Noble Metal Nanoparticle-Loaded Porphyrin Hexagonal Submicrowires Composites (M-HW): Photocatalytic Synthesis and Enhanced Photocatalytic Activity

Surface plasmon resonance (SPR) photocatalysts have attracted considerable attention because of their strong absorption capacity of visible light and enhanced photogenic carrier separation efficiency. However, the separate production of metal nanoparticles (NPs) and semiconductors limits the photogenic charge transfer. As one of the most promising organic photocatalysts, porphyrin self-assemblies with a long-range ordered structure-enhance electron transfer. In this study, plasmonic noble metal-based porphyrin hexagonal submicrowires composites (M-HW) loaded with platinum (Pt), silver (Ag), gold (Au), and palladium (Pd) NPs were synthesized through a simple in situ photocatalytic method. Homogeneous and uniformly distributed metal particles on the M-HW composites enhanced the catalytic or chemical properties of the organic functional nanostructures. Under the same loading of metal NPs, the methyl orange photocatalytic degradation efficiency of Ag-HW [kAg-HW (0.043 min−1)] composite was three times higher than that of HW, followed by Pt-HW [kPt-HW (0.0417 min−1)], Au-HW [kAu-HW (0.0312 min−1)], and Pd-HW [kPd-HW (0.0198 min−1)]. However, the rhodamine B (RhB) and eosin B photocatalytic degradations of Pt-HW were 4 times and 2.6 times those of HW, respectively. Finally, the SPR-induced electron injection, trapping, and recombination processes of the M-HW system were investigated. These results showed that M-HW plasmonic photocatalysts exhibited excellent photocatalytic performances, making them promising materials for photodegrading organic pollutants.


Introduction
Environmental pollution has become a major concern because of rapid industrial development, which greatly threatens human health and social stability [1][2][3]. As a result, photocatalysis, as an ideal environmental purification and green energy production technology using semiconductor materials, has attracted considerable scholarly attention. In addition, it uses solar energy for the photodegradation of organic pollutants [4], organic synthesis (e.g., selective oxidation and reduction), and water splitting for hydrogen generation. Therefore, the synthesis of efficient photocatalysts is crucial. The two key factors that determine the catalytic efficiency are the absorption spectrum and separation efficiency of the photogenerated charge of the materials [5]. Noble metal (such as Au, Pt, Ag, and Pd) nanoparticles (NPs) can strongly absorb visible light owing to their surface plasmon resonance (SPR) features [6][7][8][9]. They can also enhance the separation of a photogenerated

Synthesis of M-HW Nanocomposites
The synthesis of the ZnTPyP hexagonal submicrowires (HW): HW were prepared via an acid-based neutralization surfactant encapsulation self-assembly method [39,40]. Typically, 0.5 mL of ZnTPyP (0.01 M) solution was quickly injected into 9.5 mL of an aqueous solution containing cetyltrimethylammonium bromide (CTAB) (0.01 M) and NaOH (0.02 M) and was rapidly stirred at room temperature (25 °C) for 48 h. The ZnTPyP hexagonal HW was centrifuged at 9500 rpm and washed three times with water to remove the surfactant. Then, the HW was redispersed in water with a mass concentration of 6.67 mg/mL for preparing metal-organic composites (M-HW).
The synthesis of Pt-HW composite: K2PtCl4 (10 mM) solution and an equal volume of AA solution (0.1 M) were added to a 20 mL glass vial containing 10 mL of dispersed HW (0.1 mg/mL). The mixture was sonicated to ensure it was homogenized and it was then irradiated with a photocatalytic system at room temperature. All the photocatalytic reactions were irradiated using a 300 W xenon lamp equipped with a UVCUT400 filter (λ ≥ 400 nm), in which the incident light passed through a 10 cm water filter. The center of the glass vial was about 20 cm away from the light source, and the light intensity was approximately 100 mW/cm 2 . After the mixture was irradiated for 30 min, the solution changed from purple to black under visible light, indicating that the Pt metal was reduced. After the solution was centrifuged at 9500 rpm for 10 min, monodisperse Pt-HW hybrid material was collected. By adjusting the volume of K2PtCl4 solution with 10 μL (2.0% Pt-HW), 30 μL (5.6% Pt-HW), 50 μL (9.1% Pt-HW), 100 μL (16.7% Pt-HW), 200 μL (28.6% Pt-HW), 400 μL (45% Pt-HW), and the corresponding volume of AA solution, Pt-HW composites with different platinum loading were obtained.

Synthesis of M-HW Nanocomposites
The synthesis of the ZnTPyP hexagonal submicrowires (HW): HW were prepared via an acid-based neutralization surfactant encapsulation self-assembly method [39,40]. Typically, 0.5 mL of ZnTPyP (0.01 M) solution was quickly injected into 9.5 mL of an aqueous solution containing cetyltrimethylammonium bromide (CTAB) (0.01 M) and NaOH (0.02 M) and was rapidly stirred at room temperature (25 • C) for 48 h. The ZnTPyP hexagonal HW was centrifuged at 9500 rpm and washed three times with water to remove the surfactant. Then, the HW was redispersed in water with a mass concentration of 6.67 mg/mL for preparing metal-organic composites (M-HW).
The synthesis of Pt-HW composite: K 2 PtCl 4 (10 mM) solution and an equal volume of AA solution (0.1 M) were added to a 20 mL glass vial containing 10 mL of dispersed HW (0.1 mg/mL). The mixture was sonicated to ensure it was homogenized and it was then irradiated with a photocatalytic system at room temperature. All the photocatalytic reactions were irradiated using a 300 W xenon lamp equipped with a UVCUT400 filter (λ ≥ 400 nm), in which the incident light passed through a 10 cm water filter. The center of the glass vial was about 20 cm away from the light source, and the light intensity was approximately 100 mW/cm 2 . After the mixture was irradiated for 30 min, the solution changed from purple to black under visible light, indicating that the Pt metal was reduced. After the solution was centrifuged at 9500 rpm for 10 min, monodisperse Pt-HW hybrid material was collected. By adjusting the volume of K 2 PtCl 4 solution with 10 µL (2.0% Pt-HW), 30 µL (5.6% Pt-HW), 50 µL (9.1% Pt-HW), 100 µL (16.7% Pt-HW), 200 µL (28.6% Pt-HW), 400 µL (45% Pt-HW), and the corresponding volume of AA solution, Pt-HW composites with different platinum loading were obtained.
The preparation of the Au-HW composite: Au-HW composites with different Au loadings were obtained by replacing the K 2 PtCl 4 solution with 10 mM of Au(I) thiourea solution and adjusting the volume of Au(I) thiourea solution with 30 µL (5.6% Au-HW), 50 µL (9.1% Au-HW), 100 µL (16.7% Au-HW), and 200 µL (28.6% Ag-HW), and the corresponding volume of AA solution was the same to the preparation method of Pt-HW composites. Au(I) thiourea solution was freshly prepared according to a published procedure [43].

Photocatalytic Activity
The photocatalytic activity of M-HW was evaluated through the photocatalytic degradation of the organic pollutants. Precisely, 1 mg of M-HW composites (photocatalyst) was added to 40 mL of MO (20 mg/L, target dye). The mixture was stirred continuously in the dark for 30 min to obtain a homogenized mixture and achieve adsorption-desorption equilibrium. Then, the mixture was transferred to the photocatalytic reaction system and irradiated under light at a specific time, and aliquots of 4 mL of the solution were collected in 7 mL Eppendorf (Ep) tubes every 20 min, and the supernatant was removed twice using high-speed centrifugation at 9500 rpm for 10 min. The absorbance value of MO at the maximum absorption wavelength (464 nm) was measured using a visible spectrophotometer (Shanghai Prism Technology 722SP). Different target dyes, such as rhodamine B (1 × 10 −5 M, λ max = 554 nm) and eosin B (5 × 10 −5 M, λ max = 518 nm), were changed in the same condition to record the maximum absorption value. The photocatalytic activities of M-HW on different dyes were studied using the photocatalytic degradation curve.
The photocatalytic degradation curve of organic dyes can be fitted using the first-order kinetic Equation (1) as follows: where C 0 (mg/mL) and C (mg/mL) represent the initial organic dye concentration and the dye concentration after irradiation, respectively; k represents the apparent rate constants, and t represents the reaction time (min) [44]. Thus, k was used to evaluate the photocatalytic activity in this work.

Electrochemical Measurements
The electrochemical properties of the 0.1 mM ZnTPyP molecule, rhodamine B, MO, and eosin B dichloromethane solution were measured with cyclic voltammetry (CV) using the conventional three-electrode system, in which a 3.0 mm diameter glass carbon disk (0.071 cm 2 , Shanghai Chenhua) was used as the working electrode, a platinum wire was used as the counter electrode, and Ag/AgCl (silver/silver chloride) was used as the reference electrode (3.0 M KCl solution. The electrode potential was +0.22 V vs. the NHE potential, and 0.1 M of tetra-n-butylammonium hexafluorophosphate (TBAPF 6 ) was used as the electrolyte. The oxidation-reduction potential was measured through an electrochemical workstation. Based on the optical and electrochemical data, the energy levels of the HOMOs and LUMOs of the organic dyes can be estimated using Equations (2)-(4).
where E g is the energy gap and λ abs is the maximum UV-Vis absorption wavelengths value in the dichloromethane solution. E HOMO and E LUMO are the energy levels of the HOMOs and LUMOs, respectively. The standard hydrogen electrode (NHE) potential was −4.5 eV relative to the vacuum level. The CV curve test ranged from −1.6 V to 1.6 V, and the scan rate was 200 mV/s. All electrochemical tests were performed at 25 • C under N 2 saturation.

Materials Characterization
High-resolution transmission electron microscope (HRTEM) images were recorded on a JEOL JEM-2100 operating at an acceleration voltage of 200 kV. Field emission scanning electron microscopy (FESEM) images were recorded using a Nova Nano SEM 450 microscope. The UV/Vis spectra measurements of the M-HW dispersion were performed using an Agilent Technologies Cary 60. A 300 W xenon arc lamp (PLS-SXE300/300UV, Beijing Perfectlight Technology Co., Ltd., Beijing, China) installed in a laboratory lamp housing system provided with light power. The CV curves were tested using an [H] electrochemical workstation (Shanghai Chenhua Instrument Co., Ltd., Shanghai, China).

Morphology and Size Distribution of M-HW Nanocomposites
The self-assembled porphyrin networks exhibited excellent photocatalytic activity during the photodegradation of the organic pollutants, photocatalytic water splitting for hydrogen production, and the photocatalytic reduction of metal ions [45][46][47][48]. Thus, owing to the excellent photocatalytic recyclability of ZnTPyP porphyrin self-assembled HWs [49], they were used as an important template to construct organic-based SPR photocatalysts with a controllable size and spatial distribution of the metal NPs. In this study, noble metal (including Au, Ag, Pt, and Pd) nanoparticles were loaded on the surface of HW through a simple in situ photocatalytic reduction method. First, the zinc porphyrin HWs were prepared using the acid-based neutralization surfactant encapsulation the self-assembly method following the procedure of our previous report [34]. The scanning electron microscopy (SEM) image of the HWs showed that the nanostructures were well-defined one-dimensional (1D) submicrowires ( Figure 2a) with a hexagonal external profile and a narrow size distribution in both the length and diameter. The average length and the diameter of the submicrowires were 3.16 µm and 211 nm, respectively. Based on the surfactant-assisted self-assembly synthesis process of HW, a thin layer of CTAB surfactants was deposited on the surfaces of HW, resulting in the good dispersibility of the nanomaterials and the adsorption of the metal salt ions. Then, the monodisperse HWs were used for the photocatalytic reduction of K 2 PtCl 4 under irradiation of visible light in the presence of AA as an electron donor. Through the photocatalytic reaction, K 2 PtCl 4 was initially in situ reduced to form highly uniform Pt nanoparticles on the surfaces of HW. By changing the volume of the K 2 PtCl 4 solution and the corresponding volume of the AA solution, Pt-HW composites with different platinum loading were obtained. A transmission electron microscope (TEM) was used to examine the distribution of Pt nanoparticles and the change in their sizes on the surface of submicrowires with Pt loading progression under standard conditions (Figure 2b-f). The results showed that the distribution amount of Pt nanoparticles increased as the amount of feed added increased. In addition, the Pt nanoparticles with precise dimensional control were uniformly supported on the surface of the HWs, and the size was~5.7 nm by size statistics, as shown in the insert of Figure 2d. When the loading of Pt was below 23 wt%, relative to the amount of HW (Figure 2e), then the monodispersed Pt-HW nanocomposites were obtained by controlling the feed added to the K 2 PtCl 4 solution. A shell of Pt nanoparticle networks gradually formed on the surface of the photoactive porphyrin nanostructures when the Pt precursors were continuously added to the system. When the loading of Pt was greater than 50 wt%, a shell of Pt nanopar-ticle networks was formed, which is consistent with the result in the literature [39]. The shell was formed because the cationic CTAB adsorbed on the HW surface played a key role in adsorbing the negatively charged metal salt precursor, in situ photoreducted to the zero-valent metal, which then contributed to the uniform distribution of the metal particles. Such uniformly distributed metal particles enhanced the plasmon resonance and interaction between the electrons, thus contributing to the catalytic or chemical properties of the organic functional nanostructures.
ticles increased as the amount of feed added increased. In addition, the Pt nanoparticles with precise dimensional control were uniformly supported on the surface of the HWs, and the size was ~5.7 nm by size statistics, as shown in the insert of Figure 2d. When the loading of Pt was below 23 wt%, relative to the amount of HW (Figure 2e), then the monodispersed Pt-HW nanocomposites were obtained by controlling the feed added to the K2PtCl4 solution. A shell of Pt nanoparticle networks gradually formed on the surface of the photoactive porphyrin nanostructures when the Pt precursors were continuously added to the system. When the loading of Pt was greater than 50 wt%, a shell of Pt nanoparticle networks was formed, which is consistent with the result in the literature [39]. The shell was formed because the cationic CTAB adsorbed on the HW surface played a key role in adsorbing the negatively charged metal salt precursor, in situ photoreducted to the zero-valent metal, which then contributed to the uniform distribution of the metal particles. Such uniformly distributed metal particles enhanced the plasmon resonance and interaction between the electrons, thus contributing to the catalytic or chemical properties of the organic functional nanostructures. In the same way, other noble metal nanoparticles (Ag, Au, and Pd) were successfully deposited on the surface of HW (Figure 3). Ag-HW composites were synthesized by replacing the K2PtCl4 solution with silver (I) thiosulfate solution (Figure 3a-d). The Ag nanoparticles were in situ reduced and supported on the surface of HW, and the sizes of the Ag nanoparticles were ~3.9 nm (Figure 3b) by size statistics. The loading amounts of different metals were adjusted by regulating the feeding amount of the metal salt precursor. However, Au and Pd NPs did not have such a feature because the strong Ostwald In the same way, other noble metal nanoparticles (Ag, Au, and Pd) were successfully deposited on the surface of HW (Figure 3). Ag-HW composites were synthesized by replacing the K 2 PtCl 4 solution with silver (I) thiosulfate solution (Figure 3a-d). The Ag nanoparticles were in situ reduced and supported on the surface of HW, and the sizes of the Ag nanoparticles were~3.9 nm (Figure 3b) by size statistics. The loading amounts of different metals were adjusted by regulating the feeding amount of the metal salt precursor. However, Au and Pd NPs did not have such a feature because the strong Ostwald ripening effect facilitated the reduced metal particles to agglomerate during the metal salt precursor reduction process and exposed the HW surfaces [50], which might be related to the growth rate of the crystal faces of various metals and the surface energy. The Au-HW composite materials were shown in Figure 3e. The Au nanoparticles were uniformly supported on the surface of HW, and the Au particle size was~15 nm by the size statistics. The Pd particle size of the Pd-HW composite was~20 nm by the size statistics (Figure 3f). ripening effect facilitated the reduced metal particles to agglomerate during the metal salt precursor reduction process and exposed the HW surfaces [50], which might be related to the growth rate of the crystal faces of various metals and the surface energy. The Au-HW composite materials were shown in Figure 3e. The Au nanoparticles were uniformly supported on the surface of HW, and the Au particle size was ~15 nm by the size statistics. The Pd particle size of the Pd-HW composite was ~20 nm by the size statistics (Figure 3f).

UV-Vis Absorption of M-HW Nanocomposites
The self-assembled porphyrin nanostructures exhibited a strong photoelectrochemical response in the visible light region (300-800 nm) owing to couple interactions and their ordered self-assembly arrays of porphyrin molecules through noncovalent interactions [51]. The UV-Visible absorption spectra of the resulting Pt-HW nanocomposites were shown in Figure 4a. The absorption of the porphyrin HWs had the Soret band at 420 nm and 477 nm, and the Q-band at 578 nm and 617 nm. The Pt-HW nanocomposites retained the absorption of the Soret band and the Q-band of HW. Moreover, the absorption intensity at 477 nm increased with the increase in the Pt loading amount. When the loading amount of Pt was 0.1 mg, the enhanced absorption reached the maximum value. Then, the absorption intensity gradually decreased, indicating that the excess Pt gradually covered the porphyrin HWs and blocked the surface absorption, suggesting that the Pt particles were evenly distributed on the surface of porphyrin HWs rather than agglomerated into large particles during the Pt reduction process. However, other precious metals, including Ag, Au, and Pd, did not have such features because the strong Ostwald ripening effect leaded to the reduced metal particles agglomerations into large particles on the surface of HW. The absorption intensity gradually decreased with the loading amount of Ag

UV-Vis Absorption of M-HW Nanocomposites
The self-assembled porphyrin nanostructures exhibited a strong photoelectrochemical response in the visible light region (300-800 nm) owing to couple interactions and their ordered self-assembly arrays of porphyrin molecules through noncovalent interactions [51]. The UV-Visible absorption spectra of the resulting Pt-HW nanocomposites were shown in Figure 4a. The absorption of the porphyrin HWs had the Soret band at 420 nm and 477 nm, and the Q-band at 578 nm and 617 nm. The Pt-HW nanocomposites retained the absorption of the Soret band and the Q-band of HW. Moreover, the absorption intensity at 477 nm increased with the increase in the Pt loading amount. When the loading amount of Pt was 0.1 mg, the enhanced absorption reached the maximum value. Then, the absorption intensity gradually decreased, indicating that the excess Pt gradually covered the porphyrin HWs and blocked the surface absorption, suggesting that the Pt particles were evenly distributed on the surface of porphyrin HWs rather than agglomerated into large particles during the Pt reduction process. However, other precious metals, including Ag, Au, and Pd, did not have such features because the strong Ostwald ripening effect leaded to the reduced metal particles agglomerations into large particles on the surface of HW. The absorption intensity gradually decreased with the loading amount of Ag NPs (Figure 4b). The reaction solution of Pt-HW initially appeared to be purple under incandescent light due to light scattering by the porphyrin nanostructures. As the loading amount of Pt NPs increased, the dispersion of the Pt-HW nanomaterial gradually turned black (Figure 4c). Thus, the in situ photocatalytic synthesis method of SPR-based metal semiconductors M-HW is a promising photovoltaic technology aiming to emulate natural light harvesting processes and the energy storage. NPs (Figure 4b). The reaction solution of Pt-HW initially appeared to be purple under incandescent light due to light scattering by the porphyrin nanostructures. As the loading amount of Pt NPs increased, the dispersion of the Pt-HW nanomaterial gradually turned black (Figure 4c). Thus, the in situ photocatalytic synthesis method of SPR-based metal semiconductors M-HW is a promising photovoltaic technology aiming to emulate natural light harvesting processes and the energy storage.

Pt-HW Nanocomposites Photodegradation of Different Dyes
Uniformly distributed SPR metal particle semiconductors (M-HW) enhanced the catalytic or chemical properties of the organic functional nanostructures, such as the visible light photocatalytic degradation of the organic pollutants. The Pt-HW nanocomposites were used to photodegrade different organic pollutants, including MO, rhodamine B (RhB), and eosin B. A series of degradation curves with different Pt loadings on different organic substrates were obtained ( Figure 5). Several interesting catalytic features were observed: (1) when 0.1 mg of Pt was loaded on the surface of 1 mg of HW, the photocatalytic degradation performance of MO of 9.1% Pt-HW was three times that of HW (Figure 5a).
(2) The photocatalytic performance gradually increased with increasing the Pt loading and became a plateau at 9.1 wt% Pt. However, excessive Pt loading hindered the absorption and the light irradiation, thus decreasing the catalytic effects of the photocatalysts (Figure 5b). (3) Then, the photocatalytic performances of Pt-HW were evaluated by degrading rhodamine B, and the photocatalytic degrading rate of RhB of 9.1% Pt-HW was improved by four times that of HW (Figure 5c). The absorbance of RhB almost declined to 0 after 2 h, indicating the high photocatalytic activity of the photocatalyst (Figure 5d). (4) The photocatalytic performance of degrading eosin B was improved by 2.6 times that of HW (Figure 5e). (5) Figure 5f compares the photodegradation activity of different dyes of the prepared samples. Pt-HW (9.1 wt%) exhibited an enhanced photocatalytic activity compared with HW and exhibited the substrates-dependent photocatalytic activity of different dyes. We attempted to correlate the relationship between Pt-HW and different

Pt-HW Nanocomposites Photodegradation of Different Dyes
Uniformly distributed SPR metal particle semiconductors (M-HW) enhanced the catalytic or chemical properties of the organic functional nanostructures, such as the visible light photocatalytic degradation of the organic pollutants. The Pt-HW nanocomposites were used to photodegrade different organic pollutants, including MO, rhodamine B (RhB), and eosin B. A series of degradation curves with different Pt loadings on different organic substrates were obtained ( Figure 5). Several interesting catalytic features were observed: (1) when 0.1 mg of Pt was loaded on the surface of 1 mg of HW, the photocatalytic degradation performance of MO of 9.1% Pt-HW was three times that of HW (Figure 5a). (2) The photocatalytic performance gradually increased with increasing the Pt loading and became a plateau at 9.1 wt% Pt. However, excessive Pt loading hindered the absorption and the light irradiation, thus decreasing the catalytic effects of the photocatalysts (Figure 5b). (3) Then, the photocatalytic performances of Pt-HW were evaluated by degrading rhodamine B, and the photocatalytic degrading rate of RhB of 9.1% Pt-HW was improved by four times that of HW (Figure 5c). The absorbance of RhB almost declined to 0 after 2 h, indicating the high photocatalytic activity of the photocatalyst (Figure 5d). (4) The photocatalytic performance of degrading eosin B was improved by 2.6 times that of HW (Figure 5e). (5) Figure 5f compares the photodegradation activity of different dyes of the prepared samples. Pt-HW (9.1 wt%) exhibited an enhanced photocatalytic activity compared with HW and exhibited the substrates-dependent photocatalytic activity of different dyes. We attempted to correlate the relationship between Pt-HW and different substrates to study the cocatalyst pairs of metal particles in the porphyrin assemblies to provide additional surface sites, enhance the probability of photogenerated charge transport separation in the photocatalytic process, and improve the effect of the interface charge-transfer efficiency because of the SPR effect. substrates to study the cocatalyst pairs of metal particles in the porphyrin assemblies to provide additional surface sites, enhance the probability of photogenerated charge transport separation in the photocatalytic process, and improve the effect of the interface charge-transfer efficiency because of the SPR effect.  The experimental results showed that the higher the HOMO orbit energy, the easier it loses electrons [52][53][54]. Porphyrins are a class of organic complexes with unique macrocyclic conjugated structures. ZnTPyP molecules had higher HOMO orbital energy levels than the dye molecules ( Figure 6 and Table 1). The ZnTPyP molecules in HW were more likely to lose electrons and create photogenerated holes under UV-Vis light radiation. The holes had strong oxidizing effects and captured the electrons of the dye molecules in the excited state. The excitation electrons of the HW combined with oxygen to produce superoxide radicals, which evolved into hydroxyl radicals, further leading to the degradation of the dyes [55]. The different oxidation potentials of the organic dyes and the complexity of the molecular structures led to different enhancement effects of the same catalyst on different dyes. Nanomaterials 2023, 13, x FOR PEER REVIEW 10 of 17 The experimental results showed that the higher the HOMO orbit energy, the easier it loses electrons [52][53][54]. Porphyrins are a class of organic complexes with unique macrocyclic conjugated structures. ZnTPyP molecules had higher HOMO orbital energy levels than the dye molecules ( Figure 6 and Table 1). The ZnTPyP molecules in HW were more likely to lose electrons and create photogenerated holes under UV-Vis light radiation. The holes had strong oxidizing effects and captured the electrons of the dye molecules in the excited state. The excitation electrons of the HW combined with oxygen to produce superoxide radicals, which evolved into hydroxyl radicals, further leading to the degradation of the dyes [55]. The different oxidation potentials of the organic dyes and the complexity of the molecular structures led to different enhancement effects of the same catalyst on different dyes.

M-HW (M = Ag, Au, and Pd) Effects on the Enhancement of Photodegradation
The photocatalytic degradation curves of Ag-HW (Figure 7a), Au-HW, and Pd-HW (Figure 7b) nanocomposites were obtained. The first order kinetics of the visible light photocatalytic degradation curve of MO (Figure 7c) using different nanocomposites, namely Ag-HW, Au-HW, and Pd-HW, of the same metal loading were performed using Equation (1). Under the same SPR metal loading (0.1 mg), the photocatalytic performance of Ag-HW toward MO degradation was the best among the nanocomposites. The photocatalytic performance of kAg-HW (0.043 min −1 ) increased by three times that of HW, followed by kPt-HW (0.0417 min −1 ) > kAu-HW (0.0312 min −1 ) > kPd-HW(0.0198 min −1 ) > kHW (0.014 min −1 ), suggesting that the M-HW degradation efficiency was higher than that of HW (Figure 7d). These results showed that M-HW exhibits a good enhancement effect. The result of kAg-HW and kPt-HW were 24% and 20% higher than that of knanodisc (0.0347 min −1 ), respectively.

M-HW (M = Ag, Au, and Pd) Effects on the Enhancement of Photodegradation
The photocatalytic degradation curves of Ag-HW (Figure 7a), Au-HW, and Pd-HW (Figure 7b) nanocomposites were obtained. The first order kinetics of the visible light photocatalytic degradation curve of MO (Figure 7c) using different nanocomposites, namely Ag-HW, Au-HW, and Pd-HW, of the same metal loading were performed using Equation (1). Under the same SPR metal loading (0.1 mg), the photocatalytic performance of Ag-HW toward MO degradation was the best among the nanocomposites. The photocatalytic performance of k Ag-HW (0.043 min −1 ) increased by three times that of HW, followed by k Pt-HW (0.0417 min −1 ) > k Au-HW (0.0312 min −1 ) > k Pd-HW (0.0198 min −1 ) > k HW (0.014 min −1 ), suggesting that the M-HW degradation efficiency was higher than that of HW (Figure 7d). These results showed that M-HW exhibits a good enhancement effect. The result of k Ag-HW and k Pt-HW were 24% and 20% higher than that of k nanodisc (0.0347 min −1 ), respectively. The above experimental results showed that the Ag-HW nanocomposite had the best photocatalytic degradation performance among the other composites. On the one hand, the surface plasma enhancement effect of Ag enhanced the separation of the charge. On the other hand, a small amount of the Ag2S/Ag heterojunction was formed after the photoreduction process of silver-(I) thiosulfate used as a precursor [56]. We further detected the hydroxyl radicals (·OH) and singlet oxygen ( 1 O2) yield of the prepared samples under light irradiation. After Pt NPs were loaded on HW, the productions of ·OH ( Figure 7e) and 1 O2 (Figure 7f) using Pt-HW were almost twice of using HW, which further confirmed the excellent catalytic activity of the SPR photocatalysts.

Photocatalytic Degradation Analysis
The large π-electron conjugated systems and close packing between zinc porphyrin molecules endowed them with long-wave absorption, the low energy level of the molecules, and the charge transfer between the molecules. The HW photodegradation of the organic dyes underwent three steps ( Figure 8): first, the zinc porphyrin molecule was irradiated under visible light, the electrons in the HOMO orbital of HW were excited and transferred to the LUMO orbital, and the electrons in the LUMO orbital combined with the oxygen in the air to generate superoxide radicals, which in turn evolved into hydroxyl radicals and further degraded the dye. However, the holes had oxidizing properties to despoil the electrons of the dye molecule, resulting in the continuous oxidization and decomposition of the dye molecules. The different oxidation potentials of the organic dyes and the complexity of the molecular structure enhanced the catalytic effect of the catalyst on different dyes. When certain amounts of precious metals (including Ag, Au, Pt, and Pd) were loaded on the surface of HW, the M-HW photodegradation of organic dyes underwent three steps (Figure 8). The improved efficiency of the visible light photocatalytic degradation of the organic dyes could be attributed to the following reasons: (1) these precious metal nanoparticles had SPR in the visible light region, which enhanced the light The above experimental results showed that the Ag-HW nanocomposite had the best photocatalytic degradation performance among the other composites. On the one hand, the surface plasma enhancement effect of Ag enhanced the separation of the charge. On the other hand, a small amount of the Ag 2 S/Ag heterojunction was formed after the photoreduction process of silver-(I) thiosulfate used as a precursor [56]. We further detected the hydroxyl radicals (·OH) and singlet oxygen ( 1 O 2 ) yield of the prepared samples under light irradiation. After Pt NPs were loaded on HW, the productions of ·OH ( Figure 7e) and 1 O 2 (Figure 7f) using Pt-HW were almost twice of using HW, which further confirmed the excellent catalytic activity of the SPR photocatalysts.

Photocatalytic Degradation Analysis
The large π-electron conjugated systems and close packing between zinc porphyrin molecules endowed them with long-wave absorption, the low energy level of the molecules, and the charge transfer between the molecules. The HW photodegradation of the organic dyes underwent three steps ( Figure 8): first, the zinc porphyrin molecule was irradiated under visible light, the electrons in the HOMO orbital of HW were excited and transferred to the LUMO orbital, and the electrons in the LUMO orbital combined with the oxygen in the air to generate superoxide radicals, which in turn evolved into hydroxyl radicals and further degraded the dye. However, the holes had oxidizing properties to despoil the electrons of the dye molecule, resulting in the continuous oxidization and decomposition of the dye molecules. The different oxidation potentials of the organic dyes and the complexity of the molecular structure enhanced the catalytic effect of the catalyst on different dyes. When certain amounts of precious metals (including Ag, Au, Pt, and Pd) were loaded on the surface of HW, the M-HW photodegradation of organic dyes underwent three steps (Figure 8). The improved efficiency of the visible light photocatalytic degradation of the organic dyes could be attributed to the following reasons: (1) these precious metal nanoparticles had SPR in the visible light region, which enhanced the light absorption of the porphyrin organic functional nanostructures, improved the energy conversion efficiency, and resulted in a good photostability, and (2) the electron interactions between precious metals nanoparticles and organic functional nanomaterials formed a higher Schottky barrier, which could effectively prevent the recombination of the photogenerated electrons and holes, and change the transmission route of the photogenerated electrons, thereby promoting the interface electrons. The charge transfer process enhanced the photocatalytic activity of the porphyrin self-assemblies [57][58][59][60]. (3) The work functions of Ag, Au, Pd, and Pt were 4.26, 5.1, 5.12, and 5.65 eV, respectively; that is, the Schottky barrier height after the HW was loaded with different metals (Ag < Au< Pd < Pt), which was responsible for the differences in the photocatalytic performance. However, the catalytic properties of the experiment did not correspond with these results due to the size of the metal particles, and the Pt and Ag nanoparticles were smaller in size, thus exhibiting better photocatalytic properties. This result showed that a substantial part of the electrons from the LUMO of HW was injected into the M NPs through the SPR excitation, which significantly enhanced the photogenerated charge transport separation and retarded the charge recombination during the photocatalytic process, thereby improving the visible light photocatalytic activity for the degradation of the organic pollutants. This result showed that the SPR metals provided an additional active site that enhanced the photogenerated charge transport separation during the photocatalytic process and improved the transfer efficiency of the interface charge. These findings provide an important reference into the application of organic-based SPR photocatalysis. absorption of the porphyrin organic functional nanostructures, improved the energy conversion efficiency, and resulted in a good photostability, and (2) the electron interactions between precious metals nanoparticles and organic functional nanomaterials formed a higher Schottky barrier, which could effectively prevent the recombination of the photogenerated electrons and holes, and change the transmission route of the photogenerated electrons, thereby promoting the interface electrons. The charge transfer process enhanced the photocatalytic activity of the porphyrin self-assemblies [57][58][59][60]. (3) The work functions of Ag, Au, Pd, and Pt were 4.26, 5.1, 5.12, and 5.65 eV, respectively; that is, the Schottky barrier height after the HW was loaded with different metals (Ag < Au< Pd < Pt), which was responsible for the differences in the photocatalytic performance. However, the catalytic properties of the experiment did not correspond with these results due to the size of the metal particles, and the Pt and Ag nanoparticles were smaller in size, thus exhibiting better photocatalytic properties. This result showed that a substantial part of the electrons from the LUMO of HW was injected into the M NPs through the SPR excitation, which significantly enhanced the photogenerated charge transport separation and retarded the charge recombination during the photocatalytic process, thereby improving the visible light photocatalytic activity for the degradation of the organic pollutants. This result showed that the SPR metals provided an additional active site that enhanced the photogenerated charge transport separation during the photocatalytic process and improved the transfer efficiency of the interface charge. These findings provide an important reference into the application of organic-based SPR photocatalysis. Figure 8. The charge-transfer process and mechanism of enhancing the photocatalytic performance. Figure 8. The charge-transfer process and mechanism of enhancing the photocatalytic performance.

Conclusions
In summary, we successfully modified noble metal nanoparticles (Au, Ag, Pt, and Pd) on the surface of ZnTPyP HWs (M-HW) using an in situ photocatalytic method. The prepared M-HW nanocomposites photocatalysts were used to photodegrade different organic pollutants, and the results showed the photocatalytic degradation constant of k Ag-HW (0.043 min −1 ) was the highest, followed by k Pt-HW (0.0417 min −1 ) > k Au-HW (0.0312 min −1 ) > k Pd-HW (0.0198 min −1 ) > k HW (0.014 min −1 ) under the same loading conditions (0.1 mg). The degradation efficiency of M-HW was superior to that of nanodisc, indicating that M-HW had the best photocatalytic degradation activity. The result of k Ag-HW and k Pt-HW was 24% and 20% higher than that of k nanodisc (0.0347 min −1 ), respectively. These precious metal nanoparticles had an SPR in the visible light region, which enhanced the visible light absorption of porphyrin self-assemblies. The special base barrier enhanced the separation of the photogenerated charge during the photocatalytic process and improved the interface charge-transfer efficiency, thereby enhancing the photocatalytic activity of the porphyrin self-assemblies. As a novel technology, surface plasmon was first applied to porphyrin self-assemblies, which increased their light absorption and improved the energy conversion efficiency without changing the organic nanostructure. In addition, it has a unique advantage, making it a promising technology for preparing self-assembled nanostructures for photovoltaic and energy storage devices.