WO3 Nanorods Decorated with Very Small Amount of Pt for Effective Hydrogen Evolution Reaction

The electrochemical hydrogen evolution reaction (HER) is one of the most promising green methods for the efficient production of renewable and sustainable H2, for which platinum possesses the highest catalytic activity. Cost-effective alternatives can be obtained by reducing the Pt amount and still preserving its activity. The Pt nanoparticle decoration of suitable current collectors can be effectively realized by using transition metal oxide (TMO) nanostructures. Among them, WO3 nanorods are the most eligible option, thanks to their high stability in acidic environments, and large availability. Herein, a simple and affordable hydrothermal route is used for the synthesis of hexagonal WO3 nanorods (average length and diameter of 400 and 50 nm, respectively), whose crystal structure is modified after annealing at 400 °C for 60 min, to obtain a mixed hexagonal/monoclinic crystal structure. These nanostructures were investigated as support for the ultra-low-Pt nanoparticles (0.2–1.13 μg/cm2): decoration occurs by drop casting some drops of a Pt nanoparticle aqueous solution and the electrodes were tested for the HER in acidic environment. Pt-decorated WO3 nanorods were characterized by performing scanning electron microscopy (SEM), X-ray diffraction analysis (XRD), Rutherford backscattering spectrometry (RBS), linear sweep voltammetry (LSV), electrochemical impedance spectroscopy (EIS) and chronopotentiometry. HER catalytic activity is studied as a function of the total Pt nanoparticle loading, thus obtaining an outstanding overpotential of 32 mV at 10 mA/cm2, a Tafel slope of 31 mV/dec, a turn-over frequency of 5 Hz at −15 mV, and a mass activity of 9 A/mg at 10 mA/cm2 for the sample decorated with the highest Pt amount (1.13 μg/cm2). These data show that WO3 nanorods act as excellent supports for the development of an ultra-low-Pt-amount-based cathode for efficient and low-cost electrochemical HER.


Introduction
The increasing global energy demand, the finite supply of fossil fuels, and the related global warming and environmental pollution pushes the attention of the scientific community to the development of renewable and sustainable energy sources. In this scenario, H 2 is a key player since it is characterized by high reactivity and its energy content is three times higher than gasoline [1]. The H 2 -based economy represents a valid green alternative to solve the problems related to fossil fuel combustion. H 2 naturally exists combined with other elements and not in the pure elemental gas form [2], so the production of H 2 gas, starting from H-based compounds, is fundamental for the development of an efficient H 2 -based economy.
One of the most sustainable and eco-friendly methods to produce green H 2 is electrochemical water splitting, which coincides with the separation of water in H 2 and O 2 (hydrogen and oxygen evolution reaction, respectively), thanks to an external potential bias [3][4][5]. Platinum is the most active catalyst for the hydrogen evolution reaction (HER) process, especially in acidic environments [6]. Nevertheless, the limited worldwide supply and the high cost of Pt hinders its use for large-scale H 2 production through electrochemical water splitting [7,8]. For the establishment of a carbon-neutral economy, a significant reduction of the Pt load for HER is urgently needed [9]. A potential solution is the development of a low-cost and efficient support for Pt to reduce its utilization. Transition metal oxide (TMO)-based nanostructures possess high electrochemical stability in both acidic and alkaline media, are earth abundant, and their electrochemical properties depend on morphology and crystal structure. They can be useful as Pt supports, giving a high surface to volume ratio if the charge exchange towards the catalytic noble element is not hindered. Decoration with very low amounts of Pt nanoparticles allows the exploitation of the synergistic effect between Pt nanoparticles and TMO-based nanostructures. This strategy enables the lowering of the total production cost, without affecting the Pt electrocatalytic efficiency. Xie et al. [10] synthesized MoO 2 on multiwalled carbon nanotubes (MWCNTs) and decorated these nanocomposites with a low amount of Pt nanoparticles (0.47 mg/cm 2 ). The electrochemical analysis in 0.5 M H 2 SO 4 confirms the excellent activity of the decorated nanocomposite, which shows an overpotential at 10 mA/cm 2 of 60 mV, compared to those of the bare composite which is about 500 mV.
Several earth-abundant TMO-based electrocatalysts have been studied for the activation of efficient HER in acidic conditions [4,6,11,12]. Among them, WO 3 represents a suitable candidate thanks to its large availability and high electrochemical stability at low pH, especially in the nanostructured form (nanorods, nanowires, nanosheets) [13][14][15]. Unfortunately, in their pristine form, WO 3 nanostructures possesses a poor electron transport ability and few active sites for hydrogen ion absorption, which result in a poor HER ability [7,16,17]. Many efforts have been made with the aim of improving the HER catalytic activity of WO 3 nanostructures, such as the realization of heterostructures by coupling WO 3 with other transition-metals-based materials (WS 2 , WSe 2 , or WC) [18][19][20] and embedding with carbon-based materials [21,22]. In our previous work [13], we proposed a low cost and simple approach to improve the HER catalytic activity of WO 3 , reducing the overpotential at 10 mA/cm 2 from 460 mV (for as-prepared fully hexagonal WO 3 ) to 170 mV (for hexagonal/monoclinic mixed-phase WO 3 nanorods).
Here, we report a decoration of phase engineered WO 3 nanorods with an ultra-low amount of Pt nanoparticles as a new strategy to further improve H 2 production. The HER catalytic activity is studied as a function of Pt-loading reaching a notable overpotential of 32 mV at 10 mA/cm 2 , a Tafel slope of 31 mV/dec, and an unprecedented turn-over frequency and mass activity of 5 Hz at −15 mV and 9 A/mg at 10 mA/cm 2 , respectively.

Synthesis of WO 3 Nanorods and Pt Nanoparticles
All the reagents were purchased from Sigma-Aldrich, (St. Louis, MO, USA) and used without further purification. WO 3 nanorods were hydrothermally synthesized according to our previous work [14,23]. In brief, the precursor solution was prepared using sodium tungstate (Na 2 WO 4 , 0.825 g) dissolved in deionized water (19 mL). Then, 3 M hydrochloric acid (HCl) and sodium chloride (NaCl) were used to acidify the solution (until a 2.2 pH) and as capping agent, respectively. The thermal treatment was conducted in a muffle by using a 25 mL autoclave, at 180 • C for 3 h. The obtained nanostructures were collected and washed by centrifugating with water and ethanol several times (6000 RPM for 10 min). The powders were calcinated on a hot plate in air at 400 • C, as described in our previous work [13], to obtain a partial hexagonal to monoclinic phase transition until reaching similar contents. The annealing time was set as 60 min, so that the hexagonal and monoclinic crystallites phases had comparable volumes [14].
Pt nanoparticles were synthesized according to Bruno et al. [24], thus using a room temperature and green chemical reduction method. Ascorbic acid (AA, 30 µL of a 33 mM solution) was used as reducing acid and was dispersed in a H 2 PtCl 6 solution (30 mL of 0.2 mM solution). The obtained dispersion was stirred for 5 min.
The Pt electrode was prepared by sputtering deposition on a graphene paper ((GP, 2 × 1 cm 2 , 240 µm thick, Sigma Aldrich, St. Louis, MO, USA)) substrate, using a sputter apparatus Emitech K550X A (Ashford Kent, UK), in which the GP was the cathode, facing the Pt source (purity of 99.999%). Next, 100 nm of Pt film was deposited on the GP substrate, with a covered area of 1 cm 2 , by setting the emission current at 50 mA and the deposition time at 16 min.

Electrode Preparation
WO 3 nanorods powder was dissolved in water (4 mg/mL) and sonicated for 10 min to reach a homogeneous aqueous dispersion. GP was used as substrate after a polishing procedure with water and ethanol. The WO 3 -based dispersion was used for drop coating the GP substrate, thus covering a 0.3 cm 2 area (drying in air for 20 min at 70 • C allowed solvent evaporation). A Mettler Toledo MX5 Microbalance (sensitivity: 0.01 mg) was used to measure the mass of the electrode (substrate + WO 3 nanorods) and of the bare substrate. Some drops of the Pt dispersion (5 µL volume) were drop coated on the WO 3 nanorodbased electrodes, which were labeled 5Pt-WO 3 , 10Pt-WO 3 , and 20Pt-WO 3 , respectively, depending on the used drops number.

Characterization of the Pt-Decorated WO 3 Nanorods
Film structure was analyzed through X-ray Diffraction (XRD) by using a Smartlab Rigaku diffractometer (Rigaku Corporation, Tokyo, Japan), at a grazing incidence of 0.5 • , equipped with a rotating anode of Cu Kα radiation operating at 45 kV and 200 mA. The scans were acquired from 10 • to 70 • with a step of 0.02 • . The morphological analyses were carried out using a Gemini Field Emission SEM Carl Zeiss SUPRATM 25 (FEG-SEM, Carl Zeiss Microscopy GmbH, Jena, Germany) scanning electron microscope (SEM) in IN-LENS mode. For the determination of Pt content, Rutherford backscattering spectrometry (RBS, 2.0 MeV He + beam at normal incidence) with a 165 • backscattering angle was employed, using a 3.5 MV HVEE Singletron accelerator. RBS spectra were analyzed using XRump software (version 0.91) [25]. The electrochemical measurements were performed at room temperature using a potentiostat (VersaSTAT 4, Princeton Applied Research, Oak Ridge, TN, USA) and a three-electrode setup with a graphite rod electrode as a counter electrode (to avoid Pt contamination), a saturated calomel electrode (SCE) as reference, and the Pt-decorated WO 3 electrodes as working electrodes, in a 1 M H 2 SO 4 supporting electrolyte.

Electrochemical Measurements
Electric current values were normalized to the geometrical-immersed surface area of each electrode. The conversion of the measured potential vs. SCE into the reversible hydrogen electrode (RHE) was carried out according to the Nernst equation [19,26]: where E Θ SCE is the standard potential of the SCE electrode at 25 • C (0.241 V) and E SCE is the measured potential vs. SCE. The HER activities of WO 3 and of Pt-decorated WO 3based electrodes were investigated using a linear sweep voltammetry (LSV) recorded at 5 mV/s from −0.2 V to −0.8 V vs. SCE. All the obtained potentials vs. RHE were manually corrected using iR u compensation as follows: where i is the electrode current and R u [Ohms] is the uncompensated resistance, measured using electrochemical impedance spectroscopy (EIS) [27], which is performed from 10 5 to 10 −1 Hz in a potentiostatic mode with an AC voltage of 5 mV at the open circuit potential  Figure S1. The Tafel slope was defined as the slope of the linear fit of the potential vs. log(j(mA/cm 2 )) plot, according with the follow equation [28]: where E RHE is the iR u -free potential (V), b is the Tafel slope (V/dec), J is the current density (mA/cm 2 ), and a is a constant. The appropriate potential region for the Tafel slope analysis was chosen to ensure that the measured current density resulted only from the faradaic reaction which occurs during the HER mechanism [28].

Morphological and Structural Analysis
WO 3 nanorods were synthesized using the hydrothermal route, and the post-synthesis thermal annealing (400 • C for 60 min) was conducted with the aim of improving the HER catalytic activity according to our previous work [14]. A partial hexagonal to monoclinic phase transition was achieved after the thermal annealing, as shown in the XRD pattern of Figure S2, in which the XRD pattern of the WO 3 nanorods is compared with the characteristic XRD patterns of the hexagonal and monoclinic WO 3 . Our previous analysis confirmed the formation of stable hexagonal/monoclinic phase junctions in these conditions, which were able to confer a higher HER catalytic activity than that of the pure hexagonal WO 3 nanorods. The reference intensity ratio (RIR) method was used for the calculation of phase composition in a hybrid phase structure, thus obtaining the monoclinic (hexagonal) weight ratio in the WO 3 -based nanorods of 56% (44%) (details in the Supplementary Materials). Figure 1a shows a low-magnification SEM image (in tilt view) of the bare WO 3 nanorods electrode, which is composed of randomly aligned nanorods covering the GP substrate. The image shows the role of WO 3 nanorods in realizing a highly exposed active surface due to 3D nanorods agglomeration. Figure 1b shows low-magnification SEM images of the 10Pt-WO 3 electrode, in which Pt nanoparticles (indicated by yellow circles, average diameter of 50 nm) are in contact with the WO 3 nanorods. Further details of Pt nanoparticles realized with this method are reported in Refs. [24,29]. Figure S3 shows a low-magnification SEM image of the 10Pt_WO 3 electrode in which Pt nanoparticles (highlighted in yellow) are homogeneously scattered all over WO 3 nanorods. Nanomaterials 2023, 13, x FOR PEER REVIEW 4 of 10 (OCP vs. SCE) as shown in Figure S1. The Tafel slope was defined as the slope of the linear fit of the potential vs. log(j(mA/cm 2 )) plot, according with the follow equation [28]: where ERHE is the iRu-free potential (V), b is the Tafel slope (V/dec), J is the current density (mA/cm 2 ), and a is a constant. The appropriate potential region for the Tafel slope analysis was chosen to ensure that the measured current density resulted only from the faradaic reaction which occurs during the HER mechanism [28].

Morphological and Structural Analysis
WO3 nanorods were synthesized using the hydrothermal route, and the post-synthesis thermal annealing (400 °C for 60 min) was conducted with the aim of improving the HER catalytic activity according to our previous work [14]. A partial hexagonal to monoclinic phase transition was achieved after the thermal annealing, as shown in the XRD pattern of Figure S2, in which the XRD pattern of the WO3 nanorods is compared with the characteristic XRD patterns of the hexagonal and monoclinic WO3. Our previous analysis confirmed the formation of stable hexagonal/monoclinic phase junctions in these conditions, which were able to confer a higher HER catalytic activity than that of the pure hexagonal WO3 nanorods. The reference intensity ratio (RIR) method was used for the calculation of phase composition in a hybrid phase structure, thus obtaining the monoclinic (hexagonal) weight ratio in the WO3-based nanorods of 56% (44%) (details in the Supplementary Materials). Figure 1a shows a low-magnification SEM image (in tilt view) of the bare WO3 nanorods electrode, which is composed of randomly aligned nanorods covering the GP substrate. The image shows the role of WO3 nanorods in realizing a highly exposed active surface due to 3D nanorods agglomeration. Figure 1b shows low-magnification SEM images of the 10Pt-WO3 electrode, in which Pt nanoparticles (indicated by yellow circles, average diameter of 50 nm) are in contact with the WO3 nanorods. Further details of Pt nanoparticles realized with this method are reported in Refs. [24,29]. Figure S3 shows a low-magnification SEM image of the 10Pt_WO3 electrode in which Pt nanoparticles (highlighted in yellow) are homogeneously scattered all over WO3 nanorods. By considering the assumption for which the total Pt content does not depend on the decorated substrate, the same Pt dispersion volume used for the Pt-decorated electrodes was drop casted on Si substrates and measured using RBS analysis. Figure 1c shows the enlargement of the RBS spectrum in correspondence with the Pt peak (at 1837 keV) for the 5Pt_WO3, the 10Pt_WO3, and the 20Pt_WO3 electrodes (blue, yellow, and green lines, respectively). The area of the peak is strictly correlated to the total Pt dose which results in By considering the assumption for which the total Pt content does not depend on the decorated substrate, the same Pt dispersion volume used for the Pt-decorated electrodes was drop casted on Si substrates and measured using RBS analysis. Figure 1c shows the enlargement of the RBS spectrum in correspondence with the Pt peak (at 1837 keV) for the 5Pt_WO 3 , the 10Pt_WO 3 , and the 20Pt_WO 3 electrodes (blue, yellow, and green lines, respectively). The area of the peak is strictly correlated to the total Pt dose which results in 6.08 × 10 14 , 1.31 × 10 15 , and 3.51 × 10 15 at/cm 2 for the 5Pt_WO 3 , the 10Pt_WO 3, and the Nanomaterials 2023, 13, 1071 5 of 10 20Pt_WO 3 electrodes, respectively. Thus, considering the Pt-covered area, the total Pt mass was calculated as follows: where S is the geometrical deposited area of the electrode substrate, N A is the Avogadro number and M m(Pt) is the Pt molar mass. The total mass results were 0.2, 0.43 and 1.13 µg/cm 2 for the 5Pt_WO 3 , the 10Pt_WO 3 , and the 20Pt_WO 3 electrodes, respectively. All these results are reported in Table 1.  Figure 2a shows the iR u -corrected LSV curve obtained for the WO 3 , the 5Pt_WO 3 , the 10Pt_WO 3 , the 20Pt_WO 3 , and the Pt electrodes (red, blue, yellow, green, purple lines) at 5 mV/s. The polarization curves of the WO 3 differ from the other curves for the presence of a current plateau at low potentials (red curve), which results in a much lower HER.  (4) where S is the geometrical deposited area of the electrode substrate, NA is the Avogadro number and is the Pt molar mass. The total mass results were 0.2, 0.43 and 1.13 μg/cm 2 for the 5Pt_WO3, the 10Pt_WO3, and the 20Pt_WO3 electrodes, respectively. All these results are reported in Table 1.  Figure 2a shows the iRu-corrected LSV curve obtained for the WO3, the 5Pt_WO3, the 10Pt_WO3, the 20Pt_WO3, and the Pt electrodes (red, blue, yellow, green, purple lines) at 5 mV/s. The polarization curves of the WO3 differ from the other curves for the presence of a current plateau at low potentials (red curve), which results in a much lower HER. Catalytic activity of the bare WO3 electrode with respect to those of the Pt-decorated electrodes. The Pt-decorated WO3 polarization curves show a rapid increase in the absolute value of the current density, thus suggesting a huge H2 production activity, which is more pronounced for the electrode with the highest Pt content (20Pt_WO3), as expected. The overpotential at 10 mA/cm 2 ( ) is the most common parameter used for the comparison of the HER catalytic activity. To achieve a current density of 10 mA/cm 2 , the values are 173 mV, 63 mV, 44 mV, 32 mV, and 27 mV for the WO3, the 5Pt_WO3, the 10Pt_WO3, the 20Pt_WO3, and the Pt electrodes, respectively. This is a clear indication that decoration with an additional sub microgram amount of Pt nanoparticles per cm 2 effectively improves the catalytic performances in HER. To highlight the role of Pt loading on HER catalytic activity, the current density at potentials above the (-90 mV) was reported as a function of Pt dose. Figure 2b shows the result of this exercise, in which a linear Catalytic activity of the bare WO 3 electrode with respect to those of the Pt-decorated electrodes. The Pt-decorated WO 3 polarization curves show a rapid increase in the absolute value of the current density, thus suggesting a huge H 2 production activity, which is more pronounced for the electrode with the highest Pt content (20Pt_WO 3 ), as expected. The overpotential at 10 mA/cm 2 (η) is the most common parameter used for the comparison of the HER catalytic activity. To achieve a current density of 10 mA/cm 2 , the η values are 173 mV, 63 mV, 44 mV, 32 mV, and 27 mV for the WO 3 , the 5Pt_WO 3 , the 10Pt_WO 3 , the 20Pt_WO 3 , and the Pt electrodes, respectively. This is a clear indication that decoration with an additional sub microgram amount of Pt nanoparticles per cm 2 effectively improves the catalytic performances in HER. To highlight the role of Pt loading on HER catalytic activity, the current density at potentials above the η (-90 mV) was reported as a function of Pt dose. Figure 2b shows the result of this exercise, in which a linear dependence between the measured current density and the total Pt loading is clear. We can conclude that Pt decoration linearly increases the catalysis towards HER, showing that WO 3 nanorods act as ideal support for Pt.

Electrochemical Analysis
To further elaborate the difference between HER mechanism of WO 3 and of Ptdecorated WO 3 electrodes, Tafel analysis was carried out. Figure 2c shows the Tafel plot of the WO 3 , the 5Pt_WO 3 , the 10Pt_WO 3 , and the 20Pt_WO 3 electrodes (red, blue, yellow, and green circles, respectively), calculated from the polarization curves reported in Figure 2a, according to Equation (3), in the faradaic potential range close to the η value of each tested electrode. The Tafel slope is defined from the linear fit of the Tafel plot (red, blue, yellow, and green lines, respectively), and results of 104 mV/dec, 75 mV/dec, 37 mV/dec and 31 mV/dec were obtained for the four samples, respectively (Table 1), thus confirming that Pt decoration results in convenient HER kinetics, since the Tafel slopes of Pt-decorated electrodes reach the theoretical Pt Tafel slope (30 mV/dec) in the same potential interval (from 0 V to −100 mV vs. RHE) [8].
The excellent intrinsic HER catalytic activity of the Pt-decorated WO 3 electrodes may be further confirmed by analyzing the turn-over frequency (TOF) parameter, calculated starting from the polarization curve of the 5Pt_WO 3 , 10Pt_WO 3 , and 20Pt_WO 3 electrodes (Figure 2a). The TOF is a marker of the intrinsic activity of the HER process, and it measures the amount of product formed or reactant consumed for a given amount of active catalyst per unit time, thus being a solid measure of the concentration of active sites [30]: where j is the measure current, x is equal to two (number of transferred electrons for each H 2 molecule produced), n is the Pt moles number, calculated from the RBS Pt dose, and F is the Faraday constant. Figure 3a shows the TOF extracted in a potential range close to the η value for the 5Pt_WO 3 , the 10Pt_WO 3 , and the 20Pt_WO 3 electrodes (blue, yellow, and green circles). TOF values increase with the applied potential, as expected, and they still show comparable values between the three samples. At an overpotential lower than 0.4 V, the 20Pt_WO 3 electrodes show a slightly lower TOF than that of the 5 PT_WO 3 and of 10Pt_WO 3 electrodes, due to its high mass (three and six times higher than the 10Pt_WO 3 and the 5Pt_WO 3 ones). Such a result tells us that WO 3 nanorods act as an effective support for Pt as a HER catalyst and, more than that, it shows that even after increasing the Pt loading, a saturation effect is still not visible. A further increase in the Pt loading can be sustained by this WO 3 nanorod support, which would give an additional increase in the current. The TOF value obtained at −15 mV are 5, 4, and 3 Hz for the 5Pt_WO 3 , 10Pt_WO 3 , and 20Pt_WO 3 electrodes, respectively. These TOF values are comparable with those reported for commercial Pt [8], and higher if compared with the literature results on Pt-decorated nanostructures ( Table 2). As a matter of fact, the catalytic activity of the Pt-decorated WO 3 -nanorod-based electrodes depends on the high concentration of exposed active absorption sites due to Pt decoration, thus highlighting the great potential of the Pt scalability process. Mass activity is a powerful parameter used for the comparison of the HER catalytic activity of different electrodes, which allowed us to define the activity per unit mass of electrochemical active material and takes into consideration the scalability properties. Mass activity is defined as follows, thus considering the geometrical area [6]: Mass activity = j A/cm 2 catalist loading(mg/cm 2 ) (6) Figure 3b reports the comparison between the mass activity of the state of the art Pt-based electrodes (blue balls) and of our Pt-decorated WO 3 electrodes (red ball) in acidic conditions, as a function of η [6]. The highest mass activity was obtained for the sample with the lowest Pt amount (5Pt_WO 3 ), as expected. However, our Pt-decorated WO 3 electrodes show at very low overpotential mass activity comparable with that of the state of the art on Pt-decorated electrodes, thus suggesting that despite the low Pt loading, the catalytic activity of our Pt-decorated WO 3 electrodes towards HER is very promising from the perspective of the development of efficient and a low-cost HER cathode.
Stability is an important parameter which describes the quality and the activity of an electrode, especially at those potentials at which the HER mechanism occurs. Figure 3c shows the chronopotentiometry applied to study the stability of the 20Pt-WO 3 electrode at a current density of 10 mA/cm 2 . The potential remains constant at the η value, even after 45 min of stress, thus revealing a good stability of the 20Pt_WO 3 electrode after the activation of the HER. Mass activity is a powerful parameter used for the comparison of the HER catalytic activity of different electrodes, which allowed us to define the activity per unit mass of electrochemical active material and takes into consideration the scalability properties. Mass activity is defined as follows, thus considering the geometrical area [6]: Figure 3b reports the comparison between the mass activity of the state of the art Ptbased electrodes (blue balls) and of our Pt-decorated WO3 electrodes (red ball) in acidic conditions, as a function of [6]. The highest mass activity was obtained for the sample with the lowest Pt amount (5Pt_WO3), as expected. However, our Pt-decorated WO3 electrodes show at very low overpotential mass activity comparable with that of the state of the art on Pt-decorated electrodes, thus suggesting that despite the low Pt loading, the catalytic activity of our Pt-decorated WO3 electrodes towards HER is very promising from the perspective of the development of efficient and a low-cost HER cathode.
Stability is an important parameter which describes the quality and the activity of an electrode, especially at those potentials at which the HER mechanism occurs. Figure 3c shows the chronopotentiometry applied to study the stability of the 20Pt-WO3 electrode  Table 2 compare our results with that reported in the literature on Pt-decorated metal oxide frameworks, for HER in acidic conditions. Our electrodes show a Pt content (of the order of µg/cm 2 ) 2-3 orders of magnitude lower than others, and, despite this, their electrochemical performances are much better in terms of overpotential, Tafel, TOF, and mass activity. The 20Pt_WO 3 electrode possesses the lowest η, thus revealing a very efficient HER process, confirmed also by the high TOF value at −15 mV, which is due to the high activity of the electrochemical active sites.

Conclusions
We demonstrated the excellent HER activity of Pt-decorated phase-structure-engineered WO 3 nanorods, creating very promising electrodes for hydrogen generation via water electrolysis. WO 3 nanorods were synthesized using a simple hydrothermal method, followed by calcination at 400 • C, leading to a particular hexagonal/monoclinic crystal structure. The WO 3 nanorods are active as catalysts for HER, and, still, the decoration with an ultralow amount of Pt (about 1 µg/cm 2 )) considerably boosted the HER performance. The WO 3 electrode decorated with 1.13 µg/cm 2 exhibits an overpotential at 10 mA/cm 2 of 32 mV, thanks to the synergistic effect between Pt nanoparticles and WO 3 nanorods, as the Tafel analysis suggests. Moreover, the high TOF value towards with the mass activity of our ultra-low-amount Pt-decorated WO 3 -nanorod-based electrodes makes them potential candidates for sustainable hydrogen production, especially in the context in which the Pt use has to be controlled and reduced.
Supplementary Materials: The following supporting information can be downloaded at: https: //www.mdpi.com/article/10.3390/nano13061071/s1: Figure S1: Nyquist plot obtained from EIS analysis at open circuit potential of the WO 3 , 5Pt_WO 3 , the 10Pt_WO 3 , and the 20Pt_WO 3 electrodes (red, blue, yellow, and green circles, respectively). Inset: Magnification of the high frequency region; Figure S2: XRD pattern of the WO 3 nanorods (red line) compared with the characteristic patterns of hexagonal and monoclinic WO 3 Figure S3: Low magnification SEM image of the 10Pt_WO3 electrode in which the most visible Pt nanoparticles are highlighted in yellow; Description of the RIR method. References [14,36,37] are cited in the Supplementary Materials.