Surface/Interface Engineering for Constructing Advanced Nanostructured Photodetectors with Improved Performance: A Brief Review

Semiconductor-based photodetectors (PDs) convert light signals into electrical signals via a photon–matter interaction process, which involves surface/interface carrier generation, separation, and transportation of the photo-induced charge media in the active media, as well as the extraction of these charge carriers to external circuits of the constructed nanostructured photodetector devices. Because of the specific electronic and optoelectronic properties in the low-dimensional devices built with nanomaterial, surface/interface engineering is broadly studied with widespread research on constructing advanced devices with excellent performance. However, there still exist some challenges for the researchers to explore corresponding mechanisms in depth, and the detection sensitivity, response speed, spectral selectivity, signal-to-noise ratio, and stability are much more important factors to judge the performance of PDs. Hence, researchers have proposed several strategies, including modification of light absorption, design of novel PD heterostructures, construction of specific geometries, and adoption of specific electrode configurations to modulate the charge-carrier behaviors and improve the photoelectric performance of related PDs. Here, in this brief review, we would like to introduce and summarize the latest research on enhancing the photoelectric performance of PDs based on the designed structures by considering their surface/interface engineering and how to obtain advanced nanostructured photo-detectors with improved performance, which could be applied to design and fabricate novel low-dimensional PDs with ideal properties in the near future.


Introduction
In recent years, following the developmental step forward of microelectronics technology, optoelectronic technology, as one of burgeoning advanced technologies, has developed rapidly and will have far-reaching effects on the lives of human beings. It involves optical display, optical storage, lasers, and other fields and is the core technology of the future information industry. It also has significant strategic importance for the state economy, technology, and defense. Various materials with different structures have attracted much more attention for their potential applications in integrated nano-or micro-optoelectronics, including light emitting diodes (LEDs) [1], solar cells [2,3], sensors [4,5], field-effect transistors (FETs) [6,7], photodetectors [8][9][10], and so on.
At present, smart photoelectric devices with excellent performance play important roles in our daily life, scientific research frontiers, high school education, and biomedical fields, and so on.
It can be observed that charge carrier generation, diffusion, and recombination modulation are all very important considerations in the construction of high-efficiency PDs [46]. The sensitivity, response speed, spectral selectivity, signal-to-noise ratio, and stability of detection are much more important factors to judge the performance of PDs [34].
To rationally implement surface and interface engineering in the PDs' design, an understanding of the effects of surface and interface on reactions is required. In this section, we highlight a few of the key factors that need to be taken into account when designing nanostructures and their hybrid nanostructures. The carrier behaviors such as generation, recombination, separation, and collection are closely related to the surface/interface of devices, especially for the nanostructured devices; thus, surface/interface engineering of nanostructured materials is critically important for influencing the performance of the fabricated devices, and how to suitably apply surface/interface properties of nanostructured PDs for building advanced devices needs continuous exploration. In this review, how the surface/interface engineering improves the performance of the constructed nanostructured PDs is demonstrated theoretically through a review of the literature.

Surface and Interface States
A surface could be defined as atomic layers that do not have three-dimensional continuous environment of bulk materials, three-dimensional continuous environment, or the periodicity of the infinite lattice that is destroyed by the existence of nanostructured surface. For crystal structures, in the direction of the vertical surface, the potential energy of lattice atoms could not have corresponding symmetry, and some new eigenvalues could be obtained in the Hamiltonian characteristic value when the Schrodinger equation is applied through the theory of quantum mechanics [47]. A new energy level could appear and be defined as a surface state, as shown in Figure 1. There are actually two kinds of surface states: intrinsic and external surface states. The intrinsic one is the surface state without foreign impurities, and the other is due to the existent of impurities from adsorbed atoms or other imperfections on the surface. (1) Generation of the photo-induced carriers in the case of external light radiation; (2) Separation, transportation, and multiplication of photo-induced charge carriers derived by the applied electric field or built-in electric field formed at the interface of the heterojunction; (3) Collection of the photocurrent generated by photo-excited carriers at both ends of electrodes, thus realizing the detection of external light radiation.
It can be observed that charge carrier generation, diffusion, and recombination modulation are all very important considerations in the construction of high-efficiency PDs [46]. The sensitivity, response speed, spectral selectivity, signal-to-noise ratio, and stability of detection are much more important factors to judge the performance of PDs [34].
To rationally implement surface and interface engineering in the PDs' design, an understanding of the effects of surface and interface on reactions is required. In this section, we highlight a few of the key factors that need to be taken into account when designing nanostructures and their hybrid nanostructures. The carrier behaviors such as generation, recombination, separation, and collection are closely related to the surface/interface of devices, especially for the nanostructured devices; thus, surface/interface engineering of nanostructured materials is critically important for influencing the performance of the fabricated devices, and how to suitably apply surface/interface properties of nanostructured PDs for building advanced devices needs continuous exploration. In this review, how the surface/interface engineering improves the performance of the constructed nanostructured PDs is demonstrated theoretically through a review of the literature.

Surface and Interface States
A surface could be defined as atomic layers that do not have three-dimensional continuous environment of bulk materials, three-dimensional continuous environment, or the periodicity of the infinite lattice that is destroyed by the existence of nanostructured surface. For crystal structures, in the direction of the vertical surface, the potential energy of lattice atoms could not have corresponding symmetry, and some new eigenvalues could be obtained in the Hamiltonian characteristic value when the Schrodinger equation is applied through the theory of quantum mechanics [47]. A new energy level could appear and be defined as a surface state, as shown in Figure  1. There are actually two kinds of surface states: intrinsic and external surface states. The intrinsic one is the surface state without foreign impurities, and the other is due to the existent of impurities from adsorbed atoms or other imperfections on the surface. Semiconductor surface research is mainly concerned with various electrical properties of surface phenomena. These phenomena involve the free carriers in the space charge region, surface states, and their mutual interactions. Although the free carrier transport in the space charge layer should be paid considerable attention, the most concerted effort in the study of the surface electrical properties has been directed towards the surface states [48]. Much research on semiconductor surfaces caused by cleaving in ultrahigh vacuum suggested that the formation of surface states is attributed to dangling bonds at the surface [49]. According to a previous report [47], the schematic diagram of the surface level is shown in Figure 1. The surface states could also be divided into donor states or acceptor states based on the behavior of the electrons. Surface states could capture, scatter generated carriers, and Semiconductor surface research is mainly concerned with various electrical properties of surface phenomena. These phenomena involve the free carriers in the space charge region, surface states, and their mutual interactions. Although the free carrier transport in the space charge layer should be paid considerable attention, the most concerted effort in the study of the surface electrical properties Nanomaterials 2020, 10, 362 4 of 24 has been directed towards the surface states [48]. Much research on semiconductor surfaces caused by cleaving in ultrahigh vacuum suggested that the formation of surface states is attributed to dangling bonds at the surface [49]. According to a previous report [47], the schematic diagram of the surface level is shown in Figure 1. The surface states could also be divided into donor states or acceptor states based on the behavior of the electrons. Surface states could capture, scatter generated carriers, and influence electric field effect, and the results could be effective photon capture, carrier generation, and combination centers, which controls surface properties of the absorbed photons and generated carriers. Scattered carriers influence surface mobility, thus affecting surface conductance.
An interface could be defined as the interface between heterostructure phases, similar to surface states. Interface states that are introduced at the interface state occur at the interface where two heterostructure media exist and contact. Thus, the continuous environment of atoms or lattice structures is destroyed by the existence of other substances. Hence, the interface states could be introduced by other atoms, lattice mismatch, interface roughness, and thermal expansion of two materials' interface. Generally speaking, there are two interface states: donor and recipient. Considering energy levels of the built heterostructures, the existing interface energy levels greatly influence carrier transport behaviors, which controls performance of the devices. The performance of the photodetector devices could be considerably improved by considering interface carrier transport properties by designing optimal heterostructures.
Commonly, interface engineering includes surface charge transfer, charge injection, and collection on the metal electrode/semiconductor interface and carrier bound state on the dielectric/semiconductor interface. On the other hand, there are a large number of defects in lattice structure, including vacancies, adsorbed atoms, grain boundaries, and impurities. Interfaces and defects have a critical influence on the properties and operational stability of metal halide perovskite optoelectronic devices. Therefore, interface and defect engineering is crucial to control the behavior of the charge carriers and to grow high quality, defect-free perovskite crystals. Yang et al. summarized the strategies of interface and defect engineering in perovskite solar cells and light-emitting diodes [50]. Due to the atomic thickness and super high specific surface area of two-dimensional TMDCs, the interface of TMDCs plays a decisive role in the device performance. Chen and other researchers summarized and highlighted advances in TMDC interfaces and defect engineering and applications in electronic devices. Various appropriate interfaces and defect engineering that effectively adjust the electrical and optical properties of the TMDCs were presented in order to achieve the ultimate goal of improving device performance [51]. By adopting appropriate defect engineering strategy, the defect fix, controlling the type and concentration of carriers, and the reduction of contact resistance could be achieved to realize high-performance electronic devices. On the other hand, controlling the defect state could increase the sensitivity of the photoconductive device or improve the response speed of the device. A heterojunction can be constructed to produce a photovoltaic effect through defect doping [52], and also the quantum electroluminescence effect can be produced using defects reasonably [53].

Surface/Interface Engineering for Improvement of Photodetector Properties
For the design and fabrication of optoelectronic devices based on nanostructures, the surface-to-volume ratios, interface areas, and interaction between surface and environment are increased dramatically, which has great impact on the performance of a PD device. For example, trapping at surface states of ZnO nanowire obviously influenced the transport and photoconduction properties of nanowires. The high surface-to-volume ratios and the existence of deep level surface trap states in nanostructures greatly extend the lifetime of photogenerated carriers. Moreover, the low dimensionality of the active area in a nanostructure device can reduce the transit time of carriers [45]. Zhou and colleagues fabricated UV photodetectors based on single In 2 O 3 nanowire, and the conductance was significantly increased by four orders of magnitude [54]. Fang  with high internal gain, which was attributed to the presence of oxygen-related hole-trap states at the surface of the nanowire. At the same time, the slow dynamics of the surface oxygen molecules' adsorption and desorption processes could result in a long response time in both the rise and decay process of a PD [45,56]. That is, the major shortcoming for ZnO based on PD applications is the strong persistent photo-induced conductivity after light illumination, which inhibits a fast recovery of the dark current [57]. Moreover, the persistent photoconductivity phenomenon was observed in PDs based on MoS 2 [58,59]. The performance of PD devices can be improved by the following ways: (a) enhancing the interaction between light and matter; (b) decreasing the adverse effects of defects; and (c) adjustment of electronic characteristics [60]. Therefore, various approaches, such as doping [61], surface functionalization [56,[62][63][64][65][66][67][68], surface carrier transport modulation [34], interface carrier-trapping/transport control [46], piezo-phototronic effects [69][70][71][72][73][74], and so on, have been utilized to improve the photoresponse performance of low-dimension nanostructure PDs for use in practical applications. The following section lists several ways to deal with surface/interface issues for improving performance of the photodetectors.

Surface-State Passivation for Terminating Dangling Bonds
As nanostructured photodetector devices have a much larger surface to volume ratio, and surface states play an important role in controlling their performance, surface-state passivation was one of the most useful solutions to deal with the mentioned issues. Surface-state passivation has been considered as one of the most effective and advanced methods to improve the performance of PDs through terminating their dangling bonds to decrease their surface states' influences. Fang et al. [64] modified the ZnO nanowalls by CdS nanoparticles and investigated the effect of CdS nanoparticles on the optical and photoelectrical properties of a PD. The surface states of ZnO nanowalls was suppressed due to the introduction of CdS nanoparticles' passivation layer; thus, the deep-level emission was reduced, and the recombination of carriers was prevented, and then the photoconductivity of ZnO nanowalls was improved obviously. Ren et al. [38] constructed nanowire-based photodetectors at mid-wavelength infrared composed of vertical selective-area n-InAsSb nanowire photoabsorber arrays on large bandgap p-InP substrate. In order to effectively inhibit the nonradiative recombination at the surface of InAsSb nanowire, the Al 2 O 3 passivation shells were introduced, as displayed in Figure 2a,b. Furthermore, it was demonstrated that the photoluminescence (PL) emission intensity of InAsSb nanowire arrays with Al 2 O 3 passivation layer increased 10-to 50-fold at 77 K. The spectral response of n-InAsSb/p-InP PDs with Al 2 O 3 passivation at a reverse bias of 0.5 V is shown in Figure 2c. Two detection peaks located at about 2.0 and 3.4µm were observed at room temperature. Nanomaterials 2020, 10, 362 5 of 24 [58,59]. The performance of PD devices can be improved by the following ways: (a) enhancing the interaction between light and matter; (b) decreasing the adverse effects of defects; and (c) adjustment of electronic characteristics [60]. Therefore, various approaches, such as doping [61], surface functionalization [56,[62][63][64][65][66][67][68], surface carrier transport modulation [34], interface carriertrapping/transport control [46], piezo-phototronic effects [69][70][71][72][73][74], and so on, have been utilized to improve the photoresponse performance of low-dimension nanostructure PDs for use in practical applications. The following section lists several ways to deal with surface/interface issues for improving performance of the photodetectors.

Surface-State Passivation for Terminating Dangling Bonds
As nanostructured photodetector devices have a much larger surface to volume ratio, and surface states play an important role in controlling their performance, surface-state passivation was one of the most useful solutions to deal with the mentioned issues. Surface-state passivation has been considered as one of the most effective and advanced methods to improve the performance of PDs through terminating their dangling bonds to decrease their surface states' influences. Fang et al. [64] modified the ZnO nanowalls by CdS nanoparticles and investigated the effect of CdS nanoparticles on the optical and photoelectrical properties of a PD. The surface states of ZnO nanowalls was suppressed due to the introduction of CdS nanoparticles' passivation layer; thus, the deep-level emission was reduced, and the recombination of carriers was prevented, and then the photoconductivity of ZnO nanowalls was improved obviously. Ren et al. [38] constructed nanowirebased photodetectors at mid-wavelength infrared composed of vertical selective-area n-InAsSb nanowire photoabsorber arrays on large bandgap p-InP substrate. In order to effectively inhibit the nonradiative recombination at the surface of InAsSb nanowire, the Al2O3 passivation shells were introduced, as displayed in Figure 2a,b. Furthermore, it was demonstrated that the photoluminescence (PL) emission intensity of InAsSb nanowire arrays with Al2O3 passivation layer increased 10-to 50-fold at 77 K. The spectral  Yang et al. reported the single ZnO nanowire PDs with large photoresponse and high internal gain; the hole-trapping mechanism was also proposed. The holes could be trapped through oxygen adsorption and desorption at surface states caused by the dangling bonds, further prolonging the lifetime of photogenerated carriers, and multiple electrons could transit through the nanowire. Finally, the photoconductive gain was realized [45]. However, the surface adsorption process could make the response time (rise and decay) of PDs become large, which is unfavorable for the performance of PDs. Chen et al. [56] constructed photoconductive ZnO nanowire/copper phthalocyanine (CuPc) hybrid PDs. A p-n heterojunction was formed at the interface of CuPc film and ZnO nanowires, leading to reduced conductivity and inhibited dark current in the ZnO NW. Under UV illumination, electron-hole pairs were generated and separated by a built-in internal electric field, and photoinduced potential was built. Meanwhile, the width of the surface depletion layer reduced, resulting in higher conductivity and increased photocurrent. The transition was rather fast and did not consider the adsorption or desorption process of molecules; thus, the rise and decay time of ZnO nanowire/CuPc photoresponse was shorter than that of the ZnO nanowire, which is shown in Figure 3. Therefore, the main reason for the improved photoresponse speed was the passivation of ZnO nanowires' surface states by CuPc film. Finally, the photoconductive gain was realized [45]. However, the surface adsorption process could make the response time (rise and decay) of PDs become large, which is unfavorable for the performance of PDs. Chen et al. [56] constructed photoconductive ZnO nanowire/copper phthalocyanine (CuPc) hybrid PDs. A p-n heterojunction was formed at the interface of CuPc film and ZnO nanowires, leading to reduced conductivity and inhibited dark current in the ZnO NW. Under UV illumination, electron-hole pairs were generated and separated by a built-in internal electric field, and photoinduced potential was built. Meanwhile, the width of the surface depletion layer reduced, resulting in higher conductivity and increased photocurrent. The transition was rather fast and did not consider the adsorption or desorption process of molecules; thus, the rise and decay time of ZnO nanowire/CuPc photoresponse was shorter than that of the ZnO nanowire, which is shown in Figure 3. Therefore, the main reason for the improved photoresponse speed was the passivation of ZnO nanowires' surface states by CuPc film. For two-dimensional nanomaterials, many reports about transition metal dichalcogenides (TMDCs) with layer structure material and interacting layers held together with weak van der Waals interaction, including MoS2 [75], MoSe2 [76], WSe2 [77], WS2 [78], and ReS2 [79], have been published. Because of their large surface volume ratio, the performance of these detectors is more sensitive to the environment. Studies have shown that physically adsorbed gas molecules, such as O2 and H2O, could deplete MoS2 and MoSe2 by removing electrons from the channels [80,81]. Konstantatos et al. constructed a high-stability and excellent-performance photodetector with an atomic layer deposited hafnium oxide (HfO2) encapsulated monolayer and bilayer MoS2, and the schematic of the PD device is shown in Figure 4a [82]. The oxide could suppress strong current drifting and degradation caused by environmental effects and effectively remove the surface atmospheric adsorbates. Unprotected MoS2 photodetector devices usually show slow response speed, which is displayed in Figure 4b. After encapsulation with HfO2, the photocurrent of the PD device was increased by about 40 times, while the decay time was reduced by more than one order of magnitude, as shown in Figure 4c. Moreover, the responsivity of MoS2 PDs was promoted by more than one order of magnitude after HfO2 For two-dimensional nanomaterials, many reports about transition metal dichalcogenides (TMDCs) with layer structure material and interacting layers held together with weak van der Waals interaction, including MoS 2 [75], MoSe 2 [76], WSe 2 [77], WS 2 [78], and ReS 2 [79], have been published. Because of their large surface volume ratio, the performance of these detectors is more sensitive to the environment. Studies have shown that physically adsorbed gas molecules, such as O 2 and H 2 O, could deplete MoS 2 and MoSe 2 by removing electrons from the channels [80,81]. Konstantatos et al. constructed a high-stability and excellent-performance photodetector with an atomic layer deposited hafnium oxide (HfO 2 ) encapsulated monolayer and bilayer MoS 2 , and the schematic of the PD device is shown in Figure 4a [82]. The oxide could suppress strong current drifting and degradation caused by environmental effects and effectively remove the surface atmospheric adsorbates. Unprotected MoS 2 photodetector devices usually show slow response speed, which is displayed in Figure 4b.
After encapsulation with HfO 2 , the photocurrent of the PD device was increased by about 40 times, while the decay time was reduced by more than one order of magnitude, as shown in Figure 4c. Moreover, the responsivity of MoS 2 PDs was promoted by more than one order of magnitude after HfO 2 encapsulation, as shown in Figure 4d. Therefore, the investigation of effective packaging technology and the prior complete removal of surface binding adsorbates is an effective way to achieve high speed and sensitive light detection. Nanomaterials 2020, 10, 362 7 of 24 and the prior complete removal of surface binding adsorbates is an effective way to achieve high speed and sensitive light detection. Certainly, other research groups have also used surface passivation to improve the performance of different detectors. Ni et al. investigated the influence of the MgO surface modification on the photocurrent and responsivity performance of TiO2@MgO core-shell nanowire array self-powered UV PDs [66]. The energy level structure between TiO2 and MgO is beneficial to the process of the separation of photogenerated electron-hole pairs and thus restrains the recombination of photogenerated carriers. Chen's group [61] have utilized a surface transfer doping method to adjust the electronic properties and work function of graphene films and then tune the Schottky barrier of Gr/Si junctions. The transition metal oxide molybdenum trioxide (MoO3) possesses high work function [83] and has displayed obvious surface transfer hole doping effects in graphene, MoS2, and other two-dimensional materials [67]. Therefore, they fabricated a Gr/Si self-powered photodetector using in situ surface functionalization of the MoO3 layer on graphene. It was demonstrated that the photocurrent responsivity of MoO3 doped Gr/Si PDs was significantly improved for a wide spectrum ranging from ultraviolet to near infrared. In addition, the external quantum efficiency, photocurrent responsivity, photovoltage responsivity, and the specific detectivity (D*) of Gr/Si devices were significantly promoted after MoO3 decoration, which was attributed to the more efficient photocarrier separation and collection process caused by the increased height of the Schottky barrier at the Gr/Si interface and the reduced series resistance of the Gr/Si device after MoO3 modification [61]. Sangyeon Pak [84] demonstrated the effects of surface functionalization on charge carrier density and photoresponse performance of the MoS2 photodetector.

Surface Plasmonic Resonance for Strong Scattering and Absorption of Incident Light
In recent years, many research groups have found that metal-surface plasma could be used to enhance the performance of detectors, which was attributed to the localized surface plasmon resonance (LSPR) effect, resulting in strong scattering and absorption of incident light, effectively separating photocarriers and transporting carriers at the interfaces of metal/semiconductor. Metal surface plasma is a hybrid electromagnetic wave mode formed by coupling of free vibrating electrons and incident photons on the metal surface. Both conductive surface plasmas at metal/dielectric interfaces and localized surface plasmas on metal nanoparticles have unique optical properties: high spatial local properties and local field enhancement properties. The unique photonic properties of surface plasmas make them widely used in subwavelength sensors, detectors, and modulators. To date, various plasmonic structures have been explored to improve the performance of photodetectors or phototransistors. In general, noble metals, for example Au [85][86][87][88][89], Ag [90][91][92], and Pt [93][94][95], are used as plasmonic metals for their useful range in the visible wavelengths, due to the excellent optical Certainly, other research groups have also used surface passivation to improve the performance of different detectors. Ni et al. investigated the influence of the MgO surface modification on the photocurrent and responsivity performance of TiO 2 @MgO core-shell nanowire array self-powered UV PDs [66]. The energy level structure between TiO 2 and MgO is beneficial to the process of the separation of photogenerated electron-hole pairs and thus restrains the recombination of photogenerated carriers. Chen's group [61] have utilized a surface transfer doping method to adjust the electronic properties and work function of graphene films and then tune the Schottky barrier of Gr/Si junctions. The transition metal oxide molybdenum trioxide (MoO 3 ) possesses high work function [83] and has displayed obvious surface transfer hole doping effects in graphene, MoS 2 , and other two-dimensional materials [67]. Therefore, they fabricated a Gr/Si self-powered photodetector using in situ surface functionalization of the MoO 3 layer on graphene. It was demonstrated that the photocurrent responsivity of MoO 3 doped Gr/Si PDs was significantly improved for a wide spectrum ranging from ultraviolet to near infrared. In addition, the external quantum efficiency, photocurrent responsivity, photovoltage responsivity, and the specific detectivity (D*) of Gr/Si devices were significantly promoted after MoO 3 decoration, which was attributed to the more efficient photocarrier separation and collection process caused by the increased height of the Schottky barrier at the Gr/Si interface and the reduced series resistance of the Gr/Si device after MoO 3 modification [61]. Sangyeon Pak [84] demonstrated the effects of surface functionalization on charge carrier density and photoresponse performance of the MoS 2 photodetector.

Surface Plasmonic Resonance for Strong Scattering and Absorption of Incident Light
In recent years, many research groups have found that metal-surface plasma could be used to enhance the performance of detectors, which was attributed to the localized surface plasmon resonance (LSPR) effect, resulting in strong scattering and absorption of incident light, effectively separating photocarriers and transporting carriers at the interfaces of metal/semiconductor. Metal surface plasma is a hybrid electromagnetic wave mode formed by coupling of free vibrating electrons and incident photons on the metal surface. Both conductive surface plasmas at metal/dielectric interfaces and localized surface plasmas on metal nanoparticles have unique optical properties: high spatial local properties and local field enhancement properties. The unique photonic properties of surface plasmas make them widely used in subwavelength sensors, detectors, and modulators. To date, various plasmonic structures have been explored to improve the performance of photodetectors or phototransistors. In general, noble metals, for example Au [85][86][87][88][89], Ag [90][91][92], and Pt [93][94][95], are used as plasmonic metals for their useful range in the visible wavelengths, due to the excellent optical property as a result of SPR. In the development of plasmonic photodetectors using Au@MoS 2 heterostructures, the photoresponsivity of the Au@ MoS 2 device was about 10 times larger than that of planar MoS 2 devices. Another type of Si-supported Au@MoS 2 p−n junction photodiode demonstrated photoresponsivity of 10−30 A/W, higher than the values reported for similar MoS 2 gateless photodevices, and the response time was less than 20 ms [88]. Luo et al. demonstrated that the photodetector device modifying plasmonic Au nanostructures onto the surface of CdTe NW exhibited the obvious photoresponse to 510 nm light illumination, with high response speed and fast recovery time [87]. A high-performance near-infrared (NIR) PD was constructed by coating single layer graphene (SLG)/InP Schottky junction diode with plasmonic SiO 2 @AuNRs; the schematic diagram of the PD and the TEM image of the SiO 2 @AuNRs on SLG film are shown in Figure 5a,b [96]. The decoration of SiO 2 @AuNRs could slightly improve the Schottky junction barrier, resulting in the increased built-in electric field, and then the separation efficiency of carriers was improved. The light trapping effect of the SiO 2 @AuNRs-SLG/InP device nearly promoted the absorption of incident light; as a result, many more holes and electrons were generated, and therefore photocurrent and responsivity were increased obviously (displayed in Figure 5c,d). Furthermore, the response rate of the SiO 2 @AuNRs-SLG/InP device was rather fast, which was able to monitor switching optical signals with a frequency up to 1 MHz, indicating its potential application in sensing high-frequency optical signals.  [87]. A high-performance near-infrared (NIR) PD was constructed by coating single layer graphene (SLG)/InP Schottky junction diode with plasmonic SiO2@AuNRs; the schematic diagram of the PD and the TEM image of the SiO2@AuNRs on SLG film are shown in Figure 5a,b [96]. The decoration of SiO2@AuNRs could slightly improve the Schottky junction barrier, resulting in the increased built-in electric field, and then the separation efficiency of carriers was improved. The light trapping effect of the SiO2@AuNRs-SLG/InP device nearly promoted the absorption of incident light; as a result, many more holes and electrons were generated, and therefore photocurrent and responsivity were increased obviously (displayed in Figure 5c,d). Furthermore, the response rate of the SiO2@AuNRs-SLG/InP device was rather fast, which was able to monitor switching optical signals with a frequency up to 1 MHz, indicating its potential application in sensing high-frequency optical signals. It was demonstrated that by coating Ag metal nanoparticles onto ZnO nanowires, the UV photodetectors exhibited higher sensitivity by four orders of magnitude with rather fast and stable response speed [90]. Arquer and colleagues reported that by introducing Ag metal nanoparticles into the PbS colloidal quantum dot photoconductive photodetectors, the absorption ability was increased due to a plasmonic scattering layer of Ag metal nanoparticles. As a result, the responsivity enhanced about 2.4-fold in the near infrared with the absorption band edge of ~1 μm [91]. Apart from noble metals, aluminum (Al) has been reported as a viable plasmonic metal for its useful range in the UV wavelengths [97,98]. Unlike the noble metals, the localized plasmon resonances can extend from the visible spectrum to the ultraviolet because the d-band of Al lies above its Fermi energy [99]. The Al element is a kind of abundant and low-cost metal found in the world, which is a better plasmonic material than Au and Ag in the UV range due to the negative real part and relatively low imaginary It was demonstrated that by coating Ag metal nanoparticles onto ZnO nanowires, the UV photodetectors exhibited higher sensitivity by four orders of magnitude with rather fast and stable response speed [90]. Arquer and colleagues reported that by introducing Ag metal nanoparticles into the PbS colloidal quantum dot photoconductive photodetectors, the absorption ability was increased due to a plasmonic scattering layer of Ag metal nanoparticles. As a result, the responsivity enhanced about 2.4-fold in the near infrared with the absorption band edge of~1 µm [91]. Apart from noble metals, aluminum (Al) has been reported as a viable plasmonic metal for its useful range in the UV wavelengths [97,98]. Unlike the noble metals, the localized plasmon resonances can extend from the visible spectrum to the ultraviolet because the d-band of Al lies above its Fermi energy [99]. The Al element is a kind of abundant and low-cost metal found in the world, which is a better plasmonic material than Au and Ag in the UV range due to the negative real part and relatively low imaginary part of its dielectric function [100]. Xu et al. [97] improved the response characteristic of ZnO nanorod array UV PDs using surface plasmonic resonance by Al nanoparticles. Compared with the pure ZnO nanorod array PDs, the responsivity of the ZnO nanorod photodetector modified with Al nanoparticles was improved from 0.12 A/W to 1.59 A/W.
Recently, it has been observed that boron (B)-doped and phosphorus (P)-doped silicon (Si) nanocrystals enable the localized surface plasmon resonance of Si nanocrystals in the mid-infrared (MIR) region [101]. Especially, the heavily B-doped silicon nanocrystals induced band-tail states that could expand the optical absorption of Si from the UV-visible region into the near-infrared region. Furthermore, the localized surface plasmon resonance of heavily B-doped silicon nanocrystals could be tunable, which is attributed to free holes above the Fermi level from the B-induced impurity band [102]. Yang et al. [103] constructed quantum dots (QDs)/graphene hybrid MIR PDs by using plasmonic B-doped Si QDs; the schematic diagram of B-doped Si-QDs/graphene PDs is illustrated in Figure 6a. In the process of operating PDs, two different optical phenomena of silicon quantum dots can be adopted, as shown in Figure 6b. In the MIR region, the LSPR of silicon quantum dots generated a strong electric field that increased the direct excitation of the underlying graphene. Therefore, the phototransistor could effectively respond to the MIR light. The UV-to-near-infrared absorption of B-doped Si QDs resulted in the generation of electrons and holes in quantum dots. The photoresponse of the PD device was obtained by transferring one type of carrier from the quantum dot to graphene and capturing another carrier in the quantum dot. Figure 6c displays that the responsivity of Si-QD/graphene PDs was reduced with the increase of the irradiance power. The responsivity was in the range of 1.2 × 10 8 to 2.2 × 10 8 A/W with the UV-to-NIR light illumination at the lowest irradiance of 0.2 µW/cm 2 . As can be seen from Figure 6d, the noise equivalent power (NEP) values of the PDs in the MIR region and the UV-to-NIR region were about 10 −10 and 10 −18 W/Hz 0.5 , respectively. The fairly small NEP value suggests that the Si-QD/graphene photodetector can be applied to low light detection. The values of D* were about 10 5 and 10 13 Jones for the MIR and the UV-to-NIR photodetection, respectively. Nanomaterials 2020, 10, 362 9 of 24 array UV PDs using surface plasmonic resonance by Al nanoparticles. Compared with the pure ZnO nanorod array PDs, the responsivity of the ZnO nanorod photodetector modified with Al nanoparticles was improved from 0.12 A/W to 1.59 A/W. Recently, it has been observed that boron (B)-doped and phosphorus (P)-doped silicon (Si) nanocrystals enable the localized surface plasmon resonance of Si nanocrystals in the mid-infrared (MIR) region [101]. Especially, the heavily B-doped silicon nanocrystals induced band-tail states that could expand the optical absorption of Si from the UV-visible region into the near-infrared region. Furthermore, the localized surface plasmon resonance of heavily B-doped silicon nanocrystals could be tunable, which is attributed to free holes above the Fermi level from the B-induced impurity band [102]. Yang et al. [103] constructed quantum dots (QDs)/graphene hybrid MIR PDs by using plasmonic B-doped Si QDs; the schematic diagram of B-doped Si-QDs/graphene PDs is illustrated in Figure 6a. In the process of operating PDs, two different optical phenomena of silicon quantum dots can be adopted, as shown in Figure 6b. In the MIR region, the LSPR of silicon quantum dots generated a strong electric field that increased the direct excitation of the underlying graphene. Therefore, the phototransistor could effectively respond to the MIR light. The UV-to-near-infrared absorption of Bdoped Si QDs resulted in the generation of electrons and holes in quantum dots. The photoresponse of the PD device was obtained by transferring one type of carrier from the quantum dot to graphene and capturing another carrier in the quantum dot. Figure 6c displays that the responsivity of Si-QD/graphene PDs was reduced with the increase of the irradiance power. The responsivity was in the range of 1.2 × 10 8 to 2.2 × 10 8 A/W with the UV-to-NIR light illumination at the lowest irradiance of 0.2 μW/cm 2 . As can be seen from Figure 6d, the noise equivalent power (NEP) values of the PDs in the MIR region and the UV-to-NIR region were about 10 −10 and 10 −18 W/Hz 0.5 , respectively. The fairly small NEP value suggests that the Si-QD/graphene photodetector can be applied to low light detection. The values of D* were about 10 5 and 10 13 Jones for the MIR and the UV-to-NIR photodetection, respectively.

Interface Carrier-Trapping/Transport Modulation
Once the design principles are defined, important parameters of interface engineering can be directly identified, containing interface compositions, areas, defects, faces, electronic coupling, and

Interface Carrier-Trapping/Transport Modulation
Once the design principles are defined, important parameters of interface engineering can be directly identified, containing interface compositions, areas, defects, faces, electronic coupling, and band bending. Before the interface engineering, the roles of the interface in the design structure should be fully understood according to the specific charge dynamics models [104]. For example, defects at the interface tend to be the recombination centers of electrons and holes, thus hindering the charge transfer across the interfaces. Therefore, eliminating the interfacial defects can improve the performance of the PDs in most situations. It has been proved that improving the quality of crystals, optimizing the arrangement of energy levels of layers, and constructing p-n or Schottky heterojunctions could be effective interfacial engineering methods to improve the performance of photodetectors [105].
It is demonstrated that surface and interface engineering play a key role in improving the performances of PDs. The generation, diffusion, and recombination/transport processes of charge carriers can influence the performance of PDs; thus, these factors should be taken into account when the PDs are built. Huang et al. [106] have constructed a new type of nanocomposite ultraviolet photodetector; the schematic drawing of the PD is shown in Figure 7a. The Frenkel excitons generated in ZnO nanoparticles and polymers could diffuse to the polymer/nanoparticles interface. Under reverse bias voltage, holes were transported in the semiconducting polymer, but the electrons were still trapped in the nanoparticles, attributed to the short percolation network for electrons and the strong quantum confinement effect of ZnO nanoparticles. Because of the strong electron trapping effect, the PDs had Schottky contact in the dark and an ohmic contact under illumination, confirmed by the dark current and photocurrent. That is, the PD device transitioned from a photodiode (in dark) to photoconductor (under illumination) via interfacial trap-controlled charge injection. The measured total noise current in the frequency range 1 to 5 kHz was mainly the shot noise, as shown in Figure 7b. The specific detectivity of hybrid PDs (shown in Figure 7c) was tens-to hundreds-fold better than that of inorganic semiconductor photodetectors. Furthermore, the response speed of the PD was rather high compared to other photodetectors based on any nanoparticles or colloidal quantum dots. It was indicated that two channels for the recombination of holes existed through the decay of the photocurrent experiment (displayed in Figure 7d). The decay process was combined with a fast component of 142 ms and a slow component of 558 ms.
Semiconductor heterojunctions with different bandgaps could exhibit different interface properties. By adjusting the arrangement of interfacial energy bands, the heterojunction structures may possess unique photoresponse characteristics. Moreover, when constructing the heterojunction for multicolor photodetection, it is necessary to have a large band deviation at the interface of the heterojunction in order to effectively extract carriers. There are larger band offsets between the Si/TiO 2 heterojunction; according to the calculation, the conduction band offset (∆E C ) and the valence band offset (∆E V ) were 0.75 eV and 2.66 eV, respectively, which would be conducive to control the transport of the carriers. Hu et al. [107] fabricated a multicolor photodetector based on the n-Si(111)/TiO 2 nanorod array heterojunction ranging from ultraviolet to visible light by controlling the applied voltage. In the case of forward bias, the band offsets would not hinder the diffusion of carriers; thus, there was no difference between the photocurrent and the dark current. The PD device exhibited multicolor detection capability under reverse bias because the motion of these carriers was controlled by the applied bias and the barrier of conduction band offset and the valence band offset.
7b. The specific detectivity of hybrid PDs (shown in Figure 7c) was tens-to hundreds-fold better than that of inorganic semiconductor photodetectors. Furthermore, the response speed of the PD was rather high compared to other photodetectors based on any nanoparticles or colloidal quantum dots. It was indicated that two channels for the recombination of holes existed through the decay of the photocurrent experiment (displayed in Figure 7d). The decay process was combined with a fast component of 142 ms and a slow component of 558 ms.  Nowadays, Perovskite material has become one of the superstar media for constructing different kinds of photoelectric devices; especially, all-inorganic cesium lead halides (CsPbX 3 , X = Cl, Br, I) represent an emerging class of materials owing to their high carrier mobility, long carrier diffusion length, and excellent visible light absorption. The high quantum efficiency (over 90%), narrow line width, and high stability make these all-inorganic perovskites suitable for application in novel optoelectronics [108]. Song et al. [108] utilized the advantages of large absorption coefficient and high quantum efficiency of the perovskites by fabricating the superior performance hybrid CsPbBr 3 perovskite/MoS 2 PD with a high photoresponsivity of 4.4 A/W and an external quantum efficiency of 302%; the schematic diagram of the hybrid PDs is displayed in Figure 8a,b. Especially, the photogenerated electrons in the perovskite were effectively transferred and injected to MoS 2 . MoS 2 monolayer acted as an electron-collecting layer for perovskite photodetectors to improve the photoelectrical response, as shown in Figure 8c-e, which could decrease the probability of carrier recombination; therefore, the photoresponsivity of the hybrid CsPbBr 3 perovskite/MoS 2 PDs improved by three orders of magnitude compared with the pure MoS 2 PD. The dark current was also obviously reduced. Furthermore, the MoS 2 layer could induce the trap passivation on the substrate and benefit the carrier transport and then improve the separation efficiency of carriers; thus, the rising time of the hybrid PD was also lowered from 65.2 to 0.72 ms after combining with MoS 2 layers, as displayed in Figure 8f. It was demonstrated that 2D nanomaterials combined with the perovskite layers could be considered as a superior candidate to realize the next-generation high-performance photodetectors. For fiber-shaped devices, the interface problems of the fiber device were more serious, which was attributed to the curved and rough surface, many more defects, and poor contacts. Hence, smoothing the rough surface and achieving better contact between all layers was particularly important for improving the performance of fiber-shaped devices. Zeng et al. [105] built and constructed an inorganic-organic-graphene hybrid fiber-shaped PD via "soft" interfaces of all layers; the schematic diagram illustrating the fabrication procedure of ZnO nanorods/PVK/graphene hybrid fiber-shaped PDs is displayed in Figure 9a. In this hybrid fiber-shaped PD, the organic semiconductor completely covered the inorganic functional layer, forming "soft" contact and smoothing its rough surface. In addition, the ultra-soft graphene could tightly wrap around the surface, creating another "soft" interface, as shown in Figure 9b. These "soft" interfaces between the various functional layers even at curved interfaces have established the tight contact; thus, the contact resistance could be significantly reduced. The ZnO nanorods array with good crystal quality was uniformly grown on the Zn wire. As seen in Figure 9d,e, the rise time of the PD with structure of ZnO/PVK/graphene was about 280 ms with fast response speed. Meanwhile, by using hard metal Ag wire instead of soft graphene as surface electrode, the response speed slowed down and the rise time of PDs increased to 6 s, as shown in Figure 9f,g. Therefore, the tight contact and reasonable interfacial energy level alignment (shown in Figure 9c) were beneficial to the separation and transportation of photogenerated electrons and holes. The results showed that the performance of the fiber-shaped PDs could be significantly improved by effective interface optimization. For fiber-shaped devices, the interface problems of the fiber device were more serious, which was attributed to the curved and rough surface, many more defects, and poor contacts. Hence, smoothing the rough surface and achieving better contact between all layers was particularly important for improving the performance of fiber-shaped devices. Zeng et al. [105] built and constructed an inorganic-organic-graphene hybrid fiber-shaped PD via "soft" interfaces of all layers; the schematic diagram illustrating the fabrication procedure of ZnO nanorods/PVK/graphene hybrid fiber-shaped PDs is displayed in Figure 9a. In this hybrid fiber-shaped PD, the organic semiconductor completely covered the inorganic functional layer, forming "soft" contact and smoothing its rough surface. In addition, the ultra-soft graphene could tightly wrap around the surface, creating another "soft" interface, as shown in Figure 9b. These "soft" interfaces between the various functional layers even at curved interfaces have established the tight contact; thus, the contact resistance could be significantly reduced. The ZnO nanorods array with good crystal quality was uniformly grown on the Zn wire. As seen in Figure 9d,e, the rise time of the PD with structure of ZnO/PVK/graphene was about 280 ms with fast response speed. Meanwhile, by using hard metal Ag wire instead of soft graphene as surface electrode, the response speed slowed down and the rise time of PDs increased to 6 s, as shown in Figure 9f,g. Therefore, the tight contact and reasonable interfacial energy level alignment (shown in Figure 9c) were beneficial to the separation and transportation of photogenerated electrons and holes. The results showed that the performance of the fiber-shaped PDs could be significantly improved by effective interface optimization. Furthermore, interface nanojunction engineering of the electron depletion effect could be utilized to improve the performance of PDs. For instance, Liu et al. [109] constructed nanojunctioninterlinked ZnO nanoparticle networks without changing the dimension and morphology of the nanoparticles using an ultrafast thermal annealing (UTA) method. Figure 10 indicates band bending, electric field, and the low conductivity surface depletion layer present due to the adsorption of oxygen molecules on the ZnO nanoparticle surfaces. Contaminants (orange shell in schematic) and surface defects could reduce the electron depletion effect, resulting in high dark current and low photocurrent, as shown in Figure 10a,b. Surface modification using UTA can eliminate surface defects and contaminants and thus restore the electron depletion effect. Finally, this caused a decrease in the dark current and an increase in photocurrent, as shown in Figure 10c,d. In addition, ZnO NP-NP interface nanojunctions could be fused into interlinked ZnO-NP networks, which could significantly reduce the potential barrier of inter-NP and thus suppress the recombination of carriers in the transport process. From Figure 10e it is evident that the photoresponse of PDs increased dramatically by about four orders of magnitude with the decreased wavelength across the band edge after UTA treatment at 800 °C for 2 s. Figure 10f displays the relationship between applied bias and detectivity for a set of samples treated with UTA at different temperatures in the range of 500 to 900 °C. The detectivity value increased at first and then descended with the increasing UTA temperature and obtained the maximum value of 1.4 × 10 13 Jones for the sample treated at 800 °C. Especially, D* after UTA treatment at 800 °C was enhanced by approximately three orders of magnitude compared with Furthermore, interface nanojunction engineering of the electron depletion effect could be utilized to improve the performance of PDs. For instance, Liu et al. [109] constructed nanojunction-interlinked ZnO nanoparticle networks without changing the dimension and morphology of the nanoparticles using an ultrafast thermal annealing (UTA) method. Figure 10 indicates band bending, electric field, and the low conductivity surface depletion layer present due to the adsorption of oxygen molecules on the ZnO nanoparticle surfaces. Contaminants (orange shell in schematic) and surface defects could reduce the electron depletion effect, resulting in high dark current and low photocurrent, as shown in Figure 10a,b. Surface modification using UTA can eliminate surface defects and contaminants and thus restore the electron depletion effect. Finally, this caused a decrease in the dark current and an increase in photocurrent, as shown in Figure 10c,d. In addition, ZnO NP-NP interface nanojunctions could be fused into interlinked ZnO-NP networks, which could significantly reduce the potential barrier of inter-NP and thus suppress the recombination of carriers in the transport process. From Figure 10e it is evident that the photoresponse of PDs increased dramatically by about four orders of magnitude with the decreased wavelength across the band edge after UTA treatment at 800 • C for 2 s. Figure 10f displays the relationship between applied bias and detectivity for a set of samples treated with UTA at different temperatures in the range of 500 to 900 • C. The detectivity value increased at first and then descended with the increasing UTA temperature and obtained the maximum value of 1.4 × 10 13 Jones for the sample treated at 800 • C. Especially, D* after UTA treatment at 800 • C was enhanced by approximately three orders of magnitude compared with that of untreated, demonstrating the significance of removing surface defects and contaminants and improving the interconnections of NP. Therefore, it is very important to achieve high-performance detection making full use of the electron depletion effect with the minimum charge combination. Nanomaterials 2020, 10,362 14 of 24 that of untreated, demonstrating the significance of removing surface defects and contaminants and improving the interconnections of NP. Therefore, it is very important to achieve high-performance detection making full use of the electron depletion effect with the minimum charge combination.

Piezo-Phototronic Effects for Modulating Carrier Transport Behavior
In fact, piezoelectric phenomena exist in materials such as semiconductors, polymers, ceramics, and even biological media. Among them, the well-known piezoelectric materials are quartz and Pb(Zr, Ti)O3, but the non-semiconductor and insulating properties limit their applications in photonic and electronic fields [110,111]. In theory, any semiconductor material with non-central symmetry could produce piezoelectric effect. Generally speaking, ZnO with wurtzite structure is the most wellknown material in the study of the piezoelectric effect; it not only has rich nanostructural morphology but also possesses much higher piezoelectric coefficients than other II-VI family materials. The transmission characteristics of carriers can be dynamically adjusted by using the effect of piezoelectric potential, so that they have potential application prospects in mechanical electronic devices, including sensors, nanorobots, and so on. When considering the interaction with light, by adjusting the magnitude of the strain and the intensity of light, the transmission properties of carriers in the device can be effectively modulated. Light-emitting diodes [112,113], solar cells [114][115][116], and photodetectors [74,[117][118][119][120] associated with the piezo-phototronic effect have attracted wide attention because of their potential application prospects. The band structure and carrier transport behavior can be dynamically modulated by taking advantage of the piezo-phototronic effect in the photodetectors.

Piezo-Phototronic Effects for Modulating Carrier Transport Behavior
In fact, piezoelectric phenomena exist in materials such as semiconductors, polymers, ceramics, and even biological media. Among them, the well-known piezoelectric materials are quartz and Pb(Zr, Ti)O 3 , but the non-semiconductor and insulating properties limit their applications in photonic and electronic fields [110,111]. In theory, any semiconductor material with non-central symmetry could produce piezoelectric effect. Generally speaking, ZnO with wurtzite structure is the most well-known material in the study of the piezoelectric effect; it not only has rich nanostructural morphology but also possesses much higher piezoelectric coefficients than other II-VI family materials. The transmission characteristics of carriers can be dynamically adjusted by using the effect of piezoelectric potential, so that they have potential application prospects in mechanical electronic devices, including sensors, nanorobots, and so on. When considering the interaction with light, by adjusting the magnitude of the strain and the intensity of light, the transmission properties of carriers in the device can be effectively modulated. Light-emitting diodes [112,113], solar cells [114][115][116], and photodetectors [74,[117][118][119][120] associated with the piezo-phototronic effect have attracted wide attention because of their potential application prospects. The band structure and carrier transport behavior can be dynamically modulated by taking advantage of the piezo-phototronic effect in the photodetectors.
The piezo-phototronic effect could be applied in different ways with designed structure [111,114]. Wang et al. [121] utilized the piezo-phototronic effect to adjust the height of the Schottky barrier at local contact; the performances of the Schottky contact metal-semiconductor-metal photodetector based on the GaN nanobelt was enhanced. Generally, the response ability of the PDs was obviously improved due to the piezotronic effect when a strain was applied on devices. In particular, the responsivity of PDs increased by 18% with a compressive strain, and their sensitivity increased from 22% to 31% [121]. The piezo-phototronic effect can not only improve the responsivity of the PDs but can also adjust the dark current of the detector. Wang et al. [122] constructed MSM ZnO micro-/nanowire PDs; the responsivity of the PDs was increased by 530% under −0.36% compressive strain, while the dark current of PDs was tuned with the applied piezo-phototronic effect.
Inspired by the enhanced performance caused by the piezo-phototronic effect, a hybrid PD based on heterojunction structure was constructed [72,73]. Zhu and colleagues [72] fabricated broad-band UV/visible/near-infrared self-powered PDs based on p-P3HT and n-CdS. When a 0.67% tensile strain was applied in the [001] direction of CdS contacting with P3HT, the photocurrent of the PDs could be increased to over 330% under UV illumination. This improvement by means of the piezo-phototronic effect could be ascribed to the increased built-in electric field in the interface of the p-n junction, which was more conducive to the separation of photogenerated carriers in CdS and P3HT. It has been reported that the piezoelectric effect that exists in MoS 2 with an odd number of atomic layers could tune the height of the Schottky barrier in metal-semiconductor contact and/or drive the nanometer device due to its non-central symmetric structure [123,124]. Wang et al. [125] fabricated a flexible photodetector based on a p-CuO film/n-MoS 2 monolayers heterojunction; the structure diagram and the optical image of PDs are shown in Figure 11a and the inset of Figure 11b, respectively. Figure 11b shows the I-V characteristics of p-CuO/n-MoS 2 heterojunction had good rectification characteristics in the dark without strain condition. Even at a forward bias voltage of 10 V, it had an ultra-low dark current of 0.039 nA, which was conducive to obtain high-performance optical sensing. Figure 11c exhibits the relationship between current and voltage of the heterojunction with different tensile strains in the dark. The dark current increased from 0.039 nA to 0.12 nA with the increase of tensile strain from 0% to 0.65% at 10 V bias, which resulted from the piezotronic effect of monolayer MoS 2 (the positive piezopotential caused by tensile strain can modulate the bandgap at the interface of the CuO and MoS 2 heterojunction). The relation between photocurrent and different tensile strains under different power density of 532 nm laser illumination is shown in Figure 11d; the photocurrent obviously increased with the increased strain due to the piezo-phototronic effect. The strain dependence of R/R 0 and detectivity of heterojunction PDs with different power densities at a bias of 10 V are displayed in Figure 11e,f, respectively. The photoresponsivity and detectivity of the PDs increased with increasing strain because of the piezo-phototronic effect.
A pure semiconductor absorbs photons with an energy larger than the band gap, which limits the wide spectral sensitivity in PD devices. In order to remove the restriction, the core/shell system is adopted for adequate light absorption. The core-shell architecture not only effectively utilizes the inherent material properties of individual components but also provides direct electrical conducting channels for the transport of photocarriers and results in reducing recombination losses; thus, it is a promising choice for improving the performance of photodetectors [118,119,126]. Wang et al. [118] investigated the influence of the piezo-phototronic effect on the photosensitivity of visible and UV PDs based on ZnO/CdS core-shell micro/nanowire, which is shown in Figure 12a. The Schottky barrier heights (SBHs) at the source and drain contacts could be adjusted by the strain induced piezopotential in the ZnO core, and the experimental results in Figure 12b demonstrated that SBHs at the source and drain contacts decreased with the increase of compressive strains. Moreover, the responsivity of ZnO/CdS nanowire-based PDs was improved dramatically by more than ten times with −0.31% compressive strain, as shown in Figure 12c. On this basis, the research group fabricated the branched ZnO/CdS double-shell nanowires array on carbon fiber (CF/ZnO-CdS wire) [117], as illustrated in Figure 12d,e. As shown in Figure 4f, the responsivity of this single CF/ZnO-CdS wire PD was enhanced about 40%-60% under compressive strain of −0.38% and decreased about 8%-20% under a 0.31% tensile strain. In addition, Zhou et al. [126] fabricated broad band PDs based on a type-II CdSe/ZnTe heterojunction core/shell nanowire array using a 100 nm thin Ag layer as top electrode, as illustrated in Figure 12g. When the core/shell nanowires array was bent under the action of external forces, the positive piezopotential on the stretched surface lowered the Schottky barrier height at the Ag-ZnTe junction (Figure 12h), which resulted in the increase of minority carrier diffusion and more carriers flowing through the interface. Combined with the type-II band alignment at the CdSe-ZnTe interfaces and the small lattice mismatch between the CdSe and ZnTe, the responsivity of this PD was enhanced by four orders of magnitude with an applied load of 0.25 kgf under 1.8 V bias, as shown in Figure 12i. Therefore, it is feasible to optimize the performance of PDs based on a multi-function NW array by the piezoelectric photoelectric effect. A pure semiconductor absorbs photons with an energy larger than the band gap, which limits the wide spectral sensitivity in PD devices. In order to remove the restriction, the core/shell system is adopted for adequate light absorption. The core-shell architecture not only effectively utilizes the inherent material properties of individual components but also provides direct electrical conducting channels for the transport of photocarriers and results in reducing recombination losses; thus, it is a promising choice for improving the performance of photodetectors [118,119,126]. Wang et al. [118] investigated the influence of the piezo-phototronic effect on the photosensitivity of visible and UV PDs based on ZnO/CdS core-shell micro/nanowire, which is shown in Figure 12a. The Schottky barrier heights (SBHs) at the source and drain contacts could be adjusted by the strain induced piezopotential in the ZnO core, and the experimental results in Figure 12b demonstrated that SBHs at the source and drain contacts decreased with the increase of compressive strains. Moreover, the responsivity of ZnO/CdS nanowire-based PDs was improved dramatically by more than ten times with −0.31% compressive strain, as shown in Figure 12c. On this basis, the research group fabricated the branched ZnO/CdS double-shell nanowires array on carbon fiber (CF/ZnO-CdS wire) [117], as illustrated in Figure 12d,e. As shown in Figure 4f, the responsivity of this single CF/ZnO-CdS wire PD was enhanced about 40%-60% under compressive strain of −0.38% and decreased about 8%-20% shown in Figure 12i. Therefore, it is feasible to optimize the performance of PDs based on a multifunction NW array by the piezoelectric photoelectric effect.

Conclusions
In conclusion, through surface/interface engineering of nanostructured photodetector devices, advanced nanostructured PDs could be constructed by engineering through modulating photon absorption, charge carrier generation, transport, and collection behaviors. Based on the review, it could be well observed that surface/interface engineering of nanostructured PDs is crucially important for affecting PD performance. More importantly, as well illustrated in the paper, through surface or interface engineering such as surface-state passivation for terminating dangling bonds, surface plasmonic resonance for strong scattering and absorption of incident light, interface carriertrapping/transport modulation, and piezo-phototronic effects for modulating carrier transport behavior in constructing PD devices, the constructed photodetectors' performance could be considerably improved as supported by reviewing published literature. Even though this brief review paper lists several key factors in the improvement of the constructed photodetector devices,

Conclusions
In conclusion, through surface/interface engineering of nanostructured photodetector devices, advanced nanostructured PDs could be constructed by engineering through modulating photon absorption, charge carrier generation, transport, and collection behaviors. Based on the review, it could be well observed that surface/interface engineering of nanostructured PDs is crucially important for affecting PD performance. More importantly, as well illustrated in the paper, through surface or interface engineering such as surface-state passivation for terminating dangling bonds, surface plasmonic resonance for strong scattering and absorption of incident light, interface carrier-trapping/transport modulation, and piezo-phototronic effects for modulating carrier transport behavior in constructing PD devices, the constructed photodetectors' performance could be considerably improved as supported by reviewing published literature. Even though this brief review paper lists several key factors in the improvement of the constructed photodetector devices, it could be pointed out that several challenges still exist in the way of commercialization of nanostructured photodetectors as shown in the following:

1.
Well controlled fabrication of nanostructured materials with uniform morphology and size for constructing designed photodetectors; 2.
Well controlled growth of nanostructures with strong absorption of incident photons; 3.
Well controlled surface/interface modification for enhancing carrier transportation; 4.
Well applied material properties (such as piezoelectric effects) for modulating carrier behavior.
Finally, we believe that advanced nanostructured photodetectors with excellent performance could be designed and fabricated for practical applications through studying the mentioned issues in depth.