Rubrene-Directed Structural Transformation of Fullerene (C60) Microsheets to Nanorod Arrays with Enhanced Photoelectrochemical Properties

One-dimensional (1D) nanostructures possess huge potential in electronics and optoelectronics, but the axial alignment of such 1D structures is still a challenging task. Herein, we report a simple method that enables two-dimensional (2D) C60 microsheets to evolve into highly ordered nanorod arrays using rubrene as a structure-directing agent. The structural transformation is accomplished by adding droplets of rubrene-m-xylene solution onto C60 microsheets and allowing the m-xylene solvent to evaporate naturally. In sharp contrast, when rubrene is absent from m-xylene, randomly oriented C60 nanorods are produced. Spectroscopic and microscopic characterizations collectively indicate a rather plausible transformation mechanism that the close lattice match allows the epitaxial growth of rubrene on C60 microsheets, followed by the reassembly of dissolved C60 along the aligned rubrene due to the intermolecular charge-transfer (CT) interactions, leading to the formation of ordered nanorod arrays. Due to the aligned structures and the CT interactions between rubrene and C60, the photocurrent density of the nanorod arrays is improved by 31.2% in the UV region relative to the randomly oriented counterpart. This work presents a facile and effective strategy for the construction of ordered fullerene nanorod arrays, providing new ideas for the alignment of fullerene and other relevant organic microstructures.


Introduction
The peculiar and fascinating properties of one-dimensional (1D) nanostructures have enabled the widespread applications in diverse fields such as electronics, photonics, energy, and so forth [1]. Of particular interest are 1D nanostructures made of π-conjugated molecules due to their mechanical flexibility, solution processability, and minimized defects [2,3]. In light of this, 1D organic nanostructures hold great promise in next-generation electronic and optoelectronic devices. For the purpose of on-demand photons/electrons transport on the macroscale, it is strongly desired that the 1D nanostructures are unidirectionally oriented. Otherwise, the anisotropic feature disappears when they are randomly aligned [4][5][6][7][8].
Several approaches have been developed for aligning 1D organic nanostructures into highly ordered arrays, including Langmuir-Blodgett (LB), dip-coating, spin-coating, templating, and printing techniques [9][10][11][12][13][14][15]. However, these methods often involve tedious and complicated procedures to fabricate organic molecules. For example, in spin coating or printing methods, regioselective substrate patterning by altering the surface wettability is required to deposit the precursor solution onto these modified regions. After solvent evaporation, organic building blocks assemble into 1D aligned nanostructures [12,15]. The LB method involves the introduction of external forces for aligning 1D nanostructures, whereas in the templating method, the utilized templates need to be removed in the

Materials and Methods
Materials: Pristine C60 was synthesized by the direct-current arc discharge method and isolated using high-performance liquid chromatography. Figure S1 displays the laser desorption ionization time-of-flight (LDI-TOF) mass spectrum of as-obtained C60 (>99.9%). Rubrene powder (>98%) was purchased from Beijing InnoChem Science & Technology Co., Ltd., Beijing, China. Analytical-grade toluene, m-xylene, isopropyl alcohol (IPA), and tert-butanol (TBA) were purchased from Beijing Chemical Ltd., China. All the chemicals were used without further purification.
Preparation of C60 microsheets (C60MSs): C60MSs were synthesized using the liquidliquid precipitation (LLIP) method [34]. Typically, 12.5 mg of C60 was dissolved in 10 mL of toluene by ultrasonication for 2 h to obtain a C60-toluene solution (1.25 mg mL −1 ). One milliliter of the C60-toluene solution was rapidly injected into a 10 mL glass vial preloaded with 3 mL of TBA, resulting in a turbid mixture. C60MSs were formed after keeping the mixture for 12 h without any disturbance at 25 °C, and then recovered by centrifugation and vacuum drying at 60 °C for 12 h.
Preparation of C60-rubrene nanorod arrays (C60-RNRAs) and C60 nanorods (C60NRs): C60-RNRAs and C60NRs were prepared by the structural transformation of C60MSs. Typically, 0.5 mg of C60MSs was dispersed in 20 μL of IPA and transferred onto a silica substrate (3 cm × 3 cm) to form a uniform C60MSs thin film upon IPA evaporation. The thin film was dried under vacuum at 60 °C for 8 h to remove residual IPA. Subsequently, 60 μL of rubrene-m-xylene solution (1 mg mL −1 ) was dribbled onto the silica substrate to

Materials and Methods
Materials: Pristine C 60 was synthesized by the direct-current arc discharge method and isolated using high-performance liquid chromatography. Figure S1 displays the laser desorption ionization time-of-flight (LDI-TOF) mass spectrum of as-obtained C 60 (>99.9%). Rubrene powder (>98%) was purchased from Beijing InnoChem Science & Technology Co., Ltd., Beijing, China. Analytical-grade toluene, m-xylene, isopropyl alcohol (IPA), and tert-butanol (TBA) were purchased from Beijing Chemical Ltd., China. All the chemicals were used without further purification.
Preparation of C 60 microsheets (C 60 MSs): C 60 MSs were synthesized using the liquidliquid precipitation (LLIP) method [34]. Typically, 12.5 mg of C 60 was dissolved in 10 mL of toluene by ultrasonication for 2 h to obtain a C 60 -toluene solution (1.25 mg mL −1 ). One milliliter of the C 60 -toluene solution was rapidly injected into a 10 mL glass vial preloaded with 3 mL of TBA, resulting in a turbid mixture. C 60 MSs were formed after keeping the mixture for 12 h without any disturbance at 25 • C, and then recovered by centrifugation and vacuum drying at 60 • C for 12 h.
Preparation of C 60 -rubrene nanorod arrays (C 60 -RNRAs) and C 60 nanorods (C 60 NRs): C 60 -RNRAs and C 60 NRs were prepared by the structural transformation of C 60 MSs. Typically, 0.5 mg of C 60 MSs was dispersed in 20 µL of IPA and transferred onto a silica substrate (3 cm × 3 cm) to form a uniform C 60 MSs thin film upon IPA evaporation. The thin film was dried under vacuum at 60 • C for 8 h to remove residual IPA. Subsequently, 60 µL of rubrene-m-xylene solution (1 mg mL −1 ) was dribbled onto the silica substrate to cover the C 60 MSs film and then naturally dried at 25 • C to generate C 60 -RNRAs. In contrast, C 60 NRs were prepared by adding 60 µL of m-xylene without rubrene. All the experimental steps were conducted at 25 • C in air atmosphere.
Photoelectrochemical measurements: Photoelectrochemical measurements of the samples were conducted through a CHI 660E electrochemical workstation (CH Instruments Inc., Shanghai, China) at 25 • C. A 500 W xenon lamp (Saifan Photoelectronic Co., Beijing, China) was utilized as the light source with filters of 400-760 nm and 350 nm to obtain the light in the corresponding ranges. A standard three-electrode system was utilized for the measurements. Two milligrams of C 60 MSs, C 60 NRs, or C 60 -RNRAs was dispersed in 4 mL of deionized water and gently agitated to form uniform suspensions, respectively. Next, 2 µL of the as-obtained suspensions were dribbled on an indium tin oxide (ITO) glass (5 mm × 60 mm) to form thin films (5 mm × 5 mm), which were used as the working electrodes. A Pt wire and an Ag/AgCl electrode were used as the counter and reference electrodes, respectively. All the measurements were performed in 0.1 M KCl at a bias voltage of 1 V. The electrolyte solution was bubbled with Ar for 30 min to remove the oxygen, and all the tests were conducted in an Ar atmosphere.
Characterizations: The morphology of the above samples was observed using a Nova NanoSEM 450 field-emission scanning electron microscope (FESEM, FEI, Eindhoven, Netherlands). Transmission electron microscopic (TEM) images were obtained by a Talos F200X G2 electron microscope (FEI, Hillsboro, OR, USA). Powder X-ray diffraction (PXRD) patterns were collected on an Empyrean diffractometer (PANalytical B.V., Eindhoven, Netherlands) with Cu Kα radiation. The d spacings of the planes were calculated according to XRD patterns and the Bragg equation (2dsinθ = nλ). Raman and photoluminescence spectra were measured on a Horiba JobinYvon LabRAM HR800 spectrometer (Horiba Group, Paris, France) using a 532 nm green laser. Fourier-transform infrared spectroscopy (FT-IR) was performed on a Bruker VERTEX 70 FTIR spectrometer (Bruker, Karlsruhe, Germany). The mass spectrum of C60-RNRAs was acquired on a Bruker MI-CROFLEX MALDI-TOF. Ultraviolet-visible (UV-vis) spectra (Bruker, Karlsruhe, Germany) were recorded on a SolidSpec-3700 spectrometer (Shimadzu, Kyoto, Japan). Thermogravimetric (TG) analysis was carried out in N2 at a heating rate of 10 • C/min on a TGA8000 (PerkinElmer, WA, USA).

Results and Discussion
C 60 MSs prepared by the LLIP method present a rhombic shape (Figure 2(a1,a2)). TEM image reveals the loosely packed character of C 60 MSs (Figure 2(a3)). HRTEM image of C 60 MSs shows its crystalline structure with a lattice spacing of 0.41 nm, which matches well with that of the (222) plane of the face-centered cubic (fcc) C 60 (a = 1.410 nm) [35,36], indicating that the ordered stacking of C 60 molecules along the [111] direction forms the rhombus sheets, whose top/bottom surfaces are exposed by the (222) plane ( Figure 2(a4)). As a good solvent of C 60 , m-xylene is known to generate rod-shaped structures by the LLIP [37,38]. In light of this, m-xylene is adopted to trigger the potential microsheetsto-nanorods transformation. Figure 2(b1,b2) show that C 60 MSs are indeed successfully transformed into C 60 NRs, but the alignment of nanorods is completely random. Moreover, the aggregated nanorods in C 60 NRs are observed under TEM (Figure 2(b3)), which displays a lattice spacing of 0.32 nm, corresponding to the (003) plane of the hexagonal close packed (hcp) C 60 (a = 2.376, c = 1.008 nm) (Figure 2(b4)) [37].
We then select rubrene as a structure-directing agent, and the reasons are discussed in the following context. After adding a solution of rubrene in m-xylene instead of only m-xylene to C 60 MSs, C 60 MSs are readily evolved into C 60 -RNRAs, as discerned in Figures 2(c1,c2) and S2, showing unidirectionally oriented nanorod arrays. More specifically, the orientation of nanorods is parallel to one of the diagonals that connects two obtuse angles of the rhomboid. After sonicating the resulting C 60 -RNRAs in water for 30 min, no other types of structures but dispersed nanorods are observed ( Figure S3), indicating the complete transformation of all the microsheets into nanorods rather than only the surface part. This is supported by the TEM image shown in Figure 2(c3). HRTEM image of one single nanorod in C 60 -RNRAs presents lattice spacings of 0.78 and 0.39 nm, which match well with those of the (210) plane of the hcp C 60 and the (400) plane of the orthorhombic rubrene (a = 1.540 nm, b = 0.748 nm, c = 2.792 nm), respectively (Figure 2(c4)) [39]. These results reveal that crystalline rubrenes are embedded into the nanorods and stacked separately with the C 60 molecules inside C 60 -RNRAs.
Powder XRD patterns of relevant samples are shown in Figure 3. C 60 MSs present the same fcc structure as the pristine C 60 powder [35], whereas C 60 NRs formed by the transformation of C 60 MSs after the evaporation of m-xylene exhibit a different hcp structure (a = 2.376 nm, c = 1.008 nm). Moreover, C 60 -RNRAs include both the hcp C 60 NRs and the orthorhombic structured rubrene (a = 1.560 nm, b = 0.736 nm, c = 2.768 nm), again indicating the existence of rubrene crystals inside C 60 -RNRAs. Note that the hcp structure Nanomaterials 2022, 12, 954 5 of 13 of C 60 and orthorhombic structure of rubrene are also obtained by simply evaporating the C 60 -m-xylene and rubrene-m-xylene solutions, respectively ( Figure S4) [37,40]. Moreover, according to the full-width at half-maximum (FWHM) values for (210) and (311) peaks of hcp C 60 in C 60 NRs and C 60 -RNRAs ( Figure S5), smaller FWHM values are obtained for C 60 -RNRAs, suggesting their higher crystallinity than C 60 NRs [41]. This is supported by the TEM image shown in Figure 2c3. HRTEM image of one single nanorod in C60-RNRAs presents lattice spacings of 0.78 and 0.39 nm, which match well with those of the (210) plane of the hcp C60 and the (400) plane of the orthorhombic rubrene (a = 1.540 nm, b = 0.748 nm, c = 2.792 nm), respectively ( Figure 2c4) [39]. These results reveal that crystalline rubrenes are embedded into the nanorods and stacked separately with the C60 molecules inside C60-RNRAs. Figure 2. SEM, TEM, and HRTEM images of C60MSs (a1-a4), C60NRs (b1-b4), and C60-RNRAs (c1-c4). Insets of (b2) and (c2) are magnified SEM images. Insets of (a4,b4,c4) are the corresponding electron diffraction patterns (The arrows point to the corresponding planes).
FTIR spectra of C 60 MSs, C 60 NRs, and C 60 -RNRAs are shown in Figure 4a. All three samples show typical absorption bands of C 60 at 1429, 1182, 574, and 526 cm −1 [42]. The absorption bands of C 60 MSs at 1461 and 728 cm −1 can be assigned to the C-H bending vibration in the benzene ring and C-H wagging vibration in methyl of toluene, respectively, indicating the presence of toluene molecules inside C 60 MSs [43]. The spectra of C 60 NRs and C 60 -RNRAs also contain the major absorption band of toluene at 1461 cm −1 , indicating toluene molecules remain in the lattices even after the structural transformation. Moreover, Nanomaterials 2022, 12, 954 6 of 13 the absorption bands at 1375 and 765 cm −1 of C 60 NRs and C 60 -RNRAs can be ascribed to C-C stretching vibration and C-H bending vibration in the benzene ring of m-xylene, respectively, suggesting the existence of m-xylene molecules in C 60 NRs and C 60 -RNRAs [44]. More importantly, additional FT-IR bands at 720 and 700 cm −1 in C 60 -RNRAs are observed. According to the FT-IR spectrum of pristine rubrene ( Figure S6a), these two bands shall be assigned to specific vibrations of rubrene molecules, which implies the presence of rubrene in C 60 -RNRAs [45]. Raman spectra are also acquired to provide further information. As shown in Figure 4b, additional Raman peaks at 211 and 1328 cm −1 detected in C 60 -RNRAs, in comparison to C 60 NRs and C 60 MSs, can be assigned to rubrene ( Figure S6b) [46]. LDI-TOF mass spectrum of C 60 -RNRAs dissolved in CS 2 also clearly shows peaks at m/z of 532 and 720, originating from rubrene and C 60 , respectively (Figure 4c). These results unambiguously confirm the presence of rubrene in C 60 -RNRAs.
Nanomaterials 2022, 12, x FOR PEER REVIEW 6 of 13 and orthorhombic structure of rubrene are also obtained by simply evaporating the C60m-xylene and rubrene-m-xylene solutions, respectively ( Figure S4) [37,40]. Moreover, according to the full-width at half-maximum (FWHM) values for (210) and (311) peaks of hcp C60 in C60NRs and C60-RNRAs ( Figure S5), smaller FWHM values are obtained for C60-RNRAs, suggesting their higher crystallinity than C60NRs [41]. FTIR spectra of C60MSs, C60NRs, and C60-RNRAs are shown in Figure 4a. All three samples show typical absorption bands of C60 at 1429, 1182, 574, and 526 cm −1 [42]. The absorption bands of C60MSs at 1461 and 728 cm −1 can be assigned to the C-H bending vibration in the benzene ring and C-H wagging vibration in methyl of toluene, respectively, indicating the presence of toluene molecules inside C60MSs [43]. The spectra of C60NRs and C60-RNRAs also contain the major absorption band of toluene at 1461 cm −1 , indicating toluene molecules remain in the lattices even after the structural transformation. Moreover, the absorption bands at 1375 and 765 cm −1 of C60NRs and C60-RNRAs can be ascribed to C-C stretching vibration and C-H bending vibration in the benzene ring of m-xylene, respectively, suggesting the existence of m-xylene molecules in C60NRs and C60-RNRAs [44]. More importantly, additional FT-IR bands at 720 and 700 cm −1 in C60-RNRAs are observed. According to the FT-IR spectrum of pristine rubrene ( Figure S6a), these two bands shall be assigned to specific vibrations of rubrene molecules, which implies the presence of rubrene in C60-RNRAs [45]. Raman spectra are also acquired to provide further information. As shown in Figure 4b, additional Raman peaks at 211 and 1328 cm −1 detected in C60-RNRAs, in comparison to C60NRs and C60MSs, can be assigned to rubrene ( Figure S6b) [46]. LDI-TOF mass spectrum of C60-RNRAs dissolved in CS2 also clearly shows peaks at m/z of 532 and 720, originating from rubrene and C60, respectively (Figure 4c). These results unambiguously confirm the presence of rubrene in C60-RNRAs.
TG analysis of C60 powder, C60MSs, C60NRs, and C60-RNRAs are then carried out to determine the solvent contents of these materials (Figure 4d). Compared to C60 powder, the weight loss of C60MSs beginning at approximately 115 °C is about 0.8 wt%, which corresponds to the contained toluene molecules. In contrast, weight losses of C60NRs and C60-RNRAs begin at approximately 55 °C, and amount to 4.8 wt% and 5.2 wt%, respectively, equal to the total amount of entrapped toluene and m-xylene molecules. Therefore, the content of m-xylene is much higher than that of toluene. In addition, C60-RNRAs show a further weight loss of 3.4 wt% above the temperature of 250 °C, which is confidently ascribed to the removal of rubrene molecules ( Figure S6c). TG analysis of C 60 powder, C 60 MSs, C 60 NRs, and C 60 -RNRAs are then carried out to determine the solvent contents of these materials (Figure 4d). Compared to C 60 powder, the weight loss of C 60 MSs beginning at approximately 115 • C is about 0.8 wt%, which corresponds to the contained toluene molecules. In contrast, weight losses of C 60 NRs and C 60 -RNRAs begin at approximately 55 • C, and amount to 4.8 wt% and 5.2 wt%, respectively, equal to the total amount of entrapped toluene and m-xylene molecules. Therefore, the content of m-xylene is much higher than that of toluene. In addition, C 60 -RNRAs show a further weight loss of 3.4 wt% above the temperature of 250 • C, which is confidently ascribed to the removal of rubrene molecules ( Figure S6c).
The UV-vis absorption and photoluminescence (PL) spectra of these samples in the steady-state mode were then performed to investigate the intermolecular interactions between C 60 and rubrene molecules. Figure 5a displays the corresponding absorption spectra of these samples. In contrast to C 60 MSs and C 60 NRs, a new absorption peak appears at approximately 730 nm for C 60 -RNRAs. Given that C 60 and rubrene are well known as electron-accepting and electron-donating materials, respectively, this new peak could be attributed to the charge transfer (CT) transitions between C 60 and rubrene as also reported by previous studies [16,47,48]. Notably, the CT interaction between C 60 and rubrene is energetically favorable ( Figure S7) [16,49]. Figure 5b shows the PL spectra of the three samples under study. Clearly, C 60 NRs exhibit the enhanced PL intensity compared to C 60 MSs, indicating that the transformation from microsheets to nanorods enhances the PL intensities due to the morphological evolution and the increase of entrapped solvents [22,50]. Moreover, C 60 -RNRAs show an obvious decrease in PL intensity along with a red shift of the PL peak (798 nm) relative to those of C 60 MSs (768 nm) and C 60 NRs (771 nm), which are frequently observed in organic cocrystals due to the CT interactions [16,47]. These The UV-vis absorption and photoluminescence (PL) spectra of these samples in the steady-state mode were then performed to investigate the intermolecular interactions between C60 and rubrene molecules. Figure 5a displays the corresponding absorption spectra of these samples. In contrast to C60MSs and C60NRs, a new absorption peak appears at approximately 730 nm for C60-RNRAs. Given that C60 and rubrene are well known as electron-accepting and electron-donating materials, respectively, this new peak could be attributed to the charge transfer (CT) transitions between C60 and rubrene as also reported by previous studies [16,47,48]. Notably, the CT interaction between C60 and rubrene is energetically favorable ( Figure S7) [16,49]. Figure 5b shows the PL spectra of the three samples under study. Clearly, C60NRs exhibit the enhanced PL intensity compared to C60MSs, indicating that the transformation from microsheets to nanorods enhances the PL intensities due to the morphological evolution and the increase of entrapped solvents [22,50]. Moreover, C60-RNRAs show an obvious decrease in PL intensity along with a red shift of the PL peak (798 nm) relative to those of C60MSs (768 nm) and C60NRs (771 nm), which are frequently observed in organic cocrystals due to the CT interactions [16,47]. These results again corroborate the occurrence of CT interactions between C60 and rubrene within C60-RNRAs [51][52][53][54]. Based on the above results, we further investigated the transformation mechanism from C60MSs to C60NRs and C60-RNRAs. According to the XRD pattern of rubrene crystals prepared by evaporating the rubrene-m-xylene solution, rubrene of the same orthorhombic structure to the pristine rubrene powder is obtained. However, the most intense diffraction peak changes from the (400) peak for crystallized rubrene to the (002) peak for original powder, indicating the growth of rubrene along the [100] direction when m-xylene evaporates ( Figure S4). HRTEM image of the rubrene film prepared by drop-drying the rubrene-m-xylene solution on the silica substrate displays a clear lattice spacing of 0.39 nm, which derives from the (400) plane of the orthorhombic rubrene, confirming again Based on the above results, we further investigated the transformation mechanism from C 60 MSs to C 60 NRs and C 60 -RNRAs. According to the XRD pattern of rubrene crystals prepared by evaporating the rubrene-m-xylene solution, rubrene of the same orthorhombic structure to the pristine rubrene powder is obtained. However, the most Nanomaterials 2022, 12, 954 8 of 13 intense diffraction peak changes from the (400) peak for crystallized rubrene to the (002) peak for original powder, indicating the growth of rubrene along the [100] direction when m-xylene evaporates ( Figure S4). HRTEM image of the rubrene film prepared by dropdrying the rubrene-m-xylene solution on the silica substrate displays a clear lattice spacing of 0.39 nm, which derives from the (400) plane of the orthorhombic rubrene, confirming again that the rubrene molecules crystallize along the [100] orientation with the gradually evaporation of m-xylene ( Figure S8). The XRD and HRTEM results of rubrene crystals obtained by evaporating the rubrene-m-xylene solution are in line with the rubrene in C 60 -RNRAs, indicating the same growth behavior of rubrene in C 60 -RNRAs with the above rubrene crystals. Notably, the (222) plane of fcc C 60 that grows along the [111] orientation has an interplanar spacing (d 222 = 0.41 nm) close to that of the (400) plane of orthorhombic rubrene (d 400 = 0.39 nm), thus affording the desired lattice matching for epitaxial growth of rubrene [29][30][31]. Therefore, as depicted in Figure 6, when the rubrene-mxylene solution drops on C 60 MSs, the epitaxial growth of [001] oriented rubrene molecules on the [111] orientation of C 60 MSs is first achieved as m-xylene evaporates. Afterwards, the emerging intermolecular CT interactions between C 60 and rubrene mediate the oriented growth of re-dissolved C 60 molecules as m-xylene gradually evaporates, eventually leading to the formation of crystalline rubrene inside C 60 nanorod arrays aligned parallelly to the obtuse diagonal of C 60 MSs. Based on the above results, we further investigated the transformation mechanism from C60MSs to C60NRs and C60-RNRAs. According to the XRD pattern of rubrene crystals prepared by evaporating the rubrene-m-xylene solution, rubrene of the same orthorhombic structure to the pristine rubrene powder is obtained. However, the most intense diffraction peak changes from the (400) peak for crystallized rubrene to the (002) peak for original powder, indicating the growth of rubrene along the [100] direction when m-xylene evaporates ( Figure S4). HRTEM image of the rubrene film prepared by drop-drying the rubrene-m-xylene solution on the silica substrate displays a clear lattice spacing of 0.39 nm, which derives from the (400) plane of the orthorhombic rubrene, confirming again that the rubrene molecules crystallize along the [100] orientation with the gradually evaporation of m-xylene ( Figure S8). The XRD and HRTEM results of rubrene crystals obtained by evaporating the rubrene-m-xylene solution are in line with the rubrene in C60-RNRAs, indicating the same growth behavior of rubrene in C60-RNRAs with the above rubrene crystals. Notably, the (222) plane of fcc C60 that grows along the [111] orientation has an interplanar spacing (d222 = 0.41 nm) close to that of the (400) plane of orthorhombic rubrene (d400 = 0.39 nm), thus affording the desired lattice matching for epitaxial growth of rubrene [29][30][31]. Therefore, as depicted in Figure 6, when the rubrene-m-xylene solution drops on C60MSs, the epitaxial growth of [001] oriented rubrene molecules on the [111] orientation of C60MSs is first achieved as m-xylene evaporates. Afterwards, the emerging intermolecular CT interactions between C60 and rubrene mediate the oriented growth of re-dissolved C60 molecules as m-xylene gradually evaporates, eventually leading to the formation of crystalline rubrene inside C60 nanorod arrays aligned parallelly to the obtuse diagonal of C60MSs. Effects of the rubrene concentration in m-xylene on the formation of nanorod arrays were also studied. When the rubrene concentration decreased from 1.0 to 0.5 mg mL −1 , the same preparation steps would give rise to nanorod arrays with a narrowed width and without the rhombic morphology compared to C60-RNRAs, indicating that 0.5 mg mL −1 Figure 6. Schematic illustration of the transformation from C 60 MSs to C 60 -RNARs.
Effects of the rubrene concentration in m-xylene on the formation of nanorod arrays were also studied. When the rubrene concentration decreased from 1.0 to 0.5 mg mL −1 , the same preparation steps would give rise to nanorod arrays with a narrowed width and without the rhombic morphology compared to C 60 -RNRAs, indicating that 0.5 mg mL −1 rubrene concentration is too low to induce adequate interactions between rubrene and C 60 ( Figure S9a). However, the increase of rubrene concentration to 2.0 mg mL −1 results in the formation of nanorod arrays with reduced ordering, which is probably due to the local aggregation of excessive amounts of rubrene ( Figure S9b). Accordingly, the rubrene concentration is a key parameter that regulates the formation of aligned nanorod arrays.
To further confirm the versatility of this rubrene-directed C 60 MSs to C 60 -RNARs conversion strategy, we then conduct control experiments by simply changing the shape or crystal phase of C 60 microsheets. The rectangle C 60 microsheets with a fcc structure (a = 1.410 nm) were also synthesized using benzene/TBA as the good/poor solvents (the concentration of C 60 -benzene solution is 2 mg mL −1 , a volume ratio of 1:3, 25 • C), respectively ( Figure S10). The rectangle microsheets were then treated using m-xylene and rubrene-m-xylene solutions (1 mg mL −1 ). As a consequence, randomly oriented nanorods were formed only when treated by m-xylene, whereas the rectangle nanorod arrays were still formed in the presence of rubrene. Furthermore, hcp C 60 microsheets (a = 1.025 nm, c = 1.072 nm, denoted as hcp 1, Figure S12) were prepared from the CCl 4 /IPA system (the concentration of C 60 -CCl 4 solution is 0.4 mg mL −1 , a volume ration of 1:3, 5 • C) [23]. However, these hcp microsheets were transformed into randomly oriented nanorods when treated with a rubrene-m-xylene solution, due undoubtedly to the lattice mismatch between hcp C 60 microsheets and orthorhombic rubrene. Even so, the orthorhombic rubrene still exists in the hcp structured C 60 microsheets (denoted as hcp 2, Figure S12). Both C 60 and rubrene are organic molecules with π-conjugated systems, showing great potential in the field of optoelectronics [55][56][57]. Therefore, we measured the photocurrent response curves of thin films on ITO glasses composed of C 60 MSs, C 60 NRs, and C 60 -RNRAs to explore their photoelectrochemical properties. To evaluate the effect of rubrene on the photoelectrochemical properties of C 60 nanorods, C 60 -RNRAs were dispersed in deionized water and then ultrasonicated for 30 min to obtain the scattered C 60 -rubrene nanorods (denoted as C 60 -RNRs). All the samples display fast and uniform photocurrent responses under both visible and UV light irradiation during every on-off cycle ( Figure 7) and are more sensitive to UV light than visible light due to their good absorption properties in the UV region (Figure 5a).

Conclusions
We have developed a rubrene-directed strategy with high simplicity and efficiency to enable the structural transformation from 2D C60 microsheets to highly ordered nanorod arrays. The key to the transformation is rooted in the lattice matching between the fcc structured C60 and orthorhombic structured rubrene. Rubrene crystals are first epitaxially grown on the C60 microsheets and then mediate the subsequent unidirectional growth of re-dissolved C60 molecules along a specific orientation, due to the intermolecular charge transfer interactions between C60 and rubrene molecules. Due to the highly oriented structures and favorable intermolecular interactions from the donator/acceptor pair, these ordered nanorod arrays show remarkable enhancement of the photoelectrochemical properties compared to randomly oriented C60 nanorods, indicating their potential application in the field of photodetectors. This work provides an in-depth understanding of the rational design and fabrication of fullerene and other ordered organic superstructures.
Author Contributions: Conceptualization, N.C., K.G. and X.L.; methodology, writing-review and editing, N.C., K.G. and X.L.; data collection, N.C. and P.Y.; visualization, N.C.; investigation, N.C., P.Y., K.G. and X.L.; supervision, K.G. and X.L. All authors have read and agreed to the published version of the manuscript. Of all the samples examined here, C 60 MSs show the lowest photocurrent density, which is due to their smaller specific surface area relative to the nanorods, thereby decreasing the utilization efficiency of light. In addition, the π-π stacking of C 60 along the 1D nanorods facilitated the charge transportation [58][59][60]. Thus, photoelectrochemical properties of the nanorods are improved compared to microsheets. Moreover, C 60 -RNRs present a higher photocurrent density than C 60 NRs. A plausible explanation is a faster recombination of photocarriers due to the intermolecular CT interactions between C 60 and rubrene in C 60 -RNRs [61][62][63]. More interestingly, the photocurrent density and the on-off ratio of C 60 -RNRAs are further improved compared to C 60 -RNRs (improved by 31.2% and 13.5% in the UV region and 21% and 7.1% in the visible region, compared with C 60 NRs and C 60 -RNRs, respectively), indicating that the larger surface area of highly ordered nanorod and excellent crystallinity of C 60 -RNRAs afford more efficient light utilization relative to that of randomly oriented nanorods [58,64]. Additionally, similar to gratings or photonic crystals, ordered nanostructures exhibit stronger absorption and less scattering properties relative to randomly aligned counterparts, therefore the photocurrent density of highly ordered C 60 -RNRAs is enhanced [64]. These results suggest the potential applications of well-aligned nanorod arrays in the fields of photodetectors and organic solar cells.

Conclusions
We have developed a rubrene-directed strategy with high simplicity and efficiency to enable the structural transformation from 2D C 60 microsheets to highly ordered nanorod arrays. The key to the transformation is rooted in the lattice matching between the fcc structured C 60 and orthorhombic structured rubrene. Rubrene crystals are first epitaxially grown on the C 60 microsheets and then mediate the subsequent unidirectional growth of re-dissolved C 60 molecules along a specific orientation, due to the intermolecular charge transfer interactions between C 60 and rubrene molecules. Due to the highly oriented structures and favorable intermolecular interactions from the donator/acceptor pair, these ordered nanorod arrays show remarkable enhancement of the photoelectrochemical properties compared to randomly oriented C 60 nanorods, indicating their potential application in the field of photodetectors. This work provides an in-depth understanding of the rational design and fabrication of fullerene and other ordered organic superstructures.

Data Availability Statement:
The data presented in this study are available on reasonable request from the corresponding author.