A Review of Titanium Dioxide (TiO2)-Based Photocatalyst for Oilfield-Produced Water Treatment

Oilfield produced water (OPW) has become a primary environmental concern due to the high concentration of dissolved organic pollutants that lead to bioaccumulation with high toxicity, resistance to biodegradation, carcinogenicity, and the inhibition of reproduction, endocrine, and non-endocrine systems in aquatic biota. Photodegradation using photocatalysts has been considered as a promising technology to sustainably resolve OPW pollutants due to its benefits, including not requiring additional chemicals and producing a harmless compound as the result of pollutant photodegradation. Currently, titanium dioxide (TiO2) has gained great attention as a promising photocatalyst due to its beneficial properties among the other photocatalysts, such as excellent optical and electronic properties, high chemical stability, low cost, non-toxicity, and eco-friendliness. However, the photoactivity of TiO2 is still inhibited because it has a wide band gap and a low quantum field. Hence, the modification approaches for TiO2 can improve its properties in terms of the photocatalytic ability, which would likely boost the charge carrier transfer, prevent the recombination of electrons and holes, and enhance the visible light response. In this review, we provide an overview of several routes for modifying TiO2. The as-improved photocatalytic performance of the modified TiO2 with regard to OPW treatment is reviewed. The stability of modified TiO2 was also studied. The future perspective and challenges in developing the modification of TiO2-based photocatalysts are explained.


Introduction
Oilfield produced water (OPW) is the by-product of oil exploration and production, both onshore and offshore, and has become one of the most significant organic pollutants on a global scale [1,2]. The physicochemical properties of OPW are highly dependent on the geological age, depth, and geochemistry of the hydrocarbon-bearing formation, as well as the chemical composition of the oil phase in the reservoir and the process of adding chemicals during oil production [2]. OPW has been estimated to be over 80 million barrels per day on average throughout the world with an 80% water cut [3].
Furthermore, another study revealed that the chemical oxygen demand (COD) rate of OPW was 2250 ppm, containing a variety of organic chemicals, such as polycyclic aromatic hydrocarbons (PAHs), surfactants, benzene toluene ethylbenzene xylenes (BTEX), phenolic compounds, and organic acids [1,3,4]. Those organic compounds have an adverse effect on environmental and human health, such as high resistance to biodegradation, high mutagenic and carcinogenic risks, such as tumour and cancer, and high toxicity to marine living things [5]. Other biological impacts due to the presence of OPW include high risk in the endocrine, non-endocrine, and reproductive systems [6].
To prevent OPW contamination to the aquatic environment, conventional physical or biological processes have been applied, such as gravimetry and ultrasonic separation, coagulation/flocculation, adsorption, membrane bioreactor, biologically active filtration, and conventional activated sludge [7][8][9][10]. Although the physical processes exhibited dispersed oil separation from OPW, numerous drawbacks can be seen, such as high operation cost, long processing time, large space requirements, possibly producing secondary pollutants and the inability of pollutant degradation [7,8]. The biological process has been known to be the most cost-effective method but still faces some disadvantages, such as along-time process, more complex management, and easy contamination [9].
Currently, the photocatalysis process using semiconductors has been chosen to be favorable in degrading the organic pollutants in OPW as it does not require additional chemicals and generates harmless compounds, such as carbon dioxide (CO2), water (H2O), and mineral acids [9]. This process involves charge carrier transfer from the photo-excited semiconductor as shown in Figure 1, which can be summarized into two steps: photoexcitation of the semiconductor, which causes the separation of electrons (e − ) and holes (h + ) as charge carriers and the migration/recombination of charge carriers with the emission of heat or light [11,12]. Various semiconductors have been investigated for use as photocatalysts, such as titanium (IV) oxide (TiO2), zinc (II) oxide (ZnO), gallium arsenide, tungsten (VI) oxide (WO3), gallium phosphide, and cadmium sulfide [13]. Among the other semiconductors, TiO2 has become a promising material that has been widely used in photocatalytic processes due to its superior properties, such as excellent optical and electronic properties, high photocatalytic activity, high chemical stability, low cost, non-toxicity, and environmental friendliness [15,16]. Several reports have found the greater beneficial properties of TiO2 over the other semiconductors, including (1) a higher photodegradation rate of Procion Red MX-5B using TiO2 photocatalyst (0.34 h −1 ) rather than using zinc (II) oxide (ZnO, 0.25 h −1 ) and tin (IV) oxide (SnO2, 0 h −1 ) [17]; and (2) Among the other semiconductors, TiO 2 has become a promising material that has been widely used in photocatalytic processes due to its superior properties, such as excellent optical and electronic properties, high photocatalytic activity, high chemical stability, low cost, non-toxicity, and environmental friendliness [15,16]. Several reports have found the greater beneficial properties of TiO 2 over the other semiconductors, including (1) a higher photodegradation rate of Procion Red MX-5B using TiO 2 photocatalyst (0.34 h −1 ) rather than using zinc (II) oxide (ZnO, 0.25 h −1 ) and tin (IV) oxide (SnO 2 , 0 h −1 ) [17]; and (2) no Ti 4+ ion was detected in the TiO 2 slurries system after the photodegradation of phenol and even after the phenol was completely degraded.
This phenomenon showcases the high stability and eco-friendliness of TiO 2 compared to the ZnO suspension system, which contains a higher amount of Zn 2+ (0.93 mM) [18,19]. In addition, the TiO 2 photocatalyst reduced COD and PAHs rates in OPW by up to 87.1% and 50% under UV irradiation, respectively [20,21]. Table 1 shows several fundamental reactions in the photocatalytic degradation of organic compounds by TiO 2 [22,23]. Table 1. Various basic reactions with the respective reaction times for the general process of organic pollutant degradation by TiO 2 photocatalyst [22,23]. Adapted with permission from American Chemical Society and Elsevier, 2022.
Recently, a few studies have been conducted on the green synthesis of TiO2 utilizing plant-assisted and microbe-assisted approaches, which have advantages, such as non-toxicity, well-maintained reagent management, and a safe procedure [40]. Plant-assisted synthesis is more stable than microbe-assisted synthesis and has a higher yield but is less expensive [41,42]. Plant-assisted synthesis of TiO2 can be performed through several steps, including: plant extraction from any part (the flowers, seeds, leaves, and roots), mixing treatment of TiO2 precursor solution with plant extract, and post-treatment (drying and In the TiO 2 (B) phase, the Ti-O octahedral connection was similar to the anatase but with a different arrangement in the monoclinic crystal [26]. Rutile was the most thermodynamically stable, while anatase, brookite, and TiO 2 (B) were metastable [27,28]. Among those crystal phases, TiO 2 anatase has long been known as the most photoactive due to a high density or localized state, slow charge carrier recombination, highly consequent surface-adsorbed radical hydroxyl, and high chemical stability [29,30].
Recently, a few studies have been conducted on the green synthesis of TiO 2 utilizing plant-assisted and microbe-assisted approaches, which have advantages, such as nontoxicity, well-maintained reagent management, and a safe procedure [40]. Plant-assisted synthesis is more stable than microbe-assisted synthesis and has a higher yield but is less expensive [41,42]. Plant-assisted synthesis of TiO 2 can be performed through several steps, including: plant extraction from any part (the flowers, seeds, leaves, and roots), mixing treatment of TiO 2 precursor solution with plant extract, and post-treatment (drying and calcination) [40].
Although TiO 2 has the potential to be one of the most efficient destructive photocatalysts for the majority of organic pollutants in OPW, it suffers from a low light absorption region and a low quantum yield, which hampers the formation of free radicals [43,44]. The capability of TiO 2 is limited by the low rate of degradation for certain organic compounds, insufficient photon energy, and mass contact for TiO 2 at the high concentration of organic pollutants [13]. Those limitations can occur because of the undesired TiO 2 properties, such as low affinity toward organic pollutants and instability of nanosized particles, which may undergo aggregation and reduce the active sites [45]. Moreover, the application of the TiO 2 -suspended system for photodegradation of OPW faced major obstacles in terms of light scattering effects and complex photocatalyst recovery steps, which possibly reduced the photocatalytic performance [45][46][47].
To overcome those issues, several modifications of TiO 2 were required to improve the photocatalyst performance in terms of boosting the charge carrier transfer, hindering the recombination of electrons and holes, and increasing the radiation light response up to the visible region. Numerous approaches have been established to achieve the improvement of TiO 2 photocatalyst in the photodegradation process with comparative and beneficial properties, such as nanostructure modification, doping, and/or impregnation of other elements and/or material toward TiO 2 photocatalysts and TiO 2 -based photocatalytic membranes (PMs) [45,48]. Hence, this review paper gives a detailed explanation regarding those approaches, various photodegradation mechanisms that have been found, and future perspectives for advancing TiO 2 -based photocatalysts in OPW treatment.

Construction of TiO 2 Nanostructures Form
The fabrication of TiO 2 by modifying the morphological form hierarchically has been well studied and gained attention due to its diverse physicochemical properties, which can improve the photocatalytic performance [48]. This strategy has become one of the excellent routes to resolve challenges related to the kinetic and thermodynamic aspects of the TiO 2 photocatalyst. Hierarchical nanostructure design for TiO 2 has gained better molecular diffusion kinetics, enhanced radiation light absorption, increased surface area, and obtained excellent charge carrier separation with a lower possibility to recombination.
Various nanostructure forms of TiO 2 have been classified into 0D, 1D, 2D, and 3D architectures, which are summarized in Figure 3. Among those architectures, the TiO 2 1D has received the most attention and has been studied by the researchers due to its beneficial aspects, such as easy processing steps, large specific surface area, high aspect ratio and chemical stability, and efficient electronic charge properties, which can be synthesized using various techniques that are shown in Table 2 [48][49][50].
The development of other types of TiO 2 1D nanostructures has been attempted, and various types have been studied well. Interestingly, Xue et al. succeeded in constructing hierarchical TiO 2 nanotrees, which were applied to the photodegradation of phenol under UV-light illumination [51]. TiO 2 nanotrees are made up of TiO 2 nanobelts or nanowires branches that are quasi-aligned vertically on a conductive substrate film, like a trunk, and can be made by immersing the trunk in alkali-hydrothermal and acidic conditions as shown in Figure 4. obtained excellent charge carrier separation with a lower possibility to recombination.
Various nanostructure forms of TiO2 have been classified into 0D, 1D, 2D, and 3D architectures, which are summarized in Figure 3. Among those architectures, the TiO2 1D has received the most attention and has been studied by the researchers due to its beneficial aspects, such as easy processing steps, large specific surface area, high aspect ratio and chemical stability, and efficient electronic charge properties, which can be synthesized using various techniques that are shown in Table 2 [48][49][50].  [48]. Reproduced with permission from Elsevier, 2022. The development of other types of TiO2 1D nanostructures has been attempted, and various types have been studied well. Interestingly, Xue et al. succeeded in constructing hierarchical TiO2 nanotrees, which were applied to the photodegradation of phenol under UV-light illumination [51]. TiO2 nanotrees are made up of TiO2 nanobelts or nanowires branches that are quasi-aligned vertically on a conductive substrate film, like a trunk, and can be made by immersing the trunk in alkali-hydrothermal and acidic conditions as shown in Figure 4.
The scanning electron microscope (SEM) and atomic force microscope (AFM) images showed the nanosheet branches that were grown on the trunks with various lengths in the range of 50-200 nm, which follows the TiO2 nanotree illustration. The enhancement of photocatalytic activity for TiO2 nanotrees is significant, with the optimal condition exhibiting a photocatalytic reaction rate of 0.346 h −1 , which is significantly higher than that of pristine TiO2 nanobelts (0.0256 h −1 ) and TiO2 nanowires (0.0154 h −1 ), despite the fact that the trunk thickness had no significant effect on the photoactivity of TiO2 nanotrees. This  [48]. Reproduced with permission from Elsevier, 2022.  Although TiO2 has been known for its beneficial effect on photocatalytic a there are some gaps that still exist in the implementation. There is no major diff especially regarding the affinity property of TiO2 toward organic compounds in OP cause this strategy only changes the stability of crystal phases and morphologica and not the molecular properties of TiO2, such as intermolecular bonding to othe pounds. Moreover, the use of TiO2-nanostructure modified still relies on the pho lytic suspended system, which has limited performance due to the light scattering and higher pollutant concentration [52].

Energy Band Engineering for TiO2
The pristine TiO2 has a larger band gap, which only absorbs UV light for char rier separation and photoactivation, which utilizes 4% of the energy in the solar spe while 45% of the energy belongs to visible light [53].
Therefore, the energy band engineering strategy plays an important role in e ing the longwave-light sensitivity of the TiO2 photocatalyst with excellent photoca The scanning electron microscope (SEM) and atomic force microscope (AFM) images showed the nanosheet branches that were grown on the trunks with various lengths in the range of 50-200 nm, which follows the TiO 2 nanotree illustration. The enhancement of photocatalytic activity for TiO 2 nanotrees is significant, with the optimal condition exhibiting a photocatalytic reaction rate of 0.346 h −1 , which is significantly higher than that of pristine TiO 2 nanobelts (0.0256 h −1 ) and TiO 2 nanowires (0.0154 h −1 ), despite the fact that the trunk thickness had no significant effect on the photoactivity of TiO 2 nanotrees. This study has revealed potential avenues for scaling up TiO 2 nanostructure modification for organic compound photodegradation in OPW.
Although TiO 2 has been known for its beneficial effect on photocatalytic activity, there are some gaps that still exist in the implementation. There is no major difference, espe-cially regarding the affinity property of TiO 2 toward organic compounds in OPW because this strategy only changes the stability of crystal phases and morphological form and not the molecular properties of TiO 2 , such as intermolecular bonding to other compounds. Moreover, the use of TiO 2 -nanostructure modified still relies on the photocatalytic suspended system, which has limited performance due to the light scattering effect and higher pollutant concentration [52].

Energy Band Engineering for TiO 2
The pristine TiO 2 has a larger band gap, which only absorbs UV light for charge carrier separation and photoactivation, which utilizes 4% of the energy in the solar spectrum while 45% of the energy belongs to visible light [53].
Therefore, the energy band engineering strategy plays an important role in enhancing the longwave-light sensitivity of the TiO 2 photocatalyst with excellent photocatalytic performance by narrowing and expanding the band gap of TiO 2 into the wide region of light absorption using different approaches as illustrated in Figure 5. This strategy can be performed through various methods, such as developing composites or mixed-phase and doping them with suitable materials that have the heterojunction system, desired morphological, and physicochemical properties that result in minimizing the charge carrier recombination and optimizing photoexcited charge carriers between their interfaces [54][55][56]. The doping of TiO2 was conducted by introducing impurity ions, both non-metal and metal elements, as dopants into the TiO2 lattice plane without changing the single phase of TiO2 to substitute the host cations and/or anions, which could give a contribution in three routes: (1) increasing the conductivity of TiO2 and the mobility of photoexcited charge carriers that lead to the reduction of photogenerated electron/hole recombination and enhancement of charge carrier separation; (2) advancing the enlargement of the light absorption region and narrowing the band gap; and (3) altering the CBM of TiO2, which may enhance the optical properties [56][57][58][59][60].
Those contributions led to the appearance of a modified photocatalytic mechanism of TiO2 as shown in Figure 6, which can be further described as followed: (a) the nonmetal doping on a TiO2 photocatalyst gained in impurity energy level, narrowed band gap, and improved oxygen vacancies, which is favorable to extend the visible-light absorption and prevent reoxidation [61][62][63][64]; and (b) the metal doping of TiO2 generated a new energy level in the band gap of TiO2, which may increase the amount of charge carrier trapping site and reduce the possibility of photogenerated electron/hole recombination [65]. The doping of TiO 2 was conducted by introducing impurity ions, both non-metal and metal elements, as dopants into the TiO 2 lattice plane without changing the single phase of TiO 2 to substitute the host cations and/or anions, which could give a contribution in three routes: (1) increasing the conductivity of TiO 2 and the mobility of photoexcited charge carriers that lead to the reduction of photogenerated electron/hole recombination and enhancement of charge carrier separation; (2) advancing the enlargement of the light absorption region and narrowing the band gap; and (3) altering the CBM of TiO 2 , which may enhance the optical properties [56][57][58][59][60].
Those contributions led to the appearance of a modified photocatalytic mechanism of TiO 2 as shown in Figure 6, which can be further described as followed: (a) the non-metal doping on a TiO 2 photocatalyst gained in impurity energy level, narrowed band gap, and improved oxygen vacancies, which is favorable to extend the visible-light absorption and prevent reoxidation [61][62][63][64]; and (b) the metal doping of TiO 2 generated a new energy level in the band gap of TiO 2 , which may increase the amount of charge carrier trapping site and reduce the possibility of photogenerated electron/hole recombination [65]. metal doping on a TiO2 photocatalyst gained in impurity energy level, narrowed band gap, and improved oxygen vacancies, which is favorable to extend the visible-light absorption and prevent reoxidation [61][62][63][64]; and (b) the metal doping of TiO2 generated a new energy level in the band gap of TiO2, which may increase the amount of charge carrier trapping site and reduce the possibility of photogenerated electron/hole recombination [65].  Various experiments have been conducted by researchers to develop the doping of TiO 2 for treating organic pollutants that were possibly presented in OPW. Wang et al. synthesized the tungsten (W)-doped TiO 2 nanoparticles synthesis using the sol-gel method for reducing the viscosity of oilfield sewage under the mercury lamp illumination [66]. The W-doped TiO 2 exhibited better photoactivity than undoped TiO 2 with the optimum conditions at 1% of W-doped TiO 2 loading, pH of 3 in the sol-gel process, and 3% of W loading on TiO 2 .
Other dopants for TiO 2 were also applied for advancing the photocatalytic process toward organic compounds that are presented in OPW, which is summarized in Table 3. The success of the photodegradation process using the doped TiO 2 can be determined by the appearance of an intermediate as the result of organic pollutant oxidation by reactive oxygen species (ROS), such as the hydroxyl radical (•OH) as illustrated in the example for the degradation mechanism of 4-nitrophenol (4-NP) by B-doped TiO 2 in Figure 7 [67]. Under UV-light illumination, B-TiO 2 generated 90% degradation of 4-NP (k = 0.0322 min −1 ), which was 11% higher than the pure TiO 2 (k = 0.006 min −1 ). This improvement can be explained by the formation of Ti 3+ due to B doping, which was responsible for enhancing the entrapment of photogenerated electron/hole as per the below reaction: Under the solar experiment, the photodegradation and adsorption rate constant of Ag-S/TiO 2 (Eg = 2.39 eV) obtained were 2.4-and 4.1-times larger than the bare TiO 2 (Eg = 3.05 eV), respectively. The BET surface area and pore volume of Ag-S/TiO 2 were found to be higher up to 60.6% and 30%, respectively. [70] Transition metal (Iron (Fe), Vanadium (V), and Tungsten (W)) Photocatalytic degradation of BTEX Solvothermal 3.14 (Fe-TiO 2 ); 2.9 (W-TiO 2 and V-TiO 2 ) The visible light catalytic activity of all doped TiO 2 under is greater than that of pure TiO 2 . The V-TiO 2 shows the highest photocatalytic activity followed by the W-TiO 2 (54% conversion) and Fe-TiO 2 (48% conversion) with the conversion of 69%. The UV-Vis diffuse reflectance spectra reveal that the V-TiO 2 has the highest visible light absorption followed by the W-TiO 2 , Fe-TiO 2 , and undoped TiO 2 . The enhancement of TiO 2 by transition metal doping is most likely due to the effect of the highest increase in visible light absorption as well as the smallest particle size among the V-TiO 2 doped samples. [71]  Photodegradation efficiencies of Ce-doped TiO 2 (CeT) gained higher than undoped TiO 2 . The degradation efficiency by the CeT was consistent with the high desired surface area, pore size, and the particle size of the catalysts. Furthermore, the proper amount of Ce on TiO 2 has less photoluminescent (PL) emission than undoped TiO 2 and P25, indicating an increase in electron-hole separation and a reduction in photoexcited charge carrier recombination. [73] doped samples.

Mangan (Mn)
Photooxidation of benzene, toluene, and xylene Sol-gel 3 Under UV irradiation and in the appearance of oxygen, the degradation of benzene, toluene, and xylene by Mn-TiO2 can be achieved with the yields 92.6%, 82.9%, and 75%, respectively. The red-shift in the band gap energy upon Mn-doped TiO2 was observed, which shows the widening of UV-Vis absorption. [72] Cerium (Ce) Visible light degradation of toluene and oxylene Sonochemical synthesis 2.89-3.07 Photodegradation efficiencies of Ce-doped TiO2 (CeT) gained higher than undoped TiO2. The degradation efficiency by the CeT was consistent with the high desired surface area, pore size, and the particle size of the catalysts. Furthermore, the proper amount of Ce on TiO2 has less photoluminescent (PL) emission than undoped TiO2 and P25, indicating an increase in electron-hole separation and a reduction in photoexcited charge carrier recombination.
[73] According to Dahl et al., the synthesis of nanoscale TiO2 composite material has been studied and widely reported in approximately 11,000 research articles that indicated the feasibility of this strategy for advancing TiO2 photocatalyst [74]. The TiO2-basedcomposite consists of more than one crystal phase in the solid phase, such as mixed-phase TiO2 or composite with non-TiO2 material.
The TiO2 composite could utilize wide range of light absorption up to visible light through a heterojunction effect, which conducted better photocatalytic performance by increasing the separation efficiency of photoexcited charge carriers between their interface or enhancing the adsorption capacity using the support material as depicted in Figure 8 [54,55,75]. Numerous TiO2-based heterostructured photocatalyst have been synthesized and applied for degrading numerous organic compounds that possibly appeared in OPW According to Dahl et al., the synthesis of nanoscale TiO 2 composite material has been studied and widely reported in approximately 11,000 research articles that indicated the feasibility of this strategy for advancing TiO 2 photocatalyst [74]. The TiO 2 -basedcomposite consists of more than one crystal phase in the solid phase, such as mixed-phase TiO 2 or composite with non-TiO 2 material.
The TiO 2 composite could utilize wide range of light absorption up to visible light through a heterojunction effect, which conducted better photocatalytic performance by increasing the separation efficiency of photoexcited charge carriers between their interface or enhancing the adsorption capacity using the support material as depicted in Figure 8 [54,55,75]. Numerous TiO 2 -based heterostructured photocatalyst have been synthesized and applied for degrading numerous organic compounds that possibly appeared in OPW with improved performance and gained appropriate surface area and band gap as shown in Table 4.
Moreover, several studies showed that there was an improvement in the performance of mixed-phase TiO 2 , such as anatase-rutile (AR) and anatase-TiO 2 (B) compared to a single phase of TiO 2 [76][77][78][79]. In addition, Ai et al. reported that TiO 2 intercalated talc nanocomposites photodegraded more than 99.5% of 2,4-dichlorophenol (2,4-DCP) in 1 h under high-pressure mercury UV-lamp illumination (λ = 365 nm) while able to maintain high stability after 20 cycles (99% of 2,4-DCP degradation). This was due to the strong absorption ability of talc, which improved the power of capture-recombination carriers and photon absorption [80]. 0.017 (4-CP); 0.0108 (3-P-1-P) Figure 8. (a) Charge carrier migration mechanism of TiO2-based nanocomposite material, including trapping on TiO2 and the second phase/component and (b) TiO2 intercalation on the support material (example: graphene), which increases the light absorption region and intensity, charge carrier life-time, and absorptivity toward organic pollutants [81].  Figure 8. (a) Charge carrier migration mechanism of TiO2-based nanocomposite material, including trapping on TiO2 and the second phase/component and (b) TiO2 intercalation on the support material (example: graphene), which increases the light absorption region and intensity, charge carrier life-time, and absorptivity toward organic pollutants [81]. Numerous TiO2-based composite materials have shown their excellent properties, including the capability to tune the surface properties, such as open coordination sites, acidity/basicity, and hydrophilicity, which play important roles in the adsorption process as one of the critical factors relevant to photocatalysis and further modification [74]. Chekem et al. synthesized the activated carbon (AC)-TiO2 composite material by coating titania on the AC surface, which has been applied in the adsorption/photodegradation of phenol as CeO2/TiO2 Phenol 76.9 2.88 0.0302 [86] Numerous TiO2-based composite materials have shown their excellent properties, including the capability to tune the surface properties, such as open coordination sites, acidity/basicity, and hydrophilicity, which play important roles in the adsorption process as one of the critical factors relevant to photocatalysis and further modification [74]. Chekem et al. synthesized the activated carbon (AC)-TiO2 composite material by coating titania on the AC surface, which has been applied in the adsorption/photodegradation of phenol as illustrated in Figure 9 [87]. CeO2/TiO2 Phenol 76.9 2.88 0.0302 [86] Numerous TiO2-based composite materials have shown their excellent properties, including the capability to tune the surface properties, such as open coordination sites, acidity/basicity, and hydrophilicity, which play important roles in the adsorption process as one of the critical factors relevant to photocatalysis and further modification [74]. Chekem et al. synthesized the activated carbon (AC)-TiO2 composite material by coating titania on the AC surface, which has been applied in the adsorption/photodegradation of phenol as illustrated in Figure 9 [87].
Research reported that AC-TiO2 with 25 wt% of TiO2 (CAT25) showed a higher adsorption capacity due to a larger surface area (q = 124.5 mg/g, SBET = 609 m 2 /g) compared [ Numerous TiO2-based composite materials have shown their excellent properties, including the capability to tune the surface properties, such as open coordination sites, acidity/basicity, and hydrophilicity, which play important roles in the adsorption process as one of the critical factors relevant to photocatalysis and further modification [74]. Chekem et al. synthesized the activated carbon (AC)-TiO2 composite material by coating titania on the AC surface, which has been applied in the adsorption/photodegradation of phenol as illustrated in Figure 9 [87].
Research reported that AC-TiO2 with 25 wt% of TiO2 (CAT25) showed a higher adsorption capacity due to a larger surface area (q = 124.5 mg/g, SBET = 609 m 2 /g) compared with pristine AC material (q = 117.4 mg/g, SBET = 571 m 2 /g), which led to the enhancement [86] mance of mixed-phase TiO2, such as anatase-rutile (AR) and anatase-TiO2(B) compared to a single phase of TiO2 [76][77][78][79]. In addition, Ai et al. reported that TiO2 intercalated talc nanocomposites photodegraded more than 99.5% of 2,4-dichlorophenol (2,4-DCP) in 1 h under high-pressure mercury UV-lamp illumination (λ = 365 nm) while able to maintain high stability after 20 cycles (99% of 2,4-DCP degradation). This was due to the strong absorption ability of talc, which improved the power of capture-recombination carriers and photon absorption [80].   Numerous TiO 2 -based composite materials have shown their excellent properties, including the capability to tune the surface properties, such as open coordination sites, acidity/basicity, and hydrophilicity, which play important roles in the adsorption process as one of the critical factors relevant to photocatalysis and further modification [74]. Chekem et al. synthesized the activated carbon (AC)-TiO 2 composite material by coating titania on the AC surface, which has been applied in the adsorption/photodegradation of phenol as illustrated in Figure 9 [87].   The TiO2-based composite photocatalyst has been utilized further for treating salineproduced water (SWP), which is similar to OPW but mixed with saline water. The photocatalytic performance of the pristine TiO2 failed to degrade organic pollutants in SWP due to the high concentration of chloride ion (Cl − ) that can neutralize HO • species and inhibit the chemical bond breaking of organic species [90].
Andreozzi et al. invented a graphene-like TiO2 nanocomposite (rGO-TiO2) using the facile hydrothermal method with high desired physicochemical properties that applied band-energy engineering, such as high surface area (up to 179.9 m 2 /g), uniform distribu- Figure 9. Scheme of (A) TiO 2 impregnation at the external porosity of AC support by surface coating (CATX, X referred to %wt of TiO 2 ) and (B) pollutant transfer towards photocatalytic center [87]. Reproduced with permission from Elsevier, 2022.
Research reported that AC-TiO 2 with 25 wt% of TiO 2 (CAT25) showed a higher adsorption capacity due to a larger surface area (q = 124.5 mg/g, S BET = 609 m 2 /g) compared with pristine AC material (q = 117.4 mg/g, S BET = 571 m 2 /g), which led to the enhancement of the adsorption/photodegradation process until approximately 95% of phenol degradation has been achieved under UV light illumination (λ = 270 nm). In addition, another study revealed the feasibility of Fe 3+ -TiO 2 -Zeolite composite material in advancing the diminution of COD concentration in oilfield wastewater both under sunlight and mercury UV-lamp irradiation by reducing the lower band from 3.06 eV (405 nm) to 2.95 eV (420 nm) [88].
Furthermore, the improvement of Fe 3+ -TiO 2 -Zeolite composite performance in the photocatalytic process was due to the involvement of Fe 3+ in trapping electrons at the composite surface and transferring electrons to the adsorbed oxygen molecule as shown in Table 5. Syed et al. also reported that the epoxy resin/nano-TiO 2 composite material as a photocatalyst showed a higher removal of organic pollutants in OPW under direct sunlight radiation in terms of reducing dissolved oxygen (DO), COD, turbidity, conductivity, and total dissolved solids [89]. The TiO 2 -based composite photocatalyst has been utilized further for treating salineproduced water (SWP), which is similar to OPW but mixed with saline water. The photocatalytic performance of the pristine TiO 2 failed to degrade organic pollutants in SWP due to the high concentration of chloride ion (Cl − ) that can neutralize HO • species and inhibit the chemical bond breaking of organic species [90].
Andreozzi et al. invented a graphene-like TiO 2 nanocomposite (rGO-TiO 2 ) using the facile hydrothermal method with high desired physicochemical properties that applied band-energy engineering, such as high surface area (up to 179.9 m 2 /g), uniform distribution of mesopore, and a slightly lower band gap compared to the pristine TiO 2 because of the formation of intraband gaps upon the incorporation of rGO [91]. Furthermore, rGO-TiO 2 with 10% amount of rGO achieved the greatest reduction of total organic carbon (TOC) among the other weight ratios (1%, 5%, and 20%) and bare TiO 2 as in Figure 10A and demonstrated the ability to degrade common organic species in OPW, such as acetic acid, phenol, naphthalene, xylene, and toluene as shown in Figure 10B [91]. The improvement of TiO2-based photocatalyst can be gained by combining nanostructure modification and energy band engineering, which is expected to have much higher performance in degrading organic species in OPW. Rongan et al. managed to fabricate S-scheme photocatalyst Bi2O3/TiO2 nanofibers (NFs) via electrospinning and in-situ photo reductive deposition processes [92].
It was confirmed that Bi2O3/TiO2 NFs possessed well desired physicochemical properties, such as high surface area (51 m 2 /g), uniform mesoporous, red-shift light absorption, The improvement of TiO 2 -based photocatalyst can be gained by combining nanostructure modification and energy band engineering, which is expected to have much higher performance in degrading organic species in OPW. Rongan et al. managed to fabricate S-scheme photocatalyst Bi 2 O 3 /TiO 2 nanofibers (NFs) via electrospinning and in-situ photo reductive deposition processes [92].
It was confirmed that Bi 2 O 3 /TiO 2 NFs possessed well desired physicochemical properties, such as high surface area (51 m 2 /g), uniform mesoporous, red-shift light absorption, and hierarchical microspheres morphology with the size around 0.5-1 µm. Moreover, Bi 2 O 3 /TiO 2 NFs showed better performance than the bare Bi 2 O 3 and pristine TiO 2 in phenol photodegradation due to the unique hierarchical porous structure as illustrated in Figure 11. The improvement of TiO2-based photocatalyst can be gained by combining nanostructure modification and energy band engineering, which is expected to have much higher performance in degrading organic species in OPW. Rongan et al. managed to fabricate S-scheme photocatalyst Bi2O3/TiO2 nanofibers (NFs) via electrospinning and in-situ photo reductive deposition processes [92].
It was confirmed that Bi2O3/TiO2 NFs possessed well desired physicochemical properties, such as high surface area (51 m 2 /g), uniform mesoporous, red-shift light absorption, and hierarchical microspheres morphology with the size around 0.5-1 µm. Moreover, Bi2O3/TiO2 NFs showed better performance than the bare Bi2O3 and pristine TiO2 in phenol photodegradation due to the unique hierarchical porous structure as illustrated in Figure  11. Figure 11. Schematic mechanism of phenol removal by photocatalysis using Bi2O3/TiO2 NFs [92]. Reproduced with permission from Elsevier, 2022.
Another combination of energy band engineering and nanostructure modification for advancing photoactivity of TiO2 was revealed by Jo et al. [93]. In their study, hydrothermal process has been applied to construct TiO2 nanotubes-coated carbon fibers (TNTUCF) with various precursor concentrations, such as 5%, 7.5%, 10%, 12.5%, and 15%. From BTEX photodegradation test under UV illumination as in Figure 12, it has been Figure 11. Schematic mechanism of phenol removal by photocatalysis using Bi 2 O 3 /TiO 2 NFs [92]. Reproduced with permission from Elsevier, 2022.
Another combination of energy band engineering and nanostructure modification for advancing photoactivity of TiO 2 was revealed by Jo et al. [93]. In their study, hydrothermal process has been applied to construct TiO 2 nanotubes-coated carbon fibers (TNTUCF) with various precursor concentrations, such as 5%, 7.5%, 10%, 12.5%, and 15%. From BTEX photodegradation test under UV illumination as in Figure 12, it has been shown that TNTUCF at 10% concentration of the precursor gained the highest degradation efficiencies of BTEX at 81%, 97%, 99%, and 99%, respectively.
Moreover, the photoactivity of TNTUCF has been significantly enhanced compared to TiO 2 nanoparticle-coated CF (TUCF) and uncoated CF (UCF). The combined effect between large adsorption capacity and reduced recombination rates of electrons and holes on TNT explained the high performance of TNTUCF toward photocatalytic degradation of BTEX. However, excess amount of precursor concentration caused coverage of active sites on CF surface that may decrease the adsorption capacity of TNTUCF.
Wang et al. invented TiO 2 photoactivity enhancement by producing a heterostructured palladium oxide-loaded corroded TiO 2 nanobelts (PdO-C-NB) through two stages, including: hydrothermal and chemical precipitation processes [94]. This advanced material integrated beneficial aspects of TiO 2 nanobelts, such as large surface area, feasible synthesis methodology, and controllable morphology, as well as heterojunction that could increase the separation of photo-induced electron-hole pairs and encourage redox reaction.
Furthermore, corroding nanobelts was a good approach for roughening the surface, which boosts surface active sites and specific surface area, providing a more appropriate surface for heterogeneous nucleation. The increased specific surface area and decreased recombination of photoexited charge carriers were ascribed to the enhanced photocatalytic activity of PdO-C-NB, as demonstrated by N 2 adsorption-desorption and PL tests, as shown in Table 6 and Figure 13a. tion efficiencies of BTEX at 81%, 97%, 99%, and 99%, respectively.
Moreover, the photoactivity of TNTUCF has been significantly enhanced compared to TiO2 nanoparticle-coated CF (TUCF) and uncoated CF (UCF). The combined effect between large adsorption capacity and reduced recombination rates of electrons and holes on TNT explained the high performance of TNTUCF toward photocatalytic degradation of BTEX. However, excess amount of precursor concentration caused coverage of active sites on CF surface that may decrease the adsorption capacity of TNTUCF. Wang et al. invented TiO2 photoactivity enhancement by producing a heterostructured palladium oxide-loaded corroded TiO2 nanobelts (PdO-C-NB) through two stages, including: hydrothermal and chemical precipitation processes [94]. This advanced material integrated beneficial aspects of TiO2 nanobelts, such as large surface area, feasible synthesis methodology, and controllable morphology, as well as heterojunction that could increase the separation of photo-induced electron-hole pairs and encourage redox reaction.
Furthermore, corroding nanobelts was a good approach for roughening the surface, which boosts surface active sites and specific surface area, providing a more appropriate surface for heterogeneous nucleation. The increased specific surface area and decreased recombination of photoexited charge carriers were ascribed to the enhanced photocatalytic activity of PdO-C-NB, as demonstrated by N2 adsorption-desorption and PL tests, as shown in Table 6 and Figure 13a.
As an outcome in Figure 13b, PdO-C-NB exhibited higher phenol degradation up to 61% within 90 min under UV light, compared to TiO2 nanobelts (NB), which acquired only 35%. Moreover, a photocatalytic mechanism was proposed, as in Figure 13b, in which the separation of electron-hole pairs was further driven by transferring electrons from TiO2 nanobelts to PdO, which could hinder recombination of those pairs and optimize photodegradation performance.   [94]. Reproduced with permission from Elsevier, 2022.

TiO2-Based Photocatalytic Membrane (PM)
Performing photocatalysis process standalone using the TiO2-based semiconductor toward OPW pollutant might not be effective for a longer time due to numerous factors that can interfere with the effectiveness and stability of photodegradation performance like complex composition in OPW, light scattering effect due to high concentration of organic species, and closure of active site on photocatalyst surface, which exacerbates the mass transfer process [95]. Therefore, the incorporation of photocatalyst with other suitable technology seems to be a good option for addressing issues related to OPW treatment on a large scale. This combination can be conducted by taking into account the various changes that have occurred, such as rate of OPW degradation, physicochemical properties of treated OPW, and endurance for long-term continuous process. As an outcome in Figure 13b, PdO-C-NB exhibited higher phenol degradation up to 61% within 90 min under UV light, compared to TiO 2 nanobelts (NB), which acquired only 35%. Moreover, a photocatalytic mechanism was proposed, as in Figure 13b, in which the separation of electron-hole pairs was further driven by transferring electrons from TiO 2 nanobelts to PdO, which could hinder recombination of those pairs and optimize photodegradation performance.

TiO 2 -Based Photocatalytic Membrane (PM)
Performing photocatalysis process standalone using the TiO 2 -based semiconductor toward OPW pollutant might not be effective for a longer time due to numerous factors that can interfere with the effectiveness and stability of photodegradation performance like complex composition in OPW, light scattering effect due to high concentration of organic species, and closure of active site on photocatalyst surface, which exacerbates the mass transfer process [95]. Therefore, the incorporation of photocatalyst with other suitable technology seems to be a good option for addressing issues related to OPW treatment on a large scale. This combination can be conducted by taking into account the various changes that have occurred, such as rate of OPW degradation, physicochemical properties of treated OPW, and endurance for long-term continuous process.
The PM became familiar with advanced technology that unites the membrane separation process with photodegradation of photocatalyst. In general, the PM produced better performance in terms of reducing membrane fouling, minimizing light scattering effect, further degrading of organic species, and improving permeate flux, and quality under light irradiation [52]. Due to those beneficial aspects, the PM also can be applied in OPW treatment. The treatment process using PM can be summarized into two types-that is, non-pressure and pressure-driven as shown in Figure 14. Several researchers have put great effort to incorporate TiO 2 -based photocatalyst on membrane with different modules, and the details are displayed in Table 7.  (2) non-pressure driven [96]. Reproduced with permission from Elsevier, 2022.   (2) non-pressure driven [96]. Reproduced with permission from Elsevier, 2022. Polymeric matrix membranes are commonly used as support media for TiO 2 -based material attachment in the construction of TiO 2 -based PM. However, this fabrication generates a large amount of waste, which causes the TiO 2 -based PM to not be environmentally friendly. Worse, the polymeric structure of PM can be degraded under exposure to light radiation. Labuto et al. investigated the detachment of numerous polymeric membranes into aqueous solution, which has been proven through the determination of the nanoparticle concentration presented during exposure of UV-light as shown in Table 8 [101]. Table 8. Amount of nanoparticles present in aqueous media for polymeric membranes not exposed and exposed to UV illumination [101]. To promote green synthesis and sustainability, free-standing TiO 2 -based PM has been employed without using polymeric membrane supports. Liu et al. synthesized freestanding Ag/TiO 2 nanofiber membranes by electrospinning, followed by dispersion and vacuum filtration, which demonstrated improved photodegradation performance in terms of degradation and constant rate up to 80% and 0.0211 min −1 , respectively, as well as higher permeate flux compared to a P25-deposited membrane and TiO 2 nanofiber membrane [102]. Song et al. constructed self-standing photocatalytic membranes from Zr-doped TiO 2 nanofibrous via electrospinning, followed by a calcination process, that had superior tensile strength up to 1.32 MPa due to a well-connected and continuous netlike structure that maintains structural integrity even when bent, thus, demonstrating their superior structural flexibility [103]. Shen et al. incorporated TiO 2 on C 3 N 4 -decorated carbon-fiber (CF) cloth as a filter-membrane-shaped photocatalyst to enhance the separation efficiency and life-time of photogenerated carriers via heterojunction that boosted the photocatalytic degradation performance up to 87% after seven grades, which was higher than CF/C 3 N 4 (60%) and CF/TiO 2 cloth (8%) as presented in Figure 15 [104].  Table 8. Amount of nanoparticles present in aqueous media for polymeric membranes not exposed and exposed to UV illumination [101].  Figure 15. Summary of the PM process using a TiO2/C3N4/CF cloth filter membrane for pollutant degradation under light radiation with high desired morphological, good performance, and schematic mechanism of electron-hole separation [104]. Reproduced with permission from Elsevier, 2022.

Challenges and Future Development
TiO2-based photocatalyst technologies are promising for OPW treatment due to high photoactivity with excellent and high desired physicochemical properties, high chemical stability, low toxicity, and environmental friendliness. Those superiorities can also be applied to treating other organic pollutant sources, such as textile dye, organic solvent, petroleum hydrocarbons, detergent, and plastics [13,105]. Despite the fact that extensive and comprehensive investigations of advanced TiO2 modification have been conducted, until Figure 15. Summary of the PM process using a TiO 2 /C 3 N 4 /CF cloth filter membrane for pollutant degradation under light radiation with high desired morphological, good performance, and schematic mechanism of electron-hole separation [104]. Reproduced with permission from Elsevier, 2022.

Challenges and Future Development
TiO 2 -based photocatalyst technologies are promising for OPW treatment due to high photoactivity with excellent and high desired physicochemical properties, high chemical stability, low toxicity, and environmental friendliness. Those superiorities can also be applied to treating other organic pollutant sources, such as textile dye, organic solvent, petroleum hydrocarbons, detergent, and plastics [13,105]. Despite the fact that extensive and comprehensive investigations of advanced TiO 2 modification have been conducted, until combinations of the approaches above in terms of free-standing TiO 2 -based PM can be studied and applied, numerous aspects of the photodegradation process have yet to be thoroughly elucidated. These include: (1) There is not much research focused on treating OPW directly, as well as optimization of photodegradation performance, taking into account numerous aspects, such as pH condition, pollutant concentration, organic species variety, and light source and intensity, which affect the quality and sustainability of those technologies themselves. Apart from the environmental consequences of high organic effluent concentration in OPW, the amount of energy required has a significant impact on the photocatalysis process. This is one of the reasons why solar photocatalysis has recieved so much interest recently. (2) A life cycle assessment (LCA) of those technologies that are needed for large scale application, especially the treatment of OPW. LCA is one of the most important tools for identifying the environmental effects of a process, as well as its feasibility and costs. Although numerous studies have applied for photodegradation, there is still a lack of understanding about their end of life. (3) In terms of industrial scale feasibility, whether the photocatalytic process should be employed as a pre-treatment or as an independent treatment for OPW degradation become major constraints.
Therefore, efforts should be made to enhance sustainability, which is expected to achive high continuous performance under solar radiation over a wider range of working conditions. To achieve this, numerous developments can be proposed as follows: a.
Determining the most appropriate semiconductor and/or doping element that boosts TiO 2 photocatalytic performance and stability, which is in agreement with physicochemical properties, such as the active surface sites, morphology, optical, and electron transfer properties. As a result, both teoritical and experimental aspects can be supported by this approach. b.
Applying the photodegradation process of the OPW model solution using common organic pollutant species, such as phenol, BTEX, etc. Then, more in-depth thermodynamic and kinetic analyses are also possible. c.
Conceptualizing the process flow design of OPW photodegradation process using high novelty TiO 2 -based PM. This needs to be considered in terms of techno-economic and LCA parameters so that the sustainability of TiO 2 -based PM can be optimized for long-term industrial applications.

Conclusions
This review summarized the TiO 2 -based photocatalyst as a game-changing technology that can be improved to address limitation of TiO 2 semiconductors for OPW treatment. Numerous approaches have been explained in-depth in this review, such as energy band engineering, the construction of TiO 2 nanostructures, and the development of TiO 2 -based PM. The success of these strategies can be determined by observing their morphological form, optical absorption, photocatalytic performance, and sustainability.
Moreover, uniting photocatalysts with other technologies could create a sustainable and stable treatment process system, such as free-standing TiO 2 -based PM, which is a combination of photocatalysis capability and a membrane separation process. LCA, research, and the development of TiO 2 -based PM are expected to be economically viable with the ability to solve current challenges and bring application to the industrial scale.