Synergistic Enhancement of Near-Infrared Emission in CsPbCl3 Host via Co-Doping with Yb3+ and Nd3+ for Perovskite Light Emitting Diodes

Perovskite nanocrystals (PeNCs) have emerged as a promising class of luminescent materials offering size and composition-tunable luminescence with high efficiency and color purity in the visible range. PeNCs doped with Yb3+ ions, known for their near-infrared (NIR) emission properties, have gained significant attention due to their potential applications. However, these materials still face challenges with weak NIR electroluminescence (EL) emission and low external quantum efficiency (EQE), primarily due to undesired resonance energy transfer (RET) occurring between the host and Yb3+ ions, which adversely affects their emission efficiency and device performance. Herein, we report the synergistic enhancement of NIR emission in a CsPbCl3 host through co-doping with Yb3+/Nd3+ ions for perovskite LEDs (PeLEDs). The co-doping of Yb3+/Nd3+ ions in a CsPbCl3 host resulted in enhanced NIR emission above 1000 nm, which is highly desirable for NIR optoelectronic applications. This cooperative energy transfer between Yb3+ and Nd3+ can enhance the overall efficiency of energy conversion. Furthermore, the PeLEDs incorporating the co-doped CsPbCl3/Yb3+/Nd3+ PeNCs as an emitting layer exhibited significantly enhanced NIR EL compared to the single doped PeLEDs. The optimized co-doped PeLEDs showed improved device performance, including increased EQE of 6.2% at 1035 nm wavelength and low turn-on voltage. Our findings highlight the potential of co-doping with Yb3+ and Nd3+ ions as a strategy for achieving synergistic enhancement of NIR emission in CsPbCl3 perovskite materials, which could pave the way for the development of highly efficient perovskite LEDs for NIR optoelectronic applications.


Introduction
The distinctive characteristics of metal halide perovskite nanocrystals (PeNCs), including their ability to tune bandgaps, exhibition of solution-phase photoluminescence (PL), and compatibility with diverse manufacturing techniques, make them highly promising for light-emitting applications.PeNC-based light-emitting diodes (PeLEDs) have been able to of 6.2%, which is approximately 2.8 times higher than that of devices based on undoped CsPbCl 3 PeNCs.These findings demonstrate the significant potential of Yb 3+ and Nd 3+ co-doping in enhancing the NIR emission and device performance of PeLEDs.

Synthesis of Single Doped and Co-Doped PeNCs
The CsPbCl 3 /Yb 3+ -doped PeNCs were synthesized using a modified hot-injection method described in a previous report [38].In a 25 mL three-neck flask, CsOAc (53.7 mg, 0.28 mmol), Pb(OAc) 2 3H 2 O (75.9 mg, 0.20 mmol), and Yb(OAc) 2 3H 2 O (4.9 mg, 0.02 mmol) were mixed with OA (0.5 mL), OAm (1.0 mL), and ODE (5.0 mL).The synthesis of co-doped CsPbCl 3 /Yb 3+ /Nd 3+ PeNCs involved varying the Nd-doping concentrations by adjusting the amount of NdBr 3 •6H 2 O (III) precursor used.The feeding amount of Yb(OAc) 2 •3H 2 O remained constant at 0.02 mmol, while the feeding amounts of NdBr 3 •6H 2 O (III) for the different samples were set at 0, 0.02, 0.04, 0.06, and 0.08 mmol, respectively.The solution was degassed at room temperature for 10 min and then heated to 120 • C for 1 h.During this heating process, all precursors completely dissolved, resulting in a transparent mixture.The reaction vessel was then refilled with N 2 and further heated to 200 • C. Once the solution reached this temperature, a swift injection of 0.20 mL TMS-Cl caused the solution to immediately become turbid.After 10 s, the solution was rapidly cooled to room temperature using an ice bath.

PeLED Device Fabrication
The fabrication of the PeLED utilized a modified method originally reported by Chiba et al. [39].The PeLED structures used in the experiment were as follows: a layer of indium tin oxide (ITO) with a thickness of 130 nm, followed by a layer of poly (3,4-ethylenedioxythiophene):polystyrene sulfonate (PEDOT:PSS) with a thickness of 40 nm.On top of that, there was a perovskite layer of CsPbCl 3 :Yb 3+ (or CsPbCl 3 :Yb 3+ /Nd 3+ ) with a thickness of 70 nm.Next, there was a layer of 1,3,5-tri(m-pyridyl-phenyl)benzene (TmPyPB) with a thickness of 30 nm, followed by a 1 nm-thick layer of LiF and a 100 nm-thick layer of aluminum (Al).To prepare the ITO-coated glass substrates, they were cleaned using a spin rinsing system and treated with deionized water and UV-ozone for 10 min.A solution of PEDOT:PSS with Nafion (55 wt %) was spin-coated onto the cleaned ITO-coated glass substrate and then annealed at 150 • C for 10 min, resulting in a 40 nm-thick layer of PEDOT:PSS.In a N 2 -filled glovebox, a layer of 1,3,5-tris(N-phenylbenzimidazol-2yl)benzene (TPBi) with a thickness of 30 nm, a 1 nm-thick layer of lithium quinolate (Liq), and a 100 nm-thick layer of aluminum (Al) were deposited onto the PEDOT:PSS/Nafion layer using thermal evaporation under high vacuum conditions (∼10−5 Pa).Finally, the fabricated PeLEDs with an active area of 2 mm 2 were encapsulated using epoxy glue and glass covers in the N 2 -filled glovebox.

Characterization
The morphology of the PeNCs synthesized in this study was investigated using highresolution transmission electron microscopy (TEM) with a JEOL JEM-F200 instrument.The chemical composition of the samples was analyzed using an Energy Dispersive Spectrometer (EDS) detector (Oxford X-MAX 65) connected to a transmission electron microscope.The size distribution histograms were obtained by analyzing the samples with a (Zetasizer Nano) (ZSE) instrument.X-ray diffraction (XRD) patterns were recorded using a (D8-Advance) instrument with Cu Kα (λ = 1.5406Å) radiation, covering the 2θ range of 10-60 • .The X-ray photoelectron spectroscopy (XPS) spectrum was analyzed using a (Thermo Fisher ESCALAB-670B Xi + ) instrument.The ultraviolet-visible (UV-vis) absorption spectra were measured using a (Perkin Elmer Lambda 950) spectrophotometer.Ultraviolet photoelectron spectroscopy (UPS) measurements were carried out with a (Thermo Fisher) Scientific Theta probe, utilizing a He I UV source (21.22 eV) under a high vacuum of approximately 10 −6 Pa and maintaining an operating voltage of −6 V.The photoluminescence (PL) spectra and time-resolved PL (TRPL) decay curves were collected using an (Edinburgh Instruments FLS-980) spectrometer equipped with a 450 W xenon lamp.The visible and near-infrared (NIR) luminescence signals were detected using a photomultiplier (PMT) (Hamamatsu, R928P) and a liquid nitrogen-cooled PMT (Hamamatsu, R5509-72), respectively.The absolute photoluminescence quantum yields (PLQYs) were measured using an integrating sphere (Edinburgh Instruments) connected to the FLS-980 spectrometer.The current density-voltage (J-V) characteristics of the PeLEDs were determined using a Keithley 2400 source meter, while the front-face electroluminescence (EL) radiance, EL spectra, and EQE were measured with a Photoresearch Spectra Scan spectrometer (PR745) simultaneously.

Results and Discussion
Transmission electron microscopy (TEM) measurements were performed to investigate the morphology and structure of CsPbCl 3 PeNCs doped with Yb 3+ and Nd 3+ ions.The samples were synthesized with a fixed concentration of Yb 3+ ions and varying concentrations of Nd 3+ ions ranging from (x = 0, 0.02, 0.04, 0.06, 0.08) TEM images are shown in Figure 1(a1-e1) CsPbCl 3 /Yb 3+ / x Nd 3+ revealed a structure similar to traditional CsPbCl 3 PeNCs [39].As the concentration of Nd 3+ ions increased in the CsPbCl 3 /Yb 3+ /Nd 3+ PeNCs, a slight reduction in the lattice size was observed which is consistent with XRD data.This can be attributed to the substitution of Yb 3+ /Nd 3+ ions for Pb 2+ ions in the CsPbCl 3 lattice.Since Pb 2+ ions have a larger ionic radius (1.19 Å) compared to Yb 3+ ions (0.90 Å) and Nd 3+ ions (1.02 Å), when Yb 3+ and Nd 3+ ions replace Pb 2+ ions in the lattice, the resulting lattice size contracts slightly.This is because the smaller Yb 3+ and Nd 3+ ions occupy the lattice positions that were previously occupied by larger Pb 2+ ions.The effect of Nd 3+ concentration on the lattice size is likely influenced by a combination of factors.These factors include the increased likelihood of Nd 3+ ions substituting for Pb 2+ ions and the increased interactions between Nd 3+ ions and the surrounding lattice as the concentration of Nd 3+ ions increase.The interplanar distances of the crystalline structure's (200) planes, as per cubic reference PDF #180366 [39], are illustrated in Figure 1(a2,a3).It is worth noting that the fixed concentration of Yb 3+ ions may also contribute to the lattice contraction.The substitution of Yb 3+ ions for Pb 2+ ions could also potentially lead to lattice contraction.Moreover, the presence of Yb 3+ ions can also influence the interaction between Nd 3+ ions and the lattice, thereby contributing to the overall lattice contraction [40].When the Nd 3+ concentration reaches x = 0.08, the cubic morphology of the CsPbCl 3 PeNCs begins to deform.This deformation indicates that additional doping beyond this concentration will have a substantial impact on the crystalline structure of the PeNCs.The histograms of the prepared PeNCs revealed an average particle size of approximately 14.3 nm to 9.7 nm with varying concentrations as shown in Figure 1(a3-e3).These TEM measurements provide insights into the morphology and structure of CsPbCl 3 PeNCs doped with Yb 3+ and Nd 3+ ions, which can aid in the development of PeLEDs with synergistic enhancement of near-infrared emission.X-ray diffraction (XRD) measurements were further conducted to examine and validate the previously performed TEM results.The XRD patterns of CsPbCl3/Yb 3+ /xNd 3+ (x = 0, 0.02, 0.04, 0.06, 0.08) were analyzed, revealing distinct diffraction peaks at specific 2θ angles.These angles were approximately 15.8°, 22.3°, 32.0°, and 40.0°, corresponding to the crystal planes (100), (101), and (200) of the cubic Pm̅ 3m CsPbCl3 space group and PDF#(18-0366), respectively [39]. Figure 2a displays the XRD peaks of the respective samples.As the concentration of Nd 3+ ions increased, the diffraction peaks shifted slightly to higher angles.This trend is consistent with the TEM measurements, which showed a slight change in lattice size as Nd 3+ concentration increased [40].When the Nd 3+ concentration reaches (x = 0.08), the diffraction peaks exhibit weakened intensity, indicating a significant decline in crystal quality and a transition to a non-cubic phase at higher levels of Nd 3+ doping.This observation suggests that nominal Nd 3+ doping preserves the cubic structure in comparison to higher levels of Nd 3+ doping.This is consistent with the TEM measurements, which showed a deformation of cubic morphology at this concentration.Table 1 provides the detailed positions of XRD peaks corresponding to different concentrations.
Table 1.The crystalline lattice constants of CsPbCl3/Yb 3+ /xNd 3+ PeNCs, Nd 3+ ion doping concentrations (x=0, 0.02, 0.04, 0.06, and 0.08), respectively.X-ray diffraction (XRD) measurements were further conducted to examine and validate the previously performed TEM results.The XRD patterns of CsPbCl 3 /Yb 3+ / x Nd 3+ (x = 0, 0.02, 0.04, 0.06, 0.08) were analyzed, revealing distinct diffraction peaks at specific 2θ angles.These angles were approximately 15.8 • , 22.3 • , 32.0 • , and 40.0 • , corresponding to the crystal planes (100), (101), and (200) of the cubic Pm3m CsPbCl 3 space group and PDF#(18-0366), respectively [39]. Figure 2a displays the XRD peaks of the respective samples.As the concentration of Nd 3+ ions increased, the diffraction peaks shifted slightly to higher angles.This trend is consistent with the TEM measurements, which showed a slight change in lattice size as Nd 3+ concentration increased [40].When the Nd 3+ concentration reaches (x = 0.08), the diffraction peaks exhibit weakened intensity, indicating a significant decline in crystal quality and a transition to a non-cubic phase at higher levels of Nd 3+ doping.This observation suggests that nominal Nd 3+ doping preserves the cubic structure in comparison to higher levels of Nd 3+ doping.This is consistent with the TEM measurements, which showed a deformation of cubic morphology at this concentration.Table 1 provides the detailed positions of XRD peaks corresponding to different concentrations.X-ray photoelectron spectroscopy (XPS) measurements were performed to investigate the surface chemistry of CsPbCl3 PeNCs doped withYb 3+/ xNd 3+ ions (where x = 0 and 0.06), as illustrated in Figure 2b.The XPS spectra of the co-doped sample exhibited distinct peaks corresponding to the core levels of Cs 3d, Pb 4f, Cl 2p, Br 3d, Yb 4d, and Nd 3d.This finding aligns with previous reports and provides compelling evidence for enhanced Pb-Yb-Nd interactions in the co-doped system [37].Specifically, the Yb 4d peaks were located at an approximate energy of 197 eV, confirming the successful incorporation of Yb 3+ ions at the surface level, as demonstrated in Figure 2c.Moreover, additional peaks corresponding to Nd 3d and Br 3d were observed at energies of 986 eV and 67.2 eV, respectively, exclusively in the co-doped sample [41].These peaks were absent in the spectra of the single doped samples, as illustrated in Figure 2d,e.Consequently, these findings strongly support the presence of Nd 3+ ions in PeNCs, directly correlated with the doping concentration, particularly in the x = 0.06 sample.Additional evidence of the surface chemistry of the CsPbCl3 PeNCs can be found in Figure S1a-c, which presents the XPS peaks corresponding to the core levels of Cs 3d, Pb 4f, and Cl 2p.

Spacing
The synergistic co-doping effect of Yb 3+ and Nd 3+ on CsPbCl3 PeNCs was further investigated using high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) imaging, elemental mapping, and energy-dispersive X-ray spectroscopy (EDS).Figure 3a displays the HAADF-STEM image of the co-doped PeNCs with an Nd 3+ concentration of (x = 0.06), revealing a cubic crystal structure, which is consistent X-ray photoelectron spectroscopy (XPS) measurements were performed to investigate the surface chemistry of CsPbCl 3 PeNCs doped withYb 3+/ x Nd 3+ ions (where x = 0 and 0.06), as illustrated in Figure 2b.The XPS spectra of the co-doped sample exhibited distinct peaks corresponding to the core levels of Cs 3d, Pb 4f, Cl 2p, Br 3d, Yb 4d, and Nd 3d.This finding aligns with previous reports and provides compelling evidence for enhanced Pb-Yb-Nd interactions in the co-doped system [37].Specifically, the Yb 4d peaks were located at an approximate energy of 197 eV, confirming the successful incorporation of Yb 3+ ions at the surface level, as demonstrated in Figure 2c.Moreover, additional peaks corresponding to Nd 3d and Br 3d were observed at energies of 986 eV and 67.2 eV, respectively, exclusively in the co-doped sample [41].These peaks were absent in the spectra of the single doped samples, as illustrated in Figure 2d,e.Consequently, these findings strongly support the presence of Nd 3+ ions in PeNCs, directly correlated with the doping concentration, particularly in the x = 0.06 sample.Additional evidence of the surface chemistry of the CsPbCl 3 PeNCs can be found in Figure S1a-c, which presents the XPS peaks corresponding to the core levels of Cs 3d, Pb 4f, and Cl 2p.
The synergistic co-doping effect of Yb 3+ and Nd 3+ on CsPbCl 3 PeNCs was further investigated using high-angle annular dark-field scanning transmission electron microscopy (HAADF-STEM) imaging, elemental mapping, and energy-dispersive X-ray spectroscopy (EDS).Figure 3a displays the HAADF-STEM image of the co-doped PeNCs with an Nd 3+ concentration of (x = 0.06), revealing a cubic crystal structure, which is consistent with the TEM photographs shown in Figure 1.To investigate the distribution of each element within the PeNCs, elemental mapping of Cs, Pb, Cl, Br, Yb, and Nd was performed.Cs, Pb, Br and Cl were found to be uniformly distributed throughout the PeNCs, as indicated by their consistent presence in the elemental maps.In contrast, Yb and Nd were predominantly localized in the center of the nanocrystals, as depicted in Figure 3b-h.The elemental mapping results confirm that the co-doped PeNCs contain all the intended elements, as the maps display the presence of Cs (red), Yb (green), Nd (yellow), Pb (blue), Cl (purple), and Br (cayenne) within the sample.Furthermore, EDS analysis was conducted to determine the atomic percentages of Cs, Pb, Cl, Br, Yb, and Nd of the corresponding samples.The EDS signals and corresponding atomic percentages are presented in Figure S2.The analysis revealed that the atomic percentages of Cs, Pb, Cl, Br, Yb, and Nd were 17%, 12%, 19.7%, 11%, 7.8%, and 4.5%, respectively.Based on the findings from the HAADF-STEM imaging, elemental mapping, and EDS measurements, it can be concluded that the co-doping of Yb 3+ and Nd 3+ ions into the CsPbCl 3 PeNCs was successful.
with the TEM photographs shown in Figure 1.To investigate the distribution of each element within the PeNCs, elemental mapping of Cs, Pb, Cl, Br, Yb, and Nd was performed.Cs, Pb, Br and Cl were found to be uniformly distributed throughout the PeNCs, as indicated by their consistent presence in the elemental maps.In contrast, Yb and Nd were predominantly localized in the center of the nanocrystals, as depicted in Figure 3b-h.The elemental mapping results confirm that the co-doped PeNCs contain all the intended elements, as the maps display the presence of Cs (red), Yb (green), Nd (yellow), Pb (blue), Cl (purple), and Br (cayenne) within the sample.Furthermore, EDS analysis was conducted to determine the atomic percentages of Cs, Pb, Cl, Br, Yb, and Nd of the corresponding samples.The EDS signals and corresponding atomic percentages are presented in Figure S2.The analysis revealed that the atomic percentages of Cs, Pb, Cl, Br, Yb, and Nd were 17%, 12%, 19.7%, 11%, 7.8%, and 4.5%, respectively.Based on the findings from the HAADF-STEM imaging, elemental mapping, and EDS measurements, it can be concluded that the co-doping of Yb 3+ and Nd 3+ ions into the CsPbCl3 PeNCs was successful.Next, we studied the optical characteristics and synergistic enhancement of near-infrared emission in the CsPbCl3 host through co-doping with Yb 3+ and Nd 3+ PeNCs.The emission spectra of PeNCs were examined at a wavelength of 370 nm, encompassing the visible and NIR regions.In the PL analysis of CsPbCl3/Yb 3+ /xNd 3+ (x = 0, 0.02, 0.04, 0.06, 0.08), the emission spectrum exhibits a prominent peak centered around 410 nm, which corresponds to the band-edge host emission of CsPbCl3, as depicted in Figure 4a.Additionally, a distinct peak is observed at approximately 950 nm, representing the NIR emission of Yb 3+ .Conversely, in the co-doped CsPbCl3 system with Yb 3+ /xNd 3+ (x = 0.02, 0.04, 0.06, and 0.08), the PL emission spectrum displays a host emission peak ranging from 425 nm to 437 nm, as illustrated in Figure 4a.Moreover, the PL emission spectra show a significant enhancement in the NIR emission from 970 nm to 1035 nm as the concentration of Nd 3+ increases as shown in Figure 4a.The enhancement is due to the increased population of excited Nd 3+ ions and improved energy transfer (ET) efficiency from CsPbCl3 to Yb 3+ facilitated by Nd 3+ ions, reducing undesired RET between the sensitizers and Yb 3+ ions leading to a redshift by 85 nm.The intensity of the single doped NIR peak is relatively low compared to the co-doped NIR peak as shown in Figure S3, indicating that the energy transfer process from CsPbCl3 to Yb 3+ is relatively inefficient in single-doped sample.The enhancement of the NIR emission is also accompanied by a decrease in the intensity of the Next, we studied the optical characteristics and synergistic enhancement of nearinfrared emission in the CsPbCl 3 host through co-doping with Yb 3+ and Nd 3+ PeNCs.The emission spectra of PeNCs were examined at a wavelength of 370 nm, encompassing the visible and NIR regions.In the PL analysis of CsPbCl 3 /Yb 3+ / x Nd 3+ (x = 0, 0.02, 0.04, 0.06, 0.08), the emission spectrum exhibits a prominent peak centered around 410 nm, which corresponds to the band-edge host emission of CsPbCl 3 , as depicted in Figure 4a.Additionally, a distinct peak is observed at approximately 950 nm, representing the NIR emission of Yb 3+ .Conversely, in the co-doped CsPbCl 3 system with Yb 3+ / x Nd 3+ (x = 0.02, 0.04, 0.06, and 0.08), the PL emission spectrum displays a host emission peak ranging from 425 nm to 437 nm, as illustrated in Figure 4a.Moreover, the PL emission spectra show a significant enhancement in the NIR emission from 970 nm to 1035 nm as the concentration of Nd 3+ increases as shown in Figure 4a.The enhancement is due to the increased population of excited Nd 3+ ions and improved energy transfer (ET) efficiency from CsPbCl 3 to Yb 3+ facilitated by Nd 3+ ions, reducing undesired RET between the sensitizers and Yb 3+ ions leading to a redshift by 85 nm.The intensity of the single doped NIR peak is relatively low compared to the co-doped NIR peak as shown in Figure S3, indicating that the energy transfer process from CsPbCl 3 to Yb 3+ is relatively inefficient in single-doped sample.The enhancement of the NIR emission is also accompanied by a decrease in the intensity of the band-edge emission of CsPbCl 3 , indicating that the ET process from CsPbCl 3 to Yb 3+ is more efficient in co-doped samples.Moreover, the PL analysis shows that as the concentration of Nd 3+ ions increase, the intensity of the NIR emission peak increases until a certain point, after which it starts to decrease.This behavior is attributed to the competing effect of the ET from Nd 3+ ions to Yb 3+ ions and the formation of nonradiative centers at high concentrations of Nd 3+ ions [42,43].Therefore, there is an optimal concentration of Nd 3+ ions for achieving the highest NIR emission intensity in co-doped CsPbCl 3 PeNCs.Furthermore, in order to thoroughly comprehend the ET mechanism from to Yb 3+ ions in Nd 3+ systems, we conducted an analysis of the absorption spectra of CsPbCl 3 /Yb 3+ / x Nd 3+ (x = 0, 0.02, 0.04, 0.06, 0.08) PeNCs samples.Moreover, we observed a distinct shoulder shift in the absorption spectra of the PeNCs, as illustrated in Figure 4b, which exhibited a correlation with the observed pattern in the PL spectra.This significant shift can likely be attributed to the intricate interactions occurring between the Nd 3+ ions and Yb 3+ ions within the material.These interactions facilitate efficient ET from the Yb 3+ ions, contributing to the overall ET process.These results suggest that the incorporation of Nd 3+ doping has a slight impact on the bandgap of the PeNCs.To validate this finding, we utilized a Tauc plot to calculate the bandgaps of each sample [44].The observed shoulder shift in the absorption spectra suggests a modification of the absorption edge and absorption onset, indicative of the bandgap modification.We have observed a slight decrease in the bandgap: the calculated bandgaps of the corresponding samples are 3.14 eV, 3.2 eV, 3.1 eV, 3.01 eV, and 3.1 eV, respectively.This further supports the influence of the Nd 3+ dopant on the electronic structure of the material as shown in Figure S4a-e.In order to investigate the influence of Nd doping on the ET kinetics of PeNCs, fluorescence decay measurements were performed.The time-resolved photoluminescence (TRPL) spectra of the samples were obtained at different Nd 3+ feeding ratios, as shown in Figure 4c.To determine the lifetimes of each sample, a bi-exponential decay equation was employed.
Nanomaterials 2023, 13, x FOR PEER REVIEW 9 of 15 The lifetime ( ) represents exciton radiative recombination, while the extended lifetime ( ) is associated with surface radiative defect recombination [35].According to Table S1, it is observed that with an increase in the Nd 3+ ratio from 0 to 0.08, the proportion of ( ) increases from 70.53% to 96.59%, while the contribution of ( ) decreases from 30.45% to 11.82%.This indicates the suppression of surface traps [45,46].The efficiency of energy transfer (ηET) to Yb 3+ ions can be determined using Equation (3).

𝜂
1 (3) The lifetime (B 1 ) represents exciton radiative recombination, while the extended lifetime (B 2 ) is associated with surface radiative defect recombination [35].According to Table S1, it is observed that with an increase in the Nd 3+ ratio from 0 to 0.08, the proportion of (B 1 ) increases from 70.53% to 96.59%, while the contribution of (B 2 ) decreases from 30.45% to 11.82%.This indicates the suppression of surface traps [45,46].The efficiency of energy transfer (η ET ) to Yb 3+ ions can be determined using Equation (3).
This equation utilizes the lifetimes' (τ and τ 0 ) emission in the presence and absence of Nd 3+ , respectively.It is evident that the efficiency of ET gradually increases with the rising Nd 3+ content, reaching above 60%.The effective ET for each sample is depicted in Figure S5.The remarkable ET can be attributed to two primary factors.Firstly, both Yb 3+ and Nd 3+ ions occupy space within the CsPbCl 3 host, resulting in a short distance between the Yb 3+ sensitizer and Nd 3+ activator.This proximity enhances the probability of ET occurring [37].The excited Nd 3+ states subsequently undergo radiative recombination processes, leading to the emission of photons and the enhancement of PLQY.As a result, PLQY in the visible region of the corresponding samples shows a significant increase from 40% to 90.5%, as illustrated in Figure 4d.
Figure 5a depicts the schematic representation Yb 3+ and Nd 3+ substituting Pb 2+ in the CsPbCl 3 host PeNCs.The chemical expressions of single and co-doped PeNCs are provided in Equations ( 4) and ( 5 The ET efficiency of the CsPbCl3/Yb 3+ /Nd 3+ perovskite system was further explained using an ET diagram, as depicted in Figure 5b.The ET diagram provides a graphical representation of the ET processes occurring within the system based on the experimental results.It was found that the NIR emission of Yb 3+ ions are significantly enhanced by the presence of Nd 3+ ions.The ET process from Nd 3+ to Yb 3+ is attributed to the efficient cross- The ET efficiency of the CsPbCl 3 /Yb 3+ /Nd 3+ perovskite system was further explained using an ET diagram, as depicted in Figure 5b.The ET diagram provides a graphical representation of the ET processes occurring within the system based on the experimental results.It was found that the NIR emission of Yb 3+ ions are significantly enhanced by the presence of Nd 3+ ions.The ET process from Nd 3+ to Yb 3+ is attributed to the efficient cross-relaxation process between the 4 F 3/2 level of Nd 3+ and the 2 F 5/2 level of Yb 3+ .This process results in the population of the 2 F 5/2 level of Yb 3+ , which then emits NIR radiation at 1035 nm.The enhancement of the NIR emission of Yb 3+ ions in the CsPbCl 3 :Yb 3+ /Nd 3+ perovskite was also observed in the external EQE measurements.The EQE of the co-doped perovskite was found to be higher than that of the CsPbCl 3 /Yb 3+ single-doped perovskite.This result indicates that the presence of Nd 3+ ions improve the ET efficiency, resulting in an increased NIR emission [37].The cross-relaxation process between Nd 3+ and Yb 3+ ions is an efficient ET mechanism in this system, which can be used to design and develop efficient NIR-emitting perovskite materials for optoelectronic applications [27]. To investigate the impact of doping on PeLED performance, CsPbCl 3 /Yb 3+ / x Nd 3+ (x = 0, 0.06) PeNCs were employed as the light-emitting layer for LED fabrication.Figure 6a,b illustrate the structure and energy diagram of the PeLED.The valence bands of (x = 0, 0.06) were determined through ultraviolet photoelectron spectroscopy (UPS) conducted in an open atmosphere (Figure S6a,b).It was observed that the energy position of (x = 0.06) slightly decreased due to the incorporation of the Nd 3+ dopant.The CsPbCl 3 /Yb 3+ /xNd 3+ (x = 0, 0.06) PeLEDs displayed EL wavelengths of approximately 950 nm and 1035 nm respectively, as indicated in Figure 6c.These emission wavelengths fall within the near-infrared range.The current density-luminance-voltage characteristics of the LEDs incorporating CsPbCl 3 /Yb 3+ / x Nd 3+ (x = 0, 0.06) dopants are presented in Figure 6d.Remarkably, the LED with the Yb 3+ / x Nd 3+ (0.06) dopant exhibited a lower turn-on voltage of only 3.0 V compared to the single Yb 3+ dopant, which had a turn-on voltage of 3.5 V.This reduction in voltage can be attributed to a decrease in the hole injection barrier between TFB and Yb 3+ / x Nd 3+ -doped CsPbCl 3 PeNCs.Figure 6e displays the measured EQE of the PeLEDs.It can be observed that the PeLEDs co-doped with Yb 3+ / x Nd 3+ (x = 0.06) exhibited higher EQE compared to those doped with Yb 3+ .The PeLEDs co-doped with Yb 3+ /Nd 3+ achieved a maximum EQE of 6.2%, which is approximately 2.38 times higher than the EQE of 2.6% obtained from the PeLEDs doped with Yb 3+ .The EQE reported here represents the highest value documented to date for wavelengths above 1000 nm.For comparison, Table 2 provides a compilation of EQE values for NIR OLEDs and PeLEDs reported in recent years.In addition, the PeLEDs co-doped with Yb 3+ /Nd 3+ demonstrated higher luminance intensity compared to the PeLEDs doped with Yb 3+ , as shown in Figure S6c.The PeLED with co-doping achieved a maximum luminance of 140 cd m −2 , which was significantly higher than that of the Yb 3+ dopant.Furthermore, the operational lifetime of the NIR LEDs is presented in Figure 6f.The PeLED with Yb 3+ /Nd 3+ dopant exhibited a longer lifetime compared to the PeLED based on the Yb 3+ dopant due to a low turn-on voltage.This low turn-on voltage not only enhances the energy efficiency of the device but also mitigates the potential for degradation over time, ultimately leading to a substantial extension of its operational lifetime.These improvements in device efficiency can be attributed to the synergistic effects of Yb 3+ and Nd 3+ ions, which enhance ET efficiency and the population of excited Nd 3+ ions.The enhanced EQE and NIR emission characteristics make these co-doped PeNCs promising candidates for applications such as photovoltaics and bioimaging, where efficient NIR emission is desired.
on voltage not only enhances the energy efficiency of the device but also mitigates th potential for degradation over time, ultimately leading to a substantial extension of it operational lifetime.These improvements in device efficiency can be attributed to the syn ergistic effects of Yb 3+ and Nd 3+ ions, which enhance ET efficiency and the population o excited Nd 3+ ions.The enhanced EQE and NIR emission characteristics make these co doped PeNCs promising candidates for applications such as photovoltaics and bioimag ing, where efficient NIR emission is desired.

Conclusions
In conclusion, the co-doping of Yb 3+ and Nd 3+ ions in CsPbCl 3 PeNCs has been demonstrated as an effective strategy to achieve synergistic enhancement of NIR emission.By incorporating Yb 3+ and Nd 3+ ions into the CsPbCl 3 host, the NIR emission above 1000 nm was significantly enhanced, making it highly desirable for NIR optoelectronic applications.The presence of Nd 3+ ions modified the emission spectrum, resulting in an 85 nm redshift.Furthermore, perovskite PeLEDs utilizing the Yb 3+ /Nd 3+ co-doped CsPbCl 3 PeNCs as the emitting layer exhibited substantially improved NIR EL compared to single-doped PeLEDs.The optimized co-doped PeLEDs demonstrated enhanced device performance, including increased EQE of 6.2% at a wavelength of 1035 nm.These findings highlight the potential of co-doping with Yb 3+ and Nd 3+ ions as a promising strategy for developing highly efficient PeLEDs for NIR optoelectronic applications.
ions, which can aid in the development of PeLEDs with synergistic enhancement of nearinfrared emission.

Table 2 .
Comparison of EQE values for as-investigated PeLED devices with NIR OLEDs and PeLED reported in recent years

Table 2 .
Comparison of EQE values for as-investigated PeLED devices with NIR OLEDs and PeLEDs reported in recent years.