Strontium-Cobaltite-Based Perovskite (SrCoO3) for Solar-Driven Interfacial Evaporation Systems for Clean Water Generation

Solar-driven evaporation technology is often used in areas with limited access to clean water, as it provides a low-cost and sustainable method of water purification. Avoiding salt accumulation is still a substantial challenge for continuous desalination. Here, an efficient solar-driven water harvester that consists of strontium-cobaltite-based perovskite (SrCoO3) anchored on nickel foam (SrCoO3@NF) is reported. Synced waterways and thermal insulation are provided by a superhydrophilic polyurethane substrate combined with a photothermal layer. The structural photothermal properties of SrCoO3 perovskite have been extensively investigated through state-of-the-art experimental investigations. Multiple incident rays are induced inside the diffuse surface, permitting wideband solar absorption (91%) and heat localization (42.01 °C @ 1 sun). Under 1 kW m−2 solar intensity, the integrated SrCoO3@NF solar evaporator has an outstanding evaporation rate (1.45 kg/m2 h) and solar-to-vapor conversion efficiency (86.45% excluding heat losses). In addition, long-term evaporation measurements demonstrate small variance under sea water, illustrating the system’s working capacity for salt rejection (1.3 g NaCl/210 min), which is excellent for an efficient solar-driven evaporation application compared to other carbon-based solar evaporators. According to the findings of this research, this system offers significant potential for producing fresh water devoid of salt accumulation for use in industrial applications.


Introduction
Fresh water scarcity is emerging as a global concern because of limited resources, an expanding global population, and climate change, which is only expected to worsen, especially in underdeveloped nations and regions [1,2]. Since three quarters of the Earth is covered by oceans, which contain 97% of the total water on the planet, sea water is a seemingly endless resource for clean water [3][4][5]. There is an urgent need to develop an effective, affordable, and long-lasting desalination technology. In recent years, there has been a surge in exploring solar-powered water evaporation owing to its environmentally friendly 2 of 14 character [6][7][8]. Unlike bulk-heating-based evaporation, solar-driven interfacial water evaporation can effectively localize thermal energy at the water-air interface, achieving high efficiency of water distillation [9][10][11][12]. To develop efficient solar-powered interfacial water evaporation, cost-effective photothermal materials with high solar absorption and phototo-thermal conversion are required [11,12]. Several photothermal materials have been reported so far, i.e., metallic nanoparticles, carbon-based materials, wood-based materials, narrow-bandgap semiconductors, and two-dimensional materials [12][13][14][15]. The use of these materials in a variety of two-and three-dimensional evaporators has resulted in a broad spectrum of water evaporation rates under the same solar irradiation (1 kW m −2 ) [16]. Integrating highly efficient photothermal materials for solar energy harvesting and solar steam generation into various two-or three-dimensional evaporators is the focus of one active area of study at present [17].
To date, several photothermal materials have been engineered to accomplish broadband solar absorption that can conform to global conditions [18]. Transition metal oxides are ubiquitous and have unique physical characteristics and vital uses [19]. The perovskite family is a functionally diverse group of compounds having the chemical formula ABO 3 [8]. Typically, alkali or alkali earth metals and transition metals make up the A and B sites, respectively. However, each compound may contain a variety of atoms on the A or B sites functioning as dopants, increasing functional versatility [20]. SrCoO 3 is a perovskite oxide and has a perfect perovskite cubic structure with the space group Pm3m, containing alkaline earth metals and transition metals [8]. In SrCoO 3 , conduction band originates from hybridization of the Co 3d and O 2p orbitals, whereas the O 2s and 4p orbitals are positioned below the conduction band. Redox processes involved in oxygen reduction and evolution on SrCoO 3 are heavily controlled by the electronic structure, and are used for energy storage and conversion applications [21][22][23]. SrCoO 3 has been investigated for diverse applications, including solar cells [24], sensors [25], electrolyzers [23], and thermochemical water-splitting reactors for H 2 production [26], due to its high oxygen permeation flux resulting from its high levels of both ionic and electronic conductivities and improved catalytic activity [21][22][23]26]. The non-stoichiometry of oxygen has a major impact on defining its electronic characteristics. Zhao et al. [27] performed in situ ambient pressure X-ray spectroscopy of SrCoO 3 to reveal its electronic structure and to investigate the electronic structure change with its oxygen stoichiometry and phase, which may then be used to explore the development of SrCoO 3 for multifunctional applications.
Here, we report an efficient solar-driven water harvester that consists of strontiumcobaltite-based perovskite (SrCoO 3 ) anchored on nickel foam (SrCoO 3 @NF) for fresh water generation. The solar evaporator provides synced water transport and good thermal insulation due to a superhydrophilic polyurethane foam (PU) as a substrate combined with a photothermal layer, as shown in Figure 1. The structural photothermal properties of SrCoO 3 perovskite have been extensively investigated through state-of-the-art experimental investigations. Multiple incident rays are induced inside the diffuse surface, allowing omnidirectional solar absorption (91%) and heat localization (42.01 • C @ 1 sun). Under 1 kW m −2 solar intensity, the integrated SrCoO 3 @NF solar evaporator has an outstanding evaporation rate (1.45 kg/m 2 h) and solar-to-vapor conversion efficiency (86.45% excluding heat losses). In addition, long-term evaporation measurements demonstrate small variance under sea water, illustrating its working capacity for salt rejection (1.3 g NaCl/210 min), which is excellent for an efficient solar-driven evaporation application compared to other carbon-based solar evaporators. This research demonstrates substantial capacity for producing fresh water free of salt ions for industrial uses.

Synthesis of Strontium-Cobaltite-Based Perovskite (SrCoO3)
Cobalt nitrate (Co(NO3)26H2O), and strontium nitrate (Sr(NO3)2) were mixed in a solution of ethylenediaminetetraacetic acid (EDTA), ammonium hydroxide (NH4OH), and citric acid (C6H8O7). The prepared mixture was heated at 260 °C while being continuously stirred in order to produce a homogeneous gel. The gel was allowed to dry in an oven at 200 °C before being pulverized into a powder. The SrCoO3 powder was then exposed to air and heated to 1000 °C for 12 h.

SrCoO3-Coated Nickel Foam Solar Evaporator
The fabrication of the self-regenerating perovskite-material-based solar evaporator was achieved using a simple coating method. A specified quantity of the final SrCoO3 powder was combined with a specified amount of terpineol (C10H18O), which is a volatile binder, to form a homogeneous slurry in a mortar pestle. The nickel foam (1.6 mm thickness) was then crafted into a circular shape with a diameter of three centimeters as an interfacial layer for the deposition of SrCoO3. A prepared homogeneous slurry of photothermal material was deposited on the nickel foam using a commercial tool. The coated nickel foam was then dried in the oven overnight at 60 °C to remove the terpineol. The nickel foam retained good hydrophilicity and microporous structure after drying. Finally, the SrCoO3 anchored on the nickel foam was placed over the PU foam substrate cut to the same diameter as the nickel foam to impart floatability with good water transport and minimum thermal conductivity. Overall, the fabrication was simple, repeatable, readily

Materials
Cobalt nitrate (Co(NO 3 ) 2 ·6H 2 O), strontium nitrate (Sr(NO 3 ) 2 ), and nickel foam substrate (20 cm × 20 cm, sheet) were purchased from Sinopharm Chemical Reagent Co. Ltd., Beijing, China. We purchased polyurethane foam (C 17 H 16 N 2 O 4 ) from Changzhou Longisland Automation Technology Co., Ltd., Changzhou, China. All of the compounds maintained a purity level of 99.9% and did not require additional purification. Deionized water was also employed in the experimental procedure.

Synthesis of Strontium-Cobaltite-Based Perovskite (SrCoO 3 )
Cobalt nitrate (Co(NO 3 ) 2 6H 2 O), and strontium nitrate (Sr(NO 3 ) 2 ) were mixed in a solution of ethylenediaminetetraacetic acid (EDTA), ammonium hydroxide (NH 4 OH), and citric acid (C 6 H 8 O 7 ). The prepared mixture was heated at 260 • C while being continuously stirred in order to produce a homogeneous gel. The gel was allowed to dry in an oven at 200 • C before being pulverized into a powder. The SrCoO 3 powder was then exposed to air and heated to 1000 • C for 12 h.

SrCoO 3 -Coated Nickel Foam Solar Evaporator
The fabrication of the self-regenerating perovskite-material-based solar evaporator was achieved using a simple coating method. A specified quantity of the final SrCoO 3 powder was combined with a specified amount of terpineol (C 10 H 18 O), which is a volatile binder, to form a homogeneous slurry in a mortar pestle. The nickel foam (1.6 mm thickness) was then crafted into a circular shape with a diameter of three centimeters as an interfacial layer for the deposition of SrCoO 3 . A prepared homogeneous slurry of photothermal material was deposited on the nickel foam using a commercial tool. The coated nickel foam was then dried in the oven overnight at 60 • C to remove the terpineol. The nickel foam retained good hydrophilicity and microporous structure after drying. Finally, the SrCoO 3 anchored on the nickel foam was placed over the PU foam substrate cut to the same diameter as the nickel foam to impart floatability with good water transport and minimum Nanomaterials 2023, 13, 1420 4 of 14 thermal conductivity. Overall, the fabrication was simple, repeatable, readily installable, and self-contained for usage in any location.

Material Characterization Information
Morphological analysis was performed using a field emission scanning electron microscope (FESEM, JSM7100F, JEOL, Tokyo, Japan) to characterize the samples. X-ray diffraction (XRD, Bruker D8 phaser, Coventry, UK) with Cu Kα radiation operating at a current up to 200 mA with a voltage of 40 kV was employed for the phase structural analysis. The elemental compositions were calculated using X-ray photoelectron spectroscopy (XPS) (Thermo Fisher Scientific Escalab 250Xi, Waltham, MA, USA) along with a monochromatic Mg Ka X-ray source. Absorption of the solar spectrum within a spectral range of 250-2500 nm was measured using an ultraviolet-visible near-infrared spectrophotometer (Shimadzu UV-vis-NIR UV-3600 double beam spectrophotometer, Kyoto, Japan) equipped with an integrating sphere. Light absorbance (A) was measured using the A = 1 − transmittance-reflectance formula. Surface temperature data were measured using an infrared camera (FLIR E4 Pro, Deer Park, NY, USA) which included two temperature-sensing thermocouples (K type, hand-held optical meter model). The Fourier-transform infrared (FT-IR) spectrum was obtained using an FT-IR tester (Nicolet iS50, Waltham, MA, USA).

Controlled Solar-Evaporation Experiment
The experimental procedure of vapor generation was performed using a solar simulator (PLS-FX300HU, Beijing Perfect light Technology Co., Ltd., Beijing, China) that can simulate multiple solar intensities up to 6 kW m −2 . In this experiment, a regular 1.5 G AM spectrum (exactly two standard terrestrial solar spectral irradiance spectra) along with an optical filter was used. The SrCoO 3 @NF solar evaporator was allowed to float freely on the water surface in a beaker (simulated sea water). The entire system was then placed on an advanced electronic balance (Mettler Toledo, ME204, the Strategy, Singapore) with a resolution of 0.001 g, which recorded the time-dependent mass variation to determine the evaporation rate, and exposed under simulated solar radiation (1 kW m −2 or one sun). After the stabilization of the evaporation system, the evaporation rates and optimized evaporation (solar to vapor conversion efficiency) were evaluated under one sun illumination (1 kW m −2 ). Inductively coupled plasma-optical emission spectrometry (ICP-OES, PerkinElmer Optima 8000, Waltham, MA, USA) was used to compare the salt concentrations before and after the water was treated. The temperature was maintained at 23 degrees Celsius and relative humidity was maintained at 40 percent throughout the experimental measurements.

Evaporation Efficiency
Using the following equation [4], we were able to determine the photothermal conversion efficiency (1-2) of the solar-driven evaporation system using SrCoO 3 @NF.
m v is the evaporation rate (1.45 kg m −2 h −1 ) under solar irradiance apart from the evaporation rate of pure water (mass flux), q solar is the incident solar energy (1 kW m −2 ), and h LV is the overall enthalpy of the liquid-to-vapor phase change including sensible heat as well as the phase enthalpy change, which can be measured using the following Equation (2) [4]: L indicates the latent heat of the phase change while it varies at different temperatures (2430 kJ kg −1 K −1 at 30 • C, and 2256 kJ kg −1 K −1 at 100 • C). Water has a specific heat capacity of 4.2 kJ kg −1 K −1 , denoted by C, and its temperature rises gradually, as shown by ∆T. During solar-powered experiments, the humidity was measured at approximately 40% and the temperature was recorded as 23.01 • C. Using the aforementioned formulas, SrCoO 3 @NF can produce vapor at 41.02 • C with a corresponding photothermal conversion efficiency of 86.45% (excluding the evaporation rate; measured in the dark to prevent heat loss due to convection and solar radiation).

Crystal Structure & Compositional Analysis
The efficient and self-regenerating perovskite oxide SrCoO 3 -based solar evaporator concentrates incident-captured light and effectively localizes heat at the interfacial surface, while the lower hydrophilic matrix provides a constant water supply and excellent salt tolerance during the process of continuous evaporation. Crystallographic, elemental, and morphological analysis of the SrCoO 3 powder was carried out via microscopic techniques, i.e., X-ray diffraction (XRD), X-ray photoelectron spectroscopy (XPS), Fourier-transform infrared spectroscopy (FTIR), and field emission scanning electron microscopy (FESEM). The XRD pattern of the perovskite SrCoO 3 powder is shown in Figure 2a 114), and (220) index planes, respectively, which is in good correspondence with previously reported data [28]. The XRD analysis reveals the formation of the tetragonal crystalline phase of the synthesized SrCoO 3 powder. Furthermore, X-ray photoelectron spectroscopy was performed to provide insight into the elemental and chemical composition of the SrCoO 3 . Figure 2b shows the full XPS survey of the SrCoO 3, showing the existence of several elements, i.e., Co2p, O1s, C1s, Sr3p, and Sr 3d, respectively. The highly resolved XPS spectrum of Co2p is demonstrated in Figure 2c, which has two splits into two distinct peaks due to the two spin-orbit doublets of the cobalt oxides positioned at 780.02 and 795.04 eV, corresponding to the Co 2p (1/2) and Co2p (3/2), respectively. The Co 2p (1/2) spin-orbit doublet is further deconvoluted into two sub-peaks located at 779.54 and 780.69 eV, assigned to the Co 3+ 2p (1/2) and Co 2+ 2p (1/2) configurations, respectively, while the Co 2p (3/2) spin-orbit doublet is further split into three distinct peaks at 794.67, 796.08, and 796.80 eV, attributed to the Co 3+ 2p (3/2) and Co 2+ 2p (3/2), respectively [8].

Surface Morphology
The morphological and microstructural analysis of the prepared perovskite SrCoO3 powder and SrCoO3 anchored on nickel foam was inspected using field-emission scanning electron microscopy (FESEM). Figure 3a-c shows the FESEM images of the SrCoO3, re- A highly resolved spectrum of the Sr 3d core level is shown in Figure 2d, which is split into four sub-peaks at 132.97, 133.32, 134.68, and 134.74 eV. The peaks at 132.97 and 134.68 eV account for the Sr 3d5/2 and Sr 3d3/2 of Sr 2+ , while the other two, at 133.32 and 134.74 eV, correspond to the Sr-O and SrCO 3 bonds, respectively [8]. The C1s spectrum of SrCoO 3 shows two main peaks, while three sub-peaks appear at 289.05, 284.32, and 284.53 eV, corresponding to the O-C=O, C-C, and C-O bonds, respectively, as shown in Figure 2e. The presence of various functional groups in SrCoO 3 was identified by performing Fourier-transform infrared spectroscopy (FTIR). Figure 2f demonstrates the FTIR spectrum of perovskite SrCoO 3 , revealing metal oxide (Sr-O, Co-O) bands with different vibration modes. The Co-O exhibits different vibrational modes ascribed to its different valences, Co 2+ , Co 3+ , and Co 4+ , with bands at the 591.96 cm −1 asymmetric vibrational modes of the tetrahedrally coordinated valence (Co 2+ ) and octahedrally coordinated valence (Co 3+ ). The assigned absorbance bands at 858 cm −1 and 1450 cm −1 show the existence of the carbonate in the specimen, and correspond to the twisting and vibration, respectively. The band at 855.39 cm −1 is due to the twisting and stretching of carbonate, revealing the presence of carbonate in the material. The other bands, 1000 to 3000 cm −1 , are mainly due to the M-O and M-O-M type vibrational modes (M=Sr, Co) [28]. The band at 1386.20 cm −1 corresponds to C-O-C type stretching, while the band at 3443.95 is due to OH stretching.

Surface Morphology
The morphological and microstructural analysis of the prepared perovskite SrCoO 3 powder and SrCoO 3 anchored on nickel foam was inspected using field-emission scanning electron microscopy (FESEM). Figure 3a-c shows the FESEM images of the SrCoO 3 , revealing randomly distributed homogeneous shapes with an average size of 100 nm and a high surface-to-volume ratio, which contributes to their enhanced light absorption and improved photothermal conversion. The FESEM image of the SrCoO 3 anchored on nickel foam (NF) is shown in Figure 3d, showing the highly porous structure of the NF, which facilitates simple water transport and hinders salt resistance. The SrCoO 3 is uniformly deposited on the walls of the NF, with which imparts a dense texture due to the homogeneously dispersed SrCoO 3 nanoparticles. This rough, dense morphology facilitates the development of an effective photothermal layer and helps to attain high surface temperatures because of the absorbed solar energy that is converted to heat at the top contact, rather than being allowed to freely diffuse downward into the bulk water.

Solar-Driven Evaporation Efficiency
Solar-driven interfacial evaporation and water desalination systems have promising potential for optimizing solar energy capture and effective photothermal conversion. Moreover, they support thermal localization at the air-liquid interface, maximized by the black composite surface, which diffuses the incident light inside the photothermal surface. The optical absorption of the SrCoO 3 was analyzed using UV-Vis spectroscopy in an integrated sphere over the full solar spectrum range (200-2500 nm). The absorption spectrum of the SrCoO 3 is shown in Figure 4a. The SrCoO 3 perovskite oxide exhibits enhanced absorption at up to 91% of the entire solar spectrum and reflects just 5%. Its superior absorption assists efficient solar-driven steam generation due to the material's rough black surface. The potential for solar light capture and the ability to effect photothermal conversion with minimal thermal conduction are crucial to the performance of any system based on solar energy. We created a solar steam generator based on the perovskite SrCoO 3 material, which has high solar absorption, high solar-to-thermal energy conversion, and low downward thermal conduction. We compared solar evaporation of pure water, PU foam, NF@PU, and SrCoO 3 @NF, for changes in surface temperature under 1 kW m −2 for 1 h using thermocouples embedded in the top layers, as shown in Figure 4b. Nanomaterials 2023, 13, x FOR PEER REVIEW 7 of 15

Solar-Driven Evaporation Efficiency
Solar-driven interfacial evaporation and water desalination systems have promising potential for optimizing solar energy capture and effective photothermal conversion. Moreover, they support thermal localization at the air-liquid interface, maximized by the black composite surface, which diffuses the incident light inside the photothermal surface. The optical absorption of the SrCoO3 was analyzed using UV-Vis spectroscopy in an integrated sphere over the full solar spectrum range (200-2500 nm). The absorption spectrum of the SrCoO3 is shown in Figure 4a. The SrCoO3 perovskite oxide exhibits enhanced absorption at up to 91% of the entire solar spectrum and reflects just 5%. Its superior absorption assists efficient solar-driven steam generation due to the material's rough black surface. The potential for solar light capture and the ability to effect photothermal conversion with minimal thermal conduction are crucial to the performance of any system based on solar energy. We created a solar steam generator based on the perovskite SrCoO3 material, which has high solar absorption, high solar-to-thermal energy conversion, and low downward thermal conduction. We compared solar evaporation of pure water, PU foam, NF@PU, and SrCoO3@NF, for changes in surface temperature under 1 kW m −2 for 1 h using thermocouples embedded in the top layers, as shown in Figure 4b.  The enhanced surface temperature of the SrCoO3@NF enabled maximum solar harvest, high heat localization inside the top photothermal layer, and outstanding thermal management using hydrophilic PU foam, which allows water transportation only up to the top surface, preventing downward thermal conduction. Therefore, the photothermal layer achieved a peak temperature of 42.21 °C, allowing for a rapid evaporation rate and The enhanced surface temperature of the SrCoO 3 @NF enabled maximum solar harvest, high heat localization inside the top photothermal layer, and outstanding thermal management using hydrophilic PU foam, which allows water transportation only up to the top surface, preventing downward thermal conduction. Therefore, the photothermal layer achieved a peak temperature of 42.21 • C, allowing for a rapid evaporation rate and improved efficiency. This enhanced surface temperature permits the rapid generation of steam, which eventually results in high photothermal conversion efficiency. The surface temperature of SrCoO 3 @NF was measured under multiple sun intensities. At higher solar intensities, the surface temperature of SrCoO 3 @NF is raised, reaching a maximum of 54.2 • C under 3 kW m −2 irradiation (Figure 4c). The interfacial thermal accumulation response of SrCoO 3 @NF under 1 kW m −2 was also captured using an infrared (IR) camera, as shown in Figure 4d-i. As expected, the SrCoO 3 @NF temperature reached 29.5 • C after 10 min, indicating a fast photothermal response. The creation of thermal localization during evaporation was facilitated by the synergistic impact of the anisotropic low thermal conductivity of SrCoO 3 @NF and the high photothermal conversion of the perovskite material SrCoO 3 . After 25 min of irradiation at a steady 1 kW m −2 , the SrCoO 3 @NF reached a surface temperature of 41.2 • C. The improved interfacial heat accumulation capability of the SrCoO 3 @NF solar evaporator is responsible for the rapid and dramatic increase in temperature.
The rough, dense surface texture of the interfacial photothermal layer of perovskite SrCoO 3 anchored on NF enables effective thermal localization by inherently dispersing incident solar intensity at the interface, which is the fundamental mechanism of the interfacial solar evaporation structure. We performed a comparative investigation of the four designed systems, i.e., pure water, PU foam, NF@PU, and SrCoO 3 @NF-based solar evaporators, to record evaporation performance under 1 kW m −2 solar intensity for 1 h. As expected, high surface temperature enabled fast evaporation and a high evaporation rate. The SrCoO 3 @NF solar evaporator attained a maximum evaporation rate of up to 1.45 kg m −2 h −1 , significantly higher than the other evaporation systems, i.e., pure water (0.32 kg m −2 h −1 ), PU foam (0.72 kg m −2 h −1 ), and NF@PU (1.08 kg m −2 h −1 ), as shown in Figure 5a. The evaporation rate of the self-regenerating SrCoO 3 @NF solar evaporator was also recorded under multiple solar intensities. A maximum evaporation rate of up to 4.06 kg m −2 h −1 was recorded under 3 k W m −2 , as shown in Figure 5b. The total efficiency of the solar-powered evaporation system can be optimized by good thermal management of the overall system. In order to design efficient heat accumulation for an effective solar-driven evaporation system, hydrophilic PU foam, which demonstrates high thermal insulation, is used. Here, a thermal conductivity meter (Hot Disk AB, TPS 2500, Sweden) was used to experimentally measure the thermal parameters of the manufactured solar-driven evaporation system. As soon as the power is turned on, a vertical sequence of temperature gradients (dT/dx) is created. The permeation heat transmission rate (q) via the SrCoO 3 @NF system can be found with the use of Fourier Equations (3) and (4) [4], as shown below: where k 1 is the thermal conductivity constant (1.05 W m −1 K −1 ) [4], x 1 is the glass slide thickness (3 mm), x 2 is the SrCoO 3 @NF thickness (30 mm), T 1 is the temperature of the heating interface, T 2 is the temperature of the bottom glass of the SrCoO 3 @NF, and T 3 is the temperature of the top glass of SrCoO 3 @NF. Given the heat transfer rate and the temperature gradient at thermal equilibrium in the material, the thermal conductivity (k) of SrCoO 3 @NF can be calculated using Equation (4) [4]:

Salt-Rejection Ability
The desalination of saltwater uses solar energy, which is a renewable and non-polluting energy source. Nevertheless, during prolonged operation in cooler temperatures, the water channels of evaporation structures tend to get obstructed due to the high salt content of sea water (3.5 wt% NaCl). The optimization of evaporation efficiency is ultimately stifled as a result of salt accumulation. Many effective methods have been proposed to address this problem, such as the introduction of innovative thin evaporation structures at the expense of thermal insulation. These delicate evaporation structures let heat escape from the top interfacial heating layer into the bulk water below. The salt-rejection and self-regeneration ability of the solar-driven SrCoO3@NF evaporation structure developed here were investigated through different experimental procedures. The SrCoO3@NF solar evaporator was placed in a beaker filled with simulated sea water (3.5 wt% NaCl) and operated for a long period of time at 1 sun solar intensity (1 kW m −2 ) while  Figure 5c shows the measured thermal conductivity of SrCoO 3 @NF (0.0756 ± 0.0076 W m −1 K −1 ), which is much lower than the thermal conductivity of pure water (0.6 W m −1 K −1 ). The high interfacial heat accumulation and superior solar-tovapor conversion efficiency are the results of optimal solar absorption and minimal thermal conduction. A real-time demonstration of the SrCoO 3 @NF solar evaporator producing vapor under 2 kW m −2 intensity is shown in Figure 5d. Figure 5e shows a corresponding infrared picture of a SrCoO 3 @NF solar evaporator operating under 2 sun conditions, revealing a heated interfacial surface with no thermal conduction, which is ideal for a fast evaporation rate in support of effective saltwater desalination. The hydrophilic PU foam effectively limits produced heat, and the infrared picture shows how the interfacial heat buildup is increased over the top matrix and shows effective thermal management compared to existing solar evaporators. The comparative solar-to-vapor conversion efficiency of the pure water, PU foam, NF@PU, and SrCoO 3 @NF were calculated as shown in Figure 5f. The self-regenerating SrCoO 3 @NF had the highest evaporation efficiency, at 86.45%, higher than the pure water (18.22%), PU foam (38.96%), or NF@PU (61.22%). Table 1 represents a comparison with other solar evaporators. Furthermore, the antifouling properties of the SrCoO 3 @NF were assessed by calculating the number of washing cycles as a function of the evaporation rate, as shown in Figure 5g. The SrCoO 3 @NF maintains smooth evaporation rates with little variation, showing excellent scalability for long-term efficacy.

Salt-Rejection Ability
The desalination of saltwater uses solar energy, which is a renewable and non-polluting energy source. Nevertheless, during prolonged operation in cooler temperatures, the water channels of evaporation structures tend to get obstructed due to the high salt content of sea water (3.5 wt% NaCl). The optimization of evaporation efficiency is ultimately stifled as a result of salt accumulation. Many effective methods have been proposed to address this problem, such as the introduction of innovative thin evaporation structures at the expense of thermal insulation. These delicate evaporation structures let heat escape from the top interfacial heating layer into the bulk water below. The salt-rejection and self-regeneration ability of the solar-driven SrCoO 3 @NF evaporation structure developed here were investigated through different experimental procedures. The SrCoO 3 @NF solar evaporator was placed in a beaker filled with simulated sea water (3.5 wt% NaCl) and operated for a long period of time at 1 sun solar intensity (1 kW m −2 ) while 1.3 g of solid NaCl was dispersed on the interfacial matrix of the SrCoO 3 @NF solar evaporator, as shown in Figure 6a-h. 1.3 g of solid NaCl was dispersed on the interfacial matrix of the SrCoO3@NF solar evaporator, as shown in Figure 6a-h. In steady-state evaporation conditions, the SrCoO3@NF evaporating structure demonstrated exceptional self-regenerating potential by rejecting all of the 1.3 g of solid NaCl in 3.5 h of constant irradiation. The highly porous and interconnected network of the heating and the insulating interface is responsible for the salt rejection and regeneration potential of the designed system. The superwetting feature of microchannels, enhanced by a crosslinking of the interfaces in a centralized macropore arrangement, allows In steady-state evaporation conditions, the SrCoO 3 @NF evaporating structure demonstrated exceptional self-regenerating potential by rejecting all of the 1.3 g of solid NaCl in 3.5 h of constant irradiation. The highly porous and interconnected network of the heating and the insulating interface is responsible for the salt rejection and regeneration potential of the designed system. The superwetting feature of microchannels, enhanced by a crosslinking of the interfaces in a centralized macropore arrangement, allows rapid evaporation and simultaneous water transport. Salt ions are transported from a high-concentration to a low-concentration location via diffusion or convection due to the potential gradient caused by the two regions' varying concentrations. A constant flow of vapor dissolves the solid NaCl, allowing it to migrate through the photothermal layer and into the bulk water below. The SrCoO 3 @NF solar evaporator's open porous assembly is oriented so that salt does not build up within. Hence, the designed system offers promising potential for industrial-level applicability for sea water desalination. The developed SrCoO 3 @NF self-regenerating solar evaporation system shows excellent photothermal conversion, quick water transfer, and fast vapor escape, which offers a potentially useful approach to efficient, effective, and long-term production of fresh water with little impact on the environment. Several brine solutions, including pure water at 2.5, 5, 10, 15, and 20 wt%, were also used to test the SrCoO 3 @NF solar evaporator's salt-resistance potential without reducing evaporation rates. As shown in Figure 7a, the developed evaporation system performance is not affected by a high salt content, and even higher salt concentrations do not significantly affect the evaporation rate. Furthermore, we investigated the cycle stability of the SrCoO 3 @NF solar evaporator by consistently operating it over 5 cycles under one solar intensity, as shown in Figure 7b. The SrCoO 3 @NF solar evaporator showed no significant change in its evaporation rate. This suggests that the system can be used for a very long time as an efficient solar-driven water evaporation system. However, evaporation structures have several challenges, the most prominent of which is mechanical fragility and structural deformation when operated consistently over a long time period, which has a major impact on the evaporation rate and efficiency of devices. As can be seen in Figure 7c, in order to examine mechanical steadiness and consistency in evaporation efficiency, the SrCoO 3 @NF system was run continuously for 8 h. In simulated saltwater conditions and 1 kW m −2 sun intensity, the self-regenerating LSCF@NFP was able to maintain a smooth evaporation rate with little discrepancy, demonstrating great scalability for long-term effectiveness. Additionally, Figure 7d shows the results of inductively coupled plasma-optical emission spectrometry (ICP-OES) measurement of the concentration of four primary salt ions (Na + , K + , Ca 2+ , Mg 2+ ) in stimulated sea water and condensed water, which was performed to evaluate the purifying potential of the developed system. After desalination, the concentration of salt ions drops by three to four orders of magnitude, far below the standards for drinking water of the World Health Organization (WHO) and the US Environmental Protection Agency (EPA). Hence, the SrCoO 3 @NF solar evaporator optimally produces potable fresh water, expanding its potential industrial applications. urement of the concentration of four primary salt ions (Na + , K + , Ca 2+ , Mg 2+ ) in stimulated sea water and condensed water, which was performed to evaluate the purifying potential of the developed system. After desalination, the concentration of salt ions drops by three to four orders of magnitude, far below the standards for drinking water of the World Health Organization (WHO) and the US Environmental Protection Agency (EPA). Hence, the SrCoO3@NF solar evaporator optimally produces potable fresh water, expanding its potential industrial applications.

Conclusions
In summary, we successfully synthesized strontium-cobaltite-based perovskite (SrCoO3) nanoparticles via the sol-gel technique. A detailed structural investigation was performed to fabricate a solar-driven water harvester composed of strontium-cobaltitebased perovskite (SrCoO3) anchored on nickel foam (SrCoO3@NF). Synced water transport and good thermal insulation are provided by a superhydrophilic polyurethane substrate

Conclusions
In summary, we successfully synthesized strontium-cobaltite-based perovskite (SrCoO 3 ) nanoparticles via the sol-gel technique. A detailed structural investigation was performed to fabricate a solar-driven water harvester composed of strontium-cobaltite-based perovskite (SrCoO 3 ) anchored on nickel foam (SrCoO 3 @NF). Synced water transport and good thermal insulation are provided by a superhydrophilic polyurethane substrate combined with a photothermal layer. Multiple incident rays are induced inside the diffuse surface, allowing omnidirectional solar absorption (91%) and heat localization (42.01 • C @ 1 sun). Under 1 kW m 2 solar intensity, the integrated SrCoO 3 @NF solar evaporator has an outstanding evaporation rate (1.45 kg/m 2 h) and solar-to-vapor conversion efficiency (86.45% excluding heat losses). In addition, long-term evaporation measurements demonstrate low variance under sea water, illustrating the system's working capacity for salt rejection (1.3 g NaCl/210 min). This research demonstrates a substantial capacity to produce fresh water free of salt ions for industrial uses.