Efficient Removal of Congo Red, Methylene Blue and Pb(II) by Hydrochar–MgAlLDH Nanocomposite: Synthesis, Performance and Mechanism

Organic dyes and heavy metals often coexist in industrial effluents, and their simultaneous removal is a grand challenge. Herein, a hydrochar and MgAl layered double hydroxide (HC–MgAlLDH) nanocomposite was prepared via a facile one-step hydrothermal route, and applied to remove anionic Congo red (CR), cationic Methylene blue (MB) and Pb(II) from aqueous solutions. The nanocomposite was formed by interweaving amorphous HC and crystalline MgAlLDH nanoplates and possessed more functional groups, lower zeta potential and larger specific surface area than uncomposited MgAlLDH. Batch removal experiments showed that the components HC and LDH dominated the CR and MB removals, respectively, whereas Pb(II) removal was conjointly controlled by the two components. The maximum Langmuir removal capacities of the nanocomposite to sole CR, MB, or Pb(II) were 348.78, 256.54 or 33.55 mg/g. In binary and ternary systems, the removal capacities of CR and MB only slightly decreased, while the capacity of Pb(II) increased by 41.13–88.61%. The increase was related to the coordination of Pb(II) with the sulfur-containing groups in dyes and the precipitation of PbSO4. Therefore, the simultaneous removal of CR, MB and Pb(II) was involved in a synergistic effect, including electrostatic adsorption, π–π interaction, coordination and precipitation. The present work shows that the HC–MgAlLDH nanocomposite has great potential for wastewater integrative treatment.


Introduction
Organic dyes are widely used in the paper, paint, plastic and textile industries, and usually have complex and various molecular structures, like azo, anthraquinonoid, and heterocyclic groups [1,2]. Due to their widespread use, refractory structures against degradation and high biological toxicity, organic dyes have been regarded as one of the main hazards in industrial wastewater [2,3]. At present, a challenge for the wastewater treatment is that different types of pollutants usually coexist together, significantly increasing the treatment difficulty and cost [4,5]. Anionic Congo red (CR) and cationic Methylene blue (MB) are two typical dyes used in industry and concomitant in the effluents as a central discharge of dye wastewaters [6]. Moreover, lead-containing compounds are often used as mordants, colorants and inorganic pigments in the printing and dyeing industry [7], inevitably leading to the coexistence of Pb(II), CR and MB. However, most technologies are inefficient for simultaneous removal of the multiple pollutants because of their different physicochemical properties (e.g., molecular size and chemical structure) [8,9]. In addition, both the heavy metals and dyes show strong toxicity, environmental persistence and bioaccumulation [10,11]. The environmental persistence makes them accumulate in the environment and consequently contaminate the food chains, and the bioaccumulation in biota causes a health threat to their consumers including humans [10,11]. More seriously, increasing data indicates that the coexisting heavy metal ions and dyes generally pose greater combined toxicity to living organisms than individually [12][13][14]. Hence, it is significant to develop effective approaches for the removal of the coexisting pollutants.
Adsorption is widely adopted to remove organic dyes or heavy metal ions due to its simple process and low cost [15]. Among the adsorbents, layered double hydroxides (LDHs) have recently attracted extensive attention because of their tunable structure, high surface area, facile synthesis, environmental friendliness and low cost. Structurally, LDHs, with a formula of [M 2+ 1−x M 3+ x (OH) 2 ] x+ (A n− ) x/n ·mH 2 O, are stacked by positively charged (M 2+ , M 3+ )(OH) 6 octahedral layers, interlayer anions (A n− ), and interlayer water molecules, where M 2+ and M 3+ are divalent (e.g., Mg 2+ , Co 2+ , Cu 2+ , Zn 2+ and Ni 2+ ) and trivalent (e.g., Al 3+ , Cr 3+ and Fe 3+ ) metal cations, x represents the ratio of M 3+ /(M 2+ + M 3+ ) and is usually between 0.18 and 0.33, and A n− includes CO 3 2− , SO 4 2− and NO 3 − [16,17]. The structural features endow LDHs with a high isoelectric point and strong interlayer anion exchangeability [18,19], which could make them become an excellent adsorbent for the removal of anionic CR. However, the adsorption of LDHs to cationic MB and Pb(II) is greatly limited due to electrostatic repulsion [20]. Modification of LDHs with other materials may be a feasible method to construct multifunctional active sites for various types of pollutants.
Hydrochar (HC), as an incomplete carbonized material, can be easily derived from cheap and widespread saccharides or other biomass at lower temperatures relative to other carbonaceous materials [21][22][23]. More importantly, HC exhibits a high adsorption affinity for heavy metal cations and cationic dyes in solution due to its abundant oxygen-bearing functional groups and high negative charge nature [24][25][26][27][28]. Therefore, the successful composition of LDH and HC may donate the material with better performance for simultaneous removal of the multiple pollutants. In particular, several recent studies on the synthesis of HC-modified LDH composites and their removals to cationic and anionic pollutants further supported such potential. For example, Memon et al. synthesized an HC and CoAlZnLDH composite through the coprecipitation of Co 2+ , Al 3+ and Zn 2+ in the presence of as-prepared HC at 60 • C, and found that the composite can simultaneously adsorb cationic and anionic dyes [29]. Dat et al. prepared MgAlLDH-capped HC spheres by hydrothermal treatment of pre-synthesized HC and MgAlLDH mixture for removal of single cationic or anionic dye [30]. Zhang et al. fabricated HC-coated MgAlLDH composites by a two-step hydrothermal method to remove either heavy metals or anionic dyes [31]. Despite all this, the removal behavior in the multi-pollutant system of dye and heavy metal was not involved, and the syntheses underwent a two-step process [30,31]. Therefore, it is necessary to develop a more simple and more economical synthesis of HC and LDH composite materials and to explore the removal performance and mechanism in multi-pollutant systems.
Herein, a series of HC-MgAlLDH nanocomposites were prepared by a one-step hydrothermal route and used for the adsorptive removal of CR, MB and Pb(II). The structural characteristics of the nanocomposites were comprehensively characterized, and the removal abilities of the three targets were systematically evaluated by batch adsorption experiments. The removal mechanisms were further explored based on the results of batch experiments and the analyses of post-adsorbents. Overall, the good removal performance of the HC-MgAlLDH nanocomposite showed potential for practical applications.

Preparation of HC-MgAlLDH Nanocomposites
Hydrothermal synthesis has been confirmed as a promising method for HC and LDH, respectively [32,33]. In the present work, HC-MgAlLDH nanocomposites (HC-MgAlLDH) were prepared by the one-pot hydrothermal synthesis. In a typical procedure, 0.004 mol of Mg(NO 3 ) 2 ·6H 2 O and 0.002 mol of Al(NO 3 ) 3 ·9H 2 O were dissolved in 50 mL of deionized water to obtain solution A, with a Mg 2+ /Al 3+ molar ratio of 2. Solution B was prepared by dissolving 0.5 mol of NaOH and 0.05 mol of Na 2 CO 3 in 250 mL of deionized water. Solution A was added dropwise into a beaker containing 10 mL of 100 g/L glucose (1.0 g) solution at room temperature and vigorous magnetic stirring, and the pH was adjusted to 9.5-10.0 using ca. 10 mL of solution B. Subsequently, the obtained suspension was transferred into a 100 mL of Teflon-lined stainless-steel autoclave. The autoclave with the suspension was sealed and placed into a programmed furnace to be kept at 180 • C for 48 h. After that, the autoclave was allowed to cool naturally to room temperature, and the resultant product was separated by centrifugation, rinsed with deionized water several times, and dried in a vacuum oven at 60 • C for 24 h. For comparisons, HC and MgAlLDH were synthesized under the same conditions, but without the addition of LDH-forming ions or glucose, respectively. In addition, the concentration of glucose was adjusted from 50 to 200 g/L to obtain the nanocomposites with different contents of HC, and the samples are denoted as xHC-MgAlLDH, where x represents the initially added weight of glucose, i.e., 0.5, 1.0, 1.5 and 2.0 g.

Characterizations
The synthesized products were identified by powder X-ray diffraction (PXRD) using a Rigaku diffractometer (40 kV, 30 mA) with Cu Kα radiation (λ = 0.154056 nm). Morphology and structure analyses were performed on a Zeiss Ultra 55 scanning electron microscope (SEM) and Libra 200FE transmission electron microscope (TEM) with an accelerating voltage of 5 and 200 kV, respectively. Analyses of energy dispersive spectroscopy (EDS) were performed on the SEM. X-ray photoelectron spectra (XPS) were obtained on a Thermo ESCALAB 250 XPS spectrometer with Al Kα radiation. N 2 adsorptiondesorption isotherms were determined by Quantachrome, Autosorb-1MP analyzer at the liquid-nitrogen temperature of 77 K. Specific surface areas were acquired according to the multipoint Brunauer-Emmett-Teller (BET) model, and total pore volumes and pore sizes were calculated based on the Barret-Joyner-Halenda (BJH) model. Zeta potential was determined by micro-electrophoresis using a Malvern Zetasizer Nano Zs90 zeta potential analyzer. The suspensions for zeta potential analyses contained 0.5% sample and 0.01 mol/L NaNO 3 , and the pH was adjusted using 0.1 mol/L NaOH and 0.1 mol/L HNO 3 . Fourier transform infrared (FT-IR) spectra were recorded on a PerkinElmer Fourier transform infrared spectroscopy, in the scan range of 4000-400 cm −1 .

Removal Experiments
Batch removal experiments were performed at 25 • C to evaluate the effects of initial solution pH, contact time, and initial CR, MB, or Pb(II) concentration on the removal by the synthesized adsorbents. Briefly, 10 mg of the adsorbent was added into an Erlenmeyer flask containing 20 mL of the working solution, and the adsorption was performed in an orbital shaker (TS2102-C) at 150 rpm. After a pre-set time, the suspension was centrifuged by high-speed centrifugation at 8000 rpm for 5 min. The concentrations of CR and MB in the supernatant were measured with a Thermo Fisher evolution 300 UV-Vis spectrophotometer at the maximum absorption wavelengths of 494 and 662 nm, respectively. The residual concentration of Pb(II) was determined by ICP-OES (PerkinElmer, optima 8300). The removal capacity q t (mg/g) for each sorbate was calculated by the following equation: where C 0 is the concentrations of CR, MB, or Pb(II) at the initial time (mg/L), C t is the concentration at any time t, V is the volume of solution (L), and m is the mass of adsorbent (g).

Phase Composition and Crystallinity
To examine the phase composition and crystallinity of the synthesized samples, XRD analyses were first performed. Figure 1a depicts the representative XRD patterns of the samples. The sample without LDH-forming ions shows a broad hump with low intensity at 2θ 15-25 • , indicating that the synthesized product is amorphous carbon [34,35]. Therefore, the HC is successfully synthesized. The sample only with LDH-forming ions exhibits seven diffraction peaks at 2θ 11.6, 23. . This demonstrates that the MgAlLDH was hydrothermally formed under the current conditions. For sample HC-MgAlLDH, all characteristic diffractions of the LDH are reliably detected, but the diffractions become much broader relative to the MgAlLDH, indicating that the LDH in the composite has lower crystallinity and smaller crystallite size. Further estimations of the crystallite sizes by the Scherrer equation show that the average size of the LDH crystallites in the composite is 61 nm, smaller than the MgAlLDH (311 nm) formed in the absence of glucose, indicating that the glucose and/or its derivatives limit crystal growth of the LDH.

Morphology and Microstructure
The morphology, microstructure and size of the prepared materials were determined by SEM and TEM observations. As can be seen from the SEM ( Figure 1b) and TEM ( Figure 1c) images, the HC-MgAlLDH is composed of numerous interweaved nanoplate-like structures with sub-100 nm sizes. Under the high-resolution bright-field mode of TEM (Figure 1d), the interweaved structures clearly show two distinct contrasts, the dark regions with obvious lattice fringes (e.g., box 1), but the light regions with an amorphous nature (e.g., box 2). Furthermore, the lattice fringes correspond well to the lattice plane of MgAlLDH, e.g., the 0.648 nm lattice fringe assigned as the (003) plane of trigonal hydrotalcite (box 1 in Figure 1d), whereas the amorphous materials can be assigned to the HC by combining the XRD results (e.g., Figure 1a). The high-resolution TEM images also show that the LDH and HC tightly coalesce together, indicating the successful formation of the HC-MgAlLDH nanocomposite. By contrast, the MgAlLDH synthesized without the addition of glucose presents a characteristic hexagonal sheet-like shape of LDH (e.g., Figure S1a) and a larger size (diameters of 200-1000 nm and a thickness of~50 nm) than the LDH in the nanocomposite. This reveals that the growth of LDH crystals was inhibited with the addition of glucose, supporting the XRD analyses. Similarly, the HC synthesized without the LDH-forming ions exhibits a different morphology from that in the nanocomposite. The HC is nanospheres with smooth surfaces and uniform diameters of 300 nm ( Figure S1b), showing the characteristics of the hydrothermal carbonization product of glucose [36]. In addition, the EDS results confirm that the nanocomposite (39.12%) has a much higher content of C than the LDH (15.48%) (Figures 1b and S1a), further confirming the composition of HC and LDH. The HC also contains 19.04% O ( Figure S1b), indicating that the nanocomposite has considerable amounts of O-rich functional groups.

Surface Chemistry and Zeta Potential
The surface chemical states and elemental composition of the samples were identified by XPS analysis. The survey spectra reveal that O, C, Mg and Al elements were detected in the prepared MgAlLDH and nanocomposite ( Figure 2a). However, compared with the LDH, the nanocomposite shows a stronger C 1s peak (Figure 2a [34]. Overall, the XPS results confirm that the HC and MgAlLDH are composited by chemical interactions, and the nanocomposite possesses abundant O=C and -OC/COOR groups. Their surface properties were further examined by a zeta potential analyzer. As shown in Figure 2f, the zeta potential of MgAlLDH is always positive at pH 2-12, probably due to the permanent positive charge of the primary lamellar plate from the isomorphic replacement of Mg 2+ by Al 3+ in LDH layers [38]. By contrast, the nanocomposite shows a much lower zeta potential at all the pH values, indicating that the modification with HC introduced oxygen-bearing functional groups with negative charges (e.g., -COO − ) to the surface of the nanocomposite. Thus, it can be anticipated that the combination of LDH with HC could improve the adsorption abilities of LDH to cationic MB and Pb(II).

Specific Surface Area and Pore Structure
The specific surface area and pore size distribution for the samples were determined by N 2 adsorption-desorption tests. The results are shown in Figure 3. For the HC-MgAlLDH, HC and MgAlLDH, all of the adsorption-desorption curves exhibit type IV isotherms (Figure 3a), revealing the presence of mesopores in the three materials. Nevertheless, the nanocomposite (Figure 3a) presents higher N 2 uptakes and a more remarkable hysteresis loop of H3 type in the range of 0.45-1.00 P/P 0 , indicating that the nanocomposite has a larger specific surface area and more slit-shaped pores [39]. The calculated BET-specific surface area (S BET ) of the nanocomposite is 152.06 m 2 /g (Figure 3a), which is sharply higher than the HC 9.14 m 2 /g, and the MgAlLDH 23.98 m 2 /g. The pore volume (V pore ) of the nanocomposite is 0.51 cm 3 /g, much larger than the V pore of the MgAlLDH 0.046 cm 3 /g or the HC 0.21 cm 3 /g (Figure 3a). In addition, the pore size distributions also demonstrate the significant porous structure in the nanocomposite, mainly in the range of 4-11 nm (Figure 3b). The increases in S BET and V pore may be conducive to the adsorption of CR, MB and Pb(II) onto the HC-MgAlLDH nanocomposite.

Optimizing the Compositional Ratio of HC and MgAlLDH
In order to screen the optimal nanocomposite, the HC, MgAlLDH, and their nanocomposites with different doping amounts of HC were used to remove single CR, MB and Pb(II) at contact time 12 h, pH 5, initial concentrations 100 mg/L for CR or MB, and 50 mg/L for Pb(II). As shown in Figure 4a, the removal capacities of the adsorbents to the three adsorbates all firstly increase, and then decrease with the HC contents. Nevertheless, it can be also seen from Figure 4a

Effect of Solution pH
The solution pH can significantly affect the adsorption performance because it may affect the surface charge of adsorbents and the species of sorbates [39]. Generally, Pb(II) can precipitate as Pb(OH) 2 in an alkaline solution (K sp,Pb(OH) 2 = 10 −15.00 ) ( Figure S2). Thus, for the single pollutant, the initial pH values ranging from 3 to 6 were selected for Pb(II) removal, and a wider pH range of 3−11 for CR and MB, but the other parameters including contact time, and the initial concentrations of CR, MB and Pb(II) were kept. The pH-dependent removal profiles for single CR, MB and Pb(II) by the nanocomposite are depicted in Figure 4b-d, respectively, and compared with the removals by LDH and HC. For the three sorbates, the nanocomposite shows much higher removal capacities than LDH and HC at all the pHs (Figure 4b-d), indicating that the composition of MgAlLDH and HC enhanced the removal performance. Specifically, the removal capacity to CR by the nanocomposite was as high as 172. 47-190.49 mg/g at pH 3-11, despite a slight decrease with the increase of pH (Figure 4b). The high removal of CR should be dominated by the component LDH in the nanocomposite because the unmodified LDH also have a similar but slightly inferior removal (Figure 4b). LDH, as a typical material with positively charged host layers, can adsorb anionic pollutants by strong electrostatic attraction [40]. In our study, the LDH always has positive zeta potentials over the pH from 3 to 11 (Figure 2f), and thus can generate strong adsorption to anionic CR. Nevertheless, the zeta potentials of the LDH decrease with increasing pH (Figure 2f). As a result, the decline in CR removal was observed either for the LDH or the nanocomposite in the scenario with higher pHs (Figure 4b). It is worth noting that the higher CR removal by the nanocomposite relative to the LDH (Figure 4b) should be attributed to its higher porosity and surface area (Figure 3). Similarly, for cationic MB, the negatively charged nanocomponent HC should significantly contribute to the removal due to the low removal of the LDH to MB (Figure 4c). The increasing removal capacity from 163.82 to 190.58 mg/g with a pH from 3 to 11 (Figure 4c) should result from the enhancement of electrostatic attraction (Figure 2f). The higher porosity and surface area could also be responsible for the higher removal capacities of the nanocomposite. However, the Pb(II) removal capacities by the nanocomposite appear to be the sum of the capacities by the nanocomponents LDH and HC (Figure 4d), implying that the two nanocomponents conjointly controlled the Pb(II) removal. In addition, the Pb(II) removal increases obviously from 18.72 to 40.36 mg/g with the pH from 3 to 6. This could be attributed to the deprotonation of -COOH to form -COO − and less competitive adsorption between Pb(II) and H + at higher pHs [34]. As a result, the wide and effective pH response could make the HC-MgAlLDH nanocomposite become a versatile adsorbent for cationic and anionic dyes and heavy metals.

Effect of Contact Time
The effects of contact time on CR, MB, or Pb(II) removal by the nanocomposite were investigated from 10 to 1440 min at initial pH 5, initial concentrations 100 mg/L for CR or MB, and 50 mg/L for Pb(II). The time-course removal profiles were depicted in Figure 5a. For the three targeted species, the removal capacities all increased very rapidly within the first 60 min, indicating that the nanocomposite possessed massive and multifunctional active sites for anionic CR and cationic MB and Pb(II). Subsequently, the increases were slow and adsorption saturations approached after about 360 min, implying that the active sites on the nanocomposite were almost completely occupied. Thus, a contact time of 720 min was used in the other batch experiments for a sufficient equilibrium state. Furthermore, the removal processes were analyzed by the nonlinear pseudo-first-order and pseudosecond-order kinetic models [41]. Detailed information on the models is provided in the Supplementary Material (Text S1), and the applicability was judged by the correlation coefficients (R 2 ). The results (Table S1) show that the pseudo-second-order model gives rise to greater R 2 values (all exceeding 0.98) than the pseudo-first-order, indicating that the removal of CR, MB, or Pb(II) onto the HC-MgAlLDH nanocomposite follows the pseudo-second-order kinetic model.  Figure 5b depicts the adsorption isotherms of CR, MB or Pb(II) determined at pH 5.0, contact time 12 h, initial concentrations 10-300 mg/L for CR or MB and 1-100 mg/L for Pb(II). It can be seen that their removal capacities increased rapidly with the equilibrium concentrations at the initial stage and then approached the maximum value. The fittings to the adsorption data by the Langmuir and Freundlich isothermal models show that all the adsorptions followed well the Langmuir model (Figure 5b and Table S2), revealing a monolayer adoption characteristic of the three sorbates on the HC-MgAlLDH [42]. Furthermore, the theoretical maximum removal capacities (q m ) determined by the Langmuir model for sole CR, MB and Pb(II) are 348.78, 256.54 and 33.55 mg/g, respectively, which are higher than partial previously reported LDH-based adsorbents (Table S3). Specifically, the q m for CR is higher than those of MgAlLDH (111.11 mg/g) [33], borate intercalated MgAlLDH (166.39 mg/g) [43], ZnFe 2 O 4 /MgAlLDH (294.12 mg/g) [44], and MgAlLDH modified diatom (305.8 mg/g), [45]. The q m for MB exceeds the values of ZIF-67/CoAlLDH (57.24 mg/g [46]), NiFeLDH decorated montmorillonite (99.18 mg/g) [20], dodecyl sulfate modified ZnAl LDH (113.00 mg/g) [47], and spherical HC capped MgAlLDH (226.00 mg/g) [30]. For Pb(II) removal, the nanocomposite also outperforms the MgAlLDH (16.93 mg/g) [48], MgFeLDH (18.45 mg/g) [19], and tartrate intercalated MgAlLDH (8.40 mg/g) [49]. Therefore, the prepared HC-MgAlLDH nanocomposite exhibited a good removal performance for single CR, MB and Pb(II).

Reusability
The reusability of an adsorbent is important for its practical application in wastewater treatment. To verify the reusability of the HC-MgAlLDH nanocomposite, the postadsorbents were regenerated by desorption with eluent agents. Specifically, 0.1 M NaOH, ethanol, and 0.01 M HCl were used to desorb the adsorbed CR, MB, and Pb(II), respectively [50][51][52]. The regenerated HC-MgAlLDH nanocomposites were then reused for four cycles. The results are presented in Figure S3. It can be seen that the removal efficiency for CR, MB, or Pb(II) slightly declined with the cycles. Despite that, the adsorbents after four cycles still have a high adsorption removal efficiency for CR (79.42%), MB (75.79%), or Pb(II) (71.45%). Moreover, the SEM and XRD analyses further reveal that the architecture and phase of adsorbents after four cycles are almost retained compared with the raw adsorbent ( Figures S4 and S5). These results demonstrate that the HC-MgAlLDH nanocomposite has excellent reusability.

Removal Performance in Binary and Ternary Systems
Considering that CR, MB, and/or Pb(II) usually coexist in industrial wastewaters (e.g., [6,7]), the removal experiments of the binary and ternary systems were performed by varying the target concentrations with the concomitants fixed at 20 mg/L. The results are shown in Figure 6a-c, accompanied by the results for single systems for comparison. For CR at each concentration (Figure 6a), its removal capacities in the systems of CR+Pb(II), CR+MB and CR+MB+Pb(II) slightly decreased, indicating that the concomitant MB and Pb(II) have a minor effect on CR removal. The removal processes also followed the Langmuir adsorption model, with the q m up to 337.55, 332.85 and 328.83 mg/g, respectively (Figure 6a and Table S2). Similarly, slight decreases in the q m of MB were also observed in MB+CR (242.69 mg/g), MB+Pb(II) (236.40 mg/g) and MB+CR+Pb(II) (188.96 mg/g) (Figure 6b and Table S2). Despite the declines in CR and MB removals, the HC-MgAlLDH still significantly outperforms the previous LDH-based composite adsorbents, as listed in Table S3. On the contrary, the Pb(II) removal was significantly enhanced by the CR and MB (Figure 6c), and the q m increased dramatically from 33.55 mg/g (sole Pb(II)) to 47.35 (Pb(II)+MB), 56.21 (Pb(II)+CR) and 63.28 mg/g (Pb(II)+CR+MB) ( Table S2). The increases should result from the complexation of Pb(II) with the adsorbed organic dye [14] or extra precipitation of PbSO 4 on the adsorbent. The details will be identified and discussed below. In conclusion, the results demonstrate that the HC-MgAlLDH nanocomposite could be an effective adsorbent for the simultaneous removal of CR, MB and Pb(II).

Insight into the Removal Mechanisms of CR, MB and Pb(II)
The adsorbent HC-MgAlLDH after adsorption treatment was further characterized by XRD, FTIR, and XPS to reveal the plausible removal mechanism. After the treatment of single CR, MB and Pb(II), no discernible variations in the XRD patterns of the postadsorbents were detected (Figure 7a), indicating that the single CR, MB and Pb(II) are removed mainly through adsorption on the nanocomposite rather than precipitation with the cations (Mg 2+ , Al 3+ ) or anions (OH − , CO 3 2− ) by dissolving the LDH [14,53]. In addition, the d 003 values of the post-adsorbent almost remain unchanged, confirming that the dye molecules and Pb(II) ions were not intercalated into the LDH interlayer space [54]. Nevertheless, the FT-IR spectrum after CR removal (Figure 7b) shows that the S-O vibration of the sulfonic group in adsorbed CR molecules shifted from 1063 to 1088 cm −1 , indicating that the interactions of electrostatic attraction/chemical bonding between CR and LDH component in the nanocomposite occur [16,33]. After treating MB, the band of =N(CH 3 ) 2 + groups in the adsorbed MB shifted from 1323 to 1329 cm −1 (Figure 7b), indicating that the electrostatic attraction between MB and HC component in the nanocomposite dominated the adsorption removal [55][56][57]. Additionally, the vibration of MB aromatic rings shifted from 1583 to 1600 cm −1 (Figure 7b), revealing that MB adsorption also occurs via the π-π interaction between the MB aromatic rings and the C=C bonds of HC component in the nanocomposite [34,55].
In addition, the high-resolution Mg 1s, Al 2p and O 1s XPS spectra show that their binding energies all increased after CR removal (Figure 8a-c), confirming that CR was also chemically adsorbed onto the nanocomposite via the complexation of CR sulfonic groups (-SO 3 − ) with the metal cations (i.e., Mg 2+ , Al 3+ ). A similar shift in the Mg 2p binding energy of Mg(OH) 2 caused by the complexation of Mg 2+ with citrate -COO − has also been reported [58]. After MB removal, however, only the O 1s binding energy exhibited a significant shift (Figure 8c), revealing that positively charged amino groups in MB interacted with the oxygen-containing functional groups (e.g., -COOH and -OH) of the nanocomponent HC [59]. After Pb(II) removal, obvious shifts to a high binding energy side can also be found, especially in the Mg 1s and O 1s spectra (Figure 8a-c). Similar shifts have been also observed in U(VI) adsorption on Mn 3 O 4 @sepiolite nanocomposite through Mn/Si/Mg-O-U(VI) bonds [60], and Pb(II) or Cd(II) adsorption on Axonopus compressusderived biochar via their complexations with the -COOH and -OH moieties [61]. In our case, therefore, the complexations of Pb(II) with the Mg/Al-O and -COOH/-OH should be formed on the HC-MgAlLDH nanocomposite.   (Figure 7a). This confirms that the formation of PbSO 4 precipitation is an additional removal mechanism for Pb(II) in the binary and ternary solutions. The SO 4 2− should originate from the desulfonation of CR and/or the oxidation of the thiazine ring in MB caused by the HC-generated free radicals [62]. Moreover, the diffraction intensity of PbSO 4 was more intense after treatment of the ternary system than the binary systems (Figure 7a), indicating that more PbSO 4 was formed in the presence of the two dyes. This should be ascribed to more SO 4 2− supply by the coexisting dyes. The PbSO 4 precipitation can further increase the removal capacity of Pb(II), supporting the high removal results (Figure 6c). It appears that the HC-MgAlLDH nanocomposite possesses much more specificity for multiple pollutant removal. Besides, the FT-IR spectra after the treatment of binary and ternary pollutants show similar shifts to those after the sole treatment (Figure 7b), indicating that the similar electrostatic attraction/chemical bonding contributes significantly to the multi-pollutant mixture removal as well.
To further explore the interactions of the S-bearing groups in CR and MB with the nanocomposite and Pb(II) during the removal, analyses on the high-resolution S 2p XPS spectra were conducted after the adsorptions (Figure 9). For the CR-adsorbed sample (Figure 9a), the S 2p spectrum shows a main peak at 168.51 eV assigned to the -SO 3 − of CR and a weak peak corresponding to thiol-type S at a lower energy of 163.43 eV [63,64], indicating that a small amount of CR on the adsorbent was reduced to thiols by the nanocomposite. As to the MB-adsorbed sample (Figure 9b), in addition to the peak of the C-S bond in MB at 164.58 eV, the peaks of oxidized-state S-O bond at a higher energy (168.91 eV) and reduced-state S-H bond at a lower energy (163.28 eV) can be clearly distinguished, indicating that the C-S bonds in the adsorbed MB were disproportionated. Previous studies have confirmed that HC with rich organic groups can act as the electron shuttle to induce the abiotic reduction of heavy metals ions (e.g., Cr(VI) and Ag(I)) and generate reactive oxygen species (e.g., •O 2 − , H 2 O 2 , and •OH) to oxidize organic pollutant (e.g., sulfadimidine and bisphenols) [65][66][67]. Therefore, in our case, the CR reduction and MB disproportionation should be associated with the HC in the nanocomposite. The S 2p spectrum after the removal of coexisting CR and MB (Figure 9c) shows an integrated state of the spectra after their single removal. Nevertheless, after treating the Pb(II)-containing binary and ternary solutions, the S 2p binding energies associated with thiol (163.28-163.43 eV) shifted to lower energy ranges (162.25-162.35 eV) (Figure 9d-f), indicating that Pb(II)-thiol complex was formed on the adsorbent [68]. In conclusion, the removal of CR, MB and Pb(II) by the HC-MgAlLDH nanocomposite involves multiple actions, including electrostatic adsorption, π-π interaction, coordination and/or precipitation crystallization.

Conclusions
In summary, the HC-MgAlLDH nanocomposite was successfully fabricated by a facile one-step hydrothermal technique and used as an adsorbent for single or simultaneous removal of anionic dye CR and cationic dye MB as well as heavy metal Pb(II). The batch removal experimental results revealed that the nanocomposite has superior removal per-formances to the single MgAlLDH and HC, and its maximum Langmuir removal capacity to CR, MB or Pb(II) is 348.78, 256.54, or 33.55 mg/g, respectively. In the multi-pollutant systems, the nanocomposite can not only dramatically increase Pb(II) removal, but also exhibits high removal of CR and MB. Therefore, the nanocomposite can act as an effective adsorbent for the simultaneous removal of CR, MB and Pb(II). Moreover, the removal of CR, MB and Pb(II) by the nanocomposite involves a series of interactions between the adsorbate species and the adsorbent, including electrostatic adsorption, π-π interaction, coordination and/or precipitation crystallization. Current results contribute to the efficient removal of various types of pollutants by developing a new and multifunctional adsorbent and advance the understanding of the interactions between heavy metals and organic dyes during wastewater treatment.
Supplementary Materials: The following supporting information can be downloaded at: https://www. mdpi.com/article/10.3390/nano13071145/s1, Text S1: Adsorption kinetic and isothermal models; Table S1: Kinetic parameters of CR, MB or Pb(II) adsorption onto the HC-MgAlLDH; Table S2: Adsorption isothermal parameters of CR, MB and Pb(II) by the HC-MgAlLDH nanocomposite in various systems; Table S3

Data Availability Statement:
The data presented in this study are available on request from the corresponding authors.