Enhanced Water Adsorption of MIL-101(Cr) by Metal-Organic Polyhedral Encapsulation for Adsorption Cooling

Metal-organic frameworks (MOFs) are one of the most promising adsorbents in the adsorption cooling system (ACS) for their outstanding water adsorption performance. Notwithstanding that fact, numerous reports pay more attention to the ACS performance improvement through enhancing equilibrium water uptake of MOFs. However, adsorption cooling performance, including specific cooling power (SCP) and coefficient of performance for cooling (COPC) of MOF/water working pairs, always depends on the water adsorption kinetics of MOFs in ACS. In this work, to increase the water adsorption rate, the preparation of MOP/MIL-101(Cr) was achieved by encapsulating hydrophilic metal-organic polyhedral (MOP) into MIL-101(Cr). It was found that the hydrophilicity of MOP/MIL-101(Cr) was enhanced upon hydrophilic MOP3 encapsulation, resulting in a remarkable improvement in water adsorption rates. Furthermore, both SCP and COPC for MOP/MIL-101(Cr)-water working pairs were also improved because of the fast water adsorption of MOP/MIL-101(Cr). In brief, an effective approach to enhance the water adsorption rate and cooling performance of MOF-water working pairs through enhancing the hydrophilicity of MOFs by encapsulating MOP into MOFs was reported in this work, which provides a new strategy for broadening the application of MOF composites in ACS.


Introduction
Increasing fuel consumption combined with anthropogenic greenhouse gas emissions are driving the escalating worldwide utilization of environmentally benign cooling technologies, especially renewable energy, to diminish global electrical energy requirements [1]. An adsorption cooling system (ACS) has been proposed, which enables the utilization of low-grade energy (e.g., solar radiation) for regeneration and water working fluid [2,3]. The efficiency indicators, including specific cooling power (SCP) and coefficient of performance for cooling (COP C ), are used to quantify the cooling performance of ACS. Both SCP and COP C are directly related to the water adsorption performance of adsorbents in terms of the level of mass exchange and the amount of heat required for regeneration [4,5]. Traditional porous adsorbents such as silica gels and zeolites are commonly employed in ACS. However, the unsatisfactory water adsorption performance and high regeneration temperatures limit their ACS performance [6][7][8]. Therefore, seeking high-performance adsorbents to enhance the adsorption cooling performance of the system has received growing attention.
The potential use of metal-organic frameworks (MOFs) [9] for ACS has recently received growing research interest [10] because of their superior water uptake [11]. MIL-101(Cr) [12] is one of the most prominent MOFs due to its ultrahigh water uptake (>1.0 g/g) and excellent chemical and structural stability in the water medium [13]. The equilibrium water uptake of MIL-101(Cr) (1.05 g/g [10]) is 3.5 times that of conventional silica gel (0.30 g/g [14]) at P = 2.85 kPa and T = 298 K. However, the superior equilibrium water hydrophilicity-directed approach [29]; the construction diagram is shown in Figure 1. Specifically, MIL-101(Cr) was added to n-hexane with stirring. Then, Cu(NO3)2 and Na + SO3 − -mBDC were dissolved in methanol and successively added to the suspension under continuous stirring. Afterward, 2,6-dimethylpyridine was added under stirring. Finally, the obtained solid was washed with DMF and deionized water and activated by heating under a vacuum. To avoid agglomeration, MOP3 content in composites varies from 5 wt.% to 35 wt.%, corresponding to MOP/MIL-101(Cr)-n where n = 5, 10, 15, 20, and 35.

MOP/MIL-101(Cr) Characterization
The prepared MOP/MIL-101(Cr) composites were first characterized by powder Xray diffraction (PXRD, PANalytical B.V., Netherlands) to confirm their crystalline structure. Then, scanning electron microscope (SEM, FEI, Netherlands) images were conducted to obtain the morphological characteristics of MOP/MIL-101(Cr) composites, from which particle size can be calculated by Image Pro Plus software. The Fourier transform infrared (FT-IR, Bruker, Germany) spectra were obtained to demonstrate MOP/MIL-101(Cr) composites' structural characteristics and confirm MOP3 encapsulation. The nitrogen (N2) adsorption isotherms were measured at 77 K (Quantachrome, US) to obtain the BET surface area, total pore volume, and pore size distribution of MOP/MIL-101(Cr) composites. The porosity of MOP/MIL-101(Cr) composites and MIL-101(Cr) were calculated using true density determined by a true density analyzer (Micromeritics, US) and bulk density based on volume measured in a container of a known volume. Differential scanning calorimeter (DSC, PerkinElmer, US) was conducted under N2 atmosphere to obtain the heat capacity of MOP/MIL-101(Cr) composites and MIL-101(Cr). Water adsorption isotherms were measured at 288, 298, and 303 K at relative pressure ranges from 0.001 to 0.9 (Quantachrome, US). The data were used to calculate the heat of adsorption of MOP/MIL-101(Cr) composites and MIL-101(Cr) using the Clausius-Clapeyron equation.

Water Adsorption Rate Measurement
Generally, the adsorption temperature and humidity were 303 K and 30% (RH) in the adsorption bed under typical cooling conditions for the ACS [33]. Thus, the dynamic water adsorption curve (Surface Measurement Systems, UK) at 303 K and 30% relative humidity was tested with the details provided in the SI, from which the water adsorption rate of MOP/MIL-101(Cr) composites and MIL-101(Cr) can be calculated by

MOP/MIL-101(Cr) Characterization
The prepared MOP/MIL-101(Cr) composites were first characterized by powder X-ray diffraction (PXRD, PANalytical B.V., Netherlands) to confirm their crystalline structure. Then, scanning electron microscope (SEM, FEI, Netherlands) images were conducted to obtain the morphological characteristics of MOP/MIL-101(Cr) composites, from which particle size can be calculated by Image Pro Plus software. The Fourier transform infrared (FT-IR, Bruker, Germany) spectra were obtained to demonstrate MOP/MIL-101(Cr) composites' structural characteristics and confirm MOP3 encapsulation. The nitrogen (N 2 ) adsorption isotherms were measured at 77 K (Quantachrome, US) to obtain the BET surface area, total pore volume, and pore size distribution of MOP/MIL-101(Cr) composites. The porosity of MOP/MIL-101(Cr) composites and MIL-101(Cr) were calculated using true density determined by a true density analyzer (Micromeritics, US) and bulk density based on volume measured in a container of a known volume. Differential scanning calorimeter (DSC, PerkinElmer, US) was conducted under N 2 atmosphere to obtain the heat capacity of MOP/MIL-101(Cr) composites and MIL-101(Cr). Water adsorption isotherms were measured at 288, 298, and 303 K at relative pressure ranges from 0.001 to 0.9 (Quantachrome, US). The data were used to calculate the heat of adsorption of MOP/MIL-101(Cr) composites and MIL-101(Cr) using the Clausius-Clapeyron equation.

Water Adsorption Rate Measurement
Generally, the adsorption temperature and humidity were 303 K and 30% (RH) in the adsorption bed under typical cooling conditions for the ACS [33]. Thus, the dynamic water adsorption curve (Surface Measurement Systems, UK) at 303 K and 30% relative humidity was tested with the details provided in the SI, from which the water adsorption rate of MOP/MIL-101(Cr) composites and MIL-101(Cr) can be calculated by differentiating the water uptake from the corresponding adsorption time. For comparison, the average water adsorption rate was obtained by dividing water uptake by adsorption time.

Mathematical Modeling of ACS
A dynamic thermal cycle of ACS ( Figure 2a) includes pre-heating (from 1 to 2), desorption (from 2 to 3), pre-cooling (from 3 to 4), and adsorption (from 4 to 1). In order to explore the adsorption cooling performance of MOP/MIL-101(Cr)-water working pairs, a typical two-bed adsorption cooling system [34] was used in this work. The two-bed ACS includes a condenser, an evaporator, two adsorption beds, and several circulation pipes, including hot water, cooling water, and chilled water circulation pipes (Figure 2b). differentiating the water uptake from the corresponding adsorption time. For com the average water adsorption rate was obtained by dividing water uptake by ad time.

Mathematical Modeling of ACS
A dynamic thermal cycle of ACS ( Figure 2a) includes pre-heating (from 1 sorption (from 2 to 3), pre-cooling (from 3 to 4), and adsorption (from 4 to 1). In explore the adsorption cooling performance of MOP/MIL-101(Cr)-water workin typical two-bed adsorption cooling system [34] was used in this work. The twoincludes a condenser, an evaporator, two adsorption beds, and several circulati including hot water, cooling water, and chilled water circulation pipes (Figure 2 As shown in Figure 2b, adsorbents in SE1 (desorption bed) are desorbed or ated (Tdes) by an external heat source (Qregen). Meanwhile, SE1 is connected with denser (Tcon and Pcon). Thereby, the desorbed water (gaseous) enters the conden SE1 and condenses into liquid water. Subsequently, the condensed water flows evaporator and evaporates into water vapor (Teva and Peva). At the same time, th heat can be taken away by water evaporation (Qeva), thus producing a cooling effe the evaporated water vapor enters SE2 (adsorption bed) from the evaporator for tion. The schematic diagram of the transient temperature ( Figure 2c) and of the w take ( Figure 2d) for two-bed ACS is shown in Figure 2. The system follows the m energy balance equations. The energy balance equation for the adsorption bed c scribed as: Here, items on the left successively represent the change in thermal energy bents (MOP/MIL-101(Cr)), the working fluid (water), and the heat exchanger. the right represent the heat of adsorption in the adsorption bed and heat transfer the adsorption bed and evaporator. ϕ = 0 at switch time (ts) and ϕ = 1 at opera As shown in Figure 2b, adsorbents in SE 1 (desorption bed) are desorbed or regenerated (T des ) by an external heat source (Q regen ). Meanwhile, SE 1 is connected with the condenser (T con and P con ). Thereby, the desorbed water (gaseous) enters the condenser from SE 1 and condenses into liquid water. Subsequently, the condensed water flows into the evaporator and evaporates into water vapor (T eva and P eva ). At the same time, the outside heat can be taken away by water evaporation (Q eva ), thus producing a cooling effect. Then, the evaporated water vapor enters SE 2 (adsorption bed) from the evaporator for adsorption. The schematic diagram of the transient temperature ( Figure 2c) and of the water uptake ( Figure 2d) for two-bed ACS is shown in Figure 2. The system follows the mass and energy balance equations. The energy balance equation for the adsorption bed can be described as: Here, items on the left successively represent the change in thermal energy of adsorbents (MOP/MIL-101(Cr)), the working fluid (water), and the heat exchanger. Items on the right represent the heat of adsorption in the adsorption bed and heat transfer between the adsorption bed and evaporator. φ = 0 at switch time (t s ) and φ = 1 at operating time (t o ). Heat capacity (C p,ad ) and heat of adsorption (q st ) for MOP/MIL-101(Cr) are shown in Table 1. The energy balance equations in the evaporator and condenser are shown in SI. The mass balance equation in ACS: The rate for the change in water mass is equal to the amount of adsorbed water during adsorption and how much water was desorbed during desorption. The equation parameters are shown in Table S1 [35].
Based on the energy and mass balance equations in ACS, SCP, and COP C of MOP/MIL-101(Cr)-water working pairs are calculated as follows: Here, Q eva and Q regen are the cooling capacity and total energy consumption of MOP/MIL-101(Cr) in ACS; t cycle is the cycle time of ACS.
The adsorption temperature (T ads ) of ACS is equal to the condensation temperature (T con ) [36], which is usually 303 K in cooling conditions ( Table 2). According to the hot water temperature generated by solar energy, the desorption temperature (T des ) is set at 353 K [37]. The chilled water inlet temperature determines the evaporation temperature (T eva ), which is generally set to 283 K for cooling. Moreover, mass flow in circulation pipes, including hot water (m hot ), cooling water (m cooling ), and chilled water (m chill ); the cycle time, including operating time (t o ) and switch time (t s ) are set based on previous reports [34,35,38] (Table 2).

Effects of Structural Characteristics on Water Adsorption Rates
A previous study showed that the structural properties of MOFs will affect their water adsorption performance. For example, the large pore volume is favorable for the equilibrium water uptake of MOFs [11]. Therefore, we first characterized the structural properties of MOP/MIL-101(Cr). Scanning electron microscopy (SEM) images demonstrated that the morphology of MOP/MIL-101(Cr) composites was not significantly changed compared with pristine MIL-101(Cr) (Figure 3a). The homogeneous distribution of Cu element in MOP/MIL-101(Cr)-5 was observed by energy dispersive spectroscopy elementary mapping ( Figure 3a). In contrast, no significant Cu signal in MIL-101(Cr) indicates the uniform distribution of MOP3 in composites. In addition, compared to MIL-101(Cr), the particle size of MOP/MIL-101(Cr) composites was not changed after MOP3 incorporation, regardless of MOP3 content. Moreover, the original crystallinity of MIL-101(Cr) was effectively preserved as demonstrated in powder X-ray diffraction (PXRD) patterns of MOP/MIL-101(Cr), which matches with MIL-101(Cr) (Figure 3b).
The successful encapsulation of MOP3 in MIL-101(Cr) was confirmed by Fourier transform infrared (FT-IR) spectra (Figure 3c). The peak at 1608 cm −1 represents the asymmetric stretching pattern of the COO − -Cu 2+ complex [39]. The peak at 1042 cm −1 results from the symmetric stretching pattern of the SO 3− [28] present in MOP3. The results are consistent with previous reports on the encapsulation of MOP3 into PCN-777 [28]. Although the morphology and crystallinity of MIL-101(Cr) are well preserved after MOP3 incorporation, BET surface area and total pore volume of MOP/MIL-101(Cr) decrease significantly upon MOP3 encapsulation (Figure 3d). Compared with MIL-101(Cr), the BET surface area and total pore volume of MOP/MIL-101(Cr)-35 decreased by 37.5% and 37.3%, respectively. In addition, the pore size of MOP/MIL-101(Cr) is gradually reduced with the increased loading of MOP3 (Figure 3e), which was also observed in a previous study on MOP/PCN-777 composites [28].

Effects of Structural Characteristics on Water Adsorption Rates
A previous study showed that the structural properties of MOFs will affect their water adsorption performance. For example, the large pore volume is favorable for the equilibrium water uptake of MOFs [11]. Therefore, we first characterized the structural prop- Furthermore, the BET surface area and total pore volume are key factors affecting the equilibrium water uptake of MOFs under high pressure [11]. Thus, the reduction in BET surface area and total pore volume leads to a decrease in equilibrium water uptake for MOP/MIL-101(Cr) at a high relative pressure of P/P0 > 0.5 (Figure 4a). However, the equilibrium water uptake of MOP/MIL-101(Cr) increased at low pressure of P/P0 < 0.5, ascribed Furthermore, the BET surface area and total pore volume are key factors affecting the equilibrium water uptake of MOFs under high pressure [11]. Thus, the reduction in BET surface area and total pore volume leads to a decrease in equilibrium water uptake for MOP/MIL-101(Cr) at a high relative pressure of P/P 0 > 0.5 (Figure 4a). However, the equilibrium water uptake of MOP/MIL-101(Cr) increased at low pressure of P/P 0 < 0.5, ascribed to enhanced hydrophilicity of MIL-101(Cr) upon hydrophilic MOP3 encapsulation. Herein, Henry's constant (K H ), which describes the affinity of adsorbents toward the water at low pressure [40], was used to quantify the hydrophilicity of MOP/MIL-101(Cr) composites. It was found that the hydrophilicity of MOP/MIL-101(Cr) gradually increased with the MOP3 content. To investigate the reason for the enhanced hydrophilicity of MOP/MIL-101(Cr), K H of MOP3 and MIL-101(Cr) were measured ( Figure S1). K H of MOP3 (K H = 0.116 g/g·kPa) is higher than MOP/MIL-101(Cr) (K H = 0.095~0.110 g/g·kPa) and MIL-101(Cr) (K H = 0.095 g/g·kPa), indicating the enhanced hydrophilicity of MOP/MIL-101(Cr) resulting from MOP3 encapsulation. According to previous reports, hydrophilicity is beneficial for enhancing water adsorption rate [18,19]. Results show that water adsorption rates of MIL-101(Cr) are significantly increased upon MOP3 encapsulation. In addition, water adsorption rates of MOP/MIL-101(Cr) are increased linearly with MOP3 content, consistent with Henry's constant.
(b) (c) (e) Furthermore, the BET surface area and total pore volume are key factors affecti equilibrium water uptake of MOFs under high pressure [11]. Thus, the reduction i surface area and total pore volume leads to a decrease in equilibrium water upta MOP/MIL-101(Cr) at a high relative pressure of P/P0 > 0.5 (Figure 4a). However, the librium water uptake of MOP/MIL-101(Cr) increased at low pressure of P/P0 < 0.5, as to enhanced hydrophilicity of MIL-101(Cr) upon hydrophilic MOP3 encapsu Herein, Henry's constant (KH), which describes the affinity of adsorbents toward the at low pressure [40], was used to quantify the hydrophilicity of MOP/MIL-101(Cr posites. It was found that the hydrophilicity of MOP/MIL-101(Cr) gradually inc with the MOP3 content. To investigate the reason for the enhanced hydrophili MOP/MIL-101(Cr), KH of MOP3 and MIL-101(Cr) were measured ( Figure S1). KH of (KH = 0.116 g/g·kPa) is higher than MOP/MIL-101(Cr) (KH = 0.095 ~ 0.110 g/g·kPa) and 101(Cr) (KH = 0.095 g/g·kPa), indicating the enhanced hydrophilicity of MOP/MIL-1 resulting from MOP3 encapsulation. According to previous reports, hydrophilicity eficial for enhancing water adsorption rate [18,19]. Results show that water adso rates of MIL-101(Cr) are significantly increased upon MOP3 encapsulation. In ad water adsorption rates of MOP/MIL-101(Cr) are increased linearly with MOP3 co consistent with Henry's constant.  Moreover, apart from surface hydrophilicity, other structure properties inc pore size, particle size and porosity may also impact on water adsorption kinetics. on diffusion theory, Knudsen diffusion and molecular diffusion dominate water a tion in micropores and mesopores, respectively. Thus, either the pores within samp ticles or the interparticle pores may impose impacts on water adsorption kinetics. dition, porosity is frequently used to represent the structural characteristics of poro dia. To explore the correlation between structural properties of MOP/MIL-101(C water adsorption rate, the impacts of particle size (Rp), pore size (D), porosity (φ hydrophilicity (KH) on the water adsorption rate (v) of MOP/MIL-101(Cr) was invest ( Figure 5). In theory, larger particle/pore size and high porosity are beneficial for diffusion in pore media [41]. However, in this work, both pore size and porosity reduced with increased MOP3 content, and the particle size remained nearly con These outcomes are not conducive to improving the water adsorption rate for MOP 101(Cr). Nevertheless, the water adsorption rates of MOP/MIL-101(Cr) exhib Moreover, apart from surface hydrophilicity, other structure properties including pore size, particle size and porosity may also impact on water adsorption kinetics. Based on diffusion theory, Knudsen diffusion and molecular diffusion dominate water adsorption in micropores and mesopores, respectively. Thus, either the pores within sample particles or the interparticle pores may impose impacts on water adsorption kinetics. In addition, porosity is frequently used to represent the structural characteristics of porous media. To explore the correlation between structural properties of MOP/MIL-101(Cr) and water adsorption rate, the impacts of particle size (R p ), pore size (D), porosity (ϕ), and hydrophilicity (K H ) on the water adsorption rate (v) of MOP/MIL-101(Cr) was investigated ( Figure 5). In theory, larger particle/pore size and high porosity are beneficial for water diffusion in pore media [41]. However, in this work, both pore size and porosity were reduced with increased MOP3 content, and the particle size remained nearly constant. These outcomes are not conducive to improving the water adsorption rate for MOP/MIL-101(Cr). Nevertheless, the water adsorption rates of MOP/MIL-101(Cr) exhibited a consistent tendency to hydrophilicity with the increase in MOP3 content. This suggests the dominant role of hydrophilicity in water adsorption rates of MOP/MIL-101(Cr). MOP/MIL-101(Cr)-35 exhibited the highest water adsorption rate, which was approximately 2.3 times that of MIL-101(Cr). consistent tendency to hydrophilicity with the increase in MOP3 content. This sugges the dominant role of hydrophilicity in water adsorption rates of MOP/MIL-101(Cr MOP/MIL-101(Cr)-35 exhibited the highest water adsorption rate, which was approx mately 2.3 times that of MIL-101(Cr).

Adsorption Cooling Performance
Cooling performance, including SCP and COPC of MOP/MIL-101(Cr)-water workin pairs, were subsequently discussed. As shown in Figure 6, the SCP of MOP/MIL-101(Cr water increases with the MOP3 content. SCP measures the capacity of the system to pro duce a cooling effect [42], mainly determined by cooling capacity (Qeva) based on Equatio (3). Furthermore, the cooling capacity (Qeva) is mainly affected by cyclic working capacit (Δqt) according to Qeva = LH·Δqt, where LH represents the latent heat of water vaporization which is a constant at fixed evaporation temperature. Δqt can be calculated by transien water uptake (Figure 2d). Therefore, the large cyclic working capacity of MOP/MIL 101(Cr) is favorable for SCP of MOP/MIL-101(Cr)-water ( Figure 6a). Notably, the cycl working capacity of MOP/MIL-101(Cr) improves with the increase in MOP3 conten which exhibits a consistent tendency with water adsorption rate ( Figure 6). This indicate that the cyclic working capacity is mainly affected by the water adsorption rate o MOP/MIL-101(Cr). Consequently, MOP/MIL-101(Cr) with fast water uptake promotes th cyclic working capacity resulting in the enhancement of SCP. Moreover, compared t MIL-101(Cr)-water, SCP of MOP/MIL-101(Cr)-water enhanced regardless of MOP3 con tent because of the fast water adsorption of MOP/MIL-101(Cr).

Adsorption Cooling Performance
Cooling performance, including SCP and COP C of MOP/MIL-101(Cr)-water working pairs, were subsequently discussed. As shown in Figure 6, the SCP of MOP/MIL-101(Cr)water increases with the MOP3 content. SCP measures the capacity of the system to produce a cooling effect [42], mainly determined by cooling capacity (Q eva ) based on Equation (3). Furthermore, the cooling capacity (Q eva ) is mainly affected by cyclic working capacity (∆q t ) according to Q eva = L H ·∆q t , where L H represents the latent heat of water vaporization, which is a constant at fixed evaporation temperature. ∆q t can be calculated by transient water uptake (Figure 2d). Therefore, the large cyclic working capacity of MOP/MIL-101(Cr) is favorable for SCP of MOP/MIL-101(Cr)-water ( Figure 6a). Notably, the cyclic working capacity of MOP/MIL-101(Cr) improves with the increase in MOP3 content, which exhibits a consistent tendency with water adsorption rate ( Figure 6). This indicates that the cyclic working capacity is mainly affected by the water adsorption rate of MOP/MIL-101(Cr). The COPC is defined as the ratio of the useful energy provided by the device and the required input [43]   The COP C is defined as the ratio of the useful energy provided by the device and the required input [43] COP C = SCP · t cycle Q regen COP C of MOP/MIL-101(Cr)-water increases with MOP3 content, which exhibited a consistent tendency with total energy consumption of system (Q regen ) and SCP (Figure 7a) as well as water adsorption rate of MOP/MIL-101(Cr) (Figure 7b). The above analysis suggests that fast water adsorption of MOP/MIL-101(Cr) can promote SCP. Subsequently, we further investigated the total energy consumption (Q regen ) of MOP/MIL-101(Cr). The COPC is defined as the ratio of the useful energy provided by the device a required input [43]  Total energy consumption (Q regen = Q ad + Q w + Q hex + Q des ) of ACS is composed of four parts based on the energy balance in the adsorption bed (Equation (1)): energy consumption by temperature rising (from adsorption temperature to desorption temperature) of adsorbents or sensible heat of adsorbents (Q ad = C p,ad (T des − T ads )), the sensible heat of adsorbed water (Q w = v · t o · C p,w (T des − T ads )) and the sensible heat of heat exchanger (Q hex = M hex M ad C p,hex (T des − T ads )) during desorption process, and energy consumption for water desorption (Q des = ∆q t ·q st ). It is noted (Figure 8) that the Q hex is a constant at the fixed temperature and mass of adsorbents. The sensible heat of MOP/MIL-101(Cr) (Q ad ) and adsorbed water (Q w ) are mainly affected by the heat capacity of MOP/MIL-101(Cr) (C p,ad ) and water adsorption rate, respectively. The slight increase in Q ad with the MOP3 content can be ascribed to the increased heat capacity of MOP/MIL-101(Cr) upon MOP3 (C p,ad = 1.77 J/g·K for MOP3, Table 1). Q w was also slightly improved because of the increased water adsorption rate of MOP/MIL-101(Cr) with MOP3 content. In contrast, the energy consumption of water desorption (Q des ) mostly contributes to total energy consumption (Figure 8a), which is ascribed to the significantly increased hydrophilicity of MOP/MIL-101(Cr) upon MOP3 encapsulation that requires the increased energy consumption for desorption. In addition, the increased heat of adsorption (q st , Table 1) and cyclic working capacity of MOP/MIL-101(Cr) resulting from fast water adsorption also favor the remarkable increase in Q des (Figure 8b). In conclusion, the improved water adsorption rate promotes SCP of MOP/MIL-101(Cr)-water working pairs, resulting in the significant enhancement of SCP. Energy consumption of MOP/MIL-101(Cr) can be enhanced by increased cyclic working capacity and heat of adsorption, which is not beneficial for improving COP C . Nonetheless, the improved SCP caused by accelerated water adsorption contributes to the enhancement of COP C . Thus, the COP C of MOP/MIL-101(Cr)-water working pairs increased with MOP3 content. motes SCP of MOP/MIL-101(Cr)-water working pairs, resulting in the significant enhancement of SCP. Energy consumption of MOP/MIL-101(Cr) can be enhanced by increased cyclic working capacity and heat of adsorption, which is not beneficial for improving COPC. Nonetheless, the improved SCP caused by accelerated water adsorption contributes to the enhancement of COPC. Thus, the COPC of MOP/MIL-101(Cr)-water working pairs increased with MOP3 content.

Conclusions
In this work, we report on a new strategy to enhance the water adsorption kinetics and cooling performance of MIL-101(Cr) and its working pair by encapsulating MOP3 into MIL-101(Cr). We prepared and characterized MOP/MIL-101(Cr) composites with different MOP3 contents and found that the encapsulation of MOP3 decreased the pore size and porosity of MIL-101(Cr), while the hydrophilicity of MOP/MIL-101(Cr) significantly enhanced with the increase in MOP3 content. Although reduced pore size and porosity are detrimental to water adsorption, the water adsorption rate of MOP/MIL-101(Cr) improved with the increase in MOP3 due to the enhancement of hydrophilicity. Based on mathematical modeling, the adsorption cooling performance, namely both SCP and COPC, of MOP/MIL-101(Cr)-water for ACS increases with the MOP3 content. This can be ascribed to the increased water adsorption rate resulting from the improved hydrophilicity of MOP/MIL-101(Cr) upon MOP3 encapsulation. These findings demonstrate the effectiveness of MOP3 encapsulation in improving the water adsorption kinetics and cooling performance of MIL-101(Cr).

Conclusions
In this work, we report on a new strategy to enhance the water adsorption kinetics and cooling performance of MIL-101(Cr) and its working pair by encapsulating MOP3 into MIL-101(Cr). We prepared and characterized MOP/MIL-101(Cr) composites with different MOP3 contents and found that the encapsulation of MOP3 decreased the pore size and porosity of MIL-101(Cr), while the hydrophilicity of MOP/MIL-101(Cr) significantly enhanced with the increase in MOP3 content. Although reduced pore size and porosity are detrimental to water adsorption, the water adsorption rate of MOP/MIL-101(Cr) improved with the increase in MOP3 due to the enhancement of hydrophilicity. Based on mathematical modeling, the adsorption cooling performance, namely both SCP and COP C , of MOP/MIL-101(Cr)-water for ACS increases with the MOP3 content. This can be ascribed to the increased water adsorption rate resulting from the improved hydrophilicity of MOP/MIL-101(Cr) upon MOP3 encapsulation. These findings demonstrate the effectiveness of MOP3 encapsulation in improving the water adsorption kinetics and cooling performance of MIL-101(Cr).