Effect of the Pillar Size on the Electrochemical Performance of Laser-Induced Silicon Micropillars as Anodes for Lithium-Ion Batteries

Silicon micropillars with tunable sizes are successfully fabricated on copper foils by using nanosecond-pulsed laser irradiation and then used as anodes for lithium-ion batteries. The size of the silicon micropillars is manipulated by using different slurry layer thicknesses ranging from a few microns to tens of microns. The effects of the pillar size on electrochemical properties are thoroughly investigated. The smaller the pillars, the better the electrochemical performance. A capacity of 1647 mAh g−1 at 0.1 C current rate is achieved in the anode with the smallest pillars, with 1215, 892, and 582 mAh g−1 at 0.2, 0.5, and 1.0 C, respectively. Although a significant difference in discharge capacity is observed in the early period of cycling among micropillars of different sizes, this discrepancy becomes smaller as a function of the cycle number. Morphological studies reveal that the expansion of micropillars occurred during long-term cycling, which finally led to the formation of island-like structures. Also, the formation of a solid electrolyte interphase film obstructs Li+ diffusion into Si for lithiation, resulting in capacity decay. This study demonstrates the importance of minimizing the pillar size and optimizing the pillar density during anode fabrication.


Introduction
Ever since Sony Corporation first commercialized lithium-ion batteries (LIBs) in 1991, LIBs have played a critical role in enabling the emergence of electric vehicles (EVs) and the widespread availability of portable electronic devices such as laptops, smartphones, and video cameras [1][2][3][4][5][6][7]. However, graphite, as the anode material of traditional LIBs, has almost reached its performance limit for energy storage, and therefore increasing the specific capacity of the anode material remains a challenge [8][9][10][11][12][13][14]. Silicon has been considered a promising anode candidate due to its low lithium-uptake potential (<0.5 V vs. Li + /Li) and unparalleled theoretical capacity (3579 mA h g −1 due to the formation of Li 15 Si 4 ), which is 10 times higher than that of a conventional graphite anode (372 mA h g −1 ) [15][16][17][18]. However, the practical application of Si as an anode material has been severely hindered by large volume changes and the instability of the solid electrolyte interphase (SEI) formed on the Si surface during electrochemical cycling [19,20]. Si undergoes large volume changes (~300%) during the

Sample Preparation
The Si waste powders from a wire saw slicing process for Si wafers in the manufacturing of solar cells were used in this study. The as-received powders from Kyocera Corporation (Higashiomi, Shiga, Japan) were used for experiments without any further processing. The Si powder was mixed with a binder polymer of polyimide and carbon black at a mass ratio of 75:15:10 and added to an organic solvent of N-methyl-2-pyrrolidone (NMP). The binder was dissolved in NMP solvent, where Si powder and carbon black particles were dispersed in it. The mixture was then agitated by a ball mill (ANZ-10S, Nitto Kagaku Co., Ltd., Nagoya, Japan) for 2 h to obtain a slurry. A layer of the slurry with thicknesses of 8, 13, and 20 µm was deposited onto a 50-µm Cu foil using a film applicator (Hohsen Corp., Osaka, Japan) and dried at 210 • C for 30 min to remove the NMP. After this step, the slurry layer is considered a solvent-free electrode tape. Then the Cu foil with slurry layer was transferred to the sample stage for laser irradiation.

Si Micropillar Growth
The slurry layer was irradiated with an Nd:YAG laser (Megaopto Co., Ltd, Wako, Saitama, Japan) having a wavelength of 532 nm. The excitation light source was a laser diode, and the laser system was air-cooled. The laser beam had a Gaussian profile with a diameter of 85 µm. A pulse width of 48.4 ns was used at a repetition frequency of 10 kHz. According to our previous study, if the laser fluence is too high or the scan speed is too low, the pillars could be ablated due to successive laser irradiation [39]. On the other hand, if the laser fluence is too low or the scan speed too high, the Si waste powders could not be completely melted [39]. Different laser fluences and scan speeds were employed for slurry layers of different thicknesses, and the most suitable ones for each condition were chosen to be used in this study. The laser fluence was 529 mJ/cm 2 for a slurry layer of 8 µm in thickness and 1057 mJ/cm 2 for slurry layers of 13 and 20 µm thickness, respectively. The scan speed was 1 mm/s. Area laser irradiation was conducted on the slurry layer to fabricate Si micropillar anodes for electrochemical testing. The line spacing was 57 µm. The laser irradiation conditions are summarized in Table 1.

Material Characterizations
The particle size of the Si waste was measured using a laser particle size analyzer (LA-960, Horiba, Ltd., Kyoto, Japan). The composition of the Si waste was analyzed with an X-ray diffractometer (D8 Advance, Bruker, Billerica, MA, USA) using Cu Kα radiation at 40 kV and 40 mA. The X-ray diffraction (XRD) results were collected from 10 • < 2θ < 100 • at a scan rate of 2 • /min. A scanning electron microscope (SEM, Model Inspect S50, FEI, OR, USA) was used to examine the surface morphology of Si micropillars. Quantitative measurement of the average base diameter of micropillars was performed using ImageJ software (National Institutes of Health, USA). Elemental analysis of the Si anode after 100 cycles was carried out using energy-dispersive X-ray (EDX) equipped with this SEM.

Electrochemical Measurements
An electrochemical cell (HS flat cell) was assembled by sandwiching a polypropylene membrane separator (Selion P2010, CS Tech Co., Ltd., Wonju, South Korea) between a lithium metal foil and a Si micropillar anode. LiPF 6 (1.0 M) in a mixture of ethylene carbonate and diethyl carbonate (1:1 vol %) was used as the liquid electrolyte (Hohsen Corp., Osaka, Japan). All electrochemical cells were assembled in an argon-filled glove box (DBO-1KP-K02, Miwa MFG). Galvanostatic cycling tests were carried out on a charge/discharge test system (HJ-1001 SM8, Hokuto Denko Corp., Tokyo, Japan) at varying current rates at room temperature. The discharge and charge cycle refer to the lithiation and delithiation of the anode, respectively. The voltage cutoffs were 0.01 and 1.5 V vs. Li/Li + . The mass loadings of Si were 2.48 mg/cm 2 for 20 µm layer thickness, 1.78 mg/cm 2 for 13 µm layer thickness, and 1.18 mg/cm 2 for 8 µm layer thickness, respectively. The current density of 1C rate used in this research was 3579 mA/g. After electrochemical testing, the electrochemical cells were disassembled in a glove box. The Si micropillar anodes were rinsed with dimethyl carbonate (DMC) solvent five times to remove the residual electrolyte. Figure 1 shows the SEM image, particle size distribution, and XRD pattern of as-received Si powders. It can be seen that the as-received Si powders had an inherently irregular morphology, with the size having a wide range from a few sub-microns to over 10 microns. As illustrated in Figure 1c, the strong X-ray diffraction peaks of the as-received waste powder were all indexed to crystal planes of silicon and no other phases were observed. In addition, since Cu Kα1 (λ = 1.5406 Å) and Cu Kα2 (λ = 1.54443 Å) radiation were both involved, the diffraction peaks were split at high angles.

Si Micropillar Growth
Appl. Sci. 2019, 9, x FOR PEER REVIEW 4 of 13 analysis of the Si anode after 100 cycles was carried out using energy-dispersive X-ray (EDX) equipped with this SEM.

Electrochemical Measurements
An electrochemical cell (HS flat cell) was assembled by sandwiching a polypropylene membrane separator (Selion P2010, CS Tech Co., Ltd., Wonju, South Korea) between a lithium metal foil and a Si micropillar anode. LiPF6 (1.0 M) in a mixture of ethylene carbonate and diethyl carbonate (1:1 vol %) was used as the liquid electrolyte (Hohsen Corp., Osaka, Japan). All electrochemical cells were assembled in an argon-filled glove box (DBO-1KP-K02, Miwa MFG). Galvanostatic cycling tests were carried out on a charge/discharge test system (HJ-1001 SM8, Hokuto Denko Corp., Tokyo, Japan) at varying current rates at room temperature. The discharge and charge cycle refer to the lithiation and delithiation of the anode, respectively. The voltage cutoffs were 0.01 and 1.5 V vs. Li/Li + . The mass loadings of Si were 2.48 mg/cm 2 for 20 µm layer thickness, 1.78 mg/cm 2 for 13 µm layer thickness, and 1.18 mg/cm 2 for 8 µm layer thickness, respectively. The current density of 1C rate used in this research was 3579 mA/g. After electrochemical testing, the electrochemical cells were disassembled in a glove box. The Si micropillar anodes were rinsed with dimethyl carbonate (DMC) solvent five times to remove the residual electrolyte. Figure 1 shows the SEM image, particle size distribution, and XRD pattern of as-received Si powders. It can be seen that the as-received Si powders had an inherently irregular morphology, with the size having a wide range from a few sub-microns to over 10 microns. As illustrated in Figure 1c, the strong X-ray diffraction peaks of the as-received waste powder were all indexed to crystal planes of silicon and no other phases were observed. In addition, since Cu Kα1 (λ = 1.5406 Å) and Cu Kα2 (λ = 1.54443 Å) radiation were both involved, the diffraction peaks were split at high angles.   13-, and 20-µm-thick slurry layers by single-line laser irradiations. Arrays of micropillars were formed along the laser irradiation path. It can be observed that the micropillars from the 20-µm-thick slurry layer were the largest (Figure 2c). With the decrease in slurry layer thickness, the micropillars became smaller and were distributed more densely (Figure 2a,b). The average base diameters of micropillars were measured and presented in Figure 2d. The diameter of micropillars growing from the 20-µm-thick slurry layer was the largest, with a value of 8 µm. By decreasing the slurry layer thickness to 13 µm, the diameter of the resultant micropillars was reduced to 6 µm. The smallest base diameter (~4 µm) was obtained from the thinnest slurry layer (8 µm), which was only half that from the 20-µm-thick slurry layer.  13-, and 20-µm-thick slurry layers by single-line laser irradiations. Arrays of micropillars were formed along the laser irradiation path. It can be observed that the micropillars from the 20-µm-thick slurry layer were the largest ( Figure 2c). With the decrease in slurry layer thickness, the micropillars became smaller and were distributed more densely (Figure 2a,b). The average base diameters of micropillars were measured and presented in Figure 2d. The diameter of micropillars growing from the 20-µm-thick slurry layer was the largest, with a value of 8 µm. By decreasing the slurry layer thickness to 13 µm, the diameter of the resultant micropillars was reduced to 6 µm. The smallest base diameter (~4 µm) was obtained from the thinnest slurry layer (8 µm), which was only half that from the 20-µm-thick slurry layer. The mechanism of Si micropillar growth from slurry layers of different thicknesses during the laser irradiation process is illustrated in Figure 3. As clarified by our previous research [39], Si particles on the top layers were directly heated by the laser and melted onto the Si particles under them. Due to the thermal conduction, with further laser heating, all the Si particles completely melted and spread out onto the Cu foil. In order to achieve stable equilibrium with low surface energy, the liquid Si merged to form larger Si islands on the Cu foil. During this process, carbon black, as a sacrificial agent, underwent plasma gasification and partial ignition in the air, generating a highpressure plasma and carbon oxide gas around the Si islands. Owing to the plasma-induced pressure around the Si islands, they were stretched along the laser beam direction and eventually micropillars were formed after solidification. In the course of this process, two scenarios were considered. If the slurry layer was thin, small Si islands formed, leading to small and thin pillars (Figure 3a). On the other hand, if a thick slurry layer was applied, the Si islands were relatively large since more particles were melted from the top layers and accumulated on the Cu foil. Therefore, larger micropillars were obtained ( Figure 3b). This study demonstrates the possibility of generating extremely small Si pillars on Cu foils by laser irradiation of a very thin layer of waste Si slurry. If the pillar was thin enough, the situation may approach that of Si NWs. The mechanism of Si micropillar growth from slurry layers of different thicknesses during the laser irradiation process is illustrated in Figure 3. As clarified by our previous research [39], Si particles on the top layers were directly heated by the laser and melted onto the Si particles under them. Due to the thermal conduction, with further laser heating, all the Si particles completely melted and spread out onto the Cu foil. In order to achieve stable equilibrium with low surface energy, the liquid Si merged to form larger Si islands on the Cu foil. During this process, carbon black, as a sacrificial agent, underwent plasma gasification and partial ignition in the air, generating a high-pressure plasma and carbon oxide gas around the Si islands. Owing to the plasma-induced pressure around the Si islands, they were stretched along the laser beam direction and eventually micropillars were formed after solidification. In the course of this process, two scenarios were considered. If the slurry layer was thin, small Si islands formed, leading to small and thin pillars (Figure 3a). On the other hand, if a thick slurry layer was applied, the Si islands were relatively large since more particles were melted from the top layers and accumulated on the Cu foil. Therefore, larger micropillars were obtained (Figure 3b). This study demonstrates the possibility of generating extremely small Si pillars on Cu foils by laser irradiation of a very thin layer of waste Si slurry. If the pillar was thin enough, the situation may approach that of Si NWs. Appl. Sci. 2019, 9, x FOR PEER REVIEW 6 of 13

Electrochemical Performance
The rate performances of Si micropillars at a series of increased current rates of 0.1, 0.2, 0.5, and 1.0 C are presented in Figure 4a. The coulombic efficiencies in the initial cycle are 79.9, 79.4, and 75.7% for Si pillars growing from 8-, 13-, and 20-µm-thick slurry layers, respectively. They all increase to over 97% in the subsequent cycles. The coulombic efficiency in the first cycle was naturally poor because the high surface-area-to-volume ratio caused more Li + to be trapped in the SEI layer [44]. It should be noted that the coulombic efficiency shows at slightly over 100% in cycle 26. The reason for this is likely to be that, in cycle 25 with a 1.0 C rate, the delithiation is not complete; some Li ions still remain in the anode. This causes the delithiation in cycle 26 to be a little higher than the lithiation, and therefore the coulombic efficiency is over 100%. The Si micropillars from 20-µm-thick slurry layer exhibited the worst performance with a capacity of 1378 mAh/g at 0.1 C and 303 mAh/g at 1.0 C, respectively. As the slurry layer thickness decreased to 13 µm, the specific capacity of micropillars increased to 1463 mAh/g at 0.1 C and 548 mAh/g at 1.0 C, respectively. The capacity was further improved when the slurry layer became much thinner. The highest capacity of 1647 mAh/g at 0.1 C was obtained for the thinnest slurry layer (8 µm), with a capacity of 582 mAh/g at 1.0 C that was almost doubled compared with that of the 20-µm-thick slurry layer. Figure 4b compares the cycling performances of Si micropillars at a current rate of 0.1 C. Significant differences in discharge capacity can be observed at the early period of cycling among the three samples. Si micropillars from the thinnest slurry layer (8 µm) present the best electrochemical performance with an initial discharge capacity of 1780 mAh/g, followed by the 13-µm-thick slurry layer with an initial discharge capacity of 1423 mAh/g. When the thickness of the slurry layer increased to 20 µm, the initial discharge capacity dropped to 1387 mAh/g. However, the subsequent capacity decay was rapid; it dropped down to nearly half of the initial discharge capacity at the 50th cycle for all the three samples. The discrepancy in discharge capacity became smaller as the cycle number increased. After 60 cycles, the discharge capacities of all three samples were very close to each other. The reversible capacities over 100 cycles of 8, 13, and 20 µm slurry layers were approximately 545, 453, and 385 mAh/g, respectively.
The enhanced electrochemical performance of Si micropillars at the early period of cycling has been achieved by reducing the slurry layer thickness. Such improvement can be attributed to the following reasons: (1) Smaller micropillars had a higher surface-area-to-volume ratio, which could reduce the occurrence of cracks on the surface and maintain the mechanical integrity. (2) Increased surface area and denser distribution of smaller micropillars provided more contact area between electrolyte and Si for large Li + flux. (3) Shorter Li + diffusion pathway in micropillars with a smaller diameter, which ensured a fast and homogeneous lithiation [35].

Electrochemical Performance
The rate performances of Si micropillars at a series of increased current rates of 0.1, 0.2, 0.5, and 1.0 C are presented in Figure 4a. The coulombic efficiencies in the initial cycle are 79.9, 79.4, and 75.7% for Si pillars growing from 8-, 13-, and 20-µm-thick slurry layers, respectively. They all increase to over 97% in the subsequent cycles. The coulombic efficiency in the first cycle was naturally poor because the high surface-area-to-volume ratio caused more Li + to be trapped in the SEI layer [44]. It should be noted that the coulombic efficiency shows at slightly over 100% in cycle 26. The reason for this is likely to be that, in cycle 25 with a 1.0 C rate, the delithiation is not complete; some Li ions still remain in the anode. This causes the delithiation in cycle 26 to be a little higher than the lithiation, and therefore the coulombic efficiency is over 100%. The Si micropillars from 20-µm-thick slurry layer exhibited the worst performance with a capacity of 1378 mAh/g at 0.1 C and 303 mAh/g at 1.0 C, respectively. As the slurry layer thickness decreased to 13 µm, the specific capacity of micropillars increased to 1463 mAh/g at 0.1 C and 548 mAh/g at 1.0 C, respectively. The capacity was further improved when the slurry layer became much thinner. The highest capacity of 1647 mAh/g at 0.1 C was obtained for the thinnest slurry layer (8 µm), with a capacity of 582 mAh/g at 1.0 C that was almost doubled compared with that of the 20-µm-thick slurry layer. Figure 4b compares the cycling performances of Si micropillars at a current rate of 0.1 C. Significant differences in discharge capacity can be observed at the early period of cycling among the three samples. Si micropillars from the thinnest slurry layer (8 µm) present the best electrochemical performance with an initial discharge capacity of 1780 mAh/g, followed by the 13-µm-thick slurry layer with an initial discharge capacity of 1423 mAh/g. When the thickness of the slurry layer increased to 20 µm, the initial discharge capacity dropped to 1387 mAh/g. However, the subsequent capacity decay was rapid; it dropped down to nearly half of the initial discharge capacity at the 50th cycle for all the three samples. The discrepancy in discharge capacity became smaller as the cycle number increased. After 60 cycles, the discharge capacities of all three samples were very close to each other. The reversible capacities over 100 cycles of 8, 13, and 20 µm slurry layers were approximately 545, 453, and 385 mAh/g, respectively.
The enhanced electrochemical performance of Si micropillars at the early period of cycling has been achieved by reducing the slurry layer thickness. Such improvement can be attributed to the following reasons: (1) Smaller micropillars had a higher surface-area-to-volume ratio, which could reduce the occurrence of cracks on the surface and maintain the mechanical integrity. (2) Increased surface area and denser distribution of smaller micropillars provided more contact area between electrolyte and Si for large Li + flux.  It is well known that the high conductivity of the active material and short path length of ions are two important factors that improve the rate performance of electrode for Li-ion batteries [45]. The characteristic time constant t for ion diffusion is proportional to the square of the diffusion length L and inversely proportional to ion diffusivity (D) [22,46], as shown in Equation (1). The reduction in the diameter of Si micropillars (equivalent to diffusion length L) is an effective way to shorten the diffusion time t, and therefore improve the electrochemical properties of electrode material.

Morphological Change of Si Micropillars during Electrochemical Cycling
To clarify the reasons for the rapid capacity decay in the early stage and the insignificant discrepancy in the capacities of three samples at the later period of cycling, as shown in Figure 4b, the morphological change of Si micropillars during electrochemical cycling was further examined. Micropillars growing from the 13-µm-thick slurry layer were used to study the morphological change during electrochemical cycling. The anode surface was characterized using SEM in terms of top view (Figure 5a), 45° tilted view (Figure 5b), and side view (Figure 5c)  It is well known that the high conductivity of the active material and short path length of ions are two important factors that improve the rate performance of electrode for Li-ion batteries [45]. The characteristic time constant t for ion diffusion is proportional to the square of the diffusion length L and inversely proportional to ion diffusivity (D) [22,46], as shown in Equation (1). The reduction in the diameter of Si micropillars (equivalent to diffusion length L) is an effective way to shorten the diffusion time t, and therefore improve the electrochemical properties of electrode material.

Morphological Change of Si Micropillars during Electrochemical Cycling
To clarify the reasons for the rapid capacity decay in the early stage and the insignificant discrepancy in the capacities of three samples at the later period of cycling, as shown in Figure 4b, the morphological change of Si micropillars during electrochemical cycling was further examined. Micropillars growing from the 13-µm-thick slurry layer were used to study the morphological change during electrochemical cycling. The anode surface was characterized using SEM in terms of top view (Figure 5a), 45 • tilted view (Figure 5b), and side view (Figure 5c) after 1, 5, 35, and 100 cycles, respectively. After give cycles, the individual pillar structure could be observed, suggesting that volume expansion of Si had not occurred significantly. SEI products may form on the surface of micropillars due to the reductive reaction of electrodes and electrolytes [47]. After 35 cycles, the pillar structure turned into a separate island-like structure of irregular shapes. This may be because Si micropillars expanded during the charge/discharge process, and adjacent pillars aggregated to form islands with irregular shapes [48]. After 100 cycles, the spaces between the islands were further reduced, and the anode surface became flat. Some cracks can be seen on the anode surface, which could be associated with the contraction of Si in the delithiation process. The similar surface morphology of Si nanowire electrodes after 100 cycles was reported by Laik et al. [49]. It should be pointed out that, even though there were cracks on the anode surface, the Si layer was attached firmly to the Cu foil after 100 cycles, as seen from Figure 5c. The strong bond between the Si pillars and Cu foil could be due to two aspects: one is the remaining electrically conductive binder existing between them, and the other is the direct interfacial diffusion occurring between Si and Cu at a high temperature [50]. This demonstrates that the pillar structure significantly absorbed the volume expansion like the Si NW structure and prevented the destructive delamination of the Si layer from the Cu foil, which had been a serious problem for Si NP anodes.
pointed out that, even though there were cracks on the anode surface, the Si layer was attached firmly to the Cu foil after 100 cycles, as seen from Figure 5c. The strong bond between the Si pillars and Cu foil could be due to two aspects: one is the remaining electrically conductive binder existing between them, and the other is the direct interfacial diffusion occurring between Si and Cu at a high temperature [50]. This demonstrates that the pillar structure significantly absorbed the volume expansion like the Si NW structure and prevented the destructive delamination of the Si layer from the Cu foil, which had been a serious problem for Si NP anodes. Figure 5d compares the thickness of the Si layer on the Cu foil after a varying number of cycles. It can be seen that the volume expansion was negligible in the first cycle and the Si layer thickness remained about 8 µm. The thickness of the Si layer increased slightly to 11 µm after five cycles. However, a huge growth in Si layer thickness to about 30 µm can be observed after 100 cycles. This means that the Si layer thickness increased by a factor of four compared with the pristine anode sample. The volume expansion of Si could be one of the causes of this change. Another cause could be the continuous formation of SEI products. According to the study of SEI growth on Si nanocones by Li et al. [47], the SEI should have grown on the surface of micropillars continuously. After filling the space among the micropillars, SEI would further form and grow on the top layer of the micropillars. The thickness of the extra SEI layer on top of the micropillars could be several micrometers after dozens of cycles [47].
The EDX spectrum of a Si micropillar anode after 100 cycles and the mapping analysis of the detected elements are shown in Figure 6. The detected elements are O, C, Si, F, and P. The presence of O, C, Si, and F is consistent with the possible SEI products such as Li2CO3, (CH2OCO2Li)2, and LiF [51]. The high amount of O is likely due to the oxidation of anode when it was transferred from the glove box to the SEM chamber for characterization. The detection of only a small amount of P (1.37 wt %) indicates that only a tiny amount of electrolyte residue is left on the Si anode. Since Li has very low energy of characteristic radiation, it cannot be detected in the EDX spectrum. The EDX result evidences that an SEI layer has formed on the top layer of the silicon anode after 100 cycles.   Figure 5d compares the thickness of the Si layer on the Cu foil after a varying number of cycles. It can be seen that the volume expansion was negligible in the first cycle and the Si layer thickness remained about 8 µm. The thickness of the Si layer increased slightly to 11 µm after five cycles. However, a huge growth in Si layer thickness to about 30 µm can be observed after 100 cycles. This means that the Si layer thickness increased by a factor of four compared with the pristine anode sample. The volume expansion of Si could be one of the causes of this change. Another cause could be the continuous formation of SEI products. According to the study of SEI growth on Si nanocones by Li et al. [47], the SEI should have grown on the surface of micropillars continuously. After filling the space among the micropillars, SEI would further form and grow on the top layer of the micropillars. The thickness of the extra SEI layer on top of the micropillars could be several micrometers after dozens of cycles [47].
The EDX spectrum of a Si micropillar anode after 100 cycles and the mapping analysis of the detected elements are shown in Figure 6. The detected elements are O, C, Si, F, and P. The presence of O, C, Si, and F is consistent with the possible SEI products such as Li 2 CO 3 , (CH 2 OCO 2 Li) 2 , and LiF [51]. The high amount of O is likely due to the oxidation of anode when it was transferred from the glove box to the SEM chamber for characterization. The detection of only a small amount of P (1.37 wt %) indicates that only a tiny amount of electrolyte residue is left on the Si anode. Since Li has very low energy of characteristic radiation, it cannot be detected in the EDX spectrum. The EDX result evidences that an SEI layer has formed on the top layer of the silicon anode after 100 cycles.  A schematic model (Figure 7) is used to illustrate the morphological change of Si micropillars during electrochemical cycling. Si micropillars expanded in the first few cycles, but the pillar structure is discernible (Figure 7b,c). SEI layers formed on the surfaces of micropillars due to the high A schematic model (Figure 7) is used to illustrate the morphological change of Si micropillars during electrochemical cycling. Si micropillars expanded in the first few cycles, but the pillar structure is discernible (Figure 7b,c). SEI layers formed on the surfaces of micropillars due to the high surface area. However, owing to limited space among micropillars, they merged with each other and formed an island-like structure (Figure 7d). After long-term cycling, an additional SEI layer formed on the top of the anode, and the anode became a flat and thick film with microsized cracks (Figure 7e). The accumulation of SEI products in the space among the micropillars as well as on the top layer of micropillars participates in the capacity decay by obstructing Li + from accessing the Si.
Appl. Sci. 2019, 9, x FOR PEER REVIEW 10 of 13 surface area. However, owing to limited space among micropillars, they merged with each other and formed an island-like structure (Figure 7d). After long-term cycling, an additional SEI layer formed on the top of the anode, and the anode became a flat and thick film with microsized cracks ( Figure  7e). The accumulation of SEI products in the space among the micropillars as well as on the top layer of micropillars participates in the capacity decay by obstructing Li + from accessing the Si. Finally, the effects of waste Si slurry thickness on the electrochemical cycling performance are investigated. As shown in Figure 8, the morphologies of the anode surfaces produced from different slurry layer thicknesses became very similar after 100 cycles. The independent micropillar structure had changed into a thick film structure, regardless of the initial diameters of the micropillars. This explains the insignificant discrepancy of the capacity of micropillars with different diameters at the later period of cycling. However, by comparing Figure 8a-c, it is clear that by using a thinner Si slurry thickness to generate thinner Si micropillars, the number of surface cracks on the anode surface could be greatly reduced. The reduction of crack generation indicates a longer service life of a LIB anode.  Finally, the effects of waste Si slurry thickness on the electrochemical cycling performance are investigated. As shown in Figure 8, the morphologies of the anode surfaces produced from different slurry layer thicknesses became very similar after 100 cycles. The independent micropillar structure had changed into a thick film structure, regardless of the initial diameters of the micropillars. This explains the insignificant discrepancy of the capacity of micropillars with different diameters at the later period of cycling. However, by comparing Figure 8a-c, it is clear that by using a thinner Si slurry thickness to generate thinner Si micropillars, the number of surface cracks on the anode surface could be greatly reduced. The reduction of crack generation indicates a longer service life of a LIB anode.
Appl. Sci. 2019, 9, x FOR PEER REVIEW 10 of 13 surface area. However, owing to limited space among micropillars, they merged with each other and formed an island-like structure (Figure 7d). After long-term cycling, an additional SEI layer formed on the top of the anode, and the anode became a flat and thick film with microsized cracks ( Figure  7e). The accumulation of SEI products in the space among the micropillars as well as on the top layer of micropillars participates in the capacity decay by obstructing Li + from accessing the Si. Finally, the effects of waste Si slurry thickness on the electrochemical cycling performance are investigated. As shown in Figure 8, the morphologies of the anode surfaces produced from different slurry layer thicknesses became very similar after 100 cycles. The independent micropillar structure had changed into a thick film structure, regardless of the initial diameters of the micropillars. This explains the insignificant discrepancy of the capacity of micropillars with different diameters at the later period of cycling. However, by comparing Figure 8a-c, it is clear that by using a thinner Si slurry thickness to generate thinner Si micropillars, the number of surface cracks on the anode surface could be greatly reduced. The reduction of crack generation indicates a longer service life of a LIB anode.

Conclusions
Si micropillars with various sizes were successfully fabricated from Si waste powder via nanosecond-pulsed laser irradiation for fabricating lithium-ion battery anodes. The pillar size was controllable by tuning the thickness of waste Si slurry layer. The smaller the thickness of the slurry layer, the smaller the size of the Si micropillars. The rate capability and capacity were dependent on the pillar size: the smaller the pillars, the better the electrochemical properties. The morphological changes of Si micropillars during the charge/discharge process caused the capacity decay in the later period of cycling. During the electrochemical cycling, Si micropillars expanded and formed an island-like structure. After 100 cycles, the Si layer was a flat and thick film with microsized cracks. The number of cracks could be reduced greatly by using a thinner Si slurry layer for micropillar generation. However, even though there was crack generation on the anode surface, the Si layer was firmly attached to the Cu foil after 100 cycles, which strongly demonstrated that the pillar structure had significantly absorbed the volume expansion and prevented the destructive delamination of the Si layer from the Cu foil.
This study has demonstrated the possibility of an efficient and environmentally friendly method of fabricating Si-based LIB anodes from waste Si materials. Future research will be focused on improving the cycling performance in the later period by optimizing the Si micropillar generation and controlling SEI formation.