Colloidal Synthesis, Characterization, and Photoconductivity of Quasi-Layered CuCrS2 Nanosheets

The current need to accelerate the adoption of photovoltaic (PV) systems has increased the need to explore new nanomaterials that can harvest and convert solar energy into electricity. Transition metal dichalcogenides (TMDCs) are good candidates because of their tunable physical and chemical properties. CuCrS2 has shown good electrical and thermoelectrical properties; however, its optical and photoconductivity properties remain unexplored. In this study, we synthesized CuCrS2 nanosheets with average dimensions of 43.6 ± 6.7 nm in length and 25.6 ± 4.1 nm in width using a heat-up synthesis approach and fabricated films by the spray-coating method to probe their photoresponse. This method yielded CuCrS2 nanosheets with an optical bandgap of ~1.21 eV. The fabricated film had an average thickness of ~570 nm, exhibiting a net current conversion efficiency of ~11.3%. These results demonstrate the potential use of CuCrS2 as an absorber layer in solar cells.


Introduction
In the context of accelerating global warming caused by fossil fuel-based hydrocarbon energy, it is essential to develop alternative ways of energy production that shift away from fossil fuels. Hence, efficient photovoltaic (PV) systems with strong absorber layers are a leading alternative approach to capturing and converting solar energy [1]. The commercially available PV systems are principally composed of crystalline silicon due to its long-term stability and high abundance. It is the gold standard in the industry; however, silicon's poor light-absorbing properties require thicker layers, leading to higher production costs and making it difficult to fabricate as flexible solar cells. The alternative, thin-film solar cells, are known as the second-generation technology because they offer an opportunity to develop flexible high-specific power photovoltaics due to their high optical absorption coefficients, desirable bandgaps, and self-passivated surfaces [2]. In recent years, 2D transition metal dichalcogenides (TMDCs) have emerged as attractive thin-film solar cell materials because of their unique physical and chemical properties. For example, the bandgap of well-known TMDCs, such as MoSe 2 , WSe 2 , MoS 2 , and WS 2 , changes from indirect to direct when these materials are reduced from multilayers to a monolayer form [3][4][5]. Therefore, some of the novel 2D TMDCs are direct bandgap semiconductors in monolayer form with excellent electronic properties and tunable bandgaps [6,7]. Due to their layered nature, these materials can potentially enable us to fabricate flexible, thinner, more efficient, and versatile solar cells [8]. 2D TMDCs offer excellent electron transport properties and high carrier mobility compared to commercially available absorber materials [9]. Current absorber materials with commercial potential are held back due to their poor stability and short shelf life [10,11]. In this context, quasi-layered CuCrS 2 appears to be a promising chalcogenide material that absorbs light over a broad range of the visible electromagnetic spectrum and exhibits a good photoconductive response. However, its optical properties have not been thoroughly investigated.

Materials
Sodium diethyldithiocarbamate (Na(DDTC) hydrate), copper (II) nitrate trihydrate (Cu(NO 3 ) 2 ·3H 2 O), chromium (III) chloride anhydrous, and analytical-grade hexane and ethanol were obtained from Sigma-Aldrich (MilliporeSigma, Burlington, MA, USA). All solids used for the synthesis of the Cu precursor were ground using a mortar and pestle and dried at atmospheric pressure and 180 • C for 18 h prior to use. Dichloromethane was purchased from Supelco (Supelco Inc., Bellefonte, PA, USA) and used without further purification. Oleylamine (OLA) distilled (min 99%) was obtained from Silver Fern (Silver Fern Chemical Inc., Seattle, WA, USA) and 1-dodecanethiol (1-DDT, 98%) was obtained from Alfa Aesar (Alfa Aesar, Ward Hill, MA, USA). These were used as received without any further purification. In a typical synthesis of layered CuCrS 2 nanosheets, 0.25 mmol of the Cu(DDTC) 2 , 0.25 mmol of CrCl 3 , and 2 mL of 1-DDT were added to a three-neck flask connected to a Schlenk line containing 10 mL of OLA. The precursor-containing mixture was then stirred and degassed with N 2 for 20 min. The solution was heated to 320 • C and maintained at this temperature for 60 min. The resulting dark mixture was then naturally cooled. The solution was split into two vial tubes, and a 1:1 mixture of hexane and ethanol was poured into the solution and centrifugally separated. The precipitate was washed and centrifuged (8000 rpm for 5 min) with hexane and ethanol until the solution became clear.

Characterization Methods
The structural characterization of the precursor was achieved via 1 H-and 13 C-NMR, using a BRUKER AVANCE 500 MHz NMR and ESI-MS on a BRUKER HCTultra PTM Discovery System on positive mode (both equipment from Bruker Co., Billerica, MA, USA). Single metallic, dark black, plate-shaped crystals of Cu(DDTC) 2 were used. A suitable crystal with dimensions of 0.08 × 0.07 × 0.04 mm 3 was selected and mounted on a Rigaku XtaLAB Synergy R, DW system, and HyPix diffractometer (Rigaku Co., Tokyo, Japan). The single-crystal X-ray diffraction data for the precursor can be found in the Supporting Information in Figure S1 and Table S1. The crystal was kept at a steady temperature of 113 (19) K during data collection. The structure was solved with the ShelXT version 2018/2 [23] solution program using dual methods and refined by full-matrix least-squares minimization on F 2 using version ShelXL 2018/3 [24]. Olex2 1.3 [25] was used as the graphical interface.
The crystallographic analyses of the as-synthesized nanoparticles were performed by X-ray diffraction using a BRUKER D2 diffractometer (Bruker Co., Billerica, MA, USA) with Cu K α (1.5406 Å) radiation. The absorbance spectra were measured using Shimadzu UV-3600i Plus UV-vis-NIR spectrophotometer (Shimadzu Co., Kyoto, Japan), and the optical bandgap was estimated from Tauc plot analysis. Scanning electron microscopy analysis was carried out using an Apreo FE-SEM (Thermo Fisher Scientific Inc., Waltham, MA, USA) to probe the surface morphology and thickness of the sprayed thin films prepared from nanoparticle suspension. The chemical composition was determined using energy-dispersive X-ray analysis (EDX). Transmission electron microscopy (TEM) and highresolution TEM analyses were performed using an FEI Tecnai 20 (Thermo Fisher Scientific Inc., Waltham, MA, USA) with a 200 kV operating beam. The nanosheets were dispersed in hexane and dropped onto a carbon-coated nickel TEM grid. Current and voltage (I-V) measurements were performed in dark and under one-sun (100 mW cm −2 , AM 1.5 G) light illumination conditions using a Princeton potentiostat (AMETEK Inc., Berwyn, PA, USA) in the applied potential window of −500 mV and +500 mV.

Copper Precursor Spectral Studies and Characterization
Through the obtained 1 H-NMR spectra of the ligand and the complex, the formation of the target compound and an improvement in the purity comparing the starting material to the product was verified. The quartet corresponding to the methylene protons in the free ligand was found at 2.7 ppm and shifted to 3.46 and 3.50 ppm in the final product. The quartet was shifted downfield due to the deshielding effect of the neighboring nitrogen. The triplet that corresponded to the methyl groups was found at 1.19 ppm and shifted downfield to 1.22 ppm, as seen in Figure 1. In the 13 C-NMR spectrum in Figure S2, the methyl groups were found at 11.07 ppm, the methylene carbons at 42.09 ppm, and the diethyldithiocarbamate carbon (NCS 2 ) at 107.61 ppm. The mass spectrum in Figure S3 confirmed the expected mass of 359 Da for Cu(DDTC) 2 , including the characteristic Cu isotope pattern.
The determined structure ( Figure 2) reveals that the complex is built up of centrosymmetric dimeric entities, where the copper (II) ions sit in a distorted square-pyramidal coordination sphere, consistent with the structures previously reported [26,27]. The basal coordination positions are occupied by four sulfur atoms belonging to the two ligand units. The fifth coordination location is formed by linking two monomeric units through a sulfur atom. This sulfur atom then occupies the equatorial site in the coordination polyhedron of the aforementioned copper (II) ion. Therefore, each bridging sulfur simultaneously The determined structure ( Figure 2) reveals that the complex is built up of centrosymmetric dimeric entities, where the copper (II) ions sit in a distorted square-pyramidal coordination sphere, consistent with the structures previously reported [26,27]. The basal coordination positions are occupied by four sulfur atoms belonging to the two ligand units. The fifth coordination location is formed by linking two monomeric units through a sulfur atom. This sulfur atom then occupies the equatorial site in the coordination polyhedron of the aforementioned copper (II) ion. Therefore, each bridging sulfur simultaneously occupies an equatorial coordination site on one copper (II) ion and an axial site on the other Cu (II). Crystal

Nanosheets: Synthesis and Characterization
As shown in Figure 3 a colloidal heat-up strategy was used to synthesize CuCrS2 nanosheets. In the heat-up synthesis strategy, all the precursors (Cu(DDTC)2, CrCl3, and 1-DDT) in a 1:1:8 ratio were dissolved in OLA under a nitrogen environment. The mixture  The determined structure ( Figure 2) reveals that the complex is built up of centrosymmetric dimeric entities, where the copper (II) ions sit in a distorted square-pyramidal coordination sphere, consistent with the structures previously reported [26,27]. The basal coordination positions are occupied by four sulfur atoms belonging to the two ligand units. The fifth coordination location is formed by linking two monomeric units through a sulfur atom. This sulfur atom then occupies the equatorial site in the coordination polyhedron of the aforementioned copper (II) ion. Therefore, each bridging sulfur simultaneously occupies an equatorial coordination site on one copper (II) ion and an axial site on the other Cu (II). Crystal

Nanosheets: Synthesis and Characterization
As shown in Figure 3 a colloidal heat-up strategy was used to synthesize CuCrS2 nanosheets. In the heat-up synthesis strategy, all the precursors (Cu(DDTC)2, CrCl3, and 1-DDT) in a 1:1:8 ratio were dissolved in OLA under a nitrogen environment. The mixture

Nanosheets: Synthesis and Characterization
As shown in Figure 3 a colloidal heat-up strategy was used to synthesize CuCrS 2 nanosheets. In the heat-up synthesis strategy, all the precursors (Cu(DDTC) 2 , CrCl 3 , and 1-DDT) in a 1:1:8 ratio were dissolved in OLA under a nitrogen environment. The mixture of precursors was heated to 320 • C. During the heat-up process, the precursors decomposed to form monomers. At 270 • C, the XRD pattern ( Figure S4) showed the presence of the CuCrS 2 and Cu 2 S phases. This result suggests that the decomposition of Cu(DDTC) 2 led to the reduction of Cu +2 to the Cu +1 state to form Cu 2 S as an intermediate phase, eventually leading to the nucleation of CuCrS 2 . At this temperature, nanohexagons, nanosheets, and impurity phases were spotted simultaneously on TEM images, as seen in Figure S4. The presence of nanohexagons decreased by increasing the temperature to 320 • C. During the heat-up process, the nanohexagons grew in the [100] direction forming nanosheets. It is important to note that different morphologies arose when octadecylamine (ODA) was added as a cosurfactant, as shown in Figure S5. Therefore, the nanosheet morphology can be attributed to using OLA as a surfactant. It is well established that OLA attaches preferentially to different facets of growing nanocrystals [28][29][30][31]. No appreciable morphological changes were detected by varying the time of the reaction. The crystallinity of CuCrS 2 was determined using X-ray diffraction. As shown in Figure 4, the major diffraction peaks were indexed to the (003), (006), (101), (012), (104), (015), (107), (018), and (110) planes. The observed diffraction peak positions for CuCrS 2 nanocrystals matched well with the literature and the standard diffraction data (ICDD# 01-079-7417) reported for CuCrS 2 [12,13,15,17,22,32]. X-ray diffraction analysis indicated that the aforementioned approach produced CuCrS 2 without any secondary phase. From the diffraction pattern, the lattice parameters were determined to be 3.481 Å (a), 3.481 Å (b), and 18.702 Å (c), consistent with the previously reported data and the reference data [18,[33][34][35].
led to the reduction of Cu +2 to the Cu +1 state to form Cu2S as an intermediate phase, eventually leading to the nucleation of CuCrS2. At this temperature, nanohexagons, nanosheets, and impurity phases were spotted simultaneously on TEM images, as seen in Figure S4. The presence of nanohexagons decreased by increasing the temperature to 320 °C. During the heat-up process, the nanohexagons grew in the [100] direction forming nanosheets. It is important to note that different morphologies arose when octadecylamine (ODA) was added as a cosurfactant, as shown in Figure S5. Therefore, the nanosheet morphology can be attributed to using OLA as a surfactant. It is well established that OLA attaches preferentially to different facets of growing nanocrystals [28][29][30][31]. No appreciable morphological changes were detected by varying the time of the reaction. The crystallinity of CuCrS2 was determined using X-ray diffraction. As shown in Figure 4, the major diffraction peaks were indexed to the (003), (006), (101), (012), (104), (015), (107), (018), and (110) planes. The observed diffraction peak positions for CuCrS2 nanocrystals matched well with the literature and the standard diffraction data (ICDD# 01-079-7417) reported for CuCrS2 [12,13,15,17,22,32]. X-ray diffraction analysis indicated that the aforementioned approach produced CuCrS2 without any secondary phase. From the diffraction pattern, the lattice parameters were determined to be 3.481 Å (a), 3.481 Å (b), and 18.702 Å (c), consistent with the previously reported data and the reference data [18,[33][34][35].   led to the reduction of Cu +2 to the Cu +1 state to form Cu2S as an intermediate phase, eventually leading to the nucleation of CuCrS2. At this temperature, nanohexagons, nanosheets, and impurity phases were spotted simultaneously on TEM images, as seen in Figure S4. The presence of nanohexagons decreased by increasing the temperature to 320 °C. During the heat-up process, the nanohexagons grew in the [100] direction forming nanosheets. It is important to note that different morphologies arose when octadecylamine (ODA) was added as a cosurfactant, as shown in Figure S5. Therefore, the nanosheet morphology can be attributed to using OLA as a surfactant. It is well established that OLA attaches preferentially to different facets of growing nanocrystals [28][29][30][31]. No appreciable morphological changes were detected by varying the time of the reaction. The crystallinity of CuCrS2 was determined using X-ray diffraction. As shown in Figure 4, the major diffraction peaks were indexed to the (003), (006), (101), (012), (104), (015), (107), (018), and (110) planes. The observed diffraction peak positions for CuCrS2 nanocrystals matched well with the literature and the standard diffraction data (ICDD# 01-079-7417) reported for CuCrS2 [12,13,15,17,22,32]. X-ray diffraction analysis indicated that the aforementioned approach produced CuCrS2 without any secondary phase. From the diffraction pattern, the lattice parameters were determined to be 3.481 Å (a), 3.481 Å (b), and 18.702 Å (c), consistent with the previously reported data and the reference data [18,[33][34][35].   The TEM micrographs show that the prescribed mixture of metal precursors, sulfur source, and solvent led to the formation of regular sheet-shaped nanoparticles with a narrow size distribution. The nanosheets had average dimensions of 43.6 ± 6.7 nm in length and 25.6 ± 4.1 nm in width, as seen from the statistical analysis in Figure S6. In conjunction with XRD, the HR-TEM images, as seen in Figure 5b,c, along with the fast Fourier transform (FFT) in Figure 5d, suggest the single crystalline nature of the nanosheets. Moreover, the average particle size of the nanosheets was estimated using the well-known Debye-Scherrer formula, which relates the size of the nanocrystallites in a solid to the broadening of a peak in the diffraction pattern. [36,37]: where λ is the wavelength of the X-ray radiation source Cu-Kα (1.5418 A); β is the FWHM (full width at half maximum) corresponding to all the peaks on the diffraction pattern; θ is the diffraction angle for lattice planes, and D is the particle diameter size. The crystallite size was calculated using all the diffraction peaks in the XRD pattern and taking the average of these. The estimated particle size for the nanosheets was 50.8 ± 5.2 nm, which agreed well with the experimental observations (from the TEM study). The indicated lattice fringe spacing of 0.622 ± 0.006 nm corresponded to the d-spacing of the (003) plane. Furthermore, the elemental composition analysis from Figure S7 and Table S2 confirmed the expected atomic composition ratio of 1:1:2.
The TEM micrographs show that the prescribed mixture of metal precursors, sulfur source, and solvent led to the formation of regular sheet-shaped nanoparticles with a narrow size distribution. The nanosheets had average dimensions of 43.6 ± 6.7 nm in length and 25.6 ± 4.1 nm in width, as seen from the statistical analysis in Figure S6. In conjunction with XRD, the HR-TEM images, as seen in Figure 5b,c, along with the fast Fourier transform (FFT) in Figure 5d, suggest the single crystalline nature of the nanosheets. Moreover, the average particle size of the nanosheets was estimated using the well-known Debye-Scherrer formula, which relates the size of the nanocrystallites in a solid to the broadening of a peak in the diffraction pattern. [36,37]: where λ is the wavelength of the X-ray radiation source Cu-Kα (1.5418 A); β is the FWHM (full width at half maximum) corresponding to all the peaks on the diffraction pattern; θ is the diffraction angle for lattice planes, and D is the particle diameter size. The crystallite size was calculated using all the diffraction peaks in the XRD pattern and taking the average of these. The estimated particle size for the nanosheets was 50.8 ± 5.2 nm, which agreed well with the experimental observations (from the TEM study). The indicated lattice fringe spacing of 0.622 ± 0.006 nm corresponded to the d-spacing of the (003) plane. Furthermore, the elemental composition analysis from Figure S7 and Table S2 confirmed the expected atomic composition ratio of 1:1:2. To gain insights into the optical properties of CuCrS2, absorption spectroscopy studies were performed. The dispersed nanosheets appeared dark brownish in color, indicating their strong absorption in the visible range of the electromagnetic spectrum. The absorption measurements were obtained from dispersed nanosheets in hexane. Figure 6 shows a typical absorption spectrum of the synthesized CuCrS2 nanosheets, exhibiting absorption in the visible range with an optimum absorption of around 700 nm. To estimate the band gap, the Tauc relationship [38][39][40] given below was used: where α is the optical absorption coefficient; hν is the photon energy; n = 2 or 1/2 for the direct and indirect bandgaps, respectively, and Eg is the energy gap of the material. The direct allowed optical transition was found for CuCrS2 with a bandgap energy that can be determined by producing a plot of (αhν) 2 vs. hν and extrapolating the linear portion of the curve to the horizontal axis of the photon energy at (αhν) 2 = 0. As shown in the inset of Figure 6, the estimated optical direct and indirect bandgaps of CuCrS2 were 1.21 ± 0.06 eV and 0.83 ± 0.03 eV, respectively, which make this material suitable for photovoltaic applications. Nanohexagons of CuCrS2, shown in Figure S8, were reported in the literature [35], and upon using the described synthesis approach, we determined the optical direct and indirect bandgaps of the nanohexagons to be 1.29 ± 0.07 eV and 0.80 ± 0.05 eV, To gain insights into the optical properties of CuCrS 2 , absorption spectroscopy studies were performed. The dispersed nanosheets appeared dark brownish in color, indicating their strong absorption in the visible range of the electromagnetic spectrum. The absorption measurements were obtained from dispersed nanosheets in hexane. Figure 6 shows a typical absorption spectrum of the synthesized CuCrS 2 nanosheets, exhibiting absorption in the visible range with an optimum absorption of around 700 nm. To estimate the band gap, the Tauc relationship [38][39][40] given below was used: where α is the optical absorption coefficient; hν is the photon energy; n = 2 or 1/2 for the direct and indirect bandgaps, respectively, and E g is the energy gap of the material. The direct allowed optical transition was found for CuCrS 2 with a bandgap energy that can be determined by producing a plot of (αhν) 2 vs. hν and extrapolating the linear portion of the curve to the horizontal axis of the photon energy at (αhν) 2 = 0. As shown in the inset of Figure 6, the estimated optical direct and indirect bandgaps of CuCrS 2 were 1.21 ± 0.06 eV and 0.83 ± 0.03 eV, respectively, which make this material suitable for photovoltaic applications. Nanohexagons of CuCrS 2 , shown in Figure S8, were reported in the literature [35], and upon using the described synthesis approach, we determined the optical direct and indirect bandgaps of the nanohexagons to be 1.29 ± 0.07 eV and 0.80 ± 0.05 eV, respectively, as seen in Figure S9. The slight difference in the values of the bandgaps between the two differently synthesized samples was most likely due to the presence of an impurity phase, as seen in the X-ray diffraction pattern of nanohexagons in Figure S10. respectively, as seen in Figure S9. The slight difference in the values of the bandgaps between the two differently synthesized samples was most likely due to the presence of an impurity phase, as seen in the X-ray diffraction pattern of nanohexagons in Figure S10.

Photoconductivity
Semiconducting materials should have an appropriate photoresponse to be suitable for use in solar cell applications. The photoconductivity was determined by analyzing the current-voltage (I-V) characteristics of CuCrS2. To study the photoconductivity of CuCrS2 nanosheets, the material was incorporated as an absorber layer in a photovoltaic structure composed of soda-lime glass/Mo/CuCrS2/Ag, as shown in the inset of Figure 7. The Cu-CrS2 thin films were prepared using a previously reported nano-ink approach [41][42][43]. A "nano-ink" stabilizing solution was prepared by resuspending ~120 mg of CuCrS2 in 25 mL of hexane. A few drops of OLA were added to stabilize the suspension. The nano-ink solution was sprayed on top of a molybdenum-coated glass substrate using a commercial spray gun to produce a thin film. The thin film was then annealed in a nitrogen environment at 375 °C for 1 h. Upon further examination, the film had a continuous surface and a thickness of 570 ± 37 nm, as seen in Figure 7a,b. An EDX analysis for the fabricated thin film confirmed the atomic ratio of 1:1:2, as seen in Figure S11 and Table S3.
The conductivity response of the annealed CuCrS2 film was measured between the bottom molybdenum layer and top silver electrodes under dark and white light illumination at 100 mWcm −2 using a Xenon lamp under air at room temperature. The photocurrent and responsivity of CuCrS2 film were calculated from the I-V curve and are summarized in Table 1. The responsivity was calculated using Equation (3) [44]: where Rλ is the responsivity (the photocurrent generated per unit power of the incident light used on the CuCrS2 film of the effective area (1.09 cm −2 ); Pλ is the intensity of illumination (100 mWcm −2 ); A is the effective area of the CuCrS2 film, and IL and ID are currents generated under illumination and dark, respectively.

Photoconductivity
Semiconducting materials should have an appropriate photoresponse to be suitable for use in solar cell applications. The photoconductivity was determined by analyzing the current-voltage (I-V) characteristics of CuCrS 2 . To study the photoconductivity of CuCrS 2 nanosheets, the material was incorporated as an absorber layer in a photovoltaic structure composed of soda-lime glass/Mo/CuCrS 2 /Ag, as shown in the inset of Figure 7. The CuCrS 2 thin films were prepared using a previously reported nano-ink approach [41][42][43]. A "nano-ink" stabilizing solution was prepared by resuspending~120 mg of CuCrS 2 in 25 mL of hexane. A few drops of OLA were added to stabilize the suspension. The nano-ink solution was sprayed on top of a molybdenum-coated glass substrate using a commercial spray gun to produce a thin film. The thin film was then annealed in a nitrogen environment at 375 • C for 1 h. Upon further examination, the film had a continuous surface and a thickness of 570 ± 37 nm, as seen in Figure 7a,b. An EDX analysis for the fabricated thin film confirmed the atomic ratio of 1:1:2, as seen in Figure S11 and Table S3.
The conductivity response of the annealed CuCrS 2 film was measured between the bottom molybdenum layer and top silver electrodes under dark and white light illumination at 100 mWcm −2 using a Xenon lamp under air at room temperature. The photocurrent and responsivity of CuCrS 2 film were calculated from the I-V curve and are summarized in Table 1. The responsivity was calculated using Equation (3) [44]: where R λ is the responsivity (the photocurrent generated per unit power of the incident light used on the CuCrS 2 film of the effective area (1.09 cm −2 ); P λ is the intensity of illumination (100 mWcm −2 ); A is the effective area of the CuCrS 2 film, and I L and I D are currents generated under illumination and dark, respectively. The photocurrent of the effective illuminated area of CuCrS 2 film is shown in Figure 7c and indicates a noticeable increase in photocurrent under illumination. The measured photocurrent was found to be 22.52 mA, and the responsivity was 0.21 A W −1 . The current conversion efficiency with respect to the dark current was calculated using Equation (4): where P in is the maximum power generated by the film, and P out is the intensity of illumination.   The photocurrent of the effective illuminated area of CuCrS2 film is shown in Figure  7c and indicates a noticeable increase in photocurrent under illumination. The measured photocurrent was found to be 22.52 mA, and the responsivity was 0.21 A W −1 . The current conversion efficiency with respect to the dark current was calculated using Equation (4): where Pin is the maximum power generated by the film, and Pout is the intensity of illumination.
The current conversion efficiency of the film was determined to be ~11.3% with respect to the dark current. Our results are comparable to Cu2CoSnS4 and Cu2CdxZn1-xSnS4 films for which similar responsivity and current efficiency values have been reported [44][45][46]. The spray-coating system does produce films with a relatively large surface roughness. Nonetheless, the roughness of the fabricated CuCrS2 thin film did not influence its  The current conversion efficiency of the film was determined to be~11.3% with respect to the dark current. Our results are comparable to Cu 2 CoSnS 4 and Cu 2 Cd x Zn 1-x SnS 4 films for which similar responsivity and current efficiency values have been reported [44][45][46]. The spray-coating system does produce films with a relatively large surface roughness. Nonetheless, the roughness of the fabricated CuCrS 2 thin film did not influence its photoconductivity, as shown in Figure S12 and Table S4. The respectable photoresponse suggests that CuCrS 2 can potentially serve as an absorber layer in thin film solar cells.

Conclusions
In summary, we successfully synthesized and determined the crystal structure of a copper (diethyldithiocarbamate) 2 precursor and synthesized phase-pure CuCrS 2 nanoparticles with nanosheet morphology. The synthesis involved the heat-up of a mixture containing the metal precursors, sulfur source, and oleylamine solvent as a capping agent. The structure, phase, morphology, and purity of the synthesized nanosheets were determined by XRD, SEM, and TEM techniques. The nanosheets' optical direct and indirect bandgaps were determined to be 1.21 ± 0.06 eV and 0.83 ± 0.03 eV from the UV-vis absorption spectra. The fabricated CuCrS 2 thin film showed good photoresponse characteristics in the current-voltage (I-V) measurements with an~11.3% current conversion efficiency with respect to the dark measurements. This study demonstrates that CuCrS 2 nanosheets have potential for their utilization in thin-film solar cell devices.
Supplementary Materials: The following supporting information can be downloaded at: https: //www.mdpi.com/article/10.3390/nano12234164/s1, Figure S1: Crystal structure of Cu(DDTC)2; Table S1: Crystallographic studies on Cu(DDTC)2; Figure S2: 13C-NMR of C(DDTC)2; Figure S3: Positive mode ESI-MS of copper precursor; Figure S4: X-ray diffraction pattern of reaction product at 270 • C; Figure S5: TEM image of the reaction product at 320 • C using OLA and ODA as surfactants; Figure S6: Statistical size analysis and corresponding TEM images of the CuCrS2 nanosheets; Figure S7: EDX spectrum of CuCrS2 nanosheets; Table S2: Elemental composition of CuCrS2 nanosheets determined by EDX; Figure S8: TEM image of CuCrS2 nanohexagons; Figure S9: (a) UV-vis absorption spectra of CuCrS2 nanohexagons, (b) and (c) shows the Tauc plot and extrapolation of the curve to determine the direct and indirect bandgap energy.; Figure S11: EDX spectrum of the fabricated CuCrS2 thin film; Table S3: Elemental composition from EDX of the fabricated thin film after annealing; Figure S12: (a) Current-voltage (I-V) characteristics of CuCrS2 thin film under white illumination at 100 mW cm −2 . SEM images of (b) the surface continuity and roughness and (c) a cross-section view of~400 nm thick CuCrS2 thin film fabricated on Mo-coated glass substrate; Table S4: Photocurrent and responsivity of fabricated CuCrS2 thin film.

Data Availability Statement:
The data presented in this study are available on request from the corresponding author.