One-Step Hydrothermal Synthesis of Nanostructured MgBi2O6/TiO2 Composites for Enhanced Hydrogen Production

A highly efficient MgBi2O6 (MBO)/TiO2 heterostructured photocatalyst for the evolution of H2 was successfully prepared using a one-step hydrothermal method. The phase structure, microstructure and optical properties of the MBO/TiO2 composites were investigated by various experimental techniques. A series of H2 production experiments were performed under visible light. The measured results indicated that the nanostructured MBO/TiO2 composite, with a stoichiometric molar ratio of MBO:TiO2 = 0.2%, displayed the best H2 production rate of 3413 μmol h−1 g−1. The excellent photocatalytic performance of the obtained composite material was due to the heterojunction formed between MBO and TiO2, which reduced the charge transfer resistance and accelerated the separation efficiency of the photogenerated electron–hole pairs. The reaction mechanism was also discussed in detail.


Introduction
The quick development of science and technology has facilitated peoples' lives, but has also resulted in an aggravated energy shortage and environmental deterioration. The development of clean fuels is one of the most important and urgent issues in the 21st century. In this regard, semiconductor photocatalysis technology is of great interest, since it can produce clean hydrogen by the direct utilization of solar energy. Since Fujishima and Honda first discovered that, under UV light irradiation, water can be decomposed to produce H 2 , using a TiO 2 electrode, numerous studies on TiO 2 have been conducted in detail to explain the reaction mechanism and to improve the photocatalytic efficiency [1,2]. TiO 2 has been considered the most widely investigated photocatalyst for H 2 production because it possesses some significant advantages, such as superior stability, non-toxicity, and low cost [3,4]. However, the more widespread application of TiO 2 in photocatalysis is greatly restricted, due to the low quantum yield and low efficiency of sunlight utilization, mainly resulting from its relatively wide bandgap of about 3.2 eV [5][6][7]. Thus, it is imminently necessary to probe novel compounds with outstanding photocatalytic properties under visible light irradiation [8,9].
In recent years, bismuth-based semiconductors, as one kind of new photocatalytic material, have been widely studied [10,11]. These compounds usually contain trivalent or pentavalent states of bismuth. It is worth noting that bismuth-based semiconductor photocatalysts possess a unique electronic structure. A continuously uplifted valence band, which reduces the band gap, is formed, due to the hybridization of O-2p and Bi-6s orbitals [12]. Bi 5+ has a different electronic structure from the trivalent bismuthate, with an empty 6s orbital, but still has a d10 blocking shell [13]. The light absorption range of these materials is expanded, due to this unique feature, which leads to improved photocatalytic performance. Among the bismuth-based compounds, MgBi 2 O 6 (MBO), with its trirutiletype structure, can be considered a visible light-responsive photocatalyst, which possesses a relatively small band gap of 1.8 eV [14]. However, compared with other well-studied photocatalysts, the photocatalytic efficiency of MBO is relatively low, which may be due to its low redox ability, mainly resulting from the narrow band gap.
Currently, one of the most valid and executable pathways to obtain a new material with significantly enhanced photocatalytic performance is to construct a semiconductor heterojunction, through combining semiconductors with different band gaps [15][16][17]. The synthesized heterostructured composites generally possess obviously enhanced photocatalytic activity, since the photoinduced electrons and holes are effectively separated and transferred to the heterojunction under the driving force of the internal electric field, and plenty of holes and electrons participating in redox reactions would be generated [18,19]. Many heterojunctions have been applied to promote photocatalytic reactions, and TiO 2based heterojunction photocatalysts, in particular, have been widely studied. For instance, Peng and co-authors reported that AgIn 5 S 8 /TiO 2 composites exhibited significantly enhanced photocatalytic performance in the production of H 2 because of the heterojunction structure built between AgIn 5 S 8 and TiO 2 [20]. Currently, MBO/TiO 2 composites have not been reported, and the improvement in photocatalytic H 2 production of TiO 2 , induced by the addition of MBO, needs to be investigated in detail.
In the present paper, we successfully synthesized the MBO/TiO 2 composite photocatalysts using a one-step hydrothermal method. Compared with pure MBO and TiO 2 , the photocatalytic performance of the MBO/TiO 2 composites clearly improved and the H 2 production rate under visible light significantly improved. The corresponding photocatalytic reaction mechanism was discussed further.

Synthesis of MBO Nanospheres and MBO/TiO 2 Photocatalysts
All synthetic chemicals were analytically pure and required no additional purification. Pure MBO was synthesized using a hydrothermal method. NaBiO 3 •5H 2 O (x = 0.025, 0.1, 0.2, 0.3, and 1.5 mmol) was dissolved in 30 mL of water with about 10 min of strong stirring to obtain solution A. MgCl 2 •2H 2 O (4x mmol) was dispersed in 30 mL of pure water and stirred for about 10 min to obtain solution B. Then, the orange mixed solution was obtained by mixing solution A with solution B and vigorously stirring for 30 min. Under the stirring state, 0.7987 g of TiO 2 (Degussa P25, Frankfurt, Germany) was gradually added to the mixed solution. The pH value of the mixture was kept at 8.5 by adding 4 mol/L of NaOH solution. The mixture was kept at 130 • C for 6 h in a 100 mL stainless steel autoclave. After this, the mixture in the autoclave was filtered to obtain the crude product. The final product was obtained via washing with pure water, as well as with absolute ethanol, several times, and then dried at 60 • C for 12 h. In this article, the molar ratios of MBO to TiO 2 were 0.01%, 0.05%, 0.2%, 0.6% and 3%, which were represented as 0.01MBO/TiO 2 , 0.05MBO/TiO 2 , 0.2MBO/TiO 2 , 0.6MBO/TiO 2 and 3MBO/TiO 2 , respectively.

Characterization of Samples
The X-ray diffractometer (XRD) (D8 Advance, Bruker, Billerica, MA, USA) was used to obtain the physical phase and used in the purity analysis of samples. The morphologies and microstructures of MBO, TiO 2 and MBO/TiO 2 were characterized using a field emission scanning electron microscope (FESEM) (FEI Quanta 450 FEG, Hillsboro, OR, USA) and a transmission electron microscope (TEM) (FEI Tecnai G20, Ther-moFisher, Waltham, MA, USA). The X-ray photoelectron spectroscopy (XPS) (Thermo ESCALAB 250Xi, ThermoFisher, Waltham, MA, USA) was employed to investigate the elemental compositions and oxidation states of the MBO/TiO 2 composites. The ultravioletvisible (UV-Vis) spectrometer (Puxi TU-1901, PERSEE, Beijing, China) was used to measure Nanomaterials 2022, 12, 1302 3 of 13 the UV-Vis diffuse reflectance spectroscopy (UV-Vis DRS) of the as-prepared samples, with barium sulfate as the reference. The photocatalytic analysis system (Labsolar-IIIAG, Perfect-light, Beijing, China) was used to examine the production of H 2 .

Photocatalytic Hydrogen Production Test
A 300 W Xe irradiation lamp was placed on the top of the photocatalytic hydrogen production reactor, which was connected to the Labsolar-III (AG) system. In a general test, 0.1 g of the heterostructured composite catalysts was added to the solution, with methanol serving as the sacrificial agent. The irradiation started to work after the air in the system was thoroughly eliminated. An online gas chromatograph (GC7900, Techcomp, Beijing, China) was used to periodically analyze the hydrogen generated from the photocatalytic reaction. The stability of the photocatalyst was checked throughout the experiment cycle. Following the same steps, it was tested 5 times under visible light. Before the reaction started, the system was evacuated and purified with nitrogen to make sure that there was no H 2 or O 2 .

Photoelectrochemical Studies
The photochemical tests were carried out using an electrochemical system (CHI-660B, Tianjin, China). A three-electrode system, with a Na 2 SO 4 electrolyte solution (0.1 M), was used in the measurements, in which the synthesized photocatalyst was firstly uniformly plated on the fluorine-doped SnO 2 conductive (FTO) glass sheet with ethanol ultrasonication, and then the binder was added dropwise, followed by drying the plated FTO glass sheet in an oven. After completion, it was removed and used as the working electrode. The saturated calomel electrode was used as the reference electrode and the platinum wire served as the counter electrode.

Phase Structure and Morphological Analysis
The crystallinity and composition of MBO, TiO 2 and the MBO/TiO 2 composites, synthesized at 130 • C with a range of molar ratios of MBO to TiO 2 , were measured using XRD, and are shown in Figure 1 Figure 1, and are well indexed to the standard XRD patterns (JCPDS No. 21-1276 and No.21-12). No other crystal phases were found from the XRD patterns of MBO/TiO 2 , indicating that the obtained composite material has high purity. It is obvious that, with the increase in the MBO component, the intensities of the XRD peaks of MBO become stronger and the characteristic diffraction peaks of TiO 2 would gradually become weaker. In addition, when the amount of added MBO is less than 0.6%, there are no diffraction peaks of MBO observed. The XRD patterns of 0.2 MBO/TiO 2 indicate that the structures of TiO 2 and MBO remain stable during the preparation of MBO/TiO 2 . The sharp and intense diffraction peaks indicate that the product crystallizes very well. The XRD results clearly demonstrate the formation of MBO/TiO 2 composites with good crystallinity via the hydrothermal method.
The measured morphologies and microstructures of pure MBO, TiO 2 and the prepared 0.2 MBO/TiO 2 composites from SEM are placed in Figure 2. It can be observed from   Figure 2f shows that MBO is in close contact with TiO 2 particles, with a size of about 30-120 nm. It can be found, from the measured lattice fringes of the composite shown in Figure 2g, that the tested lattice parameters are about 0.3516, 0.2187, and 0.3412 nm, and correspond to the (101) plane of anatase TiO 2 , the (111) plane of rutile TiO 2 [21], and the (110) plane of MBO, respectively. The interface between TiO 2 and MBO nanoparticles is clear, and can provide a reaction center for the reaction [22]. For the present study, only two components of MBO and TiO 2 formed in the heterojunction, without other impurities.  Figure 2f shows that MBO is in close contact with TiO cles, with a size of about 30-120 nm. It can be found, from the measured lattice fri the composite shown in Figure 2g, that the tested lattice parameters are about 0.2187, and 0.3412 nm, and correspond to the (101) plane of anatase TiO2, the (111 of rutile TiO2 [21], and the (110) plane of MBO, respectively. The interface betwee and MBO nanoparticles is clear, and can provide a reaction center for the reactio For the present study, only two components of MBO and TiO2 formed in the hete tion, without other impurities. To evaluate the elemental status and chemical composition of the prepared samples, the 0.2 MBO/TiO 2 catalyst was further measured using XPS. The full-scan spectrum of 0.2 MBO/TiO 2 , as presented in Figure 3a, confirms the existence of Ti, O, Mg, Bi and C elements. Generally, the adventitious hydrocarbons generated from the XPS instrument are considered to be the cause of the occurrence of the C1s peak at about 284.7 eV in the XPS full spectrum. Figure 3b shows that the peak at around 1303.8 eV can be assigned to the Mg1s peak of Mg 2+ [23]. The peaks at 529.5 eV and 531.2 eV in Figure 3c correspond to the lattice oxygen of the Ti-O/Bi-O bond in O1s, and the chemically adsorbed oxygen [21], respectively. The peaks at around 164.1 eV and 158.5 eV, presented in Figure 3d, correspond to Bi 4f 5/2 and Bi 4f 7/2 , confirming the presence of the Bi 5+ state [14,24]. In Figure 3e, there are two peaks at around 458.8 eV and 464.2 eV, which can be indexed to Ti 2p 3/2 and Ti 2p 1/2 , respectively [18], and confirm the presence of Ti 4+ cations in the MBO/TiO 2 composites [25]. As a result, the measured XPS results have proved the successful synthesis of the MBO/TiO 2 heterostructure. To evaluate the elemental status and chemical composition of the prepared sam ples, the 0.2 MBO/TiO2 catalyst was further measured using XPS. The full-scan spectrum of 0.2 MBO/TiO2, as presented in Figure 3a, confirms the existence of Ti, O, Mg, Bi and C elements. Generally, the adventitious hydrocarbons generated from the XPS instrumen are considered to be the cause of the occurrence of the C1s peak at about 284.7 eV in th XPS full spectrum. Figure 3b shows that the peak at around 1303.8 eV can be assigned t the Mg1s peak of Mg 2+ [23]. The peaks at 529.5 eV and 531.2 eV in Figure 3c correspon correspond to Bi 4f5/2 and Bi 4f7/2, confirming the presence of the Bi 5+ state [14,24]. In Figure 3e, there are two peaks at around 458.8 eV and 464.2 eV, which can be indexed to Ti 2p3/2 and Ti 2p1/2, respectively [18], and confirm the presence of Ti 4+ cations in the MBO/TiO2 composites [25]. As a result, the measured XPS results have proved the successful synthesis of the MBO/TiO2 heterostructure. The specific surface area is a factor that affects the catalytic activity of photocatalytic materials, and the specific surface area is generally measured using the N2 isothermal adsorption and desorption curves. As shown in Figure 4, the N2 isothermal adsorption and desorption curves of MBO, 0.2 MBO/TiO2 and TiO2 were 45.94 cm 2 g −1 , 59.69 cm 2 g −1 and 30.87 cm 2 g −1 , respectively. The measured results show that the prepared 0.2 The specific surface area is a factor that affects the catalytic activity of photocatalytic materials, and the specific surface area is generally measured using the N 2 isothermal adsorption and desorption curves. As shown in Figure 4, the N 2 isothermal adsorption and desorption curves of MBO, 0.2 MBO/TiO 2 and TiO 2 were 45.94 cm 2 g −1 , 59.69 cm 2 g −1 and 30.87 cm 2 g −1 , respectively. The measured results show that the prepared 0.2 MBO/TiO 2 composites with larger specific surface areas are expected to possess higher catalytic activity, in comparison with MBO and TiO 2 .

Light Absorption Spectra of MBO/TiO2 Catalysts
The absorption spectra of pure MBO, TiO2 and the 0.2 MBO/TiO2 composite photocatalysts were measured using a UV-Vis spectrophotometer, and are presented in Figure 5. We can observe that the absorption edges of pure TiO2 and MBO are at about 392 nm and 756 nm. A slight redshift of the absorption spectrum of the 0.2 MBO/TiO2 composite photocatalysts can be found in comparison with pure TiO2, and its light absorption band edge appears in the visible area greater than 400 nm, which is due to the sensitization of the narrow bandgap structure of MBO [26,27]. The following equation can be used to calculate the energy band gap (Eg) of MBO, TiO2 and MBO/TiO2: where F(R), v, h and A represent the diffuse absorption coefficient, optical frequency, Planck's constant and proportionality constant, respectively. The value of n is related to the transition type of the semiconductor (here, n = 2 corresponds to the indirect semiconductor in this article

Light Absorption Spectra of MBO/TiO 2 Catalysts
The absorption spectra of pure MBO, TiO 2 and the 0.2 MBO/TiO 2 composite photocatalysts were measured using a UV-Vis spectrophotometer, and are presented in Figure 5. We can observe that the absorption edges of pure TiO 2 and MBO are at about 392 nm and 756 nm. A slight redshift of the absorption spectrum of the 0.2 MBO/TiO 2 composite photocatalysts can be found in comparison with pure TiO 2 , and its light absorption band edge appears in the visible area greater than 400 nm, which is due to the sensitization of the narrow bandgap structure of MBO [26,27]. The following equation can be used to calculate the energy band gap (E g ) of MBO, TiO 2 and MBO/TiO 2 : where F(R), v, h and A represent the diffuse absorption coefficient, optical frequency, Planck's constant and proportionality constant, respectively. The value of n is related to the transition type of the semiconductor (here, n = 2 corresponds to the indirect semiconductor in this article). The E g values of 0.2 MBO/TiO 2 , MBO and TiO 2 are 3.1 eV, 1.65 eV and 3.2 eV, respectively. The calculated values for MBO and TiO 2 are similar to the previous reports [14,28]. The E g of 0.2 MBO/TiO 2 is slightly smaller than that of TiO 2 , which indicates that the MBO/TiO 2 composites would have a wider light response range, due to the addition of MBO with a small E g value.  [22]. Figure 6a clearly shows that the 0.2 MBO/TiO2 heterostructured composite has a much higher transient photocurrent density The measurements of the transient photocurrent response of pure TiO 2 , MBO and 0.2 MBO/TiO 2 composite materials, and the corresponding electrochemical impedance spectroscopy (EIS), are helpful for fully understanding the transmission and separation of photogenerated carriers in photocatalysts [22]. Figure 6a clearly shows that the 0.2 MBO/TiO 2 heterostructured composite has a much higher transient photocurrent density compared to pure MBO and TiO 2 . This proves that the formation of the MBO/TiO 2 heterojunction accelerates the separation of photogenerated charges and significantly enhances the photocatalytic performance of the composite catalyst. The EIS measurement is then performed to confirm the charge transfer resistance, and the arc radius of the EIS plots can reveal the response rate. The separation of the electron-hole pair and the photocatalytic reaction is faster when the radius of the impedance spectrum arc is smaller. The impedance plot presented in Figure 6b shows that the 0.2 MBO/TiO 2 heterostructured composite has a semicircle with a smaller arc, in comparison with pure MBO and TiO 2 , suggesting that the addition of MBO to TiO 2 is beneficial for separating the electron-hole pairs, owing to the reduction in charge transfer resistance; this facilitates the obvious enhancement in the photocatalytic performance of the 0.2 MBO/TiO 2 composite. The normalized plot of the transient photocurrent presented in Figure 6c shows that the transient time constant of the 0.2 MBO/TiO 2 composite is higher than that of MBO and TiO 2 , indicating a slower recombination rate [29].

Hydrogen Production Performance
The measurements of hydrogen production were carried out by adding 0.1 g of catalyst powder to an 80 mL solution, consisting of 20 mL of methanol and 60 mL of deionized water. Figure 7a shows the amount of photocatalytic hydrogen production for the MBO/TiO2 composite catalysts under 5 h of visible light irradiation. We can observe that the hydrogen production gradually increases and then decreases with the increase in MBO content. The best loading amount of MBO is about 0.2% and the maximal H2 production is 15,007 μmol·g −1 in 5 h, which is nearly 80 times higher than the hydrogen pro-

Hydrogen Production Performance
The measurements of hydrogen production were carried out by adding 0.1 g of catalyst powder to an 80 mL solution, consisting of 20 mL of methanol and 60 mL of deionized water. Figure 7a shows the amount of photocatalytic hydrogen production for Nanomaterials 2022, 12, 1302 9 of 13 the MBO/TiO 2 composite catalysts under 5 h of visible light irradiation. We can observe that the hydrogen production gradually increases and then decreases with the increase in MBO content. The best loading amount of MBO is about 0.2% and the maximal H 2 production is 15,007 µmol·g −1 in 5 h, which is nearly 80 times higher than the hydrogen production of pure TiO 2 . Figure 7a also shows that pure MBO is not capable of photocatalytic H 2 evolution. The decrease in H 2 production in the MBO/TiO 2 composites, with a higher MBO content, is probably due to the weakness of catalytic activity on the surface of TiO 2 , since the incident light is blocked and the production of electrons by TiO 2 is suppressed because of the high loading amount of MBO [30][31][32][33]. The results of the hydrogen production rate of MBO/TiO 2 are shown in Figure 7b. The hydrogen production rate of 0.2 MBO/TiO 2 is 3413 µmolh −1 g −1 , which clearly exceeds that of the samples with other components and single phases. The cycle measurements for MBO/TiO 2 were carried out to confirm the stability of the photocatalyst. The results presented in Figure 7c show that, after the fourth cycle, the H 2 production is 12,275 µmol·g −1 , and is about 82% of the first cycle. This indicates the good stability of the 0.2 MBO/TiO 2 photocatalyst. The possible reason for the slight decrease in hydrogen production is that the HCOOH formed by the decomposition of CH 3 OH slightly stimulates the activity of the photocatalyst and affects the sensitivity of the photocatalyst to light. Moreover, it can be found from Table 1 that the hydrogen production activity of MBO/TiO 2 is comparable to that of other TiO 2 -based heterojunctions, as reported in previous literature.     The potential mechanism of photocatalytic hydrogen production for MBO/TiO2 composite catalysts was investigated further, and can be clearly described using a schematic energy band diagram, as shown in Figure 9. First, the edge potential of the conduction band (ECB) and that of the valence band (EVB) for MBO and TiO2 can be calculated using the following equations [25]: Among them, χ is the electronegativity of the semiconductor (6.28 eV for MBO and 5.81 eV for TiO2). Ee (approximatively 4.5 eV) represents the energy of the free electrons in the standard hydrogen electrode [32]. After calculation, the values of EVB and ECB are 0.96 and 2.61 eV for MBO, and −0.27 and 2.9 eV for TiO2, respectively. The potential mechanism of photocatalytic hydrogen production for MBO/TiO 2 composite catalysts was investigated further, and can be clearly described using a schematic energy band diagram, as shown in Figure 9. First, the edge potential of the conduction band (ECB) and that of the valence band (EVB) for MBO and TiO 2 can be calculated using the following equations [25]:  Based on the above results and considerations, we proposed a possible hydrogen production reaction mechanism for the MBO/TiO2 composite photocatalytic system. Since the bottom of the conduction band of TiO2 is higher than MBO, the corresponding top of the valence band is lower than MBO, as shown in Figure 9. On the one hand, when the material is exposed to light, the electrons in the valence band are excited to transfer to the conduction band, and, at the same time, the holes in the valence band are generated [38]. Due to the potential difference between them, the photogenerated electrons are transferred from the conduction band of TiO2 to the conduction band of MBO, and they react with water to generate H2 and OHon the surface of the catalyst. On the other hand, the holes in the valence band can directly oxidize water to release O2 and H + . At the same time, the sacrificial agent methanol will react with OHand H + , under the action of h + , to produce CO2 and H2O, and other non-polluting substances. However, CO2 is easily soluble in water and is difficult to detect. The heterojunction is an important basis for photocatalysis. We believe that the MBO/TiO2 composite photocatalytic system can exhibit excellent photocatalytic activity, due to the rapid separation of photogenerated electron-hole pairs, which is accelerated by the MBO/TiO2 heterojunction.

Conclusions
A new MBO/TiO2 heterojunction composite material, with the highest efficiency for photocatalytic hydrogen evolution, was prepared successfully through a one-step hydrothermal method. The photocatalytic performance of the MBO/TiO2 composite is clearly superior to that of the single-component material, under visible light. Particularly, it exhibits excellent stability and the highest efficiency of hydrogen production when the molar ratio of MBO to TiO2 is 0.2%. From the test results and the above-mentioned discussion of the photocatalytic mechanism, it is evident that the separation and transfer of photoinduced electrons and holes are promoted by the formation of the MBO/TiO2 nn heterojunction, while the electron-hole pairs hardly recombine, which is a key factor in improving the photocatalytic activity.   Among them, χ is the electronegativity of the semiconductor (6.28 eV for MBO and 5.81 eV for TiO 2 ). E e (approximatively 4.5 eV) represents the energy of the free electrons in the standard hydrogen electrode [32]. After calculation, the values of E VB and E CB are 0.96 and 2.61 eV for MBO, and −0.27 and 2.9 eV for TiO 2 , respectively.
Based on the above results and considerations, we proposed a possible hydrogen production reaction mechanism for the MBO/TiO 2 composite photocatalytic system. Since the bottom of the conduction band of TiO 2 is higher than MBO, the corresponding top of the valence band is lower than MBO, as shown in Figure 9. On the one hand, when the material is exposed to light, the electrons in the valence band are excited to transfer to the conduction band, and, at the same time, the holes in the valence band are generated [38]. Due to the potential difference between them, the photogenerated electrons are transferred from the conduction band of TiO 2 to the conduction band of MBO, and they react with water to generate H 2 and OHon the surface of the catalyst. On the other hand, the holes in the valence band can directly oxidize water to release O 2 and H + . At the same time, the sacrificial agent methanol will react with OHand H + , under the action of h + , to produce CO 2 and H 2 O, and other non-polluting substances. However, CO 2 is easily soluble in water and is difficult to detect. The heterojunction is an important basis for photocatalysis. We believe that the MBO/TiO 2 composite photocatalytic system can exhibit excellent photocatalytic activity, due to the rapid separation of photogenerated electron-hole pairs, which is accelerated by the MBO/TiO 2 heterojunction.

Conclusions
A new MBO/TiO 2 heterojunction composite material, with the highest efficiency for photocatalytic hydrogen evolution, was prepared successfully through a one-step hydrothermal method. The photocatalytic performance of the MBO/TiO 2 composite is clearly superior to that of the single-component material, under visible light. Particularly, it exhibits excellent stability and the highest efficiency of hydrogen production when the molar ratio of MBO to TiO 2 is 0.2%. From the test results and the above-mentioned discussion of the photocatalytic mechanism, it is evident that the separation and transfer of photoinduced electrons and holes are promoted by the formation of the MBO/TiO 2 n-n heterojunction, while the electron-hole pairs hardly recombine, which is a key factor in improving the photocatalytic activity.