Flowery ln2MnSe4 Novel Electrocatalyst Developed via Anion Exchange Strategy for Efficient Water Splitting

Oxygen and hydrogen generated by water electrolysis may be utilized as a clean chemical fuel with high gravimetric energy density and energy conversion efficiency. The hydrogen fuel will be the alternative to traditional fossil fuels in the future, which are near to exhaustion and cause pollution. In the present study, flowery-shaped In2MnSe4 nanoelectrocatalyst is fabricated by anion exchange reaction directly grown on nickel foam (NF) in 1.0 M KOH medium for oxygen evolution reaction (OER). The physiochemical and electrical characterization techniques are used to investigate the chemical structure, morphology, and electrical properties of the In2MnSe4 material. The electrochemical result indicates that synthesized material exhibits a smaller value of Tafel slope (86 mV/dec), lower overpotential (259 mV), and high stability for 37 h with small deterioration in the current density for a long time. Hence, the fabricated material responds with an extraordinary performance for the OER process and for many other applications in the future.


Introduction
Global energy consumption will continue to increase in the near future, owing to the rise in population and industry. However, conventional non-renewable fossil fuels such as coal, gas, and oil have so many adverse effects on the environment and living beings, so it From the aforementioned characteristics, in this study, we prepared a novel In 2 MnSe 4 nano electrocatalyst for oxygen evolution reaction fabricated by anion exchange reaction. The various complementary physiochemical techniques were employed to investigate the structure, morphology and electrical properties of fabricated In 2 MnSe 4 . For electrochemical characterizations, the electrocatalyst-loaded electrode was grown on the nickel foam (NF) substrate via the drop cast method, and the porous, highly conductive loaded 3D-nickel foam substrate is responsible for demonstrating such outstanding results with long-term stability.

Fabrication of In 2 MnSe 4
In 2 MnSe 4 , the electrocatalyst was prepared by a typical anion exchange reaction. For this purpose, the whole procedure was divided into two steps, firstly, InMn-LDH (layered double hydroxides) nanosheets were prepared by preparing solutions of 0.05 M Mn(NO 3 ) 2 .4H 2 O, 0.05 M of In(NO 3 ) 3 .6H 2 O, 0.08 M of NaNO 3 and 0.1 M of NH 4 F in 125 mL of N 2 -saturated deionized water. After that, 20 µL of hydrogen peroxide (H 2 O 2 ) was poured, and then 40 mL of N 2 saturated NaOH solution (0.08 M) was added slowly while stirring on the magnetic hotplate. The reaction was maintained at room temperature for 15 h under a N 2 atmosphere. InMn-LDH nanosheets were collected and dried under vacuum conditions. Secondly, 5 mg of the synthesized LDH nanosheets and 8.2 mg of Se particles were dissolved in 20 mL of deionized water, and then 10 mg of NaBH 4 under stirring conditions. After 15 min of the stirring, the mixed solutions were then poured into hydrothermal reactor which was set at 190 • C for 15 h. Then, the autoclave was cooled down to room temperature, and the precipitates were collected by filtration and rinsed with deionized water multiple times. Finally, these precipitates were dried and stored in air-sealed vials for further processing.

Characterizations
X-ray diffraction (XRD) in the range of 20-90 • employing a Cu K radiation source (=1.5406) was used to assess the phase identification and lattice parameters of the developed nano electrode material. The surface morphology and elemental makeup of In2MnSe4 were explored using a scanning electron microscope (SEM) coupled with energy dispersive X-Ray spectroscopy (EDX) (Nano Nova SEMa-450). The functional group on the surface of the materials was confirmed via Fourier transform infrared spectroscopy (FTIR) using Alpha FTIR spectrometer, and the Brunauer Emmett Teller (BET) method measured the specific surface area of the as-synthesized material using the Micromeritics ASAP-2020 instrument.

Ink Preparation and Electrochemical Measurements
In this study, the In 2 MnSe 4 working electrode was fabricated hydrothermally and grown on the NF substate via the drop cast method. For this purpose, the NF was divided into 1 × 1 cm pieces and washed. For ink preparation in water, isopropanol and 10 µL of Nafyon (5 weight percent) were mixed to make a dispersed solution after ultrasonification for 1 h. Catalyst ink was applied on the clean and already-treated NF substrate by the drop-casting method and dried at ambient temperature before being used. Three electrode electrochemical experiments were performed using a PGSTAT (AUTOLAB-204) electrochemical workstation (Metrohm, Herisau, Switzerland), having a platinum wire, Ag/AgCl electrode, and the fabricated electrode act as a counter, reference, and working electrode, respectively. Various complementary electrochemical techniques were used; the measurements included chronoamperometry (CA), linear scan voltammetry (LSV), electrochemical impedance spectroscopy (EIS), cyclic voltammetry (CV), and electrochemical active surface area (ECSA). The CV was carried out at a scan rate of 5 mV s −1 , with both positive and negative potentials utilized in the cyclic voltametric experiments, while only the positive potential was used in the LSV. Equation (1) was used to calculate the RHE potential from the Ag/AgCl potential: The overpotential was determined by using the Formula (2): From 1000 kHz to 1 Hz, electrochemical impedance measurements were carried out utilizing 5 mV sinusoidal voltages. The Faradaic efficiency (FE) was calculated using the total charge (Q) and total oxygen generation (O 2 ) (nO 2 ) with the following Equation (3): The polarization curvature on a Tafel graph was used to monitor the catalytic and kinetics of the fabricated material with the following Equation (4): Here, η, α, n, j and F are corresponding overpotentials, charge transfer coefficient, number of etaking part in the reaction, current density, and Faraday constant, respectively. Equation (5) was used to calculate the TOF value of In 2 MnSe 4 coated on nickel foam for the OER process.
Here, m = number of moles of catalytic material, I = current in amperes, and F = Faraday constant.
The surface area of the catalyst was measured by using cyclic voltammetry recording at different scan rates in the non-faradic region in order to measure the electrical double layer capacitance (Cdl) by plotting the change in current density vs. scan rate. The resultant Cdl value has a direct relation with the electrochemical active surface area. The electrochemical impedance approach was used in alkaline solution vs. Ag/AgCl at a voltage of 0.5 V in the frequency range of 0.01-100 kHz. The Rct and Rs values were calculated using the NOVA 2.1 software via PGSTAT-204(Metrohm, Herisau, Switzerland).

Structural Analysis
The crystal structure, geometry, purity, and orientation of as-prepared indium manganese selenide were analyzed by executing XRD characterization as shown in Figure 1.  (6) [42].
where D represents average crystallite size, K constant (0.9), λ is wavelength of X-ray, β depicts line broadening at FWHM and θ = Bragg's angle. The calculated crystalline size of the synthesized particle using Scherrer's formula was 68.3 nm. ⁄ where D represents average crystallite size, K constant (0.9), λ is wavelength of X-ray depicts line broadening at FWHM and θ = Bragg's angle. The calculated crystalline size the synthesized particle using Scherrer's formula was 68.3 nm. FTIR analysis was employed to investigate the purity and functional groups of synthesized nanomaterials. The observed spectrum also confirmed the existence of me in FTIR spectrum of In2MnSe4 nanomaterials (400-4000 cm −1 ) as shown in Figure 2. Fro the spectra, the characteristic peaks of vibrational bands positioned at 428.07 cm −1 , 527 cm −1 , and 773.94 cm −1 correspond to the Mn-Se, In-Se, and Se-Mn-Se bond vibrations, spectively, corroborating the effective synthesis of the In2MnSe4 nanomaterials, while additional peak located at 1205.70 cm −1 was due to N-O stretching due to the presence NH4F. FTIR analysis was employed to investigate the purity and functional groups of the synthesized nanomaterials. The observed spectrum also confirmed the existence of metal in FTIR spectrum of In 2 MnSe 4 nanomaterials (400-4000 cm −1 ) as shown in Figure 2. From the spectra, the characteristic peaks of vibrational bands positioned at 428.07 cm −1 , 527.81 cm −1 , and 773.94 cm −1 correspond to the Mn-Se, In-Se, and Se-Mn-Se bond vibrations, respectively, corroborating the effective synthesis of the In 2 MnSe 4 nanomaterials, while the additional peak located at 1205.70 cm −1 was due to N-O stretching due to the presence of NH 4 F.

Morphological, Elemental, and Textural Analysis
The surface dimension, shape, and particle size of the produced material were investigated using scanning electron microscopy (SEM). SEM micrographs indicates that the material exhibited a flowery shape with a definite crystalline boundary as shown in Figure 3a,b. These flowery nanocrystals are responsible for plenty of electrochemically active sites and facilitate the redox reactions at the electrode, thus showing significantly outstanding electrochemical performances for OER. The crystallite size of the fabricated nanoparticle was 83.28 nm, calculated from an SEM micrograph by IMAGE.J software as shown in Figure 3c,d using plot profile and surface plot.

Morphological, Elemental, and Textural Analysis
The surface dimension, shape, and particle size of the produced material were investigated using scanning electron microscopy (SEM). SEM micrographs indicates that the material exhibited a flowery shape with a definite crystalline boundary as shown in Figure  3a,b. These flowery nanocrystals are responsible for plenty of electrochemically active sites and facilitate the redox reactions at the electrode, thus showing significantly outstanding electrochemical performances for OER. The crystallite size of the fabricated nanoparticle was 83.28 nm, calculated from an SEM micrograph by IMAGE.J software as shown in Figure 3c,d using plot profile and surface plot.
The elemental compositions were studied by using energy-dispersive X-ray spectroscopy (EDS) analysis as shown in Figure 3e. The examination reveals that the synthesized products include all of the individual elements, such as In, Mn, and Se, that are consistently aligned as shown in Figure 3e. The obtained results show that the synthesized product has no additional interfering components.
A nitrogen adsorption-desorption experiment was also used to investigate the surface attributes of the nanostructure, such as specific surface area (SSA) and average pore size as shown in Figure 4. The surface area of the In2MnSe4 was 30 m 2 g −1 with a pore size and pore volume of 0.002 A Å , and 0.25 cm 3 g −1 , respectively. A high surface area stimulates the formation of more vacant sites on the surface of the fabricated catalyst. As a result, the obtained material was a suitable electrocatalyst for the oxygen evolution reaction (OER).  The elemental compositions were studied by using energy-dispersive X-ray spectroscopy (EDS) analysis as shown in Figure 3e. The examination reveals that the synthesized products include all of the individual elements, such as In, Mn, and Se, that are consistently aligned as shown in Figure 3e. The obtained results show that the synthesized product has no additional interfering components.
A nitrogen adsorption-desorption experiment was also used to investigate the surface attributes of the nanostructure, such as specific surface area (SSA) and average pore size as shown in Figure 4. The surface area of the In 2 MnSe 4 was 30 m 2 g −1 with a pore size and pore volume of 0.002 Å, and 0.25 cm 3 g −1 , respectively. A high surface area stimulates the formation of more vacant sites on the surface of the fabricated catalyst. As a result, the obtained material was a suitable electrocatalyst for the oxygen evolution reaction (OER).

Electrical Measurement
I-V curves of synthetic products with potential ranges of 0-20 V were measured at ambient temperature. For terminal voltages, the graph clearly shows that the nanomaterials exhibited a higher current value. The ohmic quality of the produced nanocomposite was also proven by the curve. The electrical conductivity (3.1 × 10 2 moh) of the forward biased region was calculated using the following Equation (7): where I = current, V = applied voltage, L = the thickness of the pellet, and A = the crosssectional area of the pellets. The variation as a function of current concerning the voltage is seen in Figure 5. The grown nanostructure performs an excellent choice for OER because of its ohmic nature.

σ I L V A ⁄
where I = current, V = applied voltage, L = the thickness of the pellet, and A = t sectional area of the pellets. The variation as a function of current concerning the is seen in Figure 5. The grown nanostructure performs an excellent choice for OER of its ohmic nature.

Electrochemical Study
The porous flowery-shaped In2MnSe4 nanostructure has been used for the f for an oxygen evolution reaction. A three-electrode configuration was used to loaded NF as a working electrode for the oxygen evolution reaction in an alkaline at room temperature. Electrodes were categorized into two categories based on th ture such as flat surface electrodes and 3D electrodes. The flat-surface electrodes glassy carbon (GC) substrates and indium-doped tin oxide (ITO) substrates, a Cu/Ti foil, allow for single-way electrolyte penetration, controlling the reaction on face of the catalyst due to the non-porous nature. Furthermore, the 3D electrode in all active species in the catalytic process, such as carbon cloth/paper (CC/CP) and (NF), and allows electrolytes to permeate in all dimensions via various pathway The most used electrode, for example, is the GC/GP electrode, which indi catalyst's initial activity. Among all the options, the NF demonstrates high electro performance due to its high conductivity, and the performance of the nickel foam electrode has a significant impact on the rate of reaction due to its degree of we structure, electrolyte, and conductivity. The loading of the catalyst on the nickel f kept constant for the uniformity during dipping the electrode in 8 mL electrolyte geometrical surface area (0.5 cm 2 ) of the nickel foam electrode was taken into while measuring the current density.

Electrochemical Study
The porous flowery-shaped In 2 MnSe 4 nanostructure has been used for the first time for an oxygen evolution reaction. A three-electrode configuration was used to test the loaded NF as a working electrode for the oxygen evolution reaction in an alkaline solution at room temperature. Electrodes were categorized into two categories based on their structure such as flat surface electrodes and 3D electrodes. The flat-surface electrodes, such as glassy carbon (GC) substrates and indium-doped tin oxide (ITO) substrates, as well as Cu/Ti foil, allow for single-way electrolyte penetration, controlling the reaction on the surface of the catalyst due to the non-porous nature. Furthermore, the 3D electrode integrates all active species in the catalytic process, such as carbon cloth/paper (CC/CP) and Ni foam (NF), and allows electrolytes to permeate in all dimensions via various pathways.
The most used electrode, for example, is the GC/GP electrode, which indicates the catalyst's initial activity. Among all the options, the NF demonstrates high electrochemical performance due to its high conductivity, and the performance of the nickel foam working electrode has a significant impact on the rate of reaction due to its degree of wettability, structure, electrolyte, and conductivity. The loading of the catalyst on the nickel foam was kept constant for the uniformity during dipping the electrode in 8 mL electrolyte, and the geometrical surface area (0.5 cm 2 ) of the nickel foam electrode was taken into account while measuring the current density.
The porous nature, high electrical conductivity and good morphology of the catalyst species boosted OER activity, in terms of the Tafel slope, onset potential, overpotential, ECSA, and stability. Cyclic voltammetry was carried out using a stationary electrode in 1.0 M KOH electrolyte at room temperature, saturated with nitrogen, in a potential range (1 to −1 vs. Ag/AgCl), with a scan rate of 5 mV s −1 to achieve an overpotential of 259 mV to attain a current density of 10 mA cm −2 . A typical cyclic voltammogram for In 2 MnSe 4 is shown in Figure 6a.
The porous nature, high electrical conductivity and good morphology of the catalyst species boosted OER activity, in terms of the Tafel slope, onset potential, overpotential, ECSA, and stability. Cyclic voltammetry was carried out using a stationary electrode in 1.0 M KOH electrolyte at room temperature, saturated with nitrogen, in a potential range (1 to −1 vs. Ag/AgCl), with a scan rate of 5 mV s −1 to achieve an overpotential of 259 mV to attain a current density of 10 mA cm −2 . A typical cyclic voltammogram for In2MnSe4 is shown in Figure 6a.  Figure 6b displays the Tafel slope of In2MnSe4 to confirm the kinetics of the reaction, and the calculated Tafel slope was found to be 86 mV/dec as represented as in Figure 6b. The turnover frequency was another important parameter to investigate the OER performance of the fabricated material, and it shows a direct relation with OER performance, i.e., the higher the TOF, the higher the OER activity will be. The calculated TOF of the In2MnSe4 was 0.00348 s −1 . The subsequent results were compared with the already reported results as presented in Table 1.   Figure 6b displays the Tafel slope of In 2 MnSe 4 to confirm the kinetics of the reaction, and the calculated Tafel slope was found to be 86 mV/dec as represented as in Figure 6b. The turnover frequency was another important parameter to investigate the OER performance of the fabricated material, and it shows a direct relation with OER performance, i.e., the higher the TOF, the higher the OER activity will be. The calculated TOF of the In 2 MnSe 4 was 0.00348 s −1 . The subsequent results were compared with the already reported results as presented in Table ??. Electrochemical impedance spectroscopy was also employed to study the electrochemical catalytic features of fabricated material, as shown in Figure 6c. The high-frequency range showed the solution resistance (Rs) at the semicircle's origin, the mid-frequency range showed the charge transfer resistance (Rct) from the semicircle's diameter, and the low-frequency range showed the ion diffusive zone as a vertical line. The resultant Rs and Rct values are 12.73 and 1.20 ohms, respectively, according to the Nyquist impedance plot as shown in Figure 6c, indicating the high conductivity of the designed material.
In addition to the non-Faradaic zone, an electrochemical active surface area (ECSA) study was investigated using CV curves at different scan rates between 0 and 0.1 V vs. Ag/AgCl, as shown in Figure 7a. The resultant electrical double layer capacitance of 0.66 mF calculated by plotting the scan rate vs. change in the current density. The obtained double layer capacitance was used to calculate the ECSA of In 2 MnSe 4 , and was found to be 16.65 cm 2 , considering the specific capacific capacitance of the 0.04 mF cm −2 using equation ECSA = Cdl/Cs (specific capacitance). Electrochemical impedance spectroscopy was also employed to study the electrochemical catalytic features of fabricated material, as shown in Figure 6c. The high-frequency range showed the solution resistance (Rs) at the semicircle's origin, the mid-frequency range showed the charge transfer resistance (Rct) from the semicircle's diameter, and the low-frequency range showed the ion diffusive zone as a vertical line. The resultant Rs and Rct values are 12.73 and 1.20 ohms, respectively, according to the Nyquist impedance plot as shown in Figure 6c, indicating the high conductivity of the designed material.
In addition to the non-Faradaic zone, an electrochemical active surface area (ECSA) study was investigated using CV curves at different scan rates between 0 and 0.1 V vs. Ag/AgCl, as shown in Figure 7a. The resultant electrical double layer capacitance of 0.66 mF calculated by plotting the scan rate vs. change in the current density. The obtained double layer capacitance was used to calculate the ECSA of In2MnSe4, and was found to be 16.65 cm 2 , considering the specific capacific capacitance of the 0.04 mF cm −2 using equation ECSA = Cdl/Cs (specific capacitance). In addition, the newly synthesized ln2MnSe4 catalyst showed substantial OER stability. The chronoamperometry was employed to measure the working electrodes for longterm operational catalytic activity, and the results revealed that it was stable for 30 h with no noticeable decline in current density values, attributed to the electrode's high stability. This demonstrates potential for practical use in water electrolysis as shown in Figure 8. To prove the structure of the synthesized material, XRD and SEM were performed, which confirmed that the structure and morphology remained same after 30 h of stability as shown in Figure 8b,c. Hence, the enhanced electrochemical performance of the synthesized materials was due to the good flower-shaped surface morphology, because the resultant flower-shaped morphology provides more active sites on the surface of the In addition, the newly synthesized ln 2 MnSe 4 catalyst showed substantial OER stability. The chronoamperometry was employed to measure the working electrodes for long-term operational catalytic activity, and the results revealed that it was stable for 30 h with no noticeable decline in current density values, attributed to the electrode's high stability. This demonstrates potential for practical use in water electrolysis as shown in Figure 8. To prove the structure of the synthesized material, XRD and SEM were performed, which confirmed that the structure and morphology remained same after 30 h of stability as shown in Figure 8b,c. Hence, the enhanced electrochemical performance of the synthesized materials was due to the good flower-shaped surface morphology, because the resultant flower-shaped morphology provides more active sites on the surface of the fabricated material as confirmed via SEM micrographs, high surface area, and high conductivity as indicated via BET and I-V curves, respectively. fabricated material as confirmed via SEM micrographs, high surface area, and high conductivity as indicated via BET and I-V curves, respectively.

Conclusions
In this study, a facile and one-pot hydrothermal manufacturing technique was employed to produce a novel, economical nanostructured metal selenide (In2MnSe4), and was characterized by different analytical techniques. For electrochemical measurements, the fabricated material was deposited on Ni foam that functions as a high-performance oxygen evolution reaction. The fabricated In2MnSe4 electrode has the lowest overpotential of 259 mV with a smaller Tafel slope value of 86 mV dec −1 , and has the long-term durability of 30 h. Our research has shown novel methodologies for generating and fabricating In2MnSe4 nanoarchitecture that have low-cost, high-efficiency, and customizable catalysts for clean fuel generation.

Conclusions
In this study, a facile and one-pot hydrothermal manufacturing technique was employed to produce a novel, economical nanostructured metal selenide (In 2 MnSe 4 ), and was characterized by different analytical techniques. For electrochemical measurements, the fabricated material was deposited on Ni foam that functions as a high-performance oxygen evolution reaction. The fabricated In 2 MnSe 4 electrode has the lowest overpotential of 259 mV with a smaller Tafel slope value of 86 mV dec −1 , and has the long-term durability of 30 h. Our research has shown novel methodologies for generating and fabricating In 2 MnSe 4 nanoarchitecture that have low-cost, high-efficiency, and customizable catalysts for clean fuel generation.