed Pn3m + Im3m cubic phase has been previously observed in cubosomes formed by the utilized ratio of dimodan + F127 [35]. The lattice parameters of the two cubic phases were found to be a (Im3m) = 142.3 Å and a (Pn3m) = 115.6 Å. The coexistence of these phases approximately follows the Bonnet relation, described as the ratio of the cubic unit cell parameters of the Im3m:Pn3m [36]. In this case, a ratio of 1.231 was obtained, which is comparable with the literature value of 1.279 [36]. LLC mesophases are readily identified through SAXS, Figure 2d, where each phase can be identified by its characteristic Bragg peak positions. The H2 phase is identified by reflections at 1:√3:√4. These results confirmed that the presence of the UA additive results in the formation of the H2 phase with a lattice parameter of 45.6 Å. On the contrary, in the blank dispersion, composed only of DU stabilized by F127, no H2 phase was observed. For the double diamond cubic phase (Pn3m), the Bragg reflections occur at relative positions in q at √2:√3:√4:√6; while for the primitive bicontinuous cubic phase (Im3m), the Bragg peaks occur at q = √2:√4:√6:√8. This mixed Pn3m + Im3m cubic phase has been previously observed in cubosomes formed by the utilized ratio of dimodan + F127 [35]. The lattice parameters of the two cubic phases were found to be a(Im3m) = 142.3 Å and a(Pn3m) = 115.6 Å. The coexistence of these phases approximately follows the Bonnet relation, described as the ratio of the cubic unit cell parameters of the Im3m:Pn3m [36]. In this case, a ratio of 1.231 was obtained, which is comparable with the literature value of 1.279 [36].

Anti-Candida Properties of Hexosomes
Typically, results of the biological tests are expressed as a function of the studied material (here hexosomes) or an active component (here UA). However, even though biological tests are performed with the same concentration of the studied material, the ratio of the studied material and cells are very often different between tests, due to the difference in the various test parameters (such as the volume of the cells' suspension, concentration of cells, or volume of the studied material). Therefore, comparing results between such tests can be difficult and can lead to misinterpretations. In order to overcome this common issue, we presented results of all here-performed biological tests as a function of the concentration of hexosomes per cell (human cell if not indicated differently in the case of C.a. cells).
The effect of hexosomes containing UA on the growth of C.a. cells was studied for different concentrations of hexosomes prepared in two-fold serial dilution starting from the final hexosome concentration of 1.2784 wt % (corresponding to 0.3559 wt % of UA, 255.7 pghex/C.a.cell, or 71.2 pgUA/C.a.cell). The lowest final hexosome concentration in the seral dilution was 0.0025 wt % (corresponding to 0.0007 wt % of UA, 0.5 pghex/C.a.cell, or 0.1 pgUA/C.a.cell). After 24 h of incubation at 37 °C, the absorbance of the C.a. cells' suspensions containing the given concentrations of

Anti-Candida Properties of Hexosomes
Typically, results of the biological tests are expressed as a function of the studied material (here hexosomes) or an active component (here UA). However, even though biological tests are performed with the same concentration of the studied material, the ratio of the studied material and cells are very often different between tests, due to the difference in the various test parameters (such as the volume of the cells' suspension, concentration of cells, or volume of the studied material). Therefore, comparing results between such tests can be difficult and can lead to misinterpretations. In order to overcome this common issue, we presented results of all here-performed biological tests as a function of the concentration of hexosomes per cell (human cell if not indicated differently in the case of C.a. cells).
The effect of hexosomes containing UA on the growth of C.a. cells was studied for different concentrations of hexosomes prepared in two-fold serial dilution starting from the final hexosome concentration of 1.2784 wt % (corresponding to 0.3559 wt % of UA, 255.7 pg hex /C.a.cell, or 71.2 pg UA /C.a.cell). The lowest final hexosome concentration in the seral dilution was 0.0025 wt % (corresponding to 0.0007 wt % of UA, 0.5 pg hex /C.a.cell, or 0.1 pg UA /C.a.cell). After 24 h of incubation at 37 • C, the absorbance of the C.a. cells' suspensions containing the given concentrations of hexosomes was measured at 600 nm, A 600 . In order to calculate the percentage of C.a. growth, the obtained results were expressed as average percentages of A 600 readings as compared to the control (0% hexosomes). The so-obtained results are given in Figure 3a as a function of hexosome concentration per C.a. cell, while the same results as a function of hexosome (i.e., UA) concentration are given in Supplementary Figure S3. It can be seen that MIC50 was at about 2 pg hex /C.a.cell, while MIC90 was found at about 32 pg hex /C.a.cell. Since the dose of UA to which C.a. cells are exposed could not be measured, we calculated the maximal theoretical amount of UA to which a C.a. cell could be exposed to in a given experiment (if all UA from the hexosomes would come into the suspension of the incubated C.a. cells) by dividing the total mass of UA in hexosomes by the number of incubated C.a. cells. Therefore, the percentage of C.a. growth is also given as a function of the so-obtained UA concentrations per C.a. cell (Figure 3b). The corresponding MIC50 and MIC90 are at about 0.6 and 8.9 pg UA /C.a.cell, respectively. Importantly, the value for MIC90 (8.9 pg UA /C.a.cell, corresponding to 0.0445 wt % of UA) is much lower than a previously reported value (256 µg UA /mL) for C.a. cells incubated at 10 7 C.a.cells/mL [37]. This is also lower than MIC90 reported in our previous study, which was found to be between 25 and 50 pg UA /C.a.cell also at a C.a. concentration of 10 7 C.a.cells/mL [38]. This difference could be due to the reported higher efficacy of the nanostructured emulsions as compared to the other drug-delivery systems [14,15], but also due to the different concentrations tested in these studies. Indeed, it is known that an increase of the cells' concentration increases the drug-resistance of C.a. cells [39,40]. These results highlight the high anti-Candida effect of our novel hexosomes loaded with UA. In order to assess this effect after a longer period, the measurements were taken not only after 24 h of incubation, but also after 72 h. Interestingly, after 72 h of incubation, the percentage of C.a. growth in the presence of various hexosome (i.e., UA) concentrations was almost the same as that after 24 h (Supplementary Figure S4), confirming the efficacy of the hexosomes against C.a.  Figure S3. It can be seen that MIC50 was at about 2 pghex/C.a.cell, while MIC90 was found at about 32 pghex/C.a.cell. Since the dose of UA to which C.a. cells are exposed could not be measured, we calculated the maximal theoretical amount of UA to which a C.a. cell could be exposed to in a given experiment (if all UA from the hexosomes would come into the suspension of the incubated C.a. cells) by dividing the total mass of UA in hexosomes by the number of incubated C.a. cells. Therefore, the percentage of C.a. growth is also given as a function of the so-obtained UA concentrations per C.a. cell (Figure 3b). The corresponding MIC50 and MIC90 are at about 0.6 and 8.9 pgUA/C.a.cell, respectively. Importantly, the value for MIC90 (8.9 pgUA/C.a.cell, corresponding to 0.0445 wt % of UA) is much lower than a previously reported value (256 µgUA/mL) for C.a. cells incubated at 10 7 C.a.cells/mL [37]. This is also lower than MIC90 reported in our previous study, which was found to be between 25 and 50 pgUA/C.a.cell also at a C.a. concentration of 10 7 C.a.cells/mL [38]. This difference could be due to the reported higher efficacy of the nanostructured emulsions as compared to the other drug-delivery systems [14,15], but also due to the different concentrations tested in these studies. Indeed, it is known that an increase of the cells' concentration increases the drug-resistance of C.a. cells [39,40]. These results highlight the high anti-Candida effect of our novel hexosomes loaded with UA. In order to assess this effect after a longer period, the measurements were taken not only after 24 h of incubation, but also after 72 h. Interestingly, after 72 h of incubation, the percentage of C.a. growth in the presence of various hexosome (i.e., UA) concentrations was almost the same as that after 24 h (Supplementary Figure S4), confirming the efficacy of the hexosomes against C.a.  Since the results of the previous test showed MIC50 and MIC90 at about 2 and 13 pg hex /C.a.cell, respectively (corresponding to 0.6 and 8.9 pg UA /C.a.cell, respectively), we focused the rest of our study on the concentrations in the vicinity of 2 pg hex /C.a.cell (i.e., 0.6 pg UA /C.a.cell). We performed an 2,3-bis(2-methoxy-4-nitro-5-sulfo-phenyl)-2H-tetrazolium-5-carboxanilide (XTT) test, which measures the number of metabolically active C.a. cells exposed to the hexosome at given concentrations (that are approximately 1.0, 4.1, and 8.2 pg hex /C.a.cell, i.e., 0.28, 1.14, and 2.28 pg UA /C.a.cell). The results given in Figure 4 show the relative number of metabolically active C.a. cells in the presence of hexosomes (as compared to the control without hexosomes); the same result as a function of hexosome and UA concentrations are given in Supplementary Figure S5. We found that the percentage of metabolically active C.a. cells was 28% and 13% at 1.0 and 4.1 pg hex /C.a.cell, respectively, and only 4% at the highest hexosome concentration. In other words, the number of metabolically active C.a. cells was reduced by 72%, 87%, and 96% at the three studied hexosome concentrations, respectively, as compared to the control without hexosomes. The obtained XTT results showed a considerable reduction of the number of metabolically active C.a. cells in the presence of hexosomes with UA. Thus, the developed hexosomes showed antifungal activity towards C.a. cells at an early stage of colonization (after 24 h). This was so far considered as a substantial issue in the use of UA, which is typically restrained by the concentrations of the released UA, which is insufficient to combat C.a., especially at an early stage of colonization [37]. It is interesting to note that~0.28 pg UA (more precisely, 0.2847 pg UA ), corresponding to the amount of UA per C.a. cell showing an already substantial anti-Candida effect, corresponds to 9.3 × 10 9 UA molecules, while the estimation of the total number of wall proteins in a C.a. yeast cell is 2.9 × 10 6 proteins [41].
Since the results of the previous test showed MIC50 and MIC90 at about 2 and 13 pghex/C.a.cell, respectively (corresponding to 0.6 and 8.9 pgUA/C.a.cell, respectively), we focused the rest of our study on the concentrations in the vicinity of 2 pghex/C.a.cell (i.e., 0.6 pgUA/C.a.cell). We performed an 2,3bis(2-methoxy-4-nitro-5-sulfo-phenyl)-2H-tetrazolium-5-carboxanilide (XTT) test, which measures the number of metabolically active C.a. cells exposed to the hexosome at given concentrations (that are approximately 1.0, 4.1, and 8.2 pghex/C.a.cell, i.e., 0.28, 1.14, and 2.28 pgUA/C.a.cell). The results given in Figure 4 show the relative number of metabolically active C.a. cells in the presence of hexosomes (as compared to the control without hexosomes); the same result as a function of hexosome and UA concentrations are given in Supplementary Figure S5. We found that the percentage of metabolically active C.a. cells was 28% and 13% at 1.0 and 4.1 pghex/C.a.cell, respectively, and only 4% at the highest hexosome concentration. In other words, the number of metabolically active C.a. cells was reduced by 72%, 87%, and 96% at the three studied hexosome concentrations, respectively, as compared to the control without hexosomes. The obtained XTT results showed a considerable reduction of the number of metabolically active C.a. cells in the presence of hexosomes with UA. Thus, the developed hexosomes showed antifungal activity towards C.a. cells at an early stage of colonization (after 24 h). This was so far considered as a substantial issue in the use of UA, which is typically restrained by the concentrations of the released UA, which is insufficient to combat C.a., especially at an early stage of colonization [37]. It is interesting to note that ~0.28 pgUA (more precisely, 0.2847 pgUA), corresponding to the amount of UA per C.a. cell showing an already substantial anti-Candida effect, corresponds to 9.3 × 10 9 UA molecules, while the estimation of the total number of wall proteins in a C.a. yeast cell is 2.9 × 10 6 proteins [41]. Since the drug-resistance of C.a. cells increases along with the cells' concentration [39,40], the percentage of C.a. growth should be higher in the XTT test than in the MIC-determination test for similar drug-to-cell ratios (concentration 10 6 and 10 5 C.a.cells/mL, respectively). However, in our case, percentages of metabolically active C.a. cells in the XTT test were lower than percentages of the C.a. growth in the MIC-determination test. This suggests that some of the C.a. cells, which contributed to percentages of the C.a. growth, were not metabolically active.
In order to gain information on the C.a. cell type and the development in the presence of hexosomes at concentrations used in the XTT test as compared to the control without hexosomes, we performed an embedded filamentation assay for both 24 and 48 h of incubation (representative photomicrographs are given in Figure 5). The concentrations of hexosomes in agar were chosen to give the same values of hexosome concentration per C.a. cell as in the XTT test. C.a. cells in the control sample, i.e., embedded in agar without hexosomes, were, after 24 h of incubation, in the form of spindle-shaped colonies comprising yeast cells with rare peripheral hyphae and/or pseudohyphae, which had lateral yeasts (Figure 5a), as often reported [42,43]. Simultaneously, C.a. cells embedded  Since the drug-resistance of C.a. cells increases along with the cells' concentration [39,40], the percentage of C.a. growth should be higher in the XTT test than in the MIC-determination test for similar drug-to-cell ratios (concentration 10 6 and 10 5 C.a.cells/mL, respectively). However, in our case, percentages of metabolically active C.a. cells in the XTT test were lower than percentages of the C.a. growth in the MIC-determination test. This suggests that some of the C.a. cells, which contributed to percentages of the C.a. growth, were not metabolically active.
In order to gain information on the C.a. cell type and the development in the presence of hexosomes at concentrations used in the XTT test as compared to the control without hexosomes, we performed an embedded filamentation assay for both 24 and 48 h of incubation (representative photomicrographs are given in Figure 5). The concentrations of hexosomes in agar were chosen to give the same values of hexosome concentration per C.a. cell as in the XTT test. C.a. cells in the control sample, i.e., embedded in agar without hexosomes, were, after 24 h of incubation, in the form of spindle-shaped colonies comprising yeast cells with rare peripheral hyphae and/or pseudohyphae, which had lateral yeasts (Figure 5a), as often reported [42,43]. Simultaneously, C.a. cells embedded in agar with hexosomes formed yeast colonies with smaller sizes than those in the control and without any hyphae (Figure 5b-d). After 48 h of incubation, control C.a. cells embedded in agar without hexosomes formed numerous radially emerging peripheral hyphae, pseudohyphae, and lateral yeasts from spindle-shaped yeast colonies (Figure 5e). Since the incubation was at 37 • C, all embedded colonies formed hyphae, as expected [43]. In contrast, C.a. spindle-shaped colonies in agar with hexosomes consisted of yeast with rare yeast outgrowths and without filamentation even after 48 h of incubation (Figure 5f-h). We did not observe large differences between samples with different hexosome concentrations at both timepoints. Overall, these results showed that all studied hexosomes concentrations were sufficient to inhibit the yeast-to-hyphae transition and to suppress C.a. growth.
in agar with hexosomes formed yeast colonies with smaller sizes than those in the control and without any hyphae (Figures 5b-d). After 48 h of incubation, control C.a. cells embedded in agar without hexosomes formed numerous radially emerging peripheral hyphae, pseudohyphae, and lateral yeasts from spindle-shaped yeast colonies (Figure 5e). Since the incubation was at 37 °C, all embedded colonies formed hyphae, as expected [43]. In contrast, C.a. spindle-shaped colonies in agar with hexosomes consisted of yeast with rare yeast outgrowths and without filamentation even after 48 h of incubation (Figures 5f-h). We did not observe large differences between samples with different hexosome concentrations at both timepoints. Overall, these results showed that all studied hexosomes concentrations were sufficient to inhibit the yeast-to-hyphae transition and to suppress C.a. growth. The above given study demonstrates that the developed hexosomes with UA have an anti-Candida effect. Nevertheless, to use such antifungal materials in patients, the material need to display an as low as possible toxicity towards human cells. Hence, we performed a preliminary cytotoxicity study (with concentrations of hexosomes adjusted to give the same values per cell as in the previous two tests) by using the common absorbance-based 3-(4,5-dimethylthiazol-2-yl)-5-(3carboxymethoxypenyl)-2-(4-sulfophenyl)-2H-tetrazolium (MTS) test. However, in such tests the absorbance of the studied nanomaterial (here hexosomes) can contribute to the absorbance of the test itself [44], resulting in unrealistic results (see Supplementary Figure S6). Therefore, we corrected the measured absorbance by subtracting the absorbance of the corresponding amount of hexosomes in the same medium (for details see Materials and Methods). The results ( Figure 6) showed a small decrease in cell viability (87%) at the highest concentration of hexosomes per cell (8.2 pghex/cell); the same results as a function of the concentration of hexosome and UA are given in Supplementary Figure S7. Thus, our hexosomes are promising for applications in patients. The above given study demonstrates that the developed hexosomes with UA have an anti-Candida effect. Nevertheless, to use such antifungal materials in patients, the material need to display an as low as possible toxicity towards human cells. Hence, we performed a preliminary cytotoxicity study (with concentrations of hexosomes adjusted to give the same values per cell as in the previous two tests) by using the common absorbance-based 3-(4,5-dimethylthiazol-2-yl)-5-(3-carboxymethoxypenyl)-2-(4-sulfophenyl)-2H-tetrazolium (MTS) test. However, in such tests the absorbance of the studied nanomaterial (here hexosomes) can contribute to the absorbance of the test itself [44], resulting in unrealistic results (see Supplementary Figure S6). Therefore, we corrected the measured absorbance by subtracting the absorbance of the corresponding amount of hexosomes in the same medium (for details see Materials and Methods). The results ( Figure 6) showed a small decrease in cell viability (87%) at the highest concentration of hexosomes per cell (8.2 pg hex /cell); the same results as a function of the concentration of hexosome and UA are given in Supplementary Figure S7. Thus, our hexosomes are promising for applications in patients. in agar with hexosomes formed yeast colonies with smaller sizes than those in the control and without any hyphae (Figures 5b-d). After 48 h of incubation, control C.a. cells embedded in agar without hexosomes formed numerous radially emerging peripheral hyphae, pseudohyphae, and lateral yeasts from spindle-shaped yeast colonies (Figure 5e). Since the incubation was at 37 °C, all embedded colonies formed hyphae, as expected [43]. In contrast, C.a. spindle-shaped colonies in agar with hexosomes consisted of yeast with rare yeast outgrowths and without filamentation even after 48 h of incubation (Figures 5f-h). We did not observe large differences between samples with different hexosome concentrations at both timepoints. Overall, these results showed that all studied hexosomes concentrations were sufficient to inhibit the yeast-to-hyphae transition and to suppress C.a. growth. The above given study demonstrates that the developed hexosomes with UA have an anti-Candida effect. Nevertheless, to use such antifungal materials in patients, the material need to display an as low as possible toxicity towards human cells. Hence, we performed a preliminary cytotoxicity study (with concentrations of hexosomes adjusted to give the same values per cell as in the previous two tests) by using the common absorbance-based 3-(4,5-dimethylthiazol-2-yl)-5-(3carboxymethoxypenyl)-2-(4-sulfophenyl)-2H-tetrazolium (MTS) test. However, in such tests the absorbance of the studied nanomaterial (here hexosomes) can contribute to the absorbance of the test itself [44], resulting in unrealistic results (see Supplementary Figure S6). Therefore, we corrected the measured absorbance by subtracting the absorbance of the corresponding amount of hexosomes in the same medium (for details see Materials and Methods). The results ( Figure 6) showed a small decrease in cell viability (87%) at the highest concentration of hexosomes per cell (8.2 pghex/cell); the same results as a function of the concentration of hexosome and UA are given in Supplementary Figure S7. Thus, our hexosomes are promising for applications in patients. So far, UA has been used as a structural agent to build the walls of vesicles, which could be used as nanocontainers [45]. For instance, a recent study exploited the self-assembling behavior of the glycerol monoester of undecylenic acid [46]. Solely concerning UA, Bulut et al. reported the antifungal activity of UA released from emulsions and showed a higher release of UA from emulsions as compared to other liquid phases [47]. However, there were no other reports of UA employed as an antifungal agent in LLC. Beyond LLC, very few studies on materials containing UA for antifungal applications have been reported. For instance, our previous study reported poly(methyl methacrylate) (PMMA) loaded with UA, which showed fungicidal effect against both sessile (attached) and planktonic (free-floating) C.a. cells [38]. Besides that, a few studies on one commercial acrylic denture liner (i.e., Coe Soft, GC America, Alsip, IL, USA) reported that it contains UA (70 mM UA [48], or 1-5% UA [49], or a non-specified UA concentration [37]), while according to the producer this product contains zinc undecylenate [50].
Here, a new efficient anti-Candida agent was developed in the form of hexosomes loaded with UA. This material simultaneously showed the inhibition of C.a. growth and filamentation (i.e., morphogenesis or yeast-to-hyphae transition) at an early stage of colonization (24 h). We also showed that hexosomes were nontoxic to human cells at the studied concentrations, which have been efficient against C.a. This is the first reported example of hexosomes with UA, which showed high efficacy against C.a., and of the large potential of LLC nanocarriers for anti-Candida applications and, more generally, for anti-fungal applications.
By taking into consideration global health issues with fungal infections [1,2], the hexosomes reported herein are promising for future use as anti-Candida carriers.
Hexosomes were prepared by a one-pot mixing of 285.9 mg of UA, 668.0 mg of DU, 75.8 mg of F127, and 9 g of deionized water (10 wt % of dispersed material in 90 wt % of water) by applying ultrasound for 15 min using a high intensity ultrasonic tip (Branson Digital Sonifier, Branson Ultrasonic SA, Carouge, Switzerland) at 20% of the maximum power with a 1-s pulse and 1-s pause. No external sample cooling was used. The mixture was allowed to equilibrate at least for 24 h at room temperature before any dilution or biological trials.

Physicochemical Characterisation of Hexosomes
Fourier transform IR (FTIR) spectra of DU, UA, and hexosome suspensions were obtained with a Perkin Elmer Spectrum One spectrometer (series: 69288, Perkin Elmer, Schwerzenbach, Switzerland). Transmittance from 3900 to 650 cm −1 were given as the average of eight measured scans for each curve with a resolution of 4.00 cm −1 .
The zeta potential as well as hydrodynamic diameters (D h ) of the sample were measured at room temperature in zeta potential cuvettes or acrylic cuvettes (Sarstedt, Nümbrecht, Germany), respectively, with a Zetasizer Nano ZS (Malvern Instruments, Worcestershire, UK). Using dynamic light scattering, the reported values were obtained from the average of 3 × 15 measurements after the sample was diluted 1000 times.
For cryo-TEM analysis, an electron microscopy grid (Agar scientific, Essex, UK) with holey carbon film was held in tweezers and 4-5 µL of the sample solution was applied on the grid. The tweezers were mounted in an automatic plunge freezing apparatus (Vitrobot, FEI, Eindhoven, The Netherlands) to control the humidity and temperature. After blotting, the grid was immersed in a small metal container with liquid ethane that was cooled from the outside by liquid nitrogen. The speed of cooling was such that ice crystals do not have time to form. Observation was made at −170 • C in a Tecnai F 20 microscope (FEI, Eindhoven, The Netherlands) operating at 200 kV and equipped with a cryo-specimen holder Gatan 626 (Warrendale, PA, USA). Digital images were recorded with a FalconIII (FEI) camera 4098 × 4098 pixels. Magnification was between 20,000 and 30,000×, using a defocus range of −2 to −3 µm.
The morphology of the dispersed lipid samples was investigated by Small Angle X-ray scattering (SAXS) with a NanoMax-IQ (Rigaku Innovative Technologies, Auburn Hills, MI, USA) at 37 • C. 2D SAXS patterns were radially averaged, yielding 1D SAXS curves of I(q). The scattering vector, q, was calibrated using silver behenate with the q-range from 0.06 to 0.6 Å −1 , where q is the length of the scattering vector defined by q = 4π/λ sin (θ/2), with λ being the wavelength (λ = 0.1524 nm) and θ being the scattering angle. The dispersed lipid samples were loaded into 2.0-mm quartz capillaries and sealed with epoxy. Measurements were performed at 37 • C. The mean lattice parameter, a, was deduced from the corresponding set of observed interplanar distances, d (d = 2π/q), using the appropriate scattering law for the phase structure.

Microorganism and Culture Conditions
In this study, we used C.a. ATCC 10231 strain (Microbiologics, LOT 443-518-1, Cat. no. 0443P). C.a. stock was kept at −80 • C and, after recovery, kept on Sabouraud 4% Glucose Agar (SGA; Sigma Aldrich 84088) and stored at 4 • C during the experiments. For the determination of the minimum inhibitory concentration and the filamentation assay, the strain was sub-cultured on SGA for 24 h at 37 • C and an inoculum was prepared from freshly grown colonies on SGA at a concentration of 10 5 C.a.cells/mL in 0.9% sterile NaCl (Sodium chloride, 99.5%; Acros, 44730-2500 autoclaved at 121 • C for 20 min). For the XTT assay, an inoculum was adjusted to a concentration of 10 6 C.a. cells/mL in RPMI 1640 medium (Sigma Aldrich, R6504-10x1L).

Minimum Inhibitory Concentration (MIC)
Two-fold serial dilution of hexosomes was made in RPMI 1640 medium in a 96-well plate and 100 µL of C.a. suspension (concentration 10 5 C.a.cells/mL) was added to every well, which gave a final maximal hexosome concentration of 1.2784 wt % (corresponding to 0.3559 wt % of UA, or to 255.68 pg hex /C.a.cell, or to 71.17 pg UA /C.a.cell). The last sample in the serial dilution contained a final minimal hexosome concentration of 0.0025 wt % (corresponding to 0.0007 wt % of UA, or to 0.50 pg hex /C.a.cell, or to 0.14 pg UA /C.a.cell). Another 96-well plate, which contained the same two-fold dilution of hexosomes in RPMI 1640 medium and 100 µL of medium, was treated under same conditions and served as controls. Both plates were incubated at 37 • C for 24 h and 72 h. Upon incubation, the absorbance the so-obtained suspensions was measured at 600 nm, using a microplate reader (TECAN Infinite M200, Tecan, Männedorf, Switzerland). From the obtained absorbance values, the percentages of viable C.a. cells were calculated with the following equation: where Abs(C.a.; Hex; medium), Abs(Hex; medium), Abs(C.a.; medium), and Abs(medium) denote the absorbance of liquid with C.a. and hexosomes and medium, with hexosomes and medium, with C.a. and medium, and only with RPMI medium, respectively.

XTT Assay
The preparation of XTT/menadione solution was conducted as follows. For the XTT reduction assay, the XTT (Cayman, CAS 111072-31-2,)-saturated solution at 0.5 g/L was prepared in sterile PBS (Dulbecco's Phosphate Buffered Saline, Zen-Bio, Inc., Research Triangle Park, NC, USA, DPBS-1000), sterilized by filtration using a 0.22 µm pore-size filter, aliquoted into working volumes, and stored at −20 • C when not used. The stock of the XTT solution was thawed before every assay, and the menadione (Cayman Chemicals, Hamburg, Germany, CAY15950-25g) solution previously prepared in the acetone as a 10 mM stock solution was added to the XTT to have a final menadione concentration of 1 µM. The so-obtained solution is referred to as XTT/menadione.
In the wells of 96-well plates, we first added 100 µL of a C.a. inoculum (at a concentration of where Abs(C.a.; Hex; medium), Abs(Hex; medium), Abs(C.a.; medium), and Abs(medium) denote the absorbance of the liquid containing XTT: with C.a. and hexosomes and medium, with hexosomes and medium, with C.a. and medium, and only with RPMI medium, respectively.

Embedded Filamentation Assay
Hexosome suspensions in YPD-agar were prepared according to a previously described protocol [38] in order to form three different concentrations of hexosomes per C.a. cell, which corresponds to the concentrations in the XTT assay: 1.0227, 4.0908, and 8.1816 pg hex /C.a.cell, and to the concentrations of UA per C.a. cell of 0.2847, 1.1388, and 2.2776 pg UA /C.a.cell. Briefly, after autoclaving and natural cooling down to approximately 40 • C, 5 mL of YPD-agar was added into 50-mL polypropylene flat falcon tubes (Falcon 62.559.001) containing a suitable amount of hexosome suspension. To 5 mL of the so-prepared hexosome suspensions, 100 µL of C.a. (concentration 10 6 C.a.cells/mL) was added, mixed, and poured into sterile Petri dishes (with a diameter of 30 mm). After natural cooling down, Petri dishes were incubated at 37 • C and studied by an optical microscope (Nikon Eclipse Ti-E inverted microscope, Nikon Instruments Europe BV, Amsterdam, The Netherlands) after 24 h and 48 h. Photomicrographs were taken through the agar matrix.

Cytotoxicity Study of Hexosomes
Human A549 cells were cultured in RPMI-1640 medium (Sigma-Aldrich) supplemented with 10% fetal bovine serum and 2% 5000 U·mL −1 penicillin, 5 mg·mL −1 Streptomycin and 10 mg·mL −1 neomycin (Sigma-Aldrich). 4000 A549 cells per well were cultured in 96-well plates at 37 • C for 24 h, and afterwards exposed for an additional 24 h to 100 µL media containing suitable amounts of hexosomes. The same amounts of hexosomes in 100 µL media without cells, as well as cells treated only with medium served as controls. After 24 h of incubation, the supernatant of each well was removed. Then, 100 µL of MTS solution (CellTiter 96 ® AQueous One Solution Cell Proliferation Assay from Promega, Madison, WI, USA, diluted six times in medium) was added to the cells. After 2 h of incubation in the dark, the absorbance of the formazan product was measured with a microplate reader (Tecan Infinite M200 where Abs(cells; Hex; medium), Abs(Hex; medium), Abs(cells; medium), and Abs(medium) denote the absorbance of liquid containing MTS: with cells and hexosomes and medium, with hexosomes and medium, with cells and medium, and only with medium, respectively.

Supplementary Materials:
The following are available online at http://www.mdpi.com/2079-4991/8/2/91/s1, Figure S1: The average hydrodynamic diameters; Figure S2: The additional transmission electron microscopy micrographs of hexosomes, Figure S3: The effect of hexosomes on the Candida albicans (C.a.) cell growth, Figure S4: The effect of hexosomes on the Candida albicans (C.a.) cell growth, Figure S5: The percentages of metabolically active Candida albicans (C.a.) cells, Figure S6: Viability of human A594 cells incubated for 24 h with different concentrations of hexosomes, Figure S7: Viability of human A594 cells incubated for 24 h with different concentrations of hexosomes.