Ni-Rich Layered Oxide with Preferred Orientation (110) Plane as a Stable Cathode Material for High-Energy Lithium-Ion Batteries

The cathode, a crucial constituent part of Li-ion batteries, determines the output voltage and integral energy density of batteries to a great extent. Among them, Ni-rich LiNixCoyMnzO2 (x + y + z = 1, x ≥ 0.6) layered transition metal oxides possess a higher capacity and lower cost as compared to LiCoO2, which have stimulated widespread interests. However, the wide application of Ni-rich cathodes is seriously hampered by their poor diffusion dynamics and severe voltage drops. To moderate these problems, a nanobrick Ni-rich layered LiNi0.6Co0.2Mn0.2O2 cathode with a preferred orientation (110) facet was designed and successfully synthesized via a modified co-precipitation route. The galvanostatic intermittent titration technique (GITT) and electrochemical impedance spectroscopy (EIS) analysis of LiNi0.6Co0.2Mn0.2O2 reveal its superior kinetic performance endowing outstanding rate performance and long-term cycle stability, especially the voltage drop being as small as 67.7 mV at a current density of 0.5 C for 200 cycles. Due to its unique architecture, dramatically shortened ion/electron diffusion distance, and more unimpeded Li-ion transmission pathways, the current nanostructured LiNi0.6Co0.2Mn0.2O2 cathode enhances the Li-ion diffusion dynamics and suppresses the voltage drop, thus resulting in superior electrochemical performance.


Introduction
The pursuit of environmental protection and low carbon emission has been causing a daily increasing requirement of high-value ratio energy storage devices. Lithium-ion batteries (LIBs) with long cycle life, and high energy density and working potential have been occupying a high proportion of the commercial battery market [1][2][3]. Nevertheless, there is still a lack of appropriate cathode materials with ultra-stable cycle life and fast charge/discharge rates to meet the demand of next-generation batteries [4,5]. It is well known that the cathode considerably determines the whole energy density of batteries. Recently, Ni-rich LiNi x Co y Mn z O 2 (x + y + z = 1, x ≥ 0.6) layered transition metal oxides have been emerging as the most potential cathode candidates for LIBs due to their relatively higher capacity and output working voltage than LiFePO 4 , more abundant resources, and lower cost than traditional LiCoO 2 [6][7][8][9][10]. Unfortunately, its practical application still suffers from low cycle stability, severe voltage drops and poor kinetics [11,12]. There are many factors that including cation mixing, phase transition, loss of lattice oxygen, particle cracking, electrolyte decomposition,

Preparation of LiNi 0.6 Co 0.2 Mn 0.2 O 2 (NCM622) Cathode Materials
Firstly, the hydroxide precursor nanosheets were synthesized via a modified co-precipitation route. 100 mL 20 mM feed solution prepared by mixing NiSO 4 ·6H 2 O, CoSO 4 ·7H 2 O, and MnSO 4 ·H 2 O with the proportion of Ni: Co: Mn at 3:1:1. Then, the feed solution was dripped into a 50 mL NH 3 ·H 2 O (pH = 11) solution three-necked flask with continuously stirring. Synchronously, 100 mL 30 mM Na 2 CO 3 solution and 100 mL 0.6 mM NH 3 ·H 2 O solution were completely put into the flask. After that, the temperature was maintained at 55 • C and stirring velocity controlled at 800 rpm for 24 h to accomplish the co-precipitation reaction procedure. Then, the precursors were filtered, washed three cycles alternately with ultrapure water and ethanol, and dried at 80 • C overnight. The oxide composite intermediates were obtained by pre-sintering hydroxide precursor at 600 • C for 5 h in a furnace. Finally, the mixture of as-synthesized oxide precursors and Li 2 CO 3 with an appropriate proportion was calcined at 850 • C for 12 h in the air to obtain pristine LiNi 0.6 Co 0.2 Mn 0.2 O 2 , denoted as NCM622.

Characterization Methods
The crystalline structure of these materials was determined by using a PANalytical Empyrean X-ray diffractometer (XRD, PANalytical B.V., Almelo, The Netherlands) equipment with Cu-K radiation (λ = 1.54056 Å, operating at 40 kV, 45 mA). The intensity data collected by XRD was analyzed by the Rietveld improved program-General Structural Analysis System-I (GSAS-I) software package. The morphology, microstructure and elemental distribution were measured by a field emission scanning electron microscope (SEM, Zeiss Gemini DSM 982, Carl Zeiss AG, LEO Oberkochen, Germany) equipped with an EDS energy dispersive X-ray spectrometer with an acceleration voltage of 15 kV. High-resolution transmission electron microscopy (HRTEM) data was obtained by a JEM-2100F (JEOL Co., Akishima City, Tokyo, Japan) instrument operating at 200 kV. N 2 desorption and adsorption isotherms were evaluated at 77 K with a Quadrachrome adsorption instrument.

Electrochemical Measurements
The electrochemical properties were tested in CR2016 coin-type cells. These cells were assembled with the NCM622 cathode, Li metal anode, organic electrolyte, and polypropylene separators in an Ar-filled glove box. The organic electrolyte was that 1.0 M LiPF 6 dissolved in ethylene carbonate/diethylene carbonate/dimethyl carbonate (EC/DEC/DMC, 1:1:1 in volume). The NCM622 electrode was prepared by thoroughly mixing the active material, Super-P, and polyvinylidene fluoride (PVDF) with a weight ratio of 8:1:1 in N-methyl(pyrrolidinone) (NMP). Then the slurry spread onto the aluminum foil and dried in a vacuum oven at 100 • C for 12 h. The mass loading of cathode materials was measured in the range of 1.6-2.2 mg cm −2 . LAND CT2001A testing system (LAND Electronic Co. Ltd., Wuhan, China) was performed to evaluate the cycling performance and rate capacity at various current density in the voltage region of 2.8-4.4 V. Electrochemical impedance spectroscopy (EIS) was measured by an electrochemical workstation (Gamry Interface 1000, Gamry Electrochem. Instru. Co., Warminster, PA, USA) with an amplitude of 10 mV from 10 5 Hz to 10 −2 Hz. Galvanostatic Intermittent Titration Technique (GITT) was performed at a constant current pulse of 0.1 C rate for 15 min and then rest for 90 min to stabilize the cell voltage between 2.8 and 4.4 V. Figure 1 presents the detailed formation procedure of TM (Ni, Co, Mn) (oxy)hydroxide precursor and nanobricks LiNi 0.6 Co 0.2 Mn 0.2 O 2 (marked as NCM622). First, The Mn/Co ions co-substituted Ni(OH) 2 with nanoplates morphology was prepared by a modified co-precipitation route using a high-pH values ammonium hydroxide as the base solution. Subsequently, these (Ni, Co, Mn) hydroxide nanoplates were adopted as novel phase precursors for the formation of the final high nickel NCM622. XRD pattern (Figure 2a) verifies that this TM (Ni, Co, Mn) hydroxide can be precisely indexed to hexagonal α-Ni(OH) 2 (JCPDS no. 38-0715) phase. According to the XRD results, there are two fundamental phases of Ni(OH) 2 that exist in the precursor. It is interesting to note that the c-parameter of α-Ni(OH) 2 is greater than that of β-Ni(OH) 2 [42], which means that the diffraction angle of α-Ni(OH) 2 is equivalent to a low angle shift of β-Ni(OH) 2 . This phenomenon is originated from the type of anions (OH − , CO 3 2− , SO 4 2− ) and H 2 O molecules embedded in the Ni(OH) 2 lattice [43][44][45][46]. Separately, the corresponding XRD parameters were listed in Tables S1−S3. The diffraction peaks of NiOOH were associated with the easy oxidization of α-Ni(OH) 2 to NiOOH [47]. Therefore, the as-synthesized precursor is (oxy)hydroxide (TM(OH) 2 /TMOOH) and can be precisely indexed to (Ni(OH) 2 (NiOOH) 0.167 ) 0.857 (JCPDS no. 89-7111). As depicted in Figure 2d, the obtained (oxy)hydroxide precursor shows a hierarchical architecture, which is consists of randomly assembled nanosheets. To avoid destructive morphology change resulting from the crystal growth during solid-state lithiation and attain intermediate oxides composite, the (oxy)hydroxide precursor was pre-calcined at 600 • C in air condition [48]. The XRD result (Figure 2b) directly reveals the changes of (oxy)hydroxide to precursor NiO (JCPDS no. 78-0643) and MnCo 2 O 4 (JCPDS no. 84-0482). As it appears in the SEM signals (Figure 2e), this oxide composite well inherited the nanosheets' morphology.

Results and Discussion
To gain an in-depth realizing of the intermediate's elemental composition, SEM-EDS mapping was also performed. The EDS mapping signals reveal the uniform distribution and co-exists of Ni, Co, Mn, and O elements ( Figure S1). Furthermore, and the atomic ratio of Ni, Mn, and Co is determined at approximately 3:1:1, which is well consistent with the designed stoichiometric values ( Figure S2).  Figure S1). Furthermore, and the atomic ratio of Ni, Mn, and Co is determined at approximately 3:1:1, which is well consistent with the designed stoichiometric values ( Figure S2).  The structure and morphology of NCM622 materials after lithiation reaction were also investigated by XRD and SEM. Evidently, all the XRD diffraction peaks of NCM622 (Figure 2c) could be indexed to the layered hexagonal α-NaFeO2 single-phase with a space group of R3 m [49]. On The EDS mapping signals reveal the uniform distribution and co-exists of Ni, Co, Mn, and O elements ( Figure S1). Furthermore, and the atomic ratio of Ni, Mn, and Co is determined at approximately 3:1:1, which is well consistent with the designed stoichiometric values ( Figure S2).  The structure and morphology of NCM622 materials after lithiation reaction were also investigated by XRD and SEM. Evidently, all the XRD diffraction peaks of NCM622 (Figure 2c) could be indexed to the layered hexagonal α-NaFeO2 single-phase with a space group of R3 m [49]. On The structure and morphology of NCM622 materials after lithiation reaction were also investigated by XRD and SEM. Evidently, all the XRD diffraction peaks of NCM622 ( Figure 2c) could be indexed to the layered hexagonal α-NaFeO 2 single-phase with a space group of R3m [49]. On account of previous studies, the splitting of (006)/(102) and (108)/(110) peaks indicates this NCM622 cathode with a well-ordered layered structure [33,50]. Certainly, no distinct extra peaks appear in the XRD patterns suggesting the attained NCM622 cathode without any impurity phase. Figure 2f displays the SEM result of NCM622 products, which confirm that the as-prepared cathode with an architecture nanobrick morphology possesses smooth surfaces and enhanced sidewalls. Separately, the thickness of these nanobricks can be intuitively acquired as about 300 nm. Additonally, EDS mapping signals of Ni, Co, Mn, and all elements (Figure 2g) verify that all elements are uniformly distributed. It is worth noting that the thickness difference between the NCM622 and precursor nanosheet is associated with the merging of the multilayer boards during the high-temperature reaction [41]. The unique hierarchical structure is not only effectively forms good penetration of electrolytes, but also markedly increases the transport pathway for Li-ion diffusion during the delithiation/lithiation processes. To accurately verify the element composition of Li:Ni:Co:Mn in the nanobricks, ICP-OES (Agilent 720ES) measurements were performed and provided in Table S4. The results demonstrate that the molar ratio of Li:Ni:Co:Mn in nanobricks is well consistent with the expected stoichiometric ratio of LiNi 0.6 Co 0.2 Mn 0.2 O 2 .
To gain more insight into the crystal structure, the XRD pattern of this NCM622 cathode was refined and analyzed by using GSAS software. Figure 3a and Table S5 display the refined results of NCM622 material based on hexagonal phase α-NaFeO 2 (R3m) layered structure. It is worth noting that the intensity of (110) peak is stronger than (108) peak in the magnified view, and the ratio values of I (110) /I (108) is 1.06. The ratio of I (110) /I (108) over 1.0, which further indicates the abundance of exposed electroactive (110) facets NCM622 cathode possessed. This phenomenon has been reported and verified in many previous works, in which the preferential growth of the crystal structure with an exposed plane is believed to enhance the electrochemical performance [39,40,[51][52][53]. This particular structure with more exposed (110) facets of NCM622 cathode is believed to offer unobstructed Li + diffusion channels. The microstructure of NCM622 was characterized by transmission electron microscopy (TEM), high-resolution TEM (HRTEM) and fast Fourier transform (FFT). Figure 3c further verifies that the resulted NCM622 with a nanobrick structure, which is well inherited the structure from the precursor. The HRTEM image and inset FFT pattern (Figure 3e) with an interplanar distance of 2.07 Å is assigned to the (104) planes of NCM622 cathode materials. The intrinsic lithium-ion diffusion dynamic properties of current NCM622 with preferred orientation (110) facets structure was further characterized. Galvanostatic intermittent titration technique (GITT) and electrochemical impedance spectra (EIS) were carried out to analyze the Li-ion diffusion coefficient, which is the key indicator for ion transport kinetics. The DLi + is calculated by Equation (1) where is the Li + diffusivity (cm 2 s −1 ), τ is the time duration of the pulse (s), nM and VM are the molar mass (mol) and volume (cm 3 mol −1 ) of the active material, S is the cell interfacial area (cm 2 ), respectively. ΔEs is the potential difference at the state of equilibrium (V), and ΔEt is the polarization potential (V), and L is the length of Li + diffusion (cm). The applied current plus vs. cell voltage for a single titration step of GITT curves are extracted out in Figure S3, in which the different parameters of Vo, IR drop, V1, V2, V3, etc., are schematically marked out. The GITT values in the entire interval charge state are shown in Figure 4a and the corresponding calculated DLi + of NCM622 electrode lies in the range of 10 −12 -10 −8 cm s −1 (Figure 4b). The intrinsic lithium-ion diffusion dynamic properties of current NCM622 with preferred orientation (110) facets structure was further characterized. Galvanostatic intermittent titration technique (GITT) and electrochemical impedance spectra (EIS) were carried out to analyze the Li-ion diffusion coefficient, which is the key indicator for ion transport kinetics. The D Li + is calculated by Equation (1) [30,55,56]: where D Li + is the Li + diffusivity (cm 2 s −1 ), τ is the time duration of the pulse (s), n M and V M are the molar mass (mol) and volume (cm 3 mol −1 ) of the active material, S is the cell interfacial area (cm 2 ), respectively. ∆E s is the potential difference at the state of equilibrium (V), and ∆E t is the polarization potential (V), and L is the length of Li + diffusion (cm). The applied current plus vs. cell voltage for a single titration step of GITT curves are extracted out in Figure S3  Furthermore, the EIS tests were also measured and depicted in Figure 4c. The DLi + is further evaluated from the Warburg impedance date according to the following Equation (2) [57]:

2
(2) where R is the ideal gas constant, T is the absolute temperature, F is the Faraday constant, n is the number of electrons per molecule oxidized, C is the concentration of Li + in the cathode. A is the surface area of the electrode, which was determined by Brunauer-Emmett-Teller (BET) measurement using Quadrachrome adsorption isotherms at 77 k. As shown in Figure S4, the value of A was concluded as 5.92 m 2 g −1 . σ is the Warburg coefficient related to Z' in Equation (3), which is the fitted slope of the relationship between the Z' and the square root of frequency (ω −1/2 ) (Figure 4d). On account of Equations (2) and (3), DLi+ of NCM622 cathode could be calculated as 2.03 × 10 −8 cm 2 s −1 . This value is Furthermore, the EIS tests were also measured and depicted in Figure 4c. The D Li + is further evaluated from the Warburg impedance date according to the following Equation (2) [57]: where R is the ideal gas constant, T is the absolute temperature, F is the Faraday constant, n is the number of electrons per molecule oxidized, C is the concentration of Li + in the cathode. A is the surface area of the electrode, which was determined by Brunauer-Emmett-Teller (BET) measurement using Quadrachrome adsorption isotherms at 77 k. As shown in Figure S4, the value of A was concluded as 5.92 m 2 g −1 . σ is the Warburg coefficient related to Z in Equation (3), which is the fitted slope of the relationship between the Z and the square root of frequency (ω −1/2 ) (Figure 4d). On account of Equations (2) and (3), D Li+ of NCM622 cathode could be calculated as 2.03 × 10 −8 cm 2 s −1 . This value is also in good agreement with the results obtained by GITT. It is illustrated that the materials with preferred orientation (110) active facets have favorable Li-ion diffusion kinetics, which strongly supports the excellent electrochemical performance NCM622 cathode achieved.
To validate the rate capability and cycling performance NCM622 reached, the NCM622//Li half-cells were measured. Figure 4e,f show the rate capability of NCM622 at various charge-rates in the voltage range of 2.8-4.4 V. This NCM622 cathode retains a capacity of 178.6, 173.8, 162.1, 152.1, 140.6,  1551.1, 160.0, 171.7, and 179.0 mAh g −1 at 0.1, 0.2, 0.5, 1, 2, 1, 0.5, 0.2, and 0.1 C, respectively. When the current density returns to 0.1 C (from 1 to 0.1 C), yielding a capacity retention of 99%. The distinguished capacity retention proves that this NCM622 material possesses excellent rate capability. The superior performance also is an echo with previous GITT and EIS analysis. These superior properties can be attributed to the unique nanobrick structure with more exposed electroactive (110) facets and thereby reduced the diffusion distance, thus improving the Li + diffusion kinetics.
The cycling stability of NCM622 nanobriks cathode was also evaluated and displayed in Figure 5. Figure 5a shows the smooth charge/discharge curves of NCM622 for the first cycle. It delivers a high initial discharge capacity of~175 mAh g −1 and coupled with an initial coulomb efficiency (ICE) of 85% at a current density of 0.1 C. Moreover, at a certain high discharge voltage, this NCM622 cathode has a negligible discharge open circuit voltage drop of only 8.3 mV. To further unveil the charge/discharge mechanism, the corresponding differential capacity (dQ dV −1 ) curves as a function of cell voltage is provided in Figure 5b. The differential capacity curves mainly consist of a couple of redox peaks and display lower anodic peak voltages in the second charging process. Besides, the prepared NCM622 possesses a small voltage interval between the anodic and corresponding cathodic peaks indicating almost negligible polarization and well reversibility of this cathode [14]. Gratifyingly, the NCM622 material displays stable cycling performance (Figure 5c) and achieves superior capacity retention of 89.7% and 88.2% after 100 cycles at 0.2 C and 2 C, respectively. The corresponding discharge curves displayed in Figure 5h,i which vividly appear as stable discharge platforms and capacities without obvious drops and decay. As shown in Figure 5d-g, the long-term cycle stability of NCM622 was also measured at 0.5 C. Figure 5d exhibits a detailed analysis of the capacity retention of NCM cathode during the whole 200 cycles, which is conducted out through the recorded number of cycles (50 times interval) displaying a capacity retention as high as 82.2% after 200 cycles. The ICE of the nickel-rich layered cathode materials was associated with the side reactions and irreversible phase transitions at the electrode/electrolyte interface during the delithiation process. Especially for nano-sized particles, which possess highly active electrode/electrolyte interface thereby the side reactions are inevitable take place, thus causing part of the capacity irreversibly [11,15,16]. The coulombic efficiencies are all close to 100% in subsequent cycles, revealing that the NCM622 undergoes a highly reversible electrochemical reaction during the whole cycling process (Figure 5e). Figure 5f exhibits a small midpoint potential difference of 67.7 mV, suggesting a low voltage drop, thus delivering excellent long-term cycle stability. The corresponding charge/discharge curves (Figure 5g) directly present the voltage platform change reflecting the high-capacity retention this NCM622 achieved. The high-capacity retention and low voltage drop can be ascribed to the abundance of exposed (110) planes, which offers an open structure for rapid Li-ions transportation and ensures a small polarization. Also, the structure and morphology of the electrode after cycling were investigated by XRD and SEM measurements. The XRD pattern of the NCM622 electrode ( Figure S5a) in the voltage range of 2.8-4.4 V at 0.5 C rate after 200 cycles reveals that the NCM622 electrode still preserve a hexagonal crystal structure relating to the R3 m space group. Furthermore, the corresponding SEM images ( Figure S5b) indicate NCM622 cathode still maintained the nanobrick morphology with a smooth surface and sharp edges. The XRD pattern and SEM images evidence that the rational structure design well protects the structural integrity of NCM622 from destruction.
To acquire more helpful information revealing the possible changes NCM622 undergoes, the AC impedance measurements were evaluated at various cycles at a 0.5 C rate. As demonstrated in Figure  6a-e, the semicircles of high and medium frequency features can be observed for all Nyquist plots. The high and medium frequency region are associated with Rf and Rct, respectively. Based on the equivalent circuit ( Figure S6), The Rf and Rct values can be calculated and offered in Figure 6f. It can Also, the structure and morphology of the electrode after cycling were investigated by XRD and SEM measurements. The XRD pattern of the NCM622 electrode ( Figure S5(a)) in the voltage range of 2.8-4.4 V at 0.5 C rate after 200 cycles reveals that the NCM622 electrode still preserve a hexagonal crystal structure relating to the R3m space group. Furthermore, the corresponding SEM images ( Figure  S5(b)) indicate NCM622 cathode still maintained the nanobrick morphology with a smooth surface and sharp edges. The XRD pattern and SEM images evidence that the rational structure design well protects the structural integrity of NCM622 from destruction.
To acquire more helpful information revealing the possible changes NCM622 undergoes, the AC impedance measurements were evaluated at various cycles at a 0.5 C rate. As demonstrated in Figure 6a-e, the semicircles of high and medium frequency features can be observed for all Nyquist plots. The high and medium frequency region are associated with R f and R ct , respectively. Based on the equivalent circuit ( Figure S6), The R f and R ct values can be calculated and offered in Figure 6f. It can be observed that the R f values without significant changes from 50th to 150th cycles suggest that the current cathode possesses stable cathode electrolyte interface (CEI) film during the cycle process. The R ct value with continuous increase throughout the cycle is caused by the oxidative decomposition of the electrolyte on the electrode surface.

Conclusions
Ni-rich NCM622 nanobricks with preferred orientation (110) active planes are successfully synthesized via a scalable approach, which consists of a modified co-precipitation procedure followed by a solid lithiation reaction. This NCM cathode achieves superior rate capability retaining a discharge capacity of 178.6, 173.8, 162.1, 152.1, and 140.6 mAh g −1 at 0.1, 0.2, 0.5, 1, and 2 C, respectively. The GITT and EIS analysis reveal that this NCM622 exhibits a good kinetic property equipped with a Li-ion diffusion coefficient around 2.03 × 10 −8 cm 2 s −1 and a sufficiently small voltage drop (67.7 mV) at 0.5 C after 200 cycles, and superior capacity retention, ca. 89.7% (0.2 C) and 88.2% (2 C). The superior Li + storage performance NCM622 possessed could be attributed to the unique architectures with a preferred orientation (110) facet, which not only endows more channels for ion/electros transporting, but also reduces the diffusion distance and, thus, resulting in excellent diffusion dynamics and attaining superior electrochemical performance. This imaginative design

Conclusions
Ni-rich NCM622 nanobricks with preferred orientation (110) active planes are successfully synthesized via a scalable approach, which consists of a modified co-precipitation procedure followed by a solid lithiation reaction. This NCM cathode achieves superior rate capability retaining a discharge capacity of 178.6, 173.8, 162.1, 152.1, and 140.6 mAh g −1 at 0.1, 0.2, 0.5, 1, and 2 C, respectively. The GITT and EIS analysis reveal that this NCM622 exhibits a good kinetic property equipped with a Li-ion diffusion coefficient around 2.03 × 10 −8 cm 2 s −1 and a sufficiently small voltage drop (67.7 mV) at 0.5 C after 200 cycles, and superior capacity retention, ca. 89.7% (0.2 C) and 88.2% (2 C). The superior Li + storage performance NCM622 possessed could be attributed to the unique architectures with a preferred orientation (110) facet, which not only endows more channels for ion/electros transporting, but also reduces the diffusion distance and, thus, resulting in excellent diffusion dynamics and attaining superior electrochemical performance. This imaginative design sheds a light on constructing multistage structured cathode materials for the next-generation batteries.
Supplementary Materials: The following are available online at http://www.mdpi.com/2079-4991/10/12/2495/s1, Figure S1: SEM image and elemental EDS mapping of Ni, Co, Mn, O and all elements for the intermediate oxides composite, the scale bar is 90 µm in all figures, Figure S2: EDS spectrum and corresponding element composition of intermediate oxides composite, Figure S3: Applied current plus vs. cell voltage for a single titration step of GITT curves, Figure S4: N 2 adsorption/desorption isotherms of NCM622 nanobricks, Figure S5: Typical XRD pattern and SEM images of NCM622 electrode after long-term 200 cycles at 0.5 C rate, Figure S6: Equivalent circuit model is used for fitting the experimental results. Rs: solution resistance, Rf: surface film resistance, related to Li-ions diffusion in the cathode electrolyte interface (CEI), and Rct: charge transfer resistance, CPE: constant phase element, Wo: Warburg element (open), Table S1: Unit cell parameters for the two fundamental phases of Ni(OH) 2 , Table S2: X-ray diffraction parameters of α-Ni(OH) 2 based on JCPDS No.38-0715, Table S3: X-ray diffraction parameters of β-Ni(OH) 2 based on JCPDS No. 14-0117, Table S4: The ICP-OES results of NCM622 nanobricks, Table S5: Atomic site information and crystallographic data for NCM622.