Photo-Electrochemical Oxygen Evolution Reaction by Biomimetic CaMn 2 O 4 Catalyst

Featured Application: CaMn 2 O 4 , a green biomimetic catalyst, has the potential to generate oxygen by splitting water for sustainability applications. Abstract: Calcium manganese oxide catalysts are a new class of redox catalysts with signiﬁcant importance because of their structural similarity to natural oxygen-evolving complex in plant cells and the earth-abundant elemental constituents. In the present study, the photo-electrocatalytic properties of CaMn 2 O 4 in water-splitting were investigated. CaMn 2 O 4 powders with irregular shapes and nanowire shapes were synthesised using mechanochemical processing and a hydrothermal method, respectively. The anode in a photo-electrochemical cell was fabricated by embedding CaMn 2 O 4 powders within polypyrrole. The results showed that CaMn 2 O 4 induced a higher dark and light current in comparison to the control sample (polypyrrole alone). CaMn 2 O 4 nanowires exhibited higher dark and light current in comparison to irregular-shaped CaMn 2 O 4 powders. The di ﬀ erence was attributable to the higher surface area of nanowires compared to the irregular-shaped particles, rather than the di ﬀ erence in exposed crystal facets.


Introduction
The photocatalytic water splitting into its constituents, hydrogen and oxygen, has attracted much attention as a clean and renewable source of fuel. In the past, various semiconductor materials have been investigated as water oxidation catalysts [1]. However, it is still challenging to develop effective catalysts that split water under sunlight. Recently, calcium manganese oxides have gained significant attention as water oxidation catalysts, due to their earth-abundant and environmentally friendly elemental constituents and also a structural similarity to the natural photocatalytic centre in plant cells. In natural photosynthesis, bio-electricity decomposes water into hydrogen and oxygen within a unique catalytic centre composed of a CaMn 4 O 5 cluster, in the oxygen-evolving complex (OEC) enzyme in the Photosystem II protein [2][3][4]. This natural process is the most efficient known, for the photo-generation of H 2 from water. Among many calcium manganese oxides, CaMn 2 O 4 contains structural sub-units of (Mn 4 CaO x ), similar to the structure of natural CaMn 4 O 5 cluster in OEC [5,6]. This has led to extensive investigation of catalytic water oxidation properties of CaMn 2 O 4 [7][8][9]. Han et al. reported an oxygen-reduction reaction (ORR) catalytic activity of CaMn 2 O 4 microspheres consisting of aggregated nanoparticles [7]. Du et al. demonstrated that one-dimensional CaMn 2 O 4 nanostructures, synthesised using a solvothermal method, enabled quasi-four-electron transfer in the ORR [8]. These studies were electrochemical in nature and therefore were conducted without any light irradiation. It is very important to study the water splitting in the presence of light because the use of natural sunlight, as the source of energy, is the final goal in practical applications.
Najafpour et al. studied light-driven oxygen evolution by using an aqueous suspension of CaMn 2 O 4 particles, however only in the presence of various sacrificial reagents [9]. Studies of photo-catalysts in the dispersed form are of significant interest, however, from a practical perspective, it is crucial to study the immobilisation of catalysts on conducting electrodes as an anode [10]. To the best of our knowledge, there is no report on the study of light-driven electrochemical activity of CaMn 2 O 4 as a fixed anode material without sacrificial reagents.
In this study, CaMn 2 O 4 ultrafine powders were studied as an anode material in photo-electrochemical cells for their catalytic and photocatalytic properties in the water oxidation reaction. It has been reported that photocatalytic properties are greatly affected by the morphology of catalysts [11]. Therefore, we also investigated the effects of particle shapes on the photo-electrocatalytic properties of CaMn 2 O 4 .

Synthesis of Irregular-Shaped CaMn 2 O 4 Particles
All chemicals, except MnSO 4 .4H 2 O (99%, metals basis, Alfa Aesar, Heysham, Lancashire, England), were used without further purification. MnSO 4 .4H 2 O was dehydrated using the procedure reported elsewhere [12]. CaMn 2 O 4 ultrafine particles were synthesised by first producing CaMn 2 (CO 3 ) 3 nanoparticles by mechanochemical processing and subsequently thermally decompose the CaMn 2 (CO 3 ) 3 nanoparticles into CaMn 2 O 4 . CaMn 2 (CO 3 ) 3 was produced via the following reaction: Excess K 2 SO 4 (ACS, 99.0% min, Alfa Aesar, Ward Hill, MA, USA) salt was added to reduce the volume fraction of CaMn 2 (CO 3 ) 3 in the product phase so as to minimise particle agglomeration [13]. Before inducing the mechanochemical reaction, a stoichiometric amount of CaSO 4 (anhydrous, 99%, Alfa Aesar, Ward hill, MA, USA) and MnSO 4 were mixed in a hardened-steel milling vial using a SPEX 8000M mill (SPEX SamplePrep, Metuchen, NJ, USA). After 2 h of mixing, a stoichiometric amount of K 2 CO 3 (AnalaR NORMAPUR, VWR, Leuven, Belgium) along with K 2 SO 4 was introduced in the same milling vial along with hardened steel balls of 9.2 mm in diameter. The ball-to-powder mass ratio was 10:1. Then milling was performed for 4 h in a SPEX 8000M mill to obtain CaMn 2 (CO 3 ) 3 nanoparticles embedded in a K 2 SO 4 salt matrix. The as-milled powder was calcined at 950 • C for 1 h in air. Upon cooling the powder, K 2 SO 4 was removed by washing with deionised water (18 MΩ cm), using an ultrasonic bath and a centrifuge, until the total dissolved solids in the supernatant became less than 100 ppm. The washed powder was dried in an oven at 50 • C for several hours.

Synthesis of CaMn 2 O 4 Nanowires
CaCl 2 (>93%, 2 mmol, granular, anhydrous, Sigma Aldrich, Saint Louis, MO, USA) and 2.8 mmol of MnCl 2 (99.9%, Sigma Aldrich, Saint Louis, MO, USA) were mixed in 10 mL of deionised water. In another beaker, 1.2 mmol of KMnO 4 (analytical grade, Univar, Sydney, NSW, Australia) and 150 mmol of KOH (AnalaR NORMAPUR, VWR, Leuven, Belgium) were mixed in 10 mL of deionised water. Then, the KMnO 4 -KOH solution was added into the CaCl 2 -MnCl 2 solution dropwise, while stirring. A dark-brown precipitate was formed. The suspension was centrifuged to separate the precipitate from the supernatant. The remaining wet-cake was re-dispersed into 12 mL of ethanol and subjected to hydrothermal treatment at 190 • C for 40 h. The resulting precipitate was collected and washed 5-times with ethanol using a centrifuge and an ultrasonic bath.

Characterization Techniques
The crystal structure of the powders was examined at room temperature using a Bruker X-ray diffraction instrument (XRD, D 2 Phaser, Billerica, MA, USA) with Cu-Kα radiation of 1.54059 Å wavelength. The nanostructure and surface morphology of the powders were studied using a JEOL2100F field emission transmission electron microscope (TEM, JEOL, Tokyo, Japan) at 200 kV and also an Ultraplus field-emission scanning electron microscope (FESEM, Zeiss, Oberkochen, Germany) at 1 kV. The specific surface area was measured by the Brunauer-Emmett-Teller (BET) N 2 -gas adsorption method using a TriStar II 3020 system (Micromeritics, Norcross, GA, USA). Prior to BET measurements, the powders were degassed under vacuum at 150 • C for 24 h. The bandgap energy of samples was estimated from UV-Vis optical absorption spectra taken using a Cary 60 spectrophotometer (Agilent, Santa Clara, CA, USA). Optical transmittance of the samples coated on a quartz plate was measured and the absorption spectra were converted into the Tauc plot of (hvα) 2 versus hv, where h is the Planck's constant, ν is the photon's frequency, and α is the optical absorption coefficient. The linear zone of the Tauc curve was extrapolated to the energy axis to estimate the direct bandgap. X-ray photoelectron spectroscopy (XPS) was conducted using a SPECS PHOIBOS 100 Analyser installed in a high-vacuum chamber with a base pressure below 10-8 mbar. An incident monochromated X-ray beam of Al-Kα radiation with a photon energy of 1486.6 eV was used at 12 kV and 144 W. XPS binding energy spectra were recorded at a pass energy of 20 eV and a step width of 0.05-0.1 eV in the fixed analyser transmission mode. To increase the signal/noise ratio, multi-scans were conducted and the signal intensity was accumulated. Broad survey scans were recorded at a pass energy of 60 eV and a step width of 0.5 eV. XPS data analysis was carried out using the commercial CasaXPS software package.

Preparation of CaMn 2 O 4 Electrodes on Conducting Glass Slide
Prior to the deposition of electrode materials, Fluorine doped tin oxide (FTO) coated glass slides were cleaned in the following manner. First, the glass slides, immersed in acetone within a TLC chamber, were sonicated for 90 min using a MTH ultrasonic bath (Branson, Danbury, CT, USA), washed with water and air dried. Subsequently, the remaining organic contaminants from the slides were removed using a DIG UV PSD PR SERIES digital ozone-UV cleaner (Novascan, Boone, IA, USA) for 20 min. The slides were further cleaned in a PLAMAFLO PDC-FMG plasma cleaner (Harrick Plasma, Ithaca, NY, USA), followed by drying using an IKA®RCT basic hotplate (IKA, Staufen, Germany) at 60 • C.
Polypyrrole/CaMn 2 O 4 films were deposited on the cleaned FTO glass slides by spin-coating, using the following procedure. First, 85 mg of iron (III) p-toluenesulfonate (Fe(III)-pTS) (Sigma Aldrich, Saint Louis, MO, USA) was dissolved in 1 mL ethanol (Sigma Aldrich, Saint Louis, MO, USA) and sonicated for 10 min. Then, 8 mg of CaMn 2 O 4 was added to the solution and sonicated for a further hour. The resulting solution (100 µL) was drop-cast onto the slide surface using a micropipette. The slides were spun at 1500 revolutions per min (rpm) for 120 s using a WS-400B-6NPP/LITE spin-coater (Laurell Technologies, North Wales, PA, USA). After spin-coating, the sample was quickly transferred to a preheated hot plate and dried at 60 • C for 15 min. Control samples were prepared without the addition of CaMn 2 O 4 .
Vapour phase polymerisation of polypyrrole was carried out in a separate conical flask (500 mL capacity), equipped with a rubber stopper containing a crocodile clip. In the flask, 0.500 mL pyrrole (Sigma Aldrich, Saint Louis, MO, USA) was placed and the spin-coated FTO glass substrates were held above the pyrrole solution by the crocodile clip. The flask was placed in an oven at 60 • C for 25 min to allow polymerization of pyrrole on the slide surface. The sample was washed thoroughly with ethanol and left to dry overnight. A copper wire was attached to the FTO surface with conductive silver paint Appl. Sci. 2019, 9, 2196 4 of 11 and epoxy resin. Upon solidification of the silver paste, the contact area of the wire was covered with epoxy glue.

Studies of CaMn 2 O 4 Electrode on FTO as OER Photocatalysts
Working electrodes were placed within a fully-enclosed quartz cell (5 × 5 × 5 cm) inside a closed cabinet that comprised a Faraday cage. A Pt mesh (1 × 2 cm) was used as the counter electrode. A BASi Ag/AgCl aqueous salt bridge (KCl, 3 M) was used as a reference electrode. The cell was filled with a 0.2 M Na 2 SO 4 aqueous solution electrolyte, adjusted to pH 12 by adding NaOH. Prior to the experiment, nitrogen gas was bubbled in the electrolyte for 30 min. Linear sweep voltammetry (LSV) and chronoamperograms (CA) were performed using an EDAQ466 potentiostat (Biologic, Seyssinet-Pariset, ARA, France). Where applicable, a SoLux daylight MR16 halogen light bulb (12 V, 50 W, 24 • ca. 0.25 sun intensity) with a stable output range of 275-750 nm was used to illuminate the sample. The distance between light and working electrode was 10 cm. A Thorlabs visible-light bandpass filter (315-710 nm) was placed 1.5 cm in front of the light source to remove infra-red wavelengths. Figure 1 shows the X-ray diffraction pattern of the synthesised CaMn 2 O 4 powders, where the diffraction peaks can be indexed to the orthorhombic phase of CaMn 2 O 4 (JCPDS card No 74-2293) [14]. The distance between light and working electrode was 10 cm. A Thorlabs visible-light bandpass filter (315-710 nm) was placed 1.5 cm in front of the light source to remove infra-red wavelengths. Figure 1 shows the X-ray diffraction pattern of the synthesised CaMn2O4 powders, where the diffraction peaks can be indexed to the orthorhombic phase of CaMn2O4 (JCPDS card No 74-2293) [14].    (Figure 2a,b). The large particle sizes can be attributed to the higher temperature required to decompose the carbonate precursors. As evidenced in Figure 2c, irregular-shaped CaMn 2 O 4 particles showed high crystallinity with clearly distinguished lattice fringes. The CaMn 2 O 4 powder made using the hydrothermal method had wire shapes with diameters of~500 nm and varying lengths (Figure 2d,e). The inset in Figure 2e shows the electron diffraction pattern of the wires, from which the growth direction of nanowires was identified as [001] (Figure 2f). The BET surface areas of the irregular-shaped powder and nanowire powder were 4.7 m 2 g −1 and 5.4 m 2 g −1 , respectively. Figure 3 shows the XPS spectra of CaMn 2 O 4 nanowires and irregular-shaped particles. As shown in Figure 3a, two strong peaks corresponding to Mn2p3/2 and Mn2p1/2 were observed at approximately 5 of 11 641 and 653 eV, respectively. Figure 3b shows the spectra near Mn3s peaks. Average oxidation state (AOS) was calculated using the linear relationship with splitting energy between two Mn3s peaks [15]. AOS for irregular-shaped particles and nanowires was found to be 3.07 and 2.96, respectively, which is in good agreement with the theoretical value of 3.  Figure 2 shows a typical SEM and TEM images of CaMn2O4 powders. The CaMn2O4 powder made by mechanochemical processing were irregular in shape with sizes from 200 nm to 2 µm ( Figure  2a,b). The large particle sizes can be attributed to the higher temperature required to decompose the carbonate precursors. As evidenced in Figure 2c, irregular-shaped CaMn2O4 particles showed high crystallinity with clearly distinguished lattice fringes. The CaMn2O4 powder made using the hydrothermal method had wire shapes with diameters of ~500 nm and varying lengths (Figure 2d,e). The inset in Figure 2e shows the electron diffraction pattern of the wires, from which the growth direction of nanowires was identified as [001] (Figure 2f). The BET surface areas of the irregularshaped powder and nanowire powder were 4.7 m 2 g -1 and 5.4 m 2 g -1 , respectively. Figure 3 shows the XPS spectra of CaMn2O4 nanowires and irregular-shaped particles. As shown in Figure 3a, two strong peaks corresponding to Mn2p3/2 and Mn2p1/2 were observed at approximately 641 and 653 eV, respectively. Figure 3b shows the spectra near Mn3s peaks. Average oxidation state (AOS) was calculated using the linear relationship with splitting energy between two Mn3s peaks [15]. AOS for irregular-shaped particles and nanowires was found to be 3.07 and 2.96, respectively, which is in good agreement with the theoretical value of 3.        Figure 5 shows the electrocatalytic performance of the samples, tested in 0.2 M Na2SO4 aqueous solution, with the pH adjusted to 12, at 1.00 V (vs Ag/AgCl) bias, with and without light illumination.  As shown in Figure 5, a significant increase in both dark-and photo-current was observed for the PPy/CaMn2O4 films in comparison to the control PPy film alone. A significant increase in photocurrent was also observed when a small amount of CaMn2O4 powder was added to the PPy polymer. The control PPy film exhibited light and dark current densities of 447 µA cm −2 and 230 µA As shown in Figure 5, a significant increase in both dark-and photo-current was observed for the PPy/CaMn 2 O 4 films in comparison to the control PPy film alone. A significant increase in photocurrent was also observed when a small amount of CaMn 2 O 4 powder was added to the PPy polymer. The control PPy film exhibited light and dark current densities of 447 µA cm −2 and 230 µA cm −2 , respectively, whereas the films prepared from the mixture of CaMn 2 O 4 and PPy produced 701 µA cm −2 and 326 µA cm −2 for irregular-shaped particles, and 769 µA cm −2 and 380 µA cm −2 for nanowires in light and dark, respectively. It is also clear that the CaMn 2 O 4 nanowires/PPy film produced higher dark and photocurrents than the irregular-shaped CaMn 2 O 4 /PPy film. Evolved gas was traced using a customised apparatus, as shown in Figure S1. The analysis confirmed the production of oxygen at the anode as shown in Figure S2.

Studies on Current Density
Catalytic and photocatalytic activities occur on the surface of catalysts. Hence, in order to examine the intrinsic catalytic properties of materials, it is often convenient to normalise the indicators of photocatalytic activity with the specific surface area of materials. Table 1 compares the BET specific surface areas and increases in dark-and photo-current with regard to the control electrode, between irregular-shaped CaMn 2 O 4 powder and CaMn 2 O 4 nanowires. Since the optical bandgap energies of irregular-shaped CaMn 2 O 4 powder and CaMn 2 O 4 nanowires are nearly the same, the differences in the surface-area-normalised increase in photo-current, ∆I L /S, is expected to arise from the difference in particle shapes. Table 1 shows that ∆I L /S values of irregular-shaped CaMn 2 O 4 powder and CaMn 2 O 4 nanowires are similar to each other. The results suggest that the influence of particle shapes on the light-driven catalysis of CaMn 2 O 4 is relatively weak. It is speculated that the exposed facets along the growth-direction of nanowires do not have significantly different catalytic activities compared to the other crystal faces. On the other hand, the surface-area-normalised increase in photo-current, ∆I D /S, was higher for the electrode with nanowires than the electrode with irregular-shaped particles. The reason may be attributed to the difference in electric conductivity within the CaMn 2 O 4 /PPy composite electrode. Rod-or wire-shaped particles have a lower percolation threshold [16] and, given the semiconducting nature of CaMn 2 O 4 , wire-shaped particles will result in higher electrical conductivity than irregular-shaped particles in polymer composites. Table 1. Comparison between irregular-shaped CaMn 2 O 4 powder and CaMn 2 O 4 nanowires for Brunauer-Emmett-Teller (BET) specific surface area, increase in dark-and photo-current with regard to control electrode; BET specific surface area (S), dark current (I D ), photo-current (I L ), increase in dark current with respect to control (∆I D ), increase in photo-current with respect to control (∆I L ).

EIS and Tafel Plot Studies
In order to investigate the nature of the catalytic process, electrochemical impedance spectroscopy (EIS) and Tafel plot studies were undertaken. EIS was conducted potentiostatically at 1.00 V (vs. Ag/AgCl) under the same conditions as the amperometric studies, with the same light source. Figure 6a,b shows the Nyqist and Bode plots, respectively, of the irregular-shaped particles/PPy film, the nanowires/PPy, and the control PPy electrodes without CaMn 2 O 4 , in the dark and under light illumination.
Following previous work in our laboratory [17], the EIS data were modelled with the equivalent circuit shown in Figure 6c. The modelled results are depicted as the solid lines in Figure 6a. As can be seen, the modelled data yielded an excellent match with the measured data. source. Figure 6a,b shows the Nyqist and Bode plots, respectively, of the irregular-shaped particles/PPy film, the nanowires/PPy, and the control PPy electrodes without CaMn2O4, in the dark and under light illumination.
Following previous work in our laboratory [17], the EIS data were modelled with the equivalent circuit shown in Figure 6c. The modelled results are depicted as the solid lines in Figure 6a. As can be seen, the modelled data yielded an excellent match with the measured data.  Table 2 shows the results derived from the modelling. It is evident from Table 2 that Cdl was the highest for the CaMn2O4 nanowires/PPy sample. The capacitance Cdl is a comparative measure of the  Table 2 shows the results derived from the modelling. It is evident from Table 2 that C dl was the highest for the CaMn 2 O 4 nanowires/PPy sample. The capacitance C dl is a comparative measure of the active area of the samples tested. Polypyrrole films exhibited the lowest values for C dl . The higher catalytic performance of the CaMn 2 O 4 nanowires/PPy sample could, therefore, be attributed, at least in part, to a larger catalytically active area of nanowires. Table 2. Data from electrochemical impedance spectroscopy (ohmic resistance (R el )), adsorption resistance (R ad ), diffuse layer capacitance (C dl ), catalytic charge transfer resistance (R CT ), and capacitance expressed in terms of a constant phase element (Q CPE , n CPE , and C CPE ). Data from Tafel plot studies (slope (A), exchange current density (i o )). 'dark' = without light illumination; 'light' = with light illumination. In oxygen evolution (photo)electrocatalysis at pH 12, the catalytic performance may be controlled by reactant adsorption to the catalyst (with an associated resistance due to adsorption, R ad ) or by the fundamental catalytic turnover process (with an associated charge transfer resistance, R CT ) [17]. In the present study, operating at 1.00 V vs Ag/AgCl (compared to 0.8 V in previous studies [17]) appears to have made adsorption much less of an impediment than the catalytic turnover process, with the R CT being, in all cases greater than the R ad . Both the R CT and the R ad were low in comparison with previous conducting polymer films prepared by us [17]; this is to be expected from the higher applied bias.
Comparing the nanowires/PPy with the irregular-shaped particle/PPy, the resistances were marginally lower for the former than the latter, under both dark and light conditions, but of the same order as the control PPy film. The CaMn 2 O 4 nanowires/PPy was, therefore, a slightly better catalyst than the irregular-shaped CaMn 2 O 4 particles/PPy, particularly under light illumination. The ohmic resistance, R el , was of the same order for all samples (17.83-17.91 Ω cm 2 ) ( Table 2). Higher C dl values were observed for both samples under light illumination. Hence the major effect of the light illumination appears to be the increase in the electrochemically active area of the films. Figure 7 shows Tafel plots of the catalysts at much higher overpotentials than previously examined [17], with resulting data tabulated in the last two columns of Table 2. The exchange current density, i o , provides a measure of the rate of catalysis at the reversible potential when the overpotential is zero. The catalytic performance as a function of increasing bias is given by the Tafel slope. As shown in Table 2, the higher applied potential also appears to have had a beneficial effect on the Tafel data, which were improved relative to previous studies [17]. The exchange current density and the Tafel slope of the prepared samples varied in the order nanowires/PPy < irregular-shaped particles/PPy. However, the difference between the nanowires/PPy and irregular-shaped particles/PPy was insignificant, which explains nearly the same photocurrent produced by the samples. The slightly higher dark-and photo-current for the nanowires/PPy in comparison to irregular-shaped particles/PPy could be attributed to the higher electrochemically active area of the former relative to the latter.

Conclusion
In the present study, CaMn2O4 ultrafine powders with different morphologies were synthesised and their catalytic performance in photo-electrochemical water splitting was investigated. CaMn2O4 powders with irregular-shapes and nanowire shapes were synthesised using a dry mechanochemical method and a hydrothermal method, respectively.
To study their photo-electrocatalytic properties, CaMn2O4 powders were embedded within polypyrrole to form an anode in a photo-electrochemical cell. It was found that irrespective of the morphology of CaMn2O4, the presence of CaMn2O4 in the electrode resulted in a higher dark and light current, in comparison to the control without CaMn2O4. The evolution of O2 gas from the electrode surface was also observed. Thus, CaMn2O4 showed a catalytic property in the water oxidation reaction. Upon light illumination, the current density was increased and the evolution of O2 gas also increased, demonstrating the photocatalytic nature of CaMn2O4.
The electrode with CaMn2O4 nanowires exhibited higher dark-and light-current in comparison to the electrode with irregular-shaped CaMn2O4 particles. Electrochemical impedance spectroscopy studies revealed that the electrochemically active area increased in the order: PPy alone < irregularshaped CaMn2O4 particles/PPy < CaMn2O4 nanowires/PPy, which was identified as a reason for the

Conclusions
In the present study, CaMn 2 O 4 ultrafine powders with different morphologies were synthesised and their catalytic performance in photo-electrochemical water splitting was investigated. CaMn 2 O 4 powders with irregular-shapes and nanowire shapes were synthesised using a dry mechanochemical method and a hydrothermal method, respectively.
To study their photo-electrocatalytic properties, CaMn 2 O 4 powders were embedded within polypyrrole to form an anode in a photo-electrochemical cell. It was found that irrespective of the morphology of CaMn 2 O 4 , the presence of CaMn 2 O 4 in the electrode resulted in a higher dark and light current, in comparison to the control without CaMn 2 O 4 . The evolution of O 2 gas from the electrode surface was also observed. Thus, CaMn 2 O 4 showed a catalytic property in the water oxidation reaction.
Upon light illumination, the current density was increased and the evolution of O 2 gas also increased, demonstrating the photocatalytic nature of CaMn 2 O 4 .
The electrode with CaMn 2 O 4 nanowires exhibited higher dark-and light-current in comparison to the electrode with irregular-shaped CaMn 2 O 4 particles. Electrochemical impedance spectroscopy studies revealed that the electrochemically active area increased in the order: PPy alone < irregular-shaped CaMn 2 O 4 particles/PPy < CaMn 2 O 4 nanowires/PPy, which was identified as a reason for the higher dark and photocurrent of CaMn 2 O 4 nanowires/PPy electrode. However, surface-area-normalised data suggest that the influence of particle shapes on the light-driven catalysis of CaMn 2 O 4 is relatively weak. The result suggests that the difference in catalytic activities among the crystal facets of CaMn 2 O 4 is small.