Metal-Ion Intercalation Mechanisms in Vanadium Pentoxide and Its New Perspectives

The investigation into intercalation mechanisms in vanadium pentoxide has garnered significant attention within the realm of research, primarily propelled by its remarkable theoretical capacity for energy storage. This comprehensive review delves into the latest advancements that have enriched our understanding of these intricate mechanisms. Notwithstanding its exceptional storage capacity, the compound grapples with challenges arising from inherent structural instability. Researchers are actively exploring avenues for improving electrodes, with a focus on innovative structures and the meticulous fine-tuning of particle properties. Within the scope of this review, we engage in a detailed discussion on the mechanistic intricacies involved in ion intercalation within the framework of vanadium pentoxide. Additionally, we explore recent breakthroughs in understanding its intercalation properties, aiming to refine the material’s structure and morphology. These refinements are anticipated to pave the way for significantly enhanced performance in various energy storage applications.


Introduction
Vanadium pentoxide (V 2 O 5 ) features a layered crystal structure, consisting of vanadium oxide layers separated by intercalation sites [1] (Figure 1).VO 5 pyramids exhibit a remarkable degree of flexibility compared to other polyhedral structures, enabling more efficient support for reversible intercalation.In the case of orthorhombic V 2 O 5 , it demonstrates the capability to absorb water from both atmospheric conditions and solutions, resulting in the formation of V 2 O 5 •nH 2 O [2,3].Notably, some of this water can be intercalated between the bilayers of V 2 O 5 .The absorbed water molecules manifest as neutral molecules (H 2 O) or oxonium cations (H 3 O + ) due to the inherent acidity of V 5+ ions.The presence of protons is often associated with acidic conditions (i.e., in acid-base equilibrium, protons may be involved in the transfer of H + ), contributing to the negative charge within the V 2 O 5 m− with organic solvents in nonaqueous electrolytes and the exchange of oxonium cations with outer cations (Li + , Mg 2+ , Al 3+ , etc.) in the electrolyte solution.Notably, the deintercalation of protons may coincide with the intercalation of other cations in battery applications, as highlighted in a study by González et al. [4].The cationic exchange between vanadium oxide and the solution is particularly pronounced in amorphous or poorly crystallized vanadium oxides.
The layered structure of V 2 O 5 facilitates the intercalation of various ions, including lithium and sodium [5][6][7], rendering vanadium oxide a viable choice as an electrode active material in lithium-ion batteries (LIBs).The success of LIBs as widely used power sources for portable electronic devices stems from their impressive energy density, allowing them to store a substantial amount of energy within a compact and lightweight structure.LIBs boast a low self-discharge rate, ensuring a prolonged retention of charge during periods of inactivity, thereby enhancing the reliability of electronic devices.Moreover, their extended cycle life contributes to long-term economic advantages.Beyond lithium, other elements such as sodium and magnesium, which are more abundant, pave the way for the emergence of "post-lithium batteries", presenting potential competitiveness against LIBs in terms of cost and sustainability.
Nanomaterials 2023, 13, x FOR PEER REVIEW 2 of 29 the V2O5 m− layers.This material serves as a protonic conductor, allowing for the exchange of water with organic solvents in nonaqueous electrolytes and the exchange of oxonium cations with outer cations (Li + , Mg 2+ , Al 3+ , etc.) in the electrolyte solution.Notably, the deintercalation of protons may coincide with the intercalation of other cations in battery applications, as highlighted in a study by González et al. [4].The cationic exchange between vanadium oxide and the solution is particularly pronounced in amorphous or poorly crystallized vanadium oxides.The layered structure of V2O5 facilitates the intercalation of various ions, including lithium and sodium [5][6][7], rendering vanadium oxide a viable choice as an electrode active material in lithium-ion batteries (LIBs).The success of LIBs as widely used power sources for portable electronic devices stems from their impressive energy density, allowing them to store a substantial amount of energy within a compact and lightweight structure.LIBs boast a low self-discharge rate, ensuring a prolonged retention of charge during periods of inactivity, thereby enhancing the reliability of electronic devices.Moreover, their extended cycle life contributes to long-term economic advantages.Beyond lithium, other elements such as sodium and magnesium, which are more abundant, pave the way for the emergence of "post-lithium batteries", presenting potential competitiveness against LIBs in terms of cost and sustainability.Vanadium pentoxide, known for its ease of fabrication, has sparked considerable interest in intercalation reactions, particularly within the realm of LIBs.Recently, there has been a growing consideration of post-lithium batteries, which could potentially rival lithium-based systems in terms of the natural abundance of elements, sustainability, and costeffectiveness.The wealth of experience accumulated in the field of LIBs offers valuable insights that could pave the way for the development of innovative post-lithium battery technologies.This review aims to thoroughly investigate the application of V2O5 in batteries.The exploration begins by reviewing the methods of synthesis, and then examining the intercalation of both univalent and multivalent ions.The discussion finally delves into pivotal strategies designed to further enhance battery electrochemistry through its utilization.

Synthetic Methods
The morphological characteristics of electrode materials are significantly influenced by the chosen preparative routes, creating a notable impact on the nature of the electrodeelectrolyte interphase and, consequently, the accessibility of insertion ions.It is paramount to carefully consider the selection of synthetic methods to obtain a balance between performance, cost, and environmental impact.This section aims to present some of the pertinent synthetic methods documented in the literature, underscoring the importance of each approach in achieving materials with optimized performance and balanced environmental considerations.Vanadium pentoxide, known for its ease of fabrication, has sparked considerable interest in intercalation reactions, particularly within the realm of LIBs.Recently, there has been a growing consideration of post-lithium batteries, which could potentially rival lithium-based systems in terms of the natural abundance of elements, sustainability, and cost-effectiveness.The wealth of experience accumulated in the field of LIBs offers valuable insights that could pave the way for the development of innovative post-lithium battery technologies.This review aims to thoroughly investigate the application of V 2 O 5 in batteries.The exploration begins by reviewing the methods of synthesis, and then examining the intercalation of both univalent and multivalent ions.The discussion finally delves into pivotal strategies designed to further enhance battery electrochemistry through its utilization.

Synthetic Methods
The morphological characteristics of electrode materials are significantly influenced by the chosen preparative routes, creating a notable impact on the nature of the electrode-electrolyte interphase and, consequently, the accessibility of insertion ions.It is paramount to carefully consider the selection of synthetic methods to obtain a balance between performance, cost, and environmental impact.This section aims to present some of the pertinent synthetic methods documented in the literature, underscoring the importance of each approach in achieving materials with optimized performance and balanced environmental considerations.

Sol-Gel
This method relies on dissolving chemical reagents to guarantee a comprehensive blending of elements.Frequently, soluble salts of the composing elements are dissolved in aqueous media, such as sodium vanadate and ammonium vanadate (NH 4 VO 3 ), although vanadium alkoxides (e.g., vanadyl acetylacetonate) have been also often employed.To circumvent the selective precipitation of insoluble salts with varying compositions, a chelating agent is introduced before evaporating the solvent, such as an alkoxy ligand (e.g., triisopropoxide and butoxyacetylacetonate).This process results in the creation of a stable and uniform gel, ensuring a homogeneous mixture of elements at the atomic level.The intimate blending of these composing elements facilitates the production of highly crystalline samples characterized by a uniform particle distribution and nanometric size, even at low synthesis temperatures and short heating times [9].
During the last few decades, many gel products of V 2 O 5 such as hydrogels, xerogels, aerogels, bronzes, and other oxides have been prepared by this method [10].

Hydrothermal Process
The hydrothermal process relies on the effects of high temperature and pressure to create an environment where the solvent, typically water, can dissolve reagents that are otherwise scarcely soluble.This facilitates the reaction process and leads to the precipitation of the desired product.Notably, this technique generally produces products that are highly pure and crystalline, with a straightforward operational procedure.However, it is important to acknowledge that the reaction yield tends to be low, potentially impacting its eventual industrial applicability.
To enhance the material's crystallinity and consequently improve the electrochemical performance, a subsequent thermal treatment can be applied.The strategic use of appropriate surfactants can guide crystal growth in specific directions, enabling the preparation of samples with a controlled size and shape [11].For instance, V 2 O 5 nanotubes can be synthesized at 180 • C for 7 days with the addition of PEO as a surfactant [12].The study's findings indicated that these nanorod assemblies exhibit a lower specific capacity at initial stages but demonstrate superior cyclability compared to dispersed V 2 O 5 nanotubes.

Spray-Drying
The spray-drying process aims to produce finely powdered granular products.This involves atomizing the precursor's solution into suspended droplets, resulting in the formation of globular powders after rapid solvent evaporation in a hot gas stream.The maintenance of negative pressure in the drying room ensures the creation of pure products, while preventing the dispersion of airborne dust.
Lin et al. conducted the synthesis of V 2 O 5 using ultrasonic spray pyrolysis at varying temperatures [13].At 500 • C, they successfully produced spherical and densely nanostructured V 2 O 5 particles, while observing a significant change in morphology as the synthesis temperature increased to 700 • C. The spherical V 2 O 5 underwent testing, revealing an initial discharge capacity of approximately 403 mAh g −1 .However, issues with retention arose due to inherent phase changes occurring at low voltages.Notably, adjusting the voltage limit from 1.5 to 2.0 V resulted in improved cycle performance for the V 2 O 5 cathode.On a similar note, Ng et al. employed a one-step and scalable flame spray pyrolysis process to prepare V 2 O 5 nanoparticles ranging from 30 to 60 nm [14].Through careful optimization of the processing conditions, such as the precursor concentration and injection rate, they achieved particles with the lowest specific surface area and highest phase purity.This material demonstrated remarkable performance, retaining 110 mAh g −1 after 100 cycles at 100 mA g −1 .Moreover, it exhibited a superior specific charge, reaching 100 mAh g −1 at 2000 mA g −1 .Recent studies further corroborated that this method can be very convenient for the preparation of vanadium pentoxide electrodes [15].

Electrospinning
The electrospinning method involves a precursor solution within a capillary.To overcome surface tension and serve as a structural directing template for fiber formation, a polymer is introduced.Once the electrostatic field applied between the capillary and the receiving surface surpasses the surface tension of the droplet, a fine jet of precursor is ejected.Following solvent evaporation and solidification in the air, nanofibers are meticulously formed and collected.Despite being a straightforward and adaptable approach for crafting nanomaterials, the ultimate product's characteristics are contingent upon specific attributes of the precursor solution.Factors such as the molecular weight of chemical reagents, stirring speed and duration, as well as environmental temperature and moisture play pivotal roles in determining the final outcome [16].Common vanadium precursors are vanadium isopropoxide, vanadyl acetylacetonate, ammonium metavanadate, and V 2 O 5 powder, while the polymers include poly(vinyl acetate), poly(methylmethacrylate), and poly(vinyl alcohol) [17].Nevertheless, concerning issues such as low efficiency and the complexity of numerous process parameters along with the production of small material quantities pose a hurdle to achieving a widespread industrial applicability.
Both V 2 O 5 fibers [18] and composite V 2 O 5 /C fibers [19] can be prepared.Initial investigations into the synthesis of V 2 O 5 revealed that the morphology of the fibers could be precisely tailored by adjusting the annealing temperature.Furthermore, by adeptly controlling the parameters during calcination, the prospect of crafting V 2 O 3 and VO 2 nanofibers becomes a feasible consideration [18].The fibers consisted of linked V 2 O 5 particles.Tolosa et al. used a multi-step procedure including sol−gel synthesis, followed by electrospinning and controlled thermal treatment to prepare hybrid fibers composed of V 2 O 5 and VO 2 engulfed in conductive carbon.The former V 2 O 5 /C presented a high specific capacity of 316 mAh g −1 , though the rate handling was less favorable [19].

Electrochemical Deposition
Electrochemical deposition relies on the reaction occurring at the surface of the electrode in an electrolytic cell.This process involves the application of a current, prompting the precipitation of insoluble products that coalesce into thin films.Achieving an optimal thin-film quality hinges on carefully managing factors such as the electrolyte concentration, pH, current density, cell potential, deposition time, and temperature [20][21][22].
Tepavcevic et al. reported nanostructured bilayered V 2 O 5 prepared by the electrochemical deposition of 0.1 M VOSO 4 aqueous solution on pure Ni foil, followed by vacuum annealing at 120 • C [23].Sodium insertion involved the appearance of both long-and short-range order.Nevertheless, sodium extraction induced the loss of long-range order, whereas short-range order was preserved.This cathode material performed 250 mAh g −1 and a power density of 1200 W kg −1 .

Template
This preparative method employs a template substance, with options including both hard and soft templates.Hard templates feature precisely defined void spaces, often comprised of channels, pores, or interconnected hollow areas.On the other hand, soft templates typically involve polymers and organic surfactants.In a standard synthesis process, the templating substance is blended or impregnated with the liquid precursor, leading to the formation of the solid product after a chemical reaction.Subsequently, the template must be removed to complete the process.
The wide array of structural and morphological possibilities inherent in various template precursors enables the creation of a diverse range of nanostructured electrode materials, encompassing one-dimensional nanowires or nanotubes, two-dimensional films, and three-dimensional interconnected porous architectures.Electrode materials crafted through this method typically showcase advantageous morphological traits, such as reduced particle size, expansive surface area, and robust structural integrity.These properties facilitate swift charge transfer and foster an optimal electrode-electrolyte interphase, playing a pivotal role in achieving superior electrochemical performance [24].
In the initial findings, hexadecylamine emerged as a soft template in structurally guiding the creation of vanadium oxide nanotubes, resulting in an impressive specific capacity of up to 180 mAh g −1 .However, it is worth noting that the authors observed a gradual decrease in charge over successive cycles, attributed to a decline in electroactivity [25].Recently, Youn et al. reported (1D) nanostructured VO 2 (B) and V 2 O 5 •nH 2 O single-crystalline nanobelts prepared with cellulose nanocrystals (CNCs) as templating material.These nanobelts exhibited a high specific capacity (>300 mAh g −1 ) and long lifespan (>244 mAh g −1 at 50 cycles) [26].

Intercalation in Battery Electrode
The intercalation sites within V 2 O 5 act as open spaces where lithium ions can insert themselves between the layers.During the charging process, these intercalation sites undergo reduction as lithium ions are inserted, causing the reduction from V 5+ to V 4+ , or even V 3+ .As the lithium ions' intercalation increases into the V 2 O 5 cathode, the crystal structure of V 2 O 5 expands to accommodate the inserted lithium ions.The resulting compound is typically represented as Li x V 2 O 5 , where "x" is the variable number of lithium ions that has been intercalated into the structure [27].Depending on the extent of Li-ion intercalation (x), the structural evolution of orthorhombic V 2 O 5 can undergo various phase transitions, leading to the formation of α-, ε-, δ-, and ω-phases.Figure 2 [28] indicates the crystal structures of various phases in V 2 O 5 .It is indicated that lithiation-induced volume expansion from α-V 2 O 5 to δ-Li x V 2 O 5 is near 11% [19].The method of cyclic voltammetry (CV) is convincing to characterize the insertion number of the Li x V 2 O 5 phases (Figure 2) [29].In that perspective, the phase transitions are reflected in three distinct potentials at about 3.4 (Li 0.5 V 2 O 5 ), 3.2 (LiV 2 O 5 ), and 2.3 V (Li 2 V 2 O 5 ) that correspond to α/ε, ε/δ, and δ/γ, respectively [19], with the following consecutive reactions [29] taking place: The α-phase is present in Li x V 2 O 5 when x < 0.1, while the ε-phase is observed within the range 0.35 < x < 0.7, resulting in a weak puckering of V 2 O 5 [30,31].When x is between 0.7 and 1, the δ-phase appears with a higher degree of puckering in the V 2 O 5 layers [23].Beyond x = 1, an irreversible transformation occurs to the γ-phase.The γ-phase can be reversibly cycled in the range 0 ≤ x ≤ 2 corresponding to theoretical capacity of 294 mAh g −1 [23].Further intercalation of a third lithium ion results in the formation of the ω-phase, which has a tetragonal structure with lattice parameters of a = 4.1 Å and c = 9.2 [19].
During discharging, lithium ions begin to deintercalate from the cathode and move back into the anode and the lithium-ion electrolyte, involving the oxidation of V 4+ or V 3+ back to V 5+ .In Li x V 2 O 5 with x ≤ 1, the formation of the α, ε, and δ phases is observed.The orthorhombic α-, ε-, and δ-phases consist of [VO 5 ] square pyramids and exhibit significant puckering [32], while the γ-phase is irreversible and metastable (γ/γ'), transforming completely upon discharging.The ω-phase indicates irreversible structural changes and a rapid loss in capacity values with increased cycling.
Nevertheless, there is an irreversible transformation of γ-Li x V 2 O 5 from δ-Li x V 2 O 5 when discharge takes place beyond x = 1 as one can see from the structural relationship between the two phases [33].In specific, there is a weak puckering of the double chains of VO 5 pyramids in δ-V 2 O 5 , while it is more pronounced for γ-Li x V 2 O 5 , with the VO 5 pyramids alternate up and down individually instead of forming pairs as in δ-Li x V 2 O 5 .
Nevertheless, there is an irreversible transformation of γ-LixV2O5 from δ-LixV2O5 when discharge takes place beyond x = 1 as one can see from the structural relationship between the two phases [33].In specific, there is a weak puckering of the double chains of VO5 pyramids in δ-V2O5, while it is more pronounced for γ-LixV2O5, with the VO5 pyramids alternate up and down individually instead of forming pairs as in δ-LixV2O5.
Knowledge of the kinetic parameters of Li + insertion in correlation with the chemical diffusion coefficient is important to obtain information on the energy/power features of the lithium cells and a better understanding of the mechanism of lithium insertion in V2O5.A study conducted by Farcy et al. [34] through electrochemical impedance spectroscopy shed light on the influence of lithium content on the electroinsertion in V2O5, revealing discrepancies at high and intermediate frequencies with the absence of well-defined semicircles, as depicted in Figure 3.These deviations can be attributed to the porous nature of the electrode, leading to distinct potential and concentration distributions at the electrode-electrolyte interface [35].In the spectrum, a discernible straight line emerges at lower frequencies, indicative of the Warburg impedance.The position of this impedance is contingent upon the lithium intercalation content denoted by the variable 'x' in LixV₂O₅.
Exploring the diffusion coefficient of Li⁺ for different intercalation levels yields valuable insights [34].During the initial stages of the intercalation processes, the rate of lithium diffusion experiences a significant reduction due to interactions between Li⁺ ions and the V₂O₅ host lattice.This phenomenon aligns with existing research, emphasizing that lithium intercalation induces structural modifications in V₂O₅, dependent on the composition of the bronzes [36].Consequently, the diffusion coefficient reaches its maximum at lower lithium contents, gradually decreasing as 'x' increases.This diminishing trend is attributed to an escalation of the ionic interactions within the crystal lattice, constraining the mobility of the lithium ions.The maximum diffusion coefficient is observed at the lowest intercalation contents, decreasing approximately two orders of magnitude as 'x' varies from 10⁻ 2 to 0.1.Notably, a minimum value is observed for 'x' close to 0.25.
In a noteworthy study conducted by Światowska-Mrowiecka et al.
[37], it was demonstrated through X-ray photoelectron spectroscopy (XPS) analysis that the process of lithium intercalation in V2O5 thin films, prepared by thermally oxidizing vanadium metal, is not entirely reversible.Specifically, after the first deintercalation step, 34% of the vanadium ions remained in the V 4+ state, and after the second deintercalation step, this percentage decreased to 14%.This observation indicates that approximately 8% of the vanadium ions undergo irreversible reduction to V 4+ following deintercalation.This phenomenon is attributed to the entrapment of a portion of the intercalated Li + ions within the V2O5 films, likely occurring at the grain boundaries of the crystalline oxide structure.Knowledge of the kinetic parameters of Li + insertion in correlation with the chemical diffusion coefficient is important to obtain information on the energy/power features of the lithium cells and a better understanding of the mechanism of lithium insertion in V 2 O 5 .A study conducted by Farcy et al. [34] through electrochemical impedance spectroscopy shed light on the influence of lithium content on the electroinsertion in V 2 O 5 , revealing discrepancies at high and intermediate frequencies with the absence of welldefined semicircles, as depicted in Figure 3.These deviations can be attributed to the porous nature of the electrode, leading to distinct potential and concentration distributions at the electrode-electrolyte interface [35].In the spectrum, a discernible straight line emerges at lower frequencies, indicative of the Warburg impedance.The position of this impedance is contingent upon the lithium intercalation content denoted by the variable 'x' in Li x V 2 O 5 .
Exploring the diffusion coefficient of Li + for different intercalation levels yields valuable insights [34].During the initial stages of the intercalation processes, the rate of lithium diffusion experiences a significant reduction due to interactions between Li + ions and the V 2 O 5 host lattice.This phenomenon aligns with existing research, emphasizing that lithium intercalation induces structural modifications in V 2 O 5 , dependent on the composition of the bronzes [36].Consequently, the diffusion coefficient reaches its maximum at lower lithium contents, gradually decreasing as 'x' increases.This diminishing trend is attributed to an escalation of the ionic interactions within the crystal lattice, constraining the mobility of the lithium ions.The maximum diffusion coefficient is observed at the lowest intercalation contents, decreasing approximately two orders of magnitude as 'x' varies from 10 −2 to 0.1.Notably, a minimum value is observed for 'x' close to 0.25.
In a noteworthy study conducted by Światowska-Mrowiecka et al.
[37], it was demonstrated through X-ray photoelectron spectroscopy (XPS) analysis that the process of lithium intercalation in V 2 O 5 thin films, prepared by thermally oxidizing vanadium metal, is not entirely reversible.Specifically, after the first deintercalation step, 34% of the vanadium ions remained in the V 4+ state, and after the second deintercalation step, this percentage decreased to 14%.This observation indicates that approximately 8% of the vanadium ions undergo irreversible reduction to V 4+ following deintercalation.This phenomenon is attributed to the entrapment of a portion of the intercalated Li + ions within the V 2 O 5 films, likely occurring at the grain boundaries of the crystalline oxide structure.

Sodium
In recent years, sodium-ion batteries (SIBs) have emerged as a viable alternative to LIBs due to several advantages.The abundance of sodium as a resource results in lower material costs for SIBs.It exhibits enhanced safety characteristics compared to lithium, as it is less reactive and less prone to thermal runaway events.Moreover, SIBs demonstrate similar voltage levels and charge/discharge profiles to LIBs, making them compatible with existing battery technologies.They follow a similar principle of operation as LIBs, utilizing sodium ions as the charge carriers.Although the investigation of SIBs began alongside LIBs in the 1970s-1980s [38], they witnessed a significant decline with the successful commercialization of LIBs in the 1990s.However, the growing need for improved battery performance has reignited interest in SIBs.
To enhance the performance of SIBs, particular attention has been given to cathode materials.These materials face challenges such as structure degradation, low capacity, and slow kinetic diffusion properties due to the larger size of sodium ions (1.02 Å for Na + ) compared to lithium ions (0.76 Å for Li + ) [39,40].Therefore, research efforts are focused on exploring and developing cathode materials that can overcome these limitations and deliver improved performance in SIBs.
Orthorhombic V2O5 has been recognized as a promising cathode due to its open structure, which enables the reversible accommodation of Na + ions.The crystal structure of layered V2O5, which has an orthorhombic Pmmn lattice [41], undergoes a phase transition when sodiated [42].This structure is composed of edge-and vertex-sharing VO5 square pyramids (Figure 4, left [43]) throughout the crystal structures of the bronzes, which are exceptionally flexible as exemplified with the layered (α-phase) and tunnel (β-phase) materials.

Sodium
In recent years, sodium-ion batteries (SIBs) have emerged as a viable alternative to LIBs due to several advantages.The abundance of sodium as a resource results in lower material costs for SIBs.It exhibits enhanced safety characteristics compared to lithium, as it is less reactive and less prone to thermal runaway events.Moreover, SIBs demonstrate similar voltage levels and charge/discharge profiles to LIBs, making them compatible with existing battery technologies.They follow a similar principle of operation as LIBs, utilizing sodium ions as the charge carriers.Although the investigation of SIBs began alongside LIBs in the 1970s-1980s [38], they witnessed a significant decline with the successful commercialization of LIBs in the 1990s.However, the growing need for improved battery performance has reignited interest in SIBs.
To enhance the performance of SIBs, particular attention has been given to cathode materials.These materials face challenges such as structure degradation, low capacity, and slow kinetic diffusion properties due to the larger size of sodium ions (1.02 Å for Na + ) compared to lithium ions (0.76 Å for Li + ) [39,40].Therefore, research efforts are focused on exploring and developing cathode materials that can overcome these limitations and deliver improved performance in SIBs.
Orthorhombic V 2 O 5 has been recognized as a promising cathode due to its open structure, which enables the reversible accommodation of Na + ions.The crystal structure of layered V 2 O 5 , which has an orthorhombic P mmn lattice [41], undergoes a phase transition when sodiated [42].This structure is composed of edge-and vertex-sharing VO 5 square pyramids (Figure 4, left [43]) throughout the crystal structures of the bronzes, which are exceptionally flexible as exemplified with the layered (α-phase) and tunnel (β-phase) materials.
The sodium-vanadium bronzes, denoted by the general formula Na x V 2 O 5 (0 < x ≤ 2), are a diverse family of compounds with mixed-valence states of vanadium ions ranging from V 4+ to V 5+ .Unlike bronzes of other transition metals, this family encompasses a wide range of structures classified as α-, β-, γ-, δ-, τ-, α', η-, κ-, and χ-phases [44][45][46][47][48].The phase of Na x V 2 O 5 depends on the value of x.At a low sodium content (0 < x < 0.2), it exists in the α-phase with no substantial alterations in the lattice parameters [38].In the range of 0.2 < x < 0.4, the β-phase is formed [36], while the specific composition Na 0.64 V 2 O 5 is called the τ-phase [32].This transition may be associated with modifications in the arrangement of vanadium and sodium ions.In 1988, Jacobsen first conducted a study on α-V 2 O 5 , channeltype β-Na x V 2 O 5 , and layered Na 1+x V 3 O 8 in all-solid-state batteries using poly(ethylene oxide)-based electrolyte at 80 • C [49].This material exhibited the insertion of 2 moles of Na + during the initial discharge, followed by the reversible discharge of 1.7 moles of Na + in subsequent cycles [41].Monoclinic β-Na 0.33 V 2 O 5 has also gained attention because of the tunnel structure, adopting three different Na intercalation sites and ensuring good structural reversibility even upon deep charge/discharge processes [33].
The α'-phase can be found when the sodium content is between 0.7 and 1 [32].For higher sodium contents, the η-phase is observed in the range of 1.45 < x < 1.8, while the κ-phase occurs in the range of 1.68 < x < 1.82 [41].The compound η-Na x V 2 O 5 or Na 9 V 14 O 35 crystallizes in a monoclinic lattice with the space group P2/c [50].Its crystal structure consists of layers oriented along the (010) direction, which are composed of VO 5 (V 4+ ) square pyramids and VO 4 (V 5+ ) tetrahedrons with the sodium atoms interspersed between these layers (Figure 4, right) [43].If all sodium ions are extracted from the structure, the theoretical capacity of η-Na x V 2 O 5 can be estimated to be approximately 163 mAh g −1 .This value, coupled with potential electrochemical activity in the anodic region, highlights the material's potential as a new intercalation system for sodium ions.Understanding the conditions that lead to η-, κ-, and χ-phases can provide insights into the material's behavior.
Nanomaterials 2023, 13, x FOR PEER REVIEW 8 of 29 of NaxV2O5 depends on the value of x.At a low sodium content (0 < x < 0.2), it exists in the α-phase with no substantial alterations in the lattice parameters [38].In the range of 0.2 < x < 0.4, the β-phase is formed [36], while the specific composition Na0.64V2O5 is called the τ-phase [32].This transition may be associated with modifications in the arrangement of vanadium and sodium ions.In 1988, Jacobsen first conducted a study on α-V2O5, channeltype β-NaxV2O5, and layered Na1+xV3O8 in all-solid-state batteries using poly(ethylene oxide)-based electrolyte at 80 °C [49].This material exhibited the insertion of 2 moles of Na + during the initial discharge, followed by the reversible discharge of 1.7 moles of Na + in subsequent cycles [41].Monoclinic β-Na0.33V2O5has also gained attention because of the tunnel structure, adopting three different Na intercalation sites and ensuring good structural reversibility even upon deep charge/discharge processes [33].
The α'-phase can be found when the sodium content is between 0.7 and 1 [32].For higher sodium contents, the η-phase is observed in the range of 1.45 < x < 1.8, while the κphase occurs in the range of 1.68 < x < 1.82 [41].The compound η-NaxV2O5 or Na9V14O35 crystallizes in a monoclinic lattice with the space group P2/c [50].Its crystal structure consists of layers oriented along the (010) direction, which are composed of VO5 (V 4+ ) square pyramids and VO4 (V 5+ ) tetrahedrons with the sodium atoms interspersed between these layers (Figure 4, right) [43].If all sodium ions are extracted from the structure, the theoretical capacity of η-NaxV2O5 can be estimated to be approximately 163 mAh g −1 .This value, coupled with potential electrochemical activity in the anodic region, highlights the material's potential as a new intercalation system for sodium ions.Understanding the conditions that lead to η-, κ-, and χ-phases can provide insights into the material's behavior.Electrochemical impedance spectroscopy is also utilized to investigate the Na + kinetics reaction for a deep understanding of the sodium insertion-extraction mechanism in γ'-V2O5 [51].γ'-V2O5 is characterized by a high (001) preferred orientation corresponding to the stacking of platelets along the c-axis.It exhibits a layered structure differing from that of α-V2O5, distinguished by a notable layer puckering.This distinctive feature involves the assembly of infinite ribbons, comprised of VO₅ edges-sharing distorted pyramids and accentuated by a generous interlayer spacing of 5.02 Å (in contrast to the 4.37 Å observed in α-V₂O₅).These ribbons interconnect along the a-direction, giving rise to intricately puckered slabs that align in stacks along the c-direction, as illustrated in Figure 5.
The crucial electrochemical parameters of the sodiated electrode such as cathode impedance, charge transfer resistance, and double-layer capacity are indicated in Figure 5.The cathode impedance exhibits low values, typically ranging from 300-400 Ω, except for instances of very low sodium content, indicative of high cathode impedance.As sodium uptake progresses, the cathode impedance follows suit, rising from approximately 100 Ω at x = 0.2 to 350 Ω at x = 0.6 and peaking at 700 Ω for x = 0.97 (Figure 5a).Notably, the fully sodiated sample displays a cathode impedance nearly double that of a sodium-free electrode, underscoring the challenging nature of sodium extraction.Concurrently, the gradual and linear growth of Rct with x (as illustrated in Figure 5b) signifies a deceleration in Electrochemical impedance spectroscopy is also utilized to investigate the Na + kinetics reaction for a deep understanding of the sodium insertion-extraction mechanism in γ'-V 2 O 5 [51].γ'-V 2 O 5 is characterized by a high (001) preferred orientation corresponding to the stacking of platelets along the c-axis.It exhibits a layered structure differing from that of α-V 2 O 5 , distinguished by a notable layer puckering.This distinctive feature involves the assembly of infinite ribbons, comprised of VO 5 edges-sharing distorted pyramids and accentuated by a generous interlayer spacing of 5.02 Å (in contrast to the 4.37 Å observed in α-V 2 O 5 ).These ribbons interconnect along the a-direction, giving rise to intricately puckered slabs that align in stacks along the c-direction, as illustrated in Figure 5.
The crucial electrochemical parameters of the sodiated electrode such as cathode impedance, charge transfer resistance, and double-layer capacity are indicated in Figure 5.The cathode impedance exhibits low values, typically ranging from 300-400 Ω, except for instances of very low sodium content, indicative of high cathode impedance.As sodium uptake progresses, the cathode impedance follows suit, rising from approximately 100 Ω at x = 0.2 to 350 Ω at x = 0.6 and peaking at 700 Ω for x = 0.97 (Figure 5a).Notably, the fully sodiated sample displays a cathode impedance nearly double that of a sodium-free electrode, underscoring the challenging nature of sodium extraction.Concurrently, the gradual and linear growth of R ct with x (as illustrated in Figure 5b) signifies a deceleration in charge transfer kinetics during discharge.In the biphasic region (where γ'-V 2 O 5 and γ-Na 0.7 V 2 O 5 coexist), R ct increases from 22 to 38 Ω, while a more pronounced increase (by a factor of 2) is observed in the 0.7 < x ≤ 0.97 solid-solution domain.This trend highlights the adverse impact of deep sodiation on electron transport, leading to a linear decrease in exchange current density with x, dropping from 1 mA cm −2 for γ'-V 2 O 5 to only 0.4 mA cm −2 for γ-Na 0.97 V 2 O 5 .Turning attention to Figure 5c, the evolution of the double-layer capacity reveals compelling insights.The C dl parameter demonstrates an increase from approximately 18 µF cm −2 for γ'-V 2 O 5 to about 30 µF cm −2 for Na 0.97 V 2 O 5 .Notably, this substantial 50% increase in C dl during Na insertion contrasts with the more modest 15% reported increase during Li insertion in γ'-V 2 O 5 .This discrepancy is attributed to the larger volume change induced by sodiation in γ'-V 2 O 5 compared to that induced by lithiation (17% vs. 4.4%).Furthermore, examples from other studies underscore the close correlation between C dl and volume change in cathode materials, such as a 10% increase in C dl for a 5% volume change in nanosized V 2 O 5 [52] and a constant C dl for the Cr 0.11 V 2 O 5.16 mixed oxide with a limited volume change not exceeding 3.5% [53].
The results show a strong correlation between the evolution of cathode impedance, charge transfer resistance, double-layer capacity, and the apparent chemical sodium diffusion coefficient with the structural changes induced during sodiation.In the region of the richest Na uptake (0.6 < x ≤ 0.97) in γ-Na x V 2 O 5 , a faster sodium diffusion is observed, while electron transport is slowed down due to the highly localized electron character of the sodiated phase.Other issues that need investigation is the relationship between the depth of discharge and the kinetics to provide insights of cycling performance optimizations along with strategies to accommodate volume changes and enhance the material's ability to withstand the expansion and contraction cycles.The results show a strong correlation between the evolution of cathode impedance, charge transfer resistance, double-layer capacity, and the apparent chemical sodium diffusion coefficient with the structural changes induced during sodiation.In the region of the richest Na uptake (0.6 < x ≤ 0.97) in γ-NaxV2O5, a faster sodium diffusion is observed, while electron transport is slowed down due to the highly localized electron character of the sodiated phase.Other issues that need investigation is the relationship between the depth of discharge and the kinetics to provide insights of cycling performance optimizations along with strategies to accommodate volume changes and enhance the material's ability to withstand the expansion and contraction cycles.The Na + ion intercalation/deintercalation reaction mechanism in V2O5 has also been investigated by X-ray diffraction (XRD), transmission electron microscopy (TEM), and near-edge X-ray absorption fine structure (NEXAFS) spectroscopy to gain a better understanding of the mechanisms involved and design more efficient electrode materials [54].The changes in the lattice structure during Na + intercalation/deintercalation and the charge-discharge process are summarized in Figure 6.Sodium intercalation and deintercalation occur along the ab planes with ordered chains of layers connected through corner and edge sharing.The intercalation of Na ions leads to an expansion of the interlayer distance along the c-axis, from 4.4 to 4.8 Å at the fully discharged rate.In that process, V2O5 undergoes a transformation to the crystalline phase of NaV2O5, while partially amorphous Na2V2O5 coexists as a minor phase.The Na + ions in the NaV2O5 structure occupy the Wyckoff position of 2b between the van der Waals, causing an expansion of the c-axis.During the charging process, Na + ions are extracted, and V2O5 returns to its original crystal structure, with NaV2O5 present as a minor phase.The Na + ion intercalation/deintercalation reaction mechanism in V 2 O 5 has also been investigated by X-ray diffraction (XRD), transmission electron microscopy (TEM), and nearedge X-ray absorption fine structure (NEXAFS) spectroscopy to gain a better understanding of the mechanisms involved and design more efficient electrode materials [54].The changes in the lattice structure during Na + intercalation/deintercalation and the charge-discharge process are summarized in Figure 6.Sodium intercalation and deintercalation occur along the ab planes with ordered chains of layers connected through corner and edge sharing.The intercalation of Na ions leads to an expansion of the interlayer distance along the c-axis, from 4.4 to 4.8 Å at the fully discharged rate.In that process, V 2 O 5 undergoes a transformation to the crystalline phase of NaV 2 O 5 , while partially amorphous Na 2 V 2 O 5 coexists as a minor phase.The Na + ions in the NaV 2 O 5 structure occupy the Wyckoff position of 2b between the van der Waals, causing an expansion of the c-axis.During the charging process, Na + ions are extracted, and V 2 O 5 returns to its original crystal structure, with NaV 2 O 5 present as a minor phase.The electrochemical properties of α-V2O5 are investigated at room temperature fo the first time in a 1 M NaClO4/PC (propylene carbonate) electrolyte.When Na + ions ar inserted into V2O5, the pristine α-V2O5 structure remained unchanged, with no significan alterations in lattice parameters observed at low sodium concentrations (x ≤ 0.2 i NaxV2O5) [55].However, for sodium amounts in the range of 0.2 ≤ x ≤ 1.6, the insertion o Na ions leads to notable changes in the lattice parameters within 0.2 ≤ x ≤ 0.7, followed b slight changes in 0.7 ≤ x ≤ 1.6.During the first Na + insertion, an irreversible phase calle NaV2O5 is formed.However, this NaV2O5 phase can subsequently reversibly accommo date 0.8 Na + within the potential range of 1.4 V to 3.0 V versus Na + /Na.To that point, it i worth mentioning that Ali and coworkers proposed an alternative reaction mechanism suggesting the presence of a two-phase mixture consisting of NaV2O5 (major phase) an Na2V2O5 (minor phase) during the discharge process [44].The Na2V2O5 includes crysta line and amorphous-like phases.Upon the charging process, the material returns to th original V2O5 structure with the presence of NaV2O5 minor phases.
Despite the existence of studies suggesting alternative reaction mechanisms and th observation of phase changes during the insertion and extraction of Na + ions, a compre hensive understanding of the intricate processes involved in the Na + insertion mechanism remains elusive.To fully elucidate the precise mechanism and shed light on the underly ing processes occurring during Na + insertion into V2O5, further research and investigatio are required.

Potassium
Potassium-ion batteries (PIBs) have gained attention due to the abundance (i.e 17,000 ppm in Earth's crust as compared with Li resource being only 20 ppm) and cos effectiveness of potassium.The redox potential of K + /K (−2.93 V vs. standard hydroge electrode (SHE)) is very close to that of Li + /Li (−3.04 V vs. SHE), indicating that PIBs an LIBs may have similar energy densities, theoretically [56].
PIBs have a similar working principle of "rocking star" with LIBs.However, the exhibit a lower performance compared to LIBs.The structural transformation from α-V2O to KVO [57,58] (Figure 7 [59]) involves the insertion of K + ions into the layers, resulting i layer slippage.Notably, the distortion at the edges of the lattice enhances the probabilit of insertion occurring between the two layers.As a result, the VO5 square pyramid under goes a backward rotation, following the typical motion observed in VO5.Driven by lowe thermodynamic energy, the vanadium atoms within the lattice reorganize themselves an establish stable VO6 octahedra by forming new bonds with oxygen atoms.Ultimately through this process of structural evolution, the KVO layer structure is formed.The electrochemical properties of α-V 2 O 5 are investigated at room temperature for the first time in a 1 M NaClO 4 /PC (propylene carbonate) electrolyte.When Na + ions are inserted into V 2 O 5 , the pristine α-V 2 O 5 structure remained unchanged, with no significant alterations in lattice parameters observed at low sodium concentrations (x ≤ 0.2 in Na x V 2 O 5 ) [55].However, for sodium amounts in the range of 0.2 ≤ x ≤ 1.6, the insertion of Na ions leads to notable changes in the lattice parameters within 0.2 ≤ x ≤ 0.7, followed by slight changes in 0.7 ≤ x ≤ 1.6.During the first Na + insertion, an irreversible phase called NaV 2 O 5 is formed.However, this NaV 2 O 5 phase can subsequently reversibly accommodate 0.8 Na + within the potential range of 1.4 V to 3.0 V versus Na + /Na.To that point, it is worth mentioning that Ali and coworkers proposed an alternative reaction mechanism, suggesting the presence of a two-phase mixture consisting of NaV 2 O 5 (major phase) and Na 2 V 2 O 5 (minor phase) during the discharge process [44].The Na 2 V 2 O 5 includes crystalline and amorphous-like phases.Upon the charging process, the material returns to the original V 2 O 5 structure with the presence of NaV 2 O 5 minor phases.
Despite the existence of studies suggesting alternative reaction mechanisms and the observation of phase changes during the insertion and extraction of Na + ions, a comprehensive understanding of the intricate processes involved in the Na + insertion mechanism remains elusive.To fully elucidate the precise mechanism and shed light on the underlying processes occurring during Na + insertion into V 2 O 5 , further research and investigation are required.

Potassium
Potassium-ion batteries (PIBs) have gained attention due to the abundance (i.e., 17,000 ppm in Earth's crust as compared with Li resource being only 20 ppm) and costeffectiveness of potassium.The redox potential of K + /K (−2.93 V vs. standard hydrogen electrode (SHE)) is very close to that of Li + /Li (−3.04 V vs. SHE), indicating that PIBs and LIBs may have similar energy densities, theoretically [56].
PIBs have a similar working principle of "rocking star" with LIBs.However, they exhibit a lower performance compared to LIBs.The structural transformation from α-V 2 O 5 to KVO [57,58] (Figure 7 [59]) involves the insertion of K + ions into the layers, resulting in layer slippage.Notably, the distortion at the edges of the lattice enhances the probability of insertion occurring between the two layers.As a result, the VO 5 square pyramid undergoes a backward rotation, following the typical motion observed in VO 5 .Driven by lower thermodynamic energy, the vanadium atoms within the lattice reorganize themselves and establish stable VO 6 octahedra by forming new bonds with oxygen atoms.Ultimately, through this process of structural evolution, the KVO layer structure is formed.The presence of a compact interlayer space and tightly arranged VO5 square pyramids in α-V2O5 poses difficulties for the insertion and diffusion of K + ions within its crystal structure [60,61].Theoretical strategies propose that lowering the oxidation state of vanadium in α-V2O5 could induce the transformation of square pyramids into octahedra, which would expand the crystal structure and create a larger interlayer space suitable for K + ion diffusion [49].However, achieving precise control over the oxidation states of vanadium presents challenges and may result in impurities within the material.
Additionally, the ionic radius of K + (1.38 Å) compared with that of Li + (0.76 Å) or Na + (1.02 Å) limits the number of suitable host materials capable of accommodating K without large stresses or volume changes [29].In addition, repulsive K + -K + coulombic interactions could limit transport properties in the crystal framework and, as a consequence, the rate capability of the battery [62].
The potassium intercalation potential of the α-V2O5 polymorph has been relatively unexplored.Previous research has demonstrated the formation of an orthorhombic KxV2O5 bronze structure at high temperatures using a potassium electrolyte [63].However, the extraction of potassium has been limited to only 50%.Recent investigations have focused on studying metastable V2O5 polymorphs that are obtained by removing cations from MxV2O5 bronzes through topochemical processes [64].Density functional theory (DFT) calculations have revealed that these cation-free metastable phases exhibit lower diffusion barriers and higher operating voltages, which renders them promising for potassium storage [53].
The process of K + ion insertion into α-V2O5 nanoparticles was thoroughly investigated using advanced techniques such as in operando synchrotron diffraction, in operando XAS, in situ Raman, XPS, and TEM [65].The experimental observations revealed that during the initial stages of K + ion insertion, V2O5 undergoes a solid-solution phase transformation, leading to the formation of the K0.6V2O5 phase.As the insertion process progresses, a combination of solid-solution and two-phase reactions occurs simultaneously.This suggests that the system deviates significantly from equilibrium, which can be attributed to the presence of kinetic barriers and transport limitations.Furthermore, the formation and subsequent degradation of a solid electrolyte interphase (SEI) were observed during the K + ion insertion process.This indicates the occurrence of substantial side reactions, which have a distinct impact on the degradation mechanism of the material.
The γ'-V2O5 polymorph, which is derived from the γ-LiV2O5 phase through the electrochemical lithiation of α-V2O5, possesses advantageous characteristics.While maintaining orthorhombic symmetry like α-V2O5, γ'-V2O5 exhibits a larger interlayer spacing and a corrugated structure [62].Interestingly, γ'-V2O5 can effectively accommodate a significant quantity of potassium (up to 0.9 K + ions per mole) between its puckered layers at a voltage of 3.3 V versus K + /K (Figure 8) [62].Detailed structural analysis within the voltage range of 4.4 V to 2.4 V has revealed that the potassiation process in γ'-V2O5 triggers a distinctive structural rearrangement, resulting in the crystallization of K0.78V2O5 in the Pnma space group.This transition is accompanied by a moderate interlayer expansion of 9.4% The presence of a compact interlayer space and tightly arranged VO 5 square pyramids in α-V 2 O 5 poses difficulties for the insertion and diffusion of K + ions within its crystal structure [60,61].Theoretical strategies propose that lowering the oxidation state of vanadium in α-V 2 O 5 could induce the transformation of square pyramids into octahedra, which would expand the crystal structure and create a larger interlayer space suitable for K + ion diffusion [49].However, achieving precise control over the oxidation states of vanadium presents challenges and may result in impurities within the material.
Additionally, the ionic radius of K + (1.38 Å) compared with that of Li + (0.76 Å) or Na + (1.02 Å) limits the number of suitable host materials capable of accommodating K without large stresses or volume changes [29].In addition, repulsive K + -K + coulombic interactions could limit transport properties in the crystal framework and, as a consequence, the rate capability of the battery [62].
The potassium intercalation potential of the α-V 2 O 5 polymorph has been relatively unexplored.Previous research has demonstrated the formation of an orthorhombic K x V 2 O 5 bronze structure at high temperatures using a potassium electrolyte [63].However, the extraction of potassium has been limited to only 50%.Recent investigations have focused on studying metastable V 2 O 5 polymorphs that are obtained by removing cations from M x V 2 O 5 bronzes through topochemical processes [64].Density functional theory (DFT) calculations have revealed that these cation-free metastable phases exhibit lower diffusion barriers and higher operating voltages, which renders them promising for potassium storage [53].
The process of K + ion insertion into α-V 2 O 5 nanoparticles was thoroughly investigated using advanced techniques such as in operando synchrotron diffraction, in operando XAS, in situ Raman, XPS, and TEM [65].The experimental observations revealed that during the initial stages of K + ion insertion, V 2 O 5 undergoes a solid-solution phase transformation, leading to the formation of the K 0.6 V 2 O 5 phase.As the insertion process progresses, a combination of solid-solution and two-phase reactions occurs simultaneously.This suggests that the system deviates significantly from equilibrium, which can be attributed to the presence of kinetic barriers and transport limitations.Furthermore, the formation and subsequent degradation of a solid electrolyte interphase (SEI) were observed during the K + ion insertion process.This indicates the occurrence of substantial side reactions, which have a distinct impact on the degradation mechanism of the material.
The γ'-V 2 O 5 polymorph, which is derived from the γ-LiV 2 O 5 phase through the electrochemical lithiation of α-V 2 O 5 , possesses advantageous characteristics.While maintaining orthorhombic symmetry like α-V 2 O 5 , γ'-V 2 O 5 exhibits a larger interlayer spacing and a corrugated structure [62].Interestingly, γ'-V 2 O 5 can effectively accommodate a significant quantity of potassium (up to 0.9 K + ions per mole) between its puckered layers at a voltage of 3.3 V versus K + /K (Figure 8) [62].Detailed structural analysis within the voltage range of 4.4 V to 2.4 V has revealed that the potassiation process in γ'-V 2 O 5 triggers a distinctive structural rearrangement, resulting in the crystallization of K 0.78 V 2 O 5 in the P nma space group.This transition is accompanied by a moderate interlayer expansion of 9.4% upon potassium insertion (in comparison to 18% during sodiation) [62].In this new structure, the V 2 O 5 layers consist of alternating up-and down-oriented VO 5 pairs within the interlayer spacing, in contrast to the alternating single VO 5 pyramids observed in γ'-V 2 O 5 .This change in structure highlights the unique capacity of the pristine γ'-V 2 O 5 lattice to minimize structural modifications during the incorporation of K + ions [62].
Nanomaterials 2023, 13, x FOR PEER REVIEW 12 of 29 upon potassium insertion (in comparison to 18% during sodiation) [62].In this new structure, the V2O5 layers consist of alternating up-and down-oriented VO5 pairs within the interlayer spacing, in contrast to the alternating single VO5 pyramids observed in γ'-V2O5.This change in structure highlights the unique capacity of the pristine γ'-V2O5 lattice to minimize structural modifications during the incorporation of K + ions [62].Bilayered vanadium oxide (δ-V2O5) represents another highly promising cathode material suitable for high-capacity applications [66].Its structure comprises double layers of V-O, creating a notable interlayer spacing of approximately 11.5 Å, which is facilitated by the presence of water molecules [67].This expanded interlayer space offers ample room for the intercalation of ions.By utilizing potassium ions (K + ), both singly and doubly charged ions can be inserted within the interlayer region of the δ-V2O5 phase [68].The resulting compound, known as δ-KxV2O5•nH2O, exhibits a bilayered structure with an interlayer spacing reduced to 9.62 Å [61].Remarkably, it demonstrates an initial capacity of 226 mAh g −1 when employing an organic electrolyte [59].The charge storage mechanism within the K-preintercalated δ-V2O5 phase is primarily governed by diffusion-limited intercalation [59].
It is important to highlight that although the intercalation mechanism of K + ions in V2O5 exhibits similarities to Li + ion intercalation, there are notable differences.The larger size of K + ions compared to Li + ions can introduce structural distortions and impose limitations on the intercalation process, resulting in lower performance when compared with LIBs.Furthermore, it is crucial to consider that the specific properties and performance characteristics can vary depending on the form of V₂O₅ employed.

Magnesium
The intercalation mechanism of Mg 2+ in V2O5 involves a reversible electrochemical process during charging/discharging according to the following reaction [69]: During the charging (insertion), Mg 2 ⁺ ions are introduced into the structure of V2O5 through the open channels that exist between the layers of vanadium oxide.An oxidationreduction (redox) reaction occurs, causing the Mg 2 ⁺ ions to undergo oxidation and release electrons, which are then transferred to the electrode material.Consequently, the interlayer spacing between the vanadium oxide layers expands, enabling the incorporation of the magnesium ions within the V2O5 structure.The Mg 2 ⁺ ions are subsequently stored within the V2O5 lattice, leading to the formation of a compound known as magnesium vanadium pentoxide (MgxV2O5), where the variable x represents the extent of magnesium intercalation.When discharging takes place, the previously stored magnesium ions are released from the V2O5 lattice, moving in the opposite direction.Bilayered vanadium oxide (δ-V 2 O 5 ) represents another highly promising cathode material suitable for high-capacity applications [66].Its structure comprises double layers of V-O, creating a notable interlayer spacing of approximately 11.5 Å, which is facilitated by the presence of water molecules [67].This expanded interlayer space offers ample room for the intercalation of ions.By utilizing potassium ions (K + ), both singly and doubly charged ions can be inserted within the interlayer region of the δ-V 2 O 5 phase [68].The resulting compound, known as δ-K x V 2 O 5 •nH 2 O, exhibits a bilayered structure with an interlayer spacing reduced to 9.62 Å [61].Remarkably, it demonstrates an initial capacity of 226 mAh g −1 when employing an organic electrolyte [59].The charge storage mechanism within the K-preintercalated δ-V 2 O 5 phase is primarily governed by diffusion-limited intercalation [59].
It is important to highlight that although the intercalation mechanism of K + ions in V 2 O 5 exhibits similarities to Li + ion intercalation, there are notable differences.The larger size of K + ions compared to Li + ions can introduce structural distortions and impose limitations on the intercalation process, resulting in lower performance when compared with LIBs.Furthermore, it is crucial to consider that the specific properties and performance characteristics can vary depending on the form of V 2 O 5 employed.

Magnesium
The intercalation mechanism of Mg 2+ in V 2 O 5 involves a reversible electrochemical process during charging/discharging according to the following reaction [69]: During the charging (insertion), Mg 2+ ions are introduced into the structure of V 2 O 5 through the open channels that exist between the layers of vanadium oxide.An oxidationreduction (redox) reaction occurs, causing the Mg 2+ ions to undergo oxidation and release electrons, which are then transferred to the electrode material.Consequently, the interlayer spacing between the vanadium oxide layers expands, enabling the incorporation of the magnesium ions within the V 2 O 5 structure.The Mg 2+ ions are subsequently stored within the V 2 O 5 lattice, leading to the formation of a compound known as magnesium vanadium pentoxide (Mg x V 2 O 5 ), where the variable x represents the extent of magnesium intercalation.When discharging takes place, the previously stored magnesium ions are released from the V 2 O 5 lattice, moving in the opposite direction.
In the initial investigations conducted by Novák et al. [69], it was observed that the intercalation of Mg 2+ into V 2 O 5 is a slow and incomplete process at room temperature.The α-V 2 O 5 phase is the most thermodynamically stable and is composed of double-chain sheets formed by square pyramidal units, which lie parallel to the α-axis (Figure 9) [70].Upon the Mg 2+ insertion, the oxidation of vanadium ions decreases from V 5+ to V 4+ and they become coordinated between the sheets of the V 2 O 5 pyramids.In the α-phase, the calculated energy barrier for the insertion of Mg 2+ is approximately 975 mV, causing irreversible Mg 2+ processes.Additionally, it needs to be noted that the insertion of Mg 2+ being higher than 0.5 mole is not practical since V 2 O 5 undergoes a structural transition, transforming into the ε phase (Figure 9) [70], which has lower potential and a weak driving force for Mg 2+ intercalation.Figure 9 indicates the ε phase corresponding to a specific ordering of Mg atoms in α-V 2 O 5 at half magnesiation.
In the initial investigations conducted by Novák et al. [69], it was observed that the intercalation of Mg 2+ into V2O5 is a slow and incomplete process at room temperature.The α-V2O5 phase is the most thermodynamically stable and is composed of double-chain sheets formed by square pyramidal units, which lie parallel to the α-axis (Figure 9) [70].Upon the Mg 2+ insertion, the oxidation of vanadium ions decreases from V 5+ to V 4+ and they become coordinated between the sheets of the V2O5 pyramids.In the α-phase, the calculated energy barrier for the insertion of Mg 2+ is approximately 975 mV, causing irreversible Mg 2+ processes.Additionally, it needs to be noted that the insertion of Mg 2+ being higher than 0.5 mole is not practical since V2O5 undergoes a structural transition, transforming into the ε phase (Figure 9) [70], which has lower potential and a weak driving force for Mg 2+ intercalation.Figure 9 indicates the ε phase corresponding to a specific ordering of Mg atoms in α-V2O5 at half magnesiation.The realization of a functional magnesium-ion battery (MIB) with a high energy density remains an ongoing challenge.Consequently, layered V2O5 has been both the focus of such endeavors and a subject of controversy.More recent studies have indicated that α-V2O5 is capable of reversible intercalation of at least 1 mole of Mg 2+ at 110 °C when using an ionic liquid electrolyte with high chemical and anodic stability [71].Figure 10 indicates that α-V2O5 has a small reversible capacity of 16 mAh g −1 at 25 °C, which increased 20-fold to 295 mAh g −1 at 110 °C.This process resulted in the highest observed Mg capacities to date [72].In particular, the ability to reversibly intercalate at least one Mg 2+ per unit formula was demonstrated without significant co-intercalation of H2O or H + , nor competition with the conversion to MgO and VOy, for y < 2. The realization of a functional magnesium-ion battery (MIB) with a high energy density remains an ongoing challenge.Consequently, layered V 2 O 5 has been both the focus of such endeavors and a subject of controversy.More recent studies have indicated that α-V 2 O 5 is capable of reversible intercalation of at least 1 mole of Mg 2+ at 110 • C when using an ionic liquid electrolyte with high chemical and anodic stability [71].Figure 10 indicates that α-V 2 O 5 has a small reversible capacity of 16 mAh g −1 at 25 • C, which increased 20-fold to 295 mAh g −1 at 110 • C.This process resulted in the highest observed Mg capacities to date [72].In particular, the ability to reversibly intercalate at least one Mg 2+ per unit formula was demonstrated without significant co-intercalation of H 2 O or H + , nor competition with the conversion to MgO and VO y , for y < 2. By incorporating PEDOT, the interlayer spacing of V 2 O 5 was controlled, resulting in the development of a bilayered V 2 O 5 /PEDOT (VOP) composite with an intercalation topology [73].This composite demonstrated rapid and reversible charge storage for MIB cathodes.To gain insights into the mechanism of Mg 2+ ion storage within VOP during the charge/discharge processes, in situ XRD, ex situ XRD, and ex situ XPS analyses were performed.
During the insertion and extraction of Mg 2+ ions between the interlayers of VOP, the Mg 2+ ions undergo solvation by water molecules promoting the activation process and lowering the desolvation energy [73].The interlayer spacing of the (001) plane of VOP was measured to be 19.02Å in the charged state at +1.0 V (Figure 11, left), which is approximately 4.37 times larger than that of pristine V 2 O 5 .In addition, the interlayer spacing in the discharge state at −1.0 V was estimated to be 20.16Å (Figure 11, right) [73].These measurements provide valuable information about the structural changes occurring within VOP during the intercalation and deintercalation of Mg 2+ ions.By incorporating PEDOT, the interlayer spacing of V₂O₅ was controlled, resulting the development of a bilayered V2O5/PEDOT (VOP) composite with an intercalation pology [73].This composite demonstrated rapid and reversible charge storage for M cathodes.To gain insights into the mechanism of Mg 2 ⁺ ion storage within VOP during charge/discharge processes, in situ XRD, ex situ XRD, and ex situ XPS analyses were p formed.
During the insertion and extraction of Mg 2 ⁺ ions between the interlayers of VOP, Mg 2 ⁺ ions undergo solvation by water molecules promoting the activation process a lowering the desolvation energy [73].The interlayer spacing of the (001) plane of VOP w measured to be 19.02Å in the charged state at +1.0 V (Figure 11, left), which is appro mately 4.37 times larger than that of pristine V2O5.In addition, the interlayer spacing the discharge state at −1.0 V was estimated to be 20.16Å (Figure 11, right) [73].Th measurements provide valuable information about the structural changes occurr within VOP during the intercalation and deintercalation of Mg 2 ⁺ ions.

Calcium
In contrast with the vast knowledge available about the Li + intercalation mechani the nature and crystal structure of the phase formed for the case of Ca 2+ are even less plored.The available DFT studies predict migration barriers of about 1.7-1.9eV in α-V with an average voltage of about 3.2 V vs. Ca 2+ /Ca [71].The polymorph α-CaV2O5 [ prepared by solid-state reaction enables an appropriate coordination for the Ca 2+ [74].
Seung-Tae Hong et al. [75] introduced a novel intercalation mechanism Ca0.28V2O5•H2O wherein upon charging, Ca 2+ ions are extracted from every two interlay leaving only a fraction of calcium ions in the remaining interlayers.Upon dischargi irregular insertions of Ca 2+ ions occur within the interlayers, leading to stacking faults

Calcium
In contrast with the vast knowledge available about the Li + intercalation mechanism, the nature and crystal structure of the phase formed for the case of Ca 2+ are even less explored.The available DFT studies predict migration barriers of about 1.7-1.9eV in α-V 2 O 5 with an average voltage of about 3.2 V vs. Ca 2+ /Ca [71].The polymorph α-CaV 2 O 5 [71] prepared by solid-state reaction enables an appropriate coordination for the Ca 2+ [74].
Seung-Tae Hong et al. [75] introduced a novel intercalation mechanism for Ca 0.28 V 2 O 5 •H 2 O wherein upon charging, Ca 2+ ions are extracted from every two interlayers, leaving only a fraction of calcium ions in the remaining interlayers.Upon discharging, irregular insertions of Ca 2+ ions occur within the interlayers, leading to stacking faults.
Another study presented the utilization of the acetonitrile-water hybrid electrolyte in Ca 0.25 V 2 O 5 •nH 2 O, referred to as CVO.The crystal structure of CVO, illustrated in the accompanying Figure 12 [76], reveals a layered configuration with inserted Ca 2+ ions occupying the interlayer spaces of V 2 O 5 .These divalent ions form robust ionic bonds with oxygen atoms, creating polyhedral pillars (CaO 7 ).These pillars effectively stabilize the V 2 O 5 layers and prevent potential structural failure during the cycling of the battery [77].Another study presented the utilization of the acetonitrile-water hybrid electrolyte in Ca0.25V2O5•nH2O, referred to as CVO.The crystal structure of CVO, illustrated in the accompanying Figure 12 [76], reveals a layered configuration with inserted Ca 2+ ions occupying the interlayer spaces of V2O5.These divalent ions form robust ionic bonds with oxygen atoms, creating polyhedral pillars (CaO7).These pillars effectively stabilize the V2O5 layers and prevent potential structural failure during the cycling of the battery [77].Double-sheet V2O5•nH2O (Figure 13) was reported as a reversible host structure for Ca 2+ ions [78].The presence of water molecules (n) in the structure depends on synthetic and environmental factors.The crystal structure of double-sheet V2O5•nH2O consists of bilayers, with each bilayer composed of two opposing sheets of V2O5 [79].These sheets are constructed using VO5 square pyramidal units, which are either corner-or edge- Double-sheet V 2 O 5 •nH 2 O (Figure 13) was reported as a reversible host structure for Ca 2+ ions [78].The presence of water molecules (n) in the structure depends on synthetic and environmental factors.The crystal structure of double-sheet V 2 O 5 •nH 2 O consists of bilayers, with each bilayer composed of two opposing sheets of V 2 O 5 [79].These sheets are constructed using VO 5 square pyramidal units, which are either corner-or edge-shared.The two V 2 O 5 sheets face each other at a distance of approximately 2.8 Å, while the interlayer spacing between the double-sheet layers is greater than 8 Å, providing room for crystal water [72].
Figure 12.Structure evolution of V2O5 during charging/discharging processes of Ca 2+ [76].Image adapted from Ref. [76].Double-sheet V2O5•nH2O (Figure 13) was reported as a reversible host structure for Ca 2+ ions [78].The presence of water molecules (n) in the structure depends on synthetic and environmental factors.The crystal structure of double-sheet V2O5•nH2O consists of bilayers, with each bilayer composed of two opposing sheets of V2O5 [79].These sheets are constructed using VO5 square pyramidal units, which are either corner-or edgeshared.The two V2O5 sheets face each other at a distance of approximately 2.8 Å, while the interlayer spacing between the double-sheet layers is greater than 8 Å, providing room for crystal water [72].The mechanism for storing Ca 2+ ions involves both bulk intercalation and surface capacitance reactions [70].Analytical techniques such as XRD, TEM, elemental analyses, and bond-valence-sum map (BVSM) calculations were employed to investigate the Ca 2+ transport and the electrochemical reaction.The results unequivocally indicate that the transportation of Ca 2+ ions plays a significant role in the electrochemical reaction demonstrating a new type of calcium-intercalating host material [70].[78].Image adapted from Ref. [78].
The mechanism for storing Ca 2+ ions involves both bulk intercalation and surface capacitance reactions [70].Analytical techniques such as XRD, TEM, elemental analyses, and bond-valence-sum map (BVSM) calculations were employed to investigate the Ca 2+ transport and the electrochemical reaction.The results unequivocally indicate that the transportation of Ca 2+ ions plays a significant role in the electrochemical reaction demonstrating a new type of calcium-intercalating host material [70].

Trivalent Cations
The chemical intercalation of aluminum in aerogel V 2 O 5 with trimethylaluminum in heptane was reported in 1998 [80].These chemically intercalated aluminum ions in Al 1.33 V 2 O 5 were employed in an electrochemical cell for intercalation into a V 2 O 5 counterelectrode, in a sort of Al-ion battery, using Al(CF 3 SO 3 ) 3 in propylene carbonate as the electrolyte solution.
Several authors have reported the intercalation of aluminum ions into V 2 O 5 using AlCl 3 aqueous electrolytes, although it is still debated.The deintercalation of aluminum in V 2 O 5 using an aqueous solution takes place in the voltage range between ca.−0.3 V and +0.1 V vs. MSE with a reversible capacity of about 120 mAh g −1 (Figure 14, left) [81].The low capacity at high current density is indicative of an intercalation reaction controlled by solid-state diffusion.The aluminum ion is highly polarizing, and its charge is shielded by the dipoles of the water molecules in its coordination sphere.The electrochemical reaction for the intercalation of hydrated aluminum in V 2 O 5 can be written as The resulting Al-intercalated vanadium oxide is amorphous at approximately x = 0.5, in contrast to the crystalline character of the Li-intercalated compound.It is worth noting that the electrochemical behavior in an aqueous solution of aluminum could be better than that in an aqueous lithium solution, and this fact can be related to the great polarizing power of the aluminum ion and its tendency to be in hydrated form.However, the diffusion of the hydrated aluminum ion in the solid electrode can be sluggish.After preparing V 2 O 5 particles with nanosheets-like morphology by hydrothermal method, the capacity is increased up to 140 mAh g −1 at high current density, and the capacity retention is excellent [82].On the other hand, the interlayer spacing of V 2 O 5 during the deintercalation of aluminum remains nearly unchanged.
Beyond aqueous electrolytes, binder-free V 2 O 5 and an ionic liquid as an electrolyte also support the intercalation of Al 3+ at around between 0.0 and 1.2 V vs. Al 3+ /Al [83].Although most Al in the ionic liquid exists in the form of AlCl 4 − and Al 2 Cl 7 − , it seems that the cation Al 3+ is intercalated.The voltages of the peaks in the CV results suggest that aluminum prefers to intercalate on the inner layer sites (site-a) (Figure 14, right) [83].
The resulting Al-intercalated vanadium oxide is amorphous at approximately x = 0.5, in contrast to the crystalline character of the Li-intercalated compound.It is worth noting that the electrochemical behavior in an aqueous solution of aluminum could be better than that in an aqueous lithium solution, and this fact can be related to the great polarizing power of the aluminum ion and its tendency to be in hydrated form.However, the diffusion of the hydrated aluminum ion in the solid electrode can be sluggish.After preparing V2O5 particles with nanosheets-like morphology by hydrothermal method, the capacity is increased up to 140 mAh g −1 at high current density, and the capacity retention is excellent [82].On the other hand, the interlayer spacing of V2O5 during the deintercalation of aluminum remains nearly unchanged.
Beyond aqueous electrolytes, binder-free V2O5 and an ionic liquid as an electrolyte also support the intercalation of Al 3+ at around between 0.0 and 1.2 V vs. Al 3+ /Al [83].Although most Al in the ionic liquid exists in the form of AlCl4 − and Al2Cl7 − , it seems that the cation Al 3+ is intercalated.The voltages of the peaks in the CV results suggest that aluminum prefers to intercalate on the inner layer sites (site-a) (Figure 14, right) [83].

Dual-Ion Intercalation
The hydrated vanadium oxide V2O5•nH2O, referred to as VOH, was utilized for the simultaneous intercalation of one-valent metal K + and a divalent alkaline earth metal Mg 2+ , denoted as KMgVOH (Figure 15) [84].The figure presents the structural models of the three samples, MgVOH, KVOH, and KMgVOH.Introducing Mg 2+ or K + into the V-O interlayer causes a change in the interlayer spacing.In specific, upon Mg 2+ insertion, the

Dual-Ion Intercalation
The hydrated vanadium oxide V 2 O 5 •nH 2 O, referred to as VOH, was utilized for the simultaneous intercalation of one-valent metal K + and a divalent alkaline earth metal Mg 2+ , denoted as KMgVOH (Figure 15) [84].The figure presents the structural models of the three samples, MgVOH, KVOH, and KMgVOH.Introducing Mg 2+ or K + into the V-O interlayer causes a change in the interlayer spacing.In specific, upon Mg 2+ insertion, the spacing expands to 14.1 Å, while K + intercalation leads to a spacing of 10.4 Å [84].On the other hand, when both metal ions are simultaneously intercalated, the spacing remains the same as with VOH (i.e., 11.4 Å) [84].Overall, it was observed that Mg 2+ insertion increases the layer spacing of VOH, thereby widening the ion transport channels and enhancing the battery's capacity [84].Conversely, K + intercalation brings the V-O layers closer together, leading to a stabilized structure for the material [84].spacing expands to 14.1 Å, while K + intercalation leads to a spacing of 10.4 Å [84].On the other hand, when both metal ions are simultaneously intercalated, the spacing remains the same as with VOH (i.e., 11.4 Å) [84].Overall, it was observed that Mg 2+ insertion increases the layer spacing of VOH, thereby widening the ion transport channels and enhancing the battery's capacity [84].Conversely, K + intercalation brings the V-O layers closer together, leading to a stabilized structure for the material [84].A synergistic mechanism involving the combination of Zn 2+ and H + (Figure 16) was successfully achieved in Li0.45V2O5•0.89H2O(LVO) nanoplates within 2 M ZnSO4 [85].During the initial stage (1.5 to 0.7 V), both Zn 2+ and a small number of H + ions are inserted into LVO nanoplates, resulting in a continuous reduction of the interlaminar spacing from its original value of 10.45 Å to 9.45 Å [85].This reduction is primarily attributed to the strong A synergistic mechanism involving the combination of Zn 2+ and H + (Figure 16) was successfully achieved in Li 0.45 V 2 O 5 •0.89H 2 O (LVO) nanoplates within 2 M ZnSO 4 [85].During the initial stage (1.5 to 0.7 V), both Zn 2+ and a small number of H + ions are inserted into LVO nanoplates, resulting in a continuous reduction of the interlaminar spacing from its original value of 10.45 Å to 9.45 Å [85].This reduction is primarily attributed to the strong electrostatic attraction between the negatively charged VO x layers and the positively charged divalent Zn 2+ ions.As the interlayer distance decreases and active sites between the LVO layers become available for Zn 2+ insertion, a second discharge stage is initiated (0.7 to 0.3 V), during which only H + ions are inserted into the LVO with the formation of flake-like Zn 4 SO 4 (OH) 6 •0.5H 2 O (ZHS) structures on the surface of the LVO cathode [85].In this second discharge stage, any excess of OH -ions is consumed through the generation of these flake-like ZHS structures [85].Finally, during the recharge process, the extracted H + ions can dissolve the ZHS structures, which is advantageous for improving the cycle stability of the battery system.

Recent Advances in the Intercalation Properties of Vanadium Pentoxides
Enhancing electrodes derived from vanadium compounds can be achieved through two primary avenues: the exploration of novel structures and the fine-tuning of particles.As an alternative to low-pressure α-V2O5, the high-pressure variant of vanadium oxide, β-V2O5, has demonstrated potential viability as an electrode for both lithium and sodium cells [86,87].Nevertheless, the synthesis procedure under high-pressure conditions appears to pose challenges for scalability in large-scale applications.
Reducing the particle size through ball-milling significantly enhances the electrochemical properties of γ′-V2O5, showcasing improved diffusivity and accelerated sodium diffusion within the single-phase region [88].
The integration of nanosheets from bilayered V2O5 with graphene layers to create a two-dimensional heterostructure holds the potential to expedite interfacial charge transfer, facilitating swift pseudocapacitive multi-electron reactions [89].Through the strategic engineering of the vanadium oxide heterostructures, this approach aims to achieve highenergy and high-power lithium storage.Notably, the predominant contribution to charge storage in lithium cells for this V2O5/graphene heterostructure arises from pseudocapacitance.
To further refine the structure and morphology of V2O5, a recent synthetic method

Recent Advances in the Intercalation Properties of Vanadium Pentoxides
Enhancing electrodes derived from vanadium compounds can be achieved through two primary avenues: the exploration of novel structures and the fine-tuning of particles.As an alternative to low-pressure α-V 2 O 5 , the high-pressure variant of vanadium oxide, β-V 2 O 5 , has demonstrated potential viability as an electrode for both lithium and sodium cells [86,87].Nevertheless, the synthesis procedure under high-pressure conditions appears to pose challenges for scalability in large-scale applications.
Reducing the particle size through ball-milling significantly enhances the electrochemical properties of γ ′ -V 2 O 5 , showcasing improved diffusivity and accelerated sodium diffusion within the single-phase region [88].
The integration of nanosheets from bilayered V 2 O 5 with graphene layers to create a two-dimensional heterostructure holds the potential to expedite interfacial charge transfer, facilitating swift pseudocapacitive multi-electron reactions [89].Through the strategic engineering of the vanadium oxide heterostructures, this approach aims to achieve high-energy and high-power lithium storage.Notably, the predominant contribution to charge storage in lithium cells for this V 2 O 5 /graphene heterostructure arises from pseudocapacitance.
To further refine the structure and morphology of V 2 O 5 , a recent synthetic method has been reported [90].This involves the calcination of self-assembled surfactant 1,3-bis[(3octadecyl-1)-imidazolio)methyl]benzene (gemini) and [V 10 O 28 ] 6− clusters, resulting in orthorhombic V 2 O 5 in the form of rod-like particles.The length of the rods increases with the calcination temperature.

Cationic Doping
The utilization of cationic doping in V 2 O 5 cathodes is employed to enhance their electrochemical performance, addressing drawbacks such as their limited electronic and ionic conductivity as well as stability issues.By introducing extra charge carriers into the lattice, cationic doping facilitates the movement of electrons and ions during charge/discharge processes.This, in turn, improves conductivity and prevents structural deterioration throughout cycling [91][92][93][94][95]. Additionally, the incorporation of cationic doping serves to enhance the number of active sites available for ion intercalation.This, in turn, contributes to heightened ion storage capacity, translating into increased energy density and an extended lifespan for the battery.
Currently, there is no consensus among researchers regarding the optimal theoretical approach for treating doped V 2 O 5 .In an effort to address this issue, Jovanović et al. employed density functional theory (DFT) calculations to provide a general overview of the effects of 3d element doping (from Sc to Zn) in V 2 O 5 [91].Their study revealed that interstitial doping resulted in an expansion of the V 2 O 5 lattice, while substitutional doping had a relatively minor impact on the structure [94].However, it had a significant effect on the electronic structure, leading to a reduction in the band gap of V 2 O 5 and an improvement in conductivity.This theoretical analysis confirms doping as a promising strategy for modifying the structural and electronic properties of V 2 O 5 .
Starting with Mn and Ni, it was indicated that the high concentration of both dopants in V 2 O 5 •nH 2 O clearly presented effects in morphology resulting in the presence of radial aggregates (Figure 17) [92].The pre-intercalation of Ni and Mn in the interlayer space resulted in an improvement in the delivered capacity and rate capability, likely attributed to the presence of dopants and induced morphological changes.Notably, Ni-doped V 2 O 5 electrodes exhibited a higher initial capacity (350 mAh g −1 ) compared to Mn-doped ones (290 mAh g −1 ).Overall, all the doped samples delivered higher specific capacities than the undoped ones.In the case of the doped samples, the irreversible capacity loss during the first cycle most likely originated by the Li + reaction with the trapped water molecules in the V 2 O 5 interlayer (Figure 18) [92].
In another study, the potential of Cu doping was investigated, as Cu is known for its advantageous combination of electrical conductivity and cost, making it a practical candidate for doping [96].The researchers examined the electrodeposited V 2 O 5 doped with 1 wt.%Cu, showing a discharge capacity of up to 362 mAh g −1 , which corresponds to 86.2% of the theoretical capacity (420 mAh g −1 ) [97] for the insertion of two Li + ions [98].The enhanced capacity of the Cu-doped thin-film electrode, compared to the pure electrode, can be attributed to three factors: an increase in active area, the vine fiber structure, and the higher electronic conductivity resulting from Cu doping.The vine fiber structure provides more sites for the embedding Li + and allows the accommodation of larger volume changes during cycling [88].Furthermore, the incorporation of Cu 2+ in V 2 O 5 led to an increase in V 4+ content within the material.The doping process facilitated the generation of additional small polaritons by coupling the negative charge on the V 4+ with the lattice deformation induced by the presence of Cu 2+ .As a result, the electronic conductivity of the Cu-doped V 2 O 5 was enhanced [88].Finally, it is also worth noting that the capacity reported is higher than that of the Y-doped V 2 O 5 (224 mAh g −1 ) [99].
material [101].In conclusion, the inclusion of Sn doping positively impacts electrochemical performance by providing charge carriers in the form of electron polarons and serving as nucleation sites for the formation of the lithiation phase during Li intercalation.Following with Sn, Li et al. indicated that the 4% Sn 4+ -doped V 2 O 5 presented the highest capacity (292 mAh g −1 and 162.5 mAh g −1 at 50 and 2000 mA g −1 ) and best cycling (0.36% for Sn 0.04 V 1.96 O 5−δ and 0.74% for V 2 O 5 at a current density of 200 mA g −1 ) (Figure 19) [100].The improved performance can be attributed to the presence of V 4+ and the creation of oxygen vacancies resulting from Sn doping.DFT calculations were employed to investigate the formation of Sn-related defects and their effects.The analysis focused on point-defect formation energies and properties to determine the most probable defect and its charge compensation mechanism [101].The study revealed that the most favorable defect is the substitution of Sn for VO, accompanied by a bound polaron at a V center serving as the charge compensation.The polaron possesses an escape barrier of 0.55 eV, enabling it to migrate away from the defect center [100].This escape process generates charge carriers that significantly enhance the electronic conductivity compared to that of the undoped material [101].In conclusion, the inclusion of Sn doping positively impacts electrochemical performance by providing charge carriers in the form of electron polarons and serving as nucleation sites for the formation of the lithiation phase during Li intercalation.Studies have investigated the effects of Co doping in various lithium-based materi such as LiFePO4 [102,103].In the case of LiFePO4, it has been observed that a high conc tration of Co doping negatively impacts the performance, whereas a low level of Co d ing leads to a noticeable improvement in capacity [104].In a pioneering work by Ji et hydrothermally grown Co-doped V2O5 exhibited a capacity of 394.98 mAh g −1 after 50 cles at 30 mA g −1 [105].This improvement can be attributed to the higher electronic c ductivity of the doped materials, which alleviates the strain experienced during Li + ins tion/extraction and slows down the structural degradation.
Cerium, being the most abundant rare earth element, possesses a relatively large dius and a strong affinity for oxygen.It is commonly selected as a structure stabilizer enhance the ion conductivity [106].Furthermore, its unique structure, characterized b half-filled 4f electron orbit, allows variable electronic properties [107].In specific, wh Ce is doped into V2O5 (Ce0.1V2O5),microspheres with an average diameter of 2-5 µm formed (Figure 20) and superior electrochemical performance is achieved compared that of the undoped V2O5 [108].The Ce-doped microspheres exhibited a high reversi capacity of 260 mAh g −1 at 294 mA g −1 , with a capacity retention of approximately 88.9 after 200 cycles.This enhanced performance is attributed to the enlargement of the int planar spacing in V2O5, which reduces the charge transfer resistance and improves diffusion coefficient of Li + .Studies have investigated the effects of Co doping in various lithium-based materials such as LiFePO 4 [102,103].In the case of LiFePO 4 , it has been observed that a high concentration of Co doping negatively impacts the performance, whereas a low level of Co doping leads to a noticeable improvement in capacity [104].In a pioneering work by Ji et al., hydrothermally grown Co-doped V 2 O 5 exhibited a capacity of 394.98 mAh g −1 after 50 cycles at 30 mA g −1 [105].This improvement can be attributed to the higher electronic conductivity of the doped materials, which alleviates the strain experienced during Li + insertion/extraction and slows down the structural degradation.
Cerium, being the most abundant rare earth element, possesses a relatively large radius and a strong affinity for oxygen.It is commonly selected as a structure stabilizer to enhance the ion conductivity [106].Furthermore, its unique structure, characterized by a half-filled 4f electron orbit, allows variable electronic properties [107].In specific, when Ce is doped into V 2 O 5 (Ce 0.1 V 2 O 5 ), microspheres with an average diameter of 2-5 µm are formed (Figure 20) and superior electrochemical performance is achieved compared to that of the undoped V 2 O 5 [108].The Ce-doped microspheres exhibited a high reversible capacity of 260 mAh g −1 at 294 mA g −1 , with a capacity retention of approximately 88.93% after 200 cycles.This enhanced performance is attributed to the enlargement of the interplanar spacing in V 2 O 5 , which reduces the charge transfer resistance and improves the diffusion coefficient of Li + .
formed (Figure 20) and superior electrochemical performance is achieved compared to that of the undoped V2O5 [108].The Ce-doped microspheres exhibited a high reversible capacity of 260 mAh g −1 at 294 mA g −1 , with a capacity retention of approximately 88.93% after 200 cycles.This enhanced performance is attributed to the enlargement of the interplanar spacing in V2O5, which reduces the charge transfer resistance and improves the diffusion coefficient of Li + .Yttrium (Y 3+ ) is also an effective dopant that can significantly improve the electrochemical performance of electrode materials.This is primarily due to its large radius (90 pm), high electric charge, and strong self-polarization ability [109,110].While there have been studies on the reversible intercalation of Y 3+ into the host structure of V2O5, there have been no reports focusing on SIBs [111].In a recent study, Y 3+ was pre-intercalated Yttrium (Y 3+ ) is also an effective dopant that can significantly improve the electrochemical performance of electrode materials.This is primarily due to its large radius (90 pm), high electric charge, and strong self-polarization ability [109,110].While there have been studies on the reversible intercalation of Y 3+ into the host structure of V 2 O 5 , there have been no reports focusing on SIBs [111].In a recent study, Y 3+ was pre-intercalated into Y 0.02 V 2 O 5 , resulting in significantly enhanced cycling stability and superior rate capability.The specific capacity achieved was 119 mAh g −1 after 100 cycles, which is notably higher than that of the pure V 2 O 5 electrode (84 mAh g −1 ) [95].The improved performance of the doped V 2 O 5 can be attributed to several factors [104].Firstly, the Y 3+ doping leads to an increase in low-valence vanadium ions (V 4+ ), which enhances the electrical conductivity of V 2 O 5 and facilitates the movement of charge carriers within the material.Secondly, the structural integrity of V 2 O 5 is enhanced due to the incorporation of Y 3+ ions maintaining the stability and integrity of the electrode material during charge and discharge cycles.Lastly, the presence of Y 3+ ions suppresses the irreversible phase transition of hydrated V 2 O 5 , mitigating structural degradation and ensuring a more reversible electrochemical reaction.Overall, the utilization of Y 3+ doping in V 2 O 5 electrodes holds promise for enhancing the electrochemical performance in energy storage devices, primarily by improving electrical conductivity, enhancing structural integrity, and suppressing irreversible phase transitions [104].
The selection of the most suitable cationic dopant in V 2 O 5 for improved electrochemical measurements and their application in energy storage systems is influenced by various factors, including the battery components and the desired performance metrics depending on the application requirements (Table 1).According to the available research data, introducing Ni into V 2 O 5 has demonstrated enhancements in the capacity, rate capability, and cycling stability of V 2 O 5 -based electrodes.Ni doping improves charge transfer kinetics and enhances the structural stability during charge/discharge cycles.Another promising dopant is Cu, which aids in the formation of a three-dimensional nanoscale net-like structure, leading to an increased specific surface area and improved transport capacity within the electrode.While Ni and Cu have shown favorable results, other dopants such as Mn, Co, and Ce have also been explored, demonstrating positive impacts on the electrochemical performance of V 2 O 5 .Nonetheless, the optimal choice of dopant should be determined based on comprehensive studies that consider a specific battery system and performance objectives.

Electrolytes and Interfaces
Overcoming challenges associated with the dissolution of vanadium compounds, especially in the case of layered-type compounds, and addressing interfacial reactivity are crucial hurdles.Various strategies have been proposed to tackle these issues.An intriguing alternative involves the use of hybrid organic-water solvents in the electrolyte solution, such as the ether-water mixture.Wang et al. discovered that a hybrid electrolyte solution, specifically, tetraethylene glycol dimethyl ether (TEGDME)-water, significantly enhances the diffusion coefficient of magnesium intercalated in layered sodium vanadate (NaV 8 O 20 •nH 2 O) [112].In this hybrid solution, TEGDME, ClO 4 − ions, and water molecules coordinate with magnesium ions, as depicted in Figure 21.This coordination promotes the swift transport of cations, expanding the electrochemical stability window.The extended chain length of TEGDME strengthens interactions between water molecules (e.g., hydrogen bonding interactions) and TEGDME, consequently raising the overpotential for water splitting.The interaction between magnesium and water ligands reduces the activity of free water in the electrolyte solution, contributing to an enlarged voltage window.Furthermore, the interface layer exhibits robustness owing to the decomposition of TEGDME and the formation of a protective film.This suppresses the dissolution of vanadium, resulting in an impressive cycle life of 1000 cycles.Mechanistic studies on the electrochemical reactions confirm that Na + in the original sodium vanadate undergoes deintercalation and is replaced by Mg 2+ during cycling.The reversible intercalation of Mg 2+ is facilitated by the shielding effect of water molecules.Carlo simulation [112].Image adapted from Ref. [112].
Research has demonstrated that electrode materials featuring higher oxidation states of vanadium ions exhibit increased solubility in electrolyte solutions containing carbonate solvents, consequently leading to battery failure.For instance, the solubility of VO2F surpasses that of Li2−xVO2F.Utilizing highly concentrated solutions, such as 5.5 M LiFSI in DMC, results in a lower quantity of free solvent molecules.Consequently, this diminishes the dissolution of vanadium-based electrodes, such as Li2−xVO2F [113].Additionally, the use of more concentrated electrolytes contributes to a reduction in interfacial resistance.
Within the hybrid aqueous/organic electrolytes, it has recently been found that the Carlo simulation [112].Image adapted from Ref. [112].
Research has demonstrated that electrode materials featuring higher oxidation states of vanadium ions exhibit increased solubility in electrolyte solutions containing carbonate solvents, consequently leading to battery failure.For instance, the solubility of VO 2 F surpasses that of Li 2−x VO 2 F. Utilizing highly concentrated solutions, such as 5.5 M LiFSI in DMC, results in a lower quantity of free solvent molecules.Consequently, this diminishes the dissolution of vanadium-based electrodes, such as Li 2−x VO 2 F [113].Additionally, the use of more concentrated electrolytes contributes to a reduction in interfacial resistance.
Within the hybrid aqueous/organic electrolytes, it has recently been found that the acetonitrile component of the acetonitrile-water solvent mixture suppresses the dissolution of vanadium species from layered Ca x V 2 O 5 •nH 2 O during electrochemical cycling, while water molecules accelerate the diffusion kinetics [76].Another rationale for the observed enhancement upon the addition of water to the solution can be attributed to the generation of protons.Protons, formed through the dissociation of H 2 O, are incorporated into V 2 O 5 , serving as charge carriers and exhibiting a preference for binding with vanadyl oxygen.Calculations indicate that the inserted protons contribute to a reduction in the band gap and a simultaneous improvement in electronic conductivity [114].Protons diffuse faster than magnesium in V 2 O 5 , and the preinserted protons decrease the Mg diffusion barrier.
Crafting heterostructures stands as another viable strategy for tailoring interfaces.An illustrative instance involves enhancing structural stability through bonds with carbon.Song et al. ingeniously suggested the formation of V-O-C chemical bonds to augment sodium-intercalation kinetics, resulting in an extraordinary lifespan of 3000 cycles at 5C [115].In this context, Na 5 V 12 O 32 is bonded to reduced graphene oxide.Computational analyses revealed a reduced energy barrier for sodium diffusion at the interface between Na 5 V 12 O 32 and carbon.
Given that the high capacity of V 2 O 5 has high structural instability, a promising avenue to enhance cycling stability involves integrating V 2 O 5 with bronzes like NaV 6 O 15 or Ca 0.17 V 2 O 5 within a composite electrode.Consequently, the V 2 O 5 /Ca 0.17 V 2 O 5 thin-film electrode in sodium cells exhibits reduced polarization, superior insertion kinetics, and enhanced cycling stability compared to those of standalone V 2 O 5 [116].It was observed that XRD reflections are displaced upon sodium intercalation, while the reflections of Ca 0.17 V 2 O 5 are not displaced, and consequently, it is inferred that V 2 O 5 is the host framework for sodium insertion, while Ca 0.17 V 2 O 5 is a "pillar" for structural stability.
Intercalation of the conductive polymer poly 3,4-ethylenedioxythiophene (PEDOT) into V 2 O 5 forms a PEDOT-V 2 O 5 heterostructure, expansion of the interlayer spacing from 0.78 to 1.03 nm, and easier Ca intercalation [112].Besides that, the inserted PEDOT links the V 2 O 5 layers together, avoiding the structural collapse during the electrochemical cycling.

Conclusions
In summary, although V 2 O 5 possesses exceptional properties for intercalation reactions, several drawbacks have prevented their implementation in more successful batteries.There is a consensus about the relevance of designing synthesis methods for controlling the microstructure and texture of the particles as a main path to optimize the electrochemistry of vanadium oxides.However, several of the synthesis methods employed in research laboratories may be not easy to scale up.On the other hand, the fabrication of nanostructures and nanoparticles with higher particle area exposed to the electrolyte solution can raise the apparent capacity to the pseudocapacitive contribution.
The mechanism of the intercalation of lithium into V 2 O 5 is very complex and involves the formation of many phases, and this issue is typically detrimental for achieving high reversibility in rechargeable batteries.Compared to that of lithium, the mechanism for intercalation of other cations remains less explored.The sodium-vanadium bronzes, Na x V 2 O 5 , comprise a wide variety of structural properties.It seems that larger cations, such as potassium, tend to be more irreversibly trapped in the framework of the vanadium oxide, but we cannot completely discard that the optimization of the vanadium oxide structure and microstructure render new electrode materials for suitable potassium-ion batteries.The efficiency of intercalation of divalent cations, magnesium ions, and calcium-ions is particularly governed by the solvent properties, the co-intercalation, and the shielding of the magnesium charge.Beyond univalent and divalent cations, the intercalation of aluminum (III) potentially may be very useful to provide higher capacities.The mechanism of the aluminum-ion batteries would be strongly dependent on the electrolyte and solvent (organic, aqueous, ionic liquid and hybrid organic-aqueous), and it has still been little explored.For example, the "aluminum-intercalation" could involve the intercalation of Al 3+ , protons, AlCl 4 − , and other ions, depending on the electrolyte solution and the host properties.The instability of vanadium compounds in certain electrolyte solutions can be a main drawback, although this could be fixed by using a mixture of solvents.Another option to improve the electrochemistry could be simultaneously employing several ions for intercalation.Thus, the optimization of the electrolyte solutions is a main task for advancing this field.It has been found that the replacement of a small amount of vanadium by another metal can have a very positive effect in the electrochemistry, and more efforts should be addressed in this way.
In summary, the main strategies to improve the electrochemistry of the V 2 O 5 electrode are reducing particle size, tailoring the particle morphology, modifying the interface's electrode/electrolyte, pre-intercalation or co-intercalation, creating heterostructures, and cation or anion substitution.Having in mind the large opportunities and the systems that remain unexplored or little studied, we think that, in addition to the tremendous experimental work that remains to be done before developing futures batteries, the DFT calculations could help to pre-select the most promising materials and microstructures for post-lithium batteries.

Nanomaterials 2023 ,
13,  x FOR PEER REVIEW 9 of 29 charge transfer kinetics during discharge.In the biphasic region (where γ'-V2O5 and γ-Na0.7V2O5coexist), Rct increases from 22 to 38 Ω, while a more pronounced increase (by a factor of 2) is observed in the 0.7 < x ≤ 0.97 solid-solution domain.This trend highlights the adverse impact of deep sodiation on electron transport, leading to a linear decrease in exchange current density with x, dropping from 1 mA cm −2 for γ'-V2O5 to only 0.4 mA cm −2 for γ-Na0.97V2O5.Turning attention to Figure5c, the evolution of the double-layer capacity reveals compelling insights.The Cdl parameter demonstrates an increase from approximately 18 µF cm −2 for γ'-V2O5 to about 30 µF cm −2 for Na0.97V2O5.Notably, this substantial 50% increase in Cdl during Na insertion contrasts with the more modest 15% reported increase during Li insertion in γ'-V2O5.This discrepancy is attributed to the larger volume change induced by sodiation in γ'-V2O5 compared to that induced by lithiation (17% vs. 4.4%).Furthermore, examples from other studies underscore the close correlation between Cdl and volume change in cathode materials, such as a 10% increase in Cdl for a 5% volume change in nanosized V2O5[52] and a constant Cdl for the Cr0.11V2O5.16mixed oxide with a limited volume change not exceeding 3.5%[53].

Figure 14 .
Figure 14.Voltage-capacity curves of V2O5 in aluminum aqueous cell (left).Schematic illustration of the two different intercalation sites of the VO5 units near the planar oxygen atom (site-a) and close to the apical oxygen atom (site-b) (right) [81].

Figure 14 .
Figure 14.Voltage-capacity curves of V 2 O 5 in aluminum aqueous cell (left).Schematic illustration of the two different intercalation sites of the VO 5 units near the planar oxygen atom (site-a) and close to the apical oxygen atom (site-b) (right) [81].

Figure 19 .
Figure 19.Rate tests and cycling performance of the electrodes at 200 mA g −1 [100].The cathod anode, and electrolyte are the pure and doped vanadium pentoxide, the Li metal, and LiPF6/EC/DMC, respectively.Image adapted from Ref. [100].

Figure 19 .
Figure 19.Rate tests and cycling performance of the electrodes at 200 mA g −1 [100].The cathodes, anode, and electrolyte are the pure and doped vanadium pentoxide, the Li metal, and the LiPF 6 /EC/DMC, respectively.Image adapted from Ref. [100].

Nanomaterials 2023 ,
13, x FOR PEER REVIEW 23 of 29Furthermore, the interface layer exhibits robustness owing to the decomposition of TEGDME and the formation of a protective film.This suppresses the dissolution of vanadium, resulting in an impressive cycle life of 1000 cycles.Mechanistic studies on the electrochemical reactions confirm that Na + in the original sodium vanadate undergoes deintercalation and is replaced by Mg 2+ during cycling.The reversible intercalation of Mg 2+ is facilitated by the shielding effect of water molecules.

Table 1 .
Specific capacity and capacity retention of cationic doped V 2 O 5 .