Liquid-Metal-Mediated Electrocatalyst Support Engineering toward Enhanced Water Oxidation Reaction

Functional and robust catalyst supports are vital in the catalysis field, and the development of universal and efficient catalyst support is essential but challenging. Traditional catalyst fabrication methods include the carbonization of ordered templates and high−temperature dehydration. All these methods involve complicated meso−structural disordering and allow little control over morphology. To this end, a eutectic GaInSn alloy (EGaInSn) was proposed and employed as an intermediate to fabricate low−dimensional ordered catalyst support materials. Owing to the lower Gibbs free energy of Ga2O3 compared to certain types of metals (e.g., Al, Mn, Ce, etc.), we found that a skinny layer of metal oxides could be formed and exfoliated into a two−dimensional nanosheet at the interface of liquid metal (LM) and water. As such, EGaInSn was herein employed as a reaction matrix to synthesize a range of two−dimensional catalyst supports with large specific surface areas and structural stability. As a proof−of-concept, Al2O3 and MnO were fabricated with the assistance of LM and were used as catalyst supports for loading Ru, demonstrating enhanced structural stability and overall electrocatalytic performance in the oxygen evolution reaction. This work opens an avenue for the development of functional support materials mediated by LM, which would play a substantial role in electrocatalytic reactions and beyond.


Introduction
Electrochemical energy conversion and storage are important solutions in the pursuit of attaining the green utilization of renewables in the form of chemical energy. In these areas, electrocatalytic water splitting has long been considered an indispensable method for producing green hydrogen (H 2 ) with the use of renewable electricity [1][2][3][4]. Unfortunately, the question of how to develop functional and robust electrocatalysts with excellent overall performance remains a scientific issue. Most commercial electrocatalysts are usually produced by dispersing active metal species in or on a support material to maximize the overall catalyst stability, durability, and catalytic activity. Furthermore, the electronic structure of an electrocatalyst can be well modulated through metal−support interaction, which can be accessed through a wise choice of a range of different types of support materials. Support materials are therefore rather significant in the development of functional electrocatalysts-a consensus that has been widely accepted within the electrocatalysis community, as an increasing number of efforts concentrated on support materials have been published very recently [5][6][7][8][9][10]. Most of these works typically focus on the tuning of metal−support interaction, while studies on the design and fabrication of functional support materials are rarely reported. Meanwhile, traditional catalyst support fabrication typically relies on hydrothermal reactions, template methods, high-temperature dehydration, etc., which involve complicated meso−structural disordering and have morphologies which are difficult to control [11][12][13][14]. The development of reliable production methods for catalyst supports is urgently needed and has many scientific implications.
In the meantime, we found that lots of catalyst supports that play significant roles in thermal catalysis and electrocatalysis are usually fabricated via conventional methods such as high−temperature decomposition and chemical vapor deposition. The specific surface areas and robust structure stability of the supports are not necessarily well sustained through such harsh reaction conditions. Therefore, finding an alternative catalyst support fabrication strategy with mild reaction conditions and well−modulated structures is essential.
In the present work, gallium−based liquid metal was employed for the synthesis of δ−Al 2 O 3 and MnO, in which the LM serves as a reaction environment and can be repeatedly used after proper and easy separation, featuring low−cost, readily available, and environmentally friendly. This method represents a novel way to produce δ−Al 2 O 3 and MnO precursors at room temperature. The precursors can be generated from the interface of EGaInSn droplets with H 2 O, and then, the product can be collected after being sintered in a furnace. This low−level aggregation of δ−Al 2 O 3 and MnO exhibits quasi−two−dimensional structures with a large surface area, as well as thermal stability, which provides an opportunity for the fabrication of catalyst supports. This work investigated the electrocatalytic performance of δ−Al 2 O 3 and MnO against the performance of Ru−loaded supports to demonstrate that Al 2 O 3 and MnO are versatile and advantageous catalyst supports and that Ru can be loaded to improve performance. A detailed analysis was shown for a better understanding of the performance of this kind of material.

Catalyst Support Fabrication (Al 2 O 3 and MnO)
Eutectic GaInSn alloy was prepared by co−melting a particular weight amount of Ga (65%), In (24%), and Sn (11%). In the preparation of Al 2 O 3 support, EGaInSn (g) and Al foil (g) were ground in an Argon−filled glove box where the oxygen level and water level were controlled at levels lower than~2 ppm. The grinding process usually takes 30 min to fully and completely finish the alloying process, and the alloy surface becomes shiny and metallic. For concentrations exceeding 20% aluminum, solid Al lumps were observed, which means the amount of aluminum was excessive. In the subsequent step, nearly 2 g of the as−prepared Ga−Al alloy was transferred into a glass vial. Then, 2 mL of deionized (DI) water was rapidly added to the glass vials (volume 7 mL) when the glass vial was removed from the Argon−filled glovebox. The amount of DI water needed to cover the metal droplet surface to maximize the interfacial reaction area. The reaction occurred immediately when DI water was added, and then continued for nearly 30 min. On the surface of EGaInSn droplets, 2D nanosheets were formed. The hydrogen bubbles instantly formed on the surface of droplets and accordingly, the metal oxide nanosheets were exfoliated. To obtain a pure sample, the sample was allowed to stand for 15 min. The suspension was transferred to an oven and dried at 80 • C overnight to obtain the precursor Al(OH) 3 . Finally, the as−prepared Al(OH) 3 was calcined at 1000 • C (ramping rate of 1 • C min −1 ) in a Muffle furnace for 15 h to obtain the Al 2 O 3 . The metals Ga, In, Sn, Al, and Mn were purchased from Sigma Aldrich and used directly without further purification.
In terms of MnO synthesis, 2 g of EGaInSn and 0.066 g of manganese powder were ground in an Ar−filled glovebox for 15 min to form a uniform and skinny alloy. Then, the formed alloys were transferred to a vial and moved from the glove box, during which, the water was added instantly. After the 30 min reaction and then being stewed for 15 min, the suspension was dried at 100 • C overnight. Finally, the MnO was obtained after calcination at 400 • C in a Muffle furnace for 4 h.

Physical Characterization:
Powder X−ray diffraction (XRD) patterns of the as−prepared samples were tested by using a PANalytical Empyrean X−ray diffraction meter with Cu Kα radiation (λ = 0.15406 nm) from 20 • to 80 • . For XRD measurement, samples were ground with a mortar and pestle and then transferred onto a sample holder. The surface morphologies and electronic structures of the as−prepared samples were detected using scanning electron microscopy (SEM) and transmission electron microscopy (TEM, JEOL−2010). Gatan microscopy 2.32 was used to process the captured images. X−ray photoelectron spectroscopy was performed using a Thermo Fisher KAlpha system photoelectron spectrometer (100 Analyser, SPECS, Berlin, Germany, Alka X-Rays).

Electrochemical Characterization
Electrochemical measurements were carried out on a three−electrode setup (PINE Research Instrument Inc. Durham, NC, USA). A glass carbon electrode, a 1 M Hg/HgO electrode, and a graphite rod were used as the working electrode, reference electrode, and counter electrode, respectively. For the preparation of catalyst ink, a 2.0 mg sample was dispersed into a 500 µL mixed solution that contained 16 µL of Nafion solution, 100 µL of isopropanol, and 384 µL of DI water and sonicated for 4 h to form a homogeneous ink. Then, 10 µL of as−prepared catalyst ink was dropped onto the GC electrode (mass loading 0.204 mg cm −2 ) and dried at room temperature. A multichannel potentiostat (VSP-300, BioLogic Science Instrument) collected all the electrochemical data. For the test of OER, cyclic voltammetry was collected at a sweeping rate of 50 mV s −1 . Linear sweep voltammetry (LSV) was recorded at the scan rate of 5 mV s −1 with a 1600 rpm rotating speed.

Results and Discussion
The catalyst support was synthesized successfully via a solution reaction followed by calcination, in which liquid metal is served as a reaction mediator. Figure 1a shows the schematic illustration of the synthetic procedure, of which the details can be found in the Experimental Section. Specifically, a certain amount of the metals (Al or Mn) and the commercial EGaInSn were ground to form uniform alloys in which the weight ratio of Al or Mn was kept at 20%. The formed alloy droplets were transferred to glass vials in the presence of DI water, and the reaction went ahead at 100 • C for 0.5 h to obtain the precursors. Due to the Gibbs free energy (∆G f ) for Al 2 O 3 being lower than that of Ga 2 O 3 , a skinny layer of Al 2 O 3 was instantly generated at the surface of the alloyed droplets [21,24,25]. In the presence of water droplets, the metal hydroxides were formed as a white aerogel, and the unreacted LM could be recycled for further utilization, indicating that the LM principally served as a reaction matrix and was not involved in the reaction. The metal oxide supports could be obtained accordingly after the as-prepared metal hydroxides' sintering. The X−ray diffraction patterns of the as−prepared δ−Al 2 O 3 and MnO are shown in Figure 1b      Furthermore, X−ray photoelectron spectroscopy (XPS) measurements were taken to characterize the chemical composition of the as−prepared supports. The Al 2p spectrum, as shown in Figure 3a, exhibited a prominent peak at the binding energy of 74.47 eV, which could be attributed to the oxidation state (+3) of Al. Meanwhile, the O 1s spectra in Figure 3b  Furthermore, X−ray photoelectron spectroscopy (XPS) measurements were taken to characterize the chemical composition of the as−prepared supports. The Al 2p spectrum, as shown in Figure 3a, exhibited a prominent peak at the binding energy of 74.47 eV, which could be attributed to the oxidation state (+3) of Al. Meanwhile, the O 1s spectra in Figure 3b    Based on the above−mentioned discussions, the support growth principle can be reasonably deduced to demonstrate the following reaction equations: 2Al + 6H2O →2Al(OH)3 + 3H2 (1) 2Al(OH)3 →Al2O3 + 3H2O (2) Mn + 2H2O → Mn(OH)2 + H2  Based on the above−mentioned discussions, the support growth principle can be reasonably deduced to demonstrate the following reaction equations: 2Al + 6H 2 O →2Al(OH) 3 + 3H 2 (1) The LM-assisted interface reactions between metal and water droplets at intermediate temperature give rise to the formation of metal hydroxides, which are described in Equations (1) and (3). Subsequently, the annealing process at high−temperature conditions promotes the phase transformation from metal hydroxides to metal oxides, leading to the generation of metal oxide supports.
Next, we discuss the role of metal oxides as supporting materials in electrocatalytic reactions, which is illustrated in Figure 4. Accordingly, the as−prepared metal oxides were used as supports to immobilize metal nanoparticles to verify their applicability.

Conclusions
In summary, we demonstrated a sustainable method to synthesize (δ−Al2O3 and MnO) catalyst supports via the mediation of EGaInSn liquid metals. The precursor of a metal hydroxide nanosheet can be formed on the liquid metal/water interface in the presence of water droplets at room temperature, and these can be easily exfoliated and transformed into metal oxide supports via a simple annealing process. Furthermore, the quasitwo-dimensional δ−Al2O3 and MnO with high specific surface areas were employed as catalyst supports, whereby the structural stability and oxygen evolution kinetics were improved through the immobilization of Ru nanoparticles. This work not only offers an easy quasi−two−dimensional catalyst support fabrication method mediated by LM but also demonstrates its vital applications in electrocatalytic reactions.

Conclusions
In summary, we demonstrated a sustainable method to synthesize (δ−Al 2 O 3 and MnO) catalyst supports via the mediation of EGaInSn liquid metals. The precursor of a metal hydroxide nanosheet can be formed on the liquid metal/water interface in the presence of water droplets at room temperature, and these can be easily exfoliated and transformed into metal oxide supports via a simple annealing process. Furthermore, the quasi-two-dimensional δ−Al 2 O 3 and MnO with high specific surface areas were employed as catalyst supports, whereby the structural stability and oxygen evolution kinetics were improved through the immobilization of Ru nanoparticles. This work not only offers an easy quasi−two−dimensional catalyst support fabrication method mediated by LM but also demonstrates its vital applications in electrocatalytic reactions.