Efficient Hydrogen Evolution Reaction with Bulk and Nanostructured Mitrofanovite Pt3Te4

Here, we discuss the key features of electrocatalysis with mitrofanovite (Pt3Te4), a recently discovered mineral with superb performances in hydrogen evolution reaction. Mitrofanovite is a layered topological metal with spin-polarized topological surface states with potential applications for spintronics. However, mitrofanovite is also an exceptional platform for electrocatalysis, with costs of the electrodes suppressed by 47% owing to the partial replacement of Pt with Te. Remarkably, the Tafel slope in nanostructured mitrofanovite is just 33 mV/dec, while reduced mitrofanovite has the same Tafel slope (36 mV/dec) as state-of-the-art electrodes of pure Pt. Mitrofanovite also affords surface stability and robustness to CO poisoning. Accordingly, these findings pave the way for the advent of mitrofanovite for large-scale hydrogen production.


Introduction
In recent years, renewable sources have played a pivotal role in the context of energy production, constituting a valid alternative to nonrenewable energy sources now close to exhaustion [1][2][3]. On the other hand, renewable energy sources are inexhaustible and have a low environmental impact. Accordingly, the capability to meet world energy demand in a sustainable way, minimizing both dependence on the unstable fossil fuel market and associated emissions, is one of the main challenges of the 21st century.
In this context, hydrogen could play a key role in the future of energy devices and their related implications for economy [4][5][6][7]. Hydrogen is the most abundant light element Nanomaterials 2022, 12, 558 2 of 11 of the universe. Its combustion reaction has a high calorific value, with the production of only water, avoiding the formation of greenhouse gases. It should not be considered as an energy source, but rather as an energy carrier, that is, a compound capable of conveying energy from one form to another.
Energy produced from renewable sources through water splitting can be stored through the formation of chemical bonds that are formed by the splitting of the H 2 O molecule [8,9]. Nowadays, 3% of the world's hydrogen production concerns the electrolysis of water. Produced hydrogen can be stored, transported, and for energy purposes it can be used in fuel cells with the purpose of producing electricity again.
The water splitting reaction is endothermic and therefore requires energy that can be supplied by the flow of an electric current through an electrochemical cell.
Water splitting is a process consisting of two reactions, the hydrogen evolution reaction (HER) [10,11] and the oxygen evolution reaction (OER) in which two catalysts are required, one for the oxidation of water into O 2 , and another for the reduction of protons to H 2 .
In the cathodic part of Equation (1) HER takes place: In a basic and acidic electrolyte, respectively. HER begins with the Volmer step, which involves the bond of hydrogen to the electrode at an adsorption site M: M + H 2 O + e − → MH ads + OH − M + H + + e − → MH ads (5) And it is completed with a desorption step that takes place through the Tafel reaction: MH ads → 2M + H 2 (6) Or via Heyrovsky's reaction: MH ads + H + + e − → H 2 + M (8) Thus, HER is a reduction reaction (hydrogen goes from an oxidation state +1 to 0) so it will take place at the cathode.
Definitely, green hydrogen production has enormous potential in providing a cycle of use of sustainable energy and opening a new paradigm for different industrial sectors that today mainly depend on fossil fuels and for which decarbonization is challenging. Electrolytic production of hydrogen faces technological challenges to develop scalable methods with inferior energy consumption. The key point is to reduce the cost of raw materials used as electrocatalysts currently based on pure platinum (Pt). Thus, the production of high purity hydrogen requires low-cost electrocatalysts, with relatively low loading of noble metals in electrodes.
Despite the excellent performances of Pt in HER, the high cost (>30 US $/g) and the restricted obtainability of Pt make unavoidable the quest of economic and earth-abundant potential alternatives [12][13][14][15]. One possible solution is to reduce Pt content by using Pt-based alloys [14,16].
Considering its crucial technological relevance, the identification of efficient electrocatalysts for HER with high activity, cost-effectiveness, and long-term stability represents one of the most important open challenges in electrochemistry.
In particular, mitrofanovite is a recently discovered mineral [17], which was demonstrated to be a topological metal with spin-polarized surface states, with subsequent capabilities for applications in spintronics [18]. Nevertheless, recent findings from different groups highlight the huge potential of mitrofanovite for hydrogen production [19,20]. In this Feature Article, the main features of electrocatalysis with mitrofanovite are discussed, with a particular focus on the effects of dimensionality on the catalytic performances. Moreover, we provide a comparison with parental compounds to highlight the capabilities of mitrofanovite.

Materials and Methods
Single crystals of Pt 3 Te 4 were grown from the self-flux method. The mixtures of high purity Pt foil and Te ingots with a molar ratio of 51:49 were placed in an alumina crucible and sealed into a quartz ampoule. The quartz ampule was heated to 1080 • C for 24 h, then slowly cooled at a rate of 1 • C/h up to 970 • C. The excess flux was separated by centrifugation.
Micro-Raman spectra were acquired with a He-Ne laser source (λ = 632.8 nm) with a LABRAM spectrometer equipped with an optical microscope with a 100x MPLAN with numerical aperture of 0.9. The system operates in a back-scattering configuration and all the measure were carried out at room temperature.
X-ray photoelectron spectroscopy (XPS) measurements were performed at the Advanced Photoelectric Experiments-HE (APE-HE) beamline of the Elettra synchrotron in Trieste, Italy. XPS spectra were acquired at room temperature and in normal emission with an Omicron EA125 hemispherical analyser.
Atomic force microscopy (AFM) images were acquired with a Digital D5000, Veeco system operating in Tapping-mode.
Theoretical methods to calculate HER and OER are reported in Section S1 of the Supporting Information.
High-resolution electron energy loss spectroscopy (HREELS) experiments were carried out with an Ibach-type spectrometer with an energy resolution of 0.5 eV. The primary electron beam energy was 4 eV. All spectra were taken at room temperature and in specular geometry, with an incident angle of 55 • with respect to the sample normal.
The synchrotron X-ray diffraction (SXRD) patterns were collected from 100 to 480 K with the MYTHEN detector with 15 keV beam at beam line 09A, Taiwan Photon Source, National Synchrotron Radiation Research Center (NSRRC) in Hsinchu, Taiwan. The single crystal was pulverized and packed in a 0.1 mm borosilicate capillary to minimize the absorption effect. The capillary was kept spinning during data collection for powder averaging.
Electrochemical tests were carried out on a Bio-Logic VSP-300 electrochemical workstation with a typical three-electrode system, in which a bulk Pt 3 Te 4 plate, a Pt wire and a saturated Ag/AgCl were used as the working electrode, the counter electrode, and the reference electrode, respectively. The inherent electrochemical behaviour of Pt 3 Te 4 was in 0.05 M phosphate buffered saline electrolyte (pH 7.0) at a scan rate of 50 mV s −1 . For HER tests, the polarization curves were obtained using LSV in 0.5 M H 2 SO 4 at a scan rate of 2 mV s −1 . The chronopotentiometric test was performed in 0.5 M H 2 SO 4 at a potential of −0.053 V (vs RHE).

Results and Discussion
The crystal structure of Pt 3 Te 4 was formed by two different alternate Pt 2 Te 2 and PtTe 2 sublayers, bonded along the vertical direction by a combination of electrostatic and van der Waals non-covalent forces (Figure 1a-c). In the PtTe 2 (Pt 2 Te 2 ) sublayer, one (two) Pt atomic layers is (are) sandwiched between two Te atomic layers. Specifically, mitrofanovite belongs to the R-3m (No.166) space group with calculated lattice parameters equal to a = 3.99 Å and c = 35.40 Å. The single crystal of Pt 3 Te 4 displays three Raman active modes at~107, 132, and 169 cm −1 , assigned to A 1g , 2LA(M) and E g phonons, respectively (Figure 1d). To identify the phase, we carried out SXRD experiments, using a synchrotron-based facility to reduce the broadening of peaks compared to in-house XRD systems. All diffraction peaks in Figure 1e match with the Pt 3 Te 4 structure (ICSD # 41372). Our single crystals did not display any minimal trace of contamination, as demonstrated by the XPS survey acquired with synchrotron radiation to enhance surface sensitivity and energy resolution (Figure 1f). Nanomaterials 2022, 11, x FOR PEER REVIEW 4 of 11 at ~107, 132, and 169 cm −1 , assigned to A1g, 2LA(M) and Eg phonons, respectively ( Figure  1d). To identify the phase, we carried out SXRD experiments, using a synchrotron-based facility to reduce the broadening of peaks compared to in-house XRD systems. All diffraction peaks in Figure 1e match with the Pt3Te4 structure (ICSD # 41372). Our single crystals did not display any minimal trace of contamination, as demonstrated by the XPS survey acquired with synchrotron radiation to enhance surface sensitivity and energy resolution ( Figure 1f). To study the surface chemical reactivity of single crystal Pt3Te4, we carried out synchrotron-based XPS experiments, whose superior energy resolution compared to standard XPS could unravel core-level shifts inaccessible with laboratory X-ray sources. Specifically, we studied the evolution of the surface chemical reactivity in oxygen and humid environment and finally in ambient atmosphere ( Figure 2). The Pt-4f core level spectra was split into two components related to Pt-4f7/2 and Pt-4f5/2 shifted by 3.3 eV. The Pt-4f7/2 component was characterized by two components located at binding energies (BEs) of 71.5 and 72.3 eV, respectively ( Figure 2b). Actually, the presence of these two well-distinct spectral components was due to the PtTe2 and Pt2Te2 sub-units [18]. The Te-3d core level was characterized by one doublet shifted by 10.4 eV, with the binding energy of Te-3d5/2 peak of 573.1 eV (Figure 2a). To study the surface chemical reactivity of single crystal Pt 3 Te 4 , we carried out synchrotron-based XPS experiments, whose superior energy resolution compared to standard XPS could unravel core-level shifts inaccessible with laboratory X-ray sources. Specifically, we studied the evolution of the surface chemical reactivity in oxygen and humid environment and finally in ambient atmosphere ( Figure 2). The Pt-4f core level spectra was split into two components related to Pt-4f 7/2 and Pt-4f 5/2 shifted by 3.3 eV. The Pt-4f 7/2 component was characterized by two components located at binding energies (BEs) of 71.5 and 72.3 eV, respectively ( Figure 2b). Actually, the presence of these two well-distinct spectral components was due to the PtTe 2 and Pt 2 Te 2 sub-units [18]. The Te-3d core level was characterized by one doublet shifted by 10.4 eV, with the binding energy of Te-3d 5/2 peak of 573.1 eV (Figure 2a). Pt-4f core level spectra of Pt3Te4 single crystal. The crystal was exfoliated in UHV to prevent oxidation and subsequently exposed to 10 4 L (1 L = 10 −6 Torr·s) of oxygen (red spectra) and water (violet spectra). The yellow spectra represent the air exposed sample. The photon energy is 900 eV, all the spectra are normalized to the maximum.
After the modification of the surface towards 10 4 L of oxygen and water, no changes in the core levels of Pt and Te were observed. Only after air exposure did the Te-3d core level show the emergence of two new features with BEs of 575.7 and 573.8 eV for the J=5/2 component, corresponding to TeO2 and Te(0), respectively ( Figure 2a). Moreover, the Te termination evolved into a nanometric oxide layer, whose thickness was estimated by quantitative XPS. Conversely, in the case of the Pt3Te4-nanocrystal, tellurium-oxide was always present [20].
Furthermore, the environmental stability of Pt3Te4 was studied through the analysis of the time evolution of AFM images (Figure 3a,b). In details, in Figure 3b the height profile along a specific direction remained constant during the air exposure, demonstrating that the morphology of the surface was unchanged. The relative stability of the surface of mitrofanovite made it a suitable candidate as an electrocatalyst. Theoretical modelling indicates that physisorption and further decomposition of molecular oxygen were exothermic processes for both PtTe2 and Pt2Te2 surfaces (Table 1).
Step-by-step modelling of the oxidation process demonstrated that only Te atoms were oxidized on the surface layers of Pt3Te4 (Figure 4), in perfect agreement with the experimental results (Figure 2). Note that Pt centered on the surfaces of Pt3Te4 remained available for interaction with hydrogen even after oxidation. The crystal was exfoliated in UHV to prevent oxidation and subsequently exposed to 10 4 L (1 L = 10 −6 Torr·s) of oxygen (red spectra) and water (violet spectra). The yellow spectra represent the air exposed sample. The photon energy is 900 eV, all the spectra are normalized to the maximum.
After the modification of the surface towards 10 4 L of oxygen and water, no changes in the core levels of Pt and Te were observed. Only after air exposure did the Te-3d core level show the emergence of two new features with BEs of 575.7 and 573.8 eV for the J = 5/2 component, corresponding to TeO 2 and Te(0), respectively ( Figure 2a). Moreover, the Te termination evolved into a nanometric oxide layer, whose thickness was estimated by quantitative XPS. Conversely, in the case of the Pt 3 Te 4 -nanocrystal, tellurium-oxide was always present [20].
Furthermore, the environmental stability of Pt 3 Te 4 was studied through the analysis of the time evolution of AFM images (Figure 3a,b). In details, in Figure 3b the height profile along a specific direction remained constant during the air exposure, demonstrating that the morphology of the surface was unchanged. The relative stability of the surface of mitrofanovite made it a suitable candidate as an electrocatalyst. Pt-4f core level spectra of Pt3Te4 single crystal. The crystal was exfoliated in UHV to prevent oxidation and subsequently exposed to 10 4 L (1 L = 10 −6 Torr·s) of oxygen (red spectra) and water (violet spectra). The yellow spectra represent the air exposed sample. The photon energy is 900 eV, all the spectra are normalized to the maximum.
After the modification of the surface towards 10 4 L of oxygen and water, no changes in the core levels of Pt and Te were observed. Only after air exposure did the Te-3d core level show the emergence of two new features with BEs of 575.7 and 573.8 eV for the J=5/2 component, corresponding to TeO2 and Te(0), respectively ( Figure 2a). Moreover, the Te termination evolved into a nanometric oxide layer, whose thickness was estimated by quantitative XPS. Conversely, in the case of the Pt3Te4-nanocrystal, tellurium-oxide was always present [20].
Furthermore, the environmental stability of Pt3Te4 was studied through the analysis of the time evolution of AFM images (Figure 3a,b). In details, in Figure 3b the height profile along a specific direction remained constant during the air exposure, demonstrating that the morphology of the surface was unchanged. The relative stability of the surface of mitrofanovite made it a suitable candidate as an electrocatalyst. Theoretical modelling indicates that physisorption and further decomposition of molecular oxygen were exothermic processes for both PtTe2 and Pt2Te2 surfaces (Table 1).
Step-by-step modelling of the oxidation process demonstrated that only Te atoms were oxidized on the surface layers of Pt3Te4 (Figure 4), in perfect agreement with the experimental results (Figure 2). Note that Pt centered on the surfaces of Pt3Te4 remained available for interaction with hydrogen even after oxidation. Theoretical modelling indicates that physisorption and further decomposition of molecular oxygen were exothermic processes for both PtTe 2 and Pt 2 Te 2 surfaces (Table 1).
Step-by-step modelling of the oxidation process demonstrated that only Te atoms were oxidized on the surface layers of Pt 3 Te 4 (Figure 4), in perfect agreement with the experimental results ( Figure 2). Note that Pt centered on the surfaces of Pt 3 Te 4 remained available for interaction with hydrogen even after oxidation.   In Figure 5, we report the cyclic voltammetry tests by directly using Pt3Te4 bulk plate as the working electrode. Unlike PtTe2, under neutral conditions, the evolution of hydrogen in Pt3Te4 becomes prominent for potential values below −1.35 V (vs Ag/AgCl), while for PtTe2, it is not prominent up to potential values below −1.8 V (vs Ag/AgCl) [21,22], this reveals a very promising catalytic activity for Pt3Te4. Furthermore, in Figure 5, we show the cyclic voltammetry tests on the modified surface of Pt3Te4 to deeply study the heterogeneous electron transfer. Considering that Pt3Te4 undergoes redox behavior under different applied potentials, both the pristine Pt3Te4 and the same system modified by different electrochemical treatments were investigated. Herein  In Figure 5, we report the cyclic voltammetry tests by directly using Pt 3 Te 4 bulk plate as the working electrode. Unlike PtTe 2 , under neutral conditions, the evolution of hydrogen in Pt 3 Te 4 becomes prominent for potential values below −1.35 V (vs. Ag/AgCl), while for PtTe 2 , it is not prominent up to potential values below −1.8 V (vs. Ag/AgCl) [21,22], this reveals a very promising catalytic activity for Pt 3 Te 4 . Furthermore, in Figure 5, we show the cyclic voltammetry tests on the modified surface of Pt 3 Te 4 to deeply study the heterogeneous electron transfer. Considering that Pt 3 Te 4 undergoes redox behavior under different applied potentials, both the pristine Pt 3 Te 4 and the same system modified by different electrochemical treatments were investigated. Herein, commonly used [Fe(CN) 6  To compare the effectiveness of mitrofanovite for HER, we adopt as figures of merit (i) the Tafel slope (to assess kinetics at the electrode/electrolyte interface) and (ii) η10, i.e., the overpotential required to attain a cathodic current density of 10 mA cm −2 per geometric area. The Tafel slope estimates the potential increase necessary to increase the current density by one order of magnitude. In the case of an insufficient coverage of hydrogen atoms H ads , the Volmer reaction would be the rate limiting step for the HER, resulting in a theoretical Tafel slope around 120 mV/dec. Conversely, for the highest values of H ads , the HER-kinetic is dominated by the Heyrovsky or Tafel reaction, resulting in Tafel slopes around 30-40 mV/dec. To compare the effectiveness of mitrofanovite for HER, we adopt as figures of merit (i) the Tafel slope (to assess kinetics at the electrode/electrolyte interface) and (ii) η10, i.e., the overpotential required to attain a cathodic current density of 10 mA cm −2 per geometric area. The Tafel slope estimates the potential increase necessary to increase the current density by one order of magnitude. In the case of an insufficient coverage of hydrogen atoms Hads, the Volmer reaction would be the rate limiting step for the HER, resulting in a theoretical Tafel slope around 120 mV/dec. Conversely, for the highest values of Hads, the HER-kinetic is dominated by the Heyrovsky or Tafel reaction, resulting in Tafel slopes around 30-40 mV/dec.
In Figure 6, we compare the performances of mitrofanovite for HER with other Ptbased chalcogenides, such as PtS2, PtSe2, and PtTe2. The pristine Pt3Te4 has a Tafel slope of ~49 mV/dec, while this value is modified in ~36 and 44 mV/dec for the reduced and oxidized surface of Pt3Te4, respectively. Note that the value of the Tafel slope in the reduced Pt3Te4 is comparable with the pristine Pt. Moreover, for all Pt3Te4 systems, including the oxidized surface, the Tafel slope is inferior to Pt-based dichalcogenides PtS2, PtSe2, and PtTe2 (Figure 6a) [22][23][24][25][26] with a comparable value to those of Pt films and Pt/C [27]. Thus, the electrochemical treatment of the Pt3Te4 surface improves its performance as an electrocatalyst, and this can be correlated to an increase in the heterogeneous electron transfer capability. Additionally, from the inspection of Figure 6b it is evident that the Tafel slope of Pt3Te4 decreases with the dimensionality. In fact, in the case of Pt3Te4 nanocrystals, the reported Tafel slope was 33 mV/dec and the reported current density was as high as 7000 mA/cm 2 , which should be attributed to the formation of numerous edges and defects in the growth process and the consequent near-zero Gibbs free-energy change of hydrogen adsorption [20].
Notably, vibrational data ( Figure 7) demonstrated that Pt3Te4 showed outstanding tolerance to CO (contrary to pure Pt, which suffers CO poisoning) and stability in a water environment, with subsequent high suitability for HER in both acidic and alkaline conditions. Physisorption of CO on Te vacancies was even more energetically unfavorable than on defects-free surfaces (+3.74 and +6.76 kJ/mol for the PtTe2 and Pt2Te2 terminations of the Pt3Te4 surface, respectively). In Figure 6, we compare the performances of mitrofanovite for HER with other Ptbased chalcogenides, such as PtS 2 , PtSe 2 , and PtTe 2 . The pristine Pt 3 Te 4 has a Tafel slope of~49 mV/dec, while this value is modified in~36 and 44 mV/dec for the reduced and oxidized surface of Pt 3 Te 4 , respectively. Note that the value of the Tafel slope in the reduced Pt 3 Te 4 is comparable with the pristine Pt. Moreover, for all Pt 3 Te 4 systems, including the oxidized surface, the Tafel slope is inferior to Pt-based dichalcogenides PtS 2 , PtSe 2 , and PtTe 2 (Figure 6a) [22][23][24][25][26] with a comparable value to those of Pt films and Pt/C [27]. Thus, the electrochemical treatment of the Pt 3 Te 4 surface improves its performance as an electrocatalyst, and this can be correlated to an increase in the heterogeneous electron transfer capability. Additionally, from the inspection of Figure 6b it is evident that the Tafel slope of Pt 3 Te 4 decreases with the dimensionality. In fact, in the case of Pt 3 Te 4 nanocrystals, the reported Tafel slope was 33 mV/dec and the reported current density was as high as 7000 mA/cm 2 , which should be attributed to the formation of numerous edges and defects in the growth process and the consequent near-zero Gibbs free-energy change of hydrogen adsorption [20].
Notably, vibrational data ( Figure 7) demonstrated that Pt 3 Te 4 showed outstanding tolerance to CO (contrary to pure Pt, which suffers CO poisoning) and stability in a water environment, with subsequent high suitability for HER in both acidic and alkaline conditions. Physisorption of CO on Te vacancies was even more energetically unfavorable than on defects-free surfaces (+3.74 and +6.76 kJ/mol for the PtTe 2 and Pt 2 Te 2 terminations of the Pt 3 Te 4 surface, respectively).
To validate robustness to CO poisoning, we carried out high-resolution electron energy loss spectroscopy experiments, which is especially sensitive to CO adsorption (see our review for CO adsorption on catalytic surfaces [32] for more details), due to the high oscillating dipole. We carried out the experiment in specular conditions in order to maximize the sensitivity to dipole oscillations. Explicitly, we dosed CO onto (i) Pt3Te4   (111). On the other hand, no CO-derived features are achieved even after exposure to 1010 L on Pt3Te4(001) and PtTe2(001). Specifically, the CO-derived features are the vibration of the whole CO molecule against the substrate at 50 meV [32,33] and the intramolecular C-O stretching [32], whose energy depends on the adsorption site: 230 meV for three-fold site, selectively occupied  [19,20], MoTe 2 [20], Pt film [20], platinum dichalcogenides [22][23][24][25], platinum [27], and Pt/C [19]. (b) Comparison of Tafel plots for different Pt 3 Te 4 crystals. Purple, green, light blue, and yellow lines represent pristine Pt 3 Te 4 , reduced Pt 3 Te 4 , oxidized Pt 3 Te 4 , and Pt 3 Te 4 nanocrystals, respectively. For the sake of comparison, we also report Pt (black), Pt film (violet) and Pt/C (magenta). The figure is built using data from Refs. [19,20], and the spectra was renormalized to simplify the visualization. Figure 6. (a) Tafel slope vs overpotential for Pt3Te4 [19,20], MoTe2 [20], Pt film [20], platinum dichalcogenides [22][23][24][25], platinum [27], and Pt/C [19]. (b) Comparison of Tafel plots for different Pt3Te4 crystals. Purple, green, light blue, and yellow lines represent pristine Pt3Te4, reduced Pt3Te4, oxidized Pt3Te4, and Pt3Te4 nanocrystals, respectively. For the sake of comparison, we also report Pt (black), Pt film (violet) and Pt/C (magenta). The figure is built using data from Refs. [19,20], and the spectra was renormalized to simplify the visualization.
To validate robustness to CO poisoning, we carried out high-resolution electron energy loss spectroscopy experiments, which is especially sensitive to CO adsorption (see our review for CO adsorption on catalytic surfaces [32] for more details), due to the high oscillating dipole. We carried out the experiment in specular conditions in order to maximize the sensitivity to dipole oscillations. Explicitly, we dosed CO onto (i) Pt3Te4 (001) (111). On the other hand, no CO-derived features are achieved even after exposure to 1010 L on Pt3Te4(001) and PtTe2(001). Specifically, the CO-derived features are the vibration of the whole CO molecule against the substrate at 50 meV [32,33] and the intramolecular C-O stretching [32], whose energy depends on the adsorption site: 230 meV for three-fold site, selectively occupied  (111). On the other hand, no CO-derived features are achieved even after exposure to 1010 L on Pt 3 Te 4 (001) and PtTe 2 (001). Specifically, the CO-derived features are the vibration of the whole CO molecule against the substrate at 50 meV [32,33] and the intramolecular C-O stretching [32], whose energy depends on the adsorption site: 230 meV for three-fold site, selectively occupied on Ni, while it is a minority on Pt 3 Ni(111) and Pt(111), and 250 meV for the on-top adsorption site, a majority on both Pt 3 Ni(111) and Pt(111).
To obtain more information on the stability of Pt 3 Te 4 electrodes in the electrochemical environment, Pt-4f ( Figure 8a) and Te-3d (Figure 8b) core levels were measured on both asprepared and postmortem electrodes. From the inspection of Figure 8, it is quite evident that Pt 3 Te 4 electrodes were not affected by degradation after electrochemical treatment, with just negligible changes. The only change is in the Te core level where we observe a lower component of tellurium oxide after the reaction. On the other hand, the electrochemical stability is a crucial aspect in electrocatalysis. The chronopotentiometric curve (Figure 8c) in 0.5 M H 2 SO 4 at a potential of −0.053 V vs RHE, showing negligible attenuation in a timescale extended up to three days further validates the outstanding chemical and electrocatalytic stability of Pt 3 Te 4 .
To obtain more information on the stability of Pt3Te4 electrodes in the electrochemical environment, Pt-4f ( Figure 8a) and Te-3d (Figure 8b) core levels were measured on both as-prepared and postmortem electrodes. From the inspection of Figure 8, it is quite evident that Pt3Te4 electrodes were not affected by degradation after electrochemical treatment, with just negligible changes. The only change is in the Te core level where we observe a lower component of tellurium oxide after the reaction. On the other hand, the electrochemical stability is a crucial aspect in electrocatalysis. The chronopotentiometric curve (Figure 8c) in 0.5 M H2SO4 at a potential of −0.053 V vs RHE, showing negligible attenuation in a timescale extended up to three days further validates the outstanding chemical and electrocatalytic stability of Pt3Te4.

Conclusions
In this paper, we discussed the key features ruling electrocatalysis with mitrofanovite (Pt3Te4), a recently discovered mineral with superb performances in HER.
Mitrofanovite has a surface stable even upon exposure to ambient atmosphere, with just a sub-nanometric oxide skin.
Mitrofanovite represents an exceptional platform for electrocatalysis, with costs of the electrodes suppressed by 47% owing to the partial replacement of Pt with Te. Remarkably, the Tafel slope in nanostructured mitrofanovite is just 33 mV/dec, while reduced mitrofanovite has the same Tafel slope (36 mV/dec) than state-of-the-art electrodes of pure Pt. Contrary to Pt, mitrofanovite is not affected by CO poisoning.
Accordingly, these results pave the way for the advent of mitrofanovite for largescale hydrogen production.

Conclusions
In this paper, we discussed the key features ruling electrocatalysis with mitrofanovite (Pt 3 Te 4 ), a recently discovered mineral with superb performances in HER.
Mitrofanovite has a surface stable even upon exposure to ambient atmosphere, with just a sub-nanometric oxide skin.
Mitrofanovite represents an exceptional platform for electrocatalysis, with costs of the electrodes suppressed by 47% owing to the partial replacement of Pt with Te. Remarkably, the Tafel slope in nanostructured mitrofanovite is just 33 mV/dec, while reduced mitrofanovite has the same Tafel slope (36 mV/dec) than state-of-the-art electrodes of pure Pt. Contrary to Pt, mitrofanovite is not affected by CO poisoning.
Accordingly, these results pave the way for the advent of mitrofanovite for large-scale hydrogen production.

Conflicts of Interest:
The authors declare no conflict of interest.