The Inﬂuences of Assisting Gas Type and Process Parameters on the Fiber Laser Microproﬁling of Thin CoCr Tubes for Vascular Stents

: Cobalt chromium (CoCr) alloy tubes have been widely used in manufacturing of vascular stents, due to their excellent bio-mechanical properties, especially their high strength. In recent years, ﬁber lasers have been used in the micro-machining of vascular stents, given their better cutting quality than neodymium-doped yttrium aluminum garnet (Nd:YAG) lasers. A comparison study of CoCr ﬁber laser cutting with oxygen and argon is presented, and the differences, such as surface topography, chemical composition, and kerfs geometry, between the oxygen cuts and argon cuts are studied. Three types of topographies are obtained for the oxygen cuts, and the underlying reason for the different topographies are discussed. The inﬂuences of key parameters including power, repetition rate, pulse width, and cutting speed on the cutting quality are analyzed. The present research can also provide an optimization guideline for the micro-proﬁling of CoCr vascular stents.


Introduction
Vascular stents are tiny mesh-like devices that are placed into an obstructed artery to open the lumen and allow smooth blood circulation [1]. Based on a stent's expansion method, stents are classified into two categories: balloon-expanding and self-expanding. Materials such as 316L stainless steel, L605 CoCr alloy, and polymer are used for manufacturing balloon-expanding stents. NiTi alloy is used for manufacturing self-expanding stents, given its superior elastic and shape memory properties. In recent years, CoCr alloy has gained interest due to its excellent radial strength and, therefore, its ability to produce extra-thin struts with increased strength [2]. They are also MRI (Magnetic Resonance Imaging) compatible as well as radiopaque.
The design of stents is complex and, as they are very small, precise manufacturing processes are necessary. Because of the non-contact, precise, and localized energy inputs [3], 3D laser profiling has become the primary choice for stent cutting. Considerable research has been conducted on neodymium-doped yttrium aluminum garnet (Nd:YAG) laser cutting of stents. Kathuria et al. [4] described the precision manufacturing of stainless steel stents using a Nd:YAG laser, and a noticeable heat-affected zone (HAZ) was detected in the cross-sections. To minimize the HAZ size, optimized process parameters (a high repetition rate and short pulse width) were suggested. Pfeifer et al. [5] investigated the Nd:YAG laser cutting of NiTi alloys and studied the influences of process parameters on cutting quality. The detected HAZ size ranged from 6 to 30 µm. Embrittlement in the HAZ can lead to microcracks and shorten a stent's fatigue life, as described by Miller et al. [6]. Sudheer et al. [7]

Laser Cutting
A tube profiling system for stent manufacturing was used in this work. The system was integrated with a fiber laser (SPI), of which the pulse wave shape was rectangular. The maximum power was 200 W, and the laser spot size was about 20 µm. The laser was coupled to a cutting head with a 50 mm focal lens and a coaxial nozzle with a 0.4 mm diameter for the addition of an assisting gas. To control positioning, a highly integrated linear/rotary motion platform (Aerotech) was used. The rotary axis accuracy was ±15 arcsec, and the linear axis accuracy was ±0.5 µm. To avoid back damage, a copper wire with an outer diameter of 50 µm was inserted into the tube during the cutting process.
As shown in Figure 1, a ring with three grooves was designed to evaluate basic characteristics, such as surface topography, kerf width, dross formation, and HAZ.

Materials
The CoCr tubes used in the experiments were designed specifically for the production of balloon-expanding stents. The tubes had an outer diameter of 2.0 mm and a wall thickness of 150 μm. The chemical composition of the CoCr tubes is given in Table 1.

Laser Cutting
A tube profiling system for stent manufacturing was used in this work. The system was integrated with a fiber laser (SPI), of which the pulse wave shape was rectangular. The maximum power was 200 W, and the laser spot size was about 20 μm. The laser was coupled to a cutting head with a 50 mm focal lens and a coaxial nozzle with a 0.4 mm diameter for the addition of an assisting gas. To control positioning, a highly integrated linear/rotary motion platform (Aerotech) was used. The rotary axis accuracy was ±15 arcsec, and the linear axis accuracy was ±0.5 μm. To avoid back damage, a copper wire with an outer diameter of 50 μm was inserted into the tube during the cutting process.
As shown in Figure 1, a ring with three grooves was designed to evaluate basic characteristics, such as surface topography, kerf width, dross formation, and HAZ. To study the influences of process gas type on cutting quality, two sets of experiments were conducted. Oxygen and argon were taken as the assisting gases in Set A and Set B, separately. The oxygen reaction released extra energy in the laser cutting process, and the thermal balance equation was calculated by Equation (1).
is the power abstracted, is the energy released during the oxidation reaction process, H is the enthalpy change, and is the thermal conduction. Thereby, the cutting process with oxygen requires less than the cutting process under argon conditions, as argon is inert. Thus, different process parameter scopes were needed in the two sets of experiments. The key parameters (laser power, repetition rate, pulse width, and cutting speed) were varied in the experiments. Their variation scopes are shown in Tables 2 and 3.
High gas pressure can benefit the ejection of the melt and cooling of the cutting kerf, which in turn reduces the HAZ and dross formation. Therefore, the gas pressure was usually set as high as possible [5]. However, in the profiling of stents, high gas pressures may bend and decline the dimension accuracies of the stents, as the stents are flexible [19]. Based on the preliminary experiments, the gas pressure was constant at 6 bar. To study the influences of process gas type on cutting quality, two sets of experiments were conducted. Oxygen and argon were taken as the assisting gases in Set A and Set B, separately. The oxygen reaction released extra energy in the laser cutting process, and the thermal balance equation was calculated by Equation (1).
P las is the power abstracted, Q oxid is the energy released during the oxidation reaction process, H t is the enthalpy change, and Q cond is the thermal conduction. Thereby, the cutting process with oxygen requires less P las than the cutting process under argon conditions, as argon is inert. Thus, different process parameter scopes were needed in the two sets of experiments. The key parameters (laser power, repetition rate, pulse width, and cutting speed) were varied in the experiments. Their variation scopes are shown in Tables 2 and 3.
High gas pressure can benefit the ejection of the melt and cooling of the cutting kerf, which in turn reduces the HAZ and dross formation. Therefore, the gas pressure was usually set as high as possible [5]. However, in the profiling of stents, high gas pressures may bend and decline the Appl. Sci. 2017, 7, 608 4 of 12 dimension accuracies of the stents, as the stents are flexible [19]. Based on the preliminary experiments, the gas pressure was constant at 6 bar.

Cutting Surface Topography
Distinctions in the surface topographies between oxygen cuts and argon cuts were observed from both macro and micro views. Traditional striation topography could be observed on the cutting surface of the oxygen cuts. However, only layer topography was observed on the cutting surface of all argon cuts with different process parameters, as shown in Figures 2a and 3a. In the micro view, abundant micrometer particles and voids were formed on the surface of the oxygen cuts, as shown in Figure 2b; meanwhile, no particles or voids could be observed on the argon cuts, and the surfaces were smooth and compact at the micrometer scale, as shown in Figure 3b.   Tables 4 and 5, respectively, show the chemical composition of the oxygen cuts surface and the argon cuts surface. "Original" in the table indicates the laser cuts without any post process, and "Pickling" represents the laser cuts processed using acid pickling.

Element Compositions of the Cutting Surface
About 33% oxygen was observed on the original oxygen cuts surface, and the contents of Cr, Co, as well as other elements, had changed. The chemical composition of the argon cuts surfaces showed little change, except for small amounts of oxygen (about 3.43%) and carbon (about 4.03%). The results demonstrated that the oxygen conditions can change the chemical composition of the cuts on the surface, while the argon conditions did not. Acid is usually used for eliminating dross formation in the manufacturing process of stents, which was induced by laser cutting. The samples were etched in a solution (HF:HNO3:H2O, 2:15:83) for three hours at room temperature. Figure 4 shows an image of the oxygen cuts with acid pickling. The particles and voids disappeared, and the surface topography changed compared with the original topography. Figure 5 shows the argon cuts with acid pickling, and the results showed that the acid pickling process had no influences on the surface topography.   Tables 4 and 5, respectively, show the chemical composition of the oxygen cuts surface and the argon cuts surface. "Original" in the table indicates the laser cuts without any post process, and "Pickling" represents the laser cuts processed using acid pickling.

Element Compositions of the Cutting Surface
About 33% oxygen was observed on the original oxygen cuts surface, and the contents of Cr, Co, as well as other elements, had changed. The chemical composition of the argon cuts surfaces showed little change, except for small amounts of oxygen (about 3.43%) and carbon (about 4.03%). The results demonstrated that the oxygen conditions can change the chemical composition of the cuts on the surface, while the argon conditions did not. Acid is usually used for eliminating dross formation in the manufacturing process of stents, which was induced by laser cutting. The samples were etched in a solution (HF:HNO3:H2O, 2:15:83) for three hours at room temperature. Figure 4 shows an image of the oxygen cuts with acid pickling. The particles and voids disappeared, and the surface topography changed compared with the original topography. Figure 5 shows the argon cuts with acid pickling, and the results showed that the acid pickling process had no influences on the surface topography.  Tables 4 and 5, respectively, show the chemical composition of the oxygen cuts surface and the argon cuts surface. "Original" in the table indicates the laser cuts without any post process, and "Pickling" represents the laser cuts processed using acid pickling. About 33% oxygen was observed on the original oxygen cuts surface, and the contents of Cr, Co, as well as other elements, had changed. The chemical composition of the argon cuts surfaces showed little change, except for small amounts of oxygen (about 3.43%) and carbon (about 4.03%). The results demonstrated that the oxygen conditions can change the chemical composition of the cuts on the surface, while the argon conditions did not.

Element Compositions of the Cutting Surface
Acid is usually used for eliminating dross formation in the manufacturing process of stents, which was induced by laser cutting. The samples were etched in a solution (HF:HNO 3 :H 2 O, 2:15:83) for three hours at room temperature. Figure 4 shows an image of the oxygen cuts with acid pickling. The particles and voids disappeared, and the surface topography changed compared with the original topography. Figure 5 shows the argon cuts with acid pickling, and the results showed that the acid pickling process had no influences on the surface topography.  The energy dispersion spectrum (EDS) results of the cuts processed with acid pickling are also shown in Tables 3 and 4. For the oxygen cuts, the content of Cr and oxygen decreased remarkably. For the argon cuts, the elements composition was similar to the original surface. Chromic oxide is easy to dissolve in acid, and it could then be concluded that the particles on the oxygen cuts surface are oxides. Thereby, the dross formation on the oxygen cuts was easily removed by the acid pickling process. However, the acid pickling process had a limited influence on the argon cuts surface, and the dross formation was not eliminated.

Kerf Geometry and Dross Formation
Because of the recast layer and dross formation, irregular kerfs were observed in both the oxygen cuts and the argon cuts. Dross formation was also attached to the inside walls of the tubes, as shown in Figure 6. However, with the acid pickling process, a different phenomenon was observed. As shown in Figure 7, neat kerfs were obtained on the oxygen cuts and dross formation was eliminated. Unneat kerfs still existed on the argon cuts and dross formation did not decrease.   The energy dispersion spectrum (EDS) results of the cuts processed with acid pickling are also shown in Tables 3 and 4. For the oxygen cuts, the content of Cr and oxygen decreased remarkably. For the argon cuts, the elements composition was similar to the original surface. Chromic oxide is easy to dissolve in acid, and it could then be concluded that the particles on the oxygen cuts surface are oxides. Thereby, the dross formation on the oxygen cuts was easily removed by the acid pickling process. However, the acid pickling process had a limited influence on the argon cuts surface, and the dross formation was not eliminated.

Kerf Geometry and Dross Formation
Because of the recast layer and dross formation, irregular kerfs were observed in both the oxygen cuts and the argon cuts. Dross formation was also attached to the inside walls of the tubes, as shown in Figure 6. However, with the acid pickling process, a different phenomenon was observed. As shown in Figure 7, neat kerfs were obtained on the oxygen cuts and dross formation was eliminated. Unneat kerfs still existed on the argon cuts and dross formation did not decrease.  The energy dispersion spectrum (EDS) results of the cuts processed with acid pickling are also shown in Tables 3 and 4. For the oxygen cuts, the content of Cr and oxygen decreased remarkably. For the argon cuts, the elements composition was similar to the original surface. Chromic oxide is easy to dissolve in acid, and it could then be concluded that the particles on the oxygen cuts surface are oxides. Thereby, the dross formation on the oxygen cuts was easily removed by the acid pickling process. However, the acid pickling process had a limited influence on the argon cuts surface, and the dross formation was not eliminated.

Kerf Geometry and Dross Formation
Because of the recast layer and dross formation, irregular kerfs were observed in both the oxygen cuts and the argon cuts. Dross formation was also attached to the inside walls of the tubes, as shown in Figure 6. However, with the acid pickling process, a different phenomenon was observed. As shown in Figure 7, neat kerfs were obtained on the oxygen cuts and dross formation was eliminated. Unneat kerfs still existed on the argon cuts and dross formation did not decrease.
Unneat kerfs influence the stents' dimension accuracy, as well as the surface quality. Dross formation is unacceptable in the manufacturing process of vascular stents, as it can be detrimental to a person's health after being implanted into a vein.
For improving surface quality and eliminating HAZ, an electrochemical polishing process is necessary in the manufacturing process of metal stents, and is always followed by the acid pickling process. Using a polishing process, the salient materials on a stent's surface can be removed; however, unneat kerfs and dross formation with argon cuts are harder to resolve through the polishing process. Thereby, oxygen is more suitable than argon as the assisting gas in the fiber laser cutting process of vascular stents. Figure 8 shows a sample processed with an electrochemical polishing step.

Kerf Geometry and Dross Formation
Because of the recast layer and dross formation, irregular kerfs were observed in both the oxygen cuts and the argon cuts. Dross formation was also attached to the inside walls of the tubes, as shown in Figure 6. However, with the acid pickling process, a different phenomenon was observed. As shown in Figure 7, neat kerfs were obtained on the oxygen cuts and dross formation was eliminated. Unneat kerfs still existed on the argon cuts and dross formation did not decrease.
(a) (b) Figure 6. Kerf geometry and dross formation of the cuts before the acid pickling process: (a) oxygen cut; and (b) argon cut. Unneat kerfs influence the stents' dimension accuracy, as well as the surface quality. Dross formation is unacceptable in the manufacturing process of vascular stents, as it can be detrimental to a person's health after being implanted into a vein.
For improving surface quality and eliminating HAZ, an electrochemical polishing process is necessary in the manufacturing process of metal stents, and is always followed by the acid pickling process. Using a polishing process, the salient materials on a stent's surface can be removed; however, unneat kerfs and dross formation with argon cuts are harder to resolve through the polishing process. Thereby, oxygen is more suitable than argon as the assisting gas in the fiber laser cutting process of vascular stents. Figure 8 shows a sample processed with an electrochemical polishing step.

Influences of the Processing Parameters on Cutting Quality
Oxygen cuts were selected as research objects and the influences of the processing parameters on cutting quality were discussed in terms of surface topography, kerf width, and HAZ.

Surface Topography
As shown in Figure 9, different surface topographies were observed, which can be classified into three types: molten globule topography, striation topography, and molten pool topography. Molten globule topography has many globules on the cutting surface; striation topography is a regular topography in the fiber laser cutting process; and molten pool topography has irregular pools on the surface.
The repetition rate and pulse width have similar influences on surface topography; by increasing Unneat kerfs influence the stents' dimension accuracy, as well as the surface quality. Dross formation is unacceptable in the manufacturing process of vascular stents, as it can be detrimental to a person's health after being implanted into a vein.
For improving surface quality and eliminating HAZ, an electrochemical polishing process is necessary in the manufacturing process of metal stents, and is always followed by the acid pickling process. Using a polishing process, the salient materials on a stent's surface can be removed; however, unneat kerfs and dross formation with argon cuts are harder to resolve through the polishing process. Thereby, oxygen is more suitable than argon as the assisting gas in the fiber laser cutting process of vascular stents. Figure 8 shows a sample processed with an electrochemical polishing step.

Influences of the Processing Parameters on Cutting Quality
Oxygen cuts were selected as research objects and the influences of the processing parameters on cutting quality were discussed in terms of surface topography, kerf width, and HAZ.

Surface Topography
As shown in Figure 9, different surface topographies were observed, which can be classified into three types: molten globule topography, striation topography, and molten pool topography. Molten globule topography has many globules on the cutting surface; striation topography is a regular topography in the fiber laser cutting process; and molten pool topography has irregular pools on the surface.
The repetition rate and pulse width have similar influences on surface topography; by increasing repetition rate (or pulse width), molten globule topography, striation topography, and molten pool topography appear successively.

Influences of the Processing Parameters on Cutting Quality
Oxygen cuts were selected as research objects and the influences of the processing parameters on cutting quality were discussed in terms of surface topography, kerf width, and HAZ.

Surface Topography
As shown in Figure 9, different surface topographies were observed, which can be classified into three types: molten globule topography, striation topography, and molten pool topography. Molten globule topography has many globules on the cutting surface; striation topography is a regular topography in the fiber laser cutting process; and molten pool topography has irregular pools on the surface.
The repetition rate and pulse width have similar influences on surface topography; by increasing repetition rate (or pulse width), molten globule topography, striation topography, and molten pool topography appear successively. The pulse's wave shape is rectangle, and average power can be calculated using Equation (2). The applied laser energy per cutting length ( ) is an important parameter that determines the heat input and mass of molten melt in the kerf section. can be calculated using Equation (3).
represents the peak power controlled by the power modulated fiber laser, represents the duty ratio, represents the pulse width, represents the laser frequency, and represents the cutting speed.
With a low repetition rate (or pulse width), the applied laser energy per cutting length is low, and the mass of the melt is limited. Most of the melt is ejected from the cutting kerf, accompanied with a small amount of melt being turned into globules, induced by the cooling and ejecting effect of the assisting gas. With intermediate , an appropriate amount of metal is molten and regular striation topography is formed because of the combined effects of high repetition rate, pulses, and assisting gas. With high repetition rate (or pulse width), an excess of heat is concentrated in the base material, an excessive mass of metal is molten, and then the melt with good fluidity is ejected, and thereby forming pool topography with the ejecting effect of the assisting gas.
Based on Equation (3), has the same impact on as and . However, different phenomena were observed in the cutting surface topography. As shown in Figure 9c, only striation topography was observed. In the given process parameter range, with increasing , the striations became coarser and no molten globule topography or molten pool topography appeared. It could then be concluded that, although has the same impact on as and , it has slighter influences on the surface topography compared to and . and not only determine the value The pulse's wave shape is rectangle, and average power P ave can be calculated using Equation (2). The applied laser energy per cutting length (E pcl ) is an important parameter that determines the heat input and mass of molten melt in the kerf section. E pcl can be calculated using Equation (3).
P pk represents the peak power controlled by the power modulated fiber laser, δ represents the duty ratio, τ represents the pulse width, f represents the laser frequency, and ν represents the cutting speed. With a low repetition rate (or pulse width), the applied laser energy per cutting length is low, and the mass of the melt is limited. Most of the melt is ejected from the cutting kerf, accompanied with a small amount of melt being turned into globules, induced by the cooling and ejecting effect of the assisting gas. With intermediate E pcl , an appropriate amount of metal is molten and regular striation topography is formed because of the combined effects of high repetition rate, pulses, and assisting gas. With high repetition rate (or pulse width), an excess of heat is concentrated in the base material, an excessive mass of metal is molten, and then the melt with good fluidity is ejected, and thereby forming pool topography with the ejecting effect of the assisting gas.
Based on Equation (3), P pk has the same impact on E pcl as τ and f . However, different phenomena were observed in the cutting surface topography. As shown in Figure 9c, only striation topography was observed. In the given process parameter range, with increasing P pk , the striations became coarser and no molten globule topography or molten pool topography appeared. It could then be concluded that, although P pk has the same impact on E pcl as τ and f , it has slighter influences on the surface topography compared to τ and f . τ and f not only determine the value of E pcl , but also the heating and thermal conduction process. The heating and thermal conduction processes have underlying and complex impacts on cutting quality.
ν has more complex impacts on cutting quality, which not only influence the valve of E pcl , but also the cooling and ejecting effects. As shown in Figure 9d, with both low and high values for ν, globules could be observed on the cutting surface. With a low ν, E pcl is high, but the cooling effect is strengthened, and a topography combined with globules and pools was observed. Increasing ν will decrease E pcl and weaken the ejecting and cooling effects. With a high ν, a topography mixed with globules, striations, and pools was observed.

Kerf Width
Stents' struts are very small, and their widths are about 150 − 250 µm. To ensure the accuracy of strut width, path skewing of about one half the kerf width from the design path is necessary in the laser cutting process. To study the kerf width quantitatively, three positions, the entrance, middle, and exit of the kerf, were measured. To eliminate the impacts of machine rotating precision and measuring error, three kerfs around the ring were measured and then averaged. The samples were processed with acid before measuring. Figure 10 shows the influence of the process parameters on the kerf width.
Appl. Sci. 2017, 7, 608 9 of 12 of , but also the heating and thermal conduction process. The heating and thermal conduction processes have underlying and complex impacts on cutting quality. has more complex impacts on cutting quality, which not only influence the valve of , but also the cooling and ejecting effects. As shown in Figure 9d, with both low and high values for , globules could be observed on the cutting surface. With a low , is high, but the cooling effect is strengthened, and a topography combined with globules and pools was observed. Increasing will decrease and weaken the ejecting and cooling effects. With a high , a topography mixed with globules, striations, and pools was observed.

Kerf Width
Stents' struts are very small, and their widths are about 150 250 μm. To ensure the accuracy of strut width, path skewing of about one half the kerf width from the design path is necessary in the laser cutting process. To study the kerf width quantitatively, three positions, the entrance, middle, and exit of the kerf, were measured. To eliminate the impacts of machine rotating precision and measuring error, three kerfs around the ring were measured and then averaged. The samples were processed with acid before measuring. Figure 10 shows the influence of the process parameters on the kerf width. Typical horn-kerfs were obtained in this research. All kerfs' middle widths were narrower than the entrance and exit widths. Kerf width gradually increased with increasing repetition rate and pulse width. Increasing the repetition rate or pulse width increased the power density, as well as the mass of melt. Accordingly, the kerf width was enlarged. The increased power also made a wider kerf. However, the effect was not as obvious as increasing pulse width or repetition rate.
Increasing cutting speed resulted in a widening of kerf width. However, when the speed exceeded a specific value, the kerf was narrowed. Cutting speed influenced the mass of the melt, Typical horn-kerfs were obtained in this research. All kerfs' middle widths were narrower than the entrance and exit widths. Kerf width gradually increased with increasing repetition rate and pulse width. Increasing the repetition rate or pulse width increased the power density, as well as the mass of melt. Accordingly, the kerf width was enlarged. The increased power also made a wider kerf. However, the effect was not as obvious as increasing pulse width or repetition rate.
Increasing cutting speed resulted in a widening of kerf width. However, when the speed exceeded a specific value, the kerf was narrowed. Cutting speed influenced the mass of the melt, the cooling effect, combustion-supporting effect, as well as the ejecting strength. A low cutting speed would lead to a higher power density and a greater mass of melt, but the cooling effect was strong, which would take away the amount of heat and limit the mass of the melt. Thus, the cutting kerf was narrow. With a high cutting speed and low power density, the mass of molten melt was limited. Weakening the ejecting-strength with a high cutting speed also contributed to narrowing the cutting kerf, which is why the cutting kerf was narrow with both low and high cutting speeds. Figure 11 shows a representative microstructure of cutting kerfs. A clear boundary could be seen between the substrate material and the re-crystallization zone. The substrate material's grains were much larger than those of the re-crystallization zone. In the re-crystallization zone, the smallest grains were observed near the cutting kerf, which were induced by the fast cooling effect.

Heat Affected Zone
Appl. Sci. 2017, 7, 608 10 of 12 the cooling effect, combustion-supporting effect, as well as the ejecting strength. A low cutting speed would lead to a higher power density and a greater mass of melt, but the cooling effect was strong, which would take away the amount of heat and limit the mass of the melt. Thus, the cutting kerf was narrow. With a high cutting speed and low power density, the mass of molten melt was limited.
Weakening the ejecting-strength with a high cutting speed also contributed to narrowing the cutting kerf, which is why the cutting kerf was narrow with both low and high cutting speeds. Figure 11 shows a representative microstructure of cutting kerfs. A clear boundary could be seen between the substrate material and the re-crystallization zone. The substrate material's grains were much larger than those of the re-crystallization zone. In the re-crystallization zone, the smallest grains were observed near the cutting kerf, which were induced by the fast cooling effect. Based on the measurements of all cuts, the thickness of the re-crystallization zone ranged between 4 μm to 10 μm, and no noticeable difference in the HAZ size between different cuts were observed. The material in the HAZ had a different micro-structure than that of the substrate material, which should be removed using electrochemical polishing technology to ensure the material's bio-mechanical properties.

Conclusions
Oxygen and argon have different impacts on the CoCr fiber laser cutting process. Oxygen helps molten melt burning, and an amount of oxide particles were observed on the surface of the oxygen cuts. Dross formation could be easily eliminated by the acid pickling process, and therefore neat cutting kerfs and non-dross formation could be obtained. Through the acid pickling process, the cut compositions were similar to the raw material. Argon is a type of inert gas, and, when protected with argon, the cutting process does not change the composition of the cuts. The cutting surface was compact and the acid pickling process had no effect on the cutting surface topography or dross formation. Dross formation and un-neat kerfs are challenges in argon cuts for manufacturing CoCr stents. Compared with inert gases, oxygen is preferential as the assisting gas in the fiber laser cutting of CoCr stents.
Three types of topographies were obtained in the oxygen cuts: molten globule topography, striation topography, and molten pool topography. Cuts with molten globule topography were difficult to separate from the tubes. In this case, in the manufacturing process of stents, fragments attach to the stent struts and lead to waste products. Molten pool topography is also not ideal, Based on the measurements of all cuts, the thickness of the re-crystallization zone ranged between 4 µm to 10 µm, and no noticeable difference in the HAZ size between different cuts were observed. The material in the HAZ had a different micro-structure than that of the substrate material, which should be removed using electrochemical polishing technology to ensure the material's bio-mechanical properties.

Conclusions
Oxygen and argon have different impacts on the CoCr fiber laser cutting process. Oxygen helps molten melt burning, and an amount of oxide particles were observed on the surface of the oxygen cuts. Dross formation could be easily eliminated by the acid pickling process, and therefore neat cutting kerfs and non-dross formation could be obtained. Through the acid pickling process, the cut compositions were similar to the raw material. Argon is a type of inert gas, and, when protected with argon, the cutting process does not change the composition of the cuts. The cutting surface was compact and the acid pickling process had no effect on the cutting surface topography or dross formation. Dross formation and un-neat kerfs are challenges in argon cuts for manufacturing CoCr stents. Compared with inert gases, oxygen is preferential as the assisting gas in the fiber laser cutting of CoCr stents.
Three types of topographies were obtained in the oxygen cuts: molten globule topography, striation topography, and molten pool topography. Cuts with molten globule topography were difficult to separate from the tubes. In this case, in the manufacturing process of stents, fragments attach to the stent struts and lead to waste products. Molten pool topography is also not ideal, as pools on the cutting surface lower the surface quality. Striation topography is therefore the best choice.
The repetition rate and pulse width had similar impacts on cutting quality, including the surface topography and cutting kerf. The power had less of an impact on cutting quality than repetition rate and pulse width because of the cutting mechanism of pulsed lasers. Cutting speed had a more complex impact on cutting quality because it not only influenced the value of E pcl , but also the cooling effect, ejecting effect, and combustion-supporting effects.
In conclusion, a guideline regarding profiling CoCr stents with fiber lasers can be given: first, use oxygen as the assisting gas and confirm the gas pressure; the gas should eject the molten melt smoothly, and cannot bend the stents as stents are always flexible. Second, melt the right mass of metal with a high frequency, low pulse width, suitable power, and speed. Third, adjust the pulse or frequency to obtain striation topography.